"Hematite pellets were electro-deoxidized to iron in molten sodium hydroxide to produce iron containing about 10-wt % oxygen. The anodic reaction was the evolution of oxygen on an inert nickel anode. Before the electrochemical reaction, there is a reaction between sodium hydroxide and ferric oxide to form sodium ferrite and, in order to compensate for the reduction in sodium oxide content, 1 wt % sodium oxide is added to the melt. In a laboratory cell, the cell voltage was 1.7 V with a current density of 5000 A m-2, a current efficiency of 90% and an energy consumption of 2.8 kWh kg-1.Introduction The iron and steel industry contributes about 2.3 bn tonnes/annum of the carbon dioxide to the atmosphere, which is about 10% of the total, and some believe that, in order to prevent a catastrophic rise in the earth’s temperature, carbon dioxide emissions must be reduced by 50% come 2050. However, by 2050, it is likely that the iron and steel industry would have grown significantly so that the production may have risen to 2 or 3 bn tonnes/year so in order to meet the 50 % reduction on today’s figure, the carbon dioxide may have to be reduced to 25% or less, which is a very demanding requirement. There are probably three ways of reducing the carbon dioxide output:1. By capture and sequestration, but this may be technically very demanding.2. Reduction using hydrogen in place of carbon."

Jan 1, 2009

By Xinlei Jia, Wenming Guo, Yanling Zhang

A large amount of stainless steel dust rich in Fe, Cr, and Ni has been being generated in China. Smelting treatment is accepted as a practical method for the recovery/reutilization of these second resources, during which Fe, Cr, and Ni is reduced into one metal phase and then separated from the residue slag. Based on the typical compositions of stainless steel dust, the residual slag can be termed as CaO-SiO2-MgO-Al2O3 system. In this paper, the activity coefficients of Cr in Fe-Cr-Ni-C (-Si/Al) melt and the properties of CaO-SiO2-MgO-Al2O3- 1%CrO system thermodynamically approached. Then, in laboratory experiments, the recovery ratios of Cr and its distribution behaviors between Fe-Cr-Ni-C melt and CaO-SiO2-MgO-Al2O3 slag system were examined.

Jan 1, 2015

By B. A. Paponetti

The following report discusses the bioleaching of chalcopyrite of italian origin catalyzed by Thiobacillus ferrooxidans. The developments vcr.ius time of the main .biochemical and chemical reactions involved in the production of soiuble and insoluble species were investigated focusing on the times at which they begin and bow long they last. The precipitates were characterized both in quantity and in quality relating the rate of the process to the precipitates fonnatiom. A material. balance has been made to verify the proposed mechanism.

Jan 1, 1991

By Young-Sool Jin, Heung Nam Han, Hong Joon Kim, Jae Kon Lee

A mathematical model was developed considering non-symmetric cooling' and stress distribution in both thickness and width direction of strip on a run-out table of hot strip mill. In order to solve a transient heat transfer equation including the heat evolved from phase transformation, a finite element method coupled with thermodynamic and kinetic analyses was applied. The heat capacity of each phase and heat evolution due to phase transformation were obtained from the thermodynamic analysis of the Fe-C-Mn-Si system based on a sub lattice model. The phase transformation kinetics of the steels was derived by using an inverse additivity technique with continuous cooling experiments. Heat transfer coefficients of strips on the run-out table were, by applying an inverse method, determined from the actual mill data under various cooling conditions. As for the stress analysis, the density change of strip due to cooling and phase transformation, and the transformation superplasticity were considered. A 90nstitutive equation for the transformation superplasticity, which is related to the phase transformation kinetics and the internal stress due to the density change of strip, was applied. A finite element method was adopted to calculate the deformation behaviour of strip on a run-out table of hot strip mill. Using the models, the temperature-phase-deformation history and distribution of a strip on the run-outtable was calculated.

Jan 1, 2001

By Jiangwei Shen, Cong Wang, Haibin Zuo

The research on the formation of Silico-Ferrite of Calcium and Aluminium (SFCA) in the process of cooling and solidification is rarely reported. The crystallization process was observed by using scanning electron microscopy (SEM) and optical microscope in this paper. The effect of different cooling system on the microstructure and phase composition of the sinters was investigated to obtain the appropriate cooling rate to improve the metallurgical properties of sinters. The experimental results show that the crystallization of calcium ferrite is getting better when the cooling rate is decreased from water quenching to cooling in the air. There are a large number of hematite phases with interconnected crystal structure in the sample cooled in the air. In the case of the compressive strength, it was determined by the mineral composition and pore structure, higher SFCA and hematite contents in sinter cooling in the air lead to a higher strength. Glass phase in the water quenching sinter was the major reason for the lowest strength. High porosity contributes to a decrease in compressive strength for the sinter cooling in the furnace. Therefore the air cooling was the appropriate cooling rate to achieve high quality sinter under this experimental condition.

Jan 1, 2016

By Michael E. Stout

M.A. Industries, Inc. has developed and is now offering on a commercially available basis, complete systems to recover and recycle lead from spent SLI batteries. The system begins with the breaking and separation of the component parts of the batteries and subsequent treatment of the effluent water produced by this operation. The recyclable materials recovered from this process are metallic lead, lead paste and polypropylene. The lead paste is introduced into a process to convert it from a lead sulfate to a lead carbonate. The process also regenerates the salt solutions into reusable carbonate. The lead carbonate is then leached into an acid bath where it is later recovered by a proprietary electrolytic process. The metallic lead is recovered in a short rotary furnace producing metal for further refining and alloying. The polypropylene is further washed and then introduced to a reclaim extruder along with the proper modifiers and additives. The resulting resin can then be sold on the open market to injection molding processors. This complete system greatly reduces the amount of waste to be disposed of and completely complies with all applicable EPA guidelines.

Jan 1, 1993

By Xuyang Liu, Xuewei Lv, Chenguang Bai, Meilong Hu

"The electro-deoxidation process for ilmenite concentrate in molten salt was studied by cyclic voltammetry and AC impedance spectroscopy. The results from cyclic voltammetry are consistent with those of AC impedance spectroscopy. The results showed that the electro-deoxidation process for ilmenite concentrate consists of two steps. In the first step, Fe is reduced from the ilmenite concentrate. The second reaction is the decomposition of TiCh. CaTiCh is an intermediate product. At low voltage, the electrochemical reaction is the main step. With the increasing potential, the diffusion of ion is the main rate controlling step for the electro-deoxidation of FeTiO3.IntroductionTitania and titanium-rich products are mainly prepared from ilmenite concentrates (FeTi03), which contain about 40%-60% T1O2 after ore dressing and other physical or chemical processes [1]. At present, the main methods to prepare titania are the sulfuric acid process and the chloride process, but the sulfuric acid process consumes a large amount of sulfuric acid and the materials requirements for the chloride process are strict [2], Since the Electro-Deoxidization in Molten Salt (FFC) method was put forward in 2000, many researchers have successfully extracted the metal and alloys by this method, such as Ti, Cr, Tb, Si, Al-Si, TiV, FeTi, etc. [3-7], FeTi alloy is a typical hydrogen storage material, and because of its favorable properties, the preparation of FeTi alloy has become a hot research topic [7-9]. However, the mechanism of electro-deoxidization has not been studied thoroughly [10-11]. Therefore, in this study, the electro-deoxidation process for titanium concentrate was investigated by electrochemical methods, and the study makes a contribution to improving the current efficiency of the electrolysis."

Jan 1, 2012

By S. S. Ibrahim

The left behind material after the combusion of fossel fuel in some power stations in Cairo; weighing tens of tons every years, was investigated. The material called "Fly Ashes" containing 7.5% Ni, 10.0% V and 9.50% Cr; could be considered as a promising source of such valiable elements. As well as the small grain size (050 70 "m) of the material, and besides the complexity of their formation history, hydrometallurgical methods appeared to be the effective technique to deal with. Yet, preconcentration is possible by means of magnetic and gravity separation methods. The end product is assaying 16.60% Ni and 20.2S!; V with weight recovery of about 60.15%.

Jan 1, 1995

By Yuanbo Zhang, Guihong Han, Guanghui Li, Tao Jiang, Zengqing Sun, Yanfang Huang

"Because of small specific surface area and poor ballability, vanadium/titanium-bearing magnetite is difficult for production of oxidized pellet. A novel organic copolymer binder, modified humic acid (MHA), has been authorized recently in China. Effects of the novel MHA binder on the quality of V/Ti-bearing magnetite pellets are studied in this paper. Experimental results show the MHA binder can obviously improve the strength of green pellet. Because of better heat endurance, the MHA binder pellet has a higher strength than Peridur pellet under the same preheating conditions. Moreover, TFe grade of pellet with the MHA binder is much higher than that of the bentonite pellet. The strength of preheated pellet containing MHA binder of 0.25%~1.0% meets the requirements of oxidized pellet production by grate-kiln process. Comparatively, MHA is a promising orgainc binder for iron ore pellets. Its price is only one tenth of Peridur price and about 3 times of bentonite price.IntroductionThe iron-making practices show that the use of pellet is beneficial to blast furnace life, productivity and fuel savings. Therefore, many iron-making plants have expanded the production of oxidized pellets in order to meet the needs of modern large-scale blast furnaces [1]. Presently, bentonite is widely used to improve the quality of iron ore pellets. The negative effects of using bentonite include decreasing total iron (TFe) grade and degrading the metallurgical properties of the final products [2, 3]. Many studies, therefore, have been conducted on the application of organic binders to overcome the weakness of the inorganic bentonite. In comparison with inorganic binders, one of the biggest strengths of organic binders is low residual silica content [4]. However, those studies showed that the economics of foreign organic binder addition into pellets was not attractive. For example, the compression strength of preheated pellets and roasted pellets are both too low, resulting in powder generation and ring formation in the industrial rotary kiln [3, 4]."

Jan 1, 2011

By Richard D. Hagni

The United States is dependent upon foreign sources for more than 93% of its bauxite and alumina supply. Domestic production of bauxite, which comes from Alabama, Georgia and Arkansas, is limited to those bauxite ores containing less than about l ½ % iron. Bauxites with higher iron contents are generally not utilized because they cause problems in bauxite calcining and especially because they produce undesirable brick discoloration and cracking. In order to improve beneficiation and expand the utilization of high-iron or ferruginous bauxites, a mineralogical and textural study has been conducted on selected samples from the Eufaula, Alabama, bauxite district. Reflected light microscopic, petrographic, and X-ray techniques have shown that a variety of iron minerals are present, including hematite, goethite, lepidocrosite, siderite, pyrite, marcasite, and ilmenite. Although the iron minerals may be locally concentrated into concretions and pisolites, most occur as very fine grains that are disseminated and show a variety of intergrowths. Mineralogical and textural observations indicate that the fine-grained iron mineral grains may be amenable to high gradient magnetic separation.

Jan 1, 1981

By Z. Smieszek, J. Botor, Z. Miczkowski, S. Sobierajski

"From 1978, the direct process for the smelting of chalcocite concentrates in a flash furnace by the Outokumpu method has been applied at the Glogów II copper smelter. The chemical composition of these concentrates make it necessary to control the process very strictly. In this paper, the method for controlling and measuring the main technological parameters of the copper production by flash smelting is being presented. It includes the determination of the chemical composition of the concentrate, its grain structure, the temperature of liquid products of the process, oxygen content in process gases, as well as lead concentration in copper and copper concentration in slag.The main process parameters are determined from the mass and energy balances. The relations between parameters, such as an effect of grain structure of a concentrate on oxygen and oil consumption, and dependence of chemical composition of a concentrate on capacity and products quality are discussed. 1. IntroductionThe Polish copper concentrates, as most concentrates occurring worldwide, contain from 18% to 30% Cu, and less sulphur (7-11%) and iron (2-5%). The main copper-bearing mineral contained in the concentrates is chalcocite, while bornite and chalcopyrite are present in smaller quantities. Moreover, the organic carbon (5-7.5%), arsenic (0.05-0.3%) and lead (1.2-3.0%) are also contained in the concentrates. The gangue consists mainly of silica, aluminosilicates, calcium carbonate and magnesium carbonate. Their proportions make the addition of slag-forming agents unnecessary.The composition of Polish concentrates, especially their low iron content, allows their application in the direct flash smelting process for blister copper production. Low sulphur content is the factor which determines the necessity of oxygen application in this process."

Jan 1, 1989

The paper describes the propensity of tin to form intermetallic compounds with microalloying elements such as Nb, Ti and aluminium, which are commonly used as additions to achieve particular combination of strength and toughness. Two series of alloys were prepared by arc melting under an argon atmosphere. Each series was based on Fe, Sn and A1 with either Nb or Ti additions. The microstructures were studied using scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and microprobe analysis. It was found that the level of Nb addition has an effect on the formation of Sn-rich compounds. For small Nb additions, no Sn containing compounds were found, whereas in higher Nb alloy, a Laves phase (FezNb, hexagonal, a = 0.4830 nm and c = 0.7879 nm) containing about 1 at % Sn was found. A FezNb3 phase (cubic, a = 1.1261 nm) associated with the formation of alumina was also found but did not contain tin. No Sn containing compounds were found with Ti additions. The experimental observations have been compared with thermodynamic calculations performed using MTDATA.

Jan 1, 1999

By J. F. White

An experimental study was undertaken to evaluate the feasibility of a selective chloridizing roasting pre?treatment process for the elimination of impurities from zinc feed?stocks prior to recovering zinc by conventional unit operations. In this investigation, a number of chemistries that might serve as a basis for such a pre? treatment process were examined. A variety of chloridizing agents were admixed with EAF dust to promote the selective removal of lead and cadmium by the formation of volatile metal chlorides, he results of the experimentation firmly establish that selective chloridizing roasting is a technically feasible means of eliminating lead and cadmium from EAF dust. Excellent extraction efficiencies were accomplished with a number of chloride additives; as high as 98 percent lead extraction and 88 percent cadmium extraction were attained with minimal zinc losses, Continuous pilot?scale tests reinforced the trends established by laboratory?scale experimentation, Attempts of chlorine elimination using pyrohydrolysis were less successful. The extent of chlorine elimination was found to be highly dependent upon EAF dust sample type and treatment temperature.

Jan 1, 1996

By H. Eccles

BNFL, an internationally acclaimed company noted for its nuclear fuel cycle services and waste management technologies, collaborated with Viridian BioProcessing Ltd, a small company acknowledged for developing environmental biological processes, and an internationally recognised professor of biological sciences, to develop an unique bioremediation process for treating toxic, heavy metal contaminated land. This paper describes the process, with particular reference to the problem and scope of land contamination with toxic, heavy metals and the current available technologies. The process technologies are based on using indigenous, soil micro-organisms which can be stimulated to produce acid or sulphide ions to mobilise or precipitate the heavy metals respectively. Laboratory studies have indicated metal removal efficiencies of greater than 90 % can be achieved, whilst recovery efficiencies from the metal loaded leachate are even higher at approximately 95%.

Jan 1, 1996

By Kazuyuki Kikuta

MMAJ, a govemmental organization in Japan, has carried out a 4 year project for the development of the decontamination and metals recovering technology for the fly ashes from municipal waste incineration. Heavy metals (zinc, lead and copper) are recovered as raw materials for the non-ferrous metals production, without formation of any waste materials to be disposed. More than 500 thousands tonnes a year of fly ashes generation from the municipal waste incineration has been one of the main social issues in Japan, because most of them need to be disposed to the registered areas after decontamination, and occupy 5% of the municipal wastes disposed. The segregation, flotation and chemical process are applied to the treatment of the primary fly ash from municipal waste incineration, and MF (Mitsui-type blast furnace) Process after the chlorine removal to the secondary fly ash. The main results of experiments are -About 90% of heavy metals, zinc, lead and copper, can be recovered from the primary and the secondary fly ashes to the products for the non-ferrous metals production. -Both of the leaching residue from the primary fly ash treatment and the slag from the secondary fly ash treatment can be used as a raw material for the cement production, meaning that the decontamination technology for the ashes without the landfill has been established. -Dioxins in the primary ash can be decomposed satisfactorily, and the dioxins content in the segregation furnace gas is less than O.lng-TEQ/Nm3 without any gas cleaning system

Jan 1, 2003

By Gong-yi Guo, Yu-li Chen

"A partially-stabilized zirconia powder was prepared by metalorganic precipitation process from technical-grade zirconium oxychloride and the effluent of an acrylic acid plant. The effluent contained low molecular weight carboxylic acids, i. e., acrylic acid and acetic acid. The· developed process is based on the selective precipitation of acrylic acid at suitable pH values by the addition of zirconium oxychloride to the effluent. The resulting precipitate is a precursor that can yield a pure, ultrafine, and partially-stabilized zirconia powder. The evolution of formation of the partially-stabilized zirconia in the present process was investigated using thermal analysis, infrared spectroscopy, and X-ray diffraction technique. Environmental, technological and cost advantages will make the present process feasible for manufacturing advanced zirconia ceramics.IntroductionIn recent years the superior mechanical, thermal, electrical and chemical properties of stabilized zirconia have become the focus of growing scientific and technological interest, and hence resulted in various structural and functional applications. The great potential of the material has given rise to numerous preparation approaches to obtain the material with the excellent properties; nevertheless, an extensive number of programmes are underway worldwide aimed at understanding and improving both the preparation and behavior of stabilized zirconia ultrafine powders. (1 – 8)."

Jan 1, 2000

By S. Sugiyama, M. Kiuchi

"New metal working processes, such as the mashy-state mixing, mashy-state forging, mashy-state rolling and mashy-state extrusion are developed and applied to manufacture the so-called particle reinforced metals, fiber reinforced metals, particle reinforced cladding metals and so forth. These metal-ceramics composites are made of metal sheets, metal powders, ceramics particles and ceramics fibers. The mashy-state processes are also used to work those composites into bars, wires, tubes, plates, sheets, machine parts and other products. The working conditions necessary to manufacture sound composite products are clarified and the mechanical properties of the products are investigated. Through the investigation, it becomes clear that the mashy-state processes are useful and effective to manufacture metal-ceramics composites. It is al so known that these processes may be applied in various ways to development of new metal matrix compounds. IntroductionThe so-called metal-ceramics composites and processes to manufacture them are now being widely investigated in order to comply with increasing demands for new materials with novel and excellent mechanical properties and functions. The metal-ceramics composites are expected to have superior characteristics with respect to the elastic modulus, hardness, anti-wear resistance, high temperature strength and other mechanical properties to those of conventional metallic materials.The present authors ha v e been investigating into new metal working processes which are based upon the characteristics of metals and their alloys in the mashy-state. In the mashy-state, the metal (or alloy) includes both of the solid and liquid components. According to the fact that the partial melting takes place and the liquid component usually exists at grain boundaries, the metal in the mashy-state has quite different mechanical properties from those of the metal in the solid-state. Because of that the bonding force among grains is very weak due to the partial melting occurred at grain boundaries, the mashy metal has distinctively low flow-stress and high deformability. The mashy metal splits into grains or particles and sticks to others very easily. It is so soft as to be stirred up just like a lump of sherbet, but it is sufficiently viscous to be mixed up with other materials, such as ceramics particles and ceramics short-cut fibers."

Jan 1, 1988

By Gudrun A. Saevarsdotti

For decades tile aluminium industry has been practicing gas treatment of aluminium melts. This treatment is of great importance because of its influence on 'impurity" and inclusion removal from the melt. The gas-melt interaction is greatly influenced by the gas composition, melt temperature etc. This paper gives an overview of the interaction between argon-chlorine gas mixtures and the aluminium melt. It covers the thermodynamics of the reaction between the chlorine and a number of different elements commonly found in liquid aluminium, and discusses the behaviour of reaction products in the melt. The paper reports an experimental study of the behaviour of the chlorine-molten aluminium interface, using sodium contaminated aluminium melt with and without the addition of grain refiner.

Jan 1, 1996

By E. A. van Dijk

Dusts from steel-making processes contain substantial amounts of zinc. Such dusts are also a hazardous waste and dumping them becomes unacceptable from environmental point of view. Therefore processes that can recover zinc and possibly other metals from steel-making dusts are being investigated. The aim of this paper is a contribution to the more fundamental kinetic aspects of zinc reduction from silica free calcium ferrite slags. The effects of alumina, lime and magnesium oxide contents of the slag, the COICO, ratio and the effect of initial Fe2O3/CaO ratio were studied experimentally at 1400°C The results indicated that the reduction of zinc from molten slag was possibly a first order reaction. As expected higher COICO, ratios increased both the extent and the rate of reduction. It was also observed that a higher iron content of slag improved the reduction of zinc from calcium ferrite slags. This fact seems to support the proposed mechanism that zinc is partly reduced by ferrous iron to zinc vapour and that ferric iron is reduced by carbon monoxide. The reduction rate of zinc in these slags was decreased by increasing alumina content of the slag. Alumina decreased the calculated optical basicity of the slag showing the fact that reduction of zinc oxide was more favorable in more basic slags. Probably the formation of complex ions by alumina and zinc oxide such as ZnAl2O32+ lowers the activity of Zn2+ ions in the slag and hence render them more difficult to reduce.

Jan 1, 1999

By F. Shahbazian

attempt to systematize the knowledge on slag viscosities, the present work was carried out. The Among the physical properties of slags, viscosity is very important in understanding the mass out in the temperature range 1438-1762 Q The rotating cylinder method was used in the viscosity measurements. Crucibles and spindles made out of pure iron were employed. The transfer phenomena in metallurgical processes. The viscosities of fayalitic slags are of great interest in the non-ferrous metal industry, with special reference to copper production. In an slags were prefused before the measurements. In order to take into account the vaporization reactions involving CaF2, pre- and post measurement samples of the slags were chemically analysed and the compositions were ascertained. The results show that in the case of the CaO-SiO2 system, CaF2 additions tend to decrease the viscosity, in accordance with the expectations. In the case of the "FeO"-SiO2 system, at higher "FeO" / SiO2 ratios in the slags, a reverse trend was observed. The results are discussed on the basis of a viscosity model for silicate melts developed in the present laboratory as well as the structural considerations of silicates.

Jan 1, 2000