By Ben-Zion Weiss, Melvin R. Meyerson

FATIGUE crack propagation in some aspects can be viewed as being a result of localized plastic deformation concentrated near the tip of the crack.' Deformation is influenced by microstructure which in turn can affect the fatigue crack growth significantly. To study the effect of localized microstructural changes on fatigue crack propagation, cantilever-type notched specimens were subjected to cyclic bending at constant load amplitude. The extent of fatigue crack propagation was obtained by measuring the length of the crack by periodic observation with a microscope on the polished side of the sample,2"4 and these data were used in preparing the curves in the figures which follow. Figs. 1 (solid lines) and 2 show experimental results obtained in austenitic type 302 stainless steel containing higher than standard carbon (0.24 pct C) and 310 stainless steel. Both steels were homogenized for 8 hr at 1120°C and then water-quenched in order to prevent the precipitation of carbides. Fig. 3 shows experimental results obtained on 9440 low alloy steel in the normalized condition and in the quenched and tempered (580°C) condition. Indications of microstructural influence can be seen in scattering of the experimental data. The degree of scattering depends on both the microstructure and the amount of cyclic stress applied to the sample. For microstructures which are more easily deformed plastically, e.g., normalized or annealed as compared with hardened and tempered structures, the scattering is greater. Similarly, higher stresses produce greater scattering in the results, regardless of whether the cause of the stress increase is due to initial loading conditions or the growth in crack length. Scattering is believed to be a result of partial redistribution in the stress field around the tip caused by plastic deformation. This opinion is borne out by much smaller scattering of experimental results in the austenitic 302 high-carbon (0.24 pct C) steel. In this steel, plastic deformation in the neighborhood of the crack causes partial mar-tensitic transformation of metastable austenite,5 which in turn restrains further plastic deformation. As a result, the stress redistribution around The tip is reduced. Partial martensitic transformation was confirmed

Jan 1, 1969

By K. C. Strebig, C. W. Schultz, A. A. Selim

For some time researchers have attempted to in- crease drilling efficiency (and therefore reduce costs) by adding certain chemical agents to the circulating medium. The effect of some organic additives on the diamond drilling of quartzite was recently investigated in the laboratory by personnel of the U. S. Bureau of Mines. In these tests, the penetration rate and bit life were found to increase with the use of additives. In addition, an economic analysis of a hypothetical 1000-ft hole showed that additives can reduce drilling costs by 30%. Wetting Agents Improve Drilling Efficiency Much of the interest in the use of wetting agents to improve drilling efficiency is the result of an observation made by Rehbinder, Shreiner, and Zhigach.1 These investigators postulated that drilling creates a region of increased crack formation directly below the bit and that a circulating medium that wets the rock will also penetrate the micro- cracks of the predestruction zone. Increasing the molecular affiinity (wetting ability) of these circulating media for the surface of the rock helps the deformation and destruction by softening the rock in the zone of increased crack formation. In this manner, the hardness or strength of the rock is decreased as the medium wets the rock in the predestruction zone. This is known as the "Rehbinder effect." Rehbinder's work has prompted many investigators to examine the relationship between the use of additives and the mechanical destruction of rock. Engelmann, Terichow and Selim reported that the maximum penetration of the rock by a diamond point in a solution environment was at the isoelectric point of the mineral and solution interface.2 Improvement in rock breakage with the use of additives was observed by Frangiskos and Smith.3 Joris and McLaren suggest that additives having a lower surface tension than water will also be more efficient in cooling the diamonds.4 Additives help remove fine cuttings from the face of the bit and improve efficiency. The latter two authors also report an improvement in impregnated bit life and penetration rates with the use of soluble oil additives. All of these investigations were initiated in the hope of discovering what economic benefits will accrue with the use of additives.

Jan 10, 1969

Francis Drake, Bulawayo, Rhodesia, So. Africa (communication to the Secretary *):—I should like to place on record some data in addition to those given by Mr. Canby in his paper. I regret that my notes have been destroyed so that I can give no accurate measurements of the water jacket that I am about to describe. This furnace mas erected in Cerro Gordo, Inyo county, Cal., early in 1875, and I think it quite possible that it was the first applied in lead smelting. It was made of plate iron and elliptic in shape, the inner dimensions being about 54 by 42 in. by 48 in. high. The distance between the inner and outer plates was about 6 in. Tuyere holes, one at the back and two on each side, about 12 in. in diameter, were made in this, and in these were placed cast-iron water tuyeres about 16 in. long, the diameter of the blast orifice at the point being about 3 in. The height from tuyeres to feed door was about 9 ft., but the top of the charge was kept about 5 ft. above the tuyeres. There was a space of about 12 in. between the jacket and the top brick-work. This brick-work was supported by a cast-iron plate resting on four cast-iron columns. At the beginning, the jacket was lined with air-dried radial bricks, made of crushed quartz and fire-clay, as it was thought that the jacket would not stand the heat on its bare plates. After a short time the practice was altered and no lining mas put in. The jacket was closed at the top and had a steam drum connected by two pipes at the back. This steam drum was connected to the boiler in which the steam was made for driving the Baker blower, the rock breaker and the pumps. The bottom of the jacket mas also connected to the boiler. The jacket was run under boiler pressure (80 Ib.) for some time, but eventually cracks developed in the inner plate between the tuyere holes,

Jan 1, 1913

W. E., RUDER, Schenectady, N. Y. (written discussion *).-Professor Howe, with characteristic thoroughness, has demonstrated that Professor Jeffries' "Reversed Inheritance" explanation of the case in question is contrary to fact, as shown by many previous observers. Since the photographs were my own, I feel it my duty to say a few words in discussion. In the first place, it is to be noted that these photographs were of pressed powders, and although many of Professor Jeffries' original experiments were made from this kind of material, the nature of such a specimen must of necessity be different from that of the fused metal, although the same basic laws of grain growth may apply in both cases, certain factors, such as the rate of change, for example, are undoubtedly different in each case. That the 1000° C. grain is a natal grain is evident from its appearance contrasted with the more perfectly formed, though smaller, grains in the 1300° C. photograph. I am not sure that Professor Howe's explanation of the formation of this grain is necessarily the correct one, although it agrees with. Stead and Carpenter's results. I am inclined to think that this grain may have been formed on heating, because I have been able to produce grains of the shape and magnitude of Stead and Carpenter's grains by heating to 850° C. pure electrolytic iron, which has been subjected to a strain gradient. On reheating to 1300° C., the mobility being so much greater, the individual crystals had time for unhampered re-arrangement and growth after their second refinement on passing Ac3, so that we have in this case a true fused metal condition in which the individual crystals are arranged in true equiaxed grains of a size consistent with their high temperature anneal. In this case the grains are equiaxed, inheriting none of the columnar tendencies of the previous grain, because they were not affected by any strain gradient, except possibly some accidental local gradients. It seems to me that the introduction of pressed powders into the discussion of grain growth, where allotropic changes take place, unnecessarily complicates an already complicated problem.

Jan 1, 1918

By Frederick H. Williams

THE object of this paper is to bring to the attention of those members of the Institute who are interested in the subject, a method for the estimation of manganese, which has been frequently used in the laboratory of the Vulcan Steel Works during the last eight months, and which is deemed worthy of more general use. It is simply an adaptation of well-known processes, for the purpose of determining this element in pig iron and steel. In general, the method consists in precipitating the manganese as binoxide, dissolving in dilute sulphuric acid in the presence of an excess of a standardized solution of oxalic acid, and titrating the remainder of the oxalic acid left unoxidized with permanganate of potash. For this method, therefore,. two standardized solutions are needed, viz., a permanganate solution and an oxalic acid solution. The permanganate solution is made so that 1 c.c. is equivalent to 1 mgr. of iron. By using so weak a solution and keeping the bulk of the solution to be titrated down to 75 c.c. or a little less, the accuracy of the process is greatly increased, since the final reaction is almost if not quite as sharp as if a stronger solution were used. The oxalic acid' may be of almost any strength, but if made so that 1 c.c. requires 3 c.c. of the permanganate to oxidize it, it will auswer well. The process is then, as follows : from 1 to 2 grams of pig iron or steel are dissolved in 40 to 50 c.c. of concentrated nitric acid with the aid of heat. As soon as solution is effected, in the case of steel, add gradually and cautiously, the solution being kept boiling, sufficient pulverized chlorate of potash to precipitate the manganese as binoxide. Two grams will be a great abundance. In the me of pig iron, first remove the carbon and silica by filtering the solution through asbestos and washing with concentrated nitric acid. Filter the strong acid solution in which the binoxide has been precipitated, through asbestos with the aid. of the filter pump. When it has entirely passed through wash well with water. Blow the contents: of the funnel into the beaker in which the precipitation was made and rinse the funnel with a little water.

Jan 1, 1882

By Frederick H. Williams

The object of this paper is to bring to the attention of those members of the Institute who are interested in the subject, a method for the estimation of manganese, which has been frequently used in the labratory of the Vulcan Steel Works during he last eight months, and which is deemed worthy of more general use. It is simply an adaptation of well-known processes, for the purpose of determining this element in pig iron and steel. In general, the method consists in precipitating the manganese as binoxide dissolving in dilute sulphuric acid in the presence of an excess of a standardized solution of oxalic acid, and titrating the remainder of the oxalic acid left unoxidized with permanganate of potash. For this method, therefore, two standardized solutions are needed, viz., a permanganate solution and an oxalic acid solution. The permanganate solution is made so that 1 C.C. is equivalent to 1 mgr. of iron. By using so weak a solution and keeping tile bulk of the solution to be titrated down to 75 C.C. or a little leas, the accuracy of the process is greatly increased, since the final reaction is almost if not quite as sharp as if a stronger solution were used. The oxalic acid may be of almost any strength, but if made so that 1 c.c. requires 3 O.C. of the permanganate to oxidize it, it will auswer well. The process is then, as follows: from 1 to 2 grams of. pig iron or steel ate dissolved in 40 to 50 C.C. of concentrated nitric acid with the aid of heat. As soon as solution is erected, in the awe of steel, add gradually and cautiously, the solution being kept boiling, sufficient pulverized chlorate of potash to precipitate the manganese as binoxide. Two grams will be a great abundance. In the case of pig iron, first remove the carbon and silica by filtering the solution through asbestos and washing with concentrated nitric acid. Filter the strong acid solution in which the binoxide has been precipitated, through asbestos with the aid of the filter pump. When it has entirely passed through wash well with water. Blow the contents of the funnel into the beaker in which the precipitation was made and rinse the funnel with a little water.

Jan 1, 1882

By Willard Jillson

WITHIN the last ten years Kentucky has become celebrated for its low-sulfur bituminous coals. Prior to this time, many investigators had discovered the abundance of this coal but the fact was unknown to the general public until the last extension of Kentucky's mountain railroads was completed. The coals of Kentucky are, broadly, separated into two geographic units-the eastern and the western coal fields. On a basis of their sulfur content these coal fields fall into three units, which are indicated on the accompanying map, by numbers, 1, 2, and 3. The area marked 1, the very southeastern part of the State, shows the lowest sulfur, all coals being averaged. In this field the maximum is 1.04 per cent. and the minimum as low as 0.68 per cent.-both averages and not individual analyses, which would of course show much greater variation. Included in this group are the following counties: Lawrence, 0.87 per cent.; Martin, 0.75 per cent.; Johnson, 0.73 per cent.; Magoffin, 0.S7 per cent.; Floyd, 0.88 per cent.; Pike, 0.68 per cent.; Knott, 1.04 per cent.; Perry, 0.77 per cent.; Letcher, 0.80 per cent.; Leslie, 0.70 per cent.; Harlan, 0.79 per cent.; Knox, 0.86 per cent.; and Bell, 0.92 per cent. The total average sulfur content for these thirteen counties is 0.82 per cent. Bordering the restricted low-sulfur field of eastern Kentucky is the No. 2 belt (slightly darker), which is commonly known as the western border of the eastern coal field. Here the maximum sulfur is 2.91 per cent. and the minimum 1.05 per cent. Again these are averages and not individual analyses. The counties in this group are: Greenup, 2.60 per cent.; Boyd, 1.67 per cent.; Carter, 1.07 per cent.; Morgan, 1.40 per cent.; Wolfe, 1.83 per cent.; Lee, 2.93 per cent.; Breathitt, 1.85. per cent.; Owsley, 1.09 per cent.; Jackson, 1.06 per cent.; Rockcastle, 2.30 per cent.; Clay, 1.09 per cent.; Laurel, 1.08 per cent.; Pulaski, 2.24 per cent.; Whitley, 1.05 per cent.; McCreary, 1.50 per cent.; and Wayne. The sulfur percentage average for this area including fifteen important counties is 1.65 per cent.

Jan 9, 1919

By Hans E. Gustafsson

INTRODUCTION The Kiirunavaara iron ore mine is situated in northern Sweden about 150 km north of the Arctic Circle. The ore body has a sheetlike shape, stretches about 4000 m N-S dipping 60°E and has an average width of 85 m. The ore body is known to a depth of more than 1500 m. Mining at present has reached a depth of about 500 m. The mineral is a magnetite containing 66-68% Fe. The ore body was originally mined as an open pit from 1900-1957. From then on the mining method has been sublevel caving. Production for the last few years has been 20-25 million tons /year. Sublevel caving is a mining method with many merits. One of the most valuable is the ability of using a high degree of mechanization. Today, 25 years after sublevel caving was introduced at Kiirunavaara, the advantages of the method have been more or less exhausted, and the disadvantages are more obvious as the rock pressure increases with depth. One of the disadvantages is the high degree of waste rock in the hoisted ore. Today the waste rock content is about 25% by weight of which 20% comes from the caved rock. Second, we are calculating a relatively high loss of ore (20%). Third, selectivity is unsatisfactory when mining different grades of ore. Field testing sublevel shrinkage caving (MSTM) is primarily aimed at lowering the content of waste rock compared to sublevel caving. ECONOMIC TARGET A simple calculation shows that if the waste rock content can be lowered from 25 to 15% the operational costs of mining will be lowered by about 40 million SEK/year (US $9 million) at a production level of 20 million tons/ year. A 15% waste content is the target of the field test. In the long range a decrease in waste rock dilution will mean lower investment costs for deeper levels. DESCRIPTION OF THE MSTM MINING METHOD One reason for decision to carry out the field test was that with MSTM the development drifts from sublevel caving could be utilized and thus the project could start without delay. The only additional development work needed was the loading level. Fig. 2 shows a profile through the MSTM area 66-68% Fe. and Fig. 3 shows the loading level.

Jan 1, 1981

By Vincent P. Gianella

Barite deposits are of widespread occurrence in Nevada but there are few producing properties; most of the latter are in northern Nevada. The production of the state is small at present-in the neighborhood of 15,000 tons annually-but is steadily increasing. The barite occurs in veins and also as replacement deposits in limestone. The bulk of the production has come from the replacement deposits. It is thought that the barite was deposited from rising hot waters similar to-and probably contemporaneous with-those responsible for some of the metallic ores of the state. This paper discusses only the deposits in northern Nevada. THE commercial mining of barite did not begin in Nevada until 1916 but although the production has been small there has been a rapid increase in tonnage during the past several years. Barite is widely distributed in the state and production comes from at least nine of the seventeen counties. Apparently this is not generally known, as only two counties are mentioned in a recent publication6 dealing with barite. The increase in output is due largely to recently discovered barite deposits in northern Nevada. The principal production has come from the northern portions of Lander and Eureka counties; smaller amounts from Elko County. The discussion in this paper is confined largely to the deposits in these counties. Most of the producing area is tributary to the Western Pacific and Southern Pacific Railroads, whose tracks lie along the Humboldt River. Barite is known from other northern counties but so far the production has been small. The output has come entirely from veins and replacement deposits, the latter largely in sedimentary rocks. In general, the barite from veins is white; that from the replacement deposits usually is dark gray to black, although some is light gray or white. Most of the veins contain sulphides and many barite-bearing veins have been worked for their content of base or precious metals. PRODUCTION The recorded production in Nevada to the end of 1938, according to the U. S. Bureau of Mines,3 is 66,424 short tons, of which 57,157 tons

Jan 1, 1940

By D. P. Pope, T. Vreeland

Observations of dislocations in zinc using Berg-Barrett X-ray micrography confirm the validity of a dislocation etch for (1010) surfaces. A technique for measurement of the depth in which dislocations can be imaged in X-ray micrographs is given. This depth on (0001) surfaces of zinc was found to be 2.5 µ using a (1013) reflection and CoKa radiation. BUCHANAN and Reed-Hill (B & RH) have recently questioned the ability of a dislocation etch to reveal all of the basal dislocations which intersect (1010) surfaces in annealed zinc crystals.' This etch was developed by Brandt, Adams, and Vreeland who conducted a number of different experiments to check its ability to reveal dislocations.2,3 B & RH prepared (0001) foil specimens for transmission electron microscopy from annealed crystals and observed dislocation densities of about l08 cm per cu cm in the foils, while the etch indicated densities of the order of l04 cm per cu cm in their annealed crystals. As this etch has been used in a number of studies of dislocations in zinc, it is of considerable importance to reassess its validity in the light of the B & RH results. The X-ray work reported here was undertaken to check the ability of the etch to reveal dislocation intersections on (1070) surfaces of zinc. The X-ray technique was chosen for this check because it could be applied to the as-grown crystals with a relatively small amount of specimen preparation. We believe that the possibility of accidental deformation in preparation of the bulk specimens is considerably less than that for thin foil specimens suitable for transmission electron microscopy. Unfortunately, basal dislocations are not visible on Berg-Barrett topo-graphs of (1010) surfaces, which are the surfaces on which the etch is most effective. Therefore, a one-to-one correspondence between the etch and X-ray observations could not be made. Basal dislocations near (0001) surfaces have been observed by Schultz and Armstrong4 using the Berg-Barrett technique, but they did not report the as-grown dislocation density observed in their crystals. We have applied the X-ray technique in this study to surfaces oriented from 1 to 2 deg of the (0001) to determine the basal dislocation density, and have compared this density with that observed using the etch on a (1070) plane of the same crystal. The X-ray observations permit determination of the depth in which basal dislocations can be observed under the diffracting conditions used. SPECIMEN PREPARATION High purity zinc crystals are very soft, so a good deal of care must be exercised in the preparation of observation surfaces. As-grown crystals approximately 2.5 cm in diam and 20 cm long were acid cut into 1.25 cm cubes. A thin slab was cleaved from an (0001) surface to produce an accurately oriented reference surface on the specimen. Some of the cubes were examined in the as-machined condition while some were annealed in argon at 410°C for 2 hr. Heating and cooling rates were less than 2°C per min. Some of the specimens were scratched on a (0001) surface with a razor blade to produce fresh dislocations. Approximately 2 mm of material was acid lapped from one face of a cube to produce a surface oriented between 1 and 2 deg from the basal plane and parallel to the [1210] direction. A (1070) surface was also acid lapped. The lap used a 1 to 3 pct solution of HN03 in water to saturate a soft cloth which was backed by a stainless steel plate. The cloth was moved over the crystal surface at a rate of 20 cm per sec while a normal force of about 4 g was maintained between the cloth and the specimen. As-lapped surfaces were examined as were surfaces which were chemically and electrolytically polished after lapping. The small angle between a lapped surface and the (0001) plane was measured to 0.1 deg using a Unitron microgoniometer microscope (the cleaved surface was used as a reference in this measurement). The microscope was modified so that the intensity of reflected light could be continuously monitored on a meter. This modification produced nearly a ten-fold increase in the reproduceability of orientation readings. OBSERVATIONS The Unitron Microgoniometer observations indicated that the lapped surfaces had a terraced structure with the terraces quite rounded and spaced about 0.1 mm in the [1010] direction. The maximum change in slope between terraces was 0.25 deg, indicating a terrace height of about 0.1 µ. A Unitron measurement of the average angle between (0001) and a lapped surface was checked by micrometer measurement of the specimen and found to agree within 0.1 deg. The Berg-Barrett micrographs using (1013) reflections and CoKa radiation5 revealed subboundaries, short dislocation segments, spirals, and loops near the surfaces which were oriented from 1 to 2 deg of the (0001). Micrographs of surfaces prepared by lapping appeared very similar to those of the chemically and electrolytically polished surfaces. The loops and spirals were not extinct in (1013) or (0002) reflections, indicating that they have a nonbasal Burgers vector. Extinctions of the short, straight dislocations indicated that they belonged to an (0001)(1210) system. Fig. 1 is an example of a micrograph which shows a subboundary, and dislocation segments which are pre-

Jan 1, 1970

By J. B. Newkirk, R. W. Hendricks, R. Baro

STUDIES of the kinetics of precipitation in binary alkali halide systems are of interest from a theoretical point of view, because of the possibility of controlling diffusion rates by additions of aliovalent impurities. This note reports some preliminary results of a study of the kinetics of precipitation of AgCl from supersaturated solid solutions of AgCl in NaCl containing trace amounts of divalent cation impurities. In their study of the system NaC1- AgC1, Stokes and Li1 derived the phase diagram containing a mis-cibility gap with a broad maximum at approximately 170°C. They found that single crystals quenched from above the miscibility gap and aged at various temperatures within the two-phase region gradually turned light blue, then cloudy white, and finally opaque. The rate of transformation depended markedly on the aging temperature. The light-blue color in the early stages of aging was interpreted to be the result of Rayleigh scattering from precipitated particles less than 0.1 µ in diameter. These qualitative observations have been confirmed by us. However, a more precise tool was needed in order to quantitatively follow the growth kinetics of the precipitate particles. Because of the suspected small size of the precipitate particles and for other reasons, small-angle X-ray scattering was thought to be a suitable technique for this study. Small-angle X-ray intensities scattered from powder specimens were recorded on a General Electric XRD-5 diffractometer using the four-slit geometry described by Neynaber, Brammer, and Beeman.2 The slits were 0.08 mm wide by 10.00 mm high. It was found that, with very careful alignment, meaningful data could be obtained to within 3 min from the middle of the direct beam. Chromium radiation (?Ka = 2.29Å) was used in order to spread the scattered intensity to a relatively high angle, as indicated by Eq. [1]. A specimen containing 21.0 at. pet AgCl was prepared by melting analytic reagent-grade AgCl and NaCl under a chlorine atmosphere in a vycor cap-

Jan 1, 1964

F. JOHNSON,* Birmingham, England (written discussion t).--. Mr. Skowronski's first melting experiments tend to show that ingots with a "level set" may be obtained without oxygen. Now it is characteristic of all metals which occupy a smaller volume when solid than they do when molten to "pipe." In vertical-cast ingots, this pipe resembles a horn-shaped cavity, with the wide mouth uppermost. In horizontal-cast ingots, the pipe is a longitudinal furrow along the center-line of the ingot surface. If copper be successfully deoxidized and degasified, this furrow will inevitably be produced. In the author's oxygen-free ingots, it is. clear that gases were occluded and these gases effectively opposed the formation of a pipe or furrow by shrinkage (fluid contraction). It is riot a special property of any particular gas which produces this effect. Hence it is not surprising that the author has succeeded in producing level and overpoled ingots through the agency of sulphur. dioxide gas. That he has counteracted the overpoling influence of sulphur by means of oxygen is somewhat difficult to explain, since the well known reaction between cuprous sulphide and cuprous oxide should result in the production of sulphur dioxide gas. Why the presence of excess cuprous oxide should neutralize the overpoling influence of this gas without eliminating sulphur is not at all clear. It is to be regretted that the oxygen was not determined in the bars given in Tables 3 and 4. It is by no means established that sulphur is responsible for the over, poling of ingots given in Table 4, since carbon was used for overpoling. If, however, the same kind of poling treatment was given as that applied in the case of ingots in Table 1, the responsibility of sulphur assumes more definite shape. The author rightly points out that Mr. Johnson's theory of the equilibrium between gases and cuprous oxide does not explain why a simple addition of cuprous oxide does not correct an overpoled charge. Such a charge must be re-worked to "set" copper. This re-working (rabbling) undoubtedly forcibly removes the excess gases, which are not removable by cuprous oxide.

Jan 11, 1918

By W. D. Bennett

AN interesting effect has been observed in the vacuum etching of titanium in the high temperature ß phase. Using a high vacuum annealing furnace, operating at less than 2x10-6 mm with a tubular titanium liner, it has been found possible to etch polished metallographic specimens at different temperatures between room temperature and 1000°C without contamination or increase in hardness.' Heat etching of titanium has been reported by other workers,' but the following example is of interest as an experiment under high vacuum in the absence of any contamination. Two polished specimens of iodide-processed titanium are placed at different positions along the axis of the furnace corresponding to temperatures of 900" and 800°C above and below the a-ß transus. The specimens are then raised to these temperatures and annealed simultaneously for 3 hr under the same high vacuum conditions. After cooling and withdrawing the specimens, their surfaces are photographed without further treatment. Figs. 1 and 2 show the results for the 800" and 900°C specimens, respectively. Fig. 1, corresponding to a vacuum etch in the a region, shows a typical equiaxed structure with what appears to be a slight shift of grain boundaries. Fig. 2, corresponding to a vacuum etch in the ß region, shows an equiaxed type of structure with the growth of striations in certain grains. The striations are only superficial, as a light polish and chemical etch restores the clean equiaxed structure. The vacuum etch, occurring as it does above the a-ß transus, records the state of the metal in the ß phase by means of the surface relief produced by the selective evaporation of metal from different grains; the metal itself reverts to the equiaxed a on cooling. The nature of the ß etch" (Fig. 2) suggests that, in transforming from the close-packed-hexagonal a to the body-centered-cubic ß lenticular-shaped laminae are formed parallel to common planes of the two structures. This would explain why some grains appear to be unaffected by the etch. The technique has interesting possibilities in the investigation of the mechanics of high temperature transformation. Acknowledgment This note is published by permission of the Deputy Minister, Dept. of Mines and Technical Surveys, Ottawa, Ont., Canada.

Jan 1, 1956

By N. H. MacMillan, O. C. Dias

Recent work by Westwood et al. (reviewed in Refs. 1-6) has established that many rocks, minerals, ceramics, and glasses exhibit phenomenologically similar chemomechanical (Rebinder) effects when deformed in different liquid environments, apparently as the result of chemisorption-induced variations in their near-surface flow and flow-dependent fracture behavior. In particular, it appears that there exists an empirical, but apparently general, correlation between the near-surface flow stress of an inorganic nonmetal and its surface charge- namely, that such a solid is hardest at its zero point of charge (i.e., when its zeta potential [ ] = 0) and softens as [ ] increases, regardless of the sign of zeta. Moreover, because near-surface flow and fracture phenomena are two of the important determinants of the rates of machining and comminution processes, both Westwood et al. and others7 have been able to use this so-called "[ ]-correlation" to develop cutting fluids and grinding aids that in many instances have given rise to several fold increases in performance. In addition, Westwood et al. have demonstrated that both aqueous and organic environments can give rise to similar improvements in cutting rate for a given combination of tool and workpiece, provided that both impart the same surface charge to the work- piece (i.e., transfer the same number of electrons to or from its surface). This last finding implies that in any application it should always be possible to find some cutting fluid that is at once effective, cheap, nontoxic, and nonpolluting. Thus, reports of apparently similar environmental influences on the mechanical behavior of diamond,8 certain organic crystals and polymers,9-14 and coa1-15-21 suggest that it is pertinent to ask: (a) whether the [ ]-correlation (or any analogous relationship) extends to coal; and (b), if so, whether this relationship can be used to guide the development of superior aids for grinding coal. Accordingly, correlations have been sought between (1) the zeta potentials, (2) the hardnesses, and (3 and 4) the drilling and grinding characteristics of coals of different rank in different aqueous and organic environments. This paper reports the results of that search.

Jan 1, 1980

By J. Kittl, D. Arias

THE decomposition on cooling of the high-temperature ß bcc phases in copper- or silver-based binary systems usually takes place by a martensitic. massive, bainitic, or pearlitic reaction depending upon the particular conditions of each system. The AgAl system is one of these systems in which a massive or a martensitic transformation can occur upon cooling from the 3 phase field. Recently Hawbolt and Brown1 observed both massive and martensitic transformation products in a 22.7 at. pct A1 alloy. In the present work the massive and the martensitic transformations were investigated in a number of alloys for the composition range between 23.2 and 27.9 at. pct Al. The alloys were prepared using high-purity silver, 99.999 pct, supplied by ASARCO and aluminum, 99.999 pct, supplied by ALCOA. The metals were melted using a graphite or a sintered alumina crucible which was sealed in quartz tubes under an argon atmosphere. The alloys Were remelted to reduce segregation and homogenized in the 13 phase field for 24 hr. The weight of the alloys after homo-genization compared with the initial weight indicating the alloy composition to be within k0.1 pct of the in- tended composition. Chemical analysis of several samples confirmed the estimated alloy composition. All metallographic observations were performed on samples electropolished with ac current using a 10 pct solution of KCN and a stainless-steel electrode. The samples were cut into -1-mm-thick slices, polished, heat-treated in the ß phase field, and quenched in air, ice water, or iced brine. Some heat treatments consisted of a 2-min anneal carried out in air to allow maximum quenching speeds. Other samples were heat-treated in a vacuum of 10"4 torr and quenched using a helium blast in a quenching apparatus described elsewhere.&apos; In both cases, no appreciable losses of silver or aluminum were noted at the sample surface by sectioning and electropolishing. Table I summarizes the microstructure resulting from the various quenching treatments. The composition of the alloys investigated is also indicated on the equilibrium diagram in Fig. 1. The <, hcp phase, typical of a massive ß — cm, transformation, was observed in all alloys. A minimum temperature of 450°C was estimated for this transformation based on preliminary cooling experiments. the results being included in Fig. 1. In these

Jan 1, 1970

By John Richards

MY remarks will be confined to the experience of our company in mining the No. 8 seam of coal in Ohio, although I believe that the relationship existing here between the method of mining and the method of cleaning will hold true in many of the coal seams throughout the country. The increasing demand for a cleaner and better graded product is being felt throughout the entire coal industry, and the methods of mining are playing an important part in the control of various sizes and quality of coal produced. We have found a definite relation between the mechanical loading of coal and its preparation for the market. In the No. 8 coal seam the location of the non-combustible material is regular. The&apos; marketable coal lies in three benches, separated by streaks or bands of impurities. These impurities must be removed from the coal to properly pre pare the product for the market. Where hand-loading methods are employed, the loader removes as much of this non-combustible material as possible at the working face. The impurities that are missed by the loaders are removed as the coal passes through the preparation plant, by means of picking tables. As this method of cleaning cannot improve the quality of the extremely fine sizes, a practice has been established in the company&apos;s hand-loading mines, of undercutting the coal about 2 in. above the bottom of the seam, thereby eliminating any possibility of impurities caused by the cutting machines cutting into the rock bottom below the coal seam.

Jan 1, 1934

By Nicholas J. Grant, Noboru Komatsu

Electron-micrographic studies and hardness tests were made of an internally oxidized dispersion-strengthened Cu-12 vol pct SiO2 alloy follozuing longtime annealing at elevated temperatures. The rate of coarsening of SiO2 particles and the relationship between hardness and interpavticle spacing were Dispersion -strengthened alloys exhibit a remarkable stability of structure and properties at elevated temperatures compared with conventional alloys; nevertheless, when they are exposed to high measured. The rate of coarsening of SiO2 particles is controlled by the decomposition of SiO, rather than by the diffusion rates of silicon or oxygen through the copper matrix. The mechanism of coarsening was also studied by using a diffusion-couple technique. temperatures, weakening takes place as a result of coarsening of the dispersed phase. The theoretical treatment of the coarsening of dispersed phases has been treated by Greenwood,1 wagner,, and others3 by considering the interfacial energy of dispersions and the diffusion of solute atoms. Recently, experimental work on the coarsening of relatively insoluble, finely dispersed cobalt particles in copper was reported by Livingston,4 and on aluminum oxide in nickel by Dromsky, Lenel, and Ansell;5 according to these investigations, the rate

Jan 1, 1964

By Henry Morris

AS STATED last year, in a similar review by David White and the author, any review of the petroleum industry purporting to cover such a wide field can only mention the principal facts. This incompleteness is necessitated not only by the limitations of space, but by the delay in receiving detailed information. The principal feature of the year, in Europe, was a material increase in the consumption of petroleum products, and a notable decline in prices. Although there we relative increases in production in Roumania and Poland, the total did not by any means keep pace with the increase in consumption, which, as usual, was supplied "from America and both the Near and Far East. The interest in Asiatic production, as usual, centers around the Persian fields, which, according to the annual report of the Anglo-Persian Oil Co. published at the close of last year, it was estimated would amount to 3,775,000 tons by the close of the fiscal year, March 1, 1924. Russia also showed an increase in production. In Africa there was nothing of outstanding interest in production, although Egypt showed a decrease and the goverment refinery at Port Said was closed.

Jan 3, 1924

By J. S. Bryner

In the study of metallographic specimens in the electron microscope, there is need for a method of locating the same field in both the light microscope and the electron microscope. This need arises chiefly from the fact that in the electron microscope the magnification and degree of resolution are so much higher, and the field so much smaller than in the light rnicroscope that it is often difficult, if not impossible, to identify positively what is being observed. The difficulty is increased by the fact that, because a transparent film replica of the metal surface must be used in the electron microscope, micro-constituents can be identified not by their color but only by their texture and contours. For these reasons it is desirable to obtain a series of photographs showing the same field in both microscopes in order that the appearance of common microstructures and micro-constituents in the electron microscope may be identified and catalogued for future reference. The need for a method of locating the same field in both microscopes arises also when it becomes desirable to enlarge in the electron microscope for more detailed study a particular interesting structure observed in the light microscope. Using the standard polystyrene-silicalJ replica technique, in which the silica film replica is fished from the ethyl bromide on a 1/8 in. diam zoo-mesh specimen screen, the possibilities of locating a particular area on the film in the electron microscope are rather remote. The desired structure may be obscured by the wires of the specimen screen or unrecognizable at the high magnification. A solution to the problem would be provided if a specially designed specimen screen, containing an opening which could be absolutely identified and quickly located in the electron microscope, could be fastened to the silica film replica in such a position that the desired field on the specimen would be located at the identifiable opening in the specimen screen. The design for such a specimen screen, a method for producing it, and a technique for fastening it to the silica film replica are described below. Description OF Method The Specimen Screen A simple design for a specimen screen containing an opening easy to identify and locate in the electron microscope is one with two lines of openings at right angles in the form of a cross. Such a screen is shown in Fig I. The opening at the center of the cross is identified easily and can be located quickly in the light microscope and in the objective image of the electron microscope. The specially designed specimen screens for this work were produced in quantity by electroforming. On both sides of a polished strip of copper I X 3 X 1/8 in., twenty patterns of the cross of openings were punched with a diamond point micro-hardness tester, using a load of magnitude

Jan 1, 1949

By F. A. Forward, A. H. Ross, J. Halpern

IN treating carnotite ores by carbonate leaching it is often necessary to subject the ore to a prior roast. Among the advantages that may result from roasting are: 1) improvement in settling and filtering characteristics of the ore; 2) destruction of carbonaceous impurities that would otherwise contaminate the leach solution and consume carbonate reagent; and 3) substantial increase in extraction of vanadium, which is usually low when the un- roasted ore is leached. Recovery of vanadium may be an important factor in processing carnotite ores, and the fact that vanadium is usually recovered in good yield by acid leaching has often been an economic advantage over results obtained with carbonate leaching. It has been found that response of an ore to carbonate leaching, following roasting, depends primarily on its composition and on the conditions of the prior roast treatment, particularly with regard to the roasting temperature, the atmosphere maintained above the charge during roasting and cooling, and the presence of certain reagents. These factors, especially the last, virtually determine the extractions of uranium and vanadium attainable by carbonate leaching, as well as the reagent consumption on leaching, whereas adjustment of the leaching conditions has only a limited influence.

Jan 10, 1957