By J. J. Frawley, W. J. Childs, W. R. Maurer

The object of this investigation was to determine the growth habit of bismuth and bisrrtuth alloy dendrites as a function of supercooling. To do this, techniques were developed to increase the amount of supercooling in bismuth and bismuth alloys. For pure bismuth, the growth habit was dependent on the amount of supercooling. At low amounts of supercooling, about 10" C, prismatic dendrites were obtained. With increased supercooling, about 20 C, a hopper growth habit was observed. In many cases where hopper growth had occurred, the hopper dendrites were twinned during the growth process. This twinned surface enable prismatic dendrites to nucleate and grow by a twin plane mechanism. When the amount of supercooling was increased to about 25 °C, the growth habit was a triplanar growth. With still greater supercooling, about 3s°C, a branched growth habit occurred. The exposed planes on the prismatic, hopper,, triplane, and branched dendrites have been determined. The growth habit of the dendrites which grew along the crucible wall was found to have the (111) as the exposed plane, with <211> growth direction. It is apparent that dendritic growth of a metal is dependent on its purity and the solidification variables present. One of the solidification variables is the degree of supercooling. Supercooling, although often observed, has not been studied extensively until recent years. For dendritic growth to occur in a pure metal, the metal must be thermally supercooled. After the dendrites grow into the supercooled melt, the heat of solidification raises the temperature of the specimen to the melting point of the material and the remaining liquid will solidify at this temperature. Decanting is the removal of this remaining liquid before complete solidification. This removal of the remaining liquid after recalescence had occurred is a great aid in the study of dendritic growth. In this investigation, decanting was accomplished by a vacuum-decanting technique . Other investigators1-5 have studied the growth characteristics of various low-melting-temperature pure metals and alloys as a function of supercooling. However, large degrees of supercooling were not included. For their study of dendritic growth of lead, Weinberg and chalmersl employed a decanting technique which was achieved by pouring off the remaining liquid, exposing the solid/liquid interface. This method was employed later by Weinberg and Chalmers2 for the investigation of tin and zinc dendrites. The method for obtaining a solid/liquid interface was improved by Chalmers and Elbaum. They employed a triggered spring which was attached to the solidifying section of the specimen. Upon activation, the spring jerked the solid interface away from the liquid melt. In the study of growth from the supercooled state, a metal of low melting point which exhibited a high degree of supercooling was desired. Bismuth gave very consistent supercooling when a stannous chloride flux was employed. The maximum supercooling obtained was 91°C, with an average supercooling of between 65" and 75°C. The consistency of supercooling greater than 50°C was very high. The use of vacuum to aid in the rapid decanting of molten metal has proven to be very successful in this investigation. The vacuum gives a rapid decantation, usually leaving the solidified metal structure sharply defined. The purpose of this investigation was to study the effects of supercooling and the effects of alloy additions on the growth habit of bismuth dendrites. The structure of bismuth has been variously defined as face-centered rhombohedral, primitive rhombohedral, and hexagonal. However, bismuth has only one plane with threefold symmetry, the (111) plane, and the crystal-lographic structure is considered a 3kn structure. MATERIALS The bismuth which was employed in this investigation was obtained from the American Smelting and Refining Co. of South Plainfield, N. J. The accompanying spectrographic analysis data indicated the bismuth to be 99.999+ pct pure. The tin was obtained from the Vulcan Materials Co., Vulcan Detinning Division, Sewaren, N. J. It was classified as "extra pure". Nominal analysis was 99.999+pct. In order to prevent contamination of the bismuth melt from the atmosphere, an anhydrous stannous chloride (Fisher certified reagent grade) was added to each melt. The fluxing action obtained from the use of the chloride provided a large amount of supercooling in the specimen. APPARATUS A 30-kw, 10,000-cps motor-generator set, connected to a 6+-in.-diam air induction coil, was employed to melt and superheat the specimens. The temperatures were recorded by means of a chromel-alumel thermocouple and a potentiometric recorder. The thermocouples were 0.003 in. in diam, and were encapsulated with Pyrex glass to prevent the thermocouple from acting as a nucleating agent and also from contaminating the melt. Fig. 1 illustrates the vacuum-decanting apparatus when a liquid flux was employed. A standard 30-ml Pyrex beaker was placed on top of an asbestos insulating block. A 5-mm-ID Pyrex tube with aA-in. spacer tip attached to its end was used for the decanting tube. The spacer tip contributed significantly to a successful decanting operation. The tip located the opening of the decanting tube about -^ in. from the bottom of the

Jan 1, 1969

By W. F. Chiao

Ultrasonic attenuation, a, measurements in the frequency range of 5 to 55 mc per sec have been studied to determine their quantitative relationship with the following three variables of mixed microstructures in steels: 1) the volume percent, XF, of polygonal fer-rite in mixed structures of martensite and polygonal ferrite in Fe-Mo-B alloys: 2) volume percent, XA, of retained austenite plus martensite aggregates in high-carbon steel; and 3) substructural differences between 100 pct bainitic ferrite structures formed at various temperatures. The quantitative relationship obtained in the first two conditions by plotting a us the known structural parameters can be expressed, respectively, as: where al, a 2 and C1, Cz are constants. In the third condition the nature of the attenuation depends on the state of dislocations generated at the transformation temperatures and also on the alloy composition. From these measured results, the mechanism of ultrasonic attenuation caused by these mixed microstructures can also be studied. MUCH interest has recently been shown in the application of ultrasonic attenuation and wave velocity measurements to the study of the microstructural characteristics of steels. The general aims of most of the investigations in this field can be grouped into two categories: one is to study the mechanisms of ultrasonic losses caused by the characteristic phases in the microstructure of steel,&apos;&apos;&apos; and the other is to develop nondestructive test methods and applications for quality control.~&apos; 4 Apparently no work has been done on the evaluation of ultrasonic attenuation meas -urements as a means of quantitative determination of a given phase in the microstructure of a steel. It is well-established that the decomposition of austenite results in four main microstructural constituents—polygonal ferrite, pearlite, bainite, and martensite—and that each phase has different mechanical properties. Thus, when a steel consists of mixed microstructures, the mechanical properties can often be related to a quantitative measure of the volume percent of each phase present. This study relates ultrasonic attenuation measurements to: 1) the volume percent of polygonal ferrite in mixtures of martensite and polygonal ferrite in Fe-Mo-B alloys; 2) the substructural differences between 100 pct bainitic ferrite structures formed at various temperatures; and 3) the vol- ume percent of austenite in austenite plus martensite aggregates in a high-carbon steel. The choice of the specimen materials was based on the laboratory stocks which were suitable to produce the required mixed microstructures for this study. EXPERIMENTAL PROCEDURES Materials and Heat Treatment. Polygonal Ferrite Plus Martensite Structures. This mixture of phases was produced in a vacuum-melted Fe-Mo-B alloy. The alloy was hammer-forged at 1900" ~ to a -f-in.-sq bar. By isothermally heat treating the alloy at 1300° F for various times and then water quenching, variations in the amount of polygonal (or proeutectoid) ferrite can be controlled in a microstructure in which the balance of the material is martensite. In the present work, four different times of isothermal transformation were adopted; after heat treatment, the four specimens were machined for ultrasonic measurements. The compositions, heat treatments, and dimensions of the four specimens are listed in Table I. 100 pct Bainite Structures Formed at Different Temperatures. It has been well-established by Irvine et al.= that the presence of molybdenum and boron in ferrous alloys can retard the formation of polygonal proeutectoid ferrite and expose the bainitic transformation bay, so that a more acicular or bainitic ferrite can be obtained over a wide range of cooling rates. Their investigation6 also showed that the mechanical properties of fully bainitic steels are usually closely dependent on the substructural characteristics of the steels. For studying the substructural characteristics in completely bainitic structures, six Fe-Ni-Mo alloys, of which five were free from carbon addition and one with 0.055 pct C addition, were selected so that a wide range of hardness values for 100 pct bainitic ferrite structures could be produced by normalizing at 1900" F followed by air cooling. The different bainitic transformation temperatures were recorded during air cooling. All of the alloys were vacuum-melted and then forged at 1900" F to square bars. Data on the six specimens of these structure series are summarized in Table 11. Austenite Plus Martensite Structures. The high-carbon steel used to study austenite plus martensite structures was vacuum-melted and then forged into Q-in.-sq bar. The series of mixed structures of austenite plus martensite was produced by quenching the specimens from the austenitizing temperature to room temperature and then refrigerating them at various temperatures within the range of martensite transformation to produce different amounts of retained austenite. Data on the four specimens of this series are listed in Table 111. Quantitative Analysis of the Microstructures. The microstructures containing martensite plus polygonal ferrite were analyzed by the point-counting technique.

Jan 1, 1969

By T. V. Philip, R. E. Lenhart

When commercial silicon iron sheets of varying magnetic quality are isothermally annealed at high temperatures, extremely large grains develop in the material having good magnetic properties. These grains are of the (110) [001] orientation and are formed by secondary recrystallization. The primary driving force for this secondary recrystallization is grain boundary free energy. For the secondary grains, activation energies of 103 kcal per mole for nucleation, and of 75.5 kcal per mole for growth, were obtained. The activation energy for nucleation of the secondary grains is consistent with a model involving redistribution of a precipitate acting as the primary grain growth inhibitor. SINGLY oriented silicon iron sheet was first produced in 1935.1 The material as commercially produced today has a very highly developed preferred orientation or texture; up to 95 pct of the grains are crystallographically oriented with their (110) planes in the plane of the sheet and their [loo] directions parallel to the rolling direction. This texture, usually written as (110) [00l], is referred to as the "GOSS" or the "cube-on-edge" texture. Because the magnetic properties of this material are superior to those of the nonoriented sheets in the direction of rolling, the oriented silicon iron has acquired tremendous industrial importance especially in the manufacture of transformer cores and other electrical equipment. The commercially produced material is essentially an iron-silicon alloy containing about 3 1/4 pct Si with minor impurities totaling less than 0.15 pct. The silicon steel heat is melted in the open hearth or electric furnace. The ingots are hot rolled, with or without being slabbed, to strips of 0.100 to 0.080 in. thickness. They are then cold reduced to an intermediate thickness, recrystallized, cold reduced to final thickness, decarburized, and finally annealed at a high temperature. During this high-temperature anneal, extremely large grains with the cube-on-edge texture are produced in the sheet. Several papers have appeared in the literature2-10 relating to the production of the Goss-textured material. Most of these describe the textures produced on cold rolling and on subsequent annealing of single crystal or polycrystalline silicon iron. May and Turnbull11,12 have recently shown the necessity of a second-phase dispersed impurity in the material for the production of the Goss texture. However, none of these papers describes in detail the nucleation and growth kinetics of the (110) [001] grains during the final high-temperature anneal.* The present work, therefore, is an attempt to understand the nucleation and growth kinetics of the cube-on-edge grains in the silicon iron sheet during the final high-temperature anneal.

Jan 1, 1962

By M. Schussler, J. S. Brunhouse

Arc-melted and electron-beam melted tantalum in the cold-worked and the recrystallized conditions showed high strength, good tensile ductility, and excellent notch toughness down to 321°F. Arc-melted material, containing moderate amounts of interstitials, possessed better short-time strength than higher purity electron-beam melted material up to 2000°F. Cold-working substantially strengthened arc-melted tantalum, whereas electron-beam melted material exhibited a low work-hardening rate and possessed better formability characteristics. With identical compositions and microstructures, the mechanical properties of melted tantalum and uacuum-sintered tantalum should be similar. TANTALUM metal usage is increasing rapidly in a number of applications. The outstanding chemical corrosion resistance of tantalum accounts for its applications in chemical processing equipment for severe service conditions and for surgical uses in the medical field. The largest present requirements for tantalum are in the electronics industry, where its special properties are useful in capacitors. The high melting point (5425°F) and inherent ductility of tantalum also suggest that tantalum and tantalum-base alloys might offer an excellent combination of high strength at very high temperatures and good fabri-cability. Pure tantalum has been used in significant amounts in parts requiring high-temperature strength, such as heating elements, reflectors, and heat shields in high-vacuum high-temperature furnaces and in electronic tubes. A few very promising tantalum-base alloys have been developed and are being investigated extensively. The possibilities for tantalum as a high-temperature structural material, either unalloyed or alloyed, will become better defined when more extensive mechanical property data are known. pughl measured the tensile properties of vacuum-sintered tantalum in sheet form for the temperature range of 78" to 1500°K (-321&apos; to 2240°F), and Bechtold reported data obtained at low temperatures.&apos; Drennen3 determined creep and stress-rupture properties of both vacuum-sintered and arc-melted tantalum sheet at 1200 °F. Some additional data on the mechanical properties of tantalum at temperatures up to 5000 °F have been summarized elsewhere.4&apos;5 It is probable that large structural shapes of tantalum, either unalloyed or alloyed, can most readily be produced from ingots prepared by melting. Consequently, the present investigation was undertaken to determine more extensive short-time mechanical properties of tantalum metal consolidated by melting. EXPERIMENTAL PROCEDURE Melting and Fabrication—Two tantalum ingots were utilized in this study to obtain information on the effect of interstitial elements on mechanical properties. Both ingots were melted from Union Carbide Metals Co. tantalum dendrites.

Jan 1, 1961

By H. M. Otte

Certain choices for the shear elements of the inhomogeneous distortion in the phenomenological theory of martensite formation are examined for their agreement with crystallographic and X-ray data of iron alloys. The assumption that the shear elements must represent slip or twinning systems characteristic of bcc metals is found to covey all observations, even when a small uniform dilatation is taken into consideration. In bct martensite, (011) becomes a possible twinning or faulting plane, in addition to {112), and qualitatively similar X-ray line broadening is to be expected from both. The basic concept inherent in the current theoriesl-4 of the formation of martensite is that the interface between the parent (austenitic) and product (martensitic) phase is an invariant strain plane (i.e., one that is undistorted and unrotated). Experimental evidence that the interface is of such a nature is available in certain transformations2&apos;5&apos;6 but for the transformation in iron alloys direct observation has not proved enlightening. Internal strains resulting from the formation of the small martensite platelets within the parent austenite matrix7 make it difficult to produce the desired evidence. Indirect evidence, however, such as the continuity of scratches in passing from untrans-formed to a transformed region, strongly indicates that the habit plane in iron alloys is an invariant strain interface. The scatter in habit planes in a given specimen8 would suggest that internal stresses have a slight but definite influence. On the other hand, composition changes which affect the lattice parameter can alter the habit plane appreciably, and by an amount greater than the scatter.&apos; The success of the theories depends on the choice made for the "inhomogeneous distortion" or "complementary shear&apos;&apos; in the analysis and also on the choice for the parameter 6 representing a small uniform dilatation. In the approach developed by Wechsler, Lieberman, and Read&apos;," it is implicitly assumed that 6 is unity. In the case of iron alloys, all observations cannot be explained without varying either the inhomogeneous distortion or 6 . Bowles and Mackenzie3 considered only the effect of varying d. They found it difficult to reconcile the wide scatter of habit planes with the theory and were forced to the conclusion that it may also be necessary to consider variations or different choices of the inhomogeneous distortion. Wechsler and Read" considered a limited number of possible choices for the inhomogeneous distortion, but no variation in 6, though this could easily have been introduced if so desired. It is the purpose of the

Jan 1, 1961

By John S. Brown

As a part of a symposium on the relations of structure to ore deposition, in February 1938, the writer presented some tentative opinions derived from his experience with a number of important lead-zinc replacement deposits. These ideas were set forth, as a basis for discussion and a stimulus to further inquiry, in a mimeographed leaflet that read as follows: Intimate acquaintance with a number of lead and zinc deposits in metamorphosed limestones seems to indicate the existence of certain common features from which can be established some general principles governing the localization of ore in this type of formation. It is suspected that these principles can be applied, with modifications, to mineralization in unmetamorphosed limestone. In metamorphosed formations, some observed rules are as follows: 1. Bands or masses of pure limestone are very resistant to replacement by ore solutions, and are likely either to contain no ore or to resist replacement until near the end of mineralization. The reason for this apparently is physical, not chemical, since microscopic data indicate that when ore is deposited by far the greater part of it substitutes for carbonate. The chief factor is believed to be a lack of porosity in massive limestone that has undergone flowage and recrystallization. 2. Masses of intensely siliceous or silicated rock are likewise unfavorable ore receptacles. This seems to be accounted for by two factors: (a) chemical unsuit-ability or resistance to replacement, and (b) physical resistance to small-scale brecci-ation, which might faeilitate the opening of effective channelways for solutions. Some low-grade ore may occur, however, and also sporadic fracture fillings. 3. The optimum condition for ore reception appears to be found in bands or areas containing carbonate and silicates (or quartz) intimately mingled in something like equal proportions. In this situation movement is likely to result in mixed flowage and fracture, producing a finc-textured porosity that admits solutions freely and provides access to an abundance of replaceable carbonate. Cleavage cracks in some minerals such as diopside are believed to facilitate the penetration of solutions. 4. Certain minerals or assemblages are regarded as favorable impurities in a limestone and others as unfavorable. Original quartz, and subsequently developed diopside, and perhaps garnet, are typical favorable pre-ore gangue; in general rather equidimensional, brittle minerals. Tremolite, biotite, and probably wollastonite, are typical unfavorable pre-ore gangue; in general highly elongated and somewhat flexible minerals likely to develop under strong shearing stresses. 5. Tentative opinion is that the ratio of lime and magnesia in a limestone is of little or no importance.

Jan 1, 1941

By John S. Brown

As a part of a symposium on the relations of structure to ore deposition, in February 1938, the writer presented some tentative opinions derived from his experience with a number of important lead-zinc replacement deposits. These ideas were set forth, as a basis for discussion and a stimulus to further inquiry, in a mimeographed leaflet that read as follows: Intimate acquaintance with a number of lead and zinc deposits in metamorphosed limestones seems to indicate the existence of certain common features from which can be established some general principles governing the localization of ore in this type of formation. It is suspected that these principles can be applied, with modifications, to mineralization in unmetamorphosed limestone. In metamorphosed formations, some observed rules are as follows: 1. Bands or masses of pure limestone are very resistant to replacement by ore solutions, and are likely either to contain no ore or to resist replacement until near the end of mineralization. The reason for this apparently is physical, not chemical, since microscopic data indicate that when ore is deposited by far the greater part of it substitutes for carbonate. The chief factor is believed to be a lack of porosity in massive limestone that has undergone flowage and recrystallization. 2. Masses of intensely siliceous or silicated rock are likewise unfavorable ore receptacles. This seems to be accounted for by two factors: (a) chemical unsuit-ability or resistance to replacement, and (b) physical resistance to small-scale brecci-ation, which might faeilitate the opening of effective channelways for solutions. Some low-grade ore may occur, however, and also sporadic fracture fillings. 3. The optimum condition for ore reception appears to be found in bands or areas containing carbonate and silicates (or quartz) intimately mingled in something like equal proportions. In this situation movement is likely to result in mixed flowage and fracture, producing a finc-textured porosity that admits solutions freely and provides access to an abundance of replaceable carbonate. Cleavage cracks in some minerals such as diopside are believed to facilitate the penetration of solutions. 4. Certain minerals or assemblages are regarded as favorable impurities in a limestone and others as unfavorable. Original quartz, and subsequently developed diopside, and perhaps garnet, are typical favorable pre-ore gangue; in general rather equidimensional, brittle minerals. Tremolite, biotite, and probably wollastonite, are typical unfavorable pre-ore gangue; in general highly elongated and somewhat flexible minerals likely to develop under strong shearing stresses. 5. Tentative opinion is that the ratio of lime and magnesia in a limestone is of little or no importance.

Jan 1, 1941

By Elmars Ence, Harold Margolin

The partial isothermal section of the Ti-Cu-Zr system at 750°C has been studied. The crystal structure of Ti2Cu has been detevnlined as tetragonal and when expressed as face-centered tetragonal, a = 4.164, c = 3.611 A, and c/a = 0.867. TITANIUM systems in which ß-titanium decomposes eutectoidally into a and a compound rather readily are known as active eutectoid systems. Recently in active eutectoid alloys based on the Ti-Cu system, and containing additionally A1 and Zr, it has been found that zirconium may produce both moderate weakening and marked strengthening at elevated temperatures.&apos; In order to obtain some insight into the behavior of zirconium, an attempt was made to determine whether compounds of the type Tix Zr and TixZryCu exist. Only results of the Ti-Zr-Cu studies are reported here since data on Ti-Zr alloys will be presented in a separate publication. EXPERIMENTAL PROCEDURE Alloys were nonconsumably arc melted in argon atmosphere as 15-g buttons, prepared from materials of the following purities: Bureau of Mines electrolytic Ti — Bhn 63 OFHC copper Reactor Grade Zirconium Bhn .C 150 Prior to alloy preparation the electrolytic titanium was premelted to avoid excessive spattering of the charges during melting. The weight losses during melting did not exceed 1 pct of the total weight of the charge. The alloys prepared are listed in Table I together with analyzed compositions. in cases where they were determined. Specimens for heat treatment were wrapped in molybdenum sheet, annealed in argon-filled quartz capsules, and quenched by breaking the capsules under iced brine. About 1 to 2 sec are required to remove the capsule from the furnace, drop it into the iced brine and break it. Because of the insulation effect of the quartz, this delay in quenching should not produce a large drop in temperature. In many instances, no difference or little difference has been detected between the same specimen quartz capsule quenched or directly quenched in vacuum by an impinging stream of water.&apos; Ti-Cu-Zr alloys were homogenized for 48 hr at 825°C prior to annealing at 750°C. Annealing for 5 days at 750°C produced the same results as 11 days at temperature and it was therefore assumed that 5 days was sufficient to establish equilibrium. Titanium-copper alloys were homogenized for 40 hr at 900°C prior to heat treatment for 6 days at 750°C. Specimens for metallographic examination were electropolished and etched with the following solution:

Jan 1, 1962

By Walter R. Hibbard, Ming-Kao Yen

VARIOUS rationalizations of preferred orientations in cold worked polycrystalline metals have been based on the operation of at least two,1 three,2 five,4 an indefinite number,5 and all,6 slip systems of the type occurring in single crystals. Pickus and Mathewson3 suggested that the cold rolling texture in face-centered cubic metals could be rationalized on the basis of two or more operating slip directions symmetrically disposed about the direction of flow in such a manner that the resolved shear stress factor is equal for all operating slip systems and lattice rotations cancel each other. The importance of the direction of flow, † the necessity for the operation of slip systems capable of producing the required, changes in external dimensions, the maintenance of a common surface between adjacent grains and a symmetrical arrangement of the operating slip systems in order to produce an end orientation which is stable under additional deformation lead to the following rationalization of textures based on the type of slip systems operative in single crystals. The rationalization is intended to explain why certain orientations are suitable for deformational flow without a change in orientation and thus are stable end orientations or ideal texture orientations. It does not attempt to explain how the grains of a randomly oriented polycrystalline aggregate will reach this orientation. The rationalization is based on the following four postulates: I. The ideal textures for polycrystalline aggregates are the result of reorientations of individual crystals toward the same stable end orientation at which no further reorientation will occur even during additional deformation. Since, in simple slip, - the relative orientations of the stress axis and the active slip system determine the change in orientation during slip, it is considered that the orientation of the stress axis with respect to the ideal texture determines what slip systems must be active to retain the stable end orientation. Therefore the stable end orientation should be a symmetrical one around the stress axis with respect to the active slip systems such that lattice rotations resulting from slip will cancel each other and prevent a resultant change in orientation. (Rotational symmetry only-not translation, inversion, nor others-is considered here.) Thus a metal under a pure stress should develop a texture consisting of one or more of the crystallographically symmetrical directions, <100>, <110> or <111> for cubic metals or <0001>, <1010> or <1120> for hexagonal dose-packed metals, parallel to the stress axis. 2. Since the active slip direction is the direction of glide during simple slip and thus the direction of maximum shear movement, in the ideal texture the active slip

Jan 1, 1948

By F. Kurata, P. C. Davis, T. L. Gore

An experimental method and apparatus for the study of the low-temperature phase and volumetric behavior of volatile mixtures are described. The phase diagrams, including the critical points, and the volumetric behavior of a natural gas and a mixture of the natural gas with methane at temperatures from -40°F to -200°F and pressures to 1.200 11si are givrn. INTRODUCTION Knowledge of the phase and volumetric behavior of mixtures of the light hydrocarbons at low temperatures is becoming increasingly important as interest in low-temperature separation processes increases. Distillation at low-lemperatures has been used for some time to recover ethane and ethylene from natural gas and refinery gas for petrochemical uses. Removal of excess nitrogen from natural gas by distillation has been proposed as a means of increasing the capacity of gas transmission lines and of improving the marketability of the gas.1,2 Evaluation of the latter process has been hampered, however, by the scarcity of data from which the phase behavior of natural gases at low temperatures might be predicted. While existing correlations of vaporization equilibrium constants may be used to predict the behavior of such mixtures at lower pressures, high-pressure computations often require knowledge of the location of the critical point of the system involved. Although correlations have been developed for the prediction of the critical temperature and pressure of certain types of hydrocar-bon systems, they do not apply to very volatile systems such as nitrogen-bear-ing natural gases. This paper describes the initial stages of an investigation of the low-temperature behavior of a numher of natural gases and other gases of commercial interest. The experimental method and apparatus are described. and the phase and volumetric behavior of a natural gas and a mixture of the natural gas with methane are presented. PREVIOUS WORK The published low-temperature vapor-liquid equilibrium data for hydrocarbons and mixtures of hydrocarbons with nitrogen and helium are listed in Table I. Most of these data are for binary systems, and the data of Stutz-man and Brown" at 100 psi are the only data on a natural gas. The data of Bloomer and Parent3 on the methafie-nitrogen system, which have been phblished since this study was completed, are a valuable addition to the knowledge in this field. Prior to the publication of these data the only published critical point data on systems having critical temperatures below the ice point were those of Ruhemann.1 on the methane-

Jan 1, 1952

By John Brown

As a part of a symposium on the relations of structure to ore deposi-tion, in February 1938, the writer presented some tentative opinions derived from his experience with a number of important lead-zinc replace-ment deposits. These ideas were set forth, as a basis for discussion and a stimulus to further inquiry, in a mimeographed leaflet that read as follows: Intimate acquaintance with a number of lead and zinc deposits in metamorphosed limestones seems to indicate the existence of certain common features from which can be established some general principles governing the localization of ore in this type of formation. It is suspected that these principles can be applied, with modifica-tions, to mineralization in unmetamorphosed limestone. In metamorphosed forma-tions, some observed rules are as follows: 1. Bands or masses of pure limestone are very resistant to replacement by ore solutions, and are likely either to contain no ore or to resist replacement until near the end of mineralization. The reason for this apparently is physical, not chemical, since microscopic data indicate that when ore is deposited by far the greater part of it substitutes for carbonate. The chief factor is believed to be a lack of porosity in massive limestone that has undergone flowage and recrystallization. 2. Masses of intensely siliceous or silicated rock are likewise unfavorable ore receptacles. This seems to be accounted for by two factors: (a) chemical unsuit-ability or resistance to replacement, and (b) physical resistance to small-scale brecci-ation, which might facilitate the opening of effective channelways for solutions. Some low-grade ore may occur, however, and also sporadic fracture fillings. 3. The optimum condition for ore reception appears to be found in bands or areas containing carbonate and silicates (or quartz) intimately mingled in something like equal proportions. In this situation movement is likely to result in mixed flowage and fracture, producing a fine-textured porosity that admits solutions freely and provides access to an abundance of replaceable carbonate. Cleavage cracks in some minerals such as diopside are believed to facilitate the penetration of solutions. 4. Certain minerals or assemblages are regarded as favorable impurities in a lime-stone and others as unfavorable. Original quartz, and subsequently developed diopside, and perhaps garnet, are typical favorable pre-ore gangue; in general rather equidimensional, brittle minerals. Tremolite, biotite, and probably wollastonite, are typical unfavorable pre-ore gangue; in general highly elongated and somewhat flexible minerals likely to develop under strong shearing stresses. 5. Tentative opinion is that the ratio of lime and magnesia in a limestone-is of little or no importance.

Jan 1, 1940

By G. H. Wilson

INTRODUCED in 1946 to serve a need in power-plant operation, closed-circuit TV has been used by well over 200 organizations in approximately 25 different industries. Known as industrial television, or simply ITV, it can be described as a private system wherein the television signal is restricted in distribution, usually by confinement within coaxial cable that directly connects the TV camera to one or several monitors, Figs. 1, 2. The picture is continuous and transmission is instantaneous, permitting an observer to see an operation that may be too distant, too inaccessible, or too dangerous to be viewed directly. Destructive testing or the machining of high explosives can now be conducted hundreds of feet away by personnel who still have close control through the eyes of the TV camera. It is also possible for one man to control operations formerly requiring the co-ordinated efforts of several workers. For example, at a large midwestern cement plant conveyance of limestone from primary crusher to raw mill and loading into five storage bins once necessitated the work of two men, one having little to do but prevent spilling of material by manually moving the tripper on the belt conveyor as occasion required. TV cameras mounted on the tripper now provide bin level indication to the conveyor operator at the crusher position so he is able to control the entire loading operation remotely, Fig. 3. By means of a switch, the picture from either camera is alternately available on a single viewer, or monitor, Fig. 4. Each camera is mounted on the tripper by means of a simple adjustable support and looks down into the bin, which is identified by the number of cross members on the vertical rod. Each associated power unit is located on a platform above the camera, Fig. 5. This centralized control by means of TV often has produced superior results, and in many instances saving in operating costs has been sufficient to write off equipment costs within six months to a year. Where a key portion of a process may be enclosed or otherwise inaccessible, TV again reduces the likelihood of mistakes and permits closer control by making available to the operator valuable information he might otherwise never possess. An example of this can be found at a strip mine where the coal seam lies 50 ft or more below the overburden, which is removed by a large wheel shovel. From his centrally located position the shove1 operator was unable to judge accurately to what extent the wheel buckets engaged the earth. His chief indication of efficiency was the amount of overburden on the belt conveyor as it passed his control point 75 ft from the wheel. Now, two television cameras mounted on the tip of the boom permit the operator to view the wheel from each side and provide him with a close-up view of the buckets so that he can take immediate and continuous advantage of their capacity, quickly compensating for ground irregularities and avoiding obstructions, Fig. 6. While the word television conjures up visions of highly complex and intricate apparatus such as that employed in modern TV studios and transmitting stations, the term industrial television should indicate compact, straightforward equipment. Most present-day ITV systems contain fewer than 25 tubes including camera and picture tubes. The average home television receiver alone requires at least that many tubes. Equipment like that illustrated in Fig. 1 contains only 17 tubes, of which 3 are in the camera. It can operate continuously and dependably, without protection, in any temperature from 0" to 150°F. It consumes less current than a toaster and weighs under 140 lb. Camera and monitor may be separated by 1500 to 2000 ft and by greater distance with additional amplification. This equipment is designed to withstand vibrations up to 21/16 in. and will operate successfully under more severe conditions of vibration and heat when suitable enclosures are provided. Any number of cameras may be switched to a single monitor, and any number of monitors, within reason, used simultaneously. Two types of applications in the mining industry have already been described. A third under serious consideration by several organizations will make use of ITV for remote observation of conveyor transfer points at copper concentrating plants so that evidence of belt breakdown and plugging of transfer chutes can be spotted immediately and costly overflow of material avoided. A television camera will soon be installed to view a trough conveyor near the exit of an iron-ore crusher to indicate clogging of the crusher as evidenced by reduction or absence of material on the

Jan 1, 1955

By G. Gutzeit

METAL-ORGANIC INNER COMPLEXES AN inner complex is a cyclic chemical structure containing an inorganic cation that is bound simultaneously to several atoms in a single organic molecule; on the one hand by means of ordinary valence bonds (electron exchange), on the other hand through the action of the electric field thus created, which satisfies the so-called secondary valences. The relative positions of the salt-forming and complex-forming groups are such that most frequently a four, five, or six-membered ring results through this double attachment of the cation.1-6 The formation of inner-complex ring systems depends not only upon the nature and suitable position of the salt-forming and complex-forming groups for ring closure, but, to a great extent, also on the nature of the metallic cation entering the reaction. This selective character of chelate-forming organic compounds is one of their most interesting and most valuable properties. As a matter of fact, the largest number of their practical applications is based upon their specificity. 4,1-13 Once a chelate compound is formed, its character is definitely "organic" in nature. In other words, its properties are conditioned to a much larger degree by the carbon chains or rings than by the metallic atom. Many inner complexes are soluble in nonpolar solvents such as benzene, paraffin oil or carbon tetrachloride, while the chelate-forming reagent before closure of the metal-organic ring is water soluble. (Example: copper complex of salicyl-aldoxime.) It is obvious that such particular properties as those indicated above can be utilized whenever specificity and practically complete binding of inorganic ions into an undissociable complex are required. One of the well-known applications of chelate-forming compounds has been the development of specific reagents in analytical chemistry,, creation of the spot-test method,4,14-16 and the application of the same principles to the contact print method for determining minerals.17 CHELATE-FORMING COMPOUNDS AS COLLECTORS In the field of flotation, where selectivity is often a quality of paramount importance for the collector, various workers have lately attempted to apply their knowledge of specific organic analytical reagents to this purpose. A. C. Vivian18 has concentrated cassiterite by using ammonium nitrosophenylhydroxylamine (Cupferron) C6H5NO(=NONH4). Holman19 has tested dimethylglyoxime for the flotation of nickel oxide minerals, while deWitt has shown in a series of systematic experiments that alpha-dioximes were generally selective collectors for nickel ores. Taurin NH2(CH2)2SO3H has been proposed for the concentration of oxidized lead ores.19 Diphenylthiocarbazone

Jan 1, 1946

By J. Gordon Parr, D. H. Polonis

High purity alloys of titanium and iron, made by a technique of levitation melting, have been investigated with particular reference to martensite formation and decomposition in the hypoeutectoid range. A preliminary study has been made of the occurrence of the phase corresponding to the structure Ti2Fe. MANY of the previous investigations of Fe-Ti alloys have been made using Kroll sponge as a source of titanium; and the subsequent heat treatments to which alloys have been subjected has, on occasion, led to further contamination. Worrier,&apos;,&apos; who suggested a part of the equilibrium diagram for the binary system, and Wallbaum and coworkers,3-5 who worked largely with iron-rich alloys, all used Kroll sponge. Van Thyne, Kessler, and Hansen,6 in their determination of the equilibrium diagram, used iodide titanium for alloys up to 30 pct Fe. Duwez,7 who measured the M. temperature of titanium binary alloys with many solute elements, used iodide titanium in all cases except in his work on Ti-Fe alloys for which he used Kroll sponge. The investigation of the supposed phase Ti2Fe by Rostoker8 nvolved the use of iodide titanium. A section of the constitutional diagram, after Van Thyne et al., is reproduced in Fig. 1. Frequently too much stress is placed on the effect of contaminants in equilibrium and nonequilibrium systems, but there is no doubt that titanium alloys are extremely susceptible to interstitial atoms. Consequently, the main purpose of the work to be described was to determine those features of phase transformations in pure Ti-Fe alloys that were considered of importance in commercial heat treatments. For, although commercial alloys may not be of high purity, the investigation of a system uncomplicated by traces of impurity is a desirable starting point. Another incidental feature, the occurrence of Ti2Fe, was also investigated. The entire study was carried out using powders obtained from alloy ingots, for diffusion reactions are often more rapid in small particles than in bulk specimens. The frequently adopted practice of ascertaining phase constitutions by X-ray analysis of powders, and relating these to the microstructures and mechanical properties of bulk specimens, is considered by the authors to be open to criticism. In the martensite reactions in the Fe-Mn system, for example, it has been shown- hat similar phase distributions in solid and powder may result in different hardness values and appearance under the microscope; and it is possible that similar anomalies might occur in the Ti-Fe system. Consequently, in order to

Jan 1, 1955

By W. C. Hagel

Previous inuestigators have repovted unusually low H* and Do values for self-dzf@szon in certazn bcc metals, e.g., chromium nnd y -uvanium. It has been postulated that this is nn experimental crl -tetion for the existpnce of a four -atom ring meclzanzsm, mid there could be. zmpovtant theoretrcal Implicatlons. By utilizing a precise sectioning technique with Cr51 as the tracer, self-dzffi-lsion measurements in large grains of 99.99-pct Cr were extended from 1200° fo 1600"C. A least- squares analysis of the data yields that D 0.280 exp (-73,20U/RT) cm2 sec-&apos;. These AH* and Do unlues are not anomalous; there is little reason to believe that n vacancy mechanism is not opevatiue. Apparent differences at lower temperatures may result from preferential diffusion along short-circuititing paths and/or sample contamination. WITH continued technological effort, chromium and chromium-base alloys should ultimately become useful high-temperature structural materials. Accurate measurements of self-diffusion coefficients in the pure metal are necessary for a quantitative understanding of sintering, grain growth, creep, and other related rate processes. However, two conflicting determinations have been reported.* Using an Since careful diffusion studies normally yield Do values ranging from 0.1 to 10 cm2 sec-l, the Paxton-Gondolf results require independent experimental corroboration before an undue amount of speculation arises to explain the apparent anomaly. As discussed by Nowick6 and clearly shown by Hoffman and Turn-bull7 for self-diffusion in silver, a low AH* and Do can arise from preferential diffusion along grain boundaries or other short-circuiting paths. The most reliable data come from high-temperature measurements where volume effects predominate. Following a precise sectioning technique developed for determining silver diffusion in the intermetallic compound AgMg8 and cation diffusion in the corundum oxide Cr2O3,9 the purpose of this study was to measure true volume diffusion in high-purity, large-grain samples at higher temperatures than considered previously. Another point of interest is the frequent proposal10-12 that chromium undergoes an allotropic transformation between 1375" and 1800°C where the diffusion data might then show a discontinuity. I EXPERIMENTAL 1) Sample Preparation. The highest purity (99.997 pet) Cr currently available is produced by reduction of chromium tri-iodide. Three pounds of the resulting crystal bar were shipped in a sealed container with a complete chemical analysis from the vendor.* In conformity with the procedure used for

Jan 1, 1962

By Leonard B. Gulbransen, John R. Lewis, W. Martin Fassell, J. Hugh Hamilton

A simple reproducible method was developed for determining the ignition temperatures of magnesium and magnesium alloys and by this method magnesium and over 100 magnesium alloys were measured. The ignition temperature of magnesium was determined in O2-SO2, O2-N2 mixtures and in O2 from 0.166 to 10 atm pressure. The ignition temperature of magnesium is generally lowered by alloying and increased by an increase in oxygen pressure. WITH the expanded use of magnesium alloys in industry, ignition temperatures are of considerable importance, especially in heat treating and for service at elevated temperatures. Magnesium alloys exhibit a relatively slow linear oxidation rate up to temperatures near the melting point.&apos; At some critical temperature the rate of oxidation becomes extremely rapid. This high rate of oxidation is accompanied by the emission of light and additional characteristics suggesting a flame. The literature concerning the ignition temperatures of magnesium and magnesium alloys is relatively incomplete and the values reported by various authors are not in agreement. The most probable reasons for this are: 1—The absence of a suitable definition of ignition, and 2—the need of a standardized method of determining the ignition temperatures of inflammable metals and alloys. The exact date of the discovery of the fact that magnesium will ignite and burn is unknown. It is likely that H. Davey encountered this property of the metal during its preparation in 1808. The first reference in the literature specifically on ignition of magnesium is by Lenze, Metz, and Rubens.&apos; They investigated the inflammability of certain magnesium alloys. Brown3-&apos; reported that magnesium ribbon will ignite in air at 507 °C by what was called the rising temperature method. Hartman, Nagy, and Brown" reported that magnesium powder ignites from 475" to 560°C depending on particle size. According to Guise, Mars, and Wilson prolonged heating in air at 427°C of common casting magnesium alloy causes it to ignite. Samples of magnesium alloys were placed directly in the flame of a torch by Carapella and Shaw.&apos; These investigators obtained some evidence of melting prior to ignition. For commercial magnesium, they reported an ignition temperature of 650°C. Their values varied from 450" to 800°C for magnesium alloys. Willmore and Peterson" studied the effect of air velocity, humidity, rate of heating, and foreign metal contact on the ignition temperature of magnesium. They conclude that melting is not a prerequisite for ignition and that the conditions which influence ignition are complex and difficult to analyze. The only quantitative theoretical treatment of the ignition temperatures of magnesium and magnesium

Jan 1, 1952

By J. F. Bryson

A FULL description of past mining conditions in eastern Kentucky coal mines with reference to the cause of coal bumps and the preventive methods was given by the writer in a previous paper.1 At that time the method had been tried for a period of 13 months, successfully. The method has been enlarged add carried on for over two years, and is still successful. Recapitulating briefly from the previous paper: The No. 3 mine of the Mary Helen Coal Corporation, Coalgood, Ky., operates in the Harlan seam, and is worked by a room-and-pillar method. Cover varies from 1200 to 2000 ft. and the immediate roof over the coal is a hard, massive, sand rock, estimated to be from 70 to 90 ft. thick. The average height of coal throughout the mine is 46 inches. The reason for adopting the method were that in this mine five men had been killed by coal bumps between 1931 and 1934; many other men had been injured and coal-cutting machines had been thrown from under the cut. The morale of the workmen was at a very low ebb. Many remedies had been tried in other mines troubled by coal bumps, one method being to leave chain and room pillars in every 500 ft., to serve a bumping block; the idea being that if a bump took place it would act on the pillars left in the gob. Another method adopted was to board up a pillar, leaving a small opening at the bottom sufficient for shoveling coal. In this system the idea was that if a bump did occur on the pillar, the boards would stop flying coal so that no one would be injured. Many other methods were tried and it is safe to say that each mine troubled by coal bumps tried various remedies, none of which proved effective. On considering all that had been attempted in an effort to eliminate coal bumps, and the information gained by experience of coal bumps in various mines, it was thought that a long face with gob support would eliminate the trouble. Accordingly, on Jan. 15, 1935, a long face was started with wood cribs on 20-ft. centers. When the former paper was written on this method, the long face had been brought back a distance

Jan 1, 1937

Discussion of the paper of HOWLAND BANCROFT, presented at the Salt Lake meeting, August, 1914, and printed in Bulletin No. 91, July, 1914, pp. 1767 to 1769. THEODORE SIMONS, Butte, Mont. (communication to the Secretary*). -While preparing maps and models for use in mining litigations the writer was frequently confronted with the problem referred to in Mr. Bancroft&apos;s paper. His chart gives the apparent angle of dip with which a vein should be plotted on a vertical section not at right angles to the strike of the vein. For a quick determination of this apparent angle the writer has used an exceedingly simple graphical method, which he believes may prove helpful to engineers engaged in practical work. It is submitted, not as a criticism of Mr. Bancroft&apos;s paper, but as a means of solving the same problem when no chart is available and when calculations would consume too much time. The writer&apos;s method requires merely a few lines marked off on a piece of tracing cloth, as shown in Fig. 1: Draw line be on any convenient scale. At b erect a perpendicular, ba. By means of a protractor cut off on ba a number of angles within the probable range of variation of dip, so that a line connecting a and c, for instance, forms an angle of 60° with be, etc. With b as a center and be as a radius, draw a circle through c. This completes the tool for solving the problem. Fig. 2 represents the line of strike of the vein and db the trace of the vertical plane on which the vein is to be plotted with the apparent angle of dip. A° is the angle which this plane makes with the strike. Fig. 3 shows the application of the method: Place line cb of tracing over line db of Fig. 2 and move fore and back until line of strike becomes tangent to the circle. Connect d with the point (a) that marks the true angle of dip as found by measurement in the mine (60° in the case illustrated). The angle adb is the apparent angle of dip (C°) to be used in the vertical section. Proof.-As stated in Mr. Bancroft&apos;s paper, the apparent angle of dip is: tan C° = sin A° tan B° (1)

Jan 12, 1914

By Carville E. Sparks, Rollin Farmin

Edward Thomas (U.S. Bureau of Mines, Washington, D. C.)—This excellent article on an ingenious and successful installation of wooden rock bolts loses much of its effectiveness through an attempt by the authors to establish the general adaptability of this type of support. Possibly because they have only local experience as a guide, they imply erroneously in the first paragraph that the Bureau of Mines has been opposed to wooden bolting, although later in the article reference is made to a Bureau publication on the subject. In 1947 the Bureau of Mines decided to sponsor experiments in roof bolting in coal mines because the experience of the St. Joseph Lead Co. had indicated that this type of roof support appeared to be a roof-fall accident-prevention measure that might be adopted and also effect economies in operating cost. Justification for this belief has been borne out, particularly in coal mining. This program has been carried out under the following general program: 1—The Roof Control Section of the Bureau of Mines has advocated and initiated underground experiments under controlled conditions with many different ideas related to rock bolting since 1947. In no instance has cooperation in developing an idea been refused, no matter how ridiculous it may have seemed at first glance, if it has been requested by a mining company. 2—The Bureau of Mines has no police powers over the selection of roof-support devices and seeks none. 3—At the request of an operator, the Bureau of Mines will make comparative tests on various types of bolts underground and will submit resultant data for the operator&apos;s consideration. 4—Wherever possible, the Bureau publicizes successful installations, so that others may benefit from this experience; however, it is careful not to discriminate between manufacturers of bolts or bolt-installation equipment. Unsuccessful experiments probably should also be publicized, but from a practical standpoint it is usually not feasible. In other words, the role of the Roof Control Section of the Bureau is in line with the original purpose for which the Bureau was first organized: to serve industry through gathering, analyzing, and disseminating factual data. It would seem to be logical that the starting point for any experimentation on roof bolts in coal mines should be the time-proved practice of the

Jan 1, 1955

By C. S. Barrett, P. Coheur

AXnealing twins are common in the microstructure of copper that has been rolled and recrystallized. In such samples it follows that a twin relationship should exist between components of the re-crystallization texture,&apos; and several examples of this have been reported. For example, twin relationships have been found in recrystallized electrolytic copper sheet, as indicated in Fig. I, from a paper by Coheur and Lejeune.2 In this pole figure the cube texture (100) [001] is indicated by the hollow squares in the lower half of the figure (the pole figure for 200 reflections) and in the upper, (III), part of the figure. The texture contains, in addition to this orientation, the first-order twins of it, shown in the figure by the filled triangles. This orientation relation has been suggested by others also, under certain annealing conditions,3&apos;4 although pole figures have not been published to confirm it. Some orientations in recrystallized sheets are identical with their twins, because of the symmetry elements of the texture— this is true, for example, with the (113) [ZII] texture so commonly reported for brass—hence it appears impossible in such samples to decide whether the twin relationships result from twinning or merely from the symmetry of the deformation process. The present investigation of a commercial copper strip seems to yield an example in which annealing twins account unambiguously for the principal orientations present. It proves to be a case, also, for which the recrystallization texture cannot be viewed as derived from the deformation texture by a first or second-order twinning mechanism. Materials and Methods The samples investigated were of secondary copper (melted in belgium) to which 0.19 per cent iron had been added to raise the recrystallization temperature. How much the orientation characteristics of this metal can be ascribed to the iron content and how much to other impurities or to melting and pouring practice have not been investigated.* The rolling was done in one direction only, on a mill with rolls of about 20-cm diameter. A strip I. cm wide was reduced from 5 mm thickness to 0.05 mm by several cold passes at commercial speeds. The samples cut from this 99 per cent reduced strip were X-rayed throughout their entire thickness. A pole figure made soon after rolling and annealing was identical, within experimental error, with one that was made when a two-year interval occurred between rolling and annealing. X-ray patterns were made on a camera2 that traversed

Jan 1, 1947