By W. A. Tiller, W. C. Johnston

A high-temperature electromagnetic stirrer is described in which heating and stirring are accomplished by independently controlled power sources. The appavatus is suitable lor use at temperatures up to 1700°C in a variety of ambient atmospheres. Some typical examples of the homogenizatimz capabilities of the system are given. THERE are few processes in solidification that are not markedly affected by motion in the melt during freezing. In many instances, the mechanisms are diffusion-controlled, and the transport in the melt may be greatly accelerated by deliberately stirring the melt. In zone-refining, stirring1 assists the removal of rejected impurities from the interface, so the process proceeds at a faster rate. The transition from a planar to a cellular interface is caused by constitutional undercooling in the melt ahead of the interface: and stirring delays its onset. Stirring is valuable for homogenization of melts: and chemical reaction with sluggish kinetics may be accelerated. Finally, it has been observed that grain refinement is related to motion in the melt. Fine grain castings are usually produced by the addition of catalysts to the -melt,' catalysts which are thought to act simply as hetereogeneous nucleation centers. Even here motion is important. Richards and Rostoker 5 applied ultrasonic vibration to a solidifying A1-Cu alloy which had been innoculated with a catalyst and found that the grain diameter fell linearly with the amplitude, the peak acceleration and the power input to the melt from the transducer. Finally, mechanical and electrical stirring alone have been used to generate a fine-grained structure.6,7 Johnston ef a1.' have carried out a series of systematic investigations of grain refinement by electromagnetic stirring in a number of low melting point alloys. They found, for example, that the number of grains per unit volume in Pb-Sn alloys could be increased several orders of magnitude by stirring an undercooled melt at the moment of recalescence. In general, a relation AT .H = constant prevailed for a given grain size, where AT was the undercooling of the melt and H the field strength. In more recent work, deliberate homogeneous nucleation of slightly undercooled melts established that the mechanism of refinement must be one involving crystal fragmentation and subsequent multiplication, rather than a "shower" of nuclei effect.9 It is the purpose of this note to describe a stirring device suitable for use up to 1700°C. At low temperatures mechanical stirring and direct-current methods are feasible, but at high temperatures the problem of a protective atmosphere and of electrode corrosion rules out such procedures. The most convenient method for high temperatures is to use externally generated ac fields for both stirring and heating. With rf induction heating alone, considerable stirring and agitation can be achieved, but in general the penetration of field into the melt is small, and the stirring cannot be controlled independently of the heating. In the present experiments, separate power sources of different frequencies for heating and for stirring were used. A susceptor design was chosen so that the 450 kc rf heating field was completely absorbed in the susceptor. The stirring frequency, 400 cps, hereafter called the af field, was chosen so that a high penetration of the melt proper was achieved. EXPERIMENTAL APPARATUS The apparatus, Fig. 1, consists of a quartz tube and end plates, surrounded by an rf induction coil and six equally spaced af stirring coils, four of which are shown in full and a fifth in section. Each af stirring coil is a transformer of which the secondary is a single-turn water-cooled copper loop and the primary is composed of two 10 amp-117 v Variac cores as shown. These cores are cooled by forced air, as each of the six pairs will carry maximum currents of 15 amp for short periods. Each set of Variac windings are connected in series, but opposite sets are connected in parallel with a three-phase 400 cps 400-v source. By properly phasing the coils in this way, a rotating field is produced. Capacitors C1, C2, and C3 in Fig. 2 are used to match this inductive load to the generator. Fig. 3 shows a cutaway view of the quartz tube. The sample (1 in. diam by 1 in. high) is placed in a tapered alumina crucible. An axial W-26 pct Re thermocouple, enclosed by a protection tube, is provided. The cruci-

Jan 1, 1968

By J. L. Tokich, A. R. Troiano

Since 1921, when Hull1 discovered that cobalt can exist in the face-centered cubic and hexagonal close-packed modifications, the transitions that occur in cobalt have been extensively studied. It is generally agreed that on heating the hexagonal lattice changes to the cubic structure at ternperatures ranging from 400° to 500°C although considerable doubt exists as to the exact temperature. Data concerning the temperature of the transformation on cooling are much less concordant and their interpretation has not been satisfactory. The study is further complicated by the fact that many investigators have reported the existence of a high temperature allo-tropic change in the range 850 to 1020°C, at which the cubic lattice reverts to the hexagonal modification. The transition on cooling, which has been reported as Occurring at various temperatures from approximately 400 to 100°C, is of particular interest. Troiano and Greninger2 have recently suggested and considered the possibility Of allotropic transformations occurring in pure metals by a shear-type, diffusionless (martensite) transformation. The case of cobalt was specifically discussed and certain observations of previous investigators evaluated in terms Of this type of Of Table 1 briefly outlines the methods and results Of previous investigators Of the transformation temperatures of cobalt. Materials and Methods The major portion of this investigatioll was performed with cobalt sheet containing a total of 0.2 pet impurities with carbon present to the extent of o,I pct. After melting in an induction furnace under an atmosphere of hydrogen, the carbon con. tent analyzed 0.03 pct. Some observations were repeated with hydrogen reduced cobalt compresses analyzing 99.9 pet pure. No significant variations in results were observed employing the as-received sheet, the remelted stock, or the cobalt compresses. Filings for X ray diffraction analysis were sealed in evacuated glass ampoules. Pyrex glass tubing was used for temperatures below (600°C and for higher temperatures clear fused quartz was satisfactory. After appropriate heat treatment at various ternperatures, the specimen ampoules were furnace cooled, air cooled or quenched by crushing under distilled water. This allowed a range of cooling velocities from less than one degree C per set to greater than 1,0oo°C per sec. X ray diffraction patterns were taken with a Debye camera and filtered characteristic cobalt K-alpha radiation. The of of the existing phases was roughly approximated by visual examina-

Jan 1, 1949

By Walter E. Hopper

The Caddo oil-field, shown in Fig. 1, is located in Caddo parish, northwestern Louisiana. The known producing territory of oil is covered by townships 19 N, 20 N, 21 N, 22 N, and ranges 15 and 16 W., shown in Fig. 2. The center of the field may be taken as Oil City, 24 miles north of Shreveport, on the Kansas City Southern railway. Shreveport is the second largest city in the State, and is the connecting point of five railroad-lines. Drilling at the present time, however, is going on all over northern Louisiana, especially in Caddo and the neighboring parishes. During the winter of 1908-09 I spent 'four months in the Caddo field, under the direction of the Louisiana Geological Survey and the U. S. Geological Survey. II. History and Development. Natural gas escaping at the surface is found at numerous places in northwestern Louisiana. At Shreveport, the plant of the Shreveport Ice & Refrigerating Co. has been lighted by natural gas for 20 years. The well was drilled for water, but was abandoned on account of the gas. A test well, put down in 1905 near the western limits of Shreveport, was driven to 1,650 ft., and encountered indications of gas and oil at various depths, but did not succeed in finding enough to be profitable. Attention was first attracted to the Caddo field in 1895 by indications in water-wells from 40 to 60 ft. deep, in which the pressure of natural gas was noticeable. This indication of gas in a shallow well led to the drilling of the first well in the Caddo field, the old Savage Brothers & Morricell, or the Caddo Lake Oil and Pipe Line No. 1. The rig for this well was erected in May, 1904, and drilling began in June, 1904. The well was bailed Mar. 23, 1905, with a small amount of oil. It was deepened July, 1905, and converted into a "gasser" Jan. 3, 1906. It was abandoned January, 1907. In consequence of the finding of oil in the Savage well, drilling-operations were pushed with energy; and in April, 1905,

Jan 1, 1912

CONTENTS PAGE Need for Research in Foundry Pig Iron. By Richard Moldenke. (With Discussion) 1 Carbon Characteristics of Copper-bearing Pig Iron. By W. B. Coleman. (With Discussion) 12 A Pig Iron, Low in Total Carbon, is in Demand for Use in Various Industries. By Enrique Touceda. (With Discussion) 24 Carbon in Pig Iron. By Ralph H. Sweetser. (With Discussion) 28 Second Session (Discussion) 37 Need for Research in Foundry Pig Iron BY RICHARD MOLDENKE,* WATCHUNG, N. J. So FAR as the quality of the product is concerned, the history of the production of pig iron for foundry purposes is one of constant retrogression. The steps in this deterioration began with cold-blast charcoal pig iron, then anthracite iron, coke iron; then gradually warm to hot-blast coke iron, with the charcoal furnaces also heating their blast to get greater tonnages, and finally the present-day hot-blast coke irons with scrap additions to the ordinary burden that, according to one European report, have gone as high as 65 per cent. Parallel with this quality retrogression is the enormous increase in furnace tonnages from about 15 to over 1000 tons per day in exceptional instances of modern practice. The key to this situation is economic pressure. The effect is a growing differentiation between furnace production for gray iron and malleable foundries and, for the

Jan 1, 1927

By James M. Barker

Sulfur is a nonmetallic element of great physical and economic importance to the world. It is widely but sparingly distributed throughout the hydrosphere, lithosphere, and biosphere. Sulfur is the tenth most abundant element in the universe and eighth most abundant in the sun. In the earth's crust, which is mainly igneous, it ranks 14th, but is eighth or ninth in sediments (Kaplan, 1972; Stanton, 1972). It apparently is very abundant in the core of the earth, because it is a strong chalcophile, and it is fifth in abundance in stony and iron meteorites (Field, 1972) where it occurs as trolite (FeS). In ancient times sulfur was called brimstone, literally "burning stone." Today the term brimstone is used interchangeably with the term elemental sulfur. Shelton (1979) summarized most of the common definitions of terms, grades, and specifications for the sulfur industry as follows (with minor additions): Sources of Sulfur: Combined sulfur-Sulfur that occurs in nature combined with other elements. Cupriferous pyrites-Pyrite containing relatively minor amounts of copper sulfide minerals. Hydrogen sulfide-A toxic gas (H2S) occurring in natural gas and petroleum. Involuntary sulfur-Sulfur produced primarily as a result of legislative or process mandates. Native sulfur-Sulfur that occurs in nature in the elemental (uncombined) form. Nonferrous metal sulfides-Copper, lead, zinc, nickel, and molybdenum sulfides that are processed for their metal content. Organic sulfurs-Complex organic sulfur compounds occurring in petroleum, coal, oil shale, and tar sands. Pyrites-Iron sulfide minerals that include pyrite, marcasite, and pyrrhotite. Sulfate sulfurs-Sulfur in anhydrite and gypsum. Voluntary sulfur-Sulfur produced in response to market forces. Basic Sulfur Products Produced and Marketed: Acid sludge-Contaminated sulfuric acid usually returned to acid plants for reconstitution. Brimstone-Synonymous with crude sulfur. Bright sulfur-Crude sulfur free of discoloring impurities and bright yellow in color. Broken sulfur-Solid crude sulfur crushed to -8 in. Byproduct sulfuric acid--Sulfuric acid produced as a byproduct of a metallurgical or industrial process, generally relating to combined sulfur sources. Crude sulfur-Commercial nomenclature for elemental sulfur. Dark sulfur-Crude sulfur discolored by minor quantities of hydrocarbons ranging up to 0.3 % carbon content. Elemental sulfur-Processed sulfur in the elemental form produced from native sulfur or combined sulfur sources, generally with a minimum sulfur content of 99.5%. Formed sulfur-Elemental sulfur cast or pressed into particular shapes to enhance handling and to suppress dust generation and moisture retention. Frasch sulfur-Elemental sulfur produced from native sulfur sources by the Frasch mining process. Hydrogen sulfide-Associated with natural gas or petroleum and produced at refineries and coke oven plants; used to make sulfuric acid or recovered sulfur. Liquid sulfur-Synonymous with molten sulfur. Liquid sulfur dioxide-Purified sulfur dioxide compressed to the liquid phase. Molten sulfur-Crude sulfur in the molten phase.

Jan 1, 1983

By J. Gordon Parr, D. H. Polonis

The formation and subsequent decomposition of metastable phases in Ti-Ni alloys containing up to 11 pet (atomic) Ni have been studied. The decomposition of a completely retained ß phase and of a completely transformed 8 phase in a 6 pet alloy has been followed by X-ray diffraction and metallographic methods and by hardness determinations made during the process. The possible mechanisms of the reactions are discussed. PREVIOUS investigations of the Ti-Ni system have usually been limited to phase diagram studies; but little attention has been given to metastable phases and tempering processes. These are important, however, since equilibrium conditions are rarely achieved—nor, perhaps, are they desired—in practice. Up to the present time the available transformation data for titanium alloys appear to be restricted to isothermal transformation curves for selected binary and ternary systems. No quantitative studies have been made of the mechanism by which equilibrium is approached. Several independent investigations have been carried out to determine the Ti-Ni phase diagram. Early work by Wallbaum' and later by Long et al.' produced tentative phase diagrams which were not representative of true binary conditions, since the alloys were contaminated with oxygen and nitrogen. The most recent diagram (Fig. 1) is due to Margolin et al.," and a slight modification of the a + ß/ß boundary (shown dotted) has been proposed by McQuillan.' The structure of the phase Ti,Ni was shown by Duwez and Taylor" to be face-centered-cubic, with 96 atoms per structure cell. The formation of a martensitic ß phase (close-packed-hexagonal) in Ti-Ni alloys has generally been observed when specimens of low nickel content are rapidly cooled from the 0 (body-centered-cubic) range. Margolin et al. reported an increasing tendency for P to be retained in lump specimens as the nickel content increases. McQuillan' has studied the effect on the microstructure of delay time in quenching, and has reported the formation of pro- eutectoid a precipitate in a quenched hypoeutectoid alloy. In a previous study of Ti-Fe alloys," experiments were made on powder specimens produced by filing alloy ingots. Techniques were devised for the preparation and heat treatment of alloys, and X-ray diffraction methods were used both for structure determinations and phase ratio estimations. A similar approach has been made in this study of Ti-Ni alloys. Experimental Methods Ten alloys ranging from 0.25 pet to 18 pet Ni* * All compositions are in atomic percentages unless otherwise stated. were prepared from iodide titanium bar stock (hardness Rf 72) and Johnson-Matthey spectrographic standard nickel by levitation melting.' As a check

Jan 1, 1957

By Danforth R. Hale

Minerals for electronic and optical uses divide easily into two sections: (1) quartz and (2) minerals other than quartz. Quartz Quartz, having a great usefulness discovered by the radio communication enthusiasts about 1918, has become a subject of amazingly expanded interest in the U.S. over the past decade as a man-made mineral and a $3 million crystal-growing business. An economic summary of the commercial growing of quartz crystals has a place in a handbook directed to the mineral engineering industry when it is remembered that quartz crystals have long been an important commercial mineral, and that the raw material for “cultured quartz”- that is to say, quartz crystals grown through the ingenuity of man-is still natural quartz. Nearly all the natural crystals come from Brazil. The larger pieces which meet rigorous standards of quality are used for electronic and, to a lesser extent, optical components. Smaller pieces and fragments are used for vitreous silica. The need for high quality material in quantity led to U.S. government-sponsored research programs in the 1940s that have resulted in the factory growing of beautiful crystals of prescribed shape, size, and quality. The development of the cultured quartz crystal is typical of man's success in adapting the product of the mine to increasingly sophisticated uses. A remarkable achievement perhaps, but foreshadowed by experiments in 1908 by Giorgio Spezia (1908), an Italian geologist studying the relative effects of temperature and alkaline environment on the solubility of quartz. Modern radio equipment is most often controlled as to frequency by the presence in the circuit of a separately added "crystal"-the 1918 discovery responsible for the existence and growth of the quartz industry. The "crystal" is quartz, but this component is a carefully oriented and prepared slice from a crystal, but not a crystal as recognized by a rock hound or seen in a museum. How quartz operates to control frequencies is not a proper subject for a handbook on industrial minerals, and references should be consulted (Cady, 1964; Mason, 1964). Quartz belongs to that class of materials called dielectrics: those that do not conduct an electric current but permit electric fields to exist and act across them. Quartz shows the "piezo-electric effect," which means that when a quartz plate is mechanically deformed against its natural stiffness, one of its surfaces becomes negatively charged, the other, positively charged. When the plate is released from the stress quickly, the charges disappear as the plate regains its original shape, but because of mechanical momentum the plate deforms in the opposite direction (to a lesser amount) and the surfaces correspondingly become charged in the opposite direction. By coating the two surfaces thinly with metal and attaching flexible wires, these charges may be brought into an electronic circuit. If the surfaces are suddenly electrically charged by movement of current through the wires, the "converse piezoelectric effect" occurs -the plate deforms. Carry the thought further and it is realized that an alternating current flowing through the wires responds to the mechanical oscillation of the plate and is keyed to this oscillation. By controlling the thickness of the plate its mechanical vibration frequency can bevaried through a wide range. One type of quartz plate, called the AT-cut, having a precisely defined orientation with respect to the crystallographic axes of the crystal, vibrates on a microscopic scale much as a book would deform when placed flat on a table and the top cover moved parallel back and forth with the hand. There are at least 17 other orientations which have been studied, some of

Jan 1, 1975

By Douglas J. Harvey

The surface tension of lead-tellurium alloys (in the range 0 to 6.70 at. pct Te) ad lead-arsenic alloys (in the range 0 to 10.53 at. pct As) has been examined by the maximum bubble pressure method. The surface tension of high purity lead can be expressed over a range of temperatures (M.P. to 750°C) by the relationship = 512 — 0.133t. Arsenic and lellurium were both found to be surface active in lead. The surface excess concentration at 700°C was .found to be constant at 0.74 x 10-10 moles per sq cm for tellurium. The surface excess of arsenic at 700°C varied between 0.26 x 10-10 moles per sq cm at 0.16 at. pct to 1.5 x 10-10 moles per sq cm at 8.3 at. pet. The surface tension of lead has been investigated sporadically over the last 90 years. The first recorded study was made by Quincke1 who used a rather crude application of the drop-weight method. Hogness2 obtained the first reliable value for the surface tension of lead by measuring the pressure necessary to force the liquid metal from the end of a small capillary of known radius. Hogness gives the empirical formula: ?(surface tension)= 444 - 0.077 (l-327) which describes the relationship between surface tension and temperature ("C); This work was followed by that of Bircumshaw3 who applied the two-capillar maximum bubble pressure method of Sugden.4 The values published by Bircumshaw are in good agreement with those found by Hogness. Matuyama5 examined the surface tension of lead by the drop weight method. However, the values found are somewhat higher than those previously reported. More recent investigations by Greenaway6 and by Melford and oar' have resulted in data which are not in close agreement, but which are well within the expected range at most temperature levels. The study of the surface tension of lead alloys began with Drath and sauerwald8 who examined the lead-bismuth system. They found that the surface tension values of the alloys in this system deviated only slightly from the ideal mixture rule. Matuyarna5 examined the lead-antimony system. Bircumshaw the lead-tin, and the lead-indium system was studied by Hoar and Me1ford.10 The results of these investi- gations are summarized in Fig. 1. It may be seen that the data vary only slightly from the ideal mixture rule. As none of the metals studied and reported in the literature has a very interesting effect on the surface tension of lead,*the next logical step might be to examine the effect of metals of low solubility or nonmetals having some liquid solubility. Baes, and Kellogg11 have pointed out that the elements most likely to be surface active in liquid metals are ones of limited solubility in the liquid state and possessing weak intermolecular bonding forces in the solid state. Therefore, Group V, VI and VII nonmetals are most likely to be surface active. It was decided to examine the effect of a borderline metal, arsenic, and a nonmetal tellurium. Arsenic forms a eutectic with lead having a melting point of 290°C and a composition of 6.9 at. pct As.13 Pure arsenic sublimes when heated above 610°C. Even though alloying with lead lowers the vapor pressure, fumes containing arsenic are evolved at a very noticeable rate when lead-arsenic alloys are heated above 650°C. Tellurium raises the liquidus temperature of lead sharply to 904°C,14 the melting point of PbTe (lead-telluride). The solid solubility of tellurium in lead was determined by Greenwood and worner15 to be 0.0007 at. pct at room temperature. EXPERIMENTAL METHOD Surface Tension Measurement—The two capillary maximum bubble pressure method for measuring surface tension developed by Sugden,4 and used later

Jan 1, 1962

THE decades immediately before and after the end of the nineteenth century (1890-1910) were a period of increased activity in mineral industry education. One reason for this, undoubtedly, was the rapid increase in mineral production in the decade 1880-1890; pig iron and copper production tripled; coal, lead, and zinc output more than doubled. Most of the other mineral substances followed the same general trend. Aluminum production began in 1886; petroleum output, which in 1888 was less than it was in 1882, almost doubled in the next three years. Gold alone showed no appreciable change until its discovery at Cripple Creek in 1891, followed by the Klondike in 1896, brought to boiling a public interest in minerals that had been simmering for some years previously. The first cyanide plant in the United States was erected at Bodie in 1892, and the first chlorination plant at Cripple Creek* the next year. Silver- lead smelting had already greatly developed, and the metallurgy of copper was almost transformed. The hearth area and smelting capacity of copper reverberatory furnaces more than quadrupled between 1878 and 1894; matte converters were first erected at Butte in 1884. Copper production of the United States in 1899 was 20 times that of 1872. While it was the increased technology used in mineral production that really made the field attractive for educated young men, undoubtedly they did not realize that, and were impressed mainly by the quantitative increase in output. Another factor was the increased general interest in engineering education; three times as many men took engineering degrees in the United States in 1890 as in 1880; 1892 showed almost a 56 per cent increase over 1890. Industry had come to recognize that technical training was worth while. The mineral industry lagged somewhat at first; the total number of mining degrees

Jan 1, 1941

By Robert B Sosman

The relative temperature distribution within a coke oven and among the ovens in a battery can be obtained automatically for the operator's guidance by sighting a total-radiation pyrometer on the face of the coke as it is pushed out, and recording the surface temperature. Keeping the instrument clean and keeping its view of the coke unobstructed by smoke and dust are the principal problems. Typical records from three plants are presented in this paper, showing that the temperature patterns are reproducible. Development OF Method The method of coke pyrometry described in this paper was introduced in 1936 by E. A. Lee, then Assistant Superintendent, now Superintendent, of the Coke Plant at Lorain Works, National Tube Co., Lorain, Ohio. At the request of the Coke Committee of the United States Steel Corporation, the Research Laboratory of the Corporation undertook to adapt the method to the somewhat different conditions met with at the Gary Works of the Carnegie-Illinois Steel Corporation, Gary, Ind., and at the Clairton Works of the same Corporation at Clairton, Pa. This work was done in cooperation with the Leeds and Northrup Co. of Philadelphia and later with the Brown Instrument Co. Division of Minneapolis-Honeywell Regulator Co., Philadelphia. We of the Research Laboratory wish to express our appreci- ation of the courtesies extended by Mr. Lee, by A. N. Cole, Superintendent of the Gary coke plant, and by D. P. Finney, Assistant General Superintendent in charge of coke-plant operations at Clairton. We are also indebted to the instrument companies for the loan of a part of the equipment. At Gary and Clairton the instruments were installed and various experiments were made by J. W. Bain, of the Research Laboratory of the United States Steel Corporation. Pyrometry of Coke The coke inside a by-product oven is almost completely inaccessible to pyro-metric instruments. The temperature in the walls can conceivably be measured with thermocouples, but the atmosphere is usually strongly reducing, a condition well known to be destructive to the accuracy of the customary high-temperature couples. In some plants, periodic readings are taken with an optical pyrometer sighted into the top of the combustion flues. This is a useful measure for safety and general control, as it tends to prevent the damage that would result from overheating of the ovens. It does not, however, tell much about the temperature of the coke itself, because of the continually changing gradient in the wall between the coke and the combustion chamber. The best indication of the temperature of the coke itself must therefore be obtained by observation of the product as it is pushed out of the oven. The human eye is very sensitive to variations in brightness of a surface, and particularly to differences in brightness over a continuous hot surface.

Jan 1, 1943

By Robert B. Sosman

The relative temperature distribution within a coke oven and among the ovens in a battery can be obtained automatically for the operator's guidance by sighting a total-radiation pyrometer on the face of the coke as it is pushed out, and recording the surface temperature. Keeping the instrument clean and keeping its view of the coke unobstructed by smoke and dust are the principal problems. Typical records from three plants are presented in this paper, showing that the temperature patterns are reproducible. Development OF Method The method of coke pyrometry described in this paper was introduced in 1936 by E. A. Lee, then Assistant Superintendent, now Superintendent, of the Coke Plant at Lorain Works, National Tube Co., Lorain, Ohio. At the request of the Coke Committee of the United States Steel Corporation, the Research Laboratory of the Corporation undertook to adapt the method to the somewhat different conditions met with at the Gary Works of the Carnegie-Illinois Steel Corporation, Gary, Ind., and at the Clairton Works of the same Corporation at Clairton, Pa. This work was done in cooperation with the Leeds and Northrup Co. of Philadelphia and later with the Brown Instrument Co. Division of Minneapolis-Honeywell Regulator Co., Philadelphia. We of the Research Laboratory wish to express our appreci- ation of the courtesies extended by Mr. Lee, by A. N. Cole, Superintendent of the Gary coke plant, and by D. P. Finney, Assistant General Superintendent in charge of coke-plant operations at Clairton. We are also indebted to the instrument companies for the loan of a part of the equipment. At Gary and Clairton the instruments were installed and various experiments were made by J. W. Bain, of the Research Laboratory of the United States Steel Corporation. Pyrometry of Coke The coke inside a by-product oven is almost completely inaccessible to pyro-metric instruments. The temperature in the walls can conceivably be measured with thermocouples, but the atmosphere is usually strongly reducing, a condition well known to be destructive to the accuracy of the customary high-temperature couples. In some plants, periodic readings are taken with an optical pyrometer sighted into the top of the combustion flues. This is a useful measure for safety and general control, as it tends to prevent the damage that would result from overheating of the ovens. It does not, however, tell much about the temperature of the coke itself, because of the continually changing gradient in the wall between the coke and the combustion chamber. The best indication of the temperature of the coke itself must therefore be obtained by observation of the product as it is pushed out of the oven. The human eye is very sensitive to variations in brightness of a surface, and particularly to differences in brightness over a continuous hot surface.

Jan 1, 1943

By J. C. Trantham, J. W. Marx

From 1955 to 1958 the Phillips Petroleum Co. conducted a series of small scale counterflow combustion field tests in a tar sand about 60-ft deep and 6 to 12-ft thick near Bellamy, Mo. A total of seven different well patterns, including conventional five-spots and seven-spots plus a 15-well line drive pattern and a 10-well radial pattern, were employed. Electric heaters, gas burners and wellbore fuel packs were tested as counterflow ignition devices. Direct drive ignition followed by reversal to counterflow operation was not possible in this case because of formation plugging by the semi-solid tar during the direct drive phase. Sustained counterflow burning was achieved with wellbore fuel packs under conirolled conditions which permitted close correlation of fire front velocity, air velocity, air-oil ratios and yields for a wide variation in process parameters. The tar in place was about 10' APl with a reservoir viscosity greater than 500,000 cp. The composite oil prodlcct was 26' API with a viscosity in the range of 5 to 15 cp. Vertical sweep efficiency in the line drive pattern was essentially 100 per cent, with no evidence of gravity segregation. Original tar in place ranged between 800 and 1,000 bbllacre-ft, specific rock permeability averaged about 800 md before burning and effective air pemeability with residual oil and water in place (at the time of ignition) averaged 250 md. The volume of oil recovered during stabilized line drive counterflow burning represented about 67 per cent of the volume of tar originally in place in the burned out zones. A minimum was found when air-oil ratios were plotted against formation air velocities, and a limiting air velocity existed below which the counterflow fire front reversed and burned back over its own trajectory, using the residual coke left behind. INTRODUCTION Early in 1955 the Phillips Petroleum Co. began preparations to field test counterflow underground combustion as a method for producing oil from high viscosity hydrocarbon deposits, such as bituminous (tar) sands. At that time all published information on the use of underground burning io increase oil recovery was based on the direct drive process, in which the fire front moved through the formatim in the same direction as the injected air stream. Such direct burning is not applicable to many heavy oil sands or to most tar sands because the heat-thinned native hydrocarbon congeals in the cold rock ahead of the fire front forming a gas permeability block which smothers the combustion. Laboratory experiments first demonstrated that this permeability blocking would not occur if the fire front and the air stream moved in opposite directions. In this counterflow (reverse) burning process the heated heavy oil or tar is driven back through the combustion zone. Here thermal cracking produces relatively light hydrocarbon products which pass through the heated rock behind the fire front (largely in the vapor phase) and are incapable of causing a gas permeability block.' Exploratory wring revealed that consolidated bituminous sandstones with a combination of tar saturation, permeability, thickness and depth favorable for experimental field testing existed at several points in western Missouri. By the fall of 1955, a test site for determining technical feasibility of the counterflow process under field conditions had been selected near Bellamy, Vernon County, Mo. — about fifty miles north of Joplin. The pay zone was too thin and too shallow to constitute a commercial prospect, but these same factors permitted controlled experimental operation with a small compressor installation and with a large number of monitor wells. These were needed for adequate observation of the underground phenomena at reasonable cost. RESERVOIR CHARACTERISTICS The reservoir chosen for the experimental field tests was a 124 thick section of tar sand extending from 49 to 61 ft subsurface, with shale and siltstone laminations sealing the top and bottom. This section was part of a larger 30-ft thick tar sand deposit which extended both above and below the test zone. Core analyses showed that the 12-ft sand was effectively subdivided into two approximately equal sections, with the lower zone being consistently more permeable than the upper zone. The most significant laboratory core data are summarized in Table 1. The line drive test which is the principal subject of this report utilized only the lower 6-ft thick zone, with the upper zone regarded as part of the 55-ft overburden. WELL PATTERNS The over-all field test program involved a total of seven different well patterns, including conventional five-spots and seven-spots plus a 15-well line drive pattern and a 10-well radial pattern. In some of the tests the full 12-ft zone was employed; in other cases only the more perme-

Jan 1, 1967

By G. G. Marino, J. W. Mahar

This paper provides an understanding of the behavior and potential damage of homes resulting from sag-type mine subsidence. This is done with extensive research of numerous case histories in Illinois collected by the authors. The house response to subsidence-induced ground displacements are summarized and evaluated. A damage level criteria, specifically developed for residential structures, is presented based primarily on repair costs. Damage levels and the associated subsidence profile characteristics for each case history are compared.

Jan 1, 1986

By Charles W. Goodale, William A. Akers

The treatment of silver-ores of too low a grade to justify either smelting or preliminary roasting, and yet not " free" enough to permit of raw amalgamation, has ever been a serious problem. As bearing upon it, the operations of the Combination Mining and Milling Company of Black Pine, Deer Lodge county, Montana, during the past year may not be without interest. It is not claimed that the process to be described is not susceptible of great improvement, nor is any claim of originality made for it; but its use is, as yet, not very general, and it seems to offer a means of profitably working the large class of partially-decomposed argentiferous ores which, by reason

Jan 1, 1890

By C. A. Hansen

The furnace used for experimental work is shown in Fig. 1. One fireclay sagger, or pot, was set within another and the space between the two filled with Silox heat insulation. The hearth is a cast-iron plate with an imbedded ribbon of nichrome wire; this wire heater is connected to a potential regulator, which permits a very close voltage control. A mechanically driven arm is fitted with rabble blades so arranged that a uniformly thick ore bed may be maintained indefinitely. This arm is usually driven at about one revolution per minute but its speed of rotation can be varied as desired. Compressed air is led into the furnace through a meter, and it was found necessary to preheat the air in order to secure the definitely isothermal conditions sought. With this arrangement, it is possible to maintain any desired temperature constant within about 5" C. for any desired length of time and to

Jan 1, 1921

By J. H. McCormick

This plant, near Marysville, Mont., was planned to treat the ore from the Piegan and Gloster mines, the latter being one of the early and famous producers of the Marysville district. When the mill was closed in 1888, treatment consisted of stamp milling, followed by pans and settlers for pan amalgamation. The extraction was evidently poor, because, a few years later, thousands of tons of tailings were re-treated by the ranchers in the valley below the mill, by the then new cyanide process, and gave a handsome profit. In 1914, the present owners, after laboratory tests and an experimental mill run, decided upon the following treatment: crushing to 40 mesh in cyanide solution, concentration, amalgamation, classification, and cyani-dation of sands by leaching, and of slime by agitation and decantation in charges. The ore averaged about $7 per ton, gold and silver, the ratio of weight being 1 oz. gold to 7.56 oz. silver. The ratio of gold and silver in tailings was 1 oz. Au to 36.6 oz. Ag; the quartz was sharp and sandy, however finely ground, and rather difficult to slime. The mechanical equipment was a No. 5 Symons gyratory crusher; three 10-ft. Lane slow-speed Chilean mills; one Wilfley roughing and one finishing table; one submerged-type Akins classifier; five 26 by 10-ft. fir leaching tanks; one 24 by 7-ft. Dorr thickener; four 14 by 16-ft. Dorr agitators; four 6-compartment double-row zinc-boxes having compartments 18 in. wide, 18 in. deep, and 34 in. long; Johnson zinc lathe; acid and vacuum filter tanks for treating precipitate; roasting furnace; and Case tilting No. 275 crucible furnace for melting precipitate. The mill is driven by electric power supplied by the Montana Power Co. at the following rates, per kw.-hr.: 200 to 300 hp., 0.68 c.; 300 to 500 hp., 0.61 c.; 500 to 750 hp., 0.55 c.; plus $1 per month per installed motor horsepower. The plant as above described was operated from May, 1915, to the end of the year, when an additional Dorr thickener and a 12 by 12-ft. Portland revolving filter were added, increasing the nominal capacity of 100 tons per 24 hr., but not the percentage of extraction. The combined treatment, at a cost of $1.48 per ton, saved 90 per cent. of the gold arid

Jan 1, 1919

By Alan Morris

Brass rod for use in automatic screw machines is one of the major products of the brass mills. A large tonnage is consumed each year in the manufacture of an endless variety of finished articles and parts for assembly into other products. The machines that do this work have been developed to a high degree of efficiency, and their manufacturers are still striving for higher production speeds. This development has brought with it a demand for brass rod to meet the increasingly difficult machining conditions. This paper is a report of the results of tests undertaken in an effort to obtain a measure of the effects of such variables as lead content, microstructure and cold work on the machinability of brass rod. It is realized that the term "machinability" has never been well defined. Power, finish and tool life all should have a place in such a definition. In practice it is sometimes found necessary to sacrifice some of these in order to obtain a rod that will not tend to throw up a burr, or will give a burr which is easily tumbled off. Again a specially stiff rod may be necessary because of long overhang from the chuck or a rod of special characteristics is needed to take a given broaching operation without chattering. It is only through an understanding of the effect of basic mill operations on the machinability of the rod that such problems as these may be solved most economically. It is hoped that this paper, together with the discussion it may evoke, will prove to be a basis for such an understanding. Testing Apparatus The testing apparatus used was of the single-tooth milling cutter type, in all respects sirnilar to that first used and described by Airey and Oxford1 and again by Boston. The machine used in the present test is shown in Fig. 1. It is an ordinary milling machine in which a heavy pendulum has been substituted for the pulley on the arbor. If the pendulum is raised

Jan 1, 1932

By Ralph W. Smith

DEVELOPMENT of the lime industry- in Ste. Genevieve County began in a crude way in 1840. According to information furnished by the Missouri Bureau of Geology, in the early days small vertical kilns built of stone were used, and wood was the fuel. Modern development began in 1904 when one company introduced steel shells lined with firebrick. Within a few years two more companies erected similar plants, and in 1925 a fourth company began operations. Thus there are today four lime companies at Ste. Genevieve, all operating at high capacity and with a gradually increasing production. GEOLOGY The limestone of Ste. Genevieve County, which has the chemical composition and purity required for lime burning, is the upper 80 or 90 ft. of Spergen formation. The Missouri Bureau of Geology, in its geological map of Ste. Genevieve County, gives the Spergen formation a total thickness of 160 ft., but only the upper portion is pure enough for lime burning, with an average raw-stone analysis of 98.7 per cent CaC03; 0.35 Si02; 0.3 R203; 0.35 MgCO3; 0.3 S03. The Spergen, one member of the Meramac group, Iowa series, of the Mississippian system, underlies an area approximately 12 miles long north and south, by 5 miles wide east and west (Fig. 1) in Ste. Genevieve County. The entire eastern two-thirds of Ste. Genevieve County is sedimentary, the formations dipping gently toward the east on an average grade of about 4 per cent, or 2 ½ º. Thus the outcrops of the various sedimentaries run approximately north and south. A line running west from Ste. Genevieve crosses the outcrops of the sedimentaries, ranging from the top of the Mississippian to the Ozarkian geological system in a space of 12 miles. Thus with the gentle dip of 2 ½ º the 160-ft. thickness of the Spergen formation stretches out in its outcrop so that it is approximately one mile

Jan 1, 1938

By Stewart R. Wallace

Members of the Society, it is a very great honor for me to be here today and to have the opportunity of telling you about some things that have been accumulating in the back of my mind for some time. Before attempting to do so, I should acknowledge my debt to the many people who are responsible for my presence here this afternoon. To do this properly, however, would consume much of my allotted time and I will therefore mention only two men, both of whom were directly involved in the discovery of the Henderson ore body. The first of these was Robert Henderson, now dead, who at the time the work was going on was vice president of Western Operations of the Climax Molybdenum Co. Truly, he provided the environment that permitted the exploration program to function effectively, and the deposit appropriately bears his name. The second man I meant to mention was resident geologist at Urad at the time of the Henderson discovery. I think I should explain right here that the Urad ore body and the Henderson ore body, although entirely separate, are closely related deposits, and that both are located at Red Mountain in Clear Creek County, Colo.

Jan 6, 1975

By L. C. Raymond

Valuations in the mineral industry differ from those of other enterprises because mines and oil wells have a definite life so cannot be considered a perpetuity. This requires that in any mineral-property evaluation the recovery of invested capital is necessary during the life of the property. Capital write-offs for nonextractive industries are assumed to be continuously plowed back to sustain the operation and produce yields on the capital invested. The extractive or mineral industry, however, generally attempts to return to the investor both interest and principal during the life of a property. Normally this is done currently and the dividend includes both items. Where the mineral property possesses large reserves and the life factor approximates a perpetuity, the return on investment is generally comparable to that of industrial stocks. The valuation of a mineral property, at best, is based on educated estimates and judgment factors. This is particularly true as it relates to estimating selling prices over a long term or assessing the quality of management. Also, it is possible to make various assumptions as to rapidity of working out the deposit, varying time for start-up of operations, varying earning rates, so as to obtain different results with the same basic facts. Thus it is not surprising that two engineers, irrespective of their abilities, may not agree exactly even when given the same facts, but their results should be close enough to be used in establishing a fair value for trading purposes. The valuation is no better than the source of basic data and the soundness of judgment factors. Fundamentally the basic principles of mineral valuation are similar for base metals, sulfur, oil, or any other mineral. Each mineral, however, requires an engineer to have a knowledge of such factors as its occurrence, distribution, mining and processing methods, and marketing problems in order to gather and analyze all the facts and data that have a bearing on the earning potential of the property. Present Value of a Mineral Property In essence the present value of a mineral property is a sum of money in today's dollars that future income from the property are worth. It differs from the total anticipated earnings by the amount of the interest that the unrecouped investment could be expected to earn during the period of recoupment. Thus, if one could accurately estimate what a mineral property will earn during its life, after deducting all operating, administrative, capital, interest, and tax charges, the determination of present value would be a relatively simple mathematical calculation. Normally, where the expected life of the mineral property extends beyond 20 or 25 years, the discounted value of earnings beyond this period is relatively small. The petroleum industry generally discounts the annual cash flow of an operation rather than earnings since, for tax-saving purposes, earnings are kept

Jan 1, 1976