By S. R. Goodman, Hsun Hu, R. S. Cline

The quenching technique has been used to study phase relations in the composition area 2FeO.SiO2-FeO-SiO2-MnO.Si02-ZMnO.SiO2 of the system iron oxide-manganese oxide-silica under strongly reducing conditions such as exist in a gas mixture consisting of equul parts of carbon dioxide and hydrogen. Liquidus and solidus temperatures of most mixtures in the composition area studied are in the range of 1173° to 1345°C. EQUILIBRIUM relations existing among the oxides of iron, manganese, and silicon are of particular interest in two areas of steelmaking: slags and ingot inclusions. Mixtures of these oxides represent about 90 pct of the slag in the acid steelmaking process, and so dominate the chemistry of the whole refining process. These constituents also play an important role in the early slags existing at the time of the "lime boil" in the basic open hearth process. If these slags are liquid, they "wet" the lumps of lime rising from the bottom of the bath, and react with them. A liquid slag rich in CaO is then formed at the very beginning of the refining. Because the temperature is still low, all conditions for a good dephosphoriza-tion are fulfilled at this stage of the operation. Metal deoxidized with ferromanganese or silico-manganese is likely to contain, as inclusions, phases made up from among the oxides of iron, manganese, and silicon. A knowledge of stability relations existing among the phases present in this system, therefore, enables one to predict the hardness of the inclusions encountered. Moreover, because the shape of the inclusions in steel has a profound influence on the physical properties of the metal, it is important to establish whether or not the oxidic material is present as liquid or crystalline phases during heating and rolling of the steel (-1150 to 1350°C). A knowledge of melting relations in synthetic mixtures of iron oxide, manganese oxide, and silica will give a clue to these problems. Methods for determining such relations and the results obtained are described iln this paper. I) PREVIOUS WORK A number cf previous studies have dealt with the three "binary"* systems bounding the system iron oxide-mangar,.ese oxide-silica. The system iron oxide-silica was studied by Bowen and shairerl in 1932. Their data were obtained by equilibration of mixtures in contact with metallic iron. Phase relations for the system iron oxide-silica ill atmospheres of different oxygen pressures car1 be derived from data on the system FeO-Fe2O3-SiO2 as determined by Muan.2 The diagram shown iri Fig. l is a section of this system in an atmosphere of CO2 and H2 in ratio 1:l. The system manganese oxide-silica has also been the subject of several investigations. Most of the early studies suffered from a lack of proper control of the atmosphere under which the equilibrations were carried mt. Phase diagrams for the system at two well defined levels of oxygen pressures have been determined recently. Glasser3 determined stability relations in an atmosphere consisting of carbon dioxide and hydrogen in ratio 5:1, diagram Fig. 2, and Muan4 studied phase relations in the system in air.

Jan 1, 1962

By E. J. Horwood

The varying physical character and large extent of the Broken Hill lode necesarily involve the employment of a variety of underground methods. The lode had its origin in an extensive fault plane traversing metamorphosed schists conformably, as a rule, with their beds of stratification. The underground waters carrying minerals in solution deposited their contents in the original cavities formed by the faulting action, and in the enlargements of these cavities due to dynamic forces brought to bear on the rocks, more especially on the hanging-wall side of the fault. This deposition was supplemented by metasomatic replacement of a portion of the original rock contents by the argentiferous sulphides of lead and zinc which form the staple products of the district. Although the orebody is practically continuous throughout the mines, its width varies greatly, ranging from a few feet to about 350 ft. The widest portions occur in conjunction with huge folds in the inclosing country rock, almost exclusively on the hanging-wall side. The ore in these folds pitches to the south in the southern half of the field, and to the north in the northern half; there are, however, undulations in these ore channels evidently due to compression of the rocks in the direction of the channels. In the earlier days, before the orebodies had been opened up, vertical cross-sections across these bulges in the hanging wall gave the lode the appearance of the "saddle formation," so well exemplified at Bendigo in Victoria; but subsequent development of the ore channels has long since proved that the formations in the two districts are entirely different. The depth reached by the zone of complete oxidation of the sulphides varies from about 259 to 550 ft, from the original outcrop, while partial oxidation extends in places below the 1,000-ft. level. The result of oxidizing influences has been the production of ore of every grade of cohesive-ness, from that of dry sand to that of hard compact rock. The methods of mining followed in this field, and even in individual mines, are varied in accordance with the character of the ore. The general practice of the field is to sink vertical shafts, generally on the foot-

Jan 1, 1916

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.' In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator's Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By Waldemar Lindgren

I. INTRODUCTION AT the time of the discovery of America the old world had a scant supply-of the precious metals. Both the northern and the southern part of the new continent proved wonderfully rich in gold and silver and its treasures were eagerly looted; though the looting has lasted four centuries, the nines of its mountain chains are far from being exhausted. Even the later discoveries in Australasia and eastern Siberia could not rob the Western Hemisphere of its position as the greatest gold and silver producing region of the world, though finally the developments in a narrow and circumscribed area in South Africa wrested from the Americas their supremacy in the production of gold. Nevertheless the history of the two parts of the great western continent has been strikingly different. At first the Spaniards extracted vast treasures of silver from Mexico, Peru, and Bolivia, while Colombia and some placer deposits in Peru yielded a smaller quantity of gold. A couple of centuries later, a stream of gold began to flow from Brazil, the silver production from the countries mentioned above continuing strong in the meanwhile. Later on, the yield of South America diminished, but to offset this there began a wonderful series of discoveries in North America. The gold fields of California astonished the world; and when the cream of these had been skimmed off there began a no less amazing development of the Central Cordilleran gold and silver districts, which soon wade the United States the greatest producer of the precious metals. Aided by ever improving technique, extensive exploration, and a system of railroads, the yield was maintained and increased. Still later followed the discoveries of the gold fields of the arctic region and silenced those who had maintained that the zenith in gold production had passed. Recently the province of Ontario in eastern Canada

Jan 4, 1916

By C. L. T. Edwards

IN the preparation of this paper, the author has drawn upon experience with the operation of a blast furnace on 100 per cent scrap burden, which he believes was the first operation of its kind in the country. It is the writer's further belief that much of the controversy attending discussions of this subject may be obviated by the presentation of a group of facts that should be known by blast-furnace men and open-hearth men alike. The following question has been raised: "Is iron made with scrap in the blast-furnace charge as good iron as that made without scrap-made with straight ore?" This question may be answered in part by the fact that the open-hearth men of the Bethlehem Steel Co. who used pig iron from a blast furnace that operated on 100 per cent steel scrap found no difficulty in the processing of such iron other than that to be expected from the known analysis. OPERATION WITH 100 PER CENT STEEL SCRAP During World War I, there was accumulated at the Bethlehem plant of the Bethlehem Steel Co. some 22,000 tons of alloy-steel turnings and borings. This scrap material was highly corroded and, like alloy-steel turnings of that period, were as a drug on the market. There was also a small tonnage of scale, rich in valuable metal. If this scrap could be worked up into pig iron, it would become readily available for use in the open hearth. In order that the pig iron should contain the maximum percentage of nickel, permission was obtained from the Management to try a 100 per cent scrap operation. Accordingly, a blast furnace was swung over on July 25, 1919; the percentage of steel scrap increased more or less irregularly until July 29, when l00 per cent steel turnings were charged. Except for occasional charges of nickel scale as an "extra," the operation continued uninterruptedly until Aug. 27, when the furnace was swung back to the regular ore-ore and scrap-operation. During this period, the furnace production ranged from a low of 568.60 tons to a maximum of 766.07 tons. At the swing-over from i00 per cent scrap to the regular burden, the charge hung up rather severely. While the latter condition has nothing to do with the object of the paper, a brief discussion of the experience will appear later because of the interest it may have for blast-furnace operators. In Table I, results of the first and last days of the ore charge are shown, July 25 and July 29. The last column shows a summary for the period of maximum scrap charge. The furnace employed had a hearth 16 ft. 0 in., bosh 22 ft. 0 in., stock line 15 ft. 6 in., bell 11 ft. 6 in., batter ¾ in., bosh angle 73° 27' and a Baker-Neuman top, with gas-engine blowers. Analyses Range of Material Charged Gravel: Si02, 64.40 to .7o.54 per cent; A1203,3-52 to 4.58; CaO, 7.27 to 9.49; M90, 5.09 to 6.14; FeO, 1.67 to 3.34, ignition loss, 9.50 to 13.83.

Jan 1, 1941

By E. S. Lenker, H. J. Van Hook

A complete swies of solid solutions has been found between the compounds InAs and GaAs Below the solidus. The melting relations determined by differential thermal and static quenching technzques, indicate that the liquidus and solidus are of the simple ascendant type. No evidence of unmixing of the homogeneous solid solutions was observed at sub-solidus temperatures. A quenching method for locnting the solidus, using X-ray diffraction techniques, is described in some detail. THE semi-conducting properties of compounds formed by various combinations of the less familiar intermetallic elements have created an increasing interest in the phase relations in systems involving these elements. The complete phase diagram of such a system, containing a compound of special interest, will often provide information as to the most favorable conditions for preparing large crystals from a melt, as well as specifying the temperature stability of the crystalline phase or phases produced. In view of the current importance of gallium arsenide in semiconductor research and of the structural similarities of indium arsenide, it was thought that the complete phase relations of the system InAs-GaAs should be investigated. Previous work on the system Ga-As by Koster and homa' and on In-As by Liu and peretti2 has shown that GaAs and InAs are the only compounds formed, having melting points of 1238° and 942°C, respectively. In a survey of various systems of elements from groups IIIb and Vb, spengler3 also re- Mines Ltd., for his continuing encouragement and for permission to publish the results of this work. ports complete miscibility of gallium, indium, and arsenic in the liquid state. In a partial investigation of the InAs-GaAs system, Woolley and smith4 found extensive solid solution throughout the alloy range. Their subsolidus work, however, was inconclusive at temperatures below 900" and they did not determine the liquidus relationships of the system. PRESENT INVESTIGATION The starting materials used were high-purity gallium, indium, and arsenic. The method of preparation of the compounds follows that devised by M. Shafer and is described in detail in a paper by Shafer and eiser.' The end-member compounds, GaAs and InAs, were first prepared by reaction of the elements in the desired proportions in evacuated silica glass vials. The vials were rotated in a furnace as the temperature was slowly raised to insure rapid and complete reaction at low temperatures. Thereafter the starting materials, GaAs and InAs, were melted by heating the sealed vials to 1300" and 1000°C, respectively; the vials in this case were filled as completely as possible to keep the vapor space small and thereby minimize the loss of arsenic to the vapor phase. Ten binary mixtures of these compounds were then prepared by reaction of the powdered material in the solid state just below solidus temperatures. At 900C preparations containing 3, 5, 8, 10, 25, 35, 50, and 75 mol pct GaAs were found to be single homogeneous phases, indicating a complete series of solid solutions between GaAs and InAs. Moreover, it was discovered that the homogeneity of any crystalline binary preparation could be very accurately checked by X-ray diffraction because of the large differences in unit cell dimensions of the end membe5s. The cubic lattice constant ofor GaAs is a = 5.652A and that of InAs is a = 6.061A

Jan 1, 1963

By W. S. Keyes

(Read at the Amenia Meeting, October, 1877.) EASTERN NEVADA. THE State of Nevada, known par excellence as "the Silver State," occupies the major portion of the wide plateau, or so-called Great Basin, lying between the Sierra Nevada range on the west and the Wahsatch range of the Rocky Mountains on the east. It extends from the 114th degree to the 120th degree of longitude, west of Greenwich. It is limited, on the north, by the 42d degree of latitude, and on the extreme south by the 35th degree of latitude. Its general shape is that of an irregular parallelogram, from which the lower or southwestern portion has been cut off by a diagonal southeasterly line; the missing portion forms a part of the State of California on the west. The Great Basin is made up of a succession of low hills, or minor mountain ranges, running very nearly north and south, with long valleys between them. All of these mountains are more or less metalliferous. On the western rim, marking the eastern flank or foothills of the Sierra, we find granites, porphyries, and propylites. Here we note the great Comstock lode, with its free-milling gold and silver ores, and still further south the once prominent and the now reviving gold and silver-bearing districts of Esmeralda County, Nevada, and of Morro County, California. Next, at some distance to the east, we find the mining districts at and near Unionville, in Humboldt County. Still further to the east we find the Battle Mountain copper-silver district, north from the railroad, and southerly therefrom the Austin or Reese River, Belmont, and other districts. Still further east and north of the railroad, we find the Tuscarora, a new district of very

Jan 1, 1878

NEW MEMBERS The following list comprises the names of those persons Who became members during the period July 10, 1918, to Aug. 10, 1918. ARCHER, EUGENE G., assayer and Chem., Granby Cons. Min. Smelt. & Power Co.,Anyox, B. C., Canada. BAKER, ROBERT C Mech. Engr. and Draftsman, Moctezuma Copper Co., Nacozari, Son., Mexico. BARNES, EDWARD A Supt., Fort Wayne Works, General Electric Co., Fort Wayne, Ind. BARNHART, EDWIN Engr. of Tests, Bethlehem Steel Co., Sparrow's Point, Md. BENSLEY, MAURICE D Pres. and Mgr., Frontier Brass Foundry, Inc., Niagara Falls, N. Y. BRADLEY, JOHN C Met., The American Brass Co., Waterbury, Conn. BRAGG, C. T Works Mgr., Michigan Smelt. & Refin. Co., Detroit, Mich. BRYMER, GEORGE W Min. Engr., 922 Union National Bank Bldg., Scranton, Pa. CHIVVIS, NORMAN Met. Engr., More-Jones Brass & Metal Co., 3144 North Broadway, St. Louis, Mo. CRAWFORD, R. D Prof. of Mineralogy & Petrology, Univ. of Colorado, Boulder, Colo.

Jan 9, 1918

By C. F. Cockrell, K. K. Humphreys, H. E. Shajer

It is quite conceivable that the question of using coal or an alternate fuel in the future by large industrial consumers may be decided on the basis of possible profitable utilization of flyash. Accordingly, the Coal Research Bureau at West Virginia University has been attempting to develop new uses for this waste material. This effort has resulted in the development of a process for producing flyash-based face brick and other structural materials which generally exceed published specifications for competitive clay-based materials. These structural materials, containing up to 97% waste coal ash, can be produced from flyash derived from most coals without regard to the physical or chemical properties of the coal ash. Preliminary production cost estimates indicate that face brick can be manufactured at a rate of 9000 brick per hr or more with a resultant gross profit of over $24.00 per thousand brick. Plant payout time for a plant of this size would be only about 1.2 years assuming a market price of approximately $55.00 per thousand, a well established figure for comparable clay brick. With flyash production expected to more than double in the next 15 years, there is an increasing need for a practical and Profitable method for the utilization of large tonnages of this material (see Table I listing total flyash production of utilities in each state of the U.S.). Present industrial and governmental physical and chemical restrictions, particularly for use as a lightweight filler or pozzolanic material, have limited the use of flyash considerably. For those ashes which have met the required standards, utilization is not always assured because of lack of promotion and poor public acceptance. Less than 6% of the total flyash production in the U.S. was sold in 1962. The remainder was dumped in disposal areas at costs as high as $2.42 per ton.' It is quite conceivable that in the near future the question of using coal or an alternate fuel by large industrial consumers may be decided on the basis of the possible utilization of flyash. To help insure future coal demands, the Coal Research Bureau at

Jan 1, 1968

By S. S. Cole, D. L. Armant

The smelting of titaniferous ores for the past hundred years has not been successful because of thickening of the slags in the furnaces. The interest in the utilization of these iron bearing materials has been due to the extensive deposits which have been found in various parts of the world.1 The literature contains references2 to the use of titaniferous ores in blast furnaces. None of these attempts has met with success due to the lack of sufficient information as to the cause of failures and to economic considerations. Evaluation of the published information, as to the probable cause of failure in various attempts, has indicated that the presence of lower valence titanium oxide and formation of titanium carbide contributed to the failure. It was apparent that severe reducing conditions which are present in a blast furnace had been one of the factors for such failures. The previous smelting operations had as a primary objective the recovery of iron from these ores. Under these conditions the highest recovery of iron could only occur with severe reducing conditions. Application of Melting Point Data The application of the melting point data, from the system CaO-MgO-Al2O3-TiO2 reported in another paper,3 to the smelting of titaniferous ores required an extrapolation of these melting points due to the presence of other impurities from the ores. Likewise, a study of the effect of varying FeO and reduced titanium content of the slag was necessary before the data could be fully applied. The melting point data under oxidizing conditions had clearly indicated that a fluid slag with a melting point in the temperature range of 1370°C could be obtained. The smelting of a titaniferous ore had as a primary objective the production of a high titanium slag which was fluid and substantially free of iron and low in trivalent titanium. Since production of a high titanium slag was of primary importance, rather than the recovery of iron from these ores, the smelting concept could be altered to a marked degree. The ferrous oxide could be maintained at higher levels than is the normal practice in iron ores slags without being detrimental to the slags, although a loss in iron recovery resulted. During the reduction of the molten mixtures of ferrous iron and titanium, carbon acts as the reductant for changing the valence of the titanium and iron. The reaction can go further than in the case of the reduction which occurs in iron-titanium solutions. The formation of metallic iron removes iron from the system, so that the titanium oxide can be reduced to trivalent and divalent titanium oxides and also form titanium carbide which removes the titanium from the slags as a soluble constituent. The problem, therefore, resolves itself into maintaining the proper amount of ferrous iron in the slag thereby avoiding the formation of appreciable amounts of trivalent titanium and no divalent titanium oxide or titanium carbide. The latter two have been found in the viscous

Jan 1, 1950

Philip Argall, Denver, Colo. (communication to the Secretary) : Mr. Rickard expresses regret that I have not given more extracts " from the fresh leaves of nature's open book." The quotations used by me in argument were all from nature's open book, and by authorities recognized in the scientific world as being able to decipher nature's unwritten pages, if not lay bare her inmost secrets. The study of -nature should be preceded by a knowledge of her laws. Natural science is but the summary of the observations of the past or an organized and accurate knowledge of the order in which things have been observed to happen. One who ignores the 'knowledge of the past or despises that of the present and approaches nature's open book with a virgin mind but too often finds her

Jan 1, 1895

By C. E. Wood

THIS paper is a brief report of experimental work undertaken to determine whether barium oxide in any quantity increases the desulfurizing action of blast-furnace slags. Industrial furnace operation with slag containing small quantities of barium oxide, referred to later, interested S. A. Sanford of the Commercial Chemical Co., Youngstown, Ohio, to conduct experiments to furnish comparative results on desulfurization with normal slag and slag containing small quantities of barium oxide. The U. S. Bureau of Mines agreed to assist on the problem because of the possible saving in fuel if the desulfurizing action of blast-furnace slag can be substantially increased, also because the experiments would yield new information on sulfur elimination in general, a matter of economic importance in furnace practice. A more complete and fundamental study of desulfurization of iron by slag is in progress.

Jan 1, 1929

By L. M. Cathles, L. E. Murr

Results of two years of leaching of 160 metric tons of low grade industrial copper sulfide waste in a large (40` high 10` diameter) thermally insulated tank at the New Mexico Institute of Mining and Technology are analyzed in the light of a previously developed model of the waste leaching process. It is shown that the model is verified in all major aspects and that the parameters in the model that characterize the leaching of a particular sulfide waste are usefully constrained by the results of the tank leaching experiment. The similarity between waste leaching parameters determined from the tank experiment and from interpretation of the leach behavior of test dumps constructed of similar waste encourages optimism it may be possible to predict the leach behavior of field dumps from suitably interpreted column experiments using the computer model developed.

Jan 1, 1980

By J. T. Jones, H. V. Winchell

In the history of mining in this country there has been nothing exactly similar to the Mesabi iron-range in Minnesota, and the conditions there prevalent. Soft-ore mines are found in many parts of the country. In some the deposits are vertical, and are worked in open pits, or have been so worked, until it was found cheaper to go under ground. In other localities, the ore is scattered through clay beds in the form of hard lumps. These clay beds are sometimes excavated in open pits, and the ore separated by washing. On the Mesabi, the ore itself occurs in strata, and these strata appear quite flat to one standing upon the ground. The ore is soft in the main, and does not require much sorting to free it from foreign or deleterious substances. It is usually covered by the glacial drift-mantle, but occasionally passes beneath a capping of jasperoid rock called " taconite." The ore is twice or three times the thickness of the layer of drift lying upon it. This drift consists of clay, sand, and gravel, with occasional beds of large boulders. There is great difference of opinion among competent miners as to the cheapest methods of mining this ore. It is admitted that local conditions will govern largely ; but there is such a similarity among many of the mines that it seems possible to arrive at some general conclusions on the subject. A typical example of a Mesabi mine is found in the Biwabik. It is one of the largest, and is the most advanced in development. Not a single ton of ore has yet been shipped from this mine, but the expense of the explorations upon which the following description is based has exceeded $60,000. It is seldom that such accurate and complete exploration of a deposit of this magnitude has been possible in the space of time which has elapsed since the discovery of this ore-body. It lies in a new. region, and was remote from railroads until last August, yet, not only the width and length but the depth and quality of the ore-deposit have been learned, and the probable expense of' mining its 20,000,000 tons of ore has been closely figured. After careful consideration, the method of stripping and

Jan 1, 1893

By Fred DeVaney

THE coercimeter, as its name implies, is an instrument for measuring the coercive force? of magnetic substances. It was developed by Davis and Hartenheim in the Special Studies Section, Metallurgical Division. A detailed description of this apparatus may be found elsewhere.2 The coercive force determinations of magnetic materials are inter-esting because of the relationship established by Gottschalk,4 who showed a linear relationship between the magnetization coercive force and the specific surface of comminuted particles. The value of this relationship in determining grinding efficiency has been shown by Dean.3 The determination of the surface contained in the subsieve sizes has always been a difficult problem for investigators. They made approximate measurements of the surface of coarse materials by sizing on screens, but for the determination of the surface of the sub-sieve sizes it was necessary to make detailed grain counts or, elutriation tests, or to study dissolution rates. The technical literature contains many references to other methods for determining these surfaces, either by some special apparatus or by mathematical calculations based on distribution lines. Many of the methods are long and tedious, and the results of some, at least, are questionable. The turbidimeter gives quick results on ground cement. By using magnetite as the material to be ground, a simple determina-tion of its coercive force by the coercimeter, requiring 10 minutes or less, can be transposed directly and accurately into units of relative surface. This subject has been pursued further by the U. S. Bureau of Mines in cooperation with the Missouri School of Mines and Metallurgy, Rolla, Mo., and the following is a description of the results.

Jan 1, 1938

NEW MEMBERS The following list comprises the names of those persons who became members during the period June 10 to July 10, 1915: Members AGTHE, FRED. THOMAS, Quarry Supt., Atlas Portland Cement Co., Hannibal, Mo. ARTHUR, WILLIAM SEYMOUR, Project Mgr., U. S. Reclamation Service, Williston, S. D. ASH, SIMON HARRY, Deputy State Mine Inspector 503 Alaska Bldg., Seattle, Wash. BALDWIN, C. KEMBLE, Second Vice-Pres. and Chicago Mgr., Robins Conveying Belt Co., 1315 Old Colony Bldg., Chicago, 111. BOGGs, WILLIAM BRENTON, Met Douglaston, L. I., N. Y. BROWN, RALPH DARE, Min.Engr., Asst. Genl. Supt., O'Gara Coal Co., Harrisburg, 111. COLE, A. NEWTON Genl. Supt., Pennsy Coal l O., Clarion Pa. DAVIS, JOSEPH D., Chem Bureau of Mines, Washington, D. C. DEAN, DUDLEY STUART, Treas., Keweenaw Land Association, Ltd., Newport Land CO., 87 Milk St., Boston, Mass.

Jan 8, 1915

By A. P. Woods, J. A. Elias, A. J. Heckler

A method is described by whichX-ray pole figures and axis density figures may be plotted automatically. The X-ray data are obtained using a Siemens texture gonionleter and the Schulz reflection method. Composite sampling methods are used to obtain a full quadrant of the pole figure. The contour lines of the pole figure and axis density figures are drawn using a computer-controlled x-y plotter. The computer program used to draw the contours was obtained from ZBM. POLE figures used to describe crystallographic orientations of poly crystalline sheet materials are usually plotted manually from X-ray diffraction output in the form of a strip chart recording of the intensity distribution of a given crystallographic pole in physical space. Today's computers and associated plotting equipment now make it possible to plot pole figures and axis density figures automatically. Inverse pole figures have been determined by mathematically "inverting" X-ray pole figure data.'-' In general, these methods require complicated, time-consuming numerical calculations. A more economical but less accurate method is to determine the axis densities of low-index crystallographic poles using an X-ray diffractometer. When these axis densities are plotted in a unit stereographic triangle contour lines can be drawn to represent the axis density distribution. This can now be done automatically. Computers were used to plot pole figures by a method developed by Holland, Engler, and powers.' In their method intensity ratios based on a random standard sample were obtained from a strip chart recording, and the stereographic (x, y) coordinates of these ratios were determined by a computer. Symbols characteristic of different intensity ratio levels were then plotted using an automatic x, y plotter and intensity contours were drawn manually. The present paper describes a method by which pole figures and axis density figures have been automatically plotted from digital data obtained from a Siemens X-ray unit. Plotting was accomplished using an IBM 1620 computer and a Calcomp 563 digital plotter. COMPUTER PROGRAM The computer program was obtained from IBM Systems Reference Library, No. 1620-CS-05X, and was designed to plot contour maps from randomly distributed data. It consists of a set of twelve separate subprograms, four of which were used in this work. The program takes a given distribution of data points and by a numerical method determines the values at mesh points of a square grid system superimposed over the input data. The output data from this program is in a form suitable for input to the contour plotting program. A smoothing program is also available which calculates new mesh point values from a continuous function fitted to neighboring mesh points. The degree of smoothing depends on the number of points around a given grid point which are used to adjust or smooth the grid value. The contour plotting program is designed to allow the user to specify the interval, scale, and annotation of the contours to be plotted. EXPERIMENTAL PROCEDURE Pole Figure Data Points. Diffracted X-ray intensities were determined using a Siemens texture goniometer and the schulzs reflection method. Due to geometric

Jan 1, 1968

By William Kent

(Read at the Philadelphia Meeting, February, 1878.) IN the paper by Mr. Fernow, on Red Charcoal, read at the first session of this meeting, it was suggested that this fuel might be used in the blast furnace with greater economy than ordinary or black charcoal. In the discussion which followed the paper, it was stated that the charcoal furnaces of the Lake Superior District have used imperfectly burned charcoal with success, and that these furnaces have given the best results in fuel economy on record. On consulting some of our well-known metallurgical authorities the writer finds that the question of the use of red charcoal, or other imperfectly burned charcoal, or charred wood, is not at all new. In Percy's late work on Fuel, pages 409-414, are given a few facts, which are here condensed, as follows:

Jan 1, 1878

By L. C. McCabe

THE object of the present investigation was to discover a physical basis for rank differentiation of coals, particularly the coals of the Illinois basin. Vitrain1 was selected as the most appropriate coal material to use in the investigation, because of its homogeneity and ease of acquisition and handling. Previous Investigations.-Hoffman and Jenker2 have shown that their index of reflection is a characteristic of coal rank and that the Leitz slit microphotometer may he used in determining the different intensities of reflection. Zhemchuzhnikov3 measured the luster of several Russian coals with a color analyzer and found that the degree of luster was indic-ative of rank. Luster-volatile matter curves based on data from Sucan and Donetz coals were satisfactorily used for determining the rank or volatile content of other coals after the luster strength was determined. In 1934 Fisher4 reported refractive indices of 1.76 for bituminous vitrain and 1.87 for semibituminous vitrain. Investigation of Angle of Polarization.-Early in the present investiga-tion several determinations of the refractive indices of the vitrains were made by immersing the minus 150 plus 200-mesh powder in oils. It was found that all the samples fell within the range 1.6 to 1.8. However, difficulty was encountered in securing oils in this high index range that were closely enough spaced to separate some of the coals. The writers made a number of determinations of the angle of maxi-mum polarization from the polished surfaces of the vitrains and derived their refractive indices by the procedure described in the follow-ing paragraphs.

Jan 1, 1937

By Arthur S. Coffinberry, Ralph Hultgren

We have studied the gold-aluminum system by X-ray diffraction and by the microscope over the entire range of composition for temperatures between 300° and 500° C. Results obtained are shown in Fig. 1, combined with the work of Heycock and Neville1 at higher temperatures. The diagram differs in important details from that given by Hansen2 in his critical compilation of the literature of binary alloy systems. This work was undertaken both because of the intrinsic value of a knowledge of the phase diagram of this system and because of the need of theoretical metallurgy for precise and accurate data, particularly X-ray diffraction data. Systematic studies of equilibrium diagrams, particularly by Hume-Rothery,3 have shown regularities that yield a certain insight into the nature of alloying forces. It has been shown, for example, that solid solubility depends on the concentration of free electrons in the alloy, on the relative radii of solvent and solute atoms, on the forces of attraction between atoms, and on the relative stability of intermediate phases. The well-known Hume-Rothery rule states that the crystal structures and compositions of many intermediate phases depend on the electron-to-atom ratio. This has been confirmed and extended by wave mechanical calculations.4 A knowledge of the forces between atoms in alloys, even an imperfectly developed empirical one, should be a valuable guide in the preparation of technological alloys of desirable properties. Furthermore, such information is basic in such problems as rate of diffusion, age-hardening, phase transformations, and others. The most valuable data for this purpose are furnished by X-ray diffraction studies. Unfortunately, work has been

Jan 1, 1938