Search Documents

By S. P. Kinney

Sulfur has been one of the most troublesome elements encountered since the earliest days of iron smelting, and this problem will become of increasing importance as the higher sulfur coke is used, because of the rapidly diminishing supply of low-sulfur coals suitable for the manufacture of metallurgical coke. The deleterious effect of sulfur in iron and steel is well known; therefore, except in special cases, it is desirable to make the iron produced by the blast furnace as low in sulfur as possible. Sulfur enters the furnace in all of the raw materials, but principally in the coke. It comes out of the blast furnace distributed between the iron and the slag; very little passes out of the furnace with the gases. The mechanism of the reactions that cause the sulfur of the coke to pass into the slag and iron has not been studied to any great extent, although the character of the end products, and the conditions controlling the distribution of the sulfur between the iron and slag, are fairly well known. In the iron, the sulfur occurs as ferrous sulfide; or manganese sulfide in case of iron high in manganese. In the slag, the sulfur is present mostly as calcium sulfide. The presence of free sulfur1 and sulfates in blast-furnace slags is to be accounted for on the basis of oxidation of the calcium sulfide after the slag is tapped. The generally accepted reaction for the relation between the ferrous sulfide in the iron and in the coke, and the calcium sulfide in the slag, is that given by Howe? FeS + CaO + CDFe + CaS + CO

Jan 1, 1923

In 1803 the purchase of the immense territory called the province of Louisiana wm arranged between Thomas Jefferson, President of the United States, and Napoleon Bonaparte, First Consul of France. This central portion of what is now the United States was claimed in 1682 by the explorer Robert de La Salle for France, who continued to hold her title to the vast domain until 1762, when it passed by treaty to Spain, only to be retroceded to France in 1802, in consequence of Napoleon's military domination of Spain. Jefferson did not care to see New Orleans and its extensive hinterland pass into the hands of France. Spain did not matter so much; she was quiet and feeble, whereas France was restless and aggressive under Napoleon, who had dreams of founding a French colonial empire on the American continent. The expression of American feeling that Jefferson elicited came as a surprise to Napoleon, who concluded that a contest was not worth while, for his navy had been shattered by the English, and it was evident that only maritime supremacy could enable him to retain this trans-Atlantic possession; so he resolved to put it out of the grasp of England and at the same time replenish his military chest by selling Louisiana to the United States. The price was 60 million francs. By the terms of the Louisiana purchase a magnificent territory was added to the national domain; it covered more than a million square miles, or more than the total area of the United States at that time. Louisiana included the present States of Louisiana, Arkansas, Missouri, Kansas, Iowa, Nebraska, South Dakota, North Dakota, Wyoming, Montana, Oklahoma, with parts of Colorado, Idaho, and Minnesota; but

Jan 1, 1932

By Heinrich Freyn

THE American iron and steel manufacturer finds himself to-clay barely at the threshold of enormous possibilities for practicing rational economy in the use of fuels. The fuel cost is by no means the smallest of items which enter into the cost of manufacture of iron and steel products, but the great wealth of this country in high-grade fuels, together with a protective tariff, has heretofore made fuel economy relatively unimportant. In Germany, the use of raw coal for the purposes of iron and steel manufacture has been all but abandoned and large sums of money, formerly irrevocably wasted, are now being saved. When scanning the literature of this country devoted to the application of gas power, but little information will be found on a subject which, however, is destined to become of considerable importance in the United States, namely, the use of coke-oven gas for the generation of power in gas engines. This lack of information can be traced to the fact that the regenerative by-product coke oven with its large amount of surplus gas is still far from having attained in this country the universal application which it has found in Europe. This statement needs hardy any corroboration other than the evidence of statistical investigations made by E. W. Parker of the United States Geological Survey, according to which only approximately 25 per cent. of the total coke produced in this country in 1912 was made in by-product coke ovens, whereas 75 per cent. was produced in bee-hive ovens. This entailed the enormous loss of over $80,000,000 in non-recovered by-products, such as gas, tar, and ammonia, without considering the substantial loss due to the non-recovery of benzol from the coal. There are two more or less distinct fields of application of the by-product coke oven: one, to furnish as the main product metallurgical coke of specified quality, and surplus coke-oven gas as the by-product, and the other, to carbonize high-volatile coals, and thus produce as the main product large quantities of gas, high in heat value and rich in illuminants, adapted primarily for domestic heating and lighting, while domestic coke becomes the by-product.

Jan 4, 1914

By G. S. Cole, H. Biloni, G. F. Bolling

An experimental investigation of sovlze low .melting point alloys sJtows that a substvucture of isolated depressions can be the first manvestation of constitutional supercooling on solid-liquid interjaces veuealed by decanting. Electron-tni cvop vobe and wletallo gvaplic esanzinations, in tlze bulk belzind the interjace, oj the segregation associated with these isolated areas substantiate tlzei&apos;v depressed nature, since a solute of ko < 1 is enriched, and a solute of ko > 1 depleted. In contrast, the pox structuve, a set of projections often veported in the literature, leaves no trace oj. segvegation. These obserl;atims, accovlrpanied by a brief review of recent literature, point to inconsistencies between experirrental obsevvation and the idea that the fornzation of a projection is a causal step in the development of a cellular substructure. An argument is presented to show instead how it is plausible for substantial depvessiom to form in the pvesence of constitutional supercooling at dislocations threading the solid-liquid interjace. THE development of constitutional supercooling during growth from the melt leads to the formation of the cellular solidification substructure. This well-founded association between structure and instability has been basic in understanding cellular substructure and micro segregation; however, the initial formation of structure seems unclear. Rutter and Chalmers,&apos; in definitive experiments and theory, noted that in the presence of constitutional a planar interface might break down: "resulting in the formation of a small projection on an initially plane or uniformly curved interface." That is, the breakdown from a planar to a cellular interface was implied to be initiated via a projection into the unstable liquid. Later, Walton et (11. found that a structure of isolated projections, termed "pox", appeared at solid-liquid interfaces decanted under growth conditions near the onset of constitutional supercooling; the pox were taken as the indication of the instability promoted by the supercooling. Tiller and Rutter4 in their extensive work studied the shape transitions at decanted interfaces which were generally observed to proceed as— pox, "irregular cells", elongated cells, regular (hexagonal) cells, and so forth. The pox varied in size from lo-&apos; to 1CT4 cm, and tended to disappear as cells increased in number and regularity, but as noted,4 the first real array of cells did not seem to be a development from the pox. In fact these authors implied a lack of connection because they stated that the pox are denser on "irregular cells", and as cell boundaries increase in number (i.e., the cells become smaller) there is less need for the pox which do dis- appear. Thereafter, most authors dealing with either experiment or theory have accepted the reality of pox and have used them as a criterion for the onset of constitutional supercooling. In contrast, Spittle, Hunt, and smiths have now suggested that pox are irrelevant artifacts comprised of such things as entrapped oxide. This proposal invokes the observations of weinberg6 and chadwick7 each of whom have shown that the act of decanting leaves a residual liquid on a decanted interface; the remnant solid layer of the order 10 p may thus contain particles that might have been transported from the external surfaces, or elsewhere, during decanting. With the incentive of this suggestion,= some further experiments and a reexamination of the literature have been conducted, in order to question the validity of pox as evidence of an instability and to examine the initial development of the cellular substructure. 1) EXPERIMENTS Single crystals of zone-refined tin (-99.9999 pct) were grown from the melt in a controlled fashion with various, small concentration additions of lead and antimony, for which ko < 1 and > 1, respectively. The crystals were decanted at conditions near the onset of constitutional supercooling and were thus appropriate for observation of slight perturbations. It was possible to observe two types of small departure from smooth or "planar" interfaces in both cases of lead or antimony additions. Some were projections and others, if in regular array of any type, were depressions. The crystals were etched with suitable reagents progressively dissolving the decanted interface surface; projections left no record, but depressions were continuously associated with spotlike areas contrasting with the rest of the interface. Traverses were made with the beam of an electron microprobe across the regions of contrast; with lead addition the persistent spots were lead-rich, and with antimony addition the persistent spots were antimony-poor. This is consistent only with a dominant role for depressions, because if the projections had left spots but were incorrectly catalogued, a reversed observation should have been made; that is, the Pb(ko < 1) should have been depleted and the Sb(ko > 1) enriched. In the work of Cole and inegard, and elewhere, regular arrays of structure associated with the initial stage of instability have been shown, in photographs and represented as pox or projections. We believe this to be erroneous, by inference, since whenever a regular array was observed, in the present examination, it consisted of depressions, regardless of the nature of the solute, ko 1. Fig. 1 is reproduced8 as an ideal example of the possible optical illusion involved; the observer can satisfy himself from the distribution of illuminated areas that the markings are depressions. Fig. 2 from the present investigation is an interference photograph of an interface similar to that in Fig.

Jan 1, 1967

By L. C. Brown, J. S. Kirkaldy

AS part of a program to investigate the diffusive properties of dilute ternary austenites, we have made a determination of the effects of cobalt on the activity of carbon in y iron. Samples of pure iron and Fe-Co alloys were equilibrated at 1000°C in controlled CO-C02 atmospheres, following the procedure of R. P. smith.&apos; The 0.010-in.-thick samples were analyzed for carbon by microcombustion analysis2 to give a set of isoactivity curves. The latter were converted to activity-coefficient (standard state at infinite dilution) plots by combination with Smith&apos;s data&apos; for the activity of carbon in pure iron measured in a CO-C02 mixture. Table I shows the composition of the base alloys used, while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In the notation of Wagner,&apos; the interaction parameter is the second coefficient on the right, Eq. [I] adequately correlates the experimental points for those alloys which were prepared from electrolytic iron by arc-melting (2,4, and 7 pct Co). The results for the 10 pct Co alloy (supplied by Crucible Steel Co.) do not correlate with the others. In fact, the experimental points for this alloy correspond to an interaction parameter of It is possible that the interaction parameter is a function of concentration for large cobalt additions, but we are inclined to attribute the discrepancy to the presence of a significant amount of aluminum added to this alloy for deoxidation purposes (Table I). Preliminary measurements for the system Fe-C-A1 have indicated an interaction parameter of Which implies that the effect of aluminum in solution on the carbon activity is sixty times greater than the effect of an equal weight percentage of cobalt. These observations cast some doubt on the precision of the results of Chandhok, Hirth, and Dulis who used this same 10 pct alloy for their experiments, obtaining an interaction parameter of E = 2.2. There is considerable doubt as to the activity of a plane Fe-C system. Using a CH4-Ha mixture, Smith obtains cg = 6.1 for the effect of carbon on the activity of carbon in austenite, rather than the value of 8.9 given in Eq. [I]. The use of CHa-Ha mixtures has recently been questioned by Kaufman, Radcliff, and cohens who state that there is some possibility that other hydrocarbons are formed. Fortunately, the determination of the interaction parameter is not sensitive to the coefficient of Nc. For example, using the CHI-H2 results we obtain a value which is almost the same as that obtained using the CO-CO, results. The authors wish to thank Mr. E. J. Dulis of the Crucible Steel Co. of America for supplying us with samples of the 10 pct Co alloy used in their original work. Financial assistance from the American Iron and Steel Institute is gratefully acknowledged.

Jan 1, 1963

By David Browne

THE literature dealing with the physical constants of nickel is so fragmentary and unrelated, that a synopsis presents unusual difficulties. It is only within the last few years that investigators have understood the importance of placing on record not only the determinations they have made but also the composition, physical treatment, and past history of the material investigated. For this reason much of the earlier literature is valueless. Determinations have been made of the same physical constants on samples differing widely in origin, composition, and treatment, and the results differ widely among themselves. In the first place nickel is almost as flexible a term as steel. Its physical properties are widely influenced by its composition and treatment. It absorbs large quantities of gases and is exceedingly difficult to prepare in a state of chemical purity comparable to gold, silver, or copper. It is vitally affected by thermal and mechanical treatment. Hence in the following pages the recorded literature, where quoted, must be accepted with a certain reserve and used, as far as possible, as a check on later observations, in which these important factors are noted. In every case where new determinations are given, an attempt has been made to record all available information concerning the composition and treatment of the material used so that the data may serve as steppingstones toward a wider knowledge of the properties of the metal. As this synopsis is an attempt by men of metallurgical training to do what should long before have been clone by physicists, it is to be expected

Jan 9, 1919

By HORACE V. WlNCHELL

Location. THE St. Helens mining-district, indicated in sketch-map, Fig. 1, is chiefly in Townships 9 and 10 North, Ranges 5 and 6 East, of the Willamette meridian, in Skamania county, Wash. There is no railroad or even a wagon-road at present connecting it with any base of supplies; access is usually by wagon-road for FIG. I.-SKETCH-MAP OF THE STATE OF WASHINGTON. about 50 miles from the town of Castle Rock to Spirit lake, and from that point by pony-trail from 6 to 10 miles farther. History. Nearly 20 years ago two German farmers, totally inexperienced in prospecting, penetrated this region upon a hunting and fishing-trip. Their attention was drawn to numerous joints and crevices filled with black, glistening tourmaline, and con-

Oct 1, 1912

By Carl J. McHargue

Mechanical twins were produced in electron-beam melted columbium by high-speed impact at room temperature and by slow or fast compression at -196°C. The composition plane of the twins was { 112} and the shear direction was <111>. Notches in the twin bands often corresponded to traces of {110) of the matrix and appeared to be untwinned regions. Markings within the twin bands were interpreted as resulting from {110} slip in the twins. THERE has been much work in recent years concerning plastic deformation by glide, and the dislocation theory relating to glide has reached a relatively high degree of development. On the other hand, there have been fewer studies of deformation by mechanical twinning, and understanding of this process is far from satisfactory. This method of deformation is of interest for at least two reasons. First, it provides a mechanism in addition to glide for the relief of stresses, and, in the bcc and hexagonal close-packed metals may result in significant amounts of plastic flow. Secondly, there is the possibility that twins may act as barriers for dislocation movement, resulting in pile-ups which could nucleate cracks. As might be expected, the bulk of the literature on mechanical twinning in the bcc metals is concerned with iron. A good summary of the work done prior to 1954 is contained in the book by all.&apos; Recently the refractory bcc metals have become increasingly important. Limited studies have shown that tantalum,2,3 molybdenum,4,5 vanadium,6,7 tungsten,&apos; and columbium9-11 deform by mechanical twinning under some conditions. Alloys of molybdenum with rhenium and tungsten with rhenium show extensive deformation by twinning at room temperature.I2-l4 Most of these studies have dealt primarily with mechanical properties at low temperatures or have shown the existence of twins, and there is only a small amount of information concerning the conditions under which they form. The subject of the present paper is the formation of twins under stress in columbium with a consideration of their morphology. EXPERIMENTAL PROCEDURE The material used for these studies was taken from an ingot of columbium which had been melted twice by the electron-be am-method. The analysis of the ingot was (in ppm): B < 1, C = 10, Fe < 100, The cast ingot contained very large grains, and it was possible to obtain single-crystal prisms which measured from ¼ to 3/4 in. on a side. A few experiments were conducted on polycrystalline plate which was prepared by rolling material from the same ingot at room temperature and annealing at 1000 in a dynamic vacuum of 10-6 mm Hg. This gave a plate in which the grains had an average diameter of 3 mm. After the specimens were cut from the ingot, the six faces were metallographically polished and elec-tropolished to remove all traces of cold work. Most of the observations were made on the surfaces of the deformed specirllens without further treatment. Occasionally, etching after deformation was desirable. In these cases, an etchant of the composition 50 parts H2O, 5 parts HNO3 25 parts HF, and 10 parts H2SO4 was found to delineate the twins very well. Unless considerable care was taken to ensure the removal of all disturbed metal left by the mechanical polishing, etching failed to reveal many of the features discussed in this; paper. The specimen&apos;s were deformed either by impact or slow compression at 77°K (liquid-nitrogen coolant), 198°K (dry ice and acetone coolant), and 298°K. The impact load was delivered by a hammer except in one case where the load was delivered by a bullet. Slow compression was carried out on a hydraulic testing machine equipped with a chamber to hold the coolant. EXPERIMENTAL RESULTS It has been generally believed that the conditions favoring the formation of deformation twins are large grains, low temperature, and impact loading. In fact, Barrett and Bakish2 found twins in tantalum only after impact deformation at 77°K, and Adams, Roberts, and Smallman10 observed twins in columbium only at 20 For these reasons, the initial experiments of this study used impact loading. Hammer blows caused many bands resembling twins in single crystals a.t 77" but not at 198°K. Only a few slip lines were observed on any of the single-crystal specimens of this study—essentially all the deformation occurred by twinning. The appearance of the twins on the as-deformed surface is shown in Fig. 1. Although both Figs. 1(a) and l(b) are photomicrographs of twins taken at the same magnification and from the same crystal, they are startlingly different in appearance. Fig. 1(a) was taken from the crystal face approximately perpendicular to the shear direction, whereas Fig. 1(b) was taken from

Jan 1, 1962

By C. H. Mathewson, P.W. Bakararian

The greatcr part of the literature on the plastic behavior of magnesium dates back to that active period of research in crystal mechanics immediately following the widespread preparation of isolated metallic crystals large enough for the application of conventional methods of mechanical testing. These investigations, performed on single crystals, revealed an analogy between zinc and magnesium with respect to their fundamental mode of deformation. in the operation of glide and twinning, respectively, on crystallographically similar planes. Mathewson and Phillips (1928)&apos; by geometrical analysis identified the plane in magnesium as the twinning plane. Schiebold and Siebel (1931) confirmed this twinning planc, established the basal plane as the plane of slip, and a digonal axis I as the slip direction. They also rcported twin formation in a secondary role on the {IOI} plane. Schmid (1931)³ summarized and discussed the earlier evidence and presented the results of his own experiments on the effect of temperature and small amounts of soluble elements. From X-ray studies on extended wire single crystals, he concluded that slip along the basal plane in the direction of the digonal axis I closest to the stress direction was the sole slip system operating at atmospheric temperature. This conclusion was based on experiments with crystals of many different orientations relative to the stress axis. Special attention was directed to the basal plane and the digonal axis I, as the plane and direction of greatest atomic density. Determinations of resolved shear stress at the onset of plastic yielding-—i.e., the critical resolved shear stress—were also made; the average of these calculations showing 82.9 grams per sq. mm. This value varied only slightly up to 300°C. at which temperature it was found to decrease to 70.5 grams per sq. mm. The extension of his crystals at temperatures above 225°C. further disclosed the presence of new slip systems. After the origince specimens of circular section had been

Jan 1, 1943

By C. H. Mathewson, P. W. Bakararian

The greatcr part of the literature on the plastic behavior of magnesium dates back to that active period of research in crystal mechanics immediately following the widespread preparation of isolated metallic crystals large enough for the application of conventional methods of mechanical testing. These investigations, performed on single crystals, revealed an analogy between zinc and magnesium with respect to their fundamental mode of deformation. in the operation of glide and twinning, respectively, on crystallographically similar planes. Mathewson and Phillips (1928)&apos; by geometrical analysis identified the plane in magnesium as the twinning plane. Schiebold and Siebel (1931) confirmed this twinning planc, established the basal plane as the plane of slip, and a digonal axis I as the slip direction. They also rcported twin formation in a secondary role on the {IOI} plane. Schmid (1931)³ summarized and discussed the earlier evidence and presented the results of his own experiments on the effect of temperature and small amounts of soluble elements. From X-ray studies on extended wire single crystals, he concluded that slip along the basal plane in the direction of the digonal axis I closest to the stress direction was the sole slip system operating at atmospheric temperature. This conclusion was based on experiments with crystals of many different orientations relative to the stress axis. Special attention was directed to the basal plane and the digonal axis I, as the plane and direction of greatest atomic density. Determinations of resolved shear stress at the onset of plastic yielding-—i.e., the critical resolved shear stress—were also made; the average of these calculations showing 82.9 grams per sq. mm. This value varied only slightly up to 300°C. at which temperature it was found to decrease to 70.5 grams per sq. mm. The extension of his crystals at temperatures above 225°C. further disclosed the presence of new slip systems. After the origince specimens of circular section had been

Jan 1, 1943

By D. Torrey

Considering the two great interests of to-day, in iron upon the one hand and steel upon the other, and recognizing with measurable distinctness the peculiar fitness of each for special services to which they are applied, the proposition to unite the two metals in combination, to bring into simultaneous use the peculiar advantages which each offers, has great attractions. The limited success which has been attained by trying to bring about such combinations of the two metals through the use of fluxes in welding, has led to the general adoption of the opinion that an effective union of the two metals is impracticable, or to the view that if practicable it would have but limited commercial value. Such opinions are, I think, premature and erroneous, and having gained some knowledge of the character and value of the "Wheeler process" for welding iron and steel without the use of fluxes, I submit the following observations and opinions of the matter for your information, with the hope of eliciting such a discussion of the subject as it may require. The principle of the invention is to bring the two metals simultaneously to a welding heat in one pile, and then to manipulate it.

Jan 1, 1879

By Francis H. Crockard

During the past five years we have probably witnessed greater technological advances than in any similar period. Industry and science have steadily marched ahead. The makers of iron and steel products have watched with great interest the development of streamlined trains, faster and safer airplanes, the entirely new science of air-conditioning and the widespread use of stainless steels. Since 1930, we have witnessed the erection of the world&apos;s largest suspension bridge, the largest and fastest ocean liner and the spectacular Boulder Dam, while even greater things are planned in these particular fields. Other industries, too, have been moving ahead rapidly. This advance in a few years has been caused primarily by the fierce competition of the depression. Now, more than ever, is the emphasis placed upon quality and service. Makers of southern merchant pig iron have been no exception and have been confronted with increasingly strict chemical specifications and with much greater stress on physical characteristics than ever before. For example, sulfur in the iron must be held very low, competition demanding that it be in the 0.020&apos;s and low 0.030&apos;s; silicon content must be held within a very narrow range, and definite requirements of phosphorus and manganese are an essential part of the specifications. Physical characteristics are becoming of increasingly greater importance. The introduction of triple-skimmed, slow-cooled iron several years ago was the first step in this direction. Now there are a few customers who buy iron by chemical analysis and physical appearance, having found that the analysis alone is an insufficient guide to their requirements. In addition to questions of quality, the subject of cost has greatly altered the southern furnaceman&apos;s viewpoint on many things. Formerly we had low-grade but cheap raw materials, but recent developments, such as greatly increased labor rates, have raised the cost of the same

Jan 1, 1936

By Francis H. Crockard

During the past five years we have probably witnessed greater technological advances than in any similar period. Industry and science have steadily marched ahead. The makers of iron and steel products have watched with great interest the development of streamlined trains, faster and safer airplanes, the entirely new science of air-conditioning and the widespread use of stainless steels. Since 1930, we have witnessed the erection of the world&apos;s largest suspension bridge, the largest and fastest ocean liner and the spectacular Boulder Dam, while even greater things are planned in these particular fields. Other industries, too, have been moving ahead rapidly. This advance in a few years has been caused primarily by the fierce competition of the depression. Now, more than ever, is the emphasis placed upon quality and service. Makers of southern merchant pig iron have been no exception and have been confronted with increasingly strict chemical specifications and with much greater stress on physical characteristics than ever before. For example, sulfur in the iron must be held very low, competition demanding that it be in the 0.020&apos;s and low 0.030&apos;s; silicon content must be held within a very narrow range, and definite requirements of phosphorus and manganese are an essential part of the specifications. Physical characteristics are becoming of increasingly greater importance. The introduction of triple-skimmed, slow-cooled iron several years ago was the first step in this direction. Now there are a few customers who buy iron by chemical analysis and physical appearance, having found that the analysis alone is an insufficient guide to their requirements. In addition to questions of quality, the subject of cost has greatly altered the southern furnaceman&apos;s viewpoint on many things. Formerly we had low-grade but cheap raw materials, but recent developments, such as greatly increased labor rates, have raised the cost of the same

Jan 1, 1936

By Donald W. Scott

THE year just ended was the 50th anniversary of that first flight at Kittyhawk, N. C., in 1903. In this 50-year period the aviation industry made startling developments from flight distances of 120 ft-at snail&apos;s pace-to speeds of over 1300 mph and flights that circle the globe. And 1953 also was the 50th anniversary of the Utah Copper Co., the Father of our mass production porphyry copper ventures. How do developments in the mining industry stack up with the aviation industry? The mineral industry can be as proud of developments over the past 50 years as the aviation industry. Only for the developments of the mineral industry could aviation and other allied industries advance as they have. The year 1953 made its contribution to this progress, with the normal number of process and equipment developments and an abnormally high amount of activity in new plant capacity, particularly copper. Tonnages are on the increase and operating troubles are becoming more and more problems in materials handling and control. We&apos;re approaching molecular dissemination of ores with hydro and pyro methods coming to the front to take over where flotation leaves off.

Jan 2, 1954

By P. E. Rider, K. A. Gschneidner, O. D. McMasters

The solid solubilities for thirteen rare-earth metals in gold were determined by using the X-ray parametric method. Solubilities ranged from 0.1 at. pct for lanthanum in gold up to 8.8 at. pct for scandium in gold. The solubilities from lanthanum to gadolinium were very small and essentially constant, but a sharp increase occurred from gadolinium to scandium. The large solubilities for the heavy rare-earth metals were not expected because of the large size and electrochemical differences between rare-earth atoms and the gold atom. Contributions from first- and second-order elasticity theory plus an electronic contribution were found to reasonably account for a more favorable size factor. Electron transfer from the rare-earth metal to the gold Is thought to occur such that the resultant rare-earth and gold electronegativities are favorable for solid-solution formation. It was also found that this mutual adjustment of size and electronegutivity does not occur if the pure-metal size factors are greater than a critical value of 25 pet. The eutectic temperatures for ten systems were determined and these remained fairly constant at approximately 809 "C for the lighter lanthanide metal-gold systems until the Er-Au system was reached, at which Point the eutectic temperature successively increased reaching a maximum of 1040°C in the Sc-Au system. This rise was correlated to the size factor becoming more favorable for solid-solution formation at erbium. The valence state of ytterbium was found to change from two in the pure metal to three when ytterbium is dissolved in the gold matrix. RECENT results1 reported concerning the solubility of holmium in copper, silver, and gold, showed that the solubility of holmium in gold was quite large, 4.0 at. pct, compared with 1.6 in silver and 0.02 in copper. The small solubilities of holmium in silver and copper are quite reasonable in view of the large size difference (22.2 and 38.2 pct, respectively), large electronegativity difference (0.59 for both systems), and possible unfavorable valency factor (assuming one for silver and copper and three for holmium). The large solubility in gold, however, is unexpected because these same factors are also unfavorable for holmium and gold (22.5 pct size difference and 0.69 electronegativity difference), and because the light rare-earth metals, lanthanum, cerium, and praseodymium, have negligible solid solubilities in gold.2 In view of this unexpected behavior, it was felt that a study of the solid solubilities of most of the rare-earth metals in gold would be desirable to better understand the factors involved in the formation of solid solutions. Of the rare-earth metals added to gold in this study, only ytterbium is divalent in the pure metallic state (the other rare-earth metals are all trivalent) and many of its physical properties (such as the metallic radius, electronegativity, and so forth) are much different from those of the normal trivalent rare-earth metals.&apos; The properties of ytterbium are such that one would expect solid-solution formation to be less favorable for ytterbium in gold than for any of the normal trivalent rare-earth metals. But chemically ytterbium is known to possess a stable trivalent state, and it is quite possible that ytterbium may alloy as a trivalent metal under certain conditions rather than as a divalent metal. Because of the dual valency nature and because so little is known about the alloying behavior of ytterbium, the gold-rich ytterbium-gold alloys are of special interest. EXPERIMENTAL PROCEDURE Materials. The gold used in this investigation had a purity of 99.99 pct with respect to nongaseous impurities. In general the rare-earth metals were prepared by reduction of the corresponding fluoride by calcium metal.3 The impurity contents of the metals used in this study are given in Table I. Preparation of Alloys. Two- or 3-g alloy samples were prepared by arc melting. The samples, with the exception of some of the Er-Au alloys, had weight losses of 0.5 pct or less. All alloy concentrations noted in this paper are nominal compositions. After arc melting, the alloys were wrapped in tantalum foil, sealed off in quartz tubing under a partial atmosphere of argon, homogenized for approximately 200 hr at 780°C, and then quenched in cold water. X-Ray Methods. The X-ray parametric method was used in determining the solubility of the rare-earth metals in gold. filings were sealed in small tantalum tubes by welding under a helium atmosphere. The tantalum tubes were then sealed in quartz tubing under a partial argon atmosphere, and annealed for times ranging from 1/2 to 3 hr (the length of time was inversely proportional to the an-

Jan 1, 1965

By L. W. Pommier, F. B. Brien, A. K. Bhasin

The diflerential movement of solid particles through solid-liquid suspensions is very important to many branches of engineering. The flow of suspensions around immersed bodies is mainly of a turbulent nature. Problems are encountered when attempts are made, as is the general practice, to extrapolate the velocity and resistance relationships of Newton, pertaining to Newtonian systems, into non-Newtonian solid-liquid suspensions. The conventional velocity and resistance relationships for turbulent flow in fluids when applied to suspensions, do not take into consideration the two very important variables: suspension particle size and solid volume fraction. A study of the effect of suspension particle size (dgb) on the velocity of falling balls leads to the concept of a critical particle size (dgc) at which the suspensions will be Newtonian. This leads to the classification of static suspensions into two types: suspensions consisting of particle of diameter dgh > dgt, and those with dgh, < dgr. Separate velocity and resistance equations for these two types of suspensions have been proposed, taking into account both the solid particle size and solid volume fraction. The agreement between the velocities predicted from the proposed equations and the measured velocities, confirms their validity. The resistance force offered by suspensions to the movement of immersed bodies has been calculated from the proposed equations, and the effects of suspension particle size and solid volume fraction on the resistance force and velocity have been examined. The movement of immersed bodies in solid-liquid suspensions is of great importance in many areas of engineering such as minerals processing, oil well drilling, suspension flow in pipelines, and hydrometallurgy. A number of mineral dressing processes deal essentially with the movement of solids in suspensions—in particular, classification, thickening, filtration, ore washing, and gravity concentration—thus a study of the fluid characteristics of suspensions is of theoretical and practical interest.&apos; A rigorous analysis of the mechanisms of momentum transport of a solid-liquid system is complex indeed. The rheological properties of the suspensions deviate from those of liquids, varying, for example, with density, solid volume fraction, size and shape of the solid phase of the suspension, and with the density and viscosity of the liquid phase. The flow of suspensions around immersed bodies is mainly of a turbulent nature and hence studies of the turbulent flow characteristics of suspensions are of par- ticular importance. Problems are encountered when attempts are made to extrapolate the velocity and resistance relationships of Newton, pertaining to Newtonian systems, into non-Newtonian solid-liquid suspensions. Due to the numerous variables present in a suspension, certain limitations and assumptions become necessary in order to produce quantitative relationships for predicting their effects. The solid particle size and the solid volume fraction are two of the more important variables. By comparing the measured and calculated Newtonian velocities of falling balls in simple static suspensions, the existing velocity and resistance relationships have been modified to take these variables into account. In order to keep the study less complex, all other variables such as the characteristics of suspending liquid and shape of the particle are maintained constant. Objective The objective of the present investigation is to modify the Newtonian velocity and resistance equations in order to take into account the suspension particle size and solid volume fraction. Theory Liquids are classified on the basis of viscosity, which may be defined as the relationship between applied shear stress and resulting rate of shear.&apos; pure single-phase fluids composed of small light molecules behave as Newtonian liquids, having a single viscosity pa-

Jan 1, 1971

By E. T. Turkdogan, L. S. Darken

Calcium ferrite melts were equilibrated with sulfur and oxygen-bearing gases at temperatures within the range 1290°C to 1620°C. The results show that at oxygen partial pressures below 10-4 atm the sulfide-reaction occurs and at higher oxygen pressures the sulfur dissolves in the melt principally as sulfate ion. It is also observed that when the product increases, sulfate ions are converted to pyrosulfate ions and the results permit the evaluation of the pyrosulfate/sulfate ratio. It is shown that the ratio y CaSO,/rCaO increases with decreasing concentration of calcium oxide in calcium ferrite, silicate and aluminate melts. Indications are that oxy-acids, e.g. silica, alumina and ferric oxide, increase yCaS0,. A few experiments were carried out within the sul-tide range and the results are in accord with those obtained by other investigators on aluminate and silicate melts. BECAUSE of the industrial importance and theoretical interest, many investigators have studied the reactions between molten oxides, silicates or alumi-nates, and gases containing oxygen and sulfur. The early work reviewed by Schenckl and studies made by Bardenheuer and Geller2 indicates that solution of gaseous sulfur in an oxide melt resulted in the replacement of the oxide ions by the sulfide ions. Measurements made by Grant and Chipman3 on the equilibrium partition of sulfur between molten iron and complex silicate melts also demonstrated that, for a given temperature and silicate composition, the distribution of sulfur between slag and metal increased with decreasing oxygen content of the metal. Fincham and Richardson4 studied the effects of temperature and partial pressures of sulfur and oxygen on the solubility of sulfur in simple silicate and alumino-silicate melts. They observed that at oxygen partial pressures below about 10-5 atm sulfur in the gas dissolved in the melt as sulfide ions, replacing an equal number of oxide ions of the melt. At oxygen partial pressures higher than 10-3 atm, sulfur entered the melt as sulfate ions. Similar studies were made by St. Pierre and Chipman5 using calcium ferrite and calcium silico-ferrite melts. The experimental data presented in this paper were obtained in this Laboratory about 10 years ago; this is the first formal presentation although a preliminary report was given previously.6 In each of these experiments, a pure synthetic CaO-Fe2O3 melt in a platinum crucible was equilibrated with a gas mixture (SO2-O2, SO,-air, SO2-CO, or SO2-CO2-CO) at a temperature ranging from 1296°to 1620°C. The experimental technique was essentially the same as that reported by Darken and Gurry,7 the main difference being that the atmosphere in the reaction chamber contained sulfur dioxide together with oxygen, or carbon dioxide-carbon monoxide

Jan 1, 1962

By G. S. Brooks

The tendency of the oxides of such metals as aluminum, zinc, chromium, and calcium to form compounds at high tempera tures with iron oxide is well established by past investigation. Data of this reaction, as developed in laboratory research, have been contributed by Burleigh, Hofman, and Wells, in America, and by many others abroad. A partial bibliography of the subject is appended. From these authorities we learn that the ferric oxide here has the function of an acid, giving in the case of ZnO a zinc ferrite, with a normal composition of ZnOFe2O3 This formation of zinc ferrite particularly affects the success of such processes as leaching or magnetic separation, and thus becomes practically important to the metallurgist. But the meager existing data do not entirely agree; and quantitative results from muffle-practice are conspicuously absent. Furthermore, it being of some general importance to the zinc smelter in both roasting and reduction, the following few notes of operations oil a commercial scale are contributed: I. Physical Properties of Zinc Ferrite. As formed for the most part synthetically by investigators, zinc ferrite exhibits characteristic physical properties, such as octahedral crystals, dark color, and a density over 5, together with a slight magnetic attractability. In examining with the microscope many products of mechanical muffle-roasting kilns, it is, however, impossible to find individual grains which can be identified as consisting entirely of zinc ferrite. The variety of colors, especially where each grain of blende was mechanically free from marcasite, rather conveys the impression of a partial ferritization of the grain. One side or end, for example, may often have the hard, dense surface and dark red to black color of the ferrite, while the balance shows the usual light yellowish brown of a normal iron-free blende.

Jan 1, 1914

By Arthur F. Taggart, A. W. Thomas, T.C. Fitt

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943

By Arthur F. Taggart, T. C. Fitt, A. W. Thomas

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943