By Benny J. Nelson

To obtain information on the effect of gallium upon the corrosion of magnesium alloys, tests were made on the commercial alloy AM52S (Mg-3 pct Al-1 pct Zn-0.2 pct Mn) and experimental

Jan 1, 1957

By Nicholas J. Grant, H. C. Chang

Microscopic observations during creep tests were made on AI-20 pet Zn, 80 pet Ni-20 pet Cr, and 25 and 3S aluminum specimens. All these materials failed in an inter-crystalline manner under certain stress and temperature conditions. Particular atten-tion was given to the initiation and propagation of intercrystalline cracks in coarsegrained AI-20 pct Zn specimens. The geometry of the grains and grain boundaries in these specimens was known before the tests. On the basis of the observations and a knowledge of the interaction between grains and grain boundaries, a mechanism of intercrystalline fracture and propagation of the fracture has been proposed. METAL, and alloy fracture occurs essentially in two ways: transcrystalline and intemrystalline. In the past most of the work done in this field was centered on the determination of stress criteria for fracture. The specimens used for these studies were tested under varying conditions of stress state, temperature, and strain rate. Unfortunately, very little attention was given to the initiation and propagation of the fracture, whereas the nature of fracture was examined closely only after failure. Several extensive reviews of these studies have been published by Orowan, Smith, Barrett, and Petch.1, 4 It is well known that a material which exhibits a ductile and transcrystalline fracture can be made to exhibit a brittle and intercrystalline fracture by modifying its composition and by heat treatment. This modification may or may not result in microscopically observable precipitation in the grain boundaries." In the creep of any one alloy the transition of transcrystalline to intercrystalline fracture is a function of stress, strain rate, and temperature." The tendency for intercrystalline fracture to occur increases as the strain rate decreases and the testing temperature increases. Extensive work on high purity aluminum (99.995 pet) under creep conditions showed the importance of the interaction between grains and grain boundaries, and the different responses of grain and grain boundaries to the variables: stress, strain rate, and temperature.7, 8 It was also shown that grain boundary deformation necessarily has to be accommodated in the grains by various deformation means as. for example, fold formation. The type of fracture resulting from the creep of high purity aluminum was invariably found to be transcrystalline. On the other hand, 2S and 3s aluminum were, under certain conditions, found to fracture in an intercrystalline manner." One reason given for this was that the grains could accommodate to a lesser extent the deformation of the grain boundaries.19 It was decided to examine this line of reasoning in greater detail and to investigate the particular interactions between grains and grain boundaries that result in the incidence and progression of inter-ct,ystalline fracture. It is also the purpose of this paper to show where and how intercrystalline cracks start and how they propagate to result in fracture. Several alloys—Al-20 pct Zn, 80 pet Ni-20 pet Cr, 2S and 3s aluminum-— were used for this study, but attention was paid mainly to the behavior of an A1-20 pet Zn alloy, since its general creep behavior has been established." From the results of this study a mechanism of intercrystalline fracture is proposed. Experimental Procedure The experimental procedure was similar to that used in previous work and has been detailed elsewhere.' Two parallel flat surfaces were milled from an originally round specimen, giving a gage portion which was 1x0.09X0.17 in. Some round specimens, 1/4 in. round by 1 in., were also tested. The A1-20 pet Zn specimens. which were annealed at 1030°F for 24 hr, showed two to four grains across the width of the test bar, and most of the grains occupied the whole thickness of the specimenu. Before some of the specimens were subjected to creep, the grain arrangement was mapped out in a development drawing, Fig. 1. The initiation and

Jan 1, 1957

By M. R. J. Wyllie, F. Morgan, P. F. Fulton

The importance of formation factor, F, not only in electric logging but as a fundamental rock parameter has recently been stressed.',: The desirability of investigating the range of variation of the resistivity index exponent, n, in the relationship I = S ;", where I is the resistivity index and Sw the water saturation as a fraction of the void volume of a porous medium, has also been urged.3 The magnitude and variation of n with saturation and rock texture is a subject not only of theoretical interest but also one of prime importance in the interpretation of electric logs. A simple technique has recently been developed which enables both F and u to he measured with high accuracy and which may also find acceptance as a convenient method for the determination of irreducible saturation attainment in the restored state method of core analysis. Experience has taught that reproducible measurements of F are possible only if the resistance measuring electrodes are so arranged with respect to a plane face on a porous medium that they are able to make electrical contact with substantially all entry pores in that plane. In practice this may be achieved by using a platinized-platinum gauze electrode backed by some absorbent material (such as felt) which has been saturated with a fluid identical with that used to saturate the porous medium. Applicatiorl of pressure to the electrode and absorbent material then forces the gauze against the plane face of the porous medium and simultaneously squeezes saline solution through the meshes of the gauze. By this means the electrode is in continuous aqueous contact with all pores and satisfactory and reproducible low resistance contact with the porous medium is achieved. Clearly this method, although satisfactory for measurements of F, cannot be applied to the making of continuous resistance measurements on a porous medium while capillary pressure desaturation is being carried out. However, accepting the principle that for satisfactory results electrical contact must be made between a measuring electrode and all pores adja- cent to that electrude, methods of bringing electrodes into intimate contact with the surfaces of porous media were investigated. Two methods were ultimately found to be satisfactory: in the one, the metal electrode is formed on the required portion of the porous medium by the use of a metal spray gun, while in the second the electrode is painted on with an ordinary camel's hair brush. The first method has the advantage of permitting the use of any metal which can be sprayed, but has the disadvantage of requiring rather elaborate and expensive equipment. The second method is presently limited to silver electrodes although in principle other metals, e.g. platinum or gold, could be used. Moreover, the method is so simple and cheap, and has been found to be so satisfactory that it will be described in some detail. The core being investigated is cut into a right circular cylinder and is extracted and dried in the usual manner. The ends are then lightly painted with silver conducting paint* of the type used in printed electrical circuits. The quantity of paint used is not critical but the recommended, minimum compatible with entirely coating the core ends is recommended, particularly on the end that contacts the barrier. The core is then dried at atmospheric temperature for one hour or for shorter periods at any suitable elevated temperature up to about 110°C. It will be found that silver coatings so prepared are not only strongly adherent but also permeable and the core may be the core may be desaturated by the ordinary capillary pressure technique through one of the coated faces. The same permeability is characteristic also of thin metal coatings formed using the spray-gun technique. An ordinary Lucite capillary pressure desaturation cell has been adapted to a form suitable for measuring the resistivity of the saturated silver faced cores both at 100 per cent saturation (i.e., F) and at intermediate saturations down to the irreducible minimum. This has been achieved as follows: A Coors porcelain barrier, having a displacement pressure of c 30 psi was grooved across a diameter. Dimensions of this groove were c 1 mm deep and 1 mm wide at the top. The groove was then painted thickly with silver conducting paint, the paint in the groove being extended lightly over the edges of the groove for a distance of c 1 mm on each side. A 30 gauge silver wire was then arranged in the groove in a form of a spring bow, each end of the silver being held at diamet~ically opposite ends of the groove by means of plastic cement. The arc of the bow at its highest point was arranged to be a millimeter or so above the face of the barrier, while one end of the bow wire was led by means of a pressure-tight connection through the wall of the capillary pressure cell. The groove in the barrier was then Surrounded by suitably cut portions of Kleenex in the conventional manner so as to ensure capillary continuity from core to barrier, and the core placed on the barrier. The weight of the core distorted the silver spring bow and good electrical contact was thereby made between the outside of the cell and the lower painted silver electrode. Electrical connection to tile top painted silver

Jan 1, 1951

By M. R. J. Wyllie, F. Morgan, P. F. Fulton

The importance of formation factor, F, not only in electric logging but as a fundamental rock parameter has recently been stressed.',: The desirability of investigating the range of variation of the resistivity index exponent, n, in the relationship I = S ;", where I is the resistivity index and Sw the water saturation as a fraction of the void volume of a porous medium, has also been urged.3 The magnitude and variation of n with saturation and rock texture is a subject not only of theoretical interest but also one of prime importance in the interpretation of electric logs. A simple technique has recently been developed which enables both F and u to he measured with high accuracy and which may also find acceptance as a convenient method for the determination of irreducible saturation attainment in the restored state method of core analysis. Experience has taught that reproducible measurements of F are possible only if the resistance measuring electrodes are so arranged with respect to a plane face on a porous medium that they are able to make electrical contact with substantially all entry pores in that plane. In practice this may be achieved by using a platinized-platinum gauze electrode backed by some absorbent material (such as felt) which has been saturated with a fluid identical with that used to saturate the porous medium. Applicatiorl of pressure to the electrode and absorbent material then forces the gauze against the plane face of the porous medium and simultaneously squeezes saline solution through the meshes of the gauze. By this means the electrode is in continuous aqueous contact with all pores and satisfactory and reproducible low resistance contact with the porous medium is achieved. Clearly this method, although satisfactory for measurements of F, cannot be applied to the making of continuous resistance measurements on a porous medium while capillary pressure desaturation is being carried out. However, accepting the principle that for satisfactory results electrical contact must be made between a measuring electrode and all pores adja- cent to that electrude, methods of bringing electrodes into intimate contact with the surfaces of porous media were investigated. Two methods were ultimately found to be satisfactory: in the one, the metal electrode is formed on the required portion of the porous medium by the use of a metal spray gun, while in the second the electrode is painted on with an ordinary camel's hair brush. The first method has the advantage of permitting the use of any metal which can be sprayed, but has the disadvantage of requiring rather elaborate and expensive equipment. The second method is presently limited to silver electrodes although in principle other metals, e.g. platinum or gold, could be used. Moreover, the method is so simple and cheap, and has been found to be so satisfactory that it will be described in some detail. The core being investigated is cut into a right circular cylinder and is extracted and dried in the usual manner. The ends are then lightly painted with silver conducting paint* of the type used in printed electrical circuits. The quantity of paint used is not critical but the recommended, minimum compatible with entirely coating the core ends is recommended, particularly on the end that contacts the barrier. The core is then dried at atmospheric temperature for one hour or for shorter periods at any suitable elevated temperature up to about 110°C. It will be found that silver coatings so prepared are not only strongly adherent but also permeable and the core may be the core may be desaturated by the ordinary capillary pressure technique through one of the coated faces. The same permeability is characteristic also of thin metal coatings formed using the spray-gun technique. An ordinary Lucite capillary pressure desaturation cell has been adapted to a form suitable for measuring the resistivity of the saturated silver faced cores both at 100 per cent saturation (i.e., F) and at intermediate saturations down to the irreducible minimum. This has been achieved as follows: A Coors porcelain barrier, having a displacement pressure of c 30 psi was grooved across a diameter. Dimensions of this groove were c 1 mm deep and 1 mm wide at the top. The groove was then painted thickly with silver conducting paint, the paint in the groove being extended lightly over the edges of the groove for a distance of c 1 mm on each side. A 30 gauge silver wire was then arranged in the groove in a form of a spring bow, each end of the silver being held at diamet~ically opposite ends of the groove by means of plastic cement. The arc of the bow at its highest point was arranged to be a millimeter or so above the face of the barrier, while one end of the bow wire was led by means of a pressure-tight connection through the wall of the capillary pressure cell. The groove in the barrier was then Surrounded by suitably cut portions of Kleenex in the conventional manner so as to ensure capillary continuity from core to barrier, and the core placed on the barrier. The weight of the core distorted the silver spring bow and good electrical contact was thereby made between the outside of the cell and the lower painted silver electrode. Electrical connection to tile top painted silver

Jan 1, 1951

By Attilio Ligasacchi

The production of magnetite in copper smelting has been the subject of wide investigation in the past.1-9 It is accepted that most of the magnetite is produced in the converters and returned to the re-verberatory furnace with the converter slag. Part of this magnetite is circulated back to the converters in the matte. As a result, if proper fluxing practice is not followed, and temperatures in the converting process are not strictly controlled, an undesirable circulating load of magnetite may occur. This might ultimately lead to saturation in the reverberatory bath with consequent settling of the magnetite at the furnace bottom. This paper contains the cumulative results of a series of investigations on the formation and control of magnetite presently being conducted by the metallurgical department of the Chino Mines Division of Kennecott Copper Corp. THE METHOD USED FOR THE DETERMINATION OF MAGNETITE AND OTHER MAGNETIC MATERIALS Conventional wet chemical magnetite analyses are neither reproducible nor theoretically sound. These analyses are sensitive to time, temperature, and heating rate-all factors which tend to decrease their accuracy and reproducibility. To overcome the unreliability of the above method, H. W. Mossman1 developed an inductance bridge magnetite "meter" which completely replaces the wet chemical analysis with the advantage of quicker and reproducible results. Fig. 1 is a schematic diagram of the meter in use in the Chino metallurgical laboratory. When a pulverized specimen with magnetic properties is placed in coil A of the inductance bridge circuit, the permeability of the core is increased, causing a voltage drop across the coil. The unbalance is amplified to operate the balancing motor which adjusts the movable iron core in coils C and D to bring the bridge back to balance. An indicator arm connected to the movable iron core indicates directly the percent, or weight, of the magnetic material in the specimen. Coil B acts as a reference coil and a zero adjustment. The meter is standardized with a set of various amounts of -100 mesh pure magnetite crystals (99.8 pet Fe3O4) thoroughly mixed in a test tube with -100 mesh quartz sand. These mixtures are combined with inert transoptic powder and heated to 140° to 160°C (melting point of the powder) and subsequently cooled to room temperature, solidifying the whole mixture, in this manner eliminating any possible preferential orientation of the magnetite grains. In order to determine the effect of the particle size" of the magnetite and other magnetic materials on the meter determinations, five size fractions were obtained by wet screening of the 99.8 pet pure magnetite and several reverberatory matte and slag samples. The following size fractions were investigated: -80 + 100; -100 + 150; -150 + 180; -200 + 250; -250 + 300 and -100 mesh. The deviation of the meter readings for the various sizes of each sample never exceeded ±0.3 pet. This deviation is considered well within the accuracy needed for common smelter operation procedures. Further investigation proved also that grinding slag and matte samples in our laboratory disc grinder normally produced a powder constituted of 95 pet -200 + 300 mesh. For practical purposes a - 100 mesh size was used as standard for our studies. It was also found that for rapid determinations tamping of the sample in the test tube was sufficient and gave comparable results with those samples solidified with transoptic powder. For the purpose of this study we define the magnetite content in copper smelter slags and matte as the equilibrium amount of crystalline Fe3O4 existent in the specimen at a given reference temperature, excluding any secondary magnetite precipitated in the specimen during nonequilibrium conditions. MAGNETITE DETERMINATION IN SLAGS Since it is impossible to ascertain the status of equilibrium of a conventional slag sample, due to

Jan 1, 1965

By H. M. Hobart

This paper deals principally with investigations undertaken by the Welding Research Sub-committee of the Welding Committee of the Emergency Fleet Corporation. The general object of the investigations has been to extend the use of welding in the construction of merchant ships and, specifically, to provide a definite basis for obtaining the greatest economy and efficiency in employing welding in place of riveting in the construction of the hulls of such ships. Composition of_ Ship-plate Steel The chemical composition of the steel employed in such hull construction varies with the thickness of the plates. Through the courtesy of Mr. H. Jasper Cox, of Lloyd's Register of Shipping, the following information may be given concerning the kind of steel plate employed in American shipyards in 1918 for the hull construction of merchant ships. Lloyd's requirements do not relate to the chemical composition. They require a tensile strength of 58,000 lb. per sq. in. (40.75 kg. per sq. mm.) for their lower limit and 72,000 lb. per sq. in. (50.59 kg. per sq. mm.) for their upper limit. For the information of the Committee, Lloyd's obtained from their surveyors at various works data of the carbon content, which is as follows: Works Carbon Content for Plates 1/4 In. Thick 1 In. Thick A..................... 0.14 0.23 B..................... 0.14 0.25 C2.................. 0.19 0.25 D................. 0.20 0.30 E Upper limit..... 0.35 Lower limit..... 0 24 0.29 Upper limit,.... 0.25 0.30 Lower limit..... 0.21 0.27 Upper limit..... 0.25 0.35 Lower limit..... 0.22 0.28

Jan 1, 1920

By Manuel Eissler

The material presented in this paper is an abstract of a thesis submitted by the writer to the faculty of the Massachusetts Institute of Technology, as part requirement for the degree of Master of Science. The investigation was undertaken at the suggestion of Prof. H. 0. Hofman, and it was conducted, under his direction, in the laboratories of the Mining Department of the Institute. The purpose of the work was, first, to study some of the reactions that have been considered as a part of the mechanism of the chloridiz-ing roast, and second, to study the conditions under which nickel oxide and copper oxide may be chloridized. While the production of chlorine gas by various reactions during the chloridizing roast may not be primarily useful in the chloridation of metal oxides and compounds, it nevertheless serves a useful purpose in preventing the dissociation and decomposition of chlorides once they have been formed; for example, the dissociation of cupric chloride into cuprous chloride and chlorine. Therefore it was thought that a study of some chlorine-producing reactions would prove of interest, and the first series of experiments dealt with this phase of the subject. he object of the latter part of the work was to show the possibility of treating heavy sulphide ores, such as those of Sudbury, Ontario, containing much iron and small amounts of copper and nickel, by chloridizing and removing the copper, leaving an iron-nickel oxide product suitable for smelting in the blast furnace for nickel-bearing pig iron. The chloridizing of the copper would, of course, be preceded by a roast for the removal of sulphur, the sulphur oxides being available for the manufacture of sulphuric acid, if under the local conditions this product would be of commercial value. Reactions of the Chloridizing Roast Reaction of Sodium Chloride, Sulphur Trioxide, and Oxygen.—The first reaction studied was that involving the production of chlorine

Jan 1, 1915

By D. Harker, W. E. Seymour

CERTAIN alloys of iron and nickel, when rolled and annealed, possess a preferred crystal orientation: (001) in the rolling plane and [loo] in the rolling direction, when recrystallized at 850" to 1050°C after approximately 98 pct cold reduction. Since the preferred orientation makes a direction of easiest magnetization coincide with the rolling direction, these alloys, especially a 50 pct iron in nickel alloy, have found wide application in the electrical industry' for choke coils and special types of transformers. The rate of the recrystallization reaction was studied at temperatures ranging from 500° to 600°C. The heat of activation for the reaction was calculated from the observed rates, and crystal orientation determinations were made before and after re-crystallization. A vacuum melted iron-nickel alloy* analyzing 49.6 pct nickel, 0.018 pct carbon, and 0.30 pct manganese was used for the experiments. The alloy was cold-rolled 98 pct into strips 1/2 in. wide by 0.002 in. thick. Specimens 1 in. long were sealed under a vacuum (approximately 10-8 mm Hg) in 1/2 in. ID pyrex glass tubes. For heat treatment these tubes were fastened to Nicrohm wires and submerged in a molten salt bath controlled to ±2°C. (The maximum measurement error was within 3°C.) The time at temperature was varied logarithmically from one sample to another, and runs were made at 500°, 525", 550" and 575°C. A molten lead bath was used for a run at 600°C which was controlled to the same accuracy. To determine the extent of recrystallization after a particular time at a given temperature, a method was used suggested by the work of Decker, Asp, and Harker.3,4 This method employs an X-ray spectrometer whereby X rays are diffracted from crystallites whose diffracting atom planes are parallel to the rolling plane of the specimen. The intensities of the diffracted rays are measured by a Geiger counter. The counter can be rotated through a range of angle, and can be motor driven through this range at a speed of 2" per min. The measured intensities are plotted vs. angle by a potentiometer recorder. In a 50 pct iron-nickel alloy it was found that only (200) reflections were obtained from the rolling plane with recrystallized material, and that only (220) reflections were obtained from the rolling plane with unrecrystallized material. No other reflections were obtained under these conditions over a range of Bragg angle of 0 to 45" using either type of specimen. As a consequence, the intensity of the (200) reflections from the rolling plane was taken to indicate the amount of recrystallized ma-terial present in a specimen, and the corresponding intensity of the (220) reflections was taken to indicate the amount of unrecrystallized material present. To insure flatness and proper alignment of the reflecting specimen in the spectrometer, the sample was laid in a slot 1/2 in. wide x 0.001 in. deep which was machined in a 3/4x2x1/2 in. steel carrier. The specimen then was taped down with cellophane tape. This steel cradle was mounted vertically in the specimen holder of the spectrometer so that the bottom edge of the carrier rested against a horizontal shoulder. Intensity data used in plotting the percent of recrystallized material vs. time at temperature were obtained by directly counting the diffracted beam of nickel filtered copper Ka radiation used throughout the work. The X-ray spectrometer was employed also in obtaining pole figure data to be used for orientation determinations. At the beginning of this investigation a transmission pole figure holder was used." As a thickness of 0.002 in. of this alloy was found to be opaque to the copper Ka radiation, it was necessary to reduce the thickness of the pole figure specimen. A cold-worked sample was etched in a 50 pct HCl solution for 5 min and was found to transmit a

Jan 1, 1951

By Hsun Hu

Three single crystal strips of a 3 pct Si-Fe alloy with approximately (110) [001], (210) [001], and (100) [001] orientations were rolled at room temperature to 30, 50, and 70 pct reductions in thickness. Their deformation and annealing textures were studied. In most cases, the change in texture upon recrystallization and subsequent growth can be described as rotations around the <I10 > axes. A < WO > rotational relationship was also observed. The temperature dependence of recrystallization textures was discussed. WhILE considerable data have been published on the rolling and annealing textures in silicon-iron crystals, very little study has been made on the texture formation at various stages of rolling deformation, and during the process of recrystallization. Dunn&apos; in some of his early works had studied the orientation of recrystallized grains in crystals cut out from lightly rolled (10 to 20 pct reduction) large grained sheets. He found that in most cases a third-order twin relationship exists between the crystal and the recrystallized grains. This orientation relationship actually corresponds to rotations around the <110> axes. The more recent studies of Dunn &apos; and of Dunn and Koh &apos;5 on the rolling and annealing textures in various silicon-iron crystals were concerned mostly with a cold-rolling reduction of 70 pct and annealing at 980OC for recrystallization. Reductions of similar magnitude were also employed by Walter and Hibbard in rolling columnar crystal aggregates of a silicon-iron ingot. A systematic study of the effect of rolling reduction on the deforma- tion and annealing textures is still lacking. Regarding the effect of annealing temperature on the texture formation, Dunn3 has observed a change in therecrys-tallization texture by annealing a 70 pct rolled (1 10) [001] crystal first at a low temperature then atahigh temperature. But the details of texture formation during the annealing treatments were not thoroughly investigated. The present investigation was undertaken to study the texture developments at various stages of rolling deformation and of the recrystallization process, so that a better understanding on the texture formation in silicon-iron crystals may be obtained. EXPERIMENTAL PROCEDURE The three single crystals used in the present investigation were selected from the group of single crystal strips previously prepared7 from a high grade commercial Si-Fe alloy with 3 pct Si. The thickness of these single crystal strips was 0.040 in. The orientations of the three crystals as determined by the X-ray back-reflection Laue technique are shown in Table I. Each of the three crystals was rolled at room temperature along the strip direction to 30, 50, and 70

Jan 1, 1962

By A. Hultgren, B. Herrlander

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By B. Herrlander, A. Hultgren

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By D. J. McAdam

In a recent survey of the literature, the author has found evidence incompatible with prevalent views regarding the technical cohesive strength and yield strength of metals. Some of the evidence regarding the technical cohesive strength was presented in a previous paper,21 and views were presented that are believed to be in better accord with the evidence. In that paper, it was shown that the technical cohesion limit (contrary to prevalent views) varies with the combination of principal stresses,t and that the influence of plastic deformation on the technical cohesive strength is not in accordance with prevalent views. In this paper, consideration will be given to both the technical cohesion limit and the yield stress as affected by the combination of principal stresses. Evidence will be presented that the variations of the yield stress and the technical cohesion limit with the combination of principal stresses are not in accordance with prevalent views. Consideration will also be given to ductility and work-hardening capacity, which depend on the initial difference between the technical cohesion limit and the yield stress. By the "technical cohesion limit" is meant the mean stress at actual or poten- tial* fracture. An example of a rechnlcal cohesion limit is the "true" breaking stress of a tension-test specimen, the breaking load divided by the sectional area at fracture. The cohesion limit thus obtained for a ductile metal, however, has been greatly altered by the plastic deformation. It is important to consider the cohesion limit of the metal prior to this deformation, and the variation of the cohesive strength with plastic deformation. The relation between the cohesion limit and the corresponding flow stresst determines the ductility of a metal and the energy that it will absorb before fracture. In this paper, as in the previous paper,21 tensile stresses will be viewed as positive and compressive stresses as negative. The algebraically greatest principal stress will be designated S1, the least principal stress will be designated S3, and the intermediate principal stress will be designated Sz In the previous paper, attention was confined to stress combinations with two of the principal stresses equal (with the intermediate principal stress S2 equal eithel to S3 or 31). In this paper, consideration will also be given to the effect of stress combinations with all three principal stresses unequal. In the earlier sections of the paper (pp. 3I I to 324), attention will be confined to stress combinations with

Jan 1, 1942

By D. J. McAdam

In a recent survey of the literature, the author has found evidence incompatible with prevalent views regarding the technical cohesive strength and yield strength of metals. Some of the evidence regarding the technical cohesive strength was presented in a previous paper,21 and views were presented that are believed to be in better accord with the evidence. In that paper, it was shown that the technical cohesion limit (contrary to prevalent views) varies with the combination of principal stresses,t and that the influence of plastic deformation on the technical cohesive strength is not in accordance with prevalent views. In this paper, consideration will be given to both the technical cohesion limit and the yield stress as affected by the combination of principal stresses. Evidence will be presented that the variations of the yield stress and the technical cohesion limit with the combination of principal stresses are not in accordance with prevalent views. Consideration will also be given to ductility and work-hardening capacity, which depend on the initial difference between the technical cohesion limit and the yield stress. By the "technical cohesion limit" is meant the mean stress at actual or poten- tial* fracture. An example of a rechnlcal cohesion limit is the "true" breaking stress of a tension-test specimen, the breaking load divided by the sectional area at fracture. The cohesion limit thus obtained for a ductile metal, however, has been greatly altered by the plastic deformation. It is important to consider the cohesion limit of the metal prior to this deformation, and the variation of the cohesive strength with plastic deformation. The relation between the cohesion limit and the corresponding flow stresst determines the ductility of a metal and the energy that it will absorb before fracture. In this paper, as in the previous paper,21 tensile stresses will be viewed as positive and compressive stresses as negative. The algebraically greatest principal stress will be designated S1, the least principal stress will be designated S3, and the intermediate principal stress will be designated Sz In the previous paper, attention was confined to stress combinations with two of the principal stresses equal (with the intermediate principal stress S2 equal eithel to S3 or 31). In this paper, consideration will also be given to the effect of stress combinations with all three principal stresses unequal. In the earlier sections of the paper (pp. 3I I to 324), attention will be confined to stress combinations with

Jan 1, 1942

By R. W. Lai, I. Iwasaki

Some physical as well as chemical aspects of the methods of dispersion of various corn starches and their derivatives are investigated and their effects as depressants in anionic silica flotation of iron ores ascertained. The adsorption behavior of starches on hematite and quartz is strongly affected by their molecular sizes as inferred from viscosity measurements. The implication of this behavior on flotation and flocculation is discussed. Mechanical treatment of causticized starch solutions is shown to reduce the starch requirements in flotation appreciably. Starches and starch products have been used as depressants for iron oxides both in amine flotation of siliceous gangue and in soap flotation of activated silica from iron ores. Cooke and his associates1,2,3,4 extensively studied the effects of certain starches and their derivatives in the amine flotation of iron ores at near-neutral pH and found that although most starches were good flocculants for hematite and de- pressed that mineral more or less selectively1,3 they did not flocculate quartz suspensions. Further, that replacement of active groups in corn starch modified its behavior as a flocculant for hematite or quartz suspensions1 and as an iron oxide depressant. Schulz and cooke2 showed that many starches and their derivatives, except aminoethyl starch, were abstracted more effectively by Brazilian hematite than by quartz and that the adsorption of a starch product was strongly dependent on pH and on the presence of calcium ion. In soap flotation of calcium-activated quartz, certain starches and their products have been used to depress iron oxides.5&apos;6 The behavior of these substances in flotation appears at times to be at variance with those previously reported and especially with results obtained in the Mines Experiment Station laboratories. This is attributed, at least in part, to differences in flotation procedure and flowsheets and in the method of preparing the depressant. Most of the investigators referred to above, solubilized the starch products by autoclaving at 120°C. Others have used acid,7 alkali8 or oxidizing agents.9 In view of the limited knowledge of the depressing action of starches and their derivatives in iron ore flotation, particularly in soap flotation of calcium-activated silica at high alkalinity, an extensive study

Jan 1, 1965

By N. C. Fick, R. L. Rickett

DESPITE the large volume of literature on alloys of iron and silicon,1 there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carbon and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in, sheet and strip form, the constitution was determined of a series of commercial silicon steels containing 0.05 to o.08 per cent carbon and 0.20 to 4.31 per cent silicon, over the temperature range 1300° to 2500°F. These alloys were all from regular production heats and of commercial quality. The results of, the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented. MATERIAL AND PROCEDURE All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness-the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. [ ] The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired. range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1946

By T. O. Breitling

Two significant problems In mill design are environmental control and cost reduction. Environmental control is predicted to be 5-10% of total plant costs in some parts of the U.S. Operating and design companies will assign this new "unit operation" a place in the early flow sheets. More advanced environmental control will add to both capital and operating costs, so mill designers will strive to reduce other costs.

Jan 1, 1970

By C. D. Woodward

PRIOR to 1902, the tramming of ore from the stopes to the shafts, in the Butte mines, was done by man or animal power, but the demand for greater tonnage and the need for more improved methods of tramming the ore resulted in the installation of the compressed-air locomotive in a few mines. Some of the objections to animal haulage were thus eliminated, but this locomotive was not generally adopted, because of a number of limiting features. It was superseded by the electric trolley locomotive. The early types of trolley locomotives were not satisfactory from the operators&apos; viewpoint, but. they had many economic advantages and after a number of years, in which improvements were constantly made in the structural details, they became dependable, so that the use of animals for main haulage in the mines has now been practically abandoned. There are now operating in the Butte mines of the Anaconda Copper Mining Co., 185 trolley-type locomotives, each of which has replaced five animals. It cost approximately $50 per month to keep an animal, hence the economies that resulted fully justified the expenditure of electrifying the haulage systems. The haulage conditions in this company&apos;s mines possess many advantageous features that are not always found in underground mine workings. The drifts and crosscuts are large, approximately 5 ft. (1.5 m.) wide by 7 ½ ft. (2.3 m.) high, and have curves of no less than 18 ft. (5.5 m.) radius; and the roadbeds of the drifts and crosscuts have a uniform grade of 0.5 per cent. toward the shaft, or in favor of the loaded trips. In all of the mines, except two, the track gage is 18 in. (45.7 cm.), and all tracks in the main haulageways are laid with 25-lb. (11.3 kg.) rails. The stations at the shaft are large, well-lighted, clean, and cool. The average temperature of ,the stations, however, is about 75° F. (24° C.), while the average temperature in some of the drifts and crosscuts is 92° F. (33.5° C.).

Jan 2, 1922

By Chester A. Fulton

APATITE, the most abundant crystalline phosphate mineral, is found in igneous rocks and probably is the primary origin of all other phosphates, whether mineral or organic. Its chemical formula may be expressed as Ca5(Cl,F) (PO4) 3. The chlorine may be replaced almost entirely by the fluorine. It is found in large or small hexagonal prisms, usually of a vitreous luster and a green or red color, but also violet, white, or yellow. It is found largely as an accessory mineral in granitoid rocks. Its hardness is 4.5 to 5 and its specific gravity is about 3.2. There are many other phosphate minerals-for instance, amblygonite, autonite, collophane, lazulite, monazite, pyromorphite, torbenite, triphylite, turquoise, vivanite, wavellite-with base elements of calcium, magnesium, iron, aluminum, manganese, lead, cerium, lanthanum, lithium, or several of these in combination and with various amounts of water of crystallization. However, these phosphate minerals have but little value save as specimens for mineral collections, the exception perhaps being turquoise. While large deposits of igneous apatite are mined today for the production of fertilizers and chemicals, more than 90 pct of the world phosphate production is derived from secondary apatites, called phosphorites. These calcium (and magnesium, aluminum, and iron) phosphates have been formed in the alteration of sediments by solutions containing phosphoric acid. Such solutions have come from the weathering or leaching of igneous rocks containing apatite, bone deposits of prehistoric animals and marine life, or guano deposits (excreta of birds). These phosphorites are mostly alterations of phosphatic limestones that took place slowly over many years. Whether it is apatite or phosphorite that is being produced, it is known in the trade as "phosphate rock." The sedimentary phosphate deposits are of marine origin. Some, as laid down, were rich in phosphate or have become so by subsequent subaqueous action and have not been further enriched since emergence from the sea. Some were originally phosphatic limestones or marls from which calcium carbonate was dissolved away by waters containing carbon dioxide, in which calcium carbonate is much more soluble than

Jan 1, 1949

By T. S. Fuller

Various phases of the embrittlement of solid copper containing oxygen by the action of reducing gases at high temperatures are familiar to readers of metallurgical literature through the work of many experimenters. In 1900, Heynl recorded observations of copper being heated in hydrogen with the development of fine cracks, the result of the formation of steam within the metal through the action of hydrogen on the copper oxide usually found in copper. Archbutt,2 in 1905, published the results of experiments, showing that all oxygen can be removed from copper by heating to redness, for several hours, in hydrogen. Intercrystalline cracks and extreme brittle-ness developed. Archbutt attributed the brittleness to the reduction of oxides present in the copper. Bengough and Hil1,3 in 1910, encountered the now well-known embrittlement at the outset of their investigation and stated in their paper: It soon became evident that the effect of any heat treatment depended largely on the presence or absence of reducing gases in the atmosphere of the furnace, as well as on its temperature. Hence it became necessary to adopt a somewhat elaborate scheme of heat treatment. The authors found embrittlement in separate experiments due to both hydrogen and carbon monoxide and concluded that: "The gases ruin the alloys after being heated to about 650" C. in their presence." Ruder,4 in 1916, reported the results of a series of experiments made by heating commercial and deoxidized copper in hydrogen, carbon monoxide, carbon dioxide, and steam. In agreement with other writers, he found that copper containing oxygen was made brittle by reducing gases, while the deoxidized metal remained unaffected. In the case of

Jan 1, 1926

By C. E. Wood

THE Blast Furnace Studies Section, Metallurgical Division, Bureau of Mines, has been working for several years on the mechanism of desulphurization of iron and steel by slags. The usual assumption that desulphurization takes place by diffusion of FeS from metal into slag and subsequent reaction of this FeS with CaO to produce CaS has seemed to us inconsistent with a number of experimental results we have obtained. We undertook, for example, to determine the proportion of sulphur in a slag present as FeS. An entirely satisfactory method of doing this has not yet been evolved. The results of extraction with metallic antimony led to an interesting conclusion, however. FeS is readily soluble in metallic antimony, either physically or by chemical reaction. On the other hand, CaS was found to be insoluble. Hence it would appear that by rapid extraction of the slag with antimony we might expect to determine the distribution of sulphur between iron and calcium. The results showed that much of the sulphur was present as FeS. In some instances the extraction of sulphur as FeS was almost quantitative. For example, in a slag containing 3.8 grams Fe and 3.7 grams S, extraction removed 1.18 grams S and 2.12 grams Fe. If all the iron present in the antimony had been FeS, 1.21 grams S would have been extracted. In another slag with 8.6 grams Fe and 0.06 gram S present, 0.14 gram Fe and 0.08 gram S were extracted. This was obviously extraction of sulphur as FeS within the analytical error and showed that FeS was present either in solution or as a dispersion. Attempts to determine the solubility of FeS and CaS in slag by quenching and ultramicroscopic investigation have indicated that the solubility of FeS is very low, and that reactions in the slag are probably not to be considered as homogeneous. A more detailed report on these theoretical considerations will be made at a later date.

Jan 1, 1939