"In order to produce high quality metalized products and prevent from burden cohesion during pre-reduction, self-fluxed pellets were made for COREX process in the paper. The effects of reduction temperature and reducing gas composition on pre-reduction behaviors of self-fluxed pellets are studied. The results show that the prereduced pellets have poor quality and deposited carbon appears when the reduction temperature is between 600°C and 700°C. The metallization rate, reduction degree and compressive strength of prereduced pellets are promoted by the elevating reduction temperature and mole fraction of H2. Pellets reduced by pure H2 at 800°C have high metallization rate (96.2%), reduction degree (99.4%) and compressive strength (960N/pellet). In all tests, self-fluxed pellets display normal swelling (RSI<l5%) behavior which reveals that self-fluxed pellets are suitable for COREX process. Increasing reduction temperature and mole fraction ofH2 in reducing gas is benefit for pre-reduction of pellets.IntroductionCompared with Blast Furnace, the COREX process has advantages of short flow sheet, using non-coke coal and high-energy utilization. Acidic pellets and lump ores are the chief iron- bearing burden for COREX process which could lead to low melting point substance appearing in per-reduction process. In addition, the acidic hematite pellets tend to swell during the reduction [1-3]. This will result in decreasing compressive strength of pellets, burden cohesion, bad air permeability and poor work status in shaft furnace. Adding carbonate flux could restrain burden bonding to some extent in actual production, but decomposition of carbonate flux increases energy consumption. Worse still, weak reduction potential is unfavorable to iron material reduction [ 4, 5]."

Jan 1, 2013

By Zhihe Dou, Yan Li, Qiuyue Zhao, Guozhi Lv, Yan Liu, Hongliang Zhao

"Abstract: How to reduce carbon dioxide emissions has become a vexing problem, meanwhile, there exist high energy consumption and low efficiency problems in the existing CO2 capture and storage technologies. For CO2 comprehensive Utilization, this paper researches a new technology of absorbing the CO2 emission with high alkaline calcium or high alkaline wastewater sludge mineralization of calcium and invent a core device for multi-level jet carbonation. The industrial test has been carried out in China Xinyu slag Engineering Co., Ltd. The wastewater flow is 150m3/h in the pilot scale. The prepared calcium carbonate has a whiteness greater than 90%, particle size less than 150nm. The mineralization of aluminum exhaust with waste carbide indicates that the CO2 absorption rate is greater than 99.0%, CO2 concentration in the exhaust gas is lower than 0.08%, the purity of mineralized calcium carbonate is greater than 99.0% and particle size is less than 100 nm.InstructionAccording to the statistic data from IEA (2009), the carbon dioxide discharge from fossil fuel consumption in China has exceeded it in the US by the year of 2007, China, has become the largest emitter of carbon dioxide all over the world. Meanwhile, the economic scale is still on an increasing trend in the next 50-100 years, leading to a continuous increment in carbon dioxide discharge. According to the international energy agency forecasts, the energy-relative CO2 discharge in China will rise to 11,615 million tons, 91.3% higher than it in 2007. In the year of 2012, the CO2 gross discharge has reached 10,000 million tons, obviously higher than the predicted value. It is a tremendous task to reduce the emission. Non-ferrous metals industry is one of the largest emitters of carbon dioxide among the industrial circle, the whole industry might discharge a huge amount of carbon dioxide (over 600 million tons), in which the electrolytic aluminum industry is the largest energy consuming industry and CO2 emitter. At present, the CO2 discharge has focused by the whole world due to the environmental problems it causes; meanwhile, supplement of new carbon source is needed due to the exhausting oil and coal resources, so that various countries in the world are attaching importance of the recycle and purification of CO2. Many countries are studying on the cyclic utilization of carbon dioxide. Gas CO2 is mainly applied in chemical, pharmaceutical raw materials, beverage filling agent, refrigerant, inert medium, solvents, pressure source, the welding protective gas, antioxidant and fire extinguishing agent, etc. Solid CO2 is mainly applied in penicillin production, fish, cream, ice cream and other food storage and transportation at low temperature, etc. nowadays, such methods as absorption method, membrane separation, adsorption, etc. are widely used to recycle CO2, with such problems as high investment cost and technical constraints etc."

Jan 1, 2014

By Y. A. Chang

The objective of the present study is to evaluate and compile the relevant phase equilibria and thermodynamic data reported in the literature for the ternary system Cu-Fe-S. It is hoped that the results presented here will be useful to practising engineers and scientists in industry who are attempting to improve continually the existing processes of copper extraction and refining. At the same time, the present work will undoubtedly reveal the lack of some basic data which are important for the improvement of our existing extractive processes. Lastly, this work will also show that the development of theoretical models for the alloy phases in the Cu-Fe-S system is essential before complete consistency between the phase equilibria and the thermodynamic data can be achieved.

Jan 1, 1976

By R. W. Adams

A new process has been developed for leaching zinc sulphide concentrates at atmospheric pressure using air or oxygen plus nitrogen dioxide in dissolved or gaseous form as? an oxygen carrier. The process is flexible and can cope with variations in the degrees of retention and regeneration of dissolved nitrogen dioxide in the leaching phase. By controlled addition of concentrate a leach solution with low residual nitrate concentration can be produced. Following separation by filtration of unleached solids and elementa1 sulphur and conventional oxidation/precipitation of dissolved iron, the leach liquor can be treated with metallic zinc to remove the remaining nitrate and other meta111c impurities such as copper, cadmium and cobalt to provide a solution suitable for electrolytic recovery of zinc. Pilot scale testing of the process .has given zinc recoveries in the high nlnet1es, production of a hi.gh grade jarosite-free Pb/Ag residue (50% Pb.) and a saleable high grade of elemental sulphur. .A wide range of concentrates can be treated containing substantial levels of lead and copper as well as zinc. Indicative cost estimates suggest that the new process is competitive with alternative procedures such as pressure leaching.

Jan 1, 1990

By Zeng Zheng, Liu Chen, Yu Xing-Fu, Tian Su-Gui, Zhang Chao

"Single crystal nickel-base superalloy is prepared by using the various withdrawing rates. By measuring creep properties and microstructure observation, the influence of the element segregation on creep properties of the superalloys is investigated. Results show that the dendrite spacing and the segregation extent of the elements decrease with the enhancing withdrawing rate. The superalloy with smaller dendrite spacing has lower segregation of the elements and better creep resistance. The dislocations climbing over the rafted y’ phase is thought to be the deformation mechanism of the alloy during steady state creep. In the later stage of creep, the fact that some dislocations shear into the rafted y’ phase may twist the rafted y’ phase. As the creep goes on, the initiation and propagation of the cracks occur up to occurring creep fracture, which is thought to be the fracture mechanism of the superalloy during creep.1. IntroductionSingle crystal nickel-based superalloys consist of high volume fraction of ?? strengthening phase and ? matrix, and possess the excellent high-temperature mechanical and creep properties, therefore, they have become the main material to make the blades of the advanced aeroengines[1-3]. Some literatures report that the temperature-bearing and creep-resistance properties of the single crystal nickel-based superalloys can be remarkably improved as the increases content of the refractory elements, such as W and Re[4-6]."

Jan 1, 2012

By Frame Ritzert, Dennis Keller, Vijay Vasudevan, David Arenas

"An investigation was conducted to describe topologically close packed (TCP) phase instability as' a function of composition in the advanced ·Ni-base superalloy Rene N6. TCP phases are detrimental to overfill high-temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements. Thirty-four variations of polycrystalline .Rene N6 determined from a design-of-experiments approach were cast and homogenized at 13 l5°C for 80 hours followed by exposure at 1093°C for 400 hours to promote TCP formation. The alloys had the following composition ranges in atomic percent: cobalt 10.61 to 16.73, Mo 0.32 to 1.34%, W 1.85 to 2.52%, Re 1.80 to 2.11%, Ta 2.36 to 3.02%, Al 11.90 to 14.75%, and Cr 3.57 to 6.23%. Physical and chemical characteristics of all microstructures obtained were described using various analytical techniques. From these observations, a mathematical description of TCP occurrence (s and P phase) was generated for polycrystalline Rene N6.IntroductionNi-base superalloy single crystals represent the state-of-the-art for turbine engine airfoil application as they offer the best balance of properties to allow for the high operating temperatures required: for efficient engine operation.1 Current trends in alloy design take advantage of improved creep rupture strength with the addition .of higher levels of refractory elements. 2 In .particular, the addition of significantly higher levels of Re in third generation superalloys is key for both microstructural stability and creep rupture strength. 3 While the presence of the refractories is thought to provide strength benefits from solid solution hardening, a tendency for alloy instability in the form of topologically-close-packed (TCP) phases or secondary reaction· zone (SRZ) ·phenomena accompanies the high refractory content. 3 The formation of these phases in sufficient amount is detrimental to the overall high temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements.4 The tendency for a particular composition to form TCP may not be immediately known since the precipitation of TCP phases in Ni-base superalloys is nucleation controlled, thereby requiring long times at elevated temperatures to precipitate. 5 They preferentially nucleate along the octahedral planes of the Ni-base superalloys, usually in areas of refractory metal enrichment at grain boundaries or inside dendrites.5-6 In Rene N6, two closely related TCP phases, a and P, have been observed.2"

Jan 1, 1998

By Dao Su, Ganghua Fu, Xuling Chen, Yufeng Guo, Min Gan, Tao Jiang, Xiaohui Fan

"The sinter quantity and quality of limonite in the magnetite and hematite sintering models were studied and compared. For the sintering of magnetite, the results showed that the increase of limonite improved the permeability of sinter mixture, increased the sinter quantity and quality. The sinter strength and productivity were decreased when the proportion of limonite exceeded 50%. The appropriate proportion of limonite was 40%-50%. For the sintering of hematite, the sinter quantity and quality were first maintained at the same level thereafter declined, more obviously when the proportion of limonite exceeded 40%. The amount of calcium ferrite increased whose shape changed from acicular to leaflike and block gradually with the proportion of limonite increased from 0% to 80%.IntroductionWith the fierce competition of domestic and overseas iron markets in the twenty-first century, cheap ores such as limonite are used to be sintering raw materials to cut the costs of sinter and pig iron for steel making, and boosts the competitiveness of steel companies [1, 2]. In addition, as the reserve volume of hematite of high grade is reducing year by year, the usage amount of limonite in sintering are expanding in major domestic and international sintering plant [3, 4]. Sintering can be divided into two types, majoring in concentrates and fine ores, according to the different types of raw materials. The sintering characteristics of limonite in the two types above have been studied and compared in this paper, which makes a significant sense for the research of limonite sintering properties and guidance of ore proportioning in sintering plants."

Jan 1, 2012

By Mikiya Tanaka, Mikio Kobayashi, Kazuya Koyama, Yoshihiro Nishisu

Preparation of multicomponent powders are very useful and important for producing the materials with complicated and homogeneous structure. Therefore multicomponent powders have a lot of attention in the field of advanced value-added materials. The aqueous processing in hydrometallurgy has a broad potential for producing multicomponent homogeneous precipitates. Furthermore the aqueous processing has a future potential for integrating the separation, precipitation and synthesis processes. In this presentation the precipitation from homogeneous solution including rare-earths and/or common metals is presented. These precipitates probably consist of almost monodispersed, multicomponent and spherical particles by precisely controlling several reaction factors, reaction temperature, concentrations of starting materials, pH and so on. The separation of the nucleation stage and the growth stage of the particles is very important and how to control the reaction factors to realize enough separation is discussed. In this presentation the systems of Y-Eu-0, Y-Fe-0 and Y-Al-0 are mainly presented. In addition the precipitation-stripping method from organic phase is presented focusing the synthesis of multicomponent powders of Ni-La-0 system. These precipitates have multicomponents homogeneously and so they are converted to multicomponent ceramic powders by calcination. They are important compounds as phosphor, opto-magnetic materials, optical materials, hydrogen storage alloy or as the related precursors. In this presentation some characterization of these particulate materials is included.

Jan 1, 1998

By Baptiste Laubie

Agromining is a phytotechnology aiming at producing commercial metal compounds from low-grade ores thanks to hyperaccumulating plants. The fern Dichranopteris dichotoma is a rare earth element (REE) hyperaccumulator, which naturally grows on former mine tailings in China. It accumulates up to 0.35% of REEs in its aerial parts. Different hydrometallurgical processes are currently developed to recover these elements directly from the biomass or from ashes after combustion. The process presented here consists of a direct extraction by EDTA solution, followed by precipitation with acid oxalic. Optimal precipitation pH and influence of organic matter are determined by modelling and by experimental studies. The final solid contains 4.3% of REEs, with calcium as the main cationic impurity (0.45% of the precipitate). The recovery yield is similar for major REEs and is around 70%. After optimization, upscaling of the process will allow the agromining development to recover REEs from secondary resources with more environmentally friendly techniques.

By H. Y. Sohn, S. PalDey

"A new chemical synthesis process for the preparation of intermetallic compounds has been developed. It involves the vapor-phase reduction of mixtures of constituent metal chlorides by magnesium vapor to produce intermetallic compounds in the form of fine powder. The advantages of the process include (a) the use of inexpensive raw materials, (b) low reaction temperatures, and (c) products in the form of fine particles. Titanium and nickel aluminides were prepared by this method. The effect of AlCl/TiCl3 partial pressure ratio on the formation of different titanium aluminides was studied. A two-phase mixture containing 80 mol % of TiAl and 20 mol % of TiA13 formed at an AlC13/TiC13 ratio of 10. The amount of TiA13 was maximized to 72 mol% at an AlC13/TiC13 ratio of 16. The maximum conversion of the limiting chloride TiCl3 was 94 % . In the case of nickel aluminides, NiAI, NiAl3, and Ni2Al3 were formed by reducing mixtures of NiC12 and A1Cl3 vapors. The effect of the partial pressure ratios AlCl3/NiC12 and Mg/NiC12 on the formation of nickel aluminides was studied. The maximum content of NiAl obtained was 98 mol % . At the AlC13/NiC12 ratio of 19, a two-phase mixture of 17 mol% of NiAl and 83 mol% of NiA13 was produced. The product particles were very fine in the size range of 0.05 to 0.2 µm.A. IntroductionIntermetallic compounds are attracting much attention [1]. Titanium and nickel aluminides have attracted a great deal of attention from the aerospace as well as automobile industries because of their potential for high-temperature application (e.g., low density, good oxidation resistance, and high-temperature strength retention [2, 3]). Gamma TiAl and two-phase (TiAl and Ti3Al) alloys [4] are used for gas turbine engine rotational components as well as automobile exhaust valves. TiAl3 is one of the most extensively investigated aluminum-rich intermetallics. Nickel aluminides are attractive because of their low densities, relatively high melting point and good high-temperature strength properties. For example, Ni3Al shows increasing rather than decreasing yield strength with increasing temperature [5]."

Jan 1, 1998

By J. M. Demarthe

MINEMET RECHERCHE (IMETAL Group, formerly Le Nickel-Penarroya-Mokta) has studied on a laboratory scale and patented a new process to recover metal values -copper- from sulphide ores and concentrates. It combines a cupric leaching, solvent extraction and copper sulphate electrowinning according to the main following steps - A direct and selective leaching of copper sulphide ores or concentrates at atmospheric pressure with cupric chloride to form cuprous and ferrous chlorides and elemental sulphur. Pyrite remains in the sulphur residue. - The leach solution is separated into two parts -In the first one, air is injected to precipitate iron as goethite. The oxidation step can be easily realized at atmospheric pressure by maintaining an excess of cuprous and-ferrous chlorides in the liquor. Copper is extracted from the second part as cupric ion by an LIX reagent. Direct injection or air in the mixing chamber maintains good extraction conditions, so that only one mixer settler is required. - Iron, in the form of ferrous ion, is not coextracted. - Copper is stripped from the organic phase, transferred into a sulfuric phase and sent to sulphate electrowinning cells, which are now conventional in copper metallurgy. - Only electricity and air are required. After a feasibility study, the next step will be to develop it on a pilot and commercial scale.

Jan 1, 1976

By George Kazonich

The high costs and environmental problems associated with making iron and steel in the United States is driving the development of new technologies to replace the blast furnace. A prototype reactor incorporating rocket technology was designed and built. This rapid rate reactor was operated successfully and consistently made iron metal. Minus 325-mesh magnetite particles could be reduced to iron metal in less than 50 ms in a high temperature flow through reactor. Iron product was recovered inside the reactor and in a downstream cyclonic separator. The results of typical operation and how parametric changes affected the reduction of iron ore concentrates are discussed.

Jan 1, 1993

By John W. Lund

The Geo-Heat Center has been investigating the utilization of waste silica from the Cerro Prieto geothermal field for several years. The main objectives of the research were to com-bine silica with various additives to (1) form bricks for low cost housing, and (2) to produce a suitable road surfacing material. The various additives that were tested included hydrated lime, portland cement, plastic fibers, asphalt cement and emulsified asphalt. The silica-cement combination produced the strongest bricks and had the best weather resistance, whereas, the silica-lime combination produced the bricks with the lowest thermal conductivity and specific gravity density. The addition of plastic fibers to the silica-lime mixture improved both strength and weather resistance. The combination of asphalt and silica is not suitable as a road surfacing material, however, silica-cement appears promising.

Jan 1, 2006

By John R. Goode

The fist part of this paper comprises a general discussion on refractory gold ores and their mineralogy. Processing methods now in use are reviewed and test procedures for the important methods are discussed. Factors determining the selection of a process are outlined. The paper includes a survey of production plants using pressure oxidation, roasting and biological oxidation to process refractory ore. The status of processes under development is briefly reviewed.

Jan 1, 1993

By Agnes Y. Lee

he U.S. Bureau of Mines developed a method to treat lead-contaminated soil and ebonite battery casing wastes to produce a nonhazardous material. The cleanup procedure involves wet screening to separate a minus 18-mesh soil fraction; removal of metal1ic lead, rocks, wood, etc. ; carbonation to change lead sulfate to acid-soluble lead carbonate; size reduction; acid leaching; and rinsing. The casing wastes undergo size reduction and washing to remove the lead sulfate sludge before carbonation. Similarly, the minus 18-mesh soil is carbonated, then acid leached and rinsed. In leaching, fluosilicic acid (H SiF,) and hydrogen peroxide (H20,) are used to dissolve lead compounds. An electrowinning method is employed to strip lead from the lead-rich leachate. The acid content in the leachate is replenished with fresh H,SiF, acid prior to recycling. Treated casing wastes and soils pass the Toxicity Characteristic Leaching Procedure (TCLP) test and can be reclassified as nonhazardous materia1s. Based on this process, a conceptual pilot plant has been designed which will be demonstrated on wastes from two Superfund sites.

Jan 1, 1993

By Georgios Kolliopoulos

Water is a critical commodity of our generation and a key compound for the chemical and mining industries. Sustainable industrial development is directly associated with the ability to recover clean water from contaminated sources. Forward Osmosis (FO) is a low-energy footprint membrane process allowing the recovery of clean water from high salinity effluent streams. In FO, water is recovered spontaneously into a concentrated draw solution (CDS). Energy is required to separate the recovered water from the resulting dilute draw solution (DDS). In the current work, the fundamentals of the FO process and the most important aspects affecting its performance are discussed. An energy comparison of FO and conventional water recovery technologies is presented. Finally, the opportunities FO presents in the field of hydrometallurgy are analyzed.

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of&apos; about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of 873°K is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composition formed under roasting of concentrates with particle sizes less than 0.02 um (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CuFeSz2 each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forchamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By Tiejun Chun, Jian Pan, Deqing Zhu, Vinicius Mendes

"Fine manganese fines are characterized by large amount and low price compared to lump manganese ores. However, fine manganese must be agglomerated as EAF (electric arc furnace) feed. In this paper, high quality fired pellets were produced by simulating grate-kiln process to supply the feed for EAF from some imported manganese ore fines containing high combined water. Manganese ore fines assaying 44.47wt%Mn, 5.89wt%Fe, 12.09%LOI and with 72.7wt% ranging between 0.5mm and 8mm, are pretreated up to the particle size of 84.7wt% passing 0.074mm by HPGR (high press grinding roller) twice in open circuit. The finely ground manganese fines were mixed with 1.2wt% bentonite, balled at 15% moisture for 7min in disc pelletizer. The drop numbers, compressive strength and thermal shock temperature of green balls reach 11 times/0.5m, 11 N/pellet and 360oC, respectively. After the green balls drying in the oven, the dry pellets were preheated at 1050oC for 12 min and then fired at 1300oC for 12 min in electric tube furnace. The compressive strength of fired pellets reaches 2621 N/pellet. Therefore, these pellets are high quality burden for blast furnace or EAF due to high mechanical strength and high Mn grade of 49.11wt% and low detrimental elements.IntroductionManganese, mainly using as deoxidizing agent, desulfurization agent and alloying elements, is widely used in the steel company. With the rapid development of iron and steel industry in China, domestic manganese ores cannot meet the requirement, resulting large quantities manganese ores import to China [1-4]. Compared to lump manganese ores, fine manganese ores containing high combined water are characterized by large amount and low price. However, they must be agglomerated as EAF (electric arc furnace) feed. There are three ways to agglomerate the manganese fine ores, sintering, briquetting and pelletizing [5-6]. Compared to the other two methods, pelletizing technology possesses the following superiorities, such as uniform size distribution of product, stabilizing chemical composition of product and lower energy consumption in producing. Therefore, pelletizing is a superior way to treat the fine manganese ores [7]. The systematic research of producing manganese oxide pellets by fine manganese ores containing high combined water was studied in this paper."

Jan 1, 2011