Search Documents

By Wei-feng Liu

On the basis of the brief introduction of the gold-antimony concentrate smelting process in China, some problems in the original process were analyzed and the corresponding improvements were introduced in this paper, such as the treatment of antimony matte, the refinement of gold-silver alloy, the concentrating gold from gold-antimony alloy, the treatment of soda slag. The roasting method that was used to treat the antimony matte was transferred to the ore dressing method. The solvent extraction was used to refine the gold-silver alloy instead of the electrolytic method. The technology of selective chlorination leaching under controlling potential was applied to concentrate gold from the gold-antimony alloy and gold-lead alloy instead of the electrolysis method. Soda slag was recovered by the second reducing smelting method substituting for the mixed-salt method of sodium arsenate. After those improvements, the process has been done smoothly; the direct recovery rate of metals has been greatly increased. Meanwhile the procedure

Jan 1, 2008

By Helvio P. G. Santafé Jr., Ruben J. S. Rodriguez, Sergio N. Monteiro, Teresa E. Castillo

"The coir fiber extracted from the husk of the coconut fruits are worldwide available in tropical regions as a low cost lignocellulosic by-product for many applications including composite filler in automobile parts. Possible uses above room temperature require information on the thermal behavior of these coir fiber composites. Therefore, the objective of this work was to perform thermogravimetric, TGA and DTG, analysis on polyester matrix composites incorporated with different volume fractions of coir fiber. In general, it was found that thermal degradation associated with weight loss occurred in three stages. Changes were also observed in the DTG peaks that could be attributed to the coir fiber participation through the decomposition of its lignocellulosic structure.IntroductionThe development of new materials has always been motivated by the need of improved properties. This was the case of modem composites with combination of properties that surpass those of conventional monolithic metallic alloys, ceramic or polymers, from which composites are made. A typical example is the synthetic fiber reinforced composite with specific strength i. e, ultimate stress divided by density, higher than any other monolithic material. Today, however, our global society is concerned with serious environmental problems and thus demanding that new materials be developed with distinct characteristics. They are known as environmentally correct and are expected to be sustainable, which corresponds to the condition of being biodegradable, renewable, recyclable and neutral with respect to C02 emission, considered the main responsible for global warning [1]. Synthetic fiber composites cannot meet these requirements. Consequently, new composite reinforced with cellulose-based natural fiber are being developed [2-8] and are already replacing the synthetic ones in several engineering fields including the automobile industry [9-11]. These composites have additional advantages owing to the lignocellulosic fiber benefits of being diversified, abundant, less expensive, lighter and of societal interest [8]. In some cases even technical advantages such as non-abrasive effect to processing equipments and more flexibility exist in comparison to synthetic fibers."

Jan 1, 2011

By Balasivanadha Prabhu, Prasad P. Shanmugasundaram, Narayani Narasimhan

"The grain refinement and mechanical properties of 6061 aluminium alloy produced by equal channel angular pressing (ECAP) have been analyzed in this present study. A innovative triple shear ECAP die was developed for the processing.It was observed that the grain refinement takes place for greater number of passes. It was also found that reducing the process temperature gives fine grain and high microhardness and hence improved propertiesIntroductionTechnological changes in manufacturing industries have depended heavily on development in materials processing and process technologies. Modem industries need high performance materials for severe service conditions. Hence, it is necessary to improve required material properties to achieve better performance and greater service life. As mechanical properties of the materials strong! y depend on grain size ( d) - Hall-Petch relationship [ 1-4], the ultrafine grained (UFG) materials offer superior mechanical properties based on the above relation.Synthesising massive nanocrystalline materials presents a challenge to basic research as well as to application-related processing efforts. Production of ultrafine gram microstructures in metals and alloys having different crystal structures but always an initially coarse microstructure using severe plastic deformation can significantly enhance the physical and mechanical properties of materials. Severe Plastic Deformation (SPD) is an efficient method to induce ultra fine grained structure in materials by deforming it to large strains. Traditional techniques for introducing deformation of higher strains, such as forging, extrusion, drawing or rolling do have the inevitable limitation on required equipments of exerting enough load or pressure to cause uniform nanometer level grain refinement."

Jan 1, 2011

By Xiaodi Huang, Matthew Andriese, Zheng Zhang, Jiann-Yang Hwang, Zhiwei Peng

"The thermal decomposition and regeneration behaviors of wüstite were investigated by in situ high temperature X-ray diffraction (HT-XRD) under non-isothermal condition at heating rate of 4 K min-1 in vacuum ranging from 294 K to 973 K. Wüstite on heating decomposes to magnetite and iron up to 823 K, above which it exhibits marked tendency to regenerate. Investigation of thermal stability of the reaction system shows that the decomposition proceeds under kinetic reaction control while the regeneration is under thermodynamic control. Kinetics study based on the Coats-Redfern integral approximation method indicates that the decomposition reaction follows a Komatsu-Uemura model-based diffusion-controlled kinetics with activation energy of 32.860 kJ mol-1. The thermodynamics analysis of regeneration reaction demonstrates that wüstite regenerates at lower temperature than stoichiometric ferrous oxide.IntroductionOwing to its importance in preparing various magnetic ceramic/metal nanocompostites or nanocrystals with high values of coercivity for the application as recording media, wüstite (non-stoichiometric ferrous oxide) has been attracting the attention of scientists over a long period [1-6]. The thermal behavior of wüstite was investigated by several researchers and phase transformations due to thermal decomposition and regeneration of wüstite during the heating in a specific temperature range was observed [7-9]. In spite of wüstite being found to dissociate to magnetite and iron at temperatures lower than 848 K and then regenerates at higher temperature, a clear understanding of the reaction mechanisms is clearly lacking [9]."

Jan 1, 2012

By Corby G. Anderson

Over the past 15 years, numerous pressure oxidation plants for pretreatment of gold ores and concentrates have been installed throughout the world. While this technology is now established, it suffers in terms of the complex engineering and operational characteristics inherent in utilization of high temperatures (i.e. up to 225oC) and high pressures (i.e. > 3000 kPag). This paper outlines the application of an industrially proven pressure leaching methodology utilizing nitrogen species catalyzed pressure leaching and alkaline sulfide gold leaching. As such, it stands as an economic and engineering advancement in pressure leaching and non-cyanide treatment of gold ores and concentrates. In particular, the technology offers significant technical and economic advantages over traditional pressure oxidation and cyanide gold recovery in the treatment of gold bearing chalcopyrite ores and concentrates. An example of this will application will be delineated in this paper.

Jan 1, 2003

By Denise Corrêa de Oliveira

Household zinc based batteries, dry and alkaline, has become the most popular sources of electrical energy, and are widely used. Because of their heavy metals content such as mercury, zinc and manganese, spent batteries cannot be directly placed in common landfills without a pretreatment. As a municipal solid waste, these batteries may cause serious health problems and environmental impacts. These damages can be reduced by recovery (which means saving natural sources and energy), recycling and adoption of cleaner technologies. Although this worry has been increasing recently, and producers are doing efforts to reduce the mercury content, batteries still need proper safe disposal conditions or recycling processes. This work presents the efforts in progress to characterize and recycle mixed - dry and alkaline - spent batteries, by using low cost unit operations. Some possible recycling stages and recovery parameters of metals as zinc and manganese are also discussed.

Jan 1, 2001

By V. Blet

Rare earth elements (REE) are regarded today as highly critical raw materials but currently lack suitable recycling processes. A combined hydro- and pyrometallurgical process aimed at REE recovery from used NdFeB permanent magnets was recently developed by the CEA. The process integrates the physico-chemical treatment of magnets, followed by a solvent extraction step for the recovery and intra-REE separation using a selective extractant. A subsequent pyrometallurgical treatment via molten chloride salt electrolysis allowed the isolation of pure Dy metal. Technical-economic assessment and life-cycle analysis were also conducted. Following this first successful demonstration, a new project aimed at the recovery of REE from end-of-life nickel-metal-hydride batteries is currently being developed in association with industrial and academic partners. The project aims at evaluating from an experimental and economic perspective different processes converging at the production of value-added products such as cermet materials for catalytic applications, purified REO concentrates, or metallic alloys.

By I. C. Knight

The current levels of copper smelter by-product acid production are reviewed on a regional basis, together with the possible changes in the future. There will be increasing pressure for all smelters to achieve a sulphur capture level of at least 95% by the end of the decade.

Jan 1, 1996

By Mark Cross, Andrew P. Campbell, Koulis A. Pericleous

"Computational Fluid Dynamics (CFD) modelling is being used to simulate the freeze layers formed within direct smelting processes. There has been some concern whether water-cooled elements can withstand the p~ocess conditions and in particular abnormal cases where they may be splashed in molten metal.To validate the models being developed, two cases from literature have been modelled for solidification and stress analysis. The solidification case is presented in detail and is for hot molten metal flowing through a cylindrical pipe. The walls are at a temperature below the melting point for the metal. The resulting solid (or freeze) layer is within 3% of the value calculated by Sampson & Gibson9 •Preliminary modelling of the refractory-slag interactions is presented. Although three basic mechanisms: Penetration; Corrosion; and Erosion will eventually be modelled, only the penetration is considered here. The corrosion mechanism is to be modelled by tracking the time that the penetrated refractory is at the required temperature.Future work, after adding all the required physics, will focus on the modelling of a water-cooled element placed lower in the smelter. Process perturbations will be simulated to examine what these elements will withstand."

Jan 1, 2001

By Henry Hu

In high pressure die casting processes, proper control of temperature die yields a high casting production rate and superior quality components, Die temperature is usually influenced by various die design and process parameters such as size and location of intemal water cooling lines, flow rates of cooling lines, and pouring temperature of molten metal. Among them, the cooling water flow rate plays a major role in controlling thermal pattern of the die_ In order to develop an effective control strategy, data of local die temperature must be collected and analyzed, In this study, a PC-based data acquisition and control system (DACS) for die temperature control has been designed, and established, The developed DACS has three input channels for temperature signals and one input channel for water flow rate signals, as well as one output channel for a water pump, and is capable of displaying data in both curve format and value format. Implementation of the DACS in a laboratory setup has also been attempted, It should be pointed out that more advanced control mechanisms can be potentially integrated into this system in future,

Jan 1, 2003

By Xuemei Zheng, Aiyuan Ma, Jing Li, Jinhui Peng, Shaohua Yin, Libo Zhang

Zinc recovery from zinc oxide flue dust (ZOFD) by ultrasound enhanced neutral leaching process was investigated. In this study, the effects of leaching temperature, liquid/solid ratio, leaching time and ultrasound power were studied, and the conventional leaching experiments were also performed. The experimental results showed that the leaching time was greatly shortened and the leaching rate of zinc was effectively improved by the assistance of ultrasound. The optimum conditions of ultrasound-assisted leaching were determined as leaching time 20 min, temperature 35℃, and the liquid/solid ratio of 5. Under these conditions, the leaching rate of zinc was close to 80% as the ultrasound power of 540W, which was increased by 7% or so, in comparison with that of conventional leaching process.

Jan 1, 2015

By Anjan Kumari, B. K. Soni, Manis Kumar Jha, A. Vidyadhar, Vinod Kumar

"In the present paper, recovery of valuable metals from the poly-cracked ash obtained by pyrolysis of discarded PCBs has been studied following physical beneficiation and a hydrometallurgical process alternate to smelting. The ash is subjected to comminution for the separation of metallic components from non-metallic fractions by scrubbing, tabling and froth flotation which enriched the metal in the concentrate -97% which was further screened to separate high and low metal concentrate. The finer fraction containing -12% metallic value was leached in acidic solution. Almost all (Cu, Pb, Fe, etc) were leached in 4M HN03 at 90°C in 75 min at a pulp density 100 g/L. The characterization of both ash and residues were made by XRD, EPMA, EDS, etc. to validate the experimental results. The metals from the leach liquor could be recovered/separated using solvent extraction techniques which can further be processed to get pure metal salts/ sheets.IntroductionPrinted circuit boards (PCBs) are an essential component of electrical and electronic equipments (EEEs) as it plays an important role during operation of these devices. The world market of PCBs has reached nearly $60 billion in 2012, with 1.7 percent real growth over 2011 [1]. The diverse technology-driven global market is expected to grow at an average annual rate of 5% by 2014 [2]. The waste EEEs are generated due to replacement of obsolete equipments with modem ones and thus their demand is also increasing rapidly [3]. The discarded e-wastes are being piled up as landfills which affect the environment and cause health threats to living organisms, if not disposed of properly. These e-wastes contain metals some of which are precious, few are hazardous and others as valuable."

Jan 1, 2014

By Christoph Sagadin

Corrosion mechanisms between high melting synthetic ferronickel slags and refractory were investigated. The used slags were prepared by mixing and melting of specific oxides. Substrates of the applied refractory material and specimens of FeNi slags were heated in a hot stage microscope up to 1650 °C. The experiments were performed under a defined gas atmosphere of 60% CO and 40% CO2. A further examination of the formed phases between slag and refractory occurred by scanning electron microscope. The investigations indicate that the slag penetrates between magnesia grains and partly dissolves magnesia. Spot analyses show that iron diffuses into the magnesia grains, which transform to magnesiawustite, meanwhile SiO2 forms different types of olivine like forsterite and monticellite. Thermodynamic calculations confirm the formation of these phases. The combination of practical lab scale experiments and thermodynamic calculations should finally contribute to an improvement of the refractory lifetime and performance.

By Zdzislaw Miczkowski

At KGHM Polska Miedz S.A, a direct flash smelting process is used for smelting of chalcocite concentrate for the production of blister copper. The paper presents a model of complex oxidation process of single concentrate grains smelted at KGHM. The description covers main chemical reactions, phenomena of heat and mass exchange inside the grains and between a grain and the surrounding space. In the model, two zones describing the course of process inside the grain were distinguished: ? The first one, which moves faster towards the centre of a grain, both organic and carbonate carbon are freed, The process takes place without the presence of oxygen and results in an increase of the temperature in the core of the particle. ?The second zone moves slower into the grain and the rate of the movement is determined by the presence of oxygen, In that zone the sulphur is eliminated and the oxidation of the organic compounds vapours moving from deeper layers of a grain takes place. Based on the results of laboratory tests, the coefficients that describe the oxygen transportation into the grain and decide the progress in the chemical reaction were determined, The paper contains the results of model calculations for single grains reacting in environment of various content of oxygen as well as the results of model calculations for the laboratory reactor system.

Jan 1, 2003

By Ho-Jung Shin

The influence of cooling rate from 1873 to 1473 K on the size and morphology of austenite grains was studied using a Fe-O.I5 % C-I.5 % Mn alloy. The experiments were carried out at three different cooling rates of O.33KJsec, O.67KJsec and air-cooling. The austenite grain showed an isotropy at 0.33KJsec but maximized anisotropy at O.67KJsec and become much less. anisotropic. In order to account for these phenomena, a model was developed for estimating the size and morphology of austenite grains as a function of cooling rate. The driving force for the )( phase formation from 0 phase is caused by undercooling degree due to cooling rate and energy barrier is restricted to the misfit strain energy which is caused by mismatch between )( phase and 0 phase. The )( phase from 0 phase could be formed on not random orientation index systems but specific orientation systems depending on cooling rate.

Jan 1, 2001

By Dong Hoon Han

The simultaneous sulfation by sulhr dioxide and oxygen of CaO and MgO in calcined CMA (calcium magnesium acetate) were investigated. he experiments were carried out in the temperature range from 700 to 830 "C and at the SO2 concentrations of 0.3 to 1 mol %. The oxygen concentration was kept at 5 %. Each sample was calcined completely before the temperature was lowered to the sulfation temperature. According to the ranges of partial pressure of sulhr dioxide and temperature, there exist three regions for the sulfation reaction: region I in which neither oxide is sulfated, region I1 in which only CaO is sulfated, and region 111 in which both oxides are sulfated. It was shown that the MgO in calcined CMA is sulfated at a rate comparable to that of CaO by forming a mixed sulfate phase. Thus, unlike MgO contained in other desulhrization materials, the MgO content in calcined CMA can be fully utilized for flue gas desulhrization.

Jan 1, 1999

By A. Kiziltas, D. J. Gardner, C. W. Mcllwraith, J. W. Bridge, M. L. Peterson

"Dynamic mechanical thermal analysis (DMTA) tests were conducted on high-oil content, paraffin-based wax used in wax-coated granular composites. These composites make up the surface of synthetic Thoroughbred horse racetracks used in North America. The modulus and damping response from the DMTA tests were correlated with the dynamic triaxial shear strength response of the bulk track material taken at two different operational temperatures and at four strain rates. The purpose of these tests is to understand the mechanisms of shear strengthening of the bulk track material as the wax is heated through the first crystalline solid to liquid nominal transition temperature. Previous work using differential scanning calorimetry confirmed that under common operational surface temperatures, the wax coatings undergo distinct thermal transitions. The resulting increase in triaxial shear strength values affects the consistency of the racetrack which, in turn, can potentially affect Thoroughbred racing performance and safety of the track surface.IntroductionSynthetic granular composite materials are being used in nine Thoroughbred horse racetracks in the United States as well as in other tracks around the world. In one case, their use was mandated by the state of California in 2007 due to testimony that these tracks were significantly safer than traditional dirt tracks [1]. Several synthetic tracks have shown substantial reductions in injuries since switching to synthetics; one California track showed a 75% reduction in catastrophic horse injuries during the first year as compared to the previous year racing on a dirt track [2]. The composition of the tracks in the U.S. generally consist of silica sand (>70%), polymer fibers (<5%), and rubber particles (0-15%) all coated with a paraffin-based, high oil content wax [3, 4]. In a recent study of several synthetic racetracks, to include the track location in this study, the oil content ranged from 34 to over 44% by mass [5]."

Jan 1, 2011

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By Philippe Henry

"Hydrometal provides an adequate technology to reintroduce otherwise lost metal units into the industrial cycle, thereby saving resources and energy, while keeping the environment cleaner. Two case studies at an integrated hydrometallurgical recycling facility (Hydrométal) in Belgium are discussed: (I) Residual low quality acid and caustic are used in the processing of zinc industry cements to produce copper, nickel, cobalt and zinc concentrates by several consecutive selective leach - precipitation processes.(II) Copper anode slimes are treated and their precious metal contents are recovered. Depending on the composition of the slimes, separate or combined concentrates of copper, bismuth, tellurium/selenium and silver/precious metals can be produced."

Jan 1, 2008

By Malti Goel

"Technology advancements in fossil fuel based energy generation and consumption are currently being aimed at minimization of CO2 emissions. To attain energy security, India must accelerate the pace of economic development, while achieving reduction in CO2 emissions per unit of energy consumed. It would need access to advanced coal utilization technologies to be demonstrated on indigenous coal characteristics. Of specific importance would be: improvement in coal quality, increasing energy efficiency and suitability of other CO2 sequestration technologies for reducing CO2 footprints. There is need to address related risks and financial burden through adoption of policies and regulations including the issue of open access in energy research. In this paper, seven important areas of strategic plan that need to be pursued for managing CO2 emissions in steel energy sector in India are discussed.IntroductionWorld is facing a crisis of climate change, which follows in the footsteps of global energy and environment crises. Accumulation of carbon dioxide from the generation and utilization of energy is leading to greenhouse warming and climate change. The global warming is causing the boundary between four seasons to be fuzzy and resulting in more spiky weather. Significance of its impact on environment is also determining the technology development needs in various sectors of economy for taking remedial measures.To respond to climate change concerns, the steel industry is undergoing a transition. It is at the threshold of a rapid change in technology as it targets innovation to achieve 50% reduction of CO2 emissions per ton of steel produced. Fossil fuel use is the main contributor of increasing concentration of carbon dioxide in the atmosphere. The control of air pollution and CO2 capture are thus relevant for a coal based industry, whether thermal power plant or a demand side energy intensive industry. World steel production has shown phenomenal increase in first eight years of 21st century increasing from 780 Mt in 2000 to 1343 Mt in 2008 [1]. It was merely 28 Mt in 1900. The global CO2 emissions from steel industry are also increasing and became 2550 Mt (3-4% of total GHG). Indian industry contribution was 161 Mt (15% of direct emissions from industry). It is likely to grow further to keep pace with the accelerated economic growth of 8-9% per annum."

Jan 1, 2010