By S. Agatzini-Leonardou

The objective of this work was to prove repeated loading capacities and investigate the selectivity of physically stabilized algal biomass from Spirulina platensis and Chlorella sp. for the removal and recovery of cobalt, nickel and chromium from laterite heap leach liquors. The testwork was carried out on a bench scale in small glass columns and proved that it was possible to immobilize the biomass on the highly porous surface of pumice stone (kissiris). Nickel and cobalt could be removed from pure aqueous solutions of each metal by the immobilized cyanobacterial biomass. Nickel and also cobalt biosorption was sensitive to the initial solution pH. Cobalt recoveries up to 80% were achieved after 5 loading cycles, from low concentration solutions, at pH 6.0. Nickel removal was complete under the same conditions, whereas chromium sorption was ineffective. Desorption of the metal loaded columns was effected by dilute sulfuric acid. The algal species giving the best adsorption capacities for the metals under consideration was selected for further experimental work with real laterite heap leach solution produced by column leaching. A statistical analysis of all obtained results was conducted using the fraction of metal removed as response. The ratio "mass of metal removed to mass of protein contained in the immobilized cells" was determined as well. The described method might be applicable for recovery of cobalt and nickel from diluted laterite heap leach solutions, such as heap wash waters, or for their removal from waste streams of a hydrometallurgical extraction process.

Jan 1, 1997

Equilibrium calculational software programs can be effectively utilized to illustrate the importance of activity or concentration, solubility, temperature, solution pH, solution potential, and ligand complexation to students studying hydrometallurgy. The calculational program STABCAL will be demonstrated. illustrative examples for the creation of diagrams such as EH-pH, activity or concentration-pH and activity or concentration-EH will be presented to demonstrate the fundamentals of real hydrometallurgical systems. Speciation, titration and mixing will be used to simulate or predict operational processes. Applications will include treatment of Acid Mine Drainage (Berkeley Pitlake water and sediments), mass balance potential/pH diagrams, leaching and selective separation of metals from electroplating sludge, metal adsorption at femhydrite surfaces, and flowsheet development for treating mercury sulfide K106 sludge.

Jan 1, 2002

By J. W. Perez

Raw coal will often break intragranularly in either a completely random way or in a differential mode where one species will have a different rate of breakage than another. Locked coal-ash and coal-pyrite particles can also break by the preferential detachment of one species from another along zones of inherent weakness in locked particle assemblages. The mode. cf breakage is largely a function of the nature of the feed, but it is also influenced by the comminution device and the operating variables. Evidence of breakage of particles in the various modes is seen in the crushing of raw coal and middlings particles with a rotary beaker, jaw crusher, rolls, hammer mill and rod mill. Evidence from the literature indicates the detachment mode is often important for coal, ores and metallurgical products. Further confirmation comes from the crushing of a specially prepared 'ore' of sized magnetite in plaster of Paris.

Jan 1, 1988

By Isrun Bohlinger

Resources recovery of brasses for semifinished products often results in the formation of hard spots impairing the quality of following abrasive and/or surface finishing processes. A short survey is given on the recycling processes, followed by the actual knowlegde of genesis, composition, and possibilities of avoidance of hard spots. Informations on genesis and composition of hard spots are completed by data from recent experiments.

Jan 1, 1998

By Hongbo Yang, Tongbo Zhang, Ting Huang, Jingshe Li, Fangfang Song

"Liquid core length is a very important parameter of the process of continuous casting, which directly reflects the cooling status in secondary cooling zone and solidification rate of the slab. In this paper, the billet caster in some steel plant in China was chosen as the prototype of simulating. A numerical simulating model for calculating the liquid core length of continuous casting billet was built by ProCAST software, which was verified reasonable and accurate by pin-shooting technique. Based on the model, the relationships between casting speed, casting temperature and liquid core length of casting billet were found, which was very practically useful for the workers on sit to improve casting billet quality. IntroductionContinuous casting process developed very rapidly because of the high metal yield, energy saving, and low-cost 111• And the quality requirements of continuous casting billet for customers became higher and higher with the fast development of economic121• Internal defect usually is the major quality problem for continuous casting billet[3•61 , which is influenced by the solidification process of casting billet, especially the solidification process of liquid core17•81 • So it is very important to study on the relationship between casting parameters and the liquid core length which means the distance between the crystallizer meniscus and the casting billet solidification end-point. In practical production process, the workers usually control the quality of casting billet according to the liquid core length."

Jan 1, 2013

By Derek J. Fray

"A need exists for fast and accurate analysis of species in various phases at elevated temperatures. Although modern analytical techniques are very efficient, the equipment is usually situated some distance from the industrial operation and time is spent taking the sample and sending it to the analytical facility. Several minutes can easily lapse and, during this time, heat must be supplied in order to keep the system molten and, if the composition is changing rapidly due to a refining process or reaction with the environment, the information may only be of retrospective use. Perhaps more important reasons for the use of on-line sensors are that instantaneous analysis gives better control, process optimisation and the minimisation of energy losses and pollution. To date oxygen has been the only element which is measured widely using solid electrolytes. However, the analysis of many more elements is required and possible electrolytes for other species are discussed. For some elements, ~here is no suitable conducting electrolyte and, therefore, a different approach is adopted where the electrolyte, in which one species is mobile, comes to equilibrium with another species. IntroductionThere is an ever increasing demand for the development of sensors for on-line measurements in most areas of technology and, in particular, metal processing. This is especially relevant in situations where greater control can be achieved by monitoring the chemical composition of the melt during processing and where a minor constituent in the melt can have a major effect on the properties of the finished alloy. Although modern analytical techniques are fast and reliable, the equipment due to its complexity, is frequently situated away from the process area and valuable time may be spent in sampling and transportation. During this period, heat may have to be supplied to prevent solidification and the refining reactions may be continuing, and, therefore, the analytical information may not be of direct use."

Jan 1, 1988

By Baozhong Zhao

Laboratory experiments have been conducted on the removal of As, Sb and Bi from molten copper by SF 6 injection. The results showed that the impurities can be removed by SF6 injection in the? sequence of Sb >As >,Bi and the rate of Bi removal is affected significantly by the concentration levels of As and Sb in the copper melt. Analysis of the experimental data indicates that the impurity removal process is under chemical reaction control rather than by mass transfer of impurity through the molten copper phase. On the basis of experimental results, a kinetic model was developed and the order of chemical reaction and the volumetric chemical reaction rate coefficients of impurity removal were determined.

Jan 1, 1996

By D. Raghavan

In recent years, the environmental issues related to the landfill shortage received considerable importance. Many polymeric solid wastes have high resistivity to chemical and biological degradation, and options are sought by which these wastes can be recycled and reused, or reduced in volume. The present study investigated the biodegradation of polyethylene by Aspergillus niger, and biodesulfurization of rubber by pure and mixed cultures of Thiobacillus thiooxidans and Thiobacillus ferrooxidans. The fungus, A. niger, was found to metabolize portions of polyethylene. Quantitative calorimetric measurements revealed that the amorphocity of the sample decreased during biodegradation. Removal of sulfur from synthetic rubber samples containing 2 to 15% sulfur, was studied in shake flask experiments and the associated oxygen consumption was studied in Warburg respirometers. The mixed bacterial cultures were more effective in the desulfurization of rubber samples than the pure cultures of T. thiooxidans and T. ferrooxidans. The data obtained in these studies may have far reaching consequence for the development of new effective processes regarding the remediation and management of discarded polymeric packaging wastes and car tire rubber materials.

Jan 1, 1993

By Scott Samson, Weidong Wang, Shekhar Bhansali, Vandana Upadhyay

"We present an improved design for the two-arm polysilicon thermal actuator. The classic thermal actuator design produces a localized hot spot at approximately the center of the thin actuator arm. This phenomenon limits the actuator efficiency, lifetime, and reliability. Since the actuator deflection is based on thermal expansion of the material, advantage may be gained by making the temperature profile more uniform along the hot-arm length. In our design, the geometry of the thin arm is modified by forming a nonlinear structure near the approximate location of the original hot spot. Electromechanical simulations of this design show an increase in deflection, due to a flattening of the temperature profile along the hot arm. The solid model generation, finite element analysis and simulations are carried out using PEA software. Experimental devices are in the process of being fabricated by using a polysilicon rnicromachining process.1. IntroductionMost active MEMS devices employ some kind of actuating mechanism to increase functionality. Various actuating mechanisms like magnetic, electrostatic, thermal, magnetostatic and piezoelectric have been investigated and incorporated for actuating microstructures. The primary features required from many on-chip actuating mechanisms are large deflection (>10 µm), low actuation voltage, low power.consumption, reliability, fast response, ease of design and fabrication, and small size. Thermal actuation is an attractive mechanism for rnicromechanical devices requiring high actuation forces, large deflections, good linearity and low actuation voltage. Thermal actuators, also known as ""electrothermal actuators"", ""heatuators"" or ""U-shaped thermal actuators"", have been largely used in MEMS based devices to provide both in-plane and out-of-plane actuation [l] .Thermal actuators are also easily compatible with standard CMOS circuitry due to their low driving voltage. However, high power consumption remains a major drawback of the thermal actuation mechanism."

Jan 1, 2004

By Y. K. Rao

The direct reduction of lead sulfide with carbon in the presence of lime was investigated at several temperatures and under two different inert gas atmospheres. The catalyzed reduction kinetics were determined both with a nitrogen atmosphere and a helium-rich helium-nitrogen atmosphere. The reduction kinetics under the latter were d-ecidedly superior to those under the former. The differences-were interpreted in terms of faster diffusion rates in a helium medium and-synergistic effects.

Jan 1, 1983

By J. Brent Hiskey, Rebecca Grace Copp

The solvent extraction of yttrium and neodymium from copper pregnant leach solutions (PLS) using Primene JM-T, a primary aliphatic amine, has been studied. Effect of contact time, pH, sulfate concentration, and extractant concentration were investigated using synthetic and actual PLS systems. Standard experimental conditions were 5 minute contact time, pH ~2.5, and 10 % v/v Primene JM-T concentration. Distribution isotherms were constructed for the pure systems and for actual copper leach solutions. Synthetic solutions contained 100 ppm Y and ~75 ppm Nd. Samples of PLS contained 2 - 10 ppm Nd and 14 - 30 ppm Y. Results showed that complete extraction of both yttrium and neodymium occurred within five minutes and at pH values greater than 1. It was also found that sulfate concentration does not inhibit extraction at any concentration. Additionally, the distribution isotherms created show that extraction for these metals can operationally take place in one stage.

Jan 1, 2016

By H. Y. Cheng

A pulse column solvent extraction system was evaluated as an alternative to mixer-settlers for the separation and purification of rare earths. The column tested had an inside diameter of 44.5 mm and had 36 sieve plates with a free area of 25%. Pulsing was provided pneumatically using a solenoid valve controlled by a timer so that both pulse amplitude and frequency could be varied. Feed to the column was a mixed rare earth chloride solution containing 10 g RE L-1. The extractant was 5% Ionquest® 801 in Shellsol 2037 diluent. Hydraulic performance of the pulse column was excellent with no propensity towards stable emulsions or crud formation under normal operating conditions. The column was operated in organic-continuous mode with flow rates chosen so that yttrium and the heavy rare earths were extracted with high efficiency while the light rare earths were rejected. Yttrium extraction varied from 83 to 99.2%. Concentration profiles were measured in both the aqueous and organic phases, and, from this data, the height of a transfer unit (HTU), the mass transfer coefficient (Kxa) and the continuous-phase axial dispersion coefficient (Ey) were computed. The HTU ranged from 17-92 an which is within the range of values reported for other (non rare earth) pulse column systems.

Jan 1, 1992

By Tatsuo Itou

Both sales volume of Aluminum Can and its recycling rate are remarkably increasing here in Japan. In 1993, recycled can volume was 11.78 billion cans ( 116,258 metric tons ) and its recycling rate 57.8 percent. We, MITSUBISHI MATERIALS CORPORATION. the leading manufacturer of aluminum can in Japan and our affiliated companies are very deeply involved in recycling used beverage cans ( U.B.C ) and recycling them back to can stock. In this paper. I would like to present the following; 1. Recent trend of beverage can consumption in Japan. 2. Trend of aluminum can and its recycling rate in Japan. 3. Future of aluminum can business in Japan.

Jan 1, 1995

By R. David Prenganan

RSR has developed a new environmentally superior process to recover lead as high purity electn:1o'i0!1 cathode from battery scrap. The process involves crushing the batteries, separating the lead bearing material from the plastic, ebonite and separators, and separating the active material (paste) from the metallic lead fraction. The paste is desulfurized using Na2C03 to convert the PbS04 to PbC03 and produce a sodium sulfate solution. The paste is further treated to decompose the PbO2 and PbC03 to Pbo. The PbO from the treated paste is easily leached, using H2SiF6 and electrown from solution using Pbo2?coated graphite anodes. The electrown lead has a purity exceeding 99.99%. RSR is in the final design stages of a plant to produce 36,000 tons per year of electrcwon cathode from battery paste in a new plant adjacent to the present Indianapolis refinery. This paper describes the work of a pilot facility operated in the early 1980's. The paper describes the patented process in detail and compares the newly designed environmentally clean electrolytic plant to present recycling plants.

Jan 1, 1990

By José D. T. Capocchi

Viscosity of liquid lead, tin, and Pb-Sn alloys has been measured by the rotational viscometer method in the temperature range from 50 K above their respective liquidus temperature to 823 K. The results are accurate to within ±1.0 %. The variation of viscosity with temperature followed the Arrhenius-type equation µ = µo.exp(Q/RT). The composition dependence of the isothermal viscosity and the activation energy for viscous flow have not shown anomalous changes at the eutectic composition of the Pb-Sn system.

Jan 1, 2000

By S. Tandon

Equilibria studies of selenium distribution for sodium-borate slags were initiated at 1473k under reducing condition as a function of slag composition and alloy composition. The Se distribution coefficient (% Se in slag/% Se in metal) increased from 0.4 to 2.9 with increase in basicity (0.53 to 0.86) for Cu-0.446% Se alloy. However, the results are not very useful from industrial application viewpoint. Therefore, in order to improve the distribution of Se, CaO (10% to 50%) was added to the sodium-borate slag of basicity 0.864. On addition of 502 CaO, the distribution coefficient increased roughly by 100% for slag composition - 44.5% Borax, 22.2% Na2C03, 33.3% CaO and Cu-0.44677 Se alloy. Further, the value of this distribution coefficient has been found to increase by an additional 80% on addition of 20% CaF2 to the above slag for all Cu-Se alloy compositions. Also with increase in initial concentration of Se, the distribution coefficient has been noted to increase.

Jan 1, 1992

By I. S. Blair

The Mufulira smelter (1, 2,' 3, 4,) is one of three smelters situated on the Zambian Copperbelt to treat concentrates and other intermediate products produced in the area. Two mining companies, Roan Consolidated Mines Limited (RCM) and Nchanga Consolidated Copper Mines Limited (NCCM) each have 51% Zambia Government participation. RCM operates two smelters, one at its Mufulira Division and the other at its Luanshya Dl vision. NCCM operates one smelter at its Rokana Division (5). The Mufulira smelter was commissioned in 1937 with two reverberatory furnaces and four converters. The final product, blister copper, was cast from a holding furnace. In 1952 two anode furnaces and a common casting wheel were installed to feed a new and adjacent electrolytic refinery. In 1956 the smelter was extended to accommodate increasing production from the new Chibuluma mine and expansion at Mufulira mine. A third reverberatory furnace, a fifth converter and duplicate anode processing and casting facility were added. The Copperbelt smelters suffered a loss of production potential when higher ash content coals were used in reverberatory smelting furnaces from 1966 onwards. This, and the planned production increases from Mufulira and other RCM mines, indicated a smelting shortfall of 55,000 tonnes of copper a year in the combined capacity of the RCM smelters.

Jan 1, 1976

By Linlin Wu, Marlen Bertram, Chris Bayliss, Bernard de Gelas, Samantha Jones, Kurt Buxmann

"Environmental management is one of the industry cornerstones of sustainable development. In order to understand fully the environmental aspects associated with the raw material acquisition, production, use, and end-of-life operations of aluminium products, the Aluminium Industry has developed an approach based on Life Cycle Analysis (LCA) methodology.Within this framework, the Primary Aluminium Industry has established a global Life Cycle Inventory (LCI) data set. Inventory flows include inputs of raw materials, energy and water, emissions to air and water, and solid waste.This paper presents the latest LCI data update by the International Aluminium Institute for the year 2010, based on a survey of aluminium plants globally, including bauxite mining, alumina refining, anode production, electrolysis and casting. This update also includes some performance tracking based on the last LCI data collection in 2005, reflecting progress in efficiency and technology, as well as changes in the geographical location of the industry [2010 data pending]. IntroductionIn 2010 the Primary Aluminium Industry produced a total of 41 Mt of aluminium. The International Aluminium Institute (IAI) membership represents approximately 70% of total global production. The industry recognises the importance of co=itting to reducing the environmental impacts of producing primary aluminium, and the significance of working towards a more sustainable future. As part of this co=itment the IAI has developed an in depth Life Cycle Inventory programme, in which data is collected every five years, with supplementary key metrics collected annually.In 2003 the IAI released its first Report ""Life Cycle Assessment of Aluminium: Inventory Data for the Worldwide Primary Aluminium Industry"" based on the year 2000 with an update Report released in 2007, based on 2005 data.This paper presents the latest update for the year 2010 [2010 data pending]. It has been prepared with the same view of collecting all significant Life Cycle Inventory data (raw materials and energy use, air and water emissions and solid waste generated) associated with producing primary aluminium ingot from bauxite ore, with worldwide coverage. The intended purpose of the Inventory Report is to accurately characterize resource consumption and significant environmental aspects associated with the worldwide production of primary aluminium. It reflects the fuct that primary aluminium is a globally traded co=odity."

Jan 1, 2012

By Grégory Miette

The paper deals with a process that allows the recycling in a cupola of EAF dusts with 18 % Zn. It produces dusts with zinc grade higher than 50 - 55 % and commercial cast iron with less than 200 ppm Zn, 50 ppm Pb, 0.15 % S. The paper focuses mainly on lab tests made with the aim to develop an effective formulation of self reducing - melting pellets. With such a formulation, agglomerates develop a breaking load higher than 125 - 150 kg without any thermal treatment. Zinc and lead are volatilized in the cupola with yields higher than 95 % at 1200 OC, before any melting. Sulphur is transfemed into gas and slag. All these conditions allow to lower zinc, lead and sulphur grades below the cast iron specifications. Results of first bench scale tests performed at Fonderie Piret to validate the process will be presented.

Jan 1, 2002

By Rainer Schmid-Fetzer

"Isothermal solidification can be used to form strong bonds at low temperature which remain solid at much higher temperatures. The exploitation of this principally known technique for new high temperature processing steps and applications in electronic assemblies is the aim of this study. Three basically different variants of this bonding process are given. A comprehensive metallurgical screening is performed and the feasibility of binary material systems is given on a quantitative scale. Very attractive systems are spotted that have never been studied before. Detailed examples for the realization of bonding with complex ternary and multilayer systems are given. A highly innovative example is the chip stack or wafer to wafer bonding of unmetallized Si or SiC at 250°C. The proposed bond remains stable above the melting point of Si and enables entirely new semiconductor manufacturing steps. An improved die bonding process was proposed and verified experimentally.1. IntroductionIsothermal solidification can be applied to form strong bonds at relatively low temperature which remain solid at higher temperatures. The general principle of this type of joining processes is illustrated in Fig. 1. An interlayer of a low melting component, Lo, is provided as a foil or a thin film coating between the high melting joint components, Hi. The assembly is heated under moderate pressure to the bonding temperature, T 8 , and a liquid filler forms, either because the melting point of Lo is exceeded or due to a eutectic reaction between Lo and Hi. This molten filler initiates a rapid interdiffusion or reaction diffusion between Lo and Hi and the subsequent approach to an equilibrium state results in isothermal solidification. The solid phases formed at T 8 in the joint region exhibit a remelt temperature above T8 •"

Jan 1, 1996