By C. A. Doh, R. Q. Fields, M. Lebourg

A formation tester run on logging cable is now available to the oil industry. It offers a method of safely and rapidly testing possible producing formations in uncased holes. These tests can be made up the hole after running the electric log. Reservoir pressure data is continuously recorded at the surface as the fluid sample is extracted. The tester may be assembled with a reservoir of 1-, 2.75-, or 5.5-gal capacity. A retaining pad on the body of the tool is expanded against the wall of the hole at the exact depth desired; this depth is determined by electrical log control. Two bullets are then fired through the center of the retaining pad which create a connection between the formation and a flow line to the sample chamber. When the chamber is filled, a valve is closed and the fluid sample sealed at maximum pressure. The tool is retracted to minimum diameter and brought out of the hole. Electrical circuits permit a complete recording at the surface of the mechanical operations of the tool as well as the formation pressure build-up and the hydrostatic mud pressure. The tool was introduced commercially during the latter part of 1955 in the Gulf Coasts of Louisiana and Texas. Over 1,000 operations have been made to date (Sept. 1, 1956); 50 per cent of which resulted in successful tests. Failures have been due mostly to ineffective sealing in unconsolidated sands. One major company had 41 successful tests out of 80 attempts with 23 ineffective pad seals. Results for this company were very gratifying as to pinpointing gas-oil ratios, indicating productive permeabilities and aiding in determination of fluid content where electrical log and side-wall coring information were inconclusive. Eight typical pressure curves are discussed (including misruns). Six types of fluid recoveries are interpreted. Eight actual field examples of electric logs, showing the problems solved by the formation tester, are illustrated. The present applications of the tool are discussed: 1. Determination of productive fluid—varticularlv differentiating between gas and oil. 2. Determination of reservoir pressure as an aid to: (a) safety in completion technique, (b) reduction in drilling costs, and (c) reservoir analysis. 3. Determination of minimum gas-oil ratios. 4. Location of gas-oil or oil-water contacts. 5. Recovery of samples for examination and analysis: oil (gravity); gas (hydrocarbon content); water (salinity). Additional applications envisioned for the future are also given: (I) subsurface exploration based on accurate pressure, (2) recovery of fluid samples from the undisturbed reservoir for PVT work, and (3) possible quantitative study of permeabilities or productivity index. Running the formation tester requires no special pre-cautionary measures. Because full hydrostatic mud pressure is maintained at all times, well depth is no problem. Thus, the method allows safe, economical testing in wells which heretofore could only be tested by setting casing. INTRODUCTION A new method of safely and rapidly testing possible producing formations in uncased holes is achieving considerable success. The method offers promise of further advances in reservoir study. Called the formation tester, the new instrument is unique in that it operates on logging cable. It thus offers all the advantages of wire-line operations and becomes an important adjunct to present logging and side-wall coring services. The tester is operated against the wall of the hole at any depth desired. Zones to be tested are usually determined by a study of the electrical and the micro-caliper surveys. Reservoir data, as well as the operating cycle of the tool in the hole, are continuously recorded at the surface during the operation. The tester, as it was originally designed, was capable of recovering a 1-gal sample of reservoir fluid per trip in the hole. Tools with reservoirs of 2.75- and 5.5-gal capacity are now available. The 5.5-gal reservoir is equipped with a segregating system, set before going in the hole, so that the last portion of the recovery (usually 1 gal) is automatically separated from the first portion. This makes it possible

Jan 1, 1958

By R. F. Hehemann, D. J. Cometto, G. L. Houze

The w transformation in the Zr-Nb system was studied using X-ray diffraction, dilatometric, re-sistornetric, hardness, and metallographic techniques. w forms in a diffusionless, completely reaersible manner on quenching and in a diffusion-controlled manner- on aging. The temperature at which w begins to form on quenching was determined as a Junction of composition and was found to decrease with increasing solute content. w formed bv aging establishes a metastable equilibrium with an enriched ß phase. The ß/w + ß transus has been determined for this metastable equilibrium and employed to rationalize retrogression and reversion phenomena observed in these alloys. The decomposition mechanism is discussed in terms of a gradual or continuous transformation from ß to the w state. BETA- stabilizing alloying elements lower the MS temperature of the martensitic bcc (ß) to hcp (a') transformation in zirconium and titanium alloys. In certain titanium alloys, a lower symmetry modification of the martensitic structure, termed (a"), also has been reported.1,2 These martensitic transformations are suppressed when the amount of the ß-stabilizing element exceeds a critical level. However, the high-temperature ß phase cannot be quenched to room temperature without change. At alloy contents just above the critical level, |ß trans-forms to the w phase when cooled rapidly.3-6 The amount of w in quenched alloys is reduced by increasing alloy content, and this phase virtually disappears above a critical composition.5 In addition to the transformation during cooling, w also can be formed by aging ß at temperatures below approximately 500°C, and significant alloy enrichment of retained 13 accompanies the isothermal transformation.1-8 The structure of LC is closely related to that of the ß from which it forms.9-15 The bcc (ß) lattice can be generated using a hexagonal cell with three atoms located at (000) and ±(2/3, 1/3, 1/3). This cell has an axial ratio of 0.612 and is oriented with respect to the cubic cell such that (0001)H (111)C and [1120]H [101]C. Consequently, there are four possible orientations of the hexagonal cell, associated with the four (111) planes of the bee lattice. Formally w can be obtained from 0 by allowing the two atoms at the ±(2/3, 1/3, 1/3) positions to approach the coordinates ±(2/3, 1/3, 1/2) and there are four equally probable orientations of w for each 0 grain. In titanium alloys w retains the cubic axial ratio of 0.612" and hence also can be indexed as triply cubic, but this is not the case for aged Zr-Nb alloys where w is clearly hexagonal with an axial ratio of 0.622." The lattice parameters and atomic positions of w depend on thermal history and alloy content. The atomic positions (000), ±(2/3, 1/3, 1/2) provide reasonable agreement between calculated and observed diffracted intensities for w in the fully aged condition.10,14 In the quenched condition, on the other hand, the atoms appear to be displaced from the central plane12,13,15 and assume positions ±(2/3, 1/3, Z = 0.42-0.48) rather than ±(2/3, 1/3, 1/2). This results in a structure with trigonal rather than hexagonal symmetry. The readily detectable parameter and axial-ratio changes of w in Zr-Nb alloys make this system especially attractive for studying the structural changes that occur in the formation and aging of w. Particular attention in this investigation has been directed to the relationship between the structure of w in the quenched and aged conditions, and to certain aspects of the reaction kinetics. MATERIALS AND PROCEDURE Zr-5, 12, 17.5, and 25 pct Nb alloys were prepared by a double arc-melting practice, encased in stainless-steel cans and hot-rolled to 1/8-in.-thick sheet.* Charged weights have been employed for the niobium contents and interstitial analyses are reported in Table I. Dilatometric, X-ray diffraction (filtered CuK, and MoK, radiation), metallographic, and hardness techniques have been employed to follow the transformations during isothermal and quench-aging heat treatments. In quenched specimens, the electrical resistivity also was studied. Betatizing was conducted for 1 hr at 900°C. With the exception of the isothermal dilatometric studies, samples were

Jan 1, 1965

By C. W. Mueller, P. H. Robinson

A technique was developed for depositing single -crystal films of silicon on single-crystal sapphire substrates via the pyrolytic decomposition of SiH4/H2 mixtures. Electron diffraction and X-ray Laue reflection examinations of these films revealed single-crystal patterns. These films were characterized by measuring conductivity type, thickness, resistivity, and Hall mobility. Chemical etching, dislocation staining, and electron-microscopy examination have indicated the presence of low-angle grain boundaries and microtwinning in the silicon films. The role of the sapphire substrate with respect to its quality, orientation, surface finish, and thermal and chemical treatment was investigated. Hall mobility as a function of sapphire orientation was measured. A mobility equal to 88 pct of bulk silicon mobility was attained. Insulated-gate field-effect transistors which have a transconductance of 4000 pmho at 6 ma were fabricated using these films. THE technology of the fabrication of microelectronic circuits with active and passive components directly on a single wafer of semiconductor material has attained a high degree of perfection during the last few years. One inherent difficulty with the single-wafer approach has been undesirable coupling between components arising from the common base material. Several techniques have been developed for minimizing this coupling and obtaining good electrical isolation between components; however, these result in extra capacitance being added to the circuit. The extraneous capacitance of the connecting leads, resistors, and capacitors degrade circuit performance and limit the high-frequency operation of these circuits. Recently there has been considerable interestl-3 in the deposition of silicon films upon insulating substrates. The use of silicon as the semiconductor allows the subsequent utilization of the large amount of technology which has been developed for silicon for the fabrication of good active components. A sapphire substrate supplies an excellent insulating material which at the same time gives a thermal-conductivity improvement of an order of magnitude over glass-type substrates. This paper will describe the results obtained for the deposition of single-crystal silicon layers upon single-crystal sapphire substrates as well as the characterization of these films. I) APPARATUS The 'system used for the growth of silicon films on sapphire substrates by means of the pyrolysis of SiH4/H2 mixtures is shown in Fig. 1. The all-quartz reaction chamber is water-cooled and includes a quartz optical-flat window for use in conjunction with a 5 kw, 2.5 Mc per sec constant-temperature controlled rf generator. The temperature sensor for the rf generator is a thermopile which is focused through the quartz optical flat onto the susceptor surface. With this system the rf generator will hold the temperature of the susceptor to about +0.3°C at 1200°C. The susceptor is supported on a quartz sled inclined to the gas flow to increase the uniformity of the deposition. The water jacket surrounding the reaction chamber is used to keep the quartz wall temperature low enough to limit the decomposition of the silane to the rf-heated susceptor which contains the sapphire substrates. This eliminates the reaction of silicon with the hot quartz to form SiO which deposits out on the apparatus walls, thus obscuring vision, and interferes with the optical measurements of the temperature as well as with the growth process itself. Provision is also made for "n"- and 'p"-type doping by using mixtures of either phosphine or diborane in hydrogen which are added to the silane during the growth process. The hydrogen used is the purest commercially available tank hydrogen further purified by use of a palladium diffuser. The susceptors which were used include 1) spectro-scopically pure graphite, 2) high-purity molybdenum, 3) high-resistivity silicon using a low-resistivity insert to facilitate coupling to the rf generator, 4) silicon carbide-coated graphite. The latter two susceptor materials produced silicon films on sapphire substrates with more reproducible resistivities. Prior to silicon deposition all connecting lines as well as the reaction chamber are thoroughly flushed with argon and then hydrogen. After the hydrogen flow is set, the growth temperature is adjusted to 11009 to 1150°C, and when thermal equilibrium is reached the silane flow is started. The flow rate of the hydrogen must be fast enough so that turbulent flow occurs in the size of reaction tube used, otherwise a streaked nonuniform silicon deposit occurs. After the deposition

Jan 1, 1967

By Leslie W. Austen

ROTARY kiln operators will agree that some of the most severe conditions a refractory must stand occur in the hot zone of a kiln burning Portland cement, dead burn dolomite, magnesite, peri-clase, and similar materials. Frequently the operator is faced with factors beyond his control which drastically shorten the life of refractories. Shutdown due to mechanical failure can be serious if the period is of sufficiently long duration to cause the dropping of coating or the loosening of the lining. A change in slurry can affect the coating and cause ring buildup. A change in type of fuel and its effect upon the flame can cause a shift in location of the hottest zone. Weekend shutdowns or any other interruption can cause the operator trouble and may damage the refractories, since stopping and starting a rotary kiln is certainly more difficult than stopping and starting a motor. Some operators have tried to set an estimate of damage for each shutdown in equivalent days of running time. Conditions affecting the refractory may be roughly grouped in four classes: chemical attack, mechanical stress, thermal shock, and abrasion. Chemical Attack: The drive to obtain maximum production through a kiln demands maximum operating temperatures, temperatures which are limited more by the ringing up or melting of the clinker. This can cause interface temperatures at the junction of coating and refractory which require the use of a basic kiln block to withstand the chemical attack. Chemical changes take place within the refractory itself, especially in chemically bonded or unburned kiln blocks. These changes cause the formation of the ceramic or burned bond. Migrating liquids or fluxes from the kiln charge have an effect within the refractory and lead to mineral or glass formation. The alkalies, sodium and potassium, migrate into the refractory as silicates, chlorides, sulphates or other salts. They may move under capillary action or may be caused to move by volatilization with condensation in the cooler portion. Mechanical Stress: Concentrated stress may be caused by several factors or combinations thereof. I—The rings of refractories must be kept tight and rigid within the kiln, and this alone demands considerable force to hold the blocks in place. So that the force will not be concentrated, the blocks should fit the circle as perfectly as possible, with the faces in contact overall. 2—As the kiln is heated, thermal expansion takes place at the hot end of the kiln block. Since this disturbs the plane face it too can cause a concentrated stress at the two ends of the block, and shearing stress can be set up within the brick itself because of the difference in expansion between the two ends. 3—If a lining becomes loose and moves in the shell very severe stress can be set up, and as the kiln rotates this load changes and gives the effect of repeated loading. Permanent expansion of the refractory can also cause severe loading. 4—Not least important, flexing of the kiln is frequently the cause of concentrated stresses. Thermal Shock: Thermal shock, the result of heating and cooling too rapidly, occurs on starting and stopping or when a large patch of coating drops, exposing the bricks. Again, its destructive effect is often the result of phase change, liquid to solid or the reverse; dense refractories loaded with glass-forming impurities are particularly susceptible. Thermal shock is a. problem with refractories set in the wall or roof of a stationary furnace, and becomes even more serious in a rotary kiln, the tendency to spa11 being magnified with movement and concentration of stress. Uniform rate of feed and loading insures both better coating and a more uniform stress. Abrasion: If the refractories do not take a coating, abrasion can become a most destructive factor. Movement of the lining in shell or movement of loose blocks causes abrasion, which is also most destructive if the refractories do not take a coating. An analysis of the problem of basic lining for the hot zone reveals, therefore, a number of desirable characteristics: high refractoriness, basic chemical reaction, resistance to spalling, good strength at all stages, ability to take coating, true sizing, volume stability, and abrasion resistance. Increased demand

Jan 1, 1953

By N. J. Grant, A. W. Mullendore

Three aluminum alloys of 0.94, 1.92, and 5.10 pct Mg, prepared from very high purity metals, were tested at 500°, 700°, and 900°F in creep rupture. The degree of strengthening through solid-solu-tion alloying and the effects on the deformation characteristics and fracture were examined. The ductility of the alloys as a function of stress and temperature was closely followed. STUDIES of the creep process in pure metals in recent years have done much to expand the understanding of the fundamental deformation and recovery processes that contribute to overall creep behavior. In order that this knowledge may be applied to commercial alloys, it is necessary to know the principles governing the effect of alloying on the mechanisms of creep. A limited amount of work has been performed in this field, but few investigators have attempted to follow the changes in particular creep mechanisms with alloying. Recently, studies of the effects of solid-solution alloying on the plastic properties of aluminum have been conducted by Dorn, Pietrokowsky, and Tietz,1 Sherby, Anderson, and Dorn,2 and Sherby and Dorn.3 This paper presents the results of an investigation of the effect of solid-solution alloying of high purity aluminum with magnesium on the creep-rupture properties, and correlates these observations with changes in the creep mechanisms. This work is thus an extension of the creep-rupture observations of Servi and Grant4,5 and the deformation studies of Chang and Grant.6,7 Experimental Procedure Three alloys of aluminum containing approximately 1, 2, and 5 pct Mg were tested. These alloying additions are all within the solid-solubility limit at the testing temperatures.' The analysis of the materials is presented in Table I. The tests fall into two categories: l—creep-rup-ture tests at 500°, 700°, and 900°F, and 2—structure study tests performed primarily at 700°F. Speci-mens of 0.160 in. diameter with milled flats for metallographic observations" ' were utilized for the structure studies. All specimens were annealed in one step to give the desired grain size for the tests. Table II presents the annealing data and final grain sizes. The specimens were polished electrolytically before testing with Jacquet solution (2/3 acetic anhydride, 1/3 perchloric acid) at 25" to 30°C, and 15 to 20 v. Creep-rupture testing was performed under constant load with the apparatus previously described." Results and Discussion Creep-Rupture Properties: The log-log plots of creep-rupture data are presented in Figs. 1 and 2. For these very pure single-phase alloys, the minimum creep rate and the rupture life both exhibit straight-line dependence on stress in this method of plotting as they have for commercial alloys0,10 and for pure aluminum." Curve breaks, based on the use of straight-line segments, at 500°F have been found by metallographic study to correspond to a transition from low to high temperature behavior and so represent zones of equicohesion. Specimens on the high creep-rate side of the break showed normal granular deformation processes whereas those on the low creep-rate side showed rapidly increasing grain-boundary sliding and migration with extensive evidence of intercrystalline cracking at 500°F. Two micrographs of the 0.94 pct Mg alloy, Fig. 3, show the increased participation of the grain boundary in the deformation process at 500°F with decreasing stress. In Fig. 3a is shown the structure of a specimen which exhibits little deformation along the grain boundaries and failed transgranularly; in Fig. 3b is shown the increased deformation along the grain boundaries at a lower stress for a specimen which showed appreciable intercrystalline cracking. The severity of intercrystalline cracking increased with increasing magnesium content at 500°F. Intercrystalline cracking disappeared in most of the specimens at 700°F and persisted only in the 5 pct Mg alloy at high creep rates. At 900°F all of the specimens deformed with extensive grain-boundary participation, including extensive grain-boundary migration. None of the alloys at 900°F showed intercrystalline cracking.

Jan 1, 1955

By Leslie W. Austen

ROTARY kiln operators will agree that some of the most severe conditions a refractory must stand occur in the hot zone of a kiln burning Portland cement, dead burn dolomite, magnesite, peri-clase, and similar materials. Frequently the operator is faced with factors beyond his control which drastically shorten the life of refractories. Shutdown due to mechanical failure can be serious if the period is of sufficiently long duration to cause the dropping of coating or the loosening of the lining. A change in slurry can affect the coating and cause ring buildup. A change in type of fuel and its effect upon the flame can cause a shift in location of the hottest zone. Weekend shutdowns or any other interruption can cause the operator trouble and may damage the refractories, since stopping and starting a rotary kiln is certainly more difficult than stopping and starting a motor. Some operators have tried to set an estimate of damage for each shutdown in equivalent days of running time. Conditions affecting the refractory may be roughly grouped in four classes: chemical attack, mechanical stress, thermal shock, and abrasion. Chemical Attack: The drive to obtain maximum production through a kiln demands maximum operating temperatures, temperatures which are limited more by the ringing up or melting of the clinker. This can cause interface temperatures at the junction of coating and refractory which require the use of a basic kiln block to withstand the chemical attack. Chemical changes take place within the refractory itself, especially in chemically bonded or unburned kiln blocks. These changes cause the formation of the ceramic or burned bond. Migrating liquids or fluxes from the kiln charge have an effect within the refractory and lead to mineral or glass formation. The alkalies, sodium and potassium, migrate into the refractory as silicates, chlorides, sulphates or other salts. They may move under capillary action or may be caused to move by volatilization with condensation in the cooler portion. Mechanical Stress: Concentrated stress may be caused by several factors or combinations thereof. I—The rings of refractories must be kept tight and rigid within the kiln, and this alone demands considerable force to hold the blocks in place. So that the force will not be concentrated, the blocks should fit the circle as perfectly as possible, with the faces in contact overall. 2—As the kiln is heated, thermal expansion takes place at the hot end of the kiln block. Since this disturbs the plane face it too can cause a concentrated stress at the two ends of the block, and shearing stress can be set up within the brick itself because of the difference in expansion between the two ends. 3—If a lining becomes loose and moves in the shell very severe stress can be set up, and as the kiln rotates this load changes and gives the effect of repeated loading. Permanent expansion of the refractory can also cause severe loading. 4—Not least important, flexing of the kiln is frequently the cause of concentrated stresses. Thermal Shock: Thermal shock, the result of heating and cooling too rapidly, occurs on starting and stopping or when a large patch of coating drops, exposing the bricks. Again, its destructive effect is often the result of phase change, liquid to solid or the reverse; dense refractories loaded with glass-forming impurities are particularly susceptible. Thermal shock is a. problem with refractories set in the wall or roof of a stationary furnace, and becomes even more serious in a rotary kiln, the tendency to spa11 being magnified with movement and concentration of stress. Uniform rate of feed and loading insures both better coating and a more uniform stress. Abrasion: If the refractories do not take a coating, abrasion can become a most destructive factor. Movement of the lining in shell or movement of loose blocks causes abrasion, which is also most destructive if the refractories do not take a coating. An analysis of the problem of basic lining for the hot zone reveals, therefore, a number of desirable characteristics: high refractoriness, basic chemical reaction, resistance to spalling, good strength at all stages, ability to take coating, true sizing, volume stability, and abrasion resistance. Increased demand

Jan 1, 1953

By R. F. Mehl, R. F. Bunshah

A fast amplifier technique has been developed for the measurement of the rate of propagation of martensite in an Fe-29.5 pct Ni alloy. The time of formation of one plate of martensite is 3x10 sec and the rate of propagation is 3300 ft per sec approximately. IT has been known for some time that the plate-like structural unit of martensite forms from austenite with great rapidity. Wiester1 and Hane-mann, Hofmann, and Wiester took motion-pictures of the transformation as it occurs in a 1.65 pct C steel; they demonstrated that a single plate formed fully in the time interval between successive frames, viz., 1/20 sec, thus setting an upper limit. Forster and Scheil,3 using an Fe-Ni alloy with 29 pct Ni, recorded the sonic characteristics of the process electrically, upon an oscillograph, setting the upper time limit at 0.002 sec. Forster and Scheil,~ measuring the change in electrical resistance in the same alloy upon a cardiograph, set a limit of 0.02 sec. Forster and Scheil5 later, employing the same alloy, improved their technique, reporting an upper limit of 7.10 sec. In studying signals of such short duration, it is an important question whether the frequency response of the electrical system used is high enough compared to frequency of the pulse measured, or, put differently, whether the system is able to reproduce without distortion the signal arising, in this case, from the formation of a single martensite plate. Forster and Scheil (referring only to their last paper) obtained signals of a frequency of 30 kilocycles (hereinafter kc); this was about the frequency response of the equipment used; thus, if the signal had a frequency higher than 30 kc, it would still appear as a signal of frequency 30 kc. All of these results thus provided upper limits only. Recent developments in electronics have made available equipment with very high frequency response, very high sweep-speeds, high gain, etc. The electrical characteristics of such equipment, used in the present study, are given in Table I. Such equipment offers obvious attraction in the study of the rate of propagation of a martensite structural unit—and perhaps of other structural alterations proceeding at a very high rate. This paper reports an attempt to develop a technique employing such equipment to measure the time of propagation of a martensite structural unit and the variation of this with temperature, with the mode of formation—athermal and isothermal—in both polycrystalline and single-crystal samples; and from such measurements to obtain the rate of propagation. As will be seen, the results obtained are useful theoretically. Materials All data presented here are for an Fe-Ni alloy of the following analysis: 29.5 pct Ni, 0.027 pct C, 0.135 pct Mn, 0.094 pct Si, balance Fe. There were several reasons for choosing this alloy: 1—it is substantially the one used by previous investigators; 2—it exhibits both the athermala and the isothermal' mode of formation of martensite, both studied in detail by Machlin and Cohen; 3—the subzero temperatures of transformation in this alloy are experimentally very convenient; 4—it exhibits the "burst phenomenon";" 5—the change in electrical resistance upon the formation of martensite, a decrease, is great, approximately 50 pct.' The polycrystalline specimens were in the form of wires of 0.025 in. diameter; the single crystals were 1x1/4x1/4 in. Experimental Methods Electrical Apparatus: Fig. 1 is a schematic drawing of the electrical circuit used. The principle used in these measurements is the same as that used by Forster and Scheil." A small direct current, about 1 to 2 amp, is passed through the sample. When a martensite plate forms, the resistance of the sample changes and a high frequency signal is generated. This signal is picked up by the probes attached to the sample, fed into the bank of amplifiers and thence to the vertical deflection plates of a cathode-ray oscilloscope. The signal itself triggers the oscilloscope trace which flashes across the tube face and is photographed by means of a 35 mm movie camera at the end of a light-tight hood. The camera has no shutter. As soon as the signal flashes

Jan 1, 1954

By D. O. Hobson, P. L. Rittenhouse

We have recently found that many lots of Zircaloy-2 and -4 tubing tested in tension deform to cross section shapes that are "polyhedral" rather than circular. The noncircular cross sections seem to result from a circumferential variation in plastic proper -ties and, therefore, in texture. We examined the diffracted X-ray intensity from (OOOl), {1010), {ll20}, and {1011} planes parallel to the tubing surface around the entire circumference. Tubing that deformed to a circular cross section showed <5 pct variation in diffraction intensity around the circumference from any of these planes. Greater intensity variations were found for all the tubing materials that developed non-circular cross sections during deformation. In each instance the number of intensity maxima and minima was consistent with the number of sides of the &apos;polyhedral" cross section. THE effects of crystallographic texture on the mechanical properties of zirconium, zirconium alloys, and other anisotropic hexagonal materials such as titanium and hafnium have been intensively studied. If the natural crystallographic anisotropy of these materials could be controlled by selected fabrication operations, a material could be produced with a texture, or preferred orientation, in which the maximum strength directions are in the stress directions of the structure. The permissible stress levels of the structure could then be increased. Rittenhouse and Pickle-simerl have shown that highly textured Zircaloy-2 plate can vary from 52,000 to 70,000 psi in tensile yield and from 62,700 to 122,000 psi in compressive yield strengths as a function of specimen orientation. Similar texture effects have been observed in Zircaloy tubing, whose mechanical properties differ depending upon whether the tubing has basal poles predominantly radial or tangential and upon the mode of testing. These same texture effects might be troublesome if the texture in the tubing is not uniform around the tube walls. This paper is concerned with the effects of nonuniform texture on the strain behavior of commercial Zircaloy tubing. BACKGROUND Previously, various lots of commercial Zircaloy tubing were tested under selected stress conditions as part of a program to determine the four quadrants of the yield locus. One of the testing procedures was uniaxial tension and it is the influence of texture variations on the tensile deformation behavior of the tubing that is of interest here. The effect of texture on the strain behavior in tubing is very apparent from a uni-axial tensile test.2 This behavior is illustrated schematically in Fig. 1 for three different tubing textures: 1) basal poles predominantly in the radial direction; 2) basal poles predominantly in the tangential direction, and 3) basal poles equally distributed between the radial and tangential directions. In the first example most of the grains are oriented for prism slip to operate to allow axial lengthening and diametral reduction of the tube. Reduction in wall thickness requires {1122} twinning, a more difficult operation than slip.* In the second example, the texture is such that *The singleCrystal analogy will be used quite often in this paper when strong texturesare being discussed. The textured material is assumed to react as if it were a single crystal aligned in the same orientation and under the same stress system as the predominant texture._____________________________________________ prism slip operates to give axial lengthening and wall thinning. Diametral reduction requires twinning and again should be more difficult to accomplish. A specimen with basal poles equally distributed between the radial and tangential directions should exhibit about equal diametral and wall strains.* Table I shows the *Diametral strain is accomplished by a combination of circumferential and longitudinal strains. But, for the purposes of this paper, it will be considered as a strain causing a change in the length of a specified diameter.__________ strain behavior of two lots of tubing with different textures. The first tube has a texture with basal poles equally distributed between the radial and the tangential directions. The ratio of true thickness strain to true diametral strain is almost unity. The second tube has a predominantly radial basal pole texture and it is apparent that most of the total strain has occurred by diameter reduction, just as one would predict. There is over three times as much diametral strain as thickness strain. RESULTS We found that specimens from certain lots of commercially fabricated tubing did not retain round cross sections during uniaxial testing. Instead, the speci-

Jan 1, 1970

By H. L. Hartman

The drop tester has proved an invaluable tool for the investigation of percussion drilling in the laboratory in "slow motion". It has allowed the process of rock penetration by impact to be studied a single blow at a time. In the present work, the relation of cratering to indexing has been determined under conditions simulating those in the bottom of the hole at atmospheric pressure. Indexed blows form craters which are influenced by others adjacent to them. Two unique effects are involved: (1) the provision of additional free faces in proximity to the point of impact and (2) the creation of subsurface damage by the previous blow(s). Both have a pronounced influence on the volume of rock removed per blow, which governs the rate of penetration in actual drilling. The emphasis in this study was placed on determining effects of index distance and impact energy on crater volume when blows were struck on a previorusly "drilled" or damaged surface, a situation most representative of down-hole conditions. The results indicated that (I) the optimum index distance on a damaged surface is greater than on a fresh, undamaged rock surface; (2) the volume of rock broken at optimum index distance is about the same for both surface conditions with die-shaped chisels but tends to be greater on a cratered surface with wedges; (3) the optimum index distance and maximum crater volume are proportional to the energy level; (4) at a given energy level, the volume of rock broken by dies generally exceeds that by wedges; and (5) maximum crater volume varies, approximately, inversely with width of die but is nearly independent of included angle of wedge. INTRODUCTION This is the third of a series l,2 of papers reporting on one phase of a continuing program of drilling research being conducted in the Rock Mechanics Laboratory at The Pennsylvania State U. The phase under consideration is crater geometry — blow energy relations in percussion drilling. While the previous papers have discussed mainly craters produced by single blows, indexed-blow studies are the subject of this paper. The basic mechanism of drilling under study here — that of penetration of a chisel-shaped bit subjected to impact — is the one employed in probably 90 per cent of all rock drilling in mining, percussion drilling. It also forms the fundamental action in nearly all oil well drilling with the so-called rotary (roller-bit) method. Here, the action is more complex, however, and may in actuality comprise rotary-percussion drilling. Certainly, the down-hole air and mud hammer drills, which superimpose percussion on rotation, belong in this latter category. In any event, impact blows constitute one of the principal mechanisms in the vast majority of drilling, mining or petroleum, and it is essential in drilling research to study percussion in all its basic aspects. Percussion drilling can be simulated in the laboratory by means of an impact drop tester. Striking one blow at a time with chisel-shaped bits, the drop tester permits study of most of the parameters in the drilling process except blow frequency and the interrelationship of certain variables. Single-blow craters, the simplest to produce, allow the determination of basic relationships, such as volume vs blow energy; while indexed craters most closely resemble the action in real drilling and provide data for the establishment of optimum operating criteria. Indexed-blow craters are those which are influenced by others in proximity. The simplest case to visualize, and the one studied in detail here, is that in which a given crater is formed adjacent and parallel to a previous crater, such that the second crater breaks into the first. A more complex situation usually exists downhole, where indexing is achieved by rotation of a radial-winged or rolling-cutter bit. But, admittedly, the phenomenon of indexing is more likely to be understood eventually if it is first studied in its simplest form, that related to parallel craters. Limited research has been conducted on indexed blows. The most complete study was that by Simon, 3,4 who proposed universal indexing curves to relate the important variables. His work, however, was conducted entirely with rows of craters formed on a

E. A. Loria (Product Metallurgical Engineer, Crucible Steel Co. of America, Pittsburgh)—In this interesting paper, our introductory work was quoted. We would like to call attention to our sequel paper on the experimental determination of oxygen in cupola-melted cast iron,20 which was not mentioned. Vacuum-fusion oxygen values (as well as hydrogen and nitrogen) were reported for nine heats of cast iron melted in the Battelle 10-in. cupola under normal operating practice and under oxidizing conditions. The oxygen analyses ranged from 12 to 68 pprn compared to the author&apos;s computed range of 10 to 80 ppm. The average amount of oxygen found in our irons was about 20 pprn and changes in the silicon content of the iron from 1.32 to 2.35 pct had no consistent effect on the oxygen content of the iron. The gas determination specimens were poured in split steel molds that produced a clean pin, 3/8 in. diam and 2 in. long. Because freezing was almost instantaneous, the pins were entirely white iron (nongraphitic). In the early stages of the investigation, the pins were transferred to a mercury-filled trap system immediately after pouring. This was done to collect gas evolved between pouring and analysis. However, it was found that during storage for 4 weeks gas evolution was negligible. Because the vacuum-fusion analysis was usually completed within 4 days of pouring, pins from later heats were not stored in the mercury-trap system. We found some evidence that cast iron picks up oxygen during long storage, because of rusting. Earlier work by the British Cast Iron Research Association has shown that cast irons may be stored for a long time without significant change in their oxygen content. The practical significance of this study (and our own) would be in the improvement of cast-iron quality. Has the author investigated this aspect and reached any conclusions on the effect of oxygen on the mechanical properties of cast iron? The second phase of our study was to determine the properties of the test bars poured simultaneously with the gas analysis specimens. We realize that there may be complicating factors attendant in this procedure.21 Results from many test specimens measuring chill depth, transverse flexure and deflection strength, spiral fluidity, and sensitivity to hardness of gray irons ranging from 12 to 68 pprn oxygen showed that the lowering of transverse strength was the only significant undesirable effect of high oxygen content. A statistical study of the chill test results21 showed that the iron containing 22 to 46 pprn oxygen had forced chill depths that were 2/32 in. below the expected value from their composition, and irons containing less than 16 ppm oxygen had forced chill depths averaging 1/32 in. greater than the expected chill depth. Higher oxygen contents, within the range of 12 to 68 pprn did not increase forced chill depth. With the wedge tests, there was a good linear relationship between carbon equivalent of the irons and their chill depth. The results indicated that oxygen contents below 50 ppm in the iron did not affect chill depth. With 50 to 70 ppm oxygen in the iron, oxygen appeared to have a slight graphitizing tendency. These results are in disagreement with the common belief in gray iron foundries that "oxidized irons" produce high chill depths. It would be appreciated if the author would comment on this subject. Gustaf Ostberg (author&apos;s reply)—In Fig. 1 the legend of line I should read 2 pct C, 1 pct Si. The author wishes to thank Mr. Loria for calling attention to his later work, which was published after the present paper was concluded. The range of oxygen contents quoted seems to agree well with the author&apos;s values. The lack of response to variations in silicon content is probably due to the fact that the oxygen content in most cases was below the saturation level. The absence of temperature dependence, even in the case of saturation, is understandable if the difficulty in formation and escape of the deoxidation products is taken into account.

Jan 1, 1960

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, &apos; AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.&apos; The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,&apos; and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By T. K. Perkins, L. R. Kern

A study of fluid mechanics, rupture of brittle materials and the theory of elastic deformation of rocks shows that, for a given formation, crack width is essentially controlled by fluid pressure drop in the fracture. Operating conditions which cause high pressure drop along the crack (such as high injection rate and viscous fluids) will result in relatively wide cracks. Conversely, operating conditions which cause low pressure drop (low injection rates and thin fluids) will result in relatively narrow cracks. Charts and equations have been derived which permit the estimation of fracture widths for a variety of flow conditions and for both horizontal and vertical fractures. INTRODUCTION There has been considerable speculation concerning the geometry of hydraulically created fractures in the earth&apos;s crust. One of the questions of practical importance is the width of fractures under dynamic conditions, i.e., while the fracture is being created and extended. Such width information could be used, for instance, to help estimate the area of a fracture generated under various conditions. Also, there has been a recent trend toward the use of large propping partiles.13, 15 Therefore is is desirable to know what factors can be varied in order to assure entry of the large particles into the fracture. There has been some work on fracture widths reported in the literature. In particular, there have been several Russian publications dealing with this sub-jeCt.1.31,3 These papers have dealt principally with the elastic theory and the application of this theory to hydraulic fractures. These studies have not led to an engineering method for estimating fracture widths under dynamic conditions. A recent paper3 has reviewed and summarized the Russian concepts. An earlier paper- from our laboratories also discussed the application of the elastic theory to hydraulic fractures. This first approach, based largely on photoelastic studies, has proved to be too simplified to accurately describe the fracturing process. However, these early thoughts have served as a guide during the development of more exact concepts. We would like to present in this paper our current concepts regarding fracture widths and some estimates of hydraulic fracture widths for several conditions. We believe that it is now possible to predict with fair accuracy the factors influencing fracture widths. Furthermore, the method of prediction has been reduced to a simple and convenient graphical or numerical calculation. CRACKS IN A BRITTLE, ELASTIC MATERIAL Many investigators2, 4, 30 have shown that competent rocks behave elastically over some range of stresses. Of course, if the tensile stress imposed upon a rock exceeds some limiting value, then the rock will fail in tension. In similar manner, there are some limiting shear stresses that can be imposed upon rocks. Hubbert and Willis11 have discussed the shear conditions which will lead to failure. Under moderate stress conditions (such as those likely to be encountered when hydraulically fracturing) and when stresses are rapidly applied, relatively, most rocks will fail in a brittle manner. Hence, for this discussion of hydraulic fractures in the earth&apos;s crust, we assume the rocks behave as brittle, elastic materials. Let us develop the discussion in the following way. (The following thoughts are applicable only to brittle materials.) 1. First we consider a brittle, elastic system. An energy balance will show the minimum pressure necessary to fracture rock, and from this pressure we calculate the minimum crack width resulting from extension of a hydraulic fracture. 2. Then we will show that, under ordinary fracturing conditions, fracture widths are appreciably greater than the minimum widths of extending fractures. In fact, we will find that crack width is controlled by fluid pressure drop in the fracture. 3. We will discuss pressure drops in fractures and resulting crack widths for various operating conditions and both vertical and horizontal fractures. 4. Finally, we will discuss the significance of these concepts, their relationship to fracturing pressures, etc. First, consider minimum fracture extension pressures. We can shed some light on this question by considering the theory proposed by Griffith7, 8 Yo explain the rupture of brittle, elastic materials. Griffith recognized that solid materials exhibit a surface energy8 (similar to surface tension in a liquid). The fundamental concept of the Griffith theory is that, when cracks spread without the application of external work (in the interior of an elastic medium which is stressed

By W. C. Leslie, R. M. Fisher, K. G. Carroll

A nitride, believed to be Si3N, has been separated from three nitrided silicon steels. Germanium nitride, Ge3N4, has been prepared from pure germanium. Comparison of the diffraction patterns indicates that the two nitrides are isomorphous; on orthorhombic structure is suggested in place of the rhombohedral structure previously reported for Ge3N4. THE possibility that a nitride of silicon may, under appropriate conditions, precipitate in silicon steels or in steels killed with silicon makes it desirable to have some positive means of identifying such a compound. One such means is the X-ray or electron diffraction pattern of the nitride. A review of the meager data in the literature indicates that the nitride most likely to form is Si3N4, a conclusion supported by the results of a study of nitrided silicon steels to be published shortly by L. S. Darken and R. P. Smith, of this Laboratory. Unfortunately, there is available no diffraction pattern for this nitride. Data have been reported, however, for Ge3N4 which, judging from the similarity between germanium and silicon, might be expected to be isomorphous with Si3N4. An effort was made, therefore, to form such a silicon nitride, to determine its composition and diffraction pattern and, if possible, its structure. To this end a series of three silicon steels was nitrided under controlled conditions with the resultant formation of nitride particles which yielded an electron diffraction pattern in situ. The particles were then extracted from the steel and an attempt was made to determine their chemical composition. X-ray and electron diffraction patterns were also obtained from the extracted particles, which indicate that the nitride is isomorphous with Ge3N4, although a complete determination of the structure has not been possible. These results show that a silicon nitride with a well-defined diffraction pattern can form in silicon steels, and they suggest that this nitride is Si3N4. Materials and Procedures The sillicon steels investigated were In the form of thin sheet or strip and had the composition shown in Table I. The 0.58 and 1.21 pct Si steels were nitrided by holding them at 1110°F in an H2-NH3 atmosphere containing 3 pct ammonia for 48 hr. The nitride particle size was increased by subsequent heating at 1500°F for 13 1/2 hr in helium. The resulting microstructure is shown in Fig. 1. The steel containing 3.20 pct Si was nitrided at 1200°F for 16 1/2 hr after which it was held in helium at 1500°F for 4 hr. Its structure as seen under the electron microscope is illustrated by Fig. 2. As would be expected from the higher silicon content and the shorter holding time at 1500 °F, the nitride particles are smaller and more numerous than those in the 1.21 pct Si steel. The ammonia-hydrogen treatment reduced the carbon content of the steels to a very low level, so no interference was encountered from carbon or carbides. In the case of the 3.2 pct Si steel, the carbon was reduced to 0.003 pct before nitriding by heating in dry hydrogen. Attempts to obtain an X-ray diffraction pattern from polished and etched surfaces of the 1.21 and the 3.20 pct Si steels were unsuccessful. However, an electron diffraction pattern was obtained from the surface of the steels. The interplanar spacings obtained from these patterns arc shown in Table 11, col. 5. The nitride particles were then extracted from all three steels by dissolving the ferrite matrix in bromine-methyl acetate, the solution used in the Beeghly method for the extraction of aluminum nitride from steel. X-ray diffraction patterns of these residues, obtained by means of a spectrometer and by a 57 mm Debye-Scherrer powder camera using filtered cobalt or chromium radiation, are given in Table II along with the pattern obtained by

Jan 1, 1953

By R. D. Russell, R. M. Farquhar

SOTOPIC tracers have become an important aid in following the progress of chemical processes in the laboratory. It has recently been found possible to utilize a system of naturally existing iso-topic tracers to obtain information about the geological history of lead ores. Common lead, such as is found in lead deposits, is a mixture of four stable isotopes having atomic weights 204, 206, 207, and 208. Of these, the last three are identical with the lead isotopes produced as stable end products of the radioactive decays of uranium and thorium: the first, lead-204, is not known to be produced on the surface of the earth by any process. Since uranium and thorium Occur in the surface regions of the earth in amounts comparable with lead, and since the half-lives of uranium and thorium isotopes are of the same order as the age of the earth, they produce the radiogenic lead isotopes in amounts comparable to the amount of nonradiogenic lead present. Every significant exposure of a sample of lead to uranium and thorium will therefore lead to the permanent alteration of the lead isotope ratios in that sample. It is this unique property of lead that serves as a means of tracing the history of a lead sample in terms of its contacts with the radioactive elements. If lead from a lead mineral has been analyzed with a mass spectrometer, the measured isotope ratios are determined entirely by the isotope ratios of primeval lead, which are identical for all minerals, and by the particular history of the sample. It follows that for samples from any particular geological area, observed differences in the isotopic composition are enough to distinguish different geological histories. An illustration of the qualitative application of this statement is given in Table I by analyses of some galenas from the western Cordillera. Samples from deposits in Pre-Cambrian sediments have very different lead isotope ratios from those of the ores in the Paleozoic sediments. Although the two types are associated closely geographically, it is apparent that they have had quite different histories and have probably been emplaced at quite different times, as the ideas outlined in the following section suggest. Even when applied quantitatively, a lead isotope analysis can never indicate a unique history of any lead sample. However, it greatly restricts the choices available and combined with other geological and geochemical data can lead to a much better understanding of the genesis of lead ores. General Character of Lead Isotope Variations: Early isotopic analyses of common leads by Nierl showed that geologically younger leads were generally richer in isotopes of masses 206, 207, and 208, with respect to that of mass 204. This regularity of measured lead isotope ratios can be easily observed by plotting each of the ratios Pb207/Pbm and Pb205/ Pb204 against the ratio Pb206/Pb204. In both graphs the points lie scattered closely about a well defined mean curve. It was immediately supposed that this regularity resulted from the growth of all leads from a common primeval lead present at some time, To, early in the earth&apos;s history. Lead in the outer part of the earth would become continually enriched in the radiogenic isotopes as a result of the uranium and thorium intimately associated with it. The subsequent extraction of some of this lead and formation of a lead mineral free of the radioactive parents provide samples of lead existing in the earth at the time of mineralization, T. Younger leads in general will be richer in the radiogenic isotopes because they have been associated with uranium and thorium for a longer time. Then lead ratios would be given by the formulae: (Pb206/Pb204)YTPb^/Pb204) +f "(u201) kdt T (Pb207Pb204)r = (Pb208/Pb204)T0 + J (U295/Pb204) k&apos; dt T (Pb208/Pb204) t = (Pb208Pb204 + J (Th204) A." dt [1] where A, A&apos;, and A" are the decay constants of U238, U285 and Th232. Summaries of measurements of radioactivity of surface rocks, such as given by Faul,2 are of limited

Jan 1, 1958

By N. K. Chen, R. B. Pond

IN the study of slip band* formation, there have been many examples to show that they do not always appear as lines traversing the entire crystal, but as segments whose ends seem to vanish in their path through the crystal. This characteristic appearance of slip bands has been witnessed under the optical microscope at various magnifications&apos;-&apos; and also under the electron microscope.&apos; A typical example of this behavior seen with the optical microscope is shown in Fig. 1. However, the slip band studies were generally conducted on polished surfaces of single or poly-crystalline metals which had been previously deformed; i.e., the load was generally released so that the observation could be made. Any picture of slip bands so obtained can represent the surface phenomenon only in a static state of the strained material. The conditions prior to their formation cannot be definitely and clearly assigned. Thus, while a segmented slip band may suggest that slip is a growth process as supposed by the theory of the nucleation of slip,V he usual appearance of suddenly and fully developed slip bands around the crystal has generally been considered as a consequence of uniform shear of the entire slip plane akin to a cataclysmic process. Little clear-cut information is available with regard to the speed at which a slip band forms, its direction of motion, the geometry of its position with regard to its neighbors, and its dependence on orientation. A description is given in this paper of experimental apparatus by which the progressive formation of slip bands can be recorded while the specimen is undergoing deformation. Qualitative and quantitative data on the dynamic formation of slip bands will be presented with special interest concerning the propagation of slip bands, the spacing of slip bands, and their relations to strain hardening. Views on the formation of slip bands are discussed and a mechanism of the unit process involved in the formation of a slip band is proposed. Preparation of Specimens Single-crystal specimens of high purity aluminum (99.997 pct), 1/8 in. square in cross-section and 1% in. long in gage length, were made by the method of gradual solidification from the liquid state. Since no machining work could be introduced in preparation of crystals of such small size, a special mold was designed for casting them to final shape. The mold consisted of two, separate, high purity graphite blocks. Generally, 20 molds were packed together in one container so that 20 specimens could be obtained by one casting operation. This was desirable since it was possible by this method to obtain groups of crystals with similar orientations. The as-cast crystals were carefully clipped from the gate, etched, and homogenized for 24 hr at 600°C. They were then very gently polished using a 4/0 paper, re-etched, and finally electrolytically polished after the method previously described by Chen and Mathewson.6 The crystallographic orientations were determined using a back-reflection, Laue method. Tensile Testing and Photographic Method The tensile testing equipment for these tests was composed of a specially designed microtensile machine, microload cell and microclip gage with necessary appurtenances. The members of the microtensile machine consisted of three parts, as shown in Fig. 2. The chassis is equipped with an oil cylinder, A, and piston, the piston being part of the movable cross-head, B. Pressure in the oil cylinder is controlled and regulated by an external pneumatic-hydraulic cell, C, which is connected to the cylinder by a Vs in. high pressure copper tube. This cell is half filled with hydraulic oil and has a needle valve, D, on the oil exit side as well as a needle valve, E, on the gas inlet side. A quick-acting valve, F, as well as a pressure gage is provided for the gas side. The oil exits into the load piston on the microtensile machine. By connecting a tank of inert gas to the gas inlet, regulated pressures were provided over the oil so that the oil would leave the cell at a rate determined by the setting of the exit needle valve, the gas pressure, and the pressure of the oil in the load piston of the microtensile machine. With this pneumatic-hydraulic appurtenance it was possible to

Jan 1, 1953

By Fred H. Poettmann

The vaporization characteristics of carbon dioxide in a League City natural gas - Billings crude oil system were studied at three temperatures, 38°. 120°, and 202°F and for pressures ranging from 600 to 8,500 psi. Variation of carbon dioxide concentration up to 12 mole per cent in the composite showed no effect on the equilibrium vaporization ratios (K values) of the hydrocarbon constituents or on the K value of carbon dioxide itself. It was shown that carbon dioxide is more soluble in crudes than in distillates which is contrary to the behavior of methane. A working chart of carbon dioxide K values is presented. INTRODUCTION The study of the equilibrium vaporization ratios of mixtures of paraffin hydrocarbons has been rather thorough.2,6,7,8,9 In the past few years considerable attention has been paid to the vaporization characteristics of the so-called noncondensable gases such as nitrogen, carbon dioxide, and hydrogen sulfide in mixtures of hydrocarbons. since they usually occur to some extent in most crude oils and natural gases.1,3,4,5 Knowledge of this behavior is useful to both the production and refining phases of the petroleum industry. This paper reports the equilibrium vaporization ratios (K&apos;s) of carbon dioxide in a mixture of League City natural gas and Billings crude oil, and compares them to those obtained in a natural gas-distillate system. The equilibrium vaporization ratios for the hydrocarbon components in this system had previously been studied by Roland.&apos; In addition to the determination of the K values for carbon dioxide, the K values for methane and ethane were also determined in order to observe what effect, if any, the presence of carbon dioxide had on these K values. The concentration of carbon dioxide was also varied in order to observe the effect of this variable on the carbon dioxide K values. EXPERIMENTAL PROCEDURE The apparatus used in this study cotlsisted of a stainless steel equilibrium cell of about 2 liters capacity. The cell was mounted on trunions permitting rocking in a thermostatically controlled oil bath. Two high pressure valves fitted with steel tubing were mounted on the top of the cell. one was used for sampling the equilibrium gas phase and the other for sampling the equilibrium liquid phase by means of an induction tube within the cell. Stainless steel tubing from the bottom of the cell led to a mercury reservoir and manifold which was connected to a free-piston type pressure gauge manufac- lured by the American Instrunlent Ctr. and to a volumetric. putrip. The temperature of the oil bath was measured by means of a ralibrated mercury-in-glass thermometer. The recorded temperatures are believed to be accurate to ±0.5 °F. The pressures are correct to 22 psi. The crude oil used in this study was stock tank oil obtained from the Wilcox formation in the Billings Field, Noble County. Okla. The natural gas was obtained from the League City Field. Galveston County, Tex. The oil was treated with anhydrous calcium sulfate in order to remove the last traces of water. To insure a supply of constant composition gas at room temperature the cylinders of League City gas were cooled to about 30°F, inverted, and the condensed liquid was allowed to drain from the cylinders. The analysis of the gas and crude are tabulated in Table I. The carbon dioxide came from Pure Carbonic, Inc., and was .stated to have a purity of 99.5 per cent or better. The procedure used to obtain samples of the equilibrium liquid and vapor was similar to that employed by others making use of the rocking type equilibrium cell.6,7,8 The equilibrium cell was evacuated and calculated quantities of carbon dioxide, natural gas, and crude oil were charged to the cell to the desired pressure. In charging the equilibrium cell an attempt was made to maintain the ratio of the natural gas to crude oil as close as possible to that employed by Roland. After the cell was charged, samples of

Jan 1, 1951

By J. E. Drury, W. M. Byers, E. J. Lynch

Measurements made with starch ~~~~s indicate that the Presence of starch serves to depress the streaming potential of a clay mud system. Measurements with pure starch slurries show that the addition of NaCl or CaO reduces the streaming potential significantly. The addition of NaOH, however, causes only a minor reduction in potential even when there are large changes in mud resistivity. INTRODUCTION In their excellent study of the streaming potential, Hill and Anderson&apos; proposed that the presence of conductive solids within the filter medium will reduce the generated potential. This theory was demonstrated with measurements on shaly sandstone cores having various "b" factors; the cores with the higher negative b factors showed markedly lower potentials. (The factor b was originally defined by Hill and Milburn2 in an expression relating the resistivity of a shaly sandstone to the resistivity of the interstitial water: log F, = log F,, + b (log 100R,)&apos;. &apos;he factor b, therefore, is a measure of the contribution of the conductive solids to the total conductivity of the sample. It has been found experimentally to be directly related to the amount of chemically exchangeable ion per unit pore volume.) In the logical extension of this hypothesis to the streaming potential created by filtration through mud cakes, they suggested that the presence of nonconductive starch in a drilling mud would have the opposite effect; i.e., it would cause the streaming POtential to be increased. The high streaming potentials that they observed with lime muds were attributed to this cause. A cross-plot of some of their results which are relevant to this discussion is given in Fig. 1. The lime-mud curves and untreated-mud curve are taken from curves given in their paper. The gyp-mud line was estimated from their statement that the measured streaming potential for gyp muds in the range of 1.5 to 2.0 ohm-m was approximately 18 mv/1,000 psi. These gyp-mud potentials were the lowest that they reported for any of the bentonitic-clay muds, and were the only ones which were less than the untreated-mud potentials. This very low streaming potential of gyp muds has also been observed in field studies.&apos; By way of comparison, a U. of Texas publication4 gives the approxi-ate compositions for lime and gyp muds shown in Table 1. These materials are added to a bentonitic-clay mud base. It can be seen that both of these muds contain significant amounts of calcium salts and that the gyp mud has the higher concentration of starch. It would appear from this and from the data shown in Fig. 1 that starch may well be the cause of a streaming-potential reduction, rather than a potential increase. EXPERIMENTAL A series of streaming-potential experiments has been performed using a cell of a design similar to that reported by Wyllie.5 Calomel electrodes were used in both the mud slurry and the filtrate. Pressure in the cell was generated with high-pressure nitrogen. The primary objective of the investigation was to determine the effect of starch on the potential. Five different slurries were made which ranged in composition from untreated ben-tonitic mud (Baroid Aquagel) to a pure starch suspension (Baroid Im-permex). The intermediate slurries were prepared by mixing together a 9-lb/bbl clay mud with a 12-lb/bbl starch suspension in the ratios 1:3, 1:1 and 3:1. When starch was used alone, it was necessary to use an 18-Ib/bbl mixture, since leaner mixtures would not form a suitable filter cake. The clay mud used in the experiments was aged for three months before use. In addition to this series of measurements on the starch-clay mud mixtures, other experiments were performed to determine the effect on the potential of the absolute starch and Aquagel concentration, and the effect of adding various chemicals. RESULTS The effect of starch on the streaming potential is shown clcarly in Fig 2. Increasing percentages of starch resulted in n continually decreasing

By Fred H. Poettmann

The vaporization characteristics of carbon dioxide in a League City natural gas - Billings crude oil system were studied at three temperatures, 38°. 120°, and 202°F and for pressures ranging from 600 to 8,500 psi. Variation of carbon dioxide concentration up to 12 mole per cent in the composite showed no effect on the equilibrium vaporization ratios (K values) of the hydrocarbon constituents or on the K value of carbon dioxide itself. It was shown that carbon dioxide is more soluble in crudes than in distillates which is contrary to the behavior of methane. A working chart of carbon dioxide K values is presented. INTRODUCTION The study of the equilibrium vaporization ratios of mixtures of paraffin hydrocarbons has been rather thorough.2,6,7,8,9 In the past few years considerable attention has been paid to the vaporization characteristics of the so-called noncondensable gases such as nitrogen, carbon dioxide, and hydrogen sulfide in mixtures of hydrocarbons. since they usually occur to some extent in most crude oils and natural gases.1,3,4,5 Knowledge of this behavior is useful to both the production and refining phases of the petroleum industry. This paper reports the equilibrium vaporization ratios (K&apos;s) of carbon dioxide in a mixture of League City natural gas and Billings crude oil, and compares them to those obtained in a natural gas-distillate system. The equilibrium vaporization ratios for the hydrocarbon components in this system had previously been studied by Roland.&apos; In addition to the determination of the K values for carbon dioxide, the K values for methane and ethane were also determined in order to observe what effect, if any, the presence of carbon dioxide had on these K values. The concentration of carbon dioxide was also varied in order to observe the effect of this variable on the carbon dioxide K values. EXPERIMENTAL PROCEDURE The apparatus used in this study cotlsisted of a stainless steel equilibrium cell of about 2 liters capacity. The cell was mounted on trunions permitting rocking in a thermostatically controlled oil bath. Two high pressure valves fitted with steel tubing were mounted on the top of the cell. one was used for sampling the equilibrium gas phase and the other for sampling the equilibrium liquid phase by means of an induction tube within the cell. Stainless steel tubing from the bottom of the cell led to a mercury reservoir and manifold which was connected to a free-piston type pressure gauge manufac- lured by the American Instrunlent Ctr. and to a volumetric. putrip. The temperature of the oil bath was measured by means of a ralibrated mercury-in-glass thermometer. The recorded temperatures are believed to be accurate to ±0.5 °F. The pressures are correct to 22 psi. The crude oil used in this study was stock tank oil obtained from the Wilcox formation in the Billings Field, Noble County. Okla. The natural gas was obtained from the League City Field. Galveston County, Tex. The oil was treated with anhydrous calcium sulfate in order to remove the last traces of water. To insure a supply of constant composition gas at room temperature the cylinders of League City gas were cooled to about 30°F, inverted, and the condensed liquid was allowed to drain from the cylinders. The analysis of the gas and crude are tabulated in Table I. The carbon dioxide came from Pure Carbonic, Inc., and was .stated to have a purity of 99.5 per cent or better. The procedure used to obtain samples of the equilibrium liquid and vapor was similar to that employed by others making use of the rocking type equilibrium cell.6,7,8 The equilibrium cell was evacuated and calculated quantities of carbon dioxide, natural gas, and crude oil were charged to the cell to the desired pressure. In charging the equilibrium cell an attempt was made to maintain the ratio of the natural gas to crude oil as close as possible to that employed by Roland. After the cell was charged, samples of

Jan 1, 1951

By J. O. Brittain, N. R. Adsit

A number of zinc bicrystal specimens with the grain boundary loaded in simple shear were plustically deformed in creep in a vacuum at 200°C and under an argon atmosphere at 350°C. The results indicated that the amount of grain boundary sliding at a given time was controlled by the slip in the grains and was proportional to the resolved shear stress on the slip plane. Curves of grain boundary sliding vs time were found to be cyclic with no regular periodicity. ALTHOUGH grain boundary sliding (G.B.S.) has been investigated in a number of different types of tests on various materials there is substantial disagreement on the interpretation of the various observations. Gifkins1 has presented a comprehensive review of the subject of G.B.S. and fracture. He reports that the activation energy for high-temperature creep is equal to that for volume self-diffusion and that pure metals show less tendency towards intercrystalline fracture than alloys. Pure metals show appreciably greater grain boundary migration than alloys, and both grain boundary migration and grain boundary sliding follow the same general trend in time as plastic deformation during creep.&apos; While there have been a number of different mechanisms proposed to account for G.B.S., none of the models explains all the results. Since zinc has only one prominent slip system, it was hoped that experiments on G.B.S. in zinc bicrystals might enable us to separate the effect of grain boundary angle and the effect of matrix slip and thereby resolve at least one part of this complex phenomenon. EXPERIMENTAL PROCEDURE Bicrystals of pure zinc (99.99 pct) were grown by a Bridgeman technique in a furnace having a gradient of 20°C per in. The bicrystals were seeded to a desired orientation and grown in a split graphite mold which was 3/4 by 5/8 by 8 in. The mold was enclosed in a Pyrex tube and the tube was evacuated and then filled with a small amount of argon before it was placed in the furnace. The growth rates were 1/2 to I in. per hr for the bicrystals and 1/2 to 3 in. per hr for the single-crystal seeds. The longitudinal V notches served to hold the grain boundary in position during the growth process. A schematic rep- resentation of a specimen which had been cut with a jewelers saw from the bicrystals is shown in Fig. 1. All specimens of a series were cut from the same crystal, some of which were 7 in. in length. After specimen preparation the boundary was approximately 5/16 in. long and the V notches had a radius of 1/16 in. The boundaries were straight at a magnification of X100 with the exception of a few which had a gradual radius of curvature of greater than 3.2 in.-1. Laue back-reflection photograms were taken on the specimens to check the orientation of grains in the bicrystals. The method of relating the orientation of the two lattices is shown in Fig. 1, where 0 is the angle between normal to the boundary and the trace of the basal plane, is the angle in the boundary between the trace of the basal plane and a line parallel to the V notch, and x is the angle in the basal plane between the Burgers vector and the perpendicular to the grain boundary. After mechanical polishing the specimens were chemically polished.2 Subsequent to the polishing operation the specimens were encapsuled under a vacuum of better than 25 annealed at 340°C for 1 hr to remove the effects of this handling, and again chemically polished. Finally, fiduciary marks were scribed on the specimen using a micromanipulator. Creep tests, which were conducted in a modified Bausch apparatusS with the boundary loaded in simple shear, were run at a constant load (since the boundary area remained essentially constant this is approximately constant grain boundary stress). The temperature was controlled to ±1/4°C as measured on a semiprecision potentiometer with a calibrated thermocouple. The specimens were tested in a vacuum of better than 0.5 at 200°C and in purified argon at a pressure of 1/2 atm at 350°C. The op-

Jan 1, 1965