By J. M. Tobin, L. H. Cadoff, L. M. Adelsberg

The reaction between liquid zirconium and graphite at temperatures above 2000 °C has been investigated. The reaction products were found to be carbon-saturated zirconium metal and ZrC which formed between the graphite and the metal. Parabolic growth behavior was observed for the ZrC Phase at all temperatures of this investigation. The parabolic growth constant at temperatures between 2000° and 2860°C was measured to be 1.83 exp 84,300/RT) sq cm per sec. The reaclion mechanism was proposed to be the rapid carbon saturation of the liquid metal and the formation of ZrC at the metal-carbide interface with diffusion of carbon through the ZrC, the "rate - determining step" of the reaction. The concentration-independent diffusion coefficient of carbon in ZrC, (DZrC), was expressed as 0.95 exp? 78,700/RT) sq cm per sec. This value mas calculated using the temperature-invariant ZrC phase fields proposed in the literature. The [ZrQiq)] — [ZYQiq) + ZrC] phase boundary over the temperature range 2000° to 2800°C was determined and the ZrC + C eutectic temperature was found to be 2890° ± 50°C. ThE Group IV and VB transition-metal refractory carbides are of interest because of their high melting points, high temperature strength properties, and relative inertness in certain corrosive environments. The present-day understanding of these materials, however, is limited by the general unavailability of accurate and reliable physical and chemical property data. This is due primarily to the difficulties associated with the preparation of suitable, high-density, high-purity carbide samples, and the achievement and control of uniform high-temperature environments. Accurate measurement of temperature is also an important factor limiting the reliability of reported data. The Zr-C reaction was selected for investigation because of the high melting point (>34000C) and favorable nuclear properties of the reaction product, ZrC. The direct reaction method afforded an opportunity to obtain kinetic data on the fully dense carbide. In this paper, layer-growth techniques were used to estimate the diffusivity of carbon in ZrC and to investigate the phase equilibria in the Zr-C system at temperatures above 2000°C. EXPERIMENTAL PROCEDURES AND DATA Crystal bar zirconium (99.9 pct Zr), purchased from the Nuclear Materials and Engineering Corp., and ZTA graphite (99.9+ pct) were used in this study. The analyses of the materials are listed in Table I. A schematic of the high-temperature carburization apparatus is shown in Fig. 1. The sample was a zirconium metal charge in a 1/2 -in.-ID graphite crucible which was capped with a tightly fitting graphite stern. The crucible and stem were designed to closely approximate black-body conditions. The graphite crucible was packed in lampblack (outgassed 1 hr at 2100°C) which provided insulation and thermal stability to the system. The inert atmosphere was maintained by a constant flow of high-purity argon or helium gas. The nozzle-diffuser section on the top flange was sufficient to prevent back-diffusion of air into the system. Chemical analysis of the carburized samples revealed oxygen and nitrogen concentrations of less than 44 and 20 ppm, respectively. The sample was heated by induction with a Westing-house 5 kw-450 kc power source. Temperature was measured with a Milletron two-color pyrometer which was sighted into the crucible by reflection from an overhead front surface mirror. Optical losses due to glass absorption and light reflection at air-glass interfaces were minimized by the employment of the dynamic-gas seal. It was found that no correction was required for the front surface reflector. The pyrometer was calibrated periodically against a U.S. Bureau of Standards tungsten ribbon secondary standard. Temperatures inside the crucible were also calibrated against the Zr-ZrC eutectic (1850°C)1 and the Nb-Nb2C eutectic (2335°C)2,3 temperatures and agreed to within ±10°C of these values. The temperature was controlled by manually adjusting the power input; variations of

Jan 1, 1967

By J. E. Andersen, J. Halpern, C. S. Samis

In the presence of oxygen, galena is oxidized in an aqueous medium containing sodium hydroxide, in accordance with the following reaction: PbS + 2O2 + 3OH ? HPbO2 + SO4 = + H2O A novel method was devised for following this reaction which takes place in an autoclave under oxygen pressure, by measuring the concentration of HPbO2- in the solution with a cathode ray polarograph employing stationary platinum electrodes. Using this procedure a study was made of the kinetics of the reaction, in which the effect of a number of variables, including temperature, oxygen pressure, NaOH concentration, and agitation, on the rate, were determined. The results of this study are described and discussed, in terms of possible mechanisms for the reaction. IT is known that sulphide minerals can be oxidized in aqueous media in the presence of oxygen under pressure. Reactions of this type can be classified in two categories depending upon whether the products of oxidation are insoluble or soluble in the aqueous medium. An example of the first type of reaction is the oxidation of pyrite in alkaline solutions, giving rise to an insoluble iron oxide. The kinetics of this reaction have been investigated and its mechanism established.' It has been applied in the oxidation of iron sulphides present in refractory gold ores to improve the subsequent recovery of gold by cyanida-tion.' The second type of reaction finds application where it is desired to recover the metal by leaching during oxidation. In this case a medium is selected in which the oxidized mineral is soluble. For example, nickel, copper, and cobalt sulphide ores can be treated by oxidation in the presence of a solution of ammonia dissolving the nickel, copper, and cobalt as the metal ammine sulphate salts.:' A similar treatment has also been reported to apply to zinc sulphide ores.' It is known that lead sulphate is soluble in solutions of sodium hydroxide or ammonium acetate. It should therefore be possible to dissolve the lead from galena ores by aqueous oxidation with oxygen under pressure using either of these solutions. The applicability of the ammonium acetate treatment has been investigated and confirmed in a recent study.' The present paper describes the results of a similar study in which the kinetics of the oxidation of galena in sodium hydroxide solutions have been investigated. The object of this investigation was pri- marily to obtain information of a fundamental nature relating to the kinetics and mechanism of this reaction. The use of pulps of comminuted ore in a study of this type is undesirable because of the difficulty in controlling and measuring the surface area. The measurements were therefore made using galena crystals of measured surface area and in this way absolute reaction rates were obtained. The reaction was found to proceed as follows: PbS + 2O2 + 3OH ? HPbO2 + SO4 + H2O [I] The products are sodium plumbite and sodium sulphate salts which dissolve in the aqueous solution. The reaction studies were carried out in an autoclave in which a desired pressure of oxygen was maintained. The reaction was followed by measuring the concentration of lead in the solution with a cathode ray polarograph. The results obtained in this investigation are presented and discussed in the present paper. Experimental Materials: The crystals of galena were obtained from Violamac Mines, Sandon, B. C. The following impurities were indicated by spectrographic analysis carried out by the Provincial Assay Office, Victoria, B. C.: Sn, 0.02 to 0.2 pct; Sb, 0.07 to 0.7; Zn, 0.01 to 0.1; Si, Fe, Mg, As, less than 0.05 pct; Ag, 126 oz per ton, the latter determined by standard fire-assaying procedure. After cutting a specimen measuring approximately 5x7x12 mm, the crystal surfaces were ground parallel to the 100 axes using No. 2 emery, washed with water, and the dimensions were measured with a micrometer. Oxygen gas was of commercial grade and supplied in cylinders by Canadian Liquid Air. Solutions were made up with chemicals of chemically pure grade and distilled water. Equipment: Autoclave: The autoclave used in these studies was constructed of stainless steel and

Jan 1, 1954

By R. H. Edsal, G. Horvay

The transient one-dimensional heat-conduction equation is solved for two semi-infinite media, at different initial temperatures, brought into (poor) thermal contact. It is shown that the two interface temperatures gradually approach the well-known, instantaneously assumed, common interface temperature of the case of zero contact resistance. The present analysis, with slight modifications, may be used in fair approximation also for the class of problems involving a change of phase. One particular application of the boundary value problem solved in this paper concerns the determination of the temerature distribution in metal castings and molds.P This problem has been treated extensively by analytical methods (see e.g., the literature listed in Refs. 1 to 4) by electrical analogs (see e.g., Refs. 11 to 14) and also by experimental methods (see the literature listed in Refs. 4, 5), but prior to the work of Pellini and Ruddle the experimental results were rather unreliable. Immediate motivation for the work described in this paper was to better understand the results of Pellini,' which are typified by the curves of Fig. 1. Pellini cast 20-in. high, 7-in. sq steel ingots into cast-iron molds of various thicknesses. He measured the temperatures at mid-height, at a number of stations in the casting and the mold, and obtained the cooling curves shown in Fig. 1. The most conspicuous thing about Fig. 1 is the large temperature discontinuity at the interface between casting and mold, due presumably to the shrinking away of the casting from the wall and the attendant creation of an airgap, as the casting cools. Such a contact resistance slows down the anticipated freezing rate; an analytical prediction of this is of much interest in foundry practice. The determination of the effect of contact resistance in the presence of a change of phase will be dealt with, by an approximate method, in a separate paper.' In the present paper the much simpler problem is considered in which there is contact resistance but no change of phase. This problem frequently arises in the analysis of aircraft structures.+ It can initial temperature, and may be regarded as semi-infinite. We suppose the thermal properties in the two media to be time, temperature, and space independent; there are no sources or sinks within the media. In Fig. 2(a) we illustrate, schematically, the case of no contact resistance. The semi-infinite media "0" and "2:' initially at temperatures 8 (- m) and 8(+ -), respectively, are brought into contact at time t =0. A common interface temperature 8,i = is instantaneously established, and thereafter remains constant. Temperature curves are drawn for three instants of time. When there is contact resistance between the two media, the temperature equalization occurs as sketched in Fig. 2(b). Fig. 2(c) illustrates a temperature curve, using the dimension-less notation Barber-Weiner-Boley6 have stated the equations [23a, b] given below, which govern the heat transfer in the two media, and solved them for a rather complicated special case. In their example both media "O" and "2" are finite, are insulated at their far ends, and there is steady heat input into medium 2. In Eq. [27] we give the general solution of the most important special case, where the two media are semi-infinite and there are no sources or sinks. In this case the results may be stated in simple closed form. In Fig. 3, to be discussed in the next section, we illustrate the variation of the interface temperature when steel at 2760" is brought into contact with iron at 100". This example, if we disregard the effect of the heat of fusion, is comparable to Pellini's experimental results, Fig. 1. (Unfortunately, however, experimental determination of the interface temperatures was difficult to carry out, and hence Fig. 1 is not very accurate near the interface.) In Figs. 4 and 5 of the following section, we similarly compare Pellini's sandcasting tests with analytical results for the case where steel at 2760" is brought into contact with sand at 100". It will be pointed out that, insofar as the interface temperatures are concerned, heat of fusion has a minor effect, and so the present approximation, with small modifications, may be

Jan 1, 1961

By C. Zener

HE present paper has its origin in an attempt A by the author, extending over the last several years, to understand the influence of the magnetic properties of the constituent atoms upon the various properties of metals and alloys. During this study the author has been impressed by the important role which magnetism plays in the many facets of metallurgy. In writing this paper he has attempted to convey to his colleagues some concept as to the role magnetism will play in the future development of metallurgy. In some of the subjects herein discussed, such as the influence of magnetism upon phase boundaries and upon mechanical properties, only general thermodynamical properties associated with ferromagnetism are introduced. For these subjects, it is not anticipated that any serious differences of opinion will be encountered. A discussion of the other subjects requires the adoption of a quite specific model of the magnetic structure of the metal. This model is discussed under "Magnetic Shells and Their Interactions." The simple model adopted in this paper has been criticized' as being mathematically inconsistent. This criticism has been ably silenced by Dr. W. J. Carr' of this laboratory. The simple model adopted in this paper has been criticized as being inconsistent with observations on magnetic structure using neutron diffraction. This apparent discrepancy has been resolved by Bader3 who has shown that the finite velocity of neutrons prevents neutron beams from detecting the anti-ferromagnetic structure of the type predicted by the simple model adopted in this paper. Magnetic Shells and Their Interactions An electronic shell of an atom is specified by two symbols.' The first symbol is a number and denotes the total quantum number of the shell. The second symbol is a letter and denotes the orbital angular momentum of each electron within the shell. The letters s, p, d, f are used to denote an orbital angular momentum of 0, 1, 2, 3, respectively, in units of h/2a, where h is Planck's constant. As we pass from scandium to nickel in the first transition period, we eraduallv fill the 3d shell. This shell is responsible for ferromagnetism and hence may be called the magnetic shell. The component of the orbital angular momentum along some specified direction must be an integral multiple of h/2~. Thus, for a d electron this component can have any one of the values —2, —1, 0, 1, 2 times h/2a. In addition to its orbital angular momentum, each electron has an intrinsic angular momentum, hereafter called spin, due to a rotation about its own axis. This spin can have either of two components + Yz (h/2a) or — Yz (h/2~) along the specified direction. A fundamental principle of atomic structure, known as Pauli's exclusion principle, is that no two electrons in a given shell may have identical components of orbital angular momentum simultaneous with identical components of spin. The 3d shell thus may have at most ten electrons. Since an intrinsic angular momentum of a charged particle is necessarily associated with a magnetic moment, the spin of an electron may be thought of as referring to either this angular momentum or to the associated magnetic moment. The electron configuration of the ground state of the isolated atoms in the first transition row is reproduced in Table I. The superscript represents the number of electrons in each shell. For the purpose of this paper, the most important principle of atomic structure relates to the manner in which electrons are added to a shell as the atomic number is increased. This principle, commonly known as the principle of highest multiplicity or more simply as Hund's rule, states that within a given shell the maximum number of electrons have spins pointing in the same direction as is consistent with Pauli's exclusion principle. An application of this principle to the d shell is illustrated in Fig. 1, where the spin structure is given for shells containing from 1 to 10 electrons. The physical basis of Hund's rule is the exchange energy discussed first by Heisenberg in 1928. This is a coupling between electrons with parallel spins (spins pointing in the same direction), the coupling

Jan 1, 1956

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By H. W. Winkler, Discussion, V. L. Forsyth

The development of a new gar lift valve has removed many of the obstacles limiting over-all gas lift efficiency. The valve is pressure charged in place in a well, and operating pressure can be changed without pulling. Temperature and gas gradient compensation have been eliminated. Intermitting and constant flow installations, using conventional pressure-charged valves, are compared with designs incorporating the new automatic stabilizer controlled valve. Specific well performance data are presented. The means of obtaining and controlling multiple-point injection of gas are explained and contrasted with single point injection. The effect on small diameter strings and multiple string installations is discussed. The effect of flowing temperature gradient on a design using conventional pressure-charged valves, the limitations imposed by such temperature, and the obvious benefits which result from the use of automatic stabilizer controlled valves are shown. Reduction of gas requirements is stated mathematically and demonstrated with specific examples which are identified as to oil company and well. Increased fluid recovery resulting from greater drawdown is illustrated. The economic advantages are mentioned with emphasis on reduction of capital expenditures, as well as reduction in operating expenses. INTRODUCTION Much of the engineering and research work performed with gas lift has been based upon the supposition that under producing conditions gas would be injected at a single point in a well. Many tests were performed in determining the optimum size of the opening through which gas would be passed and the exact placement of the valve equipment. The objectives in a gas lift installation are to unload the well and to efficiently produce the well after it is unloaded. Until recently, the function of upper valves was simply to unload the well. An operating valve located at a proper place in a well served as a single injection point for lifting liquid to the surface. The basic problem in using such equipment is to arrive at operating depth with sufficient operating pressure to efficiently lift the liquid. Few gas lift installations are designed with all required well data available. However, regardless of the quality and availability of data, and regardless of the accuracy of the design, there is the practical problem of preparing and placing gas lift equipment in the well in exact accordance with the plans and intentions of the engineer. In recognition of these and many other problems, attention was directed toward a means of removing the need for temperature and gas gradient compensation, a way to change the gas lift installation to meet the changing requirements of the well itself, and a manner of compensating for changes in oil-water content, fluid volumes, PI, and bottom-hole pressure resulting from flood or repres-suring activity. A device which could actually set and change the operating pressure of gas lift valves in the well would meet most of these needs. There now exists a new gas lift valve which fulfills the original objectives and in so doing actually accomplishes much more. With this device, called an Automatic Stabilizer Controlled valve, there is an exact matching of valve operating pressure and well conditions. Gas is injected at more than one point in the well, thereby making controlled multiple-point injection of gas a reality. Installation calculations are materially simplified and the need for basic temperature and gas gradient data no longer exists. Section I—The Automatic Stabilizer Controlled Valve The operation of the ASC valve is more easily understood by first studying a conventional pressure-charged valve and then inserting the stabilizer element to observe the changes which result. Fig. 1 is a schematic of a conventional precharged pressure-operated valve. The pressure in the dome pd, acts downward, against the area of the bellows A,, to hold the valve closed. The resulting force Bf plus the spring effect of the bellows Sf represents the total force acting to close the valve. Correspondingly, the tubing pressure ptbg works upward against the port area Atbg and the casing pressure pc works upward against a portion of the area of the bellows

Jan 1, 1965

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,' small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.'-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By Horace Pops

Martensitic transformation has been studied during cooling and heating in ß-phase Cu-Zn alloys to which small additions have been made of Ni, Ag, Au, Cd, Ga, In, Si, Ge, Sn, and Sb. The start and finish of the martensitic reaction and the variation of transformation temperature with third-element content were determined by electrical-resistivity measurements from alloys which had either constant zinc contents or constant values of electron concentration. All of the third elements, except nickel, lowered the transformation temperature if the results were plotted along the lines of constant zinc contents in each ternary system. A significant difference in the rate of lowering of the transformation temperature per atomic percent of the third element was observed for elements which had the same nominal valence. No systematic variation of transformation temperature with the valence of the third element was observed. It is suggested that the observed increase in transformation temperature for nickel-bearing alloys is due to the transfer of electrons from the conduction band of the alloy to virtual bound states. However, electron concentration is not the most important factor controlling the instability of the 0 phase. The transformation temperatures of the ternary alloys can be predicted from the following approxilnate expression: Ms (°K) = +3280 - 80 Zn + 8 Ni - 30 Ag - 12 Au - 140 Cd -90 Ga- 145 In - 80 Ge -175 Sn - 120 Si - 150 Sb MOST binary ß -phase alloys based upon the noble metals copper, silver, and gold are unstable at low temperatures and transform spontaneously by a martensitic reaction. This transformation has been studied recently in the ordered bcc ß'-phase Cu-Zn binary al1oys1,2 where the transformation temperature is below the room temperature and decreases with an increase in zinc content. It has been reported that the transformation temperatures can be raised above room temperature by small additions of a third element such as silicon3,5 or gallium,4,5 but no quantitative study has been made. The transformation temperature of different binary alloys can be altered by third-element additions. For example, it was shown that nickel and copper may have a large effect on the Ms temperature of CU-Al6 and Au-cd7 alloys. The present investigation was made to determine systematically the influence of various third elements on the martensite-transformation temperature of Cu-Zn ß-phase alloys. Since these alloys have an electronic origin,' alloy compositions were chosen so that the transformation temperatures could be determined at constant zinc contents or at constant values of electron concentration. I) EXPERIMENTAL PROCEDURE Ten ternary alloy systems were obtained by adding nickel, the noble metals silver and gold, and some B-subgroup elements to a Cu-Zn matrix. These are arranged according to their rows and columns in the Period Table as follows: Each ternary alloy was prepared by melting and casting weighed quantities of high-purity metals (99.99+ pct) in sealed quartz tubes under a partial pressure of helium to make a 4-g ingot. The molten alloys were shaken vigorously and then quenched in water. Since the weight loss was negligible, the compositions of the ingots after casting and annealing were assumed to be the same as the nominal compositions. The ingots were homogenized after casting in helium-filled Vycor tubes for 24 hr at temperatures between 750" and 810 C and quenched into brine. Metallographic examination revealed that all alloys were homogeneous, poly crystalline ß-phase alloys, and that the grain size was in the range 1 to 5 mm. Electrical-resistivity measurements were made to determine transformation temperatures of the ternary alloys during continuous cooling or heating. Transformation temperatures of the ternary alloys can be determined by electrical-resistivity measurements since the resistance of the martensitic phase is much higher than that of the 0' phase. The technique has been described previously in connection with a study of Au-Zn alloys.9 The reproducibility of transformation temperature was approximately ±6°C. II)RESULTS A hysteresis was always observed in electrical-resistivity curves and was usually less than about 12°C.

Jan 1, 1967

By Brahm Prakash, R. Schuhmann

Chemical conditions for flotation and nonflotation of quartz with oleic acid as collector and barium, calcium, aluminum, iron, and tin as activators were studied using a simple vacuum-flotation technique in glass-stoppered graduates. The detailed study of barium activation led to an interpretation based on ideal Langmuirian chemi-sorption. FLOTATION of quartz is of practical importance as something to be avoided in soap-floating many types of ores. Clean, unactivated quartz is not floated with fatty acids and soaps, such as oleic acid and sodium oleate, in the quantities normally used for flotation. However, data in the literature indicate that almost any multivalent cation will activate quartz if given an opportunity. Thus, a common problem is to prevent activation of quartz by the various inorganic cations inevitably present in flotation pulps. Wark and his coworkers1 have demonstrated the reversibility of the chemical reactions and adsorptions involved in the activation, depression, and collection of the common sulphide minerals. The procedure in much of their work was to bring a mineral surface to equilibrium with solutions of known pH, collector concentration, and activator concentration, and then to test the floatability of the mineral by contact-angle measurement. From the data, graphs were constructed with pH and reagent concentrations as coordinates. These graphs show fields of flotation and fields of nonflotation, separated by narrow transition regions whose locations are shown by so-called contact curves. From the shapes and locations of the contact curves, which roughly separate fields of flotation from fields of nonflotation, a quantitative understanding of the interaction of the reagents with each other and with the minerals often can be deduced. The study of quartz flotation to be described in this paper follows in broad lines the approach of Wark and coworkers. That is, pH, activator concentration, and collector concentration were varied to find equilibrium conditions of flotation and non- flotation, and the results are presented graphically by means of contact curves. However, instead of testing for floatability by measuring the contact angle on a polished surface, a simple vacuum flotation technique was developed and used. Purified oleic acid was the collector and terpineol the frother. Barium activation was studied in some detail, and exploratory studies were made of activation with calcium, aluminum, ferric iron, and stannic tin. Preparation of Materials Quartz: Large lumps of high-grade vein quartz were crushed dry in a cone crusher and rolls. The —20, +28-mesh portion was screened out and used in the subsequent steps. This material was passed through a high-intensity magnetic separator to discard iron, then leached twice with hot concentrated HCl and washed repeatedly with distilled water. The cleaned sand was then wet ground with porcelain balls in a porcelain pebble mill, deslimed repeatedly by settling and decantation to discard —800-mesh material, and again washed with hot HCl followed by distilled water. The resulting stock of quartz was stored under water. Chemical analysis gave 99.8 pct SiO2. Table I gives the size analysis of the quartz used for flotation tests. Calculations from these data, using shape factors given by Gaudin and Hukki9 indicate a specific surface of about 500 cm2 per g. Blank flotation tests in distilled water, and in water with added frother, showed the prepared quartz to be completely nonfloatable and thus indicated the absence of organic contamination. Oleic Acid: The preparation of oleic acid was based on fractional vacuum distillation of methyl oleate2,3 followed by regeneration of oleic acid, and finally fractional crystallization of oleic acid from acetone solutions at low temperatures." The pure oleic acid was stored in a refrigerator. The iodine number of the oleic acid was found to be 90.0 (theoretical 89.93). Oleic acid was used in the form of a dilute water solution of sodium oleate, after preliminary flotation tests showed no effects of form of addition and order of addition of reagents when an adequate conditioning time (that is, 30 min) was provided. Other Reagents: Sodium hydroxide solutions low in carbonate were prepared by first making 1:1

Jan 1, 1951

By Brahm Prakash, R. Schuhmann

Chemical conditions for flotation and nonflotation of quartz with oleic acid as collector and barium, calcium, aluminum, iron, and tin as activators were studied using a simple vacuum-flotation technique in glass-stoppered graduates. The detailed study of barium activation led to an interpretation based on ideal Langmuirian chemi-sorption. FLOTATION of quartz is of practical importance as something to be avoided in soap-floating many types of ores. Clean, unactivated quartz is not floated with fatty acids and soaps, such as oleic acid and sodium oleate, in the quantities normally used for flotation. However, data in the literature indicate that almost any multivalent cation will activate quartz if given an opportunity. Thus, a common problem is to prevent activation of quartz by the various inorganic cations inevitably present in flotation pulps. Wark and his coworkers1 have demonstrated the reversibility of the chemical reactions and adsorptions involved in the activation, depression, and collection of the common sulphide minerals. The procedure in much of their work was to bring a mineral surface to equilibrium with solutions of known pH, collector concentration, and activator concentration, and then to test the floatability of the mineral by contact-angle measurement. From the data, graphs were constructed with pH and reagent concentrations as coordinates. These graphs show fields of flotation and fields of nonflotation, separated by narrow transition regions whose locations are shown by so-called contact curves. From the shapes and locations of the contact curves, which roughly separate fields of flotation from fields of nonflotation, a quantitative understanding of the interaction of the reagents with each other and with the minerals often can be deduced. The study of quartz flotation to be described in this paper follows in broad lines the approach of Wark and coworkers. That is, pH, activator concentration, and collector concentration were varied to find equilibrium conditions of flotation and non- flotation, and the results are presented graphically by means of contact curves. However, instead of testing for floatability by measuring the contact angle on a polished surface, a simple vacuum flotation technique was developed and used. Purified oleic acid was the collector and terpineol the frother. Barium activation was studied in some detail, and exploratory studies were made of activation with calcium, aluminum, ferric iron, and stannic tin. Preparation of Materials Quartz: Large lumps of high-grade vein quartz were crushed dry in a cone crusher and rolls. The —20, +28-mesh portion was screened out and used in the subsequent steps. This material was passed through a high-intensity magnetic separator to discard iron, then leached twice with hot concentrated HCl and washed repeatedly with distilled water. The cleaned sand was then wet ground with porcelain balls in a porcelain pebble mill, deslimed repeatedly by settling and decantation to discard —800-mesh material, and again washed with hot HCl followed by distilled water. The resulting stock of quartz was stored under water. Chemical analysis gave 99.8 pct SiO2. Table I gives the size analysis of the quartz used for flotation tests. Calculations from these data, using shape factors given by Gaudin and Hukki9 indicate a specific surface of about 500 cm2 per g. Blank flotation tests in distilled water, and in water with added frother, showed the prepared quartz to be completely nonfloatable and thus indicated the absence of organic contamination. Oleic Acid: The preparation of oleic acid was based on fractional vacuum distillation of methyl oleate2,3 followed by regeneration of oleic acid, and finally fractional crystallization of oleic acid from acetone solutions at low temperatures." The pure oleic acid was stored in a refrigerator. The iodine number of the oleic acid was found to be 90.0 (theoretical 89.93). Oleic acid was used in the form of a dilute water solution of sodium oleate, after preliminary flotation tests showed no effects of form of addition and order of addition of reagents when an adequate conditioning time (that is, 30 min) was provided. Other Reagents: Sodium hydroxide solutions low in carbonate were prepared by first making 1:1

Jan 1, 1951

By A. R. Troiano, R. F. Hehemann

The influence of partial decomposition to high temperature bainite on reaction kinetics at a lower temperature has been studied in two alloy steels. Reaction at the lower temperature is retarded by the prior treatment, and the extent of decomposition may be reduced. Interpretation of these results is based on a mechanism involving a limitation in the nucleation and growth of bainite plates. OF the major transformations in steel, the characteristics and general behavior of the bainite reaction are probably the least understood and appreciated. Limitations of space preclude a critical evaluation of the present status of the bainite transformation in this presentation; however, such a treatment will shortly appear elsewhere. Only the salient features pertinent to the present investigation will be introduced briefly here. Although the reaction curve for the formation of bainite is similar to that for a nucleation and growth process, other kinetic features are more in keeping with the martensitic mode of transformation. A definite temperature exists above which austenite will not transform to bainite.1-5 his temperature, which has been designated B., is determined by the composition of the austenite. Unlike other nucleation and growth processes, the amount of austenite transformed to .bainite is a function of reaction temperature. The extent of decomposition increases from 0 at H. to 100 pct at some lower temperature.' , This lower temperature will be designated B1 and appears to be relatively insensitive to austenite composition.% 5 The similarity in the effect of reaction temperature on the bainite and martensite transformations serves to emphasize the close connection between these two decomposition processes. Austenite decomposition in the bainite range proceeds without partition of the alloying elements.8-11 Partition of carbon has been proposed" primarily on the basis that partial transformation to bainite lowers M, and increases the amount of austenite retained at room temperature. Carbon enrichment resuslting from such partition has been employed to explain the influence of reaction temperature on the extent of decomposition.'" It should be noted, however, that no enrichment has been detected experimentally in high carbon steels.1,14,15 Lattice-parameter measurements of retained austenite in steels containing 0.3 to 0.4 pct C have indicated carbon enrichment, 3,10-18 although the split indicative of a high carbon martensite has not been reported. Carbon enrichment, if it does occur, must be highly localized around the bainite plates. Therefore, carbon enrichment does not account for the influence of temperature on the progress of the bainite reaction."' Thermal history is known to influence the martensite transformation through stabilization.20,21 No similar phenomenon in the bainite transformation has been reported. Materials and Procedure Two triple-alloy steels were chosen for this investigation. Their compositions were as given in Table I. These steels were chosen because the pearlite reaction did not interfere with the bainite reaction. Steel K was received in the cast condition and forged from 2 in. square bars to 1/2 x1 3/4 in. plates. The 4340 was received as 11/4 in. hot-rolled rounds. Both steels were homogenized in vacuum for one week at 2300°F in order to minimize segregation. A quenching dilatometer similar to that described by Flinn, Cook, and Fellows" was employed for the kinetic measurements. Dimensional changes were detected by a differential transformer coupled with a high speed recorder. The dilatometer was mounted so that it could be transferred to any one of three furnaces: a nitrogen-atmosphere austenitiz-ing furnace and two salt-bath furnaces for isothermal transformation. Dilatometer specimens were 1/32 x 1/4x 1/2 in. with a gage length of 1.4 in. All specimens were nickel plated in order to minimize decarburization during austenitizing. The austenitiz-ing conditions consisted of 10 min at the temperatures given above. Austenitizing temperatures were controlled to 210°F and transformation temperatures to ±3ºF. The precision of the dimensional measurements was estimated to be ± 5 x105 in. per in. Results and Discussion Isothermal Transformation: The characteristics of the isothermal bainite reaction will be described

Jan 1, 1955

By P. S. Kotva

Dislocation substructures in superalloy matrices of varyzng co)npositions have been studied. In general, it has been found that the alloys can be classified into ''high", ''medium", and "low" stacking fault energy classes based on the type of dislocation substructure observed in the matrix and that the substructure can be correlated to the stacking fault energy. The effect of different types of dislocation substructure and dislocation reactions on the intragranulur precipitation of carbide phases has been studied. In a Ni-Cv-Mo-Fe matrix, precipitation of MC carbides in association with stacking faults has been observed. In most superalloys, solid-solution strengthening and precipitation hardening are the chief mechanisms employed to achieve strength. The latter contribution to strength is usually achieved by the precipitation of / in certain wrought alloys. Insufficient attention has been given to the problem of obtaining strength in su-peralloys by controlling precipitation of carbides on imperfections within the matrix. The present work was undertaken to investigate the dislocation substructure in various superalloy matrices, to study the effect of such substructure on subsequent precipitation of carbides in the matrix, and to investigate whether certain modes of precipitation of carbide phases found in austenitic stainless steels2"4'6 would occur in nickel-base alloy matrices with dislocation substructures of the same type as those found in austenitic steels. 1) EXPERIMENTAL TECHNIQUES Five-pound heats of the various alloy compositions reported here were vacuum-cast. The ingots were given light deformation by rolling to break up the as-cast structure and then homogenized for 24 hr. HASTELLOY alloy X (nominal composition: Ni-2OCr-17Fe-8Mo-0.05C) was homogenized at 2150°F and In-cone1 625 (nominal composition: Ni-20Cr-5Fe-8Mo-3.5Cb-0.05C) was homogenized at 2280°F. Fabrication of 0.004-in. sheet was achieved by cold rolling with intermediate annealing treatments being carried out at the same temperature as those used for homogeniza-tion. Each solution anneal was followed by quenching. The aim of this procedure was to redissolve as much of the primary carbide phase as possible. Samples of the 0.004-in. sheet were cut and encapsulated in quartz capsules and then heat-treated in the tube furnaces. Thin foils were prepared using an ethanol-10 pct perchloric acid bath at 32°F and at a voltage of 22 v. A "window" technique was employed. Observations were made on a JEM-7 electron microscope operating at 100 kv. 2) EXPERIMENTAL RESULTS a) Types of Dislocation Substructure. Fig. 1 shows a schematic correlation between stacking fault energy, SFE, and the type of dislocation substructure observed in various matrices of nickel- and cobalt-base alloys. A precise quantitative determination of stacking fault energy is not implied in the figure but the correlation between stacking fault energy and the type of dislocation substructure obtained allows alloys to be divided into three classes in analogy with the classification employed by Swann and ~uttin~' for binary alloys of copper. Class I alloys are associated with a "high" SFE and show a cellular substructure of dislocations as typified by the micrograph of a thin foil of pure nickel deformed 4 pct at room temperature in Fig. 2. With decreasing SFE the tendency toward cell formation is lessened and dislocations tend to be arranged in coplanar groupings. Examples of this class of alloys with "medium" SFE are provided by the mi-crostructure of solution-heat-treated, quenched, and deformed thin foils of HASTELLOY alloy X, "Waspaloy" (prior to any aging), and Inconel 625. Fig. 3 shows a thin-foil micrograph of an alloy of Inconel 625 composition, solution-heat-treated, quenched, and deformed 5 pct at room temperatures. No evidence of any cell structure can be obtained in materials of "medium" stacking fault energy, Fig. 3, even after severe deformation. The stacking fault energy of the alloy shown in Fig. 3 is, however, not low enough to make the dissociation of dislocations visually obvious. As stacking fault energy decreases further, with successive addition of solute in the matrix, there is an increased tendency toward dissociation of dislocations and cross slip becomes progressively more difficult. Eventually, when the stacking fault energy is "low" enough, complete dissociation of dislocations is seen to occur as shown in Figs.

Jan 1, 1969

By R. L. Bleifuss

The object of this study was to evaluate the oxidized taconites of the western Mesabi iron range and to establish a correlation between the various basic taconite types and their concentratability. The initial work included a study of the original mineralogical and stratigraphic facies of the fresh taconite and traced the oxidation and leaching patterns developed during the conversion of this material to oxidized taconite. Subsequent studies have extended this work to include the semitaconites and also the wash and heavy media ore types widely developed in the area. Each basic original mineralogical facies or taconite type produces during alteration an equivalent secondary oxidized facies which has a unique mineralogical composition and texture. These control the concentratability of the oxidized taconites. Actually the influence of the original mineralogical composition of the iron formation extends even further and determines whether the most likely product of oxidation and leaching will be a wash ore or a heavy media ore and even to the direct shipping ores where the ratio of hematite to goethite is largely determined by the original taconite type. The relationship between original taconite, oxidized taconite, semitaconites, and wash and heavy media ores is briefly summarized in Table I. The terms are not precise and in some instances tend to overlap. The table is intended to point out only the essential differences between the various materials. The original taconite was dominantly composed of mixtures of magnetite, iron carbonate, iron silicate, and quartz (chert). In a few thin stratigraphic units, hematite was present as an original constituent. The alteration of the original taconite to oxidized taconite has resulted from the circulation of ground waters through an initial fracture system related to minor structures in the iron formation. The chemical reactions have involved the oxidation and decomposition of original minerals such as magnetite, iron carbonate, and iron silicates to hematite or goethite. The alteration at this early stage is characterized by pseudomorphic replacement of the original minerals by oxidation products although retaining the major textural features of the original taconite. There was very little secondary migration of iron at this stage and the total iron content of the rock has been only slightly increased. Further alteration of this material to form a semi-taconite, a wash or a heavy media ore, involves extensive removal of silica in solution and significant redistribution of iron units. Wash and heavy media ores are developed by the growth of coarse secondary iron layers, dominantly goethite, coupled with the removal of silica in solution and decomposition of the cherty layers. This paper is concerned primarily with the materials classified as oxidized taconites which are characterized by oxidation of the original mineral constituents with little secondary enrichment. The area studied, shown on the index map, Fig. 1, extends some 30 miles along the strike of the Biwabik formation roughly from Hibbing to Coleraine. This study was greatly facilitated by the basic stratigraphic and mineralogical studies of Gruner1 and white2. The bulk of the material in this presentation represents a portion of the author's contribution to a study sponsored by the Great Northern Railway on the oxidized taconites of the western Mesabi.3 METHOD OF APPROACH A total of 106 drill holes, representing some 30,000 ft of drilling, were examined and sampled. The drill holes were logged and some 1500 composite samples were prepared for chemical analysis and bench scale metallurgical tests. These samples were analyzed for total iron and ferrous iron; and magnetite iron was determined by a standard Davis tube test at minus 200 mesh. Standard reduction roast tests using 150-gram samples of minus 10 mesh material were made on these 1500 composite samples with a mixture of H2, CO2, N2, and H2O at a temperature of 650°C. This roasted material was pulverized through 150 mesh and concentrated in the Davis tube. The iron recoveries and concentrate grades obtained on the roasted products were used to assess the concentratability of the oxidized taconites. Detailed mineralogical work was done on thin sec-

Jan 1, 1964

By Strathmore R. B. Cooke, Eugene L. Talbot

THE perfluoro acids and derivatives show unusual surface-active properties that qualify them as possible flotation reagents. They lower the surface tension of water from 15 to 20 dynes below that obtainable with the corresponding hydrocarbon compounds.1, 2 Fluorochemicals adsorb very strongly on solid surfaces to give films that exhibit larger contact angles than films of the corresponding hydrocarbons."' * The large contact angles probably result from the terminal —CF3 group. The perfluoro acids are made by electrolysis of the corresponding carboxylic acid in anhydrous hydrogen fluoride.5 From the perfluoro acids many derivatives may be obtained, such as amides, amines, alcohols, xanthates, ethers and esters and others. Since the fluorinated analogues of the conventional hydrocarbon flotation collectors possess enhanced surface properties, a few were selected for testing. Because a survey of all possible minerals and reagent combinations would be out of the question, hematite was chosen to represent a nonsulphide system and pyrite to represent a sulphide system. The fluorinated reagents used in these experiments were prepared in the research laboratories of Minnesota Mining & Mfg. Co. Some were synthesized especially for this research. They are not available cokmercially. Separation of Nonsulphide Ores: The separation of oxides from silica has always been a challenge to the flotation industry because differences in surface properties of the minerals are normally insufficient to produce clean concentrates. Oleic acid," rosin acids,' and amine salts% ave been used to considerable extent to effect separation of metal oxides and silica. The system hematite-silica was chosen to represent the nonsulphides both because of its difficulty of separation and because large tonnages of easily obtainable material are available, such as gravity concentration tailings and nonmagnetic taconites on the Mesabi Range. The wash-ore tailings used here contained approximately 35 pct iron after desliming. Samples of the material used in this work were part of the same lot used by Chang, Cooke, and Huch9 and were prepared in an identical manner. Reagents for Nonsulphide Ores: Since one of the purposes of this investigation was to compare hydrocarbons with fluorocarbons, reagents of known behavior such as oleic acid, and the alkali metal salts of certain resin acids (Dresinates), were established as standards. Hydrocarbons and fluorocarbons of comparable chain length and other experimental fluorocarbons were tried as collectors for hematite. A list of the materials used and the concentrations of their stock solutions are given in Table I. Since silica can be selectively floated from hematite by conventional reagents," a few fluorocarbon reagents were also tried for this purpose. Their composition and concentrations are given in Table 11. Most of these reagents served the dual function of collector and frother. In the case of F-11 flotation did not occur but it served as a frother when F-6 was employed as a collector. Reagent grade sulphuric acid and sodium hydroxide were used to regulate the pH. Deionized water containing less than 0.1 ppm of salts expressed as NaCl was used for all solutions and flotation tests. The pneumatic flotation cell consisted of a 350-ml fritted glass Buechner funnel with a source of filtered air which could be controlled by a needle valve." A 50-g sample of ore and 250 ml of deionized water were added to the flotation cell and stirred slowly. The reagents were added and the pulp was conditioned before air was admitted to the cell. Approximately 15 ml of the pulp were removed for pH determination before flotation was started and were then returned to the system. The pH was again measured after flotation. Air was admitted to the cell until no further flotation occurred or until the character of the float changed markedly. Both the float and the nonfloat products were filtered, dried, weighed. and assayed for iron. The cell was washed in hot water and rinsed with deionized water after each test. Occasionally the cell was cleaned with concentrated hydrochloric acid to remove iron oxide particles from the glass frit. Experimental Results: Above a pH of 8, sodium oleate was an effective collector for hematite. The emulsification of equal parts of heavy fuel oil (20"

Jan 1, 1956

By J. F. Pierce, S. M. Enterline

Since January 1959 a zinc refiner of novel design has been in operation at Blackwell, Okla., producing 99.995+ zinc from the output of the Blackwell horizontal retort smelter. The refiner is a continuously operated, pyro-metallurgical unit with principal dimensions horizonhl permitting one floor operation. It is very ruggedly constructed. Furthermore it is not subjected to deterioration from high concentrations of iron in the feed metal because the boiling units are separate from the rectification columns and constructed with silicon carbide brick arches through which the heat is transferred radiantly to the zinc. A zinc refiner of novel design has been in operation since January 1959 at the Blackwell, Okla. plant of the Blackwell Zinc Co., Inc., a wholly owned subsidiary of American Metal Climax, Inc. Developed by the company's technical and operating staffs, the new refiner produces special high-grade zinc (nominally 99.995+ pct Zn) from the prime western1 slab output of the Blackwell horizontal retort smelter. The refiner is a continuously operated, pyromet-allurgical, high-capacity unit employing fractional distillation to separate zinc from its impurities, consisting principally of lead, cadmium, and iron. In prime western slab, these elements may vary in concentration from 0.005 to 1.6 pct. Table I shows the impurities usually encountered in the Blackwell prime western metal fed to the refiner together with their boiling points and vapor pressures at 907oC. The commercial pyrometallurgical smelting processes for extracting zinc from ore include distillation from retorts and a limited degree of refining can be accomplished by redistillation in similar retorts. To achieve special high-grade purity, an impractical number of batch redistillations would be required, however, with an accompanying loss of much metal. A continuously operated and integrated unit is required in which fractional vaporization and condensation can take place in a large number of stages. The first commercial continuously operated unit was developed by the New Jersey Zinc Co.4 In the separation of any two substances the degree of separation is limited if a mixture exists having a constant boiling point. The Zn-cd5 and Zn-pb6 systems contain no constant boiling points and hence these metals may be separated to any degree of purity. Basically, the pyrometallurgical refining of zinc involves three steps: a) iron, copper, and other metals having no appreciable vapor pressures at 907ºC concentrate in the bath when the impure zinc is boiled, b) lead, bismuth, antimony, and other metals having boiling points above but closer to that of zinc are selectively condensed from the vapor boiled from the bath, and c) cadmium and other metals having lower boiling points than zinc are fractionally distilled by reboiling and subsequent condensation of the zinc from the vapor. The boiling and condensation of zinc must be conducted in vessels constructed of materials which are refractory at the temperature involved (907 ºC) and it is highly desirable that they also be resistant to attack by the various metals. This requirement dictates construction from relatively small, simply shaped pieces which limits the pressures which may be employed to avoid leakage through the numerous joints. Stresses induced must be limited essentially to compressive ones and suitable provision must be made to permit thermal expansion of the components in order to minimize these stresses. Where heat is to be added for boiling or removed for condensation, refractory material through which the heat flows must have a high thermal conductivity. Silicon carbide is highly conductive but is subject to attack by iron and is expensive compared to other commonly employed refractories. A hard, dense aluminous fireclay is well suited to contain these metals where high thermal conductivity is not required. Zinc will penetrate the pores of fireclay brick but only to a limited depth in an exterior wall and has little effect other than an increase in weight and conductivity. The design objectives of the Amax refiner were: a) to achieve a long life by heavy, rugged construction and by employing silicon carbide refractories only where required for heat conductivity and not in contact with liquids of high iron concentrations, b) to simplify operation, manning and control by essentially horizontal construction, and c) to obtain high capacity in a single unit. DESCRIPTION Flow of metal through the Amax refiner is shown diagrammatically in Fig. 1 and schematically in Fig. 2.

Jan 1, 1963

By S. J. M. van Leeuwen, R. Feenstra

The effect of jets on bit penetration has been investigated by means of a 50-ton drilling machine and 8½-in. commercial jet bits, drilling under representative bottom-hole conditions. The conclusions apply to the drilling of impermeable rock only. Penetration rate is in all cases primarily hampered by a differential pressure effect, known as dynamic hold-down. Jet action can reduce this slightly. Major gain in penetration rate, up to 25 or 50 per cent, is already ohtained at medium-high jet power. At high bit load, penetration by soft to medium-hard-formation bits is further hampered by bit-balling. Its alleviation requires intensive tooth scavenging, which is best performed by slanted nozzles with trailing, high-velocity, high-volume jets, hitting bottom in front of the teeth. Penetration may then improve by a 100 per cent. At high bit load, bottom-balling limits the penetration of insert-type bits. In this case bottom scavenging is required, which is most effectively performed with high velocity jets from nozzles extended close to bottom. As a result of this measure, penetration may improve 70 per cent in non-friable rock, and less in friable rock. This will make the insert-type bit more versatile. Toothed hard-formation hits suffer at high bit load from both bit- and bottom-balling. Slanted nozzles, possibly much extended, with high-velocity, high-volume jets then have best prospects. INTRODUCTION For years the use of jet bits in oil well drilling has been increasing, in conjunction with ever greater hydraulic horsepower. To the same extent, the need for efficient use of the horsepower has grown.' This paper, it is hoped, will contribute to an understanding of how effective jet action may be obtained. It deals with the effect of jets on phenomena that are known' " to hamper bit penetration. To study this effect, laboratory drilling tests were performed with 8½-in. commercial bits under bottom-hole pressures representative of deep wells. The investigation has been restricted to the drilling of practically impermeable rock. In the following sections, the increase in bit penetration rates due to jetting is discussed for conditions which made the troublesome phenomena stand out one at a time. A brief definition and interpretation of these phenomena is given in Appendix A. Appendix B gives the results of measurements of fluid velocities along the hole bottom, performed in stationary flow tests. Descriptions of equipment, bits, rocks and mud are collected in Appendix C. Unless otherwise mentioned, drilling conditions were kept standard as given in Table 1. CUTTING TRANSPORT TO THE ANNULUS Jet action was for some time believed to merely improve the transport of cuttings from bottom to annulus, resulting in a clean hole bottom. Flow tests performed in 1954 at the Battelle Memorial Institute6 showed, however, that jet velocities of the order of 40 ft/sec sufficed to clear even large (0.4-in.) chips from bottom in the time between two successive tooth actions. In the field, optimum jet velocities are appreciably higher, indicating that other effects must be involved. This much is confirmed by the results of our drilling experiments in soft rocks performed under atmospheric pressure, i.e., in absence of pressure-differential effects. Fig. 1 shows that variation in the nozzle velocity from 40 to 330 ft/sec had no effect on penetration rate, unless the bit penetrated more than 7 mm per revolution, which is about half the tooth height. At such high rates—150 ft/hr at 100 rpm—cuttings would be caught in the tooth cavities, leading to bit-balling, which was noticed on inspection of the bit. The jets thus assisted in keeping the tooth cavities clean. This is just perceptibly reflected in the penetration-rate curves of Fig. 1: Much the same results were obtained in hard rocks with hard-formation three-cone bits. The conclusion is that transport of loose cuttings towards the annulus does not require a powerful jet action. In the following sections we shall see that in deep-well drilling other phenomena are of greater importance. DYNAMIC HOLD-DOWN It is generally accepted that, in deep-well drilling, bit penetration is hampered primarily by the existence of a difference in pressure between the fluid in the hole and that in the rock at the depth of cutting.2-5 In the drilling

Jan 1, 1965

By C. E. Hottman, R. K. Johnson

Fluid pressure within the pore space of shales can be determined by using data obtained from both acoustic and resistivity logs. The method involves establishing relationships between the common logarithm of shale transit time or shale resistivity and depth for hydrostatic-pres-sure formations. On a plot of transit time vs depth, a linear relationship is generally observed, whereas on a plot of resistivity vs depth, a nonlinear trend exists. Divergence of observed transit time or resistivity values from those obtained from established normal compaction trends rinder hydrostatic pressure conditions is a measure of the pore fluid pressure in the shale and, thus, in adjacent isolated permeable formations. This relationship has been empirically established with actual pressure measurements in adjacent permeable formations. The use of these data and this method permits the interpretation of fluid pres.rure from acoustic and resistivity measurements with an accuracy of approximately 0.04 psilft, or about 400 psi at 10,000 ft. The standard deviation for the resistivity method is 0.022 psi/ft, and for the acoustic method 0.020 psi/ft. Knowledge of the first occurrence of overpressures, and of the precise pressure-depth relationship in a geologic province, enab1es improvements in drilling techniques, casing progroms, completion methods and reservoir evalzmtions. INTRODUCTION CENKRAL STATEMENT Operators engaged in the search for and production of hydrocarbon reserves in Tertiary basins are more and more frequently confronted with complications associated with over pressured (abnormally high fluid pressure) formations. This is particularly true in the Texas-Louisiana Gulf Coast area. The problems associated with these formations are of direct concern to the combined activities of all phases of operations, i.e., geophysical, drilling, geological and petroleum engineering.' - Knowledge of the pressure distribution of a given area of operations would greatly reduce the magnitude of many of these complexities and in some cases would completely eliminate specific problems. his pape; presents techniques developed for estimating formation pressures from interpretations of acoustic and electric log data. Specifically: the acoustical and electrical properties of shales, reflected by conventional acoustic and electrical surveys, can be used to infer certain reservoir properties, such as formation pressure, at any level in a well. It has been possible to develop these techniques because of a firm understanding of the basic principles that govern and apply to such overpressured provinces. NORMAL PRESSUKES Normal pressures refer to formation pressures which are approximately equal to the hydrostatic head of a column of water of equal depth. If the formations were opened to the atmosphere, a column of water from the ground surface to the subsurface formation depth would balance the formation pressure. On the Gulf Coast, the shallow, predominantly sand formations contain fluids which are under hydrostatic pressure. These formations are said to be normally pressured or to have a normal pressure gradient.* Experience has shown that the normal pressure gradient on the Gulf Coast is approximately 0.465 psi/ft of depth. OVERPRESSURES Formations with pressures higher than hydrostatic are encountered at varying depths in many areas. These formations are referred to as being abnormally pressured, abnormally high pressured, or overpressured. Formation pressures up to twice the hydrostatic pressure have been observed. These formations require extreme care and much expense to drill and to exploit. COMPACTION-FLUID PRESSURE RELATIONS THEORY The generation of overpressured formations in Tertiary sections of the Gulf Coast and several other Tertiary sedimentary basins is, in general terms, considered to be primarily the result of compaction phenomena.' This portion of the paper presents a brief review of the theory which associates compaction and fluid pressure relations, and should thus provide the necessary background for an understanding of the techniques presented. See Hubbert and Rubey' for a more comprehensive treatment of this subject. The theory of the consolidation of a water-saturated clay' has been well established by workers in soil mechanics. The concept is explained by a model with perforated metal plates separated by metal springs and water and enclosed in a cylindrical tube. Fig. 1 is a schematic representation of such a model (see Ref. 5, Fig. 27, page 74). The springs simulate communication between clay particles, and the plates simulate the clay particles. Mano-

Jan 1, 1966

By K. Tangri, B. Swaroop

Simultaneous measurements of lattice (elastic) strain by X-ray line shift method and total strain with an electrical strain gage have been carried out on polycrystalli,ne nickel with the help of a specially designed tensometer attachment for the X-ray dif-fractometer. During the initial stages of deformation, the rate of increase in lattice strain closely follows the total strain until the plastic strain sets in. From then onwards, the two strains deviate from each other and with further increase in afiplied stress the rate of increase of lattice strain eventually decreases. Depending upon the mode of unloading, both compressive and tensile strains have been observed in nickel deformed up to 0.29 pct strain. These results have been explained on the basis of the effects of clustering of dislocations and also the production and behavior of point defects during loading and unloading, respectively. POLYCRYSTALS deformed plastically in a uniaxial tension test show residual lattice strains (hereafter referred to as RLS), which broaden the X-ray line profiles and shift their peak positions.''4 It is known that uniform straining of a crystal lattice (macrostrain) produced movement of ddfraction line peaks, whereas nonuniform straining (microstrain) causes line broadening.= Though the nature and origin of RLS in deformed metals is not yet clearly understood, these are believed to be due to the presence of some form of a locked-up stress system. Several possible detailed interpretations6'" of the stress system have been proposed by various workers and common to all these interpretations is the assumption that different parts of the aggregate have different tensile yield stresses; e.g., that a part A yields under a lower applied stress than a part B. Therefore, during the deformation process, the elastic strain in A will be less than that in B, and, after completion of deformation, B will tend to contract further than A but will be prevented from doing so by the restraining influence of A. Thus, when equilibrium is reached, A will be in compression while B is in tension. Although there is general agreement on the correctness of this argument, controversy still exists as to the exact nature of the parts A and B in a deformed metal. In an alternative approach to the creation of parts A and B, many other investigators have assumed that the RLS observed in unloaded specimens are in some way connected with the lack of proportionality between lattice strain and applied stress in the region above the yield stress." cullity13 has prepared a schematic summary of the results of previous workers, mainly Smith and Wood,2'11 which suggests that, above the elastic limit, the lattice strain may increase less rapidly with respect to strain, or may even decrease with increase in applied stress. If the applied stress is then decreased, the lattice strain would decrease along a line parallel to the loading line in the elastic region and thus produce a compressive residual lattice strain after unloading. At equilibrium, to balance these compressive stresses? there would have to be regions under tensile stress which may well be the grain boundaries or the substructure walls formed during deformation. The present investigation was undertaken to gain a better understanding of the nature and origin of RLS and also to experimentally verify the salient features of this hypothesis. EXPERIMENTAL Stress and strain determinations were made with a specially constructed tensometer attachment for the X-ray diffractometer, Fig. 1: which permits the following measurements simultaneously on a sheet specimen under uniaxial tension at various stress levels during loading and unloading: a) lattice strains, E=. in a direction perpendicular to the direction of pulling (x direction) from shifts in X-ray line peak positions; b) the total strain, ex, in the direction of pulling. with the help of an electrical strain gage affixed to the back of the specimen directly below the area irradiated by X-rays: and c) the applied stress, with the help of a load cell which consisted of a calibrated stainless-steel sample of dimensions identical to those of the specimen under investigation, and to which it was coupled. Because of its high stacking fault energy.I4 nickel

Jan 1, 1970

By E. J. Dulis, R. M. Fisher, K. G. Carroll

IT is well known that ferritic steels containing more than 15 pct Cr when subjected to temperatures in the range of 700" to 1000°F exhibit increasing hardness and decreasing ductility. The phenomenon has been widely termed the "885 °F embrittlement," after the temperature of most marked effect.'.' In view of the excellent review articles available in the literature3-6 only a brief account of experimentally established facts need be given here. The extent of changes in physical characteristics during embrittlement depends on chromium concentration and time at temperature, higher alloy content and longer time both promoting more rapid and extensive changes. In a 27 pct Cr steel, changes in impact strength and in angle of fracture in bending can be detected after only a 1 hr exposure at 885°F; after 50 hr this steel becomes quite brittle. Hardness increases slowly with time during thousands of hours exposure and may attain a maximum hardness number twice as large as that of the unexposed steel. Microstructural changes accompanying embrittlement have been described as an initial widening of grain boundaries followed by eventual darkening of ferrite grains. Embrittled steels etch more readily, e.g., the weight loss of a 27 pct Cr steel in acid solution may occur at a rate one hundred fold greater following exposure at 885 OF. Marked changes which accompany embrittlement have been observed in electrical resistivity, specific gravity, and magnetic coercive force. Changes in physical properties may be readily removed by heating at temperatures above the embrittling range, such as a treatment at 1100°F for 1 hr. It has frequently been noted that the 885 °F embrittlement suggests precipitation on a submicro-scopic scale of a chromium-rich constituent, the nature of which has not been revealed by X-ray diffraction. Progressive broadening of the body-centered cubic diffraction lines during embrittlement has been observed," and recent observations by Lena and Hawkes' upon single crystals have shown early asterism in X-ray photographs, disappearing within an hour at 900 °F. Many workers have ascribed8-13 the phenomenon to a precipitation of a phase (FeCr), which is known to cause embrittling effects at temperatures much higher than 885°F. Two general observations, however. suggest that a precipitation cannot be responsible for the 885°F phenomenon: 1—prior cold work greatly enhances a formation, whereas it scarcely affects the 885 °F embrittlement, and 2—the presence of an alloying element such as nickel or manganese may have an effect on the 885 °F embrittlement which is opposed to its effect upon a formation. The slight enhancement of a formation and 885°F embrittlement observed in the presence of elements with strong carbide and nitride forming tendencies' is probably a consequence of lessened chromium depletion of the matrix. The bar graph in Fig. 1 shows a typical example, taken from two 27 pct Cr steels used in this work, of the hardness after exposure for 10,000 hr at 900°, 1050°, and 1200°F. Steel A (0.03 pct C, 3.13 pct Mn) showed marked hardening at 900" and 1200°F, whereas steel B (0.12 pct C, 0.63 pct Mn) exhibited only the 900°F hardening. The cr phase was found in steel A at the higher temperatures but not in steel B. Presumably a formation is enhanced by the low-carbon and high-manganese concentrations in A," Thus there are two distinctly different hardening phenomena present which cannot both be ascribed to v precipitation without invoking a transition phase possessing remarkable properties. Materials A number of chromium steels exposed for long periods (5000 to 34,000 hr) at 900°F, as well as unexposed samples of one of the steels, were available for this investigation. Table I gives the chemical compositions and aging treatments of these steels. In addition to these steels exposed in the elevated temperature test furnaces of the National Tube Division, a number of high-chromium steels were heated for short periods in small laboratory air furnaces and lead baths. Supplementing these commercial steels, a sample of high-purity (0.018 pct C, 0.002 pct N) 28 pct Cr iron, exposed 1000 hr at 887°F. was furnished by the Union Carbide and Carbon Corp. In addition, an alloy of iron and chromium of high purity containing 46 pct Cr was used. This

Jan 1, 1954

By Arnulf Muan, D. P. Masse

PHASE relations in the system CoO-SiO2 have been determined as a basis for further investigations of thermodynamic properties of olivine solid solutions involving Co2SiO4 as a component. Previous data on the system CoO-SiO2 are incomplete or uncertain. Biltz and Lemke1 determined the melting point of cobalt orthosilicate as 1345°C , but Asanti and Kohlmeyer2 have later found a considerably higher temperature, 1420°C. The latter authors also studied melting relations of one mixture on the CO side and two mixtures on the SiO2 side of the orthosilicate composition and sketched a tentative phase diagram for a limited composition range of the system. However, no phase identification was carried out, and the authors left unanswered the question of the possible existence of a stable meta-silicate phase. Greig3 showed that a 90 wt pct SiO2-10 wt pct Co mixture at 1725°C consists of two immiscible liquid phases. The quenching technique was used in the present investigation. Mixtures of high-purity cobalt oxide ("Fisher Certified") and dehydrated silicic acid ("Baker Analyzed") were equilibrated in air atmosphere. The samples were then quenched to room temperature and the phases present were identified by microscopic and X-ray examination. The samples were kept in small envelopes made from thin (0.0004 in.) platinum foil. Thermodynamic data which have become available recently for Pt-Co alloys4 were used to check that the losses of COO from the oxide samples by alloying of cobalt with platinum in the present investigation were too small to change significantly the compositions of the oxide material during the equilibration. A vertical tube furnace with an 80 pct Pt 20 pct Rh resistance winding was used in runs up to 1510°C. Temperatures in these runs were measured with a Pt vs 90 pct Pt 10 pct Rh thermocouple calibrated against the melting point of diopside (CaMgSi2O6, 1391.5?C). The given temperatures as measured by this technique are estimated to be accurate to *5°C. Quench runs at temperatures above 1650°C were made with a modified Roberts and Morey5 strip furnace, using strip resistors composed of a 60 pct Pt-40 pct Rh alloy. Temperatures were measured with an optical pyrometer which was calibrated against the liquidus temperature of a mixture composed of 10 wt pct CaO, 90 wt pct SiO2 (1707°C). The temperatures measured with this technique have an estimated accuracy of +15°C. The results are shown graphically in Fig. 1. Only one intermediate phase, the orthosilicate Co2SiO4 with olivine-type structure, is stable in addition to the end members cobalt oxide and silica. The melting point of the orthosilicate was found to be 1415" ± 5°C. The metastilicate CoSiO3 is not stable at the temperatures of the present investigation. The two eutectic points in the system CoO-SiO2 where COO plus olivine, and olivine plus silica, coexist with liquid were found to be 72 wt pct COO and 1407°C and 63 wt pct COO and 1381°C, respectively. The melting point of cobalt oxide in air was taken as 1745?C, based on the previous data of Aukrust and Muan.6 Within limits of error (+ 5?C), identical eutectic temperatures to those determined in air were found when two representative mixtures were equilibrated at 1 atm O2 pressure and in an atmosphere of 84 vol pct CO2, 16 vol pct H2. This suggests that changes in oxidation state of cobalt in the condensed phases are not significant as far as their effect on the phase relations are concerned. This inference was substantiated by failure to detect7 any "excess oxygen" (i.e., oxygen in excess of that contained in Co2SiO4) in a sample of orthosilicate composition equilibrated in air 10°C above the liquidus temperature and subsequently quenched to room temperature. This work was carried out as part of a research program sponsored by the U.S. Atomic Energy Commission under Contract No. AT(30-1)-2781.

Jan 1, 1965