In presenting the following data on combustion in the open hearth furnace and the advisability of automatic combusion control, the author finds himself much more severely handicapped by the lack of reliable test results than he had anticipated when he first undertook to write this paper. In order thoroughly to investigate how the results of an open-hearth furnace are influenced by combustion, one would have to draw up a large number of heat-balance sheets, as Kinney and McDermottl have given for one heat in their extremely able paper on "Open Hearth Efficiency,' presented before the American Iron and Steel Institute on October 27th,1 1922. Instead of covering only one heat, however, such heat-balance sheets would have to embrace a large number of heats, and not only for one kind of fuel, but for all the various fuels in customary use. Use of Radiation-protected Pyrometer Such tests necessitate extremely careful temperature readings, and here the first serious difficulty presents itself. Nearly all the temperature readings so far published have been taken with thermocouples for the lower ranges and with optical or radiation pyrometers for the higher ranges. This method of measuring reveals the temperature of the surrounding walls, or in the case of optical or radiation measurements, the temperature of that part of the opposing walls which has been focused by the instrument. The error in ascertaining the temperature of the gases entering or the waste gases leaving the checker chambers is probably not very large, as the flowing gases impart their temperature to the walls of the flues. On the other hand, the uptakes, where the preheat temperature of gas and air are usually measured, are under the influence of radiated heat from the port ends, and correct temperature readings can here be taken only by using a radiation-protected pyrometer of the aspirating type.

Jan 1, 1926

By H. L. Talbot, R. S. Young, A. Golledge

The differentiation of oxidized forms of lead from lead sulphide in complex products by chemical analysis is of considerable importance to certain mining and metallurgical companies. A method for the separation of "oxide" lead, (non-sulphide), from sulphide lead, based on the solubility of the former and virtual insolubility of the latter in concentrated ammonium acetate solution, has been employed for many years in the industry.1,2 Unfortunately this solvent, while satisfactory for lead sulphate and carbonate, is without action on lead phosphates or vanadates, with the result that at .Rhodesia Broken Hill Development Co. where these latter minerals are present, they have counted as sulphides when using this procedure. For the control of operations in the new concentrator it became necessary to have a closer check on sulphide lead than could be obtained by the only current method of differentiating this constituent from oxidized lead. For some time this problem has engaged our attention, and after a large number of solvents had been tried, the following procedure was evolved. Like all methods depending on selective solution in a com- plex material, it will not give 100 pct separation into oxide and sulphide portions. Because of the ease of oxidation of galena this is almost an impossibility. Our procedure will, however, give a recovery of 99-100 pct of the oxidized lead, contaminated with very small quantities of lead sulphide, and a corresponding recovery of 97-98 pct of the sulphide lead. The procedure is simple and reproducible, and gives results quite .satisfactory for routine control purposes. Experimental For this work standard samples of the following pure lead minerals were obtained from Broken Hill, Northern Rhodesia. These were hand-picked specimens, and were carefully ground to —200 mesh. Since it was realized that a fair-sized sample would be necessary for this work to thoroughly test the large number of procedures we had in mind, a compromise had to be effected between a few grams of very pure minerals and a large sample of lower grade material. For this work the presence of gangue was not deleterious, so long as the oxide lead minerals did not contain lead sulphide, and vice versa. Table I shows the lead minerals used, and their total lead content, both theoretical and actual. Apart from the pyro-morphite the minerals are seen by analysis to be quite pure. Many solutions were tried in an effort to dissolve the oxidized lead minerals and

Jan 1, 1949

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By John Chipman, Carl F. Floe

A year ago the authors published a paper on the solubility of sulphur dioxide in molten copper.l The data in that paper agreed closely with that obtained by previous investigators, which, however, did not agree with the theoretical predictions for solubility of triatomic gases of this type. It has generally been assumed that the reaction of solution is: 6Cu(l) + SO2(g) = Cu2S (in Cu) + 2 Cu2O (in Cu) [I] _ (CU2S)(CU2O)2 K = (Cu)6(Pso2) [2] Neglecting the slight change in copper concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume of gas absorbed, it follows that this volume should be proportional to the cube root of the pressure. It was found that a plot of the volume absorbed versus the cube root of the pressure gave a straight line, but that this line did not pass through the origin. Calculations of the equilibrium constant for the reaction showed that it was fairly constant for pressures above 100 mm. but that actually it approached zero at lower pressures. The conclusion was made therefore that the solubility as determined could not be expressed by Eq. I or by any other simple equation, particularly at low pressures. Other investigators have concluded that the solubility of sulphur dioxide in copper as well as in several copper alloys is more nearly proportional to the square root of the pressure.* Such a conclusion, however, does not satisfactorily account for the results, even when rather complicated mechanisms for the solution are assumed. The highly improbable speculations of Lepp2 and of Schneider and Esch3 based upon hypothetical dissociation pressures of Cu2O and CU2S dissolved in copper illustrate the type of reasoning that has been used to account for the discrepancy. In the discussion of the previous paper, the authors pointed out that the discrepancy might possibly be due to impurities in the copper, although the purest form available was used. Further consideration of the problem suggested that the impurities likely to have the greatest effect on the solubility of so2 in copper were oxygen, sulphur and carbon. Accordingly, further experiments have been made to show the effects of these elements. Experimental Methods The apparatus used for measuring solubility was essentially the same as that shown in the previous paper. However, since it was desired to make measurements at low pressures, a McLeod gauge was added and 6-mm. glass tubing was substituted for the capillary. This increased the "hot volume" considerably but was necessary in order to obtain good vacuums in a reasonable length of time. A mercury diffusion pump was also installed.

Jan 1, 1942

By Carl F. Floe, John Chipman

A year ago the authors published a paper on the solubility of sulphur dioxide in molten copper.l The data in that paper agreed closely with that obtained by previous investigators, which, however, did not agree with the theoretical predictions for solubility of triatomic gases of this type. It has generally been assumed that the reaction of solution is: 6Cu(l) + SO2(g) = Cu2S (in Cu) + 2 Cu2O (in Cu) [I] _ (CU2S)(CU2O)2 K = (Cu)6(Pso2) [2] Neglecting the slight change in copper concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume of gas absorbed, it follows that this volume should be proportional to the cube root of the pressure. It was found that a plot of the volume absorbed versus the cube root of the pressure gave a straight line, but that this line did not pass through the origin. Calculations of the equilibrium constant for the reaction showed that it was fairly constant for pressures above 100 mm. but that actually it approached zero at lower pressures. The conclusion was made therefore that the solubility as determined could not be expressed by Eq. I or by any other simple equation, particularly at low pressures. Other investigators have concluded that the solubility of sulphur dioxide in copper as well as in several copper alloys is more nearly proportional to the square root of the pressure.* Such a conclusion, however, does not satisfactorily account for the results, even when rather complicated mechanisms for the solution are assumed. The highly improbable speculations of Lepp2 and of Schneider and Esch3 based upon hypothetical dissociation pressures of Cu2O and CU2S dissolved in copper illustrate the type of reasoning that has been used to account for the discrepancy. In the discussion of the previous paper, the authors pointed out that the discrepancy might possibly be due to impurities in the copper, although the purest form available was used. Further consideration of the problem suggested that the impurities likely to have the greatest effect on the solubility of so2 in copper were oxygen, sulphur and carbon. Accordingly, further experiments have been made to show the effects of these elements. Experimental Methods The apparatus used for measuring solubility was essentially the same as that shown in the previous paper. However, since it was desired to make measurements at low pressures, a McLeod gauge was added and 6-mm. glass tubing was substituted for the capillary. This increased the "hot volume" considerably but was necessary in order to obtain good vacuums in a reasonable length of time. A mercury diffusion pump was also installed.

Jan 1, 1942

By Gerhard Derge, J. Warren Stewart

Extrusion processes are used in the commercial production of a wide variety of products, as indicated by the review presented a few years ago by D. K. Crampton.' Most writers have confined themselves to a general description of the equipment and products and the engineering aspects of the process. The few studies that have dealt with the metallurgical side of extrusion have been concerned primarily with an examination of the mode of flow of the metal during extrusion. This has been accomplished by the use of composite billets, by scribing grids on symmetrical sections of billets and observing the change of dimensions in the gridwork, or by examining microstructures in extruded sections.2"8 Ariotlier limitation of these original studies is that they were confined to the extrusion of very simple shapes, usually rods having a diameter of about one-fourth that of the billet. Tin is particularly well suited to the extrusion of collapsible tubes and similar shapes in which the extruded section is very small in comparison to the diameter of the billet or slug. In modern production, impact extrusion methods are generally employed, therefore the thickness of the slug is small compared to its diameter. Under these conditions the process differs considerably from the processes that have been most fully described in the literature, and it is known that the quality of the product is very sensitive to slight variations in any one of the many variable factors involved, such as coinposition and structure of the alloy, rate of extrusion, temperature, shape of punch and die. An exhaustive examination of all of the above-mentioned problems promises to produce so many data that it seems advisable to initiate the reports at this time, even though all of the factors outlined have not been examined fully, and to confine this paper to a description of the apparatus and method. Only tin and its alloys with small amounts of copper have been considered. These are the alloys most commonly used in this country for the production of the type of articles already described.

Jan 1, 1940

By Gerhard Derge, J. Warren Stewart

Extrusion processes are used in the commercial production of a wide variety of products, as indicated by the review presented a few years ago by D. K. Crampton.' Most writers have confined themselves to a general description of the equipment and products and the engineering aspects of the process. The few studies that have dealt with the metallurgical side of extrusion have been concerned primarily with an examination of the mode of flow of the metal during extrusion. This has been accomplished by the use of composite billets, by scribing grids on symmetrical sections of billets and observing the change of dimensions in the gridwork, or by examining microstructures in extruded sections.2"8 Ariotlier limitation of these original studies is that they were confined to the extrusion of very simple shapes, usually rods having a diameter of about one-fourth that of the billet. Tin is particularly well suited to the extrusion of collapsible tubes and similar shapes in which the extruded section is very small in comparison to the diameter of the billet or slug. In modern production, impact extrusion methods are generally employed, therefore the thickness of the slug is small compared to its diameter. Under these conditions the process differs considerably from the processes that have been most fully described in the literature, and it is known that the quality of the product is very sensitive to slight variations in any one of the many variable factors involved, such as coinposition and structure of the alloy, rate of extrusion, temperature, shape of punch and die. An exhaustive examination of all of the above-mentioned problems promises to produce so many data that it seems advisable to initiate the reports at this time, even though all of the factors outlined have not been examined fully, and to confine this paper to a description of the apparatus and method. Only tin and its alloys with small amounts of copper have been considered. These are the alloys most commonly used in this country for the production of the type of articles already described.

Jan 1, 1940

By Henry G. Granger

A residence of 14 Sears in the Republic of Colombia, spent . in almost continuous traveling and prospecting-trips, has given me an intimate knowledge of the resources of that wonderful country. The man who best knows Colombia is unquestionably General Rafael Reyes, President of the Republic for the past three years, and with seven years more to serve in his present term. Such is the strength of his personality and the wisdom of his policies that his term of office will no doubt endure as long as he is milling to serve. The vastly improved economic situation and the brilliant outlook for Colombia are so directly due to the influence of President Reyes that a few lines concerning him will not be amiss, if they serve towards a better understanding of his personality. Born of a distinguished ancestry in the mountain~ of Boyaca, he is now 57 years old, just the age of his friend Porfirio Diaz when he began the work which has placed Mexico in the rank of great modern nations. It was Reyes who came to Washington to protest against the action of the government of the United States of America in

Jan 1, 1909

By E. R. Dean

A wire-feed mechanism has been employed to fabricute metal alloy film resistors to various sheet resistivities on oxidized silicon substrates. The effect of several thousand hours storage in air at elevated temperatures on the resistance and temperature coefficient of resistance is presented. Unprotected films of- sheet resistivity between 100 and 500 ohms per sq fabricated at 300°C substrate tenzperatures were unstable when stored at 150°Cfor extended periods. The higher sheet resistivity films exhibited the greatest instability; however, even the 100 ohms per sq films drijted excessively for device application. When stored at still higher temperatures, the normalized resistance increases to maximum, then decreases until a minimum value is obtained, then finally increases in resistance until open. The use of a protective overcoating of SiO has had considerable benejicial effects on the film stability, so that 250 ohms per sq films deposited on 300°C substrates are now stable after 1000 hr storage at 250°C and possess a temperature coefficient of resistance less than 200 ppm per C. The use of a low substrate temperature during depositon (100°C) enables the preparation oj resistors with very low tenperature coefficients of resistance (10 to 20 ppnl per 'C). However, these films are less stable than their higher substrate temperatuve counterparts. During extended storage, the resistance of the protected films always decreases with lower substrate films exhibiting larger normalized resistance decreases. This resistance decrease is accompanied by a linearly related increase in the temperature coefficient of resistance. The electrical behavior of these films may be explained by postulating That the structure of the films is in the transition region between thick continuous films and ultrathin island structure films so that the conductivity is the restlt of both electron scattering and tunneling-activated charge carrier creation between neighboring grains. The annealing behavior when thermally aged is the result of defect anneal, grain growth, and selective oxidation. TheRE is a considerable interest in thin metallic films for use as resistor elements in microelectronic circuits.1,2 These resistor films must be stable when exposed to elevated-temperature storage or operating ambient, possess low temperature coefficients of resistance (hereafter referred to as T.C.R.), and be of a high enough sheet resistivity to be useful. The resistivity and T.C.R. of a thin metallic film are determined by the structure and thickness of the film. Hence the stability of the film when exposed to stress would depend on the stability of the structure. The resistivity of a thin film is the result of the electrons' interaction with the lattice vibrations (electron-phonon scattering), scattering of electrons due to impurities, defects, and grain boundaries and specula reflection from the film surfaces.3' All of these effects serve to reduce the electron mean free path and result in a resistivity higher than the ideal bulk. In ultrathin films possessing essentially an island structure consisting of a planar array of aggregates separated by a few to a few tens of angstroms, conduction is dominated by a combination of tunneling and activated charge carrier reation. Thin films would be characterized by relatively low resistivity, positive T.C.R., and reasonable structure stability whereas ultrathin films possess unstable structures, negative T.C.R., and exhibit high resistivity. Feldman6 has investigated films intermediate between the two regions and postulates that the resistivity of a film in the transition region is composed of two linearly additive parts: that due to the resistance of the grains and that due to the gaps. The grain resistivity would represent the scattering of the conduction electrons by defects, surfaces, and phonon interaction while the gap term represents the tunneling contribution. For gold and platinum films, he found as the film structure becomes progressively less continuous, corresponding to thinner films, the absolute value of the T.C.R. becomes progressively smaller until negative values are observed with respective zero T.C.R.'s at about 35 and 150 ohm per sq, respectively. Recently the author7 investigated the behavior of a multicomponent alloy of nickel, chromium, and iron and found the T.C.R.'s of these films decrease with decreasing substrate temperature during deposition. The lower T.C.A. associated with lower substrate temperatures was attributed to an increased contribution to the total resistivity from the negatively temperature-dependent gap tunneling since it is well-known that thin films deposited on low-temperature substrates consist of a higher density of smaller grains than the same sheet resistivity films deposited on higher-temperature substrates. Under conditions of thermal anneal, the author found that, when various sheet resistivity films fabricated at 300°C substrate temperature are exposed to extended storage in air at 300°C, the thinner films increase in resistance until open, while the thicker films

Jan 1, 1967

By J. D. Miller Discussion by N. P. Finkelstein, M. C. Fuerstenau

The point designating 10 -4 nole/per liter sulfonate addition in Fig. 1 has been presented incorrectly. This figure, with the corrected scale, is shown at right. N. P. Finkelstein (National Institute for Metallurgy, Johannesburg, South Africa) - The qualitative conclusion the authors of this paper have reached in evaluating the influence of hydrocarbon chain length on collector effectiveness agrees with conclusions in several published reports. However, in two other

Jan 1, 1969

By Arthur B. Foote

Ore production from the property of the Miami Copper Co. began early in 1911. Until 1925 this ore came from the so-called high-grade orebodies, which contained a little over 2 per cent. copper. This ore was mined by the following methods: 1. Top slicing after mining the peaks by square setting, which produced 4,524,347 tons, including ore from square setting. 2. Shrinkage stoping with sublevel caving of the pillars, which produced 2,230,577 tons. 3. Undercut caving with hand tramming, which produced 15,427,672 tons. Estimating December tonnage, the total ore mined to the end of 1929 will amount to slightly more than 43,000,000 tons. The first method was described by E. G. Deane' and the second by D. B. Scott,' and the third, together with a general description of the mine, by J. H. Hensley, Jr.' The geology of the district has been worked out by Dr. F. L. Ransome.2 The author acknowledges also the assistance of R. W. Hughes, assistant mine superintendent, E. V. Graybeal, chief mine engineer, A. J. McDermid and S. R. Burdick, engineers of Miami Copper Co., Miami, Arizona. Factors Influencing Selection of Mining Methods The mining method described herein was selected primarily with a low mining cost in view and was developed to avoid as far as possible dilution of the already very low-grade ore. In 1924, with the exhaustion of the high-grade orebodies in sight, it was decided to develop the low-grade orebody, which at that time contained 36,000,000 tons of ore assaying 1.06 per cent. copper, and had an area of 50 acres with an average thickness of 206 ft. overlain by an average thickness of 320 ft. of barren capping.

Jan 1, 1930

Jan 1, 1916

Aamot, Olav Crone, (M'29) Chem. Engr., Elektrokemisk, Raadhusgt. 23, Oslo, Norway. Abadilla, Quirico A., (M'3S) Min. Engr., Dir., Bu¬ reau of Mines. Manila, P. I. Abbott, Agatin Townsend, (J'40) Jr. Engr., Phelps Dodge Corp., Morenci Branch, Morenci. Ariz. Abbott, Clarence E., (M'04) Civil Engr., V.P., Ten¬nessee Coal Iron & R.R.. Co., 1542 Brown -Marx Bldg.. Birmingham, Ala. Abel, Raymond L., (M'28) Chem. Engr., Command¬ing, Officer, Pittsburgh Chem. Warfare Procurement Dist., American Bank Bldg., Pittsburgh. Pa. Abel, Walter D., (M'32) Alin. Engr.. Div. of Cor¬porations, State of Calif., 403 California State Bldg., Los Angeles, Calif. Abele, Louis T., (M'31) 423 3rd Ave., Decatur, Ga. Abell, Leo M., (M'31) Mill Supt. & Met., Emperor Gold Min. Co., Led., Vatnkoula, Fiji Islands. Abernathy, G. E., (M'38) Geol., Kansas State Geol. Survey, Pittsburg, Bans. Abernathy, Jack H., (M'40) Peer. Engr., c/o Superior Oil Corp., National Bank of Tulsa Bldg., Tulsa, Okla. Aborn, Robert H., (M'10) Asst. Met., Research Lab., U. S. Steel Corp., Lincoln Highway, Kearny, N. J. Abraham, A. W., (M'39) Peer. Engr., Richfield Oil Corp., 555 S. Flower St., Los Angeles, Calif. Abramowitz, William L., (J'40) Chem., Industrial Inventions, Inc., 103 Foster Se., Peabody, Mass.

Jan 1, 1942

By R. M. Larsen

The Rocky Mountain region is defined with some variations for different purposes or by different organizations. For oil and gas development, Wyoming, Montana, Colorado, northwestern New Mexico, and Utah are included in the order of their apparent importance. Portions of adjoining states, such as North and South Dakota, Nebraska, Arizona, Nevada, and Idaho, arc attributary to this region, but have little or no oil or gas production. Nebraska and New Mexico are considered separately (see pp. 412 and 415), and most of the discussion in this report will be confined to Colorado, Montana, and Wyoming. Utah has produced about 200,000 bbl. of oil from the San Juan and Virgin fields, which are isolated and shut in at present. The Clay Basin field in northeastern Utah produces natural gas and distillate, and the Farnham field in central Utah produces carbon dioxide gas. Other Utah areas of some interest are listed in Table I. The Cedar Creek (Baker-Glendive) field in southeastern Montana extends into North Dakota, but is listed under Montana. The other states are in the main wildcat areas, and exploration in 1944 was at a minimum. However, geological and geophysical parties are reviewing them for further testing. Oil production in Colorado, Montana and Wyoming was 459,000 bbl. more than in 1943. Increases of 713,000 bbl. in Colarado and 731,000 bbl. in Montana offset a loss of 985,000 bbl. in Wyoming. This was the first decline in Wyoming since 1938. Field production figures and state totals are given in Table I. Total drilling activities in these three states and Utah increased from 687 wells making 1,442,511 ft. of hole in 1943 to 916 wells making 2,245,803 it. in 1944. Wildcat drilling increased from 163 wells making 331,193 ft. of hole in 1943 to 171 wells making 389,144 it. in 1944. These figures include all drilling wells making footage, not starts or completions, and represent an all-time high in drilling. The year 1944 witnessed the greatest concentration of seismograph activity that the region has had. The Rocky Mountain Oil Scouts Association reported that in 1943, the previous peak year, 91 crew months of work were performed; in 1944, the time was 254 crew months. About 67 per cent of the work was in Wyoming, 18 per cent in Montana, and 12 per cent in Colorado. Twenty-three blocks totaling 400,000 acres were reported assembled in Colorado, and 161 blocks totaling 4,000,000 acres in Wyoming. Information about other states was not given. Fourteen unit agreements were approved by the Department of the Interior, as compared with 13 in 1943. The 1944 agreements were all in Wyoming. In five of the unit areas, oil or gas discoveries were made, four were dry, and five were drilling Or pending' Oil companies find it advantageous to unitize blocks containing any proportion of public domain. Units for

Jan 1, 1945

By W. A. Wall, R. L. Kidd

IN present-day flotation practice, grinding of the flotation feed is carried to extremely fine sizes, 70 to 80 per cent minus 200 mesh being customary. The greatest flotation losses occur in the coarsest and finest sizes, but the losses in the very fine sizes are, of course, much the more important because of the large proportion of fines in the feed. These losses are particularly high in zinc ores so a study of the effect of size on the flotation of sphalerite has been made. The mineral used in these experi¬ments was a pure sphalerite, especially free from copper, from the Joplin district in Missouri. The sizes coarser than 200 mesh were separated by screening, the sized mineral then being deslimed on a Wilfley table. The sizes finer than 200 mesh were obtained by water elutriation as described by H. R. Bradford (M. S. Thesis, University of Utah, 1932) ; particles finer than 6.5 microns could not be obtained with the apparatus used.

Jan 1, 1933

Discussion of the paper of, RICHARD H. RICE, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin No. 89, May, 1914, pp. 721 to 743. S. G. VALENTINE, Oxford, N. J.-In a paper read at the New York meeting of the Institute last February I presented some notes taken from our experience with the turbo blower operating on a blast furnace. In connection with Mr. Rice's very interesting paper there are a few items that might be of further practical interest. The question of the reliability of this type of blower will naturally be presented. In this connection we would say that our turbo blower has been in practically continuous use during the present blast, which was begun June 7, 1912, with only three interruptions for repairs of any consequence. Soon after blowing in there was developed a tendency of the blower to surge or pulsate. This occurred on operating at a point considerably below the normal capacity of the machine, and was checked with comparatively little trouble by throttling the intake slightly and taking up a small lost motion on the governor connections, a legacy of the previous blast that had not been attended to. All this required only a few hours' time. In. March, 1914, the furnace being banked on account of a blizzard that cut off our freight deliveries for five days, the opportunity was used to replace the carbon packing on the steam-turbine shaft and to repack the steam inlet valves. In June, 1914, the blower was off 8 hr. to replace an oil ring and scrape a bearing. With these exceptions we have made continuous use of the machine and find we can depend upon it with entire safety as a piece of machinery.

Jan 4, 1915

By Allen J. Johnson

With a realization of the rapidly increasing importance of automatic stokers as a medium for domestic heating, the Anthracite Institute Laboratory has conducted extensive investigations, over a period of several years, to determine the various outstanding characteristics of stoker design and performance. The purpose of this paper is to summarize these findings as a guide to current practices. Stokees Investigated One or more models of the underfeed stokers listed below were included in the various phases of this investigation: Beckley Gilkoal Burnwell Iron Fireman Combustioneer Motor Stokor Electric Furnace Man Norristown Super-stoker Erie Heat Generator Whitney Fire Ball (Tests Incomplete.) Fuel Saver Principles of Construction.—The operating principle of the leading makes of underfeed stokers is similar (Fig. 1). A plunger1 or slowly revolving worm2, conveys the buckwheat or rice sizes of anthracite to the center of a specially constructed tuyere pot where air is admitted to the coal through suitable ports of varying design. As the fuel burns, it is slowly forced to the outside circumference of the tuyere by the pressure of the incoming coal; eventually the ash falls over the edge of the pot, either entirely by gravity or aided by mechanical sweepers. In at least one model, the entire firepot revolves. While various special details have been included in the design of a number of stokers, they do not affect the general principles as described above, and therefore have not been included in this discussion.

Jan 1, 1936

By Allen J. Johnson

With a realization of the rapidly increasing importance of automatic stokers as a medium for domestic heating, the Anthracite Institute Laboratory has conducted extensive investigations, over a period of several years, to determine the various outstanding characteristics of stoker design and performance. The purpose of this paper is to summarize these findings as a guide to current practices. Stokees Investigated One or more models of the underfeed stokers listed below were included in the various phases of this investigation: Beckley Gilkoal Burnwell Iron Fireman Combustioneer Motor Stokor Electric Furnace Man Norristown Super-stoker Erie Heat Generator Whitney Fire Ball (Tests Incomplete.) Fuel Saver Principles of Construction.—The operating principle of the leading makes of underfeed stokers is similar (Fig. 1). A plunger1 or slowly revolving worm2, conveys the buckwheat or rice sizes of anthracite to the center of a specially constructed tuyere pot where air is admitted to the coal through suitable ports of varying design. As the fuel burns, it is slowly forced to the outside circumference of the tuyere by the pressure of the incoming coal; eventually the ash falls over the edge of the pot, either entirely by gravity or aided by mechanical sweepers. In at least one model, the entire firepot revolves. While various special details have been included in the design of a number of stokers, they do not affect the general principles as described above, and therefore have not been included in this discussion.

Jan 1, 1936

By L. C. Morganroth

Magnesite both Massive and Crystalline MAGNESITES are. of two general classes-massive and crystalline. Massive magnesite occurs in serpentine, being formed by the breaking down or decay of serpentine-making minerals or rocks as olivine, etc. (All the magnesia contained by the olivine is not liberated, as a portion goes to make up the serpentine; the breaking up of this serpentine later forms more magnesite.) Serpentine in various stages of transformation is found in the vicinity of magnesite deposits. Massive magnesite is very widely distributed. It is found in Greece, . California, Africa, India, Australia, Mexico, South America, and deposits of varying sizes occur in several of the European countries. Those on the Island of Euboea, Greece, are probable the most important deposits of this character of magnesite. They have been worked for a number of years, the principal quarries or mines being 3 miles in the interior from the village of St. George. (St. George is on the west coast of the island, between the towns of Limni and Khalkis.) (Figs. 1 and 2). -The magnesite occurs in veins or lenses in serpentine. Some of these lenses are very large; one worked several years ago was approximately, 50 ft. in thickness, 75 to 100 ft. high and 300 ft. or more in length. The magnesite is pure white and makes a very prominent feature of the landscape. While massive magnesite is widely scattered over the world, many of the deposits are in veins too thin to work. The usual mode of occurrence is in the form of stock work, the deposits in Venezuela, Mexico, and many of those in California, being of this form. The veins vary in thickness from the thinness of paper up to several inches, running in all directions, occasionally leading to a mass or nucleus of some,size. The spaces between the veins are filled with a disintegrated serpentine in the form of sand. Several of the deposits in California would probably be workable, if they were more favorably situated with reference to transportation, but by far the majority of the deposits are too poor to work. At one deposit,

Jan 9, 1914