By Richard A. Mullins, James J. Merle

Systematic sampling and analysis in coal-washing plants results in product control and economical operation. A well-organized laboratory system reduces operating costs and increases sales if the operating and sales companies make full use of information it supplies. The operating cost of a control laboratory is less than 1 pct per ton of coal produced. THE system of laboratory control as practiced by the Ayrshire group of mines was begun with the construction and organization of the first laboratory in conjunction with the completion of its first wash-ery in 1941. The primary purpose of this laboratory was to maintain a check on the quality of the coal produced from the washing plant. The laboratory was equipped to determine proximate analyses, float-and-sink tests, and screen analyses, and was staffed by a chemist. an assistant. and a technician. Members AIME, are Assistant Preparation Manager and Chief Chemist, respectively, Ayrshire Collieries Corp. and Subsidiaries, Danville, Ill. Joint AIME-ASME Fuels Conference. French Lick. October 1949. TP 2855 F. Discussion (2 copies) may be sent to Transactions AIME before June 30, 1950. Manuscript received Aug. 22, 1949. Soon it became apparent (1) that product control could be accomplished, (2) that a substantial reduction in operating costs could be effected by close control of coal losses in the rejects, and (3) that information furnished by the laboratory was of continuous value to the operating and sales companies. Consequently the laboratory function was expanded to supply them with additional data as required. As the parent company expanded and new mines were added, control laboratories were established at each mine equipped with washeries, and a central laboratory was maintained at one of the mines that was located equally convenient to all of them. A well-planned control laboratory assures production of a uniform, high-quality product. Whenever coal of substandard grade is loaded inadvertently, the sales company can be informed and the proper channel of distribution made. Conversely only constant and strict laboratory supervision can insure proper production of the various grades. Knowing the product, the producer can keep out of many customers' arguments that may be both awkward and expensive. Double checking between customers and mine laboratories have solved many disputes' Some nager insist On buying coal On the analysis basis only, with penalties for substandard coal and premiums for coal above normal quality. A substantial percentage of the coal sold by the Ayrshire group is of this nature. The usual procedure is for the customer to sample and analyze the coal as it is unloaded at the plant, and the mine laboratory samples it as it is loaded at the mine for subsequent analysis by the central laboratory. Only the unloaded moisture is considered, rather than the average of mine and plant moisture, and the buyer sends duplicate samples to the central mine laboratory for this determination. The average of the two analyses determines the price of coal at the mine. In this particular case, the laboratory plays an important part in increasing realization for two reasons: (1) every attempt is made to maintain plant efficiency and product quality as high as possible, (2) check on analyses and sampling by the buyer or seller.

Jan 1, 1951

By R. C. Buehl, J. P. Riott, E. P. Shoub

PILOT-PLANT tests have demonstrated that it is possible to produce low-sulphur sponge iron (0.03 to 0.05 per cent sulphur) as a continuous process in an internally fired rotary kiln from iron ore or mill scale; a solid carbonaceous reducing agent; and dolomite to control the sulphur content. The proportion of dolomite employed is small, so that it does not add materially to the cost of the sponge iron. The entire operation is carried out at temperatures well below the melting point of iron, so that the product is discharged in granular form. Compared with other methods for the production of sponge iron, the rotary-kiln method has the advantage of simplicity and low cost of equipment and; in addition, requires little labor for the operation of the process. The pilot-plant equipment used for this work was sufficiently large to demonstrate that the production of low-sulphur sponge iron in rotary kilns is feasible and that the costs are not excessive for applications in which sponge iron has distinct advantages over competing materials. This report constitutes a part of a program by the Bureau of Mines under a special Congressional appropriation for studying gaseous and solid fuel reduction of iron ores. Numerous articles on various phases of these investigations have appeared in Bureau of Mines publications or technical journals. Other articles are being prepared and will be published in the near future. The present program, which is under the supervision of Dr. R. S. Dean, Assistant Director of the Bureau of Mines, was initiated in .1942. However, a considerable portion of the work was a continuation of previous research performed by the Bureau. Previous investigators1-4 utilizing the rotary kiln for the production of sponge iron did not develop a suitable method for controlling the sulphur content. A review of the literature shows that the sulphur content in the product usually exceeded 0.2 -per cent unless reducing agents with very low sulphur contents were employed. This high sulphur value made the product generally undesirable for use as melting stock in electric or open-hearth furnaces. The production of sponge iron in an internally fired rotary kiln has been described in detail in Bureau of Mines Bulletin 2702; consequently, this article will be confined mostly to new features of the process-that is, means for controlling the sulphur content of the sponge iron. Suitable raw materials include iron ores or mill scale; coal or coke for reducing them, and sized dolomite (-20+100-mesh) as the sulphur-controlling agent. A mixture of the raw materials in granular form is fed into the elevated end of the kiln, which is fired axially from the lower or discharge end. In the reducing zone, which is approximately one third the length of the kiln measured from the dis-

Jan 1, 1946

By R. C. Mahon

The Homer iron-ore mine is at Iron River, Mich. Because it covers a large area, 400 acres, and because there was a considerable depth of water in the glacial drift above most of the ore bodies, this mine has presented a number of unusual and often difficult operational problems. The purpose of this paper is to discuss a few of the most important problems encountered. Surface Water Mining on this property was started on one 40-acre tract. The ledge in this area was the highest on the property and, although it was a real problem, water could be handled by underground pumping. During the first period of mining, drifts were driven just under the ledge and holes were drilled through to the surface material. In later years these drifts have been extended wherever possible. Although these drifts assisted in the drainage problem, it was evident they would not be sufficient alone. Before mining on a large scale could be started on this property, the water problem had to be solved. A number of test holes were put down to the ledge, and showed that there was an average 150 ft. of water-saturated glacial drift above the ledge over the rest of the mine. The upper 70 ft. was gravel and sand and the lower 80 ft. clay and hard pan, with some narrow seams of sand and gravel. It was evident that the water above the clay seam could not be drained off through openings in the ledge and for that reason it was decided to install surface drainage wells. This method of drainage was entirely new at that time and was pioneered at the Homer mine. The sinking of the first well was started in June 1929. Immediately following the first well a number of wells were sunk, but only to the top of the clay seam. This was done with the idea that a greater capacity could be obtained in a shorter time from gravel seams where the water flowed more freely and that the cost of pumping the water above the clay seam would be considerably less than if the wells had all been sunk to the ledge at once. Before the drainage of surface water was started, 1200 gal. per min. against a head of 800 ft. was being pumped from the mine. By March of 1932, with five surface wells in operation, the mine pumping had been reduced to 150 gal. per min. At this time we were pumping 5000 gal. per min., under an average head of 110 ft. from the surface wells. The total pumping costs were 30 per cent less than in 1929 because the greater capacity was being pumped at a much lower head. From 1932 to 1936 the mine was idle and all surface pumping was stopped. Since 1936, 10 new wells have been added with a total pumping capacity of 8000 gal. per min. at the present time. The water level has been lowered 70 ft. since surface pumping was started in 1929, and it is now approximately at the top of the clay. To remove the water below the clay seam, 11 of the 15 wells were sunk to the ledge.

Jan 1, 1946

By N. J. Grant, D. S. Bloom

An investigation of the Cr-Mo-Ni ternary system and attendant binaries has been completed. Some changes in the binary diagrams are shown to be necessary. The 1250°C section of the ternary and the liquidus surface have been delineated. A system of invariant reactions existing above 1250°C has been suggested. BECAUSE chromium, molybdenum, and nickel are important not only as bases for alloying systems but also as major alloying additions for other refractory metals, a study of the phase diagrams is of great interest and importance. In addition there are interesting features of theoretical value, a number of which are of prime consideration in this work. The major aim was to determine the ternary phase diagram of these metals at and above 1250°C, with sufficient attention given to lower temperatures to permit an understanding of the conditions existing at 1250°C and above. To understand ternary systems it is essential that accurate information concerning the binary systems be available, which in turn presupposes thorough knowledge of the constituent elements. On the basis of this investigation not only were significant inaccuracies indicated in the binary systems but much consideration had to be given to one of the elements, that is, chromium. The observation has been made that chromium undergoes a crystal transformation at a temperature near its melting point. Much of the experimental data leading to the detection of this transformation and the effects of this hypothesis on the form of the Cr-Ni phase diagram have already been reported' . and will not be repeated here. The experimental methods employed in the investigation have also been covered.'-" he purity of the molybdenum utilized in this work showed by qualitative spectrographic analysis that chromium, copper, iron, silicon, and tungsten were present in quantities of 0.1 to 0.001 wt pct. During the course of the investigation more than 100 melts were made, weighing from 150 to 200 grams each. Each of these melts was sectioned for chemical analysis and for specimens for examination in the as-cast and various heat-treated conditions by X-ray and metallographic means. All X-ray diffraction patterns reproduced here were made using chromium Ka radiation although iron and copper targets were used on occasions during the investigation. Experimental Results Mo-Ni-System: The most recent comprehensive investigation of the Mo-Ni system was made by Ellinger' in 1942; the diagram as shown in the American Society for Metals Handbook is based on his work. The work done on the system in this investigation substantiated the general form of the diagram although some differences were observed. These are indicated by a comparison of Ellinger's diagram and Fig. 1, the latter showing the results of pertinent thermal analyses made in this research. It can be seen in Fig. 1 that the eutectic composition is

Jan 1, 1955

By L. Burris, G. A. Bennett, P. A. Nelson

Staznless steels ave rrzuch less seuel-ely attacketl by zinc lapov than by molten zinc systems. To determine the applicubility of stainless steels fov equipment items which would be exposed only to zinc vapor, the corvosion resistance of several stainless steels to zinc vapor was investigated in 500-hr- exposuves at 900° C. Two austenilic stainless steels, Types 304 and 3-17, suffered severe intergranular attack. Loss of nickel from these steels and micro-probe crnalyses indicated the probable formation of low-melting zinc-rich phases. Good vesistance to attack by zinc vapor, as determined by metallo-9-rpaphic excr)rtination and physical testing, Loas exhibited by Type 405 stainless steel, a jevvitic steel. Type 440C stainless steel, a tnartensitic steel, although suffering considevable loss in weight, was not structurally weakened. At Argonne National Laboratory liquid zinc and zinc-rich alloys are being employed as solvent media in pyrometallurgical processes under development for recovering and purifying discharged reactor-fuel materials.' Because of the high solubility of most metals in liquid zinc,' there are few metals which can serve as container materials for liquid zinc at temperatures much above the melting point. The poor corrosion resistance of the common metals and alloys to molten zinc has been discussed by Eldred.3 DeKany, Lavendel, and Burris4 tested some of the less-common alloys of the nonrefractory metals and found that they also have poor resistance to attack by liquid zinc and Zn-Mg solutions. Of the metallic materials, only some of the refractory metals such as tantalum, tungsten, and molybdenum and their alloys have shown resistance to attack by liquid zinc.4-7 In the process-development work at Argonne National Laboratory, tantalum and tungsten vessels have been used to hold liquid-zinc alloys. These vessels are housed in stainless-steel equipment, principally to permit maintenance of an inert atmosphere and operation at various pressures. In this experimental work, it has often been observed that Type 304 stainless steel suffers little attack by zinc vapor at temperatures up to about 800 °C. In contrast, severe attack occurs in areas where zinc condenses as a liquid. The extent of attack by zinc vapor on several stainless steels was investigated because there are possible useful applications of stainless steel for equipment items which would be exposed only to attack by zinc vapor. These applications include, for example, housings around processing equipment as indicated above and vapor lines leading from zinc stillpots or retorts to condensers. EXPERIMENTAL EQUIPMENT AND PROCEDURE The experimental procedure consisted in exposing stainless-steel test coupons to static zinc vapor for 500 hr at a temperature of about 900°C. The apparatus, shown in Fig. 1, consisted of a 12-in.-long closed tantalum tube jacketed in Type 304 stainless steel to prevent oxidation of the tantalum. A Zn-10 wtpct Mg* alloy charge of 293 g in the bottom of the

Jan 1, 1965

By W. B. Boggs, J. N. Anderson

Originally, the copper produced at the Noranda smelter was shipped in the form of blister bars to the Laurel Hill refinery of the Nichols Copper CO, New York. In 1930 a refinery was built at Montreal East to refine Noranda copper and copper from the Hudson Bay Mining & Smelting Co., at Flin Flon, Manitoba. After investigation of the probable costs of making anodes at Noranda and at Montreal, it was decided to make them at Noranda rather than to continue to make blister bars there. Fuel is a major item of expense in making anodes, and since less fuel would be required in making them from molten copper than from blister bars, a lower anode-furnace cost could be expected at Noranda than at Montreal. Further, the expense connected -with making blister bars at Noranda would be eliminated. The cost of treating anode and wire-bar furnace slags is a serious item in a refinery, and it was found that the cheapest method would be to ship such slags back to Noranda. With the anode furnace at Noranda, much less anode-furnace slag would be made at the refinery. Against these savings effected by making anodes at Noranda must be set the high operating cost of an anode furnace at Montreal, using only tank-room scrap and the Flin Flon copper. This furnace would be handling a comparatively small tonnage and would have a high cost per ton. The usual equipment for making anodes from liquid copper consists of either a stationary reverberatory furnace or a tilting Tacoma-type furnace together with an anode wheel of the Clark or Walker type. The reverberatory type of furnace has been developed from the furnace used in the old Welsh process of smelting and refining copper, while the tilting furnace is a development of the holding furnace, which is essentially a Peirce-Smith converter without tuyeres and provided with burners. Refining as carried out in either of these furnaces is a batch process; that is, several converter charges are accumulated and then refined and cast. Colonel H. H. Stout recently developed in Arizona a so-called

Jan 1, 1934

By Richard A. Mullins, James J. Merle

Systematic sampling and analysis in coal-washing plants results in product control and economical operation. A well-organized laboratory system reduces operating costs and increases sales if the operating and sales companies make full use of information it supplies. The operating cost of a control laboratory is less than 1 pct per ton of coal produced. THE system of laboratory control as practiced by the Ayrshire group of mines was begun with the construction and organization of the first laboratory in conjunction with the completion of its first wash-ery in 1941. The primary purpose of this laboratory was to maintain a check on the quality of the coal produced from the washing plant. The laboratory was equipped to determine proximate analyses, float-and-sink tests, and screen analyses, and was staffed by a chemist. an assistant. and a technician. Members AIME, are Assistant Preparation Manager and Chief Chemist, respectively, Ayrshire Collieries Corp. and Subsidiaries, Danville, Ill. Joint AIME-ASME Fuels Conference. French Lick. October 1949. TP 2855 F. Discussion (2 copies) may be sent to Transactions AIME before June 30, 1950. Manuscript received Aug. 22, 1949. Soon it became apparent (1) that product control could be accomplished, (2) that a substantial reduction in operating costs could be effected by close control of coal losses in the rejects, and (3) that information furnished by the laboratory was of continuous value to the operating and sales companies. Consequently the laboratory function was expanded to supply them with additional data as required. As the parent company expanded and new mines were added, control laboratories were established at each mine equipped with washeries, and a central laboratory was maintained at one of the mines that was located equally convenient to all of them. A well-planned control laboratory assures production of a uniform, high-quality product. Whenever coal of substandard grade is loaded inadvertently, the sales company can be informed and the proper channel of distribution made. Conversely only constant and strict laboratory supervision can insure proper production of the various grades. Knowing the product, the producer can keep out of many customers' arguments that may be both awkward and expensive. Double checking between customers and mine laboratories have solved many disputes' Some nager insist On buying coal On the analysis basis only, with penalties for substandard coal and premiums for coal above normal quality. A substantial percentage of the coal sold by the Ayrshire group is of this nature. The usual procedure is for the customer to sample and analyze the coal as it is unloaded at the plant, and the mine laboratory samples it as it is loaded at the mine for subsequent analysis by the central laboratory. Only the unloaded moisture is considered, rather than the average of mine and plant moisture, and the buyer sends duplicate samples to the central mine laboratory for this determination. The average of the two analyses determines the price of coal at the mine. In this particular case, the laboratory plays an important part in increasing realization for two reasons: (1) every attempt is made to maintain plant efficiency and product quality as high as possible, (2) check on analyses and sampling by the buyer or seller.

Jan 1, 1951

By John Norton

IN recent years, the damping capacity of metals has come to be recognized as an important index of certain types of structural change. In a number of instances, this property has proved to be particularly sensitive, but insufficient work has been done to permit a general inter-pretation. There is considerable question at the present time as to just what factors are responsible for the internal dissipation of energy when a metal is carried through a cycle of stress, and these factors must be ascertained if the value of the damping method as a metallurgical tool is to be determined. Since internal stresses are among the chief causes of dissipation of internal energy, or damping capacity, it was thought that a study of the changes in damping during the recovery and recrystalliza-tion of a cold-worked metal might throw some light upon the subject, particularly if the damping changes were correlated with other properties that are better understood. Probably more work has been done on the recrystallization phenomena of alpha brass than on any other metal, so this was chosen as the material for the present investigation. Damping measurements on brass have been made by Förster and Köster.1 They showed that the annealing of a brass that had been cold-drawn to 50 per cent reduction produced a rapid fall in the damping, a flat minimum occurring at approximately the temperature of recrystal-lization. The damping remained at a low value until grain growth was well under way and then it increased rapidly with increasing grain size. Köster and Rosenthal2 continued the work in greater detail. They pointed out that the damping decrease does not correspond to the hard-ness drop but occurs at a lower temperature, suggesting that the relief or redistribution of internal stresses has a large effect while the actual recrystallization effect is small. They also show the increase in damping at the higher annealing temperatures. Their curves are reproduced in Fig. 1.

Jan 1, 1940

By N. T. Cotman, C. H. Pickering, P. B. Crawford

A beat-conduction model has been developed to study the flow of fluids in a stratified oil reservoir which is being subjected to unsteady-state depletion. To simulate stratification, plates of different metals were joined together so that cross flow could occur between strata. A description of the model, plate construction and necessary instruments is included. The data indicate that stratified oil reservoirs experiencing cross flow may be treated as a single, homogeneous, producing sand having properties intermediate between those of the layers making up the system. A technique for averaging core-analysis data to arrive at the proper average value of rock permeability and porosity is presented INTRODUCTION Although oil has been produced from reservoirs for 100 years and reservoir injection processes have been undertaken for 40 years, the industry is still inadequately informed on the problem of reservoir inhomogeneities. Stratification is perhaps the best-known type of reservoir heterogeneity. Urenl discussed the possible significance of this nonuniformity in his 1927 paper on the theoretical aspects of water flooding. Since this time the problem of vertical permeability variations has been the subject of much discussion and numerous papers. Levorsen2 simply describes the origin of layered beds in his Geology of Petroleum. Some beds are field-wide and may be traced from well to well, while others apparently pinch-out and become discontinuous. In addition, the physical characteristics of a layer may vary from place to place. For these reasons, a stratified system is not easily defined. In calculations involving oil reservoirs in which permeabi1ities vary, methods presently used contain many simplifying assumptions. The reservoir frequently is considered as consisting of permeable layers, each of uniform vertical and lateral permeability and each behaving as if separated from adjacent layers by thin impermeable layers. Other assumptions frequently made in reservoir calculations are steady-state flow conditions, unit mobility ratio, linear geometry, average or homogeneous porosity, and negligible capillary-pressure and gravity effects. Muskat3 has. developed solutions to the stratification problem for mobility ratios other than unity for both linear and exponential permeability distributions. He assumes lateral uniformity and continuity of all productive strata and does not consider porosity. This study will take into account transient effects, cross flow and varying porosity, as well as the variations in permeability, by means of a heat analogy. Muskat5 has shown the similarity of the equations which describe the flow of fluids in a porous medium to the flow of heat through a solid. Landrum, et al,6 made an analogy between the flow of fluid in an unsymmetrical reservoir and the conduction of heat in a similarly shaped metal plate. This analogy is summarized briefly as follows. If fluid is produced from an oil reservoir above the bubble point, the resulting pressure distribution will be identical to the temperature which would result in a metal or heat-conducting plate if heat were similarly removed. This means that a study of heat flow in stratified thermal models will behave like fluid flow in stratified oil reservoirs. For mathematical correspondencies, set- Ref. 6. The fluid mobility k/p is proportional to the thermal conductivity, and the porosity-times-compressibility product is proportional to the density times specific heat of the thermal plate. EXPERIMENTAL EQUIPMENT AND PROCEDURE The stratified reservoir model used in this study is illustrated schematically in Fig. 1. A Leeds and Northrup Speedomax Type G temperature recorder

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By J. T. Norton, N. J. Grant, A. M. Gervais

An investigation of the creep deformation of coarse grained specimens of high purity aluminum in the temperature range 800' to 1150°F, permitted the formulation of a theory explaining the formation of kink bands. The X-ray Laue back-reflection technique was used in conjunction with metallographic studies to determine the crystallographic elements involved in kinking and to measure the rotations of the bands. THAT metals deform by the formation of kink bands was first shown by Orowan1 in 1942. He manually compressed cadmium single-crystal wires, the basal planes of which were parallel to the wire axis and to the direction of compression. He found that kink bands formed quite suddenly. Similar experiments were performed by Hess and Barrett2 on zinc with a hydraulic testing machine to permit slower more careful compression. They observed that kink bands formed progressively with increasing compression. Recently Washburn and Parker3 observed the formation of kink bands in zinc single-crystal specimens during tension creep experiments. Each of these authors observed the formation of kink bands but did not make a complete analyses of the crystallographic relationships. In addition to these studies on hexagonal metals, extensive investigations of kink bands formed during deformation of aluminum in tension at room temperature have been reported. Two types of deformation bands have been observed during the deformation of aluminum at room temperature. These are: 1—kink bands: these exhibit a sharp curvature of the lattice along certain surfaces, and 2—bands formed by secondary slip along certain regions. As has already been shown by Honeycombe,4 it is important to point out the difference characterizing the two types of deformation bands. In the first case. for moderate deformation, only one system of slip planes normally is active; in the second case, however, two slip systems are active in the deformation bands. The latter have a rumpled surface because of the action of the two slip systems. In the present work only the first type of band was studied and to avoid any confusion the term kink band will be used exclusively in the discussion which follows. Honeycombe' observed that very narrow kink bands (width, 0.01 mm) formed along the (110) planes during the deformation of high purity aluminum at room temperature. He observed narrower ones in commercially pure aluminum and found also that their width decreased with decreasing temperatures. Chen and Mathewson5 reported the formation of kink bands during tensile testing of single crystals of high purity aluminum at room temperature and pointed out that some rotation occurred about a [211] direction. The influence of the bending moment on the formation of kink bands was illustrated by the experiments of Rohm and Kochendorferl0 who used a Polanyi apparatus to obtain pure shear during tensile testing of high purity aluminum single crystals. Under such conditions only one slip system was active and no kink bands were observed; consequently, no noticeable asterism was detected after deformation. The influence of the bending moment will be discussed later. Calnan8 gave a detailed account of the work performed on kink bands obtained during deformation of aluminum at room temperature. Because no explanation of the process of kink band formation in creep was given in the previous investigations and because some of the above observations are vital to the following discussion the brief review of the literature has been given. It is proposed in the present work to provide an explanation of kink band formation during creep deformation at elevated temperatures. Results and Discussion Kink bands were observed to form during tensile creep testing of high purity (99.995 pct) aluminum specimens, having a very large grain size, in the temperature range 800" to 1150°F. These observations were made in grains which occupied the whole cross section of the specimen. The specimens were originally round (diameter, 0.187 in.; gage length, 1 in.) and had parallel flats milled to permit easier metallographic and X-ray observations. The final

Jan 1, 1954

By J. M. McDowell, E. C. Doty, F. Morgan

Improvements in the X-ray method of measuring liquid saturation and saturation distribution are presented. Two identical direct current amplifiers have been added to measure continuously the intensities of the X-ray tube output and the beam which has passed through the core under test. The ratio of these intensities is automatically recorded on a modified Brown Electronik Recorder. Arrangements have been made to drive the core automatically and in synchronism with the recorder chart so as to give a continuous curve showing the variation of liquid saturation along the length of the core. By determining the ratio of the two X-ray beam intensities simultaneously the measurements are made essentially independent of small fluctuation in voltage and current supplied to the tube. This improved technique has been used for investigating the fluid distribution along the length of cores and core assemblies when one fluid is displaced by another. Typical results of these studies are shown. INTRODUCTION In a previous publication' a method was described for measuring the oil saturation in cores which was based on the absorption of X-rays by the fluid content of the core. While that technique is capable of yielding accurate results, the original apparatus was not especially convenient for determining the fluid distribution along the length of a core. This was primarily due to the slow response of the amplifier and galvanometer and the necessity of making a point by point survey of the material under investigation. It was, therefore, not only possible for sections of the core having a variable or unusual saturation distribution to escape observation entirely, but changes in output of the X-ray generator between readings on the unknown and the monitor introduced errors in the measurements that could be avoided only by further stabilization of the source or by taking a large number of readings. This paper describes a method and apparatus for recording continuously and automatically the intensity of the X-ray beam that is transmitted by a core. The variation of saturation with time at a given section of the core may thus be found, or by scanning the core by driving it in synchronism with the recorder the saturation distribution may readily be determined. As indicated in the previous paper, the X-ray method possesses an advantage over the weighing technique in relative permeability experimentation in that the core need not be removed from the holder for the purpose of making a saturation measurement. Furthermore, the actual distribution of fluid and the effects upon that distribution of inflow and outflow heads may be investigated. And errors due to gas bubbles or loss of liquid that are frequently sources of error in volumetric methods of saturation determination are avoided. PRINCIPLE OF THE METHOD The energy in an X-ray beam that has passed through an absorbing material is expressed by the well known formula: E = E0, e-cd (1) where E, is the energy in the incident beam, µ the mass absorption coefficient, c the density or concentration of absorbing material, and d is the length of path of the beam in the absorber. The coefficient µ varies with the wavelength of the radiation as well as with the absorbing material. The output of an X-ray tube varies in an approximately linear manner with the tube current, but to the second or higher power of the anode voltage. Moreover, the quality or wavelength distribution of the radiation varies with the voltage.

Jan 1, 1950

By B. E. Morgan, C. K. Dumbauld

The need for a low-strength cementing composition for use in well cementing is reviewed and results are presented of laboratory and experimental field tests of a modified cement having a controlled ultimate tensile strength of approximately 200 psi. The modified cementing composition may he prepared from either high early strength or normal portland cements by the addition of bentonite clay and a suitable agent for dispersing and controlling the set of the slurry. Substitution of the modified cement for conventional slow-set cements may give better completion results in many wells because the modified cementing composition has lower set strength, lower slurry density, and greater slurry stability than conventional cement slurrieh. The lower ultimate strength allows greater penetration with less shattering of the set cement when perforating casing and cement. The lower elurry density allows the placement of longer columns of cement slurry, and the greater slurry stability reduces the possibility of having an uncemented section caused by the settling of cement particles before the cement set.. INTRODUCTION High strength lias always been one of the accepted criteria of a good cement. During the early use of portland cement in well cementing. emphasis was placed upon securing cements with higher strengths. In 1931, Barkis' reported that, "Normal oil well cements have been improved to develop greater strengths and uniformity of product, which has aided in producing successful jobs in cementing the deeper strings." As long as most wells were completed by the open-hole method. the use of cements having high strengths seemed desirable, and there was no objection raised against high-strength cementing compositions. For a number of years. how-ever, the industry has been completing a large numher of wells by setting and cementing casing through productive horizons and then obtaining production by gun-perforating the section of casing opposite the desired interval. Although this method has been generally successful, difficulties have been experienced in some cases in completing or recompleting wells because of apparent lack of adequate penetration by the bullets through the casing and surrounding sheath of cement and into producing formation. In addition to the penetration trouble: there have been indications that fracturing and shattering of the set cement by perforating might he a contributing factor in causing the failure of some jobs to exclude water or gas from oil producing zones. The possibility that cements having high set strengths were contributing to til difficully ill obtaining satihfartory perforating results has re. ceived attention during recent years. Gun perforating tests conducted in 1944 showed that the depth of bullet penetration into set cement varied with the hardness of the cement, the greater the strength of the cement the less being the penetration. In 1946, Farris2 pointed out that high strength cements were not needed in well cementing, and in 1947, data published by Oliphant and Farris3 showed that set cement was perforated without shattering at approximately 150 psi tensile strength. whereas at approximately 300 psi tensile strength severe cracking and shattering occurred. Oliphant and Farris suggested that wells be perforated at the proper time interval after placement of the cement so that the set cement would have the desired strength. Several difficulties may he encountered in trying to perforate a cement job at the correct time to catch the tensile strength near 150 psi. The rate of strength development of different cements varies considerably. This fact is illustrated by results of tensile strength measurements presented in Fig. 1. These data show that at 175°F the tensile strengths of three conventional slow-set cements varied from 75 to 235 psi at the end of 12 hours. After 24 hours, the tensile strengths varied from 200 to 455 psi. The rate of strength development is affected. also. by the temperature of the forniation, and this adds to the uncertainty of perforating at the rorrect time, since accurate well cementing temperatures may not he known in many cases. Furthermore, in the recomple-tion of wells it is sometimes necessary to perforate cement which has set for a long period and has developed maximum or final strength. In view of the apparent need for a cementing composition having a controlled ultimate strength, an investigation was

Jan 1, 1951

By R. T. Hukki, P. Voutilainen

This paper describes a new apparatus for continuous wet fine-screening. Its preferred size range seems to be from 0.1 to 1 mm. The supercritical trommel screen is a short cylindrical trommel of wedge-bar type construction operated at a speed greater than the calculated theoretical critical speed and at a speed lower than the speed at which particles introduced into it will centrifuge. The paper describes results obtained with the prototype supercritical trommel screen in pilot plant scale. The results point to a high capacity and simultaneously to a high sharpness of screening. Finally, an analysis is presented of the forces acting in screening on a supercritical trommel screen. In the era of high speed, high capacity processing of raw materials the conventional slowly rotating trommel screen is often considered a relic from the times passed. A typical trommel screen is the cylindrical trommel rotated about a horizontal or slanting axis at a relatively low speed. Its screening characteristics are well known. Trommel screens of various types of construction, methods of operation, performances and other characteristics have been described in detail by Taggart.1 The theoretical critical speed of a trommel screen is defined by the same well known equation as that applied for grinding mills: where ncritical = the numerical value of the theoretical critical speed in rpm, D 1 = the inside diameter of the trommel in feet, and D2 = the inside diameter of the trommel in meters. ncritical corresponds also to the centrifuging speed provided that the coefficient of friction f between the trommel surface and the outer layer of the charge is = 1.0. In a general case: From Eq. 2 it is seen that in all cases where f < 1.0 the centrifuging speed of the trommel is greater than the theoretical critical speed. The supercritical trommel screen concerns screening operations within that speed range which is between the theoretical critical speed defined by Eq. 1 and the centrifuging speed defined by Eq. 2, under conditions such that the coefficient of friction f<1.0. It is reported by Taggartl that the optimum speed of a conventional cylindrical trommel screen 36 in. in diam was experimentally found to be about 16 rpm. From Eq. 1, the critical speed of this trommel is 44.2 tpm. The indicated optimum speed corresponds to (16/44.2) x 100% = 36.2% of the theoretical critical speed. The optimum speed range based on information available seems to vary from 33% up to 45% of the theoretical critical value. The trommel screen operated at a supercritical speed: operates at a speed greater than the calculated theoretical critical speed; operates at a speed lower than the speed at which the charge introduced into it will centrifuge; operates within the supercritical speed range in such a way that the coarse fraction of the charge must slide in respect to the inside surface of the trommel; the outer layer of the said fraction next to the screen tends to proceed in the same direction as any selected point on the trommel surface, but now at a lower speed, and indeed at a subcritical speed; allows to a certain degree adjustment of the maximum determining particle size x of the fine product simply by a variation of the speed of the trommel within the supercritical speed range. With increasing trommel speed, finer and finer material only will get the opportunity to find its way into the fine product while the screen opening remains constant. In conventional practice, the low speed trommel is generally used for sizing of coarse and medium coarse material, but seldom for fine screening. The characteristic feature of the product passed through the conventional trommel is that the determining size x of the biggest particle is barely smaller than the nominal size of screen opening. The supercritical trommel screen, on the other hand, is best suited for sizing of relatively fine material. Furthermore, the characteristic determining size x of the biggest particle in the fine product can be substantially smaller than the nominal width of the screen opening or slot. In the trommel screen best suited for the applications

Jan 1, 1965

By F. A. Forward, V. N. Mackiw

The paper relates to the laboratory and pilot plant studies that have been carried out by Sherritt Gordon Mines Ltd., Metallurgical Research Div., in developing the ammonia pressure leach process for extracting copper, nickel, cobalt, and sulphur from high grade nickel concentrate produced from Lynn Lake ores, and describes in some detail the chemistry of the process. IT is well known&apos;.&apos; 2 that copper, nickel, cobalt, zinc, ferrous iron, and a number of other metals combine with ammonia in aqueous solution to form complex ions of the form [Me(NH,)x]"+. The stability and solubility of these ions depend on the concentration of the metal ion in solution, on the amount of NH, present, and on the amount and type of anions present, e.g., OH-, C0;-, NO,, C1-, SO;-. If ammonia is partially or completely removed from such solutions, for example by boiling, the soluble ammines tend to decompose and the metals precipitate as basic salts. These properties of metal ammines have found practical application in the commercial recovery of copper, nickel, and cobalt from a variety of ores. In an operation formerly conducted at Kennecott"" the mill tailing containing 0.80 pct Cu as copper carbonate was leached by percolation with an ammonia-ammonium carbonate solution to dissolve the copper as the ammine. At Calumet and Hecla0-" With a mill tailing containing about 0.4 pct Cu as metallic copper, it has been found necessary to aerate the ammonia-ammonium carbonate leach solutions between stages to oxidize the solubilized copper. At Nicarol"-" where nickel and cobalt occur as oxides and silicates which are not soluble in ammonia, the ore is heated to decompose silicates and to selectively reduce the nickel and cobalt to metal, leaving the iron as Fe,O,, and is then leached with ammonia-ammonium carbonate solution accompanied by aeration to dissolve nickel and cobalt as ammines. In each of these leaching operations, the anion present is CO, and the metals can be precipitated from the leach solution as oxide (copper) or hydroxide and carbonate (nickel and cobalt) by boil- ing off NH, and C02 both of which are recycled to treat a subsequent ore charge. The products-—oxide, hydroxide, or carbonate—can be treated by conventional smelting, calcining, or electrolytic methods to convert them to refined metals. Thus the procedures mentioned utilize the properties of the ammines to extract copper, nickel, and cobalt from nonsulphide ores and separate them from the leach solutions. These processes have the advantage that they can be carried out in closed vessels at atmospheric pressure, that the leaching solutions are specific for the desired metals, that the metals can be recovered as relatively pure compounds by the boiling operation, and that the NH, and CO, can be recycled. Also, as the leach solutions after boiling and filtration are substantially free of metals, NH,, and CO,, they can be discarded, thus facilitating the control of the water balance in the leaching circuit. When, as is the case with Sherritt Gordon concentrates, sulphides are treated with ammonia solution in the presence of oxygen, the leach solution contains SO,--, and an entirely different set of conditions is encountered. The ammine sulphates (of nickel, for example) are more soluble than the carbonates and can be only partially decomposed by boiling. The SO, and NH, in the solutions can not be recovered by boiling. Thus, despite the more favorable leaching conditions resulting from high solubility of the ammine sulphates, the recovery of metals, NH,, and SO, from the solutions must be effected by other means. Sherritt Gordon Nickel Concentrate Treatment The Ni-Cu-Co flotation concentrate produced at Lynn Lake&apos;" contains 12 to 16 pct Ni, 1 to 2 pct Cu, 0.2 to 0.5 pct Co, 33 to 40 pct Fe, 28 to 34 pct S, 8 to 20 pct insoluble, and less than 0.02 oz per ton precious metals. The nickel is present chiefly as pentlandite, the copper as chalcopyrite, and the iron as pyrrhotite and pyrite. Most of the cobalt is thought to be present in pentlandite, although it is known that a small amount occurs as Co-Ni-pyrite.

Jan 1, 1956

By M. J. Coolbaugh

Mining potash at depths of 3000 ft or more beneath thick water-bearing sediments in Saskatchewan presented a unique challenge to the North American mining industry. Potash is known to flow under pressure, but the knowledge of its flow characteristics at great depths was inadequate for safe design of mine workings and for assured protection from water above the salt formations. At the 3000-ft. depth of the Canadian mines, the potash is stressed beyond its elastic limit, and therefore mining design must deal primarily with its behavior as a plastic material. Recognizing that careful study would be required in order to assure safety and stability of mine workings in deep potash, IMC initiated an extensive rock mechanics investigation of structural properties of potash and salt under high-stress conditions. This presentation consists of a brief review of the development of some methods of testing potash in the laboratory and in the field; some of the rock mechanics concepts and principles derived; and their application to potash mine design. The mining of potash more than 3000 ft beneath the water-bearing sediments in Saskatchewan presented the unique challenge of designing stable mine workings and assuring protection from overhead water in a material that was believed to flow plastically, but whose behavior as a plastic material was not sufficiently known. Under the stress conditions ordinarily encountered in mining, most rocks behave as elastic materials; that is, they compress slightly under pressure, and rebound when the pressure is released. Salt and potash, however, are different. Even under the relatively low pressures encountered at shallow depths, these materials become slightly plastic and yield to stress by flowing.* The plastic properties become more pronounced at greater depth and pressure, and the question arises as to whether or not the plastic flow will be rapid enough and exert enough pressure to destroy underground structures or interrupt the mining process. It was found, however, that not only was there an insufficiency of information about the behavior of potash and salt, but conventional methods of testing these materials, such as determining the modulus of elasticity, Poisson&apos;s ratio, and uniaxial compressive strength, were inapplicable because of the high stress conditions prevailing at the 3000-ft depth. Potash under high pressure, for example, has practically no modulus of elasticity, its stress-strain relationship varies with time, and its compressive strength depends upon the degree of confinement. Elasticity and Stress/Strain Relationship: Fig. 1 shows a standard stress/strain chart for potash as made by the Department of Mines in Canada. Typically, when stress is applied to a hard-rock specimen, the specimen contracts, then expands to its original shape when the stress is withdrawn. This chart illustrates, however, that potash under stress yields to the stress by flowing, and does not expand when the stress is withdrawn. When the applied stress was held constant for 30 min, beginning at points A and C, the strain continued to increase and the potash flowed to points B and D, respectively. Points B, D, F, and H show that the potash did not return to its original shape when the stress was released. Thus it can be observed that potash has practically no elasticity and that the amount of strain depends upon the length of time that the stress is applied. Compressive Strength: The conventional method of determining the compressive strength of hard material is to find the maximum pressure that long slender specimens of the material can withstand without failing. As illustrated in Fig. 2,* line B, a standard 2-in. cube of potash subjected to a conventional type of uniaxial compressive test will exhibit a strength of about 5000 psi. However, the compressive strength exhibited can be made to change by changing the conditions under which the test is made. For example, if teflon plates lubricated with graphite are inserted between the press and the specimen, thus minimizing end constraint, the compressive strength is only about 2500 psi, shown in line A. If a specimen is cut in half, changing the width-to-height ratio to 2 : 1 instead of 1:1, and then tested without lubri-

Jan 1, 1968

By Henry Lewelling

An experimental investigation of the relative effectiveness of standard bullets and "shaped charges" in perforating dense, hard formations is reported. A method is described which simulates the conditions under which a shot is normally fired. Results are evaluated on the basis of depth of penetration, extent 01 Fracturing. extent and nature of formation damage, and other physical characteristics. INTRODUCTION A study was made of the relative merits of bullets and "shaped charges&apos;&apos; as applied to well completions in hard, dense formations such as those encountered in the Permian Basin. The planning of the laboratory program stipulated that core samples should be prepared and mounted in such a way that perforation shots of either kind"" could be fired into them, keeping the factors pertinent to good shooting practice similar to what they would be in a well. The shooting was done in a buried tank. with the sample and shooting equipment covered with water. The depth of water was calculated to he sufficient to simulate the inertial effects of well fluids for the duration of an explosion (a few micro-seconds). Flow measurements were attempted on the specimens after perforation. Due to the lack of uniformity of the limestone, shale breaks. etc., these measurements proved to be of little value to the study. The mounting materials were removed. so that the character of the penetration. fracturing, etc., could be observed. METHOD Laboratory samples were selected from the hard. dolomitic sand cores from Block 31 Field. Core pieces having a 3 3/4 in. diameter and a useful length of 10 to 12 in. were used. Selection was aimed at those pieces having a minimum of shale streaks and other irregularities. The ends were cut off square Manuscript received in the Petroleum Branch office June 28, 1951. Paper presented at the Petroleum Branch Fall Meeting in Oklahoma City, Okla., Oct. 3-5, 1951. with the diamond saw. Prior to lbeing mounted. the cores were soaked in water to prevent them from absorbing water out of the wet concrete, thus weakening it. A set of steel capsules was fabricated for holding the core Samples. Seven-in. casing was cut in two-ft lengths. of which one end was closed by "orange-peeling" and welding, and the other was threaded to accept a standard bull plug. The bull plugs were fitted with copper tube connections .so that pressure could be applied when the capsules were made up. The cores were mounted in the capsules by means of wire centralizers whose function was to hold the Core in proper position while concrete was poured and set. A special aggregate was prepared wing a graded sand and gravel mixture

Jan 1, 1952

By C. K. Dumbauld, B. E. Morgan

The need for a low-strength cementing composition for use in well cementing is reviewed and results are presented of laboratory and experimental field tests of a modified cement having a controlled ultimate tensile strength of approximately 200 psi. The modified cementing composition may he prepared from either high early strength or normal portland cements by the addition of bentonite clay and a suitable agent for dispersing and controlling the set of the slurry. Substitution of the modified cement for conventional slow-set cements may give better completion results in many wells because the modified cementing composition has lower set strength, lower slurry density, and greater slurry stability than conventional cement slurrieh. The lower ultimate strength allows greater penetration with less shattering of the set cement when perforating casing and cement. The lower elurry density allows the placement of longer columns of cement slurry, and the greater slurry stability reduces the possibility of having an uncemented section caused by the settling of cement particles before the cement set.. INTRODUCTION High strength lias always been one of the accepted criteria of a good cement. During the early use of portland cement in well cementing. emphasis was placed upon securing cements with higher strengths. In 1931, Barkis&apos; reported that, "Normal oil well cements have been improved to develop greater strengths and uniformity of product, which has aided in producing successful jobs in cementing the deeper strings." As long as most wells were completed by the open-hole method. the use of cements having high strengths seemed desirable, and there was no objection raised against high-strength cementing compositions. For a number of years. how-ever, the industry has been completing a large numher of wells by setting and cementing casing through productive horizons and then obtaining production by gun-perforating the section of casing opposite the desired interval. Although this method has been generally successful, difficulties have been experienced in some cases in completing or recompleting wells because of apparent lack of adequate penetration by the bullets through the casing and surrounding sheath of cement and into producing formation. In addition to the penetration trouble: there have been indications that fracturing and shattering of the set cement by perforating might he a contributing factor in causing the failure of some jobs to exclude water or gas from oil producing zones. The possibility that cements having high set strengths were contributing to til difficully ill obtaining satihfartory perforating results has re. ceived attention during recent years. Gun perforating tests conducted in 1944 showed that the depth of bullet penetration into set cement varied with the hardness of the cement, the greater the strength of the cement the less being the penetration. In 1946, Farris2 pointed out that high strength cements were not needed in well cementing, and in 1947, data published by Oliphant and Farris3 showed that set cement was perforated without shattering at approximately 150 psi tensile strength. whereas at approximately 300 psi tensile strength severe cracking and shattering occurred. Oliphant and Farris suggested that wells be perforated at the proper time interval after placement of the cement so that the set cement would have the desired strength. Several difficulties may he encountered in trying to perforate a cement job at the correct time to catch the tensile strength near 150 psi. The rate of strength development of different cements varies considerably. This fact is illustrated by results of tensile strength measurements presented in Fig. 1. These data show that at 175°F the tensile strengths of three conventional slow-set cements varied from 75 to 235 psi at the end of 12 hours. After 24 hours, the tensile strengths varied from 200 to 455 psi. The rate of strength development is affected. also. by the temperature of the forniation, and this adds to the uncertainty of perforating at the rorrect time, since accurate well cementing temperatures may not he known in many cases. Furthermore, in the recomple-tion of wells it is sometimes necessary to perforate cement which has set for a long period and has developed maximum or final strength. In view of the apparent need for a cementing composition having a controlled ultimate strength, an investigation was

Jan 1, 1951

By E. Eichen, G. S. Ansell. L. R. Sefton

A Technique for the Preparation of Thin Films of Two-Phase Alloys Suitable for Use in Transmission Electron Microscopy In order to obtain foil sufficiently thin to permit transmission electron microscopy of two-phase alloys, particularly alloys in which the second phase is present as a very finely dispersed second phase, a technique has been developed to permit the thinning of these materials without either the large degree of pitting present in the electrochemical or chemical thinning process or the slicing of the second phase particles accompanying the mi-crotoming process. The metal or alloy to be thinned is first ground to initial sheet thickness of approximately 0.002 in. by hand grinding on 4/0 emery paper. This starting sheet of material is then reduced in cross section by an air-abrasion technique using an S. S. White dental abrasive unit. This unit consists of a supply of compressed CO, which provides a stream of high velocity gas impinging on the metal surface. Incorporated in the machine is a hopper-type of device in which fine abrasive particles of alumina are introduced into this high velocity gas stream. The abrasive particles are irregular in shape, approximately 30 across. If any particles are introduced into the sample during thinning, they should be readily observable. Impingement of this gas abrasive mixture on the metal surface causes rapid removal of the metal in a rather uniform manner. The rates of metal removal may be adjusted by both regulating the gas pressure and amount of abrasive material introduced into the gas stream. By moving the gas stream abrasive mixture slowly about the specimen or sheet surface, a large area of the sheet may be uniformly reduced to a thickness which is then suitable for use in transmission electron microscopy. Attendant with this metal removal is a result in cold working of the metal surface due to the impingement of the abrasive particles. The resultant foils, therefore, if made from materials which are desirable to view in the annealed condition, have to be subsequently heat treated. If the alloy from which these foils have been made has been initially heavily worked or deformed during manufacture, then no subsequent heat treatment is, necessary as in the case of the SAP-type alloys. Following this initial abrasive thinning technique, the material is then given a final electropolish which is just sufficient to remove any oxide which has formed on the metal surface during the abrasion technique. Care has to be exercised in this technique to make sure that none of the attendant problems associated with the chemical or electrochemical removal process are encountered. An electrolyte solution which has been found suitable for aluminum-aluminum oxide SAP materials is one containing 78 ml of perchloric acid, 120 ml of distilled water, 700 ml of ethanol, and 100 ml of butylcellosolve. The current density used is 1 amp per sq cm and a polishing time of 3 sec on each side of the foil is used. Extreme care must be used in choosing the current density and time to ensure that just the oxide film on the specimen is removed. Times or current density which are greater than this will lead to perforation of the film due to the removal of the A1,0, particles or a complete loss of the film due to complete solution of the matrix. Once the oxide film is removed the specimens must be kept in alcohol until placed in the microscope to prevent any further oxidation. Fig. 1 shows -an electron micrograph at X28,000 of a thin foil of an aluminum-aluminum oxide SAP-type alloy prepared using this technique. The alloy consists of a matrix of commercial purity aluminum containing a very finely dispersed second phase of aluminum oxide flakes. In the electron micrograph, the dark patches are the aluminum oxide particles. The lighter portions of the micrograph are the aluminum matrix. Within the aluminum matrix, the dislocation structure of the alloy is clearly visible. This structure consists of intersecting twin boundaries and single dislocations. No abrasive particles were observed in the samples. In addition, thin films of commercial purity aluminum were prepared using this method and observed in the electron microscope. Here also, there was no evidence of abrasive particles introduced in the samples. The technique presented provides a satisfactory method for the production of thin films of aluminum-aluminum oxide SAP-type alloys for use in transmission electron microscopy where none of the usual thinning techniques appears to be satisfactory.

Jan 1, 1962

By W. B. Nelligam, J. Tittman

Refinements in radiation logging techniques during recent years have involved increasing usage of scintillation ditectors. These detectors produce voltage pulses whose heights are related to the energies of the gamma rays which initiate them. Analysis of the gamma-ray spectrum, as indicated by the pulse heights, yields information about the chemical elements composing the formations surveyed. Refined scintillation counter techniques can furnish chemical information concerning earth formations in situ, from a study of the gamma-ray spectra emitted by the formation either naturally or as a result of neutron bombardment."&apos; Accompanying the rising interest in gamma-ray scintillation spectroscopy, there has been increased activity in the development of accelerator-type neutron sources (in contrast to encapsulated chemical-mixture sources). Such neutron generators are attractive for several reasons: (1) they greatly reduce radiation hazards to personnel; (2) there is a great reduction in contamination danger if they are lost in the hole; (3) they can produce larger neutron intensities than can conveniently available encapsulated sources; and (4) they are capable of being pulsed, thus permitting new techniques in logging. In the past, both accelerator and encapsulated neutron sources have been used by others in conjunction with scintillation-detector pulse-height analysis. The results have not been too encouraging, due to the interference among different gamma-ray spectral lines and to the fact that the gamma-ray peaks were not too clearly distinguishable above the large and ill-defined background "noise".&apos;.&apos; This paper is a status report on laboratory studies of a technique using a borehole accelerator as a neutron source, which gives an improved scintillation spectrum, thus permitting more accurate chemical analyses of the formations penetrated. The Schlumberger-accelerator neutron source&apos; is presented; the origins of inelastic and of thermal-neutron, capture gamma rays are dis- cussed, and results are given for some laboratory measurements performed in borehole geometry. THE NEUTRON GENERATOR-TUBE ACCELERATOR In the attempt to develop an accelerator neutron source which would have the desirable properties outlined in the "Introduction" and which would operate satisfactorily under borehole logging conditions, a small-diameter, cylindrical, neutron generator tube has been developed. This tube utilizes the principle of accelerating deuterons (heavy hydrogen nuclei) by a high voltage so that they bombard a tritium (heavy, heavy hydrogen) target. The resulting reactions produce large numbers of neutrons of 14 Mev energy. Furthermore, the tube is permanently sealed and, thus, the use of pumping techniques in the sonde is avoided. The tube consists of a pressure control, an ion source in which the deuterons are stripped of their electrons, an accelerating gap down which the deuterons are sped by the high voltage, a secondary electron suppressor and a tritium-loaded target. Obviously, the tube requires auxiliary circuitry in a sonde for the control of the ion source, tube pressure, high voltage and other operating variables. Neutron yields, both continuous and pulsed, have been produced under simulated field conditions in the range between 1 and 10 times those conventionally used in neutron logging applications. For the experiments discussed in this paper, neutron-pulse repetition rates in the range between 500 and 5,000 pulses/sec are adequate. Furthermore, by making suitable adjustments in operating conditions, one can vary the pulse width from a minimum of several microseconds up to dc. As will be seen later, the present application to well logging does not require that one have available pulses of neutrons which are appreciably shorter than the time it takes for fast neutrons to slow down to thermal energy in water. As a consequence, much of our interest has been directed towards the operating characteristics of the tube with pulses longer than about 10 microseconds in duration. Our experience to date shows that tubes can be operated in this manner with reasonably constant, average neutron outputs.