Search Documents

By Douglas R. Cook

The discovery of the gold deposits of the Jerritt Canyon district, with proven recoverable reserves in excess of 67.6 Mg (2.4 million oz) of gold, has contributed greatly to the tremendous resurgence in exploration for disseminated gold deposits in Nevada and throughout the west. The Jerritt Canyon project, including the Bell mine, is a 70130 joint venture between Freeport Gold Co. and FMC Gold Corp., both of which are wholly owned affiliates of the respective parent companies, Freeport-McMoRan Inc. and FMC Corp. The Jerritt Canyon district is located in the center of the Independence Mountains in north-central Elko County, Nevada, approximately 48 km (30 miles) northeast of the Carlin gold mine and 68 km (42 miles) north of Elko. Although the discovery of a commercial gold mine at Jerritt resulted from Freeport's exploration activities, the initial identification of a gold prospect in this area was a consequence of a program by FMC in the search for antimony. Their program was, in part, based on data in the Nevada Bureau of Mines Bulletin 61, "Antimony Deposits in Nevada." Work on the property began in 197 1 with geologic mapping followed by sampling and geochemical analyses. FMC geologists, including Robert Hawkins, Russell Hayden, and Hal Hurst recognized the striking similarity of the area to the geologic environment of Newmont's nearby Carlin gold deposit and soon focused on the gold potential. Increases in the price of gold served to stimulate interest and support for the exploration program. Geochemical samples were collected and analyzed for gold and trace elements usually associated with gold. A strong gold anomaly was found on the North Fork of Jerritt Canyon, which was called the Alchem anomaly. Drill-testing of this anomaly in 1973 revealed significant grades and thicknesses of gold mineralization in the lower portion of the Roberts Mountain formation. This initial discovery and subsequent close-spaced drilling proved the existence of several small pods of low-grade, gold-bearing material which cropped out at their up-dip edges, causing the surface anomaly. The mineralization was very encouraging, but was not, by itself, of economic importance from the standpoint of either grade or tonnage. Freeport Exploration Co. established a district office in Reno in late 1974 with responsibilities for exploration of hard minerals in the Basin and Range Province. Emphasis of the program was directed to the discovery of precious metal deposits. Enfield Bell, as District Manager for this new office, was particularly interested in the Independence Mountains and when the opportunity for a joint venture with FMC became available in 1976, it was aggressively pursued. Enfield Bell and David Stevens evaluated the FMC data and with the support of management formulated a bid in competition with 23 other companies. Freeport was selected by FMC as partner and a joint venture agreement was successfully negotiated. In mid-summer of 1976, Freeport Exploration Co. began an expanded program of detailed mapping and geochemical sampling under the direction of Bell and Stevens that led to new interpretations of the structural and alteration patterns. Hawkins' contribution during this period must be recognized since he not only was one of the original geologists assigned to the antimony and subsequently the gold investigations, but shortly after the start of the joint venture exploration, he was hired by Freeport Exploration Co. as the project geologist for the venture. Hawkins had studied the central Independence Mountains for his thesis and his understanding of the regional geology provided an excellent background for the continued exploration of the gold de- posits. His interpretation of the structure in the vicinity of the Alchem anomaly was of significant help in the Freeport exploration program. Drilling, based on this new under- standing of the geology, revealed the edge of the Marlboro Canyon ore body, which is now being exploited in the Bell mine. Although a classic bullseye geochemical target led to the discovery of the Alchem mineralization, the bulk of the reserves known today in the Marlboro Canyon area lay

Jan 1, 1985

By J. Downie, H. A. Kendall, G. H. F. Gardner

Some cases of the motion of two miscible fluids in uniform linear models are discussed. There is no bulk flow through the models, and the convection currents are caused solely by density gradients. Horizontal, vertical and inclined positions of the models are treated separately. Analytical formulas for the motion of a narrow transition zone between the fluids are obtained and compared with measurements, and the limitations are discussed. Observations of the ultimate stabilizing effect of diffusion on the motion me compared with the theory. It is shown that fluid motion in an inclined model with a constant rate of bulk flow can be directly deduced from the cases discussed, provided the viscosity ratio is small. INTRODUCTION In some reservoirs, convection currents caused by variations in the fluid densities may be significant. For practical purposes it may be desirable either to minimize the effect, particularly in miscible displacement, or to maximize the effect as in some schemes for the production of heavy crude oils by combustion. Experiments by Craig, et al,l have shown the effectiveness of gravity in reducing the efficiency of a miscible displacement when the mixed zone between the displacing and displaced fluids is narrow compared with the height of the system. The presence of a board transition zone from one fluid to the other has been shown by Perkins, et al,2 to nullify considerably the influence of a difference in density. Indeed, the theoretical discussion given by Perrine3 has shown that when the transition zone exceeds a certain critical length the efficiency approaches 100 per cent. Many additional results 495 have been published on miscible and immiscible displacements which show the importance of density difference and also mobility ratio. The aim of the present paper is to discuss some cases of gravity segregation of miscible fluids in linear models such as are often used in the laboratory to evaluate recovery processes, and to supply additional experimental evidence in support of the conclusions. An attempt is made to calculate simply the magnitude of the fluid motion caused by density pdients and mobility ratios, and to quantify the modifications in the fluid motion produced by the combined effect of molecular and convective dispersion. However, it should be pointed out that the uniform permeability of the models and the use of only a single pair of fluids (whereas several pairs of fluids may be employed in a recovery scheme) severely restricts direct conclusions about natural reservoirs. For conciseness, the motion generated by density gradients is emphasized for the case of no bulk flow through the models. This is not a drastic limitation because, as shown in Appendix A, a fluid motion with a constant bulk flow through any linear model is equivalent to a fluid motion with no bulk flow in the same model inclined at a different angle to the horizontal, provided only that the density is a linear function of the viscosity of the fluid mixture. HORIZONTAL MODEL In this case the model is assumed to have a rectangular cross-section with a horizontal breadth b, vertical height and a great length L. Throughout.the paper it will be assumed that x-axis points along the length, the y-axis along the width and the z-axis along the height. Thus, in the present case the x, y plane is horizontal. Initially, the transition zone between the fluids is assumed to be thin and parallel to the y, z plane. An example of this situation in a practical problem arises in a scheme for using air for cushion gas in the storage of fuel gas in aquifers. 6 With the passage of time the denser fluid sinks and spreads along the bottom of the model while the lighter fluid rises. The interface extends from the top plane of the model to the bottom. Experiments have shown that for practical purposes this interface may be treated as a plane surface at all times. The surface is significantly curved, however, for viscosity ratios greater than about 10. Other complications arise with large viscosity ratios because of the nonlinear dependence of the viscosity on the composition of the mixture, so that the simple results given here are restricted to fairly low viscosity ratios.

By H. Macpherson

Durhm has a well earned reputation for supplying some of the finest coking caals in the world. The caals, in general, vary in rank from 301 to 501/2. Durham has traditionally produced foundry coke for the major proportion of the foundries in Great Britah. Durham coals can be described as clean, soft coals, which yielded, with the old hand methods of coal getting, low ash small coal because the extraneous shale was normally harder than the coal and occurred in larger pieces. Under these conditions, with a plentiful supply of cheap labor, it used to be sufficient, at most collieries, to hand clean the large sizes of coal which could then be remixed with the untreated small coal to produce carbonization coals, ready for the coke ovens, at under 5 pct ash. With the introduction of mechanical methods of coal mining, the coal gradually required more cleaning. The first method adopted to resolve this problem was the introduction of pneumatic dry cleaners for the small coal. Although such machines had little effect on the fine coal (say below 1/8 in.), they could clean the intermediate sizes of coal. This, coupled with hand cleaning the larger sizes above 1-1/2or 2 in., resulted in a combined run-of-mine mixture below 6 pct ash, capable of maintaining the quality and reputation of the cokes produced. In more recent years, the intensification of mechanization and power loading, coupled with gradual exhaustion of the cleaner seams, has created the need for a more complete method of coal cleaning. This particularly applies in the fine sizes (say below 1/50 in.) which normally vary, under present day conditions, between 15 and 35 pct ash and are much too dirty to be included in the raw state in a carbonization mixture. This pronounced change has been accelerated because legislation controlling the dust conditions of mine airs for the prevention of pneumoconiosis has resulted in tk~e extensive use of water underground and a consequent increase in moisture content of the run-of-milie output. The presence of damp fine coal decreast the efficiency of prescreening and dry cleaners, so that this type of preparation for low ash coking coals is decreasing, although it is still used satisfactorily for industrial coals in the medium ash range. Table I shows the gradual increase in mechanization, the reduction in manpower, the increased use of explosives per ton of coal extraction, and the increase in the proportion of coal cleaned by mechanical means in Great Britain. Although similar figures are not available for Durham Div. until after the date of nationalization of the coal industry, it is probable that the increase in mechanical cleaning, particularly by dry cleaners, was more marked in the Durham collieries than elsewhere in the country. As dry clealiers were replaced by coal washeries in the Gritish ccal industry, no special attempts were made to recover the slurry, with the result that large outflows of dirty water were allowed, deposits of slurry came in to lagoons and neighboring streams, and a proportion of fine material was lost from the coking coal. This position, coupled with the higher moisture of the washed coking coal, resulted in adverse effects on coke oven throughputs and coke quality. It is now realized that the natural coal fines are an essential ingredient of coking coals in obtaining the correct coke structure in metallurgical cokes. This, together with economic pressure, led to the introduction of flocculation and filtration plants for the recovery of slurries, and later, when the ash contelits of the filter cakes were too high, to the introduction of froth flotation equipment. After this position had been reached, the tailings from the froth flotation pIants were, in many cases, still allowed to constitute an undesirable effluent. Recent legislation on river pollution has changed this picture; it is now necessary to provide a circuit which is completely closed so far as solids are concerned. The gradual increase in the coal cleaned by wet methods and froth flotation in Durham Div, is shown in Table 11. It is now an accepted feature of new Washeries that. froth flotation should be an integral part of the washing process from the initial installation of the plant.

Jan 1, 1962

By R. J. Charles

SEARCH for a consistent theory to explain the relationship between energy input and size reduction in a comminution process has accumulated, over the years, an enormous amount of plant and laboratory data. Although some correlation of these data has been possible for purposes of engineering design and for the advancement of research in fracture, there is still great need of a means of predicting behaviour of a solid when it is reduced in size by mechanical forces. The best known hypotheses proposed to describe the energy-size reduction relationships in crushing and grinding stem from a common origin. The present article analyzes problems of comminution in the light of the precepts of this origin. Its object is to reconcile points of difference between these well known hypotheses and to present relationships more widely applicable to comminution studies. Theoretical Considerations: Most existing relationships between energy and size reduction of a brittle solid stem from a single, simple, empirical proposition.&apos; Although this proposition can be demonstrated by observation and experiment, no theoretical derivation is yet possible. Mathematically, the proposition may be stated as follows: dE = -Cdx/xn [1] where dE = infinitesimal energy change, C = a constant, dx = infinitesimal size change, x = object size, and n = a constant. Eq. 1 states that the energy required to make a small change in the size of an object is proportional to the size change and inversely proportional to the object size to some power n. No stipulations are placed on the exponent n in either magnitude or sign. In 1867 Rittinger2 postulated that the energy required for size reduction of a solid would be proportional to the new surface area created during the size reduction. As far as can be determined there is as yet no physical basis for Rittinger&apos;s hypothesis. Rittinger&apos;s hypothesis can be stated mathematically as follows: E, = K(oa-a-0 . [2] Er = energy input per unit volume, K = a constant, <ti = initial specific surface, and o2 = final specific surface. In the size reduction of particles of size x, to particles of another smaller size, x2, Eq. 2 becomes the well known relation: ET = K&apos; {l/x2-l/xx) [3] where K&apos; is a constant. Eq. 3 may be arrived at from the proposition given in Eq. 1 by integrating and by assigning a value of 2 to the exponent n. J dE = J - C dx/x2 E = Kt (1x - 1x) where K&apos; = C. In 1885 Kick3 proposed the theory that equivalent amounts of energy should result in equivalent geometrical changes in the sizes of the pieces of a solid. For example, if one unit of energy reduced a number of equal-sized particles to particles of one half the size, then the same amount of energy applied to the particles resulting from the first test should result again in a size reduction of one half or a final size one quarter the original size. The Kick concept may be expressed as follows: Ek = K" log x1/x2 [41 K" = a constant and E, = energy per unit volume. The expression for Kick&apos;s law may be arrived at by again integrating Eq. 1 and in this case assigning a value of 1 to the exponent n. dE= J - C dx/x Eh = - C In {x/x2) = K" log (x,/x,) where K" = 2.3 C. Application of Kick&apos;s and Rittinger&apos;s laws to comminution has met with varied success. Gross and Zimmerley4 and Piret5 have shown that Rittinger&apos;s equation applies under certain conditions of experimentation. Walker and Shaw6 express the belief that in metal turning and shaping and in grinding of both metals and minerals the production of very fine particles (less than lP) follows Kick&apos;s hypothesis, whereas Rittinger&apos;s concept is valid for the size reduction of coarse particles. For the practical case of crushing and grinding, however, neither of the above hypotheses has received general acceptance. Bond&apos; has lately proposed that since neither Kick&apos;s nor Rittinger&apos;s hypotheses seem correct for plant design work, an energy-size reduction relationship somewhere between the two would be more applicable. The fundamental statement of Bond&apos;s work

Jan 1, 1958

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.&apos;-&apos; This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,&apos; by the copper-decoration technique,&apos; by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18&apos;19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965

By David Cornell, D. L. Katz

Procedures for computing turbulent flow of gas in steady state near the well bore and a graphical method for predicting unsteady state laminar flow at distances from the well have been combined to compute pressure gradients in gas reservoirs. Methods are discussed for predicting single and multiple transients at constant flow rate in an infinite reservoir, predicting constant How rate. in a finite reservoir, reproducing and interpreting back pressure test data, and prediction of the behavior of a closed-in gas well. An example of the graphical method is given for a single transient and the results are compared to a published analytical solution. A typical calculation of the pressure gradient in a reservoir and the production of gas is made .starting with data from a hack pressure test. INTRODUCTION The calculation of pressure gradients throughouse a ga-reservoir at any point in its production history is a complex problem involving turbulent flow near the well bore and unsteady state flow of the gas from the reservoir. The problem is complicated further by the variety of boundary conditions that may be imposed upon the flow. Such boundary conditions include finite or infinite reservoirs. constant or variable rates of production, constant or varying bottom hole pressures, complex initial pressure distributions throughout the reservoir, and pressure maintenance through cycling. In addition to these problems there are the practical difficulties associated with natural gas reservoir analysis These might include: (1) variation. in the permeability and porosity throughout the formation. (2) variations in the thickness of the formation, (3) communication of the producing formation with other producing zones. (4) radial variations in permeability due to influx of drilling fluid. acidizing. or the buildup of liquid in the formation around the well, (5) partial penetration of the producing zone. (6) water flood, and many others. These problems will be considered eventually. In the mean- time, it is necessary to present methods of handling the case of radial flow through a homogeneous, regular, producing stratum to a single well uncomplicated by other factors. The idealized case of steady state, radial flow from a natural gas reservoir was studied by Elenbaas and Katz5 and by Mac-Koberts.&apos; An analysis of the unsteady flow of gases through porous media has been made by Aronofsky and Jenkins&apos; for the one dimensional laminar case with the boundary conditions of constant downstream pressure and uniform initial pressure. Solutions for the partial differential equation for unsteady state radial flow of liquids through porous media have been given by Van Everdingen and Hurst" for the constant bottom hole pressure and constant production rate cases for laminar flow in a reservoir initially at a constant pressure. The analogous heat transfer equation has been treated by Perry and Berggren9 for the case of quenching a cylindrical hole in an infinite medium to a constant temperature. The back pressure curve, which involves the variation of the bottom hole pressure as it is determined by the behavior of the reservoir as a whole. has been studied by Rawlins and Schellhardt,10 Binck-lev,&apos; Baumel and Breitung,&apos; and others. No complete. adequate treatment has been given for the unsteady state, radial flow of gases into a cylindrical hole from a porous medium with or without the presence of turbulent flow and for any set of boundary conditions. If one relies only on analytical solutions of the basic equations, a new solution must be obtained for each new boundary condition. Furthermore, the complexity of the mathematical expressions for boundary conditions other than the very simple cases limits the use of analytical solutions. Graphical methods exist, however. that are general in nature, accurate, and readily employed. The analysis of steady and unsteady, laminar and turbulent, radial flow for various boundary conditions with application to specific natural gas well problems by means of graphical procedures forms the content of this paper. STEADY STATE RADIAL FLOW EQUATION FOR LAMINAR AND TURBULENT FLOW A steady state radial flow equation for laminar and turbulent flow through unconsolidated sands has been given by Muskat as discussion of the work by Elenbaas and Katz.5 This equation is based on the properties of unconsolidated

Jan 1, 1953

By N. K. Chen, R. B. Pond

IN the study of slip band* formation, there have been many examples to show that they do not always appear as lines traversing the entire crystal, but as segments whose ends seem to vanish in their path through the crystal. This characteristic appearance of slip bands has been witnessed under the optical microscope at various magnifications&apos;-&apos; and also under the electron microscope.&apos; A typical example of this behavior seen with the optical microscope is shown in Fig. 1. However, the slip band studies were generally conducted on polished surfaces of single or poly-crystalline metals which had been previously deformed; i.e., the load was generally released so that the observation could be made. Any picture of slip bands so obtained can represent the surface phenomenon only in a static state of the strained material. The conditions prior to their formation cannot be definitely and clearly assigned. Thus, while a segmented slip band may suggest that slip is a growth process as supposed by the theory of the nucleation of slip,V he usual appearance of suddenly and fully developed slip bands around the crystal has generally been considered as a consequence of uniform shear of the entire slip plane akin to a cataclysmic process. Little clear-cut information is available with regard to the speed at which a slip band forms, its direction of motion, the geometry of its position with regard to its neighbors, and its dependence on orientation. A description is given in this paper of experimental apparatus by which the progressive formation of slip bands can be recorded while the specimen is undergoing deformation. Qualitative and quantitative data on the dynamic formation of slip bands will be presented with special interest concerning the propagation of slip bands, the spacing of slip bands, and their relations to strain hardening. Views on the formation of slip bands are discussed and a mechanism of the unit process involved in the formation of a slip band is proposed. Preparation of Specimens Single-crystal specimens of high purity aluminum (99.997 pct), 1/8 in. square in cross-section and 1% in. long in gage length, were made by the method of gradual solidification from the liquid state. Since no machining work could be introduced in preparation of crystals of such small size, a special mold was designed for casting them to final shape. The mold consisted of two, separate, high purity graphite blocks. Generally, 20 molds were packed together in one container so that 20 specimens could be obtained by one casting operation. This was desirable since it was possible by this method to obtain groups of crystals with similar orientations. The as-cast crystals were carefully clipped from the gate, etched, and homogenized for 24 hr at 600°C. They were then very gently polished using a 4/0 paper, re-etched, and finally electrolytically polished after the method previously described by Chen and Mathewson.6 The crystallographic orientations were determined using a back-reflection, Laue method. Tensile Testing and Photographic Method The tensile testing equipment for these tests was composed of a specially designed microtensile machine, microload cell and microclip gage with necessary appurtenances. The members of the microtensile machine consisted of three parts, as shown in Fig. 2. The chassis is equipped with an oil cylinder, A, and piston, the piston being part of the movable cross-head, B. Pressure in the oil cylinder is controlled and regulated by an external pneumatic-hydraulic cell, C, which is connected to the cylinder by a Vs in. high pressure copper tube. This cell is half filled with hydraulic oil and has a needle valve, D, on the oil exit side as well as a needle valve, E, on the gas inlet side. A quick-acting valve, F, as well as a pressure gage is provided for the gas side. The oil exits into the load piston on the microtensile machine. By connecting a tank of inert gas to the gas inlet, regulated pressures were provided over the oil so that the oil would leave the cell at a rate determined by the setting of the exit needle valve, the gas pressure, and the pressure of the oil in the load piston of the microtensile machine. With this pneumatic-hydraulic appurtenance it was possible to

Jan 1, 1953

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,&apos; and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,&apos; whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham&apos;s work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy&apos; found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By P. S. Kotva

Dislocation substructures in superalloy matrices of varyzng co)npositions have been studied. In general, it has been found that the alloys can be classified into &apos;&apos;high", &apos;&apos;medium", and "low" stacking fault energy classes based on the type of dislocation substructure observed in the matrix and that the substructure can be correlated to the stacking fault energy. The effect of different types of dislocation substructure and dislocation reactions on the intragranulur precipitation of carbide phases has been studied. In a Ni-Cv-Mo-Fe matrix, precipitation of MC carbides in association with stacking faults has been observed. In most superalloys, solid-solution strengthening and precipitation hardening are the chief mechanisms employed to achieve strength. The latter contribution to strength is usually achieved by the precipitation of / in certain wrought alloys. Insufficient attention has been given to the problem of obtaining strength in su-peralloys by controlling precipitation of carbides on imperfections within the matrix. The present work was undertaken to investigate the dislocation substructure in various superalloy matrices, to study the effect of such substructure on subsequent precipitation of carbides in the matrix, and to investigate whether certain modes of precipitation of carbide phases found in austenitic stainless steels2"4&apos;6 would occur in nickel-base alloy matrices with dislocation substructures of the same type as those found in austenitic steels. 1) EXPERIMENTAL TECHNIQUES Five-pound heats of the various alloy compositions reported here were vacuum-cast. The ingots were given light deformation by rolling to break up the as-cast structure and then homogenized for 24 hr. HASTELLOY alloy X (nominal composition: Ni-2OCr-17Fe-8Mo-0.05C) was homogenized at 2150°F and In-cone1 625 (nominal composition: Ni-20Cr-5Fe-8Mo-3.5Cb-0.05C) was homogenized at 2280°F. Fabrication of 0.004-in. sheet was achieved by cold rolling with intermediate annealing treatments being carried out at the same temperature as those used for homogeniza-tion. Each solution anneal was followed by quenching. The aim of this procedure was to redissolve as much of the primary carbide phase as possible. Samples of the 0.004-in. sheet were cut and encapsulated in quartz capsules and then heat-treated in the tube furnaces. Thin foils were prepared using an ethanol-10 pct perchloric acid bath at 32°F and at a voltage of 22 v. A "window" technique was employed. Observations were made on a JEM-7 electron microscope operating at 100 kv. 2) EXPERIMENTAL RESULTS a) Types of Dislocation Substructure. Fig. 1 shows a schematic correlation between stacking fault energy, SFE, and the type of dislocation substructure observed in various matrices of nickel- and cobalt-base alloys. A precise quantitative determination of stacking fault energy is not implied in the figure but the correlation between stacking fault energy and the type of dislocation substructure obtained allows alloys to be divided into three classes in analogy with the classification employed by Swann and ~uttin~&apos; for binary alloys of copper. Class I alloys are associated with a "high" SFE and show a cellular substructure of dislocations as typified by the micrograph of a thin foil of pure nickel deformed 4 pct at room temperature in Fig. 2. With decreasing SFE the tendency toward cell formation is lessened and dislocations tend to be arranged in coplanar groupings. Examples of this class of alloys with "medium" SFE are provided by the mi-crostructure of solution-heat-treated, quenched, and deformed thin foils of HASTELLOY alloy X, "Waspaloy" (prior to any aging), and Inconel 625. Fig. 3 shows a thin-foil micrograph of an alloy of Inconel 625 composition, solution-heat-treated, quenched, and deformed 5 pct at room temperatures. No evidence of any cell structure can be obtained in materials of "medium" stacking fault energy, Fig. 3, even after severe deformation. The stacking fault energy of the alloy shown in Fig. 3 is, however, not low enough to make the dissociation of dislocations visually obvious. As stacking fault energy decreases further, with successive addition of solute in the matrix, there is an increased tendency toward dissociation of dislocations and cross slip becomes progressively more difficult. Eventually, when the stacking fault energy is "low" enough, complete dissociation of dislocations is seen to occur as shown in Figs.

Jan 1, 1969

By Jr. Ensign C. O., J. W. Trammell

The two principal methods of room-and-pillar mining practiced at White Pine make it important to predict variations in the thickness and rock types of a stratum called the upper sandstone. In full column mining, the nearly barren upper sandstone occurs between two ore horizons (called upper shale and parting shale, respectively), and is mined as a part of the ore column. In general, full column mining is not practiced where excessive upper sandstone thickness causes full column ore grade to be substantially lower than parting shale ore. In parting shale mining, the upper sandstone forms the mine roof. Difficulty in predicting upper sandstone character arose because the extent and directions of its variations were not apparent in the property&apos;s diamond drilling, in which holes are spaced on 1000-ft centers. A study of sedimentary features, undertaken to improve the predictability of trends in the upper sandstone, led to an interpretation of the sedimentary environment in which the sandstone was deposited. Ripple marks, mud cracks, and cross-bedding, as well as other, less well known features, such as channel casts, flute casts, and current crescent casts, were mapped or recorded. These data, coupled with the knowledge of regional facies changes gained from studying drill core, show that the upper sandstone was deposited by a series of streams flowing northeastward over the underlying parting shale. Deposition of the lowermost bed of the upper sandstone, near the ancient shoreline, was locally preceded by erosion of the parting shale, and the greatest thicknesses of sandstone are found in channels scoured out of the parting shale. Awareness of the rather strong linear trends in the upper sandstone makes it possible to project continuous areas of thick upper sandstone through apparently isolated "highs" in the upper sandstone thickness contour map, which is based on drill-hole information. Since local exceptions to general stratigraphic trends exist, a method was also needed for esti- mating, in detail, the thickness and degree of shali-ness of upper sandstone forming the roof in active parting shale mining areas. Because locally the parting shale was thinned by erosion during the deposition of upper sandstone, parting shale thickness is inversely proportional to upper sandstone thickness. Utilizing information taken from short drill holes into the roof, curves were constructed for the correlation of parting shale thickness (measurable in the mine) with the upper sandstone total thickness, as well as the thickness of its basal member. The White Pine mine is situated in Ontonagon County, approximately 6 miles south of Lake Superior, in the Upper Peninsula of Michigan (Fig. 1). The orebody mined by White Pine Copper Co. occurs in the lowermost 20 to 25 ft of the Nonesuch formation, a series of middle- to upper-Keweenawan shales, siltstones, and sandstones. This paper discusses the solution of problems in ore grade control and mine planning arising from the presence of an essentially barren sandstone stratum within the orebody. THE OREBODY AND MINING TYPES A brief description of the orebody and mining methods is necessary to show how the upper sandstone affects mine planning and grade control. In the mine, the cupriferous zone of the Nonesuch shale is divided into three major portions, as shown in Fig. 2. Lying conformably on top of the Copper Harbor formation (or "lower sandstone") is the lower part of the orebody, the parting shale. The parting shale is overlain by the upper sandstone. On top of the upper sandstone, the basal portion (8 ft) of the upper shale is quite similar to the parting shale. Both the upper shale and parting shale are divided into a number of smaller stratigraphic units, each having a characteristic copper content, as shown by the histogram of Fig. 2. Other authors1&apos;3 have dealt in detail with the stratigraphy and mineralogy of the orebody. However, in this article, we are concerned with the major subdivisions only, and it will suffice to note the low copper content of the upper sandstone, shown in Fig. 2. At present, two types of room-and-pillar openings are created in the orebody. In one type, called parting

Jan 1, 1964

By E. J. Dulis, R. M. Fisher, K. G. Carroll

IT is well known that ferritic steels containing more than 15 pct Cr when subjected to temperatures in the range of 700" to 1000°F exhibit increasing hardness and decreasing ductility. The phenomenon has been widely termed the "885 °F embrittlement," after the temperature of most marked effect.&apos;.&apos; In view of the excellent review articles available in the literature3-6 only a brief account of experimentally established facts need be given here. The extent of changes in physical characteristics during embrittlement depends on chromium concentration and time at temperature, higher alloy content and longer time both promoting more rapid and extensive changes. In a 27 pct Cr steel, changes in impact strength and in angle of fracture in bending can be detected after only a 1 hr exposure at 885°F; after 50 hr this steel becomes quite brittle. Hardness increases slowly with time during thousands of hours exposure and may attain a maximum hardness number twice as large as that of the unexposed steel. Microstructural changes accompanying embrittlement have been described as an initial widening of grain boundaries followed by eventual darkening of ferrite grains. Embrittled steels etch more readily, e.g., the weight loss of a 27 pct Cr steel in acid solution may occur at a rate one hundred fold greater following exposure at 885 OF. Marked changes which accompany embrittlement have been observed in electrical resistivity, specific gravity, and magnetic coercive force. Changes in physical properties may be readily removed by heating at temperatures above the embrittling range, such as a treatment at 1100°F for 1 hr. It has frequently been noted that the 885 °F embrittlement suggests precipitation on a submicro-scopic scale of a chromium-rich constituent, the nature of which has not been revealed by X-ray diffraction. Progressive broadening of the body-centered cubic diffraction lines during embrittlement has been observed," and recent observations by Lena and Hawkes&apos; upon single crystals have shown early asterism in X-ray photographs, disappearing within an hour at 900 °F. Many workers have ascribed8-13 the phenomenon to a precipitation of a phase (FeCr), which is known to cause embrittling effects at temperatures much higher than 885°F. Two general observations, however. suggest that a precipitation cannot be responsible for the 885°F phenomenon: 1—prior cold work greatly enhances a formation, whereas it scarcely affects the 885 °F embrittlement, and 2—the presence of an alloying element such as nickel or manganese may have an effect on the 885 °F embrittlement which is opposed to its effect upon a formation. The slight enhancement of a formation and 885°F embrittlement observed in the presence of elements with strong carbide and nitride forming tendencies&apos; is probably a consequence of lessened chromium depletion of the matrix. The bar graph in Fig. 1 shows a typical example, taken from two 27 pct Cr steels used in this work, of the hardness after exposure for 10,000 hr at 900°, 1050°, and 1200°F. Steel A (0.03 pct C, 3.13 pct Mn) showed marked hardening at 900" and 1200°F, whereas steel B (0.12 pct C, 0.63 pct Mn) exhibited only the 900°F hardening. The cr phase was found in steel A at the higher temperatures but not in steel B. Presumably a formation is enhanced by the low-carbon and high-manganese concentrations in A," Thus there are two distinctly different hardening phenomena present which cannot both be ascribed to v precipitation without invoking a transition phase possessing remarkable properties. Materials A number of chromium steels exposed for long periods (5000 to 34,000 hr) at 900°F, as well as unexposed samples of one of the steels, were available for this investigation. Table I gives the chemical compositions and aging treatments of these steels. In addition to these steels exposed in the elevated temperature test furnaces of the National Tube Division, a number of high-chromium steels were heated for short periods in small laboratory air furnaces and lead baths. Supplementing these commercial steels, a sample of high-purity (0.018 pct C, 0.002 pct N) 28 pct Cr iron, exposed 1000 hr at 887°F. was furnished by the Union Carbide and Carbon Corp. In addition, an alloy of iron and chromium of high purity containing 46 pct Cr was used. This

Jan 1, 1954

By D. R. Hay, E. Scala

STUDIES of structure-sensitive properties, especially mechanical behavior, have shown that grain and subgrain structure play an important role. The mechanical properties of tungsten, in particular, are sensitive to the nature of the intergranular structure. Substructure and dislocation networks in single-crystal and polycrystalline tungsten have been studied by Nakayama et al.&apos; Various orders of substructure were observed ranging from a microscopic first order (grain diameter: 2 to 8 mm) to a microscopic second order (grain diameter: 50 to 300 p), and, within the latter, dislocation networks forming an even smaller order of substructure. In their single crystals, grown by arc fusion, the degree of misorientation in each order was small: 16&apos;3OU, -11, and -10" for the first-, second-, and third-order substructure, respectively. To study the properties of polycrystalline tungsten, powder metallurgy tungsten is generally used. However, in a mechanical property investigation, the zone-melted or arc-fusion crystals are more desirable than the powder metallurgy product due to their higher purity and absence of porosity and other defects inherent in consolidation by powder metallurgy. Grain boundaries can also be produced in melted stock by working and recrystallizing. However, material with subgrain mis orientations of the order of several degrees (high-angle substructure) has not been reported previously and is the subject of this communication. Crystals were grown by electron-beam, floating-zone melting. The starting material, Sylvania Pure-tung welding rod, was given one zone pass at a traversal rate of -2 mm per min. Through control of the zone temperature, it was possible to influence the degree of crystal perfection. By maintaining the zone at a high degree of superheat, high-perfection crystals could be grown. However, at temperatures only slightly above the melting point, the zone-melted crystals contained a high-angle substructure. A sensitive control of the zone temperature was not possible due to the difficulty of estimating the temperature of the zone and of providing a constant supply of power to the sample. Therefore, an empirical method, using the shape of the molten zone as a criterion, was adopted as an indication of temperature. At high degrees of superheat, the surface tension of the molten zone decreases and a neck forms at the top of the zone, whereas at low zone temperatures the diameter of the zone remains reasonably uniform. Although it was not possible to obtain a continuous variation of misfit angle, the conditions could be directed toward the growth of either high- or low-angle substructure by maintaining only a slight neck in the zone (sufficient to establish that it was molten) or a well-necked zone, respectively. Mass spectrographic analyses of both types of material revealed no significant differences in the concentrations of their impurities. The degree of misorientation at high angles was obtained by measuring the angular spread of spots corresponding to a single reflection on a Laue back-reflection photograph. Fig. 1 shows a typical Laue back-reflection photograph of a crystal with a 3-deg spread. By measuring the angular deviation of the spots corresponding to a single reflection from the mean center of the spots around which constant angular deviation contours were drawn, an average angular spread of misfit could be calculated. The angular average was weighted by the number of spots observed in each angular interval. At angles greater than 5 to 6 deg the spots from different reflections begin to overlap, and cannot be associated with a particular reflection. Laue back-reflection photographs taken at different locations on samples .with approximately 3-deg spreads showed only a small difference in angular misorientation, less than 8&apos; of arc, within individual specimens. The microstructure was examined using Berg-Barrett X-ray extinction contrast microscopy. Berg-Barrett photographs taken directly on the as-grown surface, Fig. 2, show an essentially equiaxed subgrain structure of -0.1 mm in average grain diameter in both high- and low-angle crystals. Fig. 2(a) is a photograph of a sample with a low misfit angle and Fig.

Jan 1, 1968

By J. C. Wilhoit, J. B. Cheatham

Although an oil well is a long cylindrical hole with an irregular bottom, it appears likely that the nature of the stress concentration at the bottom of the hole can be ascertained from an analysis of the stresses around a short cylindrical cavity with rounded comers and smooth bottom. Such a cavity is studied primarily because it leads more readily to a solution to the problem by the use of stress functions. In this paper the stress distribution around a short cylindrical cavity subjected to bit loading, overburden and drilling-fluid pressures is determined by means of an analytical solution which approximately satisfies the boundary conditions of the problem. From this solution the stresses at the corner of the hole are calculated to be about 35 per cent lower than comparable results obtained by photoelastic and relaxation analyses. This difference is apparently due to the large radius of curvature at the corner of the cavity in the present analysis. Since good agreement is obtained between the results of this analysis and the stresses calculated for a similar loading on a semi-infinite elastic solid, it is concluded that the bit action in the region near the center of the hole is not appreciably affected by the presence of the sides of the hole. INTRODUCTION Much has been written concerning drilling "under down-hole conditions" and pertaining to the stress distribution in the rock at the bottom of an oil well.1-5 For example, it is known that identical rocks can be drilled more rapidly at the surface than under subsurface conditions of pressure and stress.6 Information on the behavior of rocks under loading can be obtained from triaxial test data.7-9 From such tests it is found that rocks exhibit brittle failure when the confining pressure and pore pressure are equal, but the mode of failure may change to ductile as the difference between the confining pressure and the pore pressure is increased. Brittle failure implies that there is very little permanent deformation before fracture, whereas ductile failure indicates that permanent deformation takes place before fracture. Some rocks are ductile at differential pressures of 5,000 psi , but other rocks are brittle even at differential pressures of more than 50,000 psi. Cuttings embedded in mud at the bottom of the hole may act as a plastic mass which the bit teeth must penetrate in order to attack the virgin rock below. 10 During drilling, the mud pressure acts as the confing pressure, and in many cases the difference between the mud pressure and the formation pore pressure IS sufficiently low so that the rock most likely falls in a brittle manner. Very little penetratiori by the bit teeth may be required for brittle failure of the rock. For these brittle materials, the elastic stress distribution is of practical interest in determicing the possible effects of a given loading on failure. The penetration of bit teeth into ductile or plastic rock has been analyzed previously ll,12 and will not be considered further in the present work. During actual drilling, many teeth act at various points ovel an irregular hole bottom. In the present analysis a solution is obtained for an idealized problem of determining the elastic stress distribution caused by only one tooth acting alone at the center of a smooth hole bottom. It obviously is not proposed that any driller should put a special one-tooth bit on bottom, but it is hoped that extensions of the simpler problems can eventually lead to a better understanding of more complex actual drilling phenomena. To obtain a solution by the use of stress functions, a short cylindrical cavity with rounded corners and smooth bottom is studied. The solution to this problem should give an insight into the nature of the stress concentration at the bottom of an oil well which is in reality a long cylindrical hole with an irregularr bottom. After selection of the proper curvilinear co-ordinate system, the stress functions are expressed as series of Legendre polynomials. The coefficient of each term in the series is then determined to satisfy the boundary conditions at a finite number of discrete points on the boundary of the cavity with least square error. Results are compared with bottom-hole stresses obtained by photoelastic and relaxation analyses.

By Appendix by A. S. Goldoni, R. E. Tate, E. M. Cramer

The diffision coefficient for self-diffision of plutonium in the temperature range 350" to 440°C has been measured by using puZ3 as the tracer isotope. Autoradiopaphic techniques were used to inzlestigate the possibility of grain boundary diffusion, hut only evidence for volume diffusion was found. The least-squares fit of the data gives the .following equation for the diffision coefficient: The computer least-squares technique for fitting the nonlinear equations is outlined. DETERMINATION of the self-diffusion coefficient of the fcc 6 phase of plutonium is in principle a straightforward experimental task. However, the chemical reactivity, the intense @ activity, and the toxicity of plutonium put limitations on the experimental techniques. The technique selected included roll bonding for preparation of the diffusion couples and pulse-height analysis of the @-particle activity to determine the distribution of the PU tracer in the diffusion couples. EXPERIMENTAL PROCEDURE Couple Preparation. Cylinders about 0.5 in. in diam were cast from two special stocks of plutonium, one of which had been enriched in puZ3&apos;, as shown in the isotopic analyses listed in Table I. For each roll-bonded composite sheet, a cylinder 0.437 in. in diam and 0.190 in. thick was turned from each kind of plutonium on a lathe in a 98 pct He atmosphere. The two freshly machined cylinders were positioned face to face in a tube of commercially pure aluminum which had been sealed at one end by welding and the assembly was evacuated on a vacuum manifold overnight. The elapsed time between machining the faces of the plutonium cylinders and evacuating the loaded tube was about 15 min. After overnight evacuation of the assembly the indicated vacuum was 1 X 10"5 torr or better. The aluminum tube was then warmed and pinched off with a cold-welding tool. The pinched-off weld was also fusion-welded as an additional precaution against leakage of air into the evacuated assembly. The assembly was immediately heated for 30 min in a 250°C furnace and reduced in thickness by being passed through a rolling mill with rolls heated to 200°C. The rolling schedule (four passes of 100 mils each with a 10-min reheat after two passes) reduced the thickness of the assembly to 100 mils. The rolled assembly was allowed to cool normally in air. The rolled assembly was sheared at the edges and the aluminum peeled from the composite plutonium sheet. The elliptical sheet was about 0.060 in. thick and usually three 0.383-in.-diam disks could be punched from its central portion. The sheet was heated on a hot plate to the ductile low 0 range (140°C as measured by temperature-indicating pellets) before each disk was quickly punched. The quality of the bond in the disks was evaluated by metallographic examination of the scrap sheet adjoining the hole left by the punch. Only well-bonded specimens without oxide in the interface (as indicated by metallography) were considered satisfactory for further use. More than half of the specimens so examined contained sufficient oxide in the interface to be rejected. Diffusion Anneal. Each disk to be diffusion-annealed was wrapped in 1-mil-thick tantalum foil and sealed within a Pyrex capsule evacuated to 1 x 10~5 torr or better. This capsule was then sealed within another Pyrex capsule at a similar pressure. The diffusion anneals were carried out at temperatures between 350" and 440°C in Marshall furnaces adjusted to have a temperature gradient of not more than *1/2"C over a 5-in. length. This gradient was then further smoothed by using a nickel tube as a liner in the furnace. The liner was divided into three longitudinal cavities by a septum of nickel sheet to which two calibrated Chromel-Alumel thermocouples were attached. One thermocouple was used for controlling the furnace temperature by means of a Brown Pyrovane controller equipped with a Capaciline anticipation circuit; the second thermocouple was monitored twice daily with a Leeds and Northrup K-2 precision potentiometer.

Jan 1, 1964

By P. Martinez, A. F. Hoyte, F. E. Senftle

The possibility of applying a neutron activation technique for silver exploration is considered. A mobile positive-ion accelerator type neutron source is used to irradiate a small area of rock or soil in situ. By using a short period of irradiation and gamma ray spectral analysis, a technique is shown for silver exploration. Two different mobile units are described. Laboratory and preliminary field tests both indicate that a sensitivity of less than 1 oz of silver per ton of ore can be achieved. The increasing consumption of silver for industrial uses and also for coinage has caused a serious shortage of silver in this country. The silver shortage has been reviewed and analyzed by kiilsgaard1 who concludes that, "The best hope for meeting future demands for silver is through accelerated exploration for precious ores." As almost all the exposed "bonanza" type silver deposits evidently have been found, it is urgent that some sensitive geophysical technique be found to detect large, extended, but generally low-grade, secondary ores, as well as hidden vein deposits. Silver is easily made radioactive by exposure to slow neutrons; hence a neutron activation method appears promising for locating silver deposits. The principles of mineral beneficiation using neutron activation techniques were discussed some years ago.2-4 Using the same approach, a preliminary description5 has been published of neutron activation as a mineral exploration tool. An exploration technique is described in which silver is made radioactive in situ and detected with a gamma radiation counter. The technique is similar to the well-known method used for uranium exploration. THEORETICAL CONSIDERATIONS Elemental silver consists of two isotopes, Ag107 and Ag109, having naturally occurring isotopic abundances of 51.4% and 48.6%, respectively. For short periods of irradiation of silver by thermal neutrons, the long-lived 250 day, half-life isotope, Ag110m, is not produced in significant quantities. However, significant quantities of 2.3 min half-life Ag108 and 24.5 sec half-life Agl10 are formed by the following reactions. Ag108 and Agl10 emit a 0.44 Mev (million electron volts) and a 0.66 Mev gamma ray, respectively. Ag107 + n + Ag108 (2.3 min) Ag109 + n + Ag110 (24.5 sec). Because of the large capture cross section (110 barns) of Ag109, and short half-life of Ag110 (24.5 sec), the 0.66-Mev gamma ray is the most prominent emission from silver for neutron activation periods of about a minute&apos;s duration.* The 0.44-Mev gamma ray from Ag108 will also be present, but will be one or two orders of magnitude lower in intensity. The decay scheme of Ag110 is shown in Fig. 1. If the neutron irradiation time is limited to about 100 sec, the Ag110 activity will essentially reach saturation and can be used to detect the presence of silver. In a neutron flux of 10 8 neutrons/cm2/set, the induced 0.66-Mev activity in 1 g of silver will be about 2 x 107 disintegrations per sec. This is about 1000 times the measurable gamma activity of 1 g of uranium in equilibrium with all its decay products; hence there is ample activity for detection. Under the same conditions of activation, most of the other elements do not reach this relatively high disintegration rate. Although this is in favor of the proposed technique, other problems must be considered. For mobile operation, it is desirable to obtain the largest neutron flux to weight ratio. Hence we have used a small 150-kev accelerator-type neutron source rather than an isotopic source such as an americium-beryllium neutron source. By use of remote control system, an accelerator-type neutron source can be safely used without the massive shield required for an isotopic source. Moreover, an accelerator-type source is more versatile in that it allows one to use a flux of either 14-Mev or 3-Mev neutrons, depending on whether a tritium or a deuterium target is used. With a 14-Mev generator, one can obtain a flux of 10 9 neutrons/cm 2/sec, and with a 3-Mev generator, the flux is generally two orders of magnitude less. Although silver will become activated with either generator using proper moderation, detection may be

Jan 1, 1968

By E. S. Machlin

An extension of the thermodynamic theory has been made for the case of irreversible growth processes occurring by the motion of an interface. The theory is applicable to such diverse phenomena as diffusion, growth in recrystallization, continuous grain growth, growth of carbides, etc., growth of eutectoid products, growth in solidification, recovery, "slipless" flow, etc. THE publication of a recent book1 has served to focus attention on a very powerful means of treating certain irreversible processes. This method which has been formally described as the thermodynamic theory of irreversible processes is applicable to processes which involve an approach to equilibrium and for which the deviations from equilibrium are small. The irreversible processes can be classified into three groups: chemical reactions, transport processes (diffusion, heat and electrical flows), and relaxation phenomena involving a degradation of internal energy to more stable states. The limits of applicability of the theory can be precisely defined1,2 for each type of irreversible process. For example, in a chemical reaction at constant temperature and pressure, the Gibbs free energy released per mol in the process should be less than the thermal energy, RT. Another type of irreversible process, which sometimes involves a combination of the first two of the above-mentioned groups, is treated in this paper. This process is one characterized by the motion of an interface separating two regions having different values of free energy and may be briefly described as a growth process. Prigogine2 and Herring3 have treated special cases of this type of process. Previous conscious applications of the theory in metallurgy have been limited to the field of diffusion, one of the transport processes. Darken,4 Bardeen,5 Prigogine2 and others have made significant contributions in this respect. Some other applications of the theory are described in this paper. The Theory The thermodynamic theory of irreversible processes is based on the work of Onsager,6 DeDonder,7 Prigogine2 and others. A resume of the theory has been given by Prigogine2 and DeGroot.1 A brief description of the theory follows, although for a complete understanding the reader is urged to read the references. It is first assumed that the change in entropy, even for a system removed from equilibrium, is given by dS = [dU + pdV - Si µi, dn, - Sk Pk dxk]T-1 Using this expression, the irreversible entropy production in the system is calculated by subtracting the contribution to the change in entropy of the system by transfer of heat, work, or matter from the surroundings. Thus, for example, the irreversible entropy production of a system at constant temperature and pressure is given by dtS = — — dG (DeDonder7) Now it has been shown by Prigogine,2 DeDonder,7 and DeGroot1 that the rate of irreversible entropy production diS/dt, when calculated in the manner suggested, can be written as a sum of products of conjugate forces XK and fluxes Jk, i.e., d,s/ = Sk Jk Xk [I-1] dt The assumption is next made that a linear relation exists between a given flux and the forces, obtained from Eq. I-1, i.e., Ji = Sk Lik Xk (i = 1, 2, . . . n) [I-2] Generally, there is a degree of freedom in choice of the fluxes and forces. However, for all the choices consistent with Eq. I-1 the Onsager8 relations, based on the principle of microscopic reversibility, namely, Lik = Lki, are valid. The coefficients Lik, depending upon the choice of the conjugate fluxes and forces, may be more or less dependent upon the parameters defining the state of the system. In general, the proper choice of fluxes and forces utilizing Eq. I-1, makes the coefficients Lik independent of time. Also, because many of the three classes of irreversible phenomena have already been treated,1,2 a proper choice can be made by analogy. In any case, the validity of Eq. 1-2, from whatever choice made using Eq. I-1, must be tested by experimentation. The theory, thus, comprises the following steps: 1—The irreversible entropy production is calculated to yield Eq. I-1. 2—The terms in Eq. I-1 are grouped

Jan 1, 1954

By M. Cohen, D. Caplan

The scaling characteristics of three Fe-Cr alloys have been investigated by determining their weight gain vs. time curves at 1600° to 2000° F. The scales formed thereby have been examined using the techniques of X-ray diffraction and spectrographic and metal-lographic analyses in an attempt to explain the discontinuities in the curves and to elucidate the mechanism of scaling. DESPITE the considerable number of investigations that have been carried out on heat resistant alloys, the characteristics of the scales formed at high temperatures are not fully known. The research reported here was undertaken in an attempt to ascertain the mechanism of scaling of the stainless steels. Scaling experiments were carried out first, the weight increase of the specimens being followed continuously with time. It was observed that, as well as showing the expected decrease in oxidation rate with time, the oxidation curves showed breaks corresponding to intermediate periods of accelerated oxidation, after which protectiveness again increased. This phenomenon was observed with austenitic stainless steels (types 302, 309, and 330) and with Fe-Cr alloys (types 410, 430, and 446), but only the latter are treated in this report. An examination of the scales was made using the techniques of X-ray diffraction and spectrographic and metallographic analyses in an attempt to obtain a correlation between the nature of the scales and the oxidation curves. A search through the literature revealed only a very few previous reports of such periods of accelerated oxidation. Dunn&apos; found breaks in the oxidation-time curves of some Cu-Si alloys but saw no rational explanation of the phenomenon. Heindlhofer and Larsen2 attributed a discontinuity in the weight gain-time curve of iron at 1290°F to the formation of blisters, the subsequent cracking of which exposed an unprotected surface and permitted rapid oxidation until a new protective scale had been reestablished. They advanced no explanation, however, for what they termed the peculiar behavior of a 27 pct Fe-Cr alloy at 2000°F which gained weight very rapidly in between two periods of very slow weight gain. Portevin, Pretet, and Jolivet3 in describing breaks in the weight gain-time curves of Fe-A1 alloys suggested that they might be associated with the occurrence of localized and deeply oxidized areas on the specimens. Bandel4 in a general discussion of oxidation curves of heat resistant alloys considered that the discontinuities were due to a local disruption of the protective layer by the growth of iron-rich oxides. Day and Smith" in their report on the scaling of a large number of iron alloys noted but did not explain occasional relatively rapid changes in oxidation rate at higher temperatures. Chevenard and Wache6 found breaks, often two per specimen, in the oxidation curves of an 18-8 type alloy. They suggested that the cause might be a depletion in chromium of the surface layer of metal due to its selective oxidation, the resultant high concentration of iron and nickel in the scale leading to a poorly protective scale. McCullough, Fontana, and Beck&apos; explained the breaks in the oxidation curves of types 304, 430, and 410 alloys as due to mechanical ruptures. Experimental Work Table I lists the chemical compositions of the materials used. Cylindrical specimens 1/4 in. in diam and 11/2 in. long were machined from cold rolled % in. rod. After a fine finish cut with a sharp tool, the specimens were abraded while still mounted on the lathe with Nos. 2, 1, 0, and 00 metallographic grade emery papers. A 3/64 in. hole was drilled at a distance of 1/8 in. from one end to permit suspension in the furnace. Specimen Nos. 1, 2, and 3 were tested with this surface preparation. All others, after being similarly prepared, were electropolished in a perchloric-acetic electrolyte, electrical contact being made by pressing a tapered platinum hook into the drilled hole. The specimens were then washed in hot water, rinsed with distilled water, rinsed with methanol, dried at 120°F, and weighed. Thereafter,

Jan 1, 1953

By R. E. Zinkham

An investigation has been conducted to compare short transverse and longitudinal fatigue and fracture properties in 4.25-in.-thick, high strength aluminum alloy plates. One plate was produced using standard rolling techniques while the other was pre.forged before rolling. Little difference was shown in fatigue strength of longitudinal specimens taken from mid-thickness of the plate. Howeuer, in the short transverse orientation fatigue strengths at 107 cycles were about 25 and 50 pct less, respectively, for the preforged and standard rolled plate. Differences in fatigue strengths were attributed to grain size and shape as well US orientation of constituents. Fatigue crack propagation rates and fracture toughness were compared at three different stress intensity (K) levels, using a constant compliance, double cantilever, wedge-shaped specimen. In a given plate, comparable fatigue crack Propagation rates were observed in the longitudinal (i9W) and short transverse (TW) orientations. Somezuhat gveater rates were observed in the short transzerse (TR) orientation. The preforged plute gave a lower rate for all three directions. Considerable secondary cracking developed, at times, over portions of the fatigue crack in both plates, particularly at the lower stress intensity levels in the short transverse specimens. Micro structure revealed constituent stringers as possible causes of the crack branching. Fracture toughness was considerably less in both plates in the short transuerse orientation. It is concluded that preforging not only improved directional tensile properties but also the fatigue and fracture properties in general. On occasion, aluminum plates have been milled away for hinges or bolted connections and stressed through the thickness or short transverse direction. Little or no information is available concerning fatigue characteristics or fracture toughness in this loading orientation in aluminum plate, or of the effect of fabrication on these properties. It was the intent of this project to examine, develop, and apply a unique specimen that has been advocated by others to study the fatigue characteristics and fracture toughness of two differently fabricated high strength aluminum plates. Linear elastic fracture mechanics criteria may be applied to the specimen so that the fatigue crack propagation rate and fracture toughness data may be of use for design or inspection applications. Fatigue characteristics are generally measured in the longtudinal or long transverse direction, where fairly large specimens such as center notched panels,&apos; are usually employed. Limitations are evident due to plate thickness, however, in the type and size of specimen that may be tested in the short transverse direction without extensions. Therefore, a specimen that is to be loaded in this direction should, for convenience, be compact. The general type of fatigue crack propagation specimens discussed and employed herein meet this requirement. These specimens are commonly called double cantilever beam specimens and lately "crackline-loaded edge-crack specimens".2 They may vary from a slope of zero (parallel-sides) to a wedge shape, the type employed herein. In general for most specimens the stress intensity KI at the tip of a crack is a function of the load, P and crack length, a. Some varieties of the wedge shaped specimen, however, give essentially a constant stress intensity KI over a considerable range of crack length.&apos; This feature can be a valuable asset in fatigue crack propagation experiments because the stress-intensity can be controlled simply by controlling the load without regard to crack length. MATERIAL AND METHODS Material. A standard rolled (light pass reduction) and a ~reforged and rolled (heavy pass reduction) plate of 7179-T651 material were used for the evaluation. The chemistry, processing history and average tensile properties are shown in Table I. Specimen Selection and Preparation. The specimen selected for the generation of fatigue initiation or S-N data was an axial tension type and is shown in Fig. 1. Specimens were taken from mid-thickness in the longitudinal and short transverse directions from both plates. Specimens were polished with 500 grit paper in a direction parallel to the loading axis. For the fatigue crack propagation tests, the specimen shown in Fig. 2 was used. This is similar to a specimen that has been employed by Mostovoy3 for fracture toughness studies on 7075-T6 aluminum alloy. It also fortuitiously agrees quite well with the dimensions of a specimen for which Srawley and Gross2

Jan 1, 1970

By Reynold Q. Shotts

CHEMICAL methods, based on the relative rates of oxidation of fusain, bright coal, and dull coal by nitric acid, have been devised to determine these coal components.1-4 Results obtained by oxidation methods for fusain have been checked against results obtained from microscopic methods5, 6on duplicate samples of the same coals, but to the author&apos;s knowledge this has not been done for bright and dull coal components. For this reason it is not certain that the two methods of analysis identify essentially the same chemical or physical units. It would be highly desirable to see results of the application of both methods to duplicate samples, but in the absence of any such data the author has attacked the problem indirectly. From the U. S. Bureau of Mines samples were obtained of three Alabama coals which the USBM had analyzed optically and reported on over the past 30 years. These samples were subjected to analyses by oxidation rate methods. Results of this work, and comparisons with the USBM analyses, have been published." This was the first indirect approach to the problem. The present report attempts a second indirect approach by way of internal validation. By nitric oxidation samples of two whole coals were carefully analyzed for fusain, bright coal, and dull coal. One coal was analyzed in duplicate. Duplicate portions of each of the coals were divided into three density fractions by means of heavy liquids. A duplicate portion of one of the coals was divided by sieving into three size fractions. Each fraction was analyzed by oxidation and its percentage composition calculated in terms of fusain, bright coal, and dull coal. Because the weight percent of each fraction was known, a material balance calculation for the whole coal was also made. The resulting reconstituted analysis of the whole coal could be compared to that determined by direct analysis. In addition, specific reaction rate constants were determined for each component and for each whole coal or fraction. Arbitrary reactivity indexes were calculated by dividing by 100 the sum of the products of the percent of each component in the coal and its specific reaction rate constant. The resulting figure was an average reactivity index for each coal or fraction. Weighting the reactivity indexes for each fraction by the percent of the fraction in the coal gave a reactivity index for each whole coal which could be compared to that calculated directly from the whole coal analysis. If oxidation analyses really delineate definite physical entities within the coal, or even definite groups of similar entities, reconstituted analyses calculated from fraction analyses should check closely those made of the whole coal. It probably is true that optical methods identify and describe a greater variety of components than do chemical methods and that variations are wide in the appearance and quantity of those components identified optically. Chemical methods based upon differences in oxidation reaction rates would of necessity be less discriminating, as between similar components, than would optical methods. The procedures followed for oxidizing the samples, analyzing the residues, plotting and calculating the percentage of each component, and calculating its specific reaction rate constant have been fully described.&apos;-&apos; In brief the method originally proposed by Fuchs et al.1 for the determination of fusain consists of the oxidation of small samples of coal in boiling 8N nitric acid in a condenser-fitted flask. After boiling for periods of 1/2 to 4 hr, the unoxidized residue is filtered and washed. The washed residue is treated with normal sodium hydroxide, diluted, and allowed to stand for several hours. The resulting brown liquor is removed, and the filtered residue dried, weighed, ignited, and weighed again. The ash-free residue is expressed as a percent of original dry, ash-free coal. The percent residue is plotted against time, and the extrapolation of this line to zero time gives the percentage of dry ash-free fusain present in the original sample. The shape of the resulting time plots has been explained&apos; by the assumption that they are the result of two different types of reaction, the first part representing a first order reaction with rate a func-

Jan 1, 1956