By P. Dayal, L. S. Darken

THE migration of carbon in austenite under the influence of an electric current has been observed qualitatively several times.14 Lebedev and Guterman5 recently have reported quantitative measurements; their method consisted of welding a low-carbon to a high-carbon wire, passing current, and later estimating the carbon distribution metal-lographically. We believe the method reported in this paper is superior in principle since electrolytic migration and ordinary diffusion are not necessarily coupled as in the weld method; also for the first time the extent of migration is determined by combustion analysis for carbon. A uniform tubular specimen (S.A.E. 1045 or 1095) was mounted as illustrated in the figures. the whole assembly being in an atmosphere of purified nitrogen. Direct current (129 to 226 amp at 0.65 to 1.0 v) served as source both of heat and of potential gradient for carbon migration. The duration of experiment was 7.5 to 12 hr, during which time the temperature was controlled (±10°C) manually. The experimental conditions are indicated in the first five columns of table I. With this experimental arrangement, the temperature initially has a maximum value at the central plane. Also, in this vicinity (by virtue of the symmetry), the carbon entering any volume element is equal in quantity to that leaving; the loss or accumulation of carbon occurs near the electrodes since the carbon moves uniformly near the center and is "frozen" at the cold ends. Hence, providing the time of experiment is not sufficiently long to seriously influence the conditions at the central plane, carbon crosses this plane only under the influence of the electrical potential gradient and not under the influence of temperature or concentration gradient. The amount of carbon which has crossed this plane was determined by combustion analysis of the two halves of the specimen. The results of these analyses are shown in the sixth and seventh columns of table I. It will be noted that substantial amounts of carbon migrated from the anode portion to the cathode portion (except at 920°C, which temperature was too low to exhibit the effect in the allotted time). In spite of precau-tions taken, considerable decarburization occurred as may be seen by comparing cols. 8 and 5. In three cases (indicated by asterisks in table I) the specimen was ground on one side, polished, and examined metallographically before analysis. One specimen was normalized and re-examined. Micrographs of selected areas in specimens 4 and 6 are shown in figs. 1 and 2, respectively. Evidence of carbon migration from the anode toward the cathode is quite apparent. Fig. 2 shows abundant graphite as well as cementite in a region near the cathode. The temperature of this zone is estimated at about 800°C. In fig. 1, particularly in the micrograph on the extreme right (the right side of which is of unaltered carbon content), there is evidence of slight depletion of carbon in the immediate vicinity of the cathode as contrasted to the general increase in carbon of the cathode half of the specimen. Although this may be attributed in part to decarbur-ization, it is believed that it is occasioned also by thermal diffusion—migration (of carbon) from a cool to a hot zone4—a phenomenon superimposed upon the electrical migration. Evidence of carbon migration was visible particu-larly during the course of the high-temperature,

Jan 1, 1951

By A. T. Aldred, K. M. Myles

The vapor pressure of chromium over solid V-Cr alloys has been measured by the torsion-effusion method in the temperature range 1450" to 1650°K. The chemical activities as well as the free energies, entropies, and enthalpies of formation of the alloys have hem computed from the vapor-pressure data. The activities of both chromium and vanadium exhibit fairly small negative deviations from Raoult's law over the entire composition range. The values of the excess entropies and the enthalpies of formation found at 1550°K are considered in terms of the changes in the clzaracteristic properties of vanadium and chromium that occur upon alloying. RECENT interest in the theory and properties of transition-metal alloys has shown the need for relevant thermodynamic data. The present investigation of the V-Cr system was undertaken as part of a more general study of thermodynamic properties of transition-metal alloys. The system was chosen because of the reported complete solid solubility of the components at all temperatures1 and because the difference in magnitude of the vapor pressures of vanadium and chromium allowed a simple effusion technique to be used. The torsion-effusion method was employed to minimize compositional changes in the alloys during the experiments. EXPERIMENTAL Equipment. The torsion-effusion apparatus, shown diagrammatic ally in Fig. 1, consists of a torsion system suspended inside a vertical vacuum chamber whose lower end is surrounded by a high-temperature vacuum furnace. An auxiliary optical lever and screen are used to determine the angle of rotation of the effusion cell. The torsion fiber is an annealed, high-purity, tungsten wire usually between 0.003 and 0.007 cm in diameter and about 43 cm long. The wire supports a concave mirror and a rigid tantalum connector tube. The effusion cell is fastened to the lower end of the connector tube by a dovetailed yoke and har- ness arrangement. The cells, which are 1.27 cm in diameter and 4.4 cm long, were made by electron-beam welding tantalum endcaps onto a 0.025-cm-wall tantalum tube. The two orifices, formed by drilling, have similar areas ranging from 0.011 to 0.031 sq cm. The noninductive sheath-type furnace consists of a single-phase tantalum heating element 6.35 cm in diameter, 15 cm high, and 0.013 cm thick; the element is completely surrounded by radiation shields in an evacuated chamber. The power system includes a 17-kva self-saturating saturable core reactor with an integral magnetic amplifier and a water-cooled, 15-kva, step-down power transformer with a multitap secondary. Temperatures are controlled to within ±1/2o at 1600°K by means of a unit that includes a reference voltage source, a dc electronic null detector, a current-adjusting proportional band relay, and the self - saturating reactor. At 1650°K the temperature variation within the cell, vertically and horizontally, is 3/4oK. Unwanted motions of the torsion system are damped by the movement of an aluminum vane, which is mounted on the connector tube, between the poles of an electromagnet. When not in use the magnet is withdrawn and rotated 90 deg to prevent its interaction with the rotation of the system. Measurements. The vapor pressure, p, is re-

Jan 1, 1964

By W. A. Ver Wiebe

The year 1940 was singularly unmarked by sensational developments in Kansas. Routine operations were carried on in a systematic, orderly fashion and the efforts of oil producers were concentrated on extending known fields. In Kansas an arbitrary yardstick for wildcats has been set up. A well drilled mile or more from a known pool or well is now considered a wildcat. A "rank wildcat" is one that is drilled at least 2 miles from any known producer. During 1940, rank wildcats resulted in the completion of 116 test wells, among which 16 were successful in finding new oil pools and the remaining I00 were dry holes. The ratio of successful wells to dry holes, therefore, was approximately I:6. During the year, 1890 wells were completed in eastern and western Kansas. This figure is somewhat lower than that given in several trade journals, because it does not include wells that were deepened or wells that were recompleted in a different geological horizon. About three fourths of these (1423) were completed as commercial oil wells (I220 in western and 203 in eastern Kansas). The commercial gas wells completed number 58 of which 10 are in eastern Kansas and 48 in western Kansas. Of the remzining completions 147 are dry holes in eastern and 262 are dry holes in western Kansas. Based on daily potential capacity, the new discoveries of the year account for a cumulative initial production of 46,000 bbl. in eastern and 2,128,000 bbl. in western Kansas. The state of Kansas attained a new peak in production, with the total of 66,245,000 bbl. for the year 1940, the number of contributing wells being 20,779. Thus the increase over 1939, when about 58 million barrels was produced, is considerable. The previous peak occurred in 1937, when 70,761,000 bbl. was marketed. In another still earlier peak, in 1917, slightly more than 45,000,000 bbl. was produced and sold. The production of gas probably reached a new peak also during 1940, with its total of 85 1/2 billion cubic feet. Between the peak of the year 1908, when over 80 billion cubic feet was produced, and that of 1940, the production dropped to a low point of 16 billion cubic feet in the year 1921. The number of test wells drilled was larger than in 1939; that is, 1890 compared with 1458. The first peak was reached in 1904, when 2782 wells were drilled. The number dropped off rapidly, to 368 three years later, but rose to the second and highest peak in 1918, when 4671 test wells were completed. In the period between 1904 and 1912 more gas wells were completed than oil wells. Between the high peak of completions in 1918 and somewhat lower peak of 1937, the low point was reached during 1931, with the completion of only 470 test wells. In the number of new pools discovered, Kansas again ranks high among the states. The exact number depends somewhat upon the interpretation of a "new" area— whether it should be called a new pool or a long extension of an old pool. Unfortunately, the matter of securing the right kind of production allowable also enters into this question. Often the decision regarding a new pool cannot be made until other wells

Jan 1, 1941

By W. A. Ver Wiebe

The year 1940 was singularly unmarked by sensational developments in Kansas. Routine operations were carried on in a systematic, orderly fashion and the efforts of oil producers were concentrated on extending known fields. In Kansas an arbitrary yardstick for wildcats has been set up. A well drilled mile or more from a known pool or well is now considered a wildcat. A "rank wildcat" is one that is drilled at least 2 miles from any known producer. During 1940, rank wildcats resulted in the completion of 116 test wells, among which 16 were successful in finding new oil pools and the remaining I00 were dry holes. The ratio of successful wells to dry holes, therefore, was approximately I:6. During the year, 1890 wells were completed in eastern and western Kansas. This figure is somewhat lower than that given in several trade journals, because it does not include wells that were deepened or wells that were recompleted in a different geological horizon. About three fourths of these (1423) were completed as commercial oil wells (I220 in western and 203 in eastern Kansas). The commercial gas wells completed number 58 of which 10 are in eastern Kansas and 48 in western Kansas. Of the remzining completions 147 are dry holes in eastern and 262 are dry holes in western Kansas. Based on daily potential capacity, the new discoveries of the year account for a cumulative initial production of 46,000 bbl. in eastern and 2,128,000 bbl. in western Kansas. The state of Kansas attained a new peak in production, with the total of 66,245,000 bbl. for the year 1940, the number of contributing wells being 20,779. Thus the increase over 1939, when about 58 million barrels was produced, is considerable. The previous peak occurred in 1937, when 70,761,000 bbl. was marketed. In another still earlier peak, in 1917, slightly more than 45,000,000 bbl. was produced and sold. The production of gas probably reached a new peak also during 1940, with its total of 85 1/2 billion cubic feet. Between the peak of the year 1908, when over 80 billion cubic feet was produced, and that of 1940, the production dropped to a low point of 16 billion cubic feet in the year 1921. The number of test wells drilled was larger than in 1939; that is, 1890 compared with 1458. The first peak was reached in 1904, when 2782 wells were drilled. The number dropped off rapidly, to 368 three years later, but rose to the second and highest peak in 1918, when 4671 test wells were completed. In the period between 1904 and 1912 more gas wells were completed than oil wells. Between the high peak of completions in 1918 and somewhat lower peak of 1937, the low point was reached during 1931, with the completion of only 470 test wells. In the number of new pools discovered, Kansas again ranks high among the states. The exact number depends somewhat upon the interpretation of a "new" area— whether it should be called a new pool or a long extension of an old pool. Unfortunately, the matter of securing the right kind of production allowable also enters into this question. Often the decision regarding a new pool cannot be made until other wells

Jan 1, 1941

By C. R. Criss, R. J. McCormick

ThiS paper .summarizes the development and perform. ance of the Coldwater Oil field, Isabella County, Mich. Production is obtained at a depth of 3750 ft from a dolomite reservoir, which is probably both Rogers City and Dundee. There appears to be no persistent barrier to vertical fluid movement between the Rogers City and Dundee, and both formations are believed to have a common original oil-water contact. No we1ls are open to production at the level of the Dundee. The discovery of the field in 1944 was followed by the drilling of 81 producing wells and nine dry holes. By the end of 1952, the field had produced 12,763,000 bbl of oil, at which time 69 active wells were producing 3600 B/D oil and 21,000 B/D water. The reservoir has an effective natural water drive, and bottom-hole pressure has declined 75 psi from an original pressure of 1453 psi. Oil is undersaturated at reservoir conditions with a solution GOR of 512 cu ft/bbl and a saturation pressure of 1190 psi. INTRODUCTION Although the Coldwater Field is now in its ninth year of production, it ranks seventh in cumulative recovery, and second in current daily oil production in the State. Following complete development of the field in 1946, it has consistently contributed approximately 11 per cent of Michigan's daily production. Coldwater appears to have a greater pay thickness than most fields producing from the Rogers City forma- tion in the west central part of the Michigan basin. Except as influenced by the extent of closure and the thickness of the oil column, reservoir performance is believed to be representative of Rogers City fields in this part of the basin. For this reason, it is felt that the following presentation of factual data for the field will be of general interest. HISTORY AND DEVELOPMENT Discovery of the Coldwater field during Aug., 1944, followed favorable subsurface geological correlations and core tests drilled to a shallow stratigraphic marker horizon. The field is located in the west central part of the Michigan Basin in Coldwater Township (T16N-R6W), Isabella County. It is 60 miles west-northwest of Bay City, and near the geographic center of the southern peninsula of Michigan. The discovery well flowed 200 bbl of oil the first 24 hours from the Rogers City dolomite at a depth of approximately 3750 ft. Field production is principally from the Rogers City with a minor amount assumed to come from the underlying Dundee dolomite, although none of the wells are open to production at the level of the Dundee. Both the Rogers City and Dundee formations belong to the Devonian system (See Geologic Column-Fig. I.) In addition to Rogers City-Dundee oil production, sweet gas is produced from the Michigan Stray sand of the Mississippian system at a depth of 1400 ft. The gas reservoir has approximately the same areal extent as the underlying oil reservoir. Although gas production is an important feature of the Coldwater field, this report is concerned only with the oil reservoir. The productive area is approximately 3200 acres. The pool is developed on a 40 acre spacing pattern with wells drilled in the center of the north half of 40 acre tracts, except for a few off-pattern wells drilled along

Jan 1, 1955

By H. R. Ogden, E. S. Bartlett, A. G. Imgram

Notched and unnotched tensile specimens of wrought and recrystallized, oxygmted and hydro-genated tantalum and columbium were tested over a range of temperatures selected to encompass the ductile-to-brittle transition. Increasing the oxygen content of tantalum and columbium increased their strength, and raised their ductility transition temperature, but did not cause a marked deterioration of notch properties below that of commercially pure material. The adverse effects of oxygen were more pronounced for recrystallized structures than for wrought material. The effects of hydrogen are complicated by strain aging or slow strain rate hydrogen embrittlement at -105°F. However, in general, hydrogen had only a minor effect an strength, but markedly increased the effective transition tem-terature and caused a deterioration of notch properties . BCC metals including the refractory metals in Groups Va and VIa (V, Cb, Ta and Cr, Mo, W) can be expected to undergo a ductile-to-brittle transition and exhibit brittle fractures at low temperatures.' Notch embrittlement is associated with this phenomenon, and can be a serious design problem. Table I compares the tensile transition behavior and notch sensitivity of commercially pure Group Va and VIa refractory metals. The Group VIa refractory metals have considerably higher transition temperatures, and become notch sensitive at higher temperatures, than do the Group Va refractory metals. In addition, the Group VIa refractory metals are sensitive to metallurgical structure. Recrystallized structures generally have higher transition temperatures than wrought material of the same composition. The relatively poor transition behavior of the recrystallized structures of these metals is generally attributed to the segregation of interstitial impurity atoms at grain boundaries. Pronounced sensitivity to structure is not evident with commercially pure Group Va refractory metals, however. Since these metals have higher solubilities for interstitial elements than do the Group VIa metals ,4 it can be expected that higher total interstitial concentrations are necessary to develop a comparable degree of grain boundary segregation and to produce a similar sensitivity of transition temperature to structure. Increasing only the concentration of interstitial atoms in solution would tend to increase the flow stress of a metal in relation to its cleavage fracture stress and thereby raise its transition temperature, but would not be expected to cause a marked sensitivity of transition temperature to structure. A research program has been conducted at the Battelle Memorial Institute to evaluate the effects of interstitial oxygen and hydrogen on the transition behavior and notch sensitivity of tantalum and columbium, and to evaluate the effects of structure on "contaminated" material. EXPERIMENTAL PROCEDURES Notched and unnotched tensile specimens of oxygenated and hydrogenated tantalum and columbium with both wrought and recrystallized structures were tested over a range of temperatures selected to encompass the ductile-to-brittle transition Oxygen levels selected for study in both tantalum and columbium were nominally 500 and 1000 ppm, whereas nominal hydrogen contents were 150 and 500 ppm in tantalum and 150 and 300 ppm in columbium. Oxygen and hydrogen additions were made directly to 6-in. lengths of 1/2-in.-diam electron beam melted wrought bar stock, in a Sieverts Apparatus. Subsequent high-temperature annealing was required for homogenization of the oxygenated material, but was not necessary in the case of hydrogenated stock. The oxygenated and hydrogenated bars were then swaged to 1/4-in.-diam rods. Tensile specimen blanks were cut from the 1/4-in.-diam rods and annealed to achieve stress-re-

Jan 1, 1963

By A. W. Demmler

RECENTLY, Chaudron,&apos; Montariol,2 and their co-workers published the results of their studies on zone-refined aluminum. They found their material to be capable of recrystallization at —50°C, but gave no data as to the percentage reduction or time required. Their material was found to be practically non-work hardening at room temperature, but after 96 pct cold work at a low temperature and storage in liquid nitrogen it was found to recrystallize to coarse grains in less than 3 hr at 20°C. Recently, a study was made of the room temperature recrystallization characteristics of zone-melted aluminum. An ingot 14 in. in length, with a 3hx3 in. cross section, was made in an extremely high purity graphite boat under an atmosphere of dried commercial argon. It was made by first passing the molten zone along the ingot of 99.99+ pct A1 15 times. At this point, the most impure 3 in. (the end toward which the eutectic forming impurities migrated) were replaced with more of the original starting material, and 15 more traverses were made. Each traverse of the zone along the ingot required approximately 3 hr. Three ingots were prepared in this identical fashion and the chemical analyses were made spec-trographically on two of these ingots, rather than on the one used in this investigation. The analyses were made at 1 in. intervals along the ingot, in duplicate. Over the purest 5 in. of the ingot, which were most important in this investigation, there was found an average composition of <0.00004 pct Cu, <0.0003 pct Fe, <0.0001 pct Si, and <0.0001 pct Mg. In addition, the following elements were not detected spectrographically even in the more impure end of the bar: manganese, zinc, nickel, chromium, titanium, vanadium, lead, tin, boron, beryllium, bismuth, gallium, zirconium, cadmium, antimony, cobalt, and molybdenum. The original ingot was given several cold reductions, with intermediate anneals in order to refine the grains. Owing to the extreme length resulting and the ease of deforming the material plastically, it was cut into eight equal lengths and identified as shown in Fig. 1, with the highest numbered section at the purer end (that enriched with peritectic formers). Section 6 was used in the exploratory work and was found to be of exceptionally high purity, giving more rapid rates of room temperature re crystallization than any previous aluminum studied at the Alcoa Research Laboratories. This fact suggested that the entire midsection of the ingot might be of very high purity. Accordingly, section 4 was chosen for the next study. A portion of it was rolled to cold reductions of 10, 25, 40, 60, 75, and 90 pct at room temperature, and the re-crystallization of each specimen was followed by X-ray pinhole transmission photographs. The other portion received the same treatment, except that both the specimens and the rolls were maintained at 160°F in the process of rolling. The latter ortion was retarded in its recrystallization as compared to the former, probably due to the stress relief effect of the warm rolling. Both of these portions of the fourth section were found to recrystallize at a considerably slower rate than did the sixth section.

Jan 1, 1957

By L. A. Panek

Research on roof bolting has developed significant information with respect to the functions that can be performed by properly installed bolts and the methods that can be used to ensure that effective installation has been achieved. The present paper brings together results that are pertinent to the design of a bolting system for reinforcing horizontally stratified mine roof with vertical bolts. The design approach is based on the use of bolts to decrease the maximum bending stress within an arbitrary sequence of roof strata (see Fig. 2) in which the only loads are the weights of the individual beds. The use of rock bolts to achieve other objectives, such as to stabilize a fractured rock mass on the periphery of a mine opening,3 is excluded from consideration herein. Reinforcing effect of bolts consists of a friction effect and a suspension effect in combination. "Friction effect" refers to reduction of bending in a stratified roof due to clamping action of tensioned bolts, which compress the strata, thereby creating frictional resistance to displacement along planes of stratification. (The flexure of a sequence of strata is necessarily accompanied by horizontal displacement of each bed with respect to its neighbor, along mutual surfaces of contact.) Although the sliding of the beds tends to exert a shearing effect on the bolts, tests show that this has negligible influence on the bending stresses, probably because the bolts are so far apart. "Suspension effect" refers to the transfer of part of the weight of the weaker or thinner strata to one or more thick strata, which occurs when strata with differing tendencies to deflect are constrained to have equal deflection. The term "suspension" is used irrespective of whether the thin strata are above or below the thick strata, because tests show that the supporting effect of the flexurally more rigid roof strata is for practical purposes independent of their position in a bolted sequence of strata. An earlier paper4 dealt with a bolted unit in which all strata had equal flexural rigidity; bolting could develop a friction effect but no suspension effect. The present paper deals primarily with a bolted unit in which all strata do not have equal flexural rigidity, so that bolting can develop both a friction effect and a suspension effect. The reinforcing effect of the bolts was determined by a combination of experimental and theoretical stress analysis.4&apos;6&apos;7 The experimental method consisted of loading a model by rotating it in a centrifuge to simulate the gravity forces exerted about an underground excavation. Models were made from two different limestones, although the results are independent of the material because the elastic constants were taken into account in the data analysis. Electric resistance strain gages were bonded to the highest and lowest members of the bolted unit to determine the outer-fiber bending strains at the center and at the supports. The quantitative results presented herein are based on tests of 56 different models, which included a range of values for the structural parameters. Each model was tested several times, with different combinations of spacing and tension of the bolts. DESIGN EQUATIONS The effects of friction and suspension on the flexure of a bolted stratified roof can be expressed by the following equations, which give the maximum bending stress, the deflection, the friction effect, the suspension effect and the transferred load for any (the i-th) member of the bolted unit in terms of the structural parameters:

Jan 1, 1964

By J. Geertsma

In order to obtain a better insight into the pressure-volume relationship of reservoir rocks a theory of pore and rock bulk volume variations is presented. The theory is independent of the shape of the pores but is restricted to isotropic porous media built up of continuous homogeneous matrix material. The main conclusion obtained from this theory is that only three elastic constants and three viscous constants are required for describing pore and rock bulk volume variations if the porosity is explicitly introduced into the treatment. In addition, reasonable approximations are introduced for various types of reservoir rock, e.g., sandstones, limestones, and shales, which lead to further simplifications of the basic formulas. In consequence there is then a further reduction in the number of deformation constants which have to be determined experimentally. It is shown how measurements of these remaining deformation constants can be performed most conveniently. Finally the application of the theory to reservoir studies is discussed and the translation of experimental results obtained in the laboratory into reservoir behavior is considered. INTRODUCTION The decline of fluid pressure in connection with the withdrawal of fluid from an underground reservoir gives rise to a change in volume of both reservoir fluids and reservoir rock. The volume variation of the reservoir rock results in a decrease of both the pore volume and the total volume of the fluid-filled formation. Whereas the variation in volume of the reservoir fluids with pressure is usually known from PVT analysis, that in the volume of the porous medium is rarely measured, as it is considered of minor importance in reservoir engineering. Nevertheless, certain experimental results&apos; suggest that in a number of cases the neglection of the variation in pore volume may introduce errors into material balance calculations of reservoirs producing above the bubble point. Only a few experimental results on the compressibility of porous rocks have been published. The compressibility of pure quartz and of calcite can be found in a paper by Adams and Williamson&apos;. Botset and Reed&apos; carried out some experiments on the compressibility of loose sands, while Carpenter and Spencer&apos; measured the compressibility of a number of consolidated sandstones, which data were supplemented by Hughes and Cooke5. Hall&apos; finally reported a number of experiments designed to study the influence of the porosity on the compressibility of oil-bearing formations, from which it appeared that, particularly in the low porosity range, the compressibility of the pore volume is important enough to be taken into account. Difficulties, however, arise in applying these experimental results to field cases. This is partly due to the fragmentary nature of the published data. Yet even if more complete data were available, the need for a theoretical background would be strongly felt. Such a background can be partially found in studies carried out by Biot,6,7 who published a theory of elastic deformations of porous materials and their influence on fluid displacement within the pores, by Lubinski8, who studied the stress distribution in an elastic porous medium neglecting pore compressibility, and by Gass-mann" who mathematically analysed the elasticity of packings of spheres. The contributions of Biot intro-duce a number of deformation constants which are impractical for reservoir rocks from an aspect of experi-mental determination. The theory developed by dass-mann is correct but difficult to read. It appeared, how-

Jan 1, 1958

By H. K. Najarian

This paper describes recent development work on the Wheaton-Najarian Vacuum Condenser for Zinc at Josephtown Zinc Smelter, wherein, to dissipate the heat of condensation, the "airlift" action of gases bubbling through the molten zinc in the condenser is utilized to circulate the zinc through an outside "cooling well" and cooling it continuously. AN earlier paper1 gave an account of initial development of the Wheaton-Najarian Vacuum Zinc Condenser at the Josephtown Zinc Smelter of the author&apos;s company. This paper is a progress report of further development work over the years directed toward improving the efficiency and increasing the capacity of the condenser. In this type of zinc condenser, zinc vapor with accompanying noncondensable gases from electro-thermic zinc smelting furnaces is passed upwardly through a mass of molten zinc confined in a refractory-lined U-tube. The zinc vapor condenses in the molten zinc and the noncondensable gases are drawn out of the condenser by suction applied over the surface of the molten zinc. The heat of condensation of zinc, amounting roughly to 1000 Btu per lb of zinc condensed, is absorbed by the molten zinc and, in turn, is dissipated continuously to keep the temperature of molten zinc in a range to permit effective condensation. At the time of publication of our first paper, we had at Josephtown Smelter five units of 69-in.-bore metal furnaces and one larger metal furnace having 96-in. bore. Each 69-in. metal furnace had a condenser with 22-ft overall length. The 96-in.-bore furnace had a condenser with overall length of 31 ft. Condensers were of circular cross section, with corrugated steel outer shell and carborundum lining. Diameter of these condensers was 32 in. inside the refractory lining. Molten metal in the con- denser was kept cool by spraying cold water on the outside of the condenser shell. Under good operating conditions, 22-ft condensers produced some 12 tons of metal per day; and the 31-ft condenser, about 22 tons. When the furnaces produced zinc vapor at higher rates, invariably the condenser temperature would rise to levels where excessive blue powder would form and accumulation of accretions in the condenser would be accelerated. We found that, with the system of cooling in use, we had to provide heat-exchange surface of some 150 sq ft to condense 1000 lb of metal per hr with reasonable efficiency. The wall of the condensers was made up of 5/8-in.-thick corrugated-steel shell having next to it several layers of mica and inner refractory lining of special carborundum shapes to fit the corrugation in the steel shell, and having a minimum thickness of about 2 in. Relatively low rate of heat transfer through the thick condenser wall and slow internal circulation of the molten zinc limited the rate of heat exchange between hot metal within the condenser and the cold water flowing over the outer steel shell. The thickness of the condenser wall was about minimum that we considered suitable for continuous operation. As we learned to operate the electrothermic furnaces with higher power input, producing zinc vapor at higher rates, it became apparent that we needed condensers having larger heat-exchange surfaces. Our 96-in.-bore furnace had 6 single-phase power circuits with transformers rated at 500 kva each and normally good for power input of 3000 kw.

Jan 1, 1959

By C. R. Claus, G. A. Standish

Since March. 1945, the Magnolia Petroleum CO. has drilled 39 wells in Southwest Coastal Louisiana. All wells were drilled within a comparatively small radius, but the area provides a large variety of problems. The deepest well drilled was 13,518 ft, and the total depth averaged 10,977 ft. Throughout this period drilling mud control and types of mud handled were: (I) phosphate, (2) red lime (late conversion), (3) red lime starch (early conversion), (4) red lime starch oil emulsion, (5) precision controlled low alkalinity-low lime content. and (6) gel muds for completion purposes. Improvement has been obtained in effecting some or all of the following: (I) more rapid penetration, (2) reduction in drilling hazards, (3) better evaluation of cores and logs, and (4) better completions. The geological sequence of zones penetrated range from recent sediments at the grass roots through the Frio section. Anticipation of high-pressure zones and incompetent formations entails precision control of drilling mud weights, and the unconsolidated nature of the various zones requires constant attention to the filtrate, viscosity, and gel strength values. In the Chalkley field, particularly, this combination of problems exists, where the formation pressures and overburden weight density values are in very close proximity. Design of casing and drilling mud programs must be modified to fit each well. INTRODUCTION Field and research work on drilling fluids has made constant progress, enabling operators to prospect progressively deeper horizons. Numerous papers have been written on the theoretical aspects of drilling fluid devel- opment, but in the field engineers have found it difficult to evaluate the role of specific mud constitutents when dealing in terms of thousand barrel mud systems. For that reason field data is somewhat lagging in technical report writing. However, applications of new techniques in the field have usually paralleled, and in numerous instances preceded, research work. The information obtained by Magnolia Petroleum Co. in the course of drilling 39 wells within a comparatively small area in Southwest Coastal Louisiana provides an excellent opportunity of reviewing a specific example of drilling mud evolution. A large variety of problems has been coped with, the most important result being that every well was successfully drilled to its projected total depth. The discussion begins with the advent of deep drilling in this area in March, 1945, and is concluded with a resume of recent drilling operations in the Chalkley field. The primary purpose of this paper is to describe the evolution in types of drilling fluids as it occurred and its application in the solution of various drilling problems. All of this information and experience resulted in the successful drilling of the three wells in the Chalkley field, where a combination of the most sound techniques was necessary in carrying drilling operations to the projected total depths. Other operators along with service company engineers have contributed considerably through the interchange of ideas and information to this paper, but the data and conclusions which are contained are based on first-hand observation of Magnolia Petroleum Company&apos;s drilling operations. The 39 wells drilled by Magnolia Petroleum Co. average in depth 10,977 ft per well, while the maximum depth penetrated was 13,518 ft. The cost of drilling fluids have varied from $8,700 to $165,000, with the over-all drilling costs ranging from $74,000 to $543,000 per well. This wide variance illustrates the unpredictable nature of each well and the effects on over-all cost when high density muds are required to control

Jan 1, 1955

By N. K. Chen, C. H. Mathewson

Single crystals of high purity aluminum of various orientations were carefully documented after plastic extension. Special attention was given to the formation of slip lines, deformation bands, and asterism. An explanation for the geometry and mechanism of formation of deformation bands is considered. WHILE the general process of plastic extension of face-centered cubic metals is well understood,&apos; the accompanying structural changes due to slip and rotation are far more complex than ordinarily assumed. In the case of stretched single crystals of aluminum, the complicated behavior is especially marked by the formation of deformation bands, as first indicated by Collins and Mathewson." Such bands were believed by them and also by others,".&apos;7 who have discussed banded structure in general, to represent one of the important modes of lattice reorientation and to be intimately connected with the recrystallization process. Yet, despite their fundamental importance to the understanding of the mechanism df both plastic deformation and recrystallization, practically no study of the crystallographic features of these bands in their relationship to the conventional slip process has been attempted. This paper describes part of an extensive investigation on the structural behavior during plastic deformation of aluminum single crystals and is especially concerned with the characteristics of deformation bands. The investigation of the subsequent re-crystallization of deformed aluminum single crystals will be discussed in a later publication. Experimental Procedure Single crystal specimens of 99.996+ pct pure aluminum, Yz in. in diam and 5 to 6 in. in length were made both by the Bridgman method5 nd by a modified temperature gradient method.&apos;* Crystals were selected in which the lineage deviation did not exceed 2"; i.e., as determined from the back-reflection Laue X-ray photograms. These crystals were radiographed to insure that no internal porosity was present. The orientations showed good coverage of the whole area of the Taylor and Elam triangle.&apos; Orientations of the crystals were obtained by the back-reflection Laue technique described by Greninger." Crystals so selected were tapered very carefully in a lathe to obtain a linear decrease in diameter from 0.500 to 0.350 in. along a gage length of 3 in. This is considered desirable because it permits a strain gradient to be introduced in a single specimen at one initial orientation. The advantages of tapered crystals for studying the development of slip lines and recrystallized grains have been pointed out by previous investigators." The cold-worked layer resulting from the machining operation was removed by alternate etching in aqua regia and careful polishing with 2/0 emery paper until undistorted Laue back-reflection spots were obtained. A homogenization treatment at 600 °C for 24 hr was then introduced to insure the removal of residual stress. Two of the crystals so prepared were also checked by use of a glancing angle technique. Using a copper target, at 30 kv and 10 microamperes, a monochromatic beam was positioned at right angles to the axis of the crystal about which it rotated. The time of exposure was 24 hr. From these X-ray photograms, it was concluded that the present method of preparation of single crystals is satisfactory. Following this procedure, the crystals were elec-trolytically polished in a 2:l solution of methyl alcohol and concentrated nitric acid. Intermittent

Jan 1, 1952

By J. G. Kura, P. D. Frost, L. W. Eastwood

THE preparation and general properties of mag-nesium-lithium base alloys have been described in earlier papers.l,2 Lithium forms solid solutions with pure magnesium, lowers its density, and improves its formability. The improved isotropy and better formability of these alloys are attributed to the ability of lithium to convert the magnesium lattice from hexagonal (alpha phase) to body-centered-cubic (beta phase) structure. This change in structure is, however, accompanied by some limitations which make it difficult, if not impossible, to combine all the desirable properties in one composition. The most important of these limitations is the tendency of the high-strength alloys to overage and lose strength at temperatures of the order of 150" to 200°F. A study was made of the effects of composition and heat treatment on the age-hardening character- istics of the alloys. Stability of properties was determined by hardness and tensile testing of the alloys at room temperature after various periods of exposure to elevated temperatures. Precipitation-hardening curves are shown for a number of magnesium-lithium-zinc alloys in fig. 1. All the alloys were solution treated at 700°F and aged at 200°F. The reason for using the drastic quench, toluene at —105°F, was to reduce the rapid precipitation of the hardening phase which takes place at room temperature. Previous experience has shown that a hardness of about 90 to 95 Rockwell E is indicative of yield strengths in the range of 35,000 to 40,000 psi. This is a desirable strength level for magnesium-lithium base alloys with specific gravities of the order of 1.65 or less. Although the hardness level is raised by large zinc contents, a corresponding decrease in the cold formability of these alloys occurs with increasing zinc content. Thus, alloys containing up to about 10 pct Zn and having hardnesses of the order of 70 to 75 Rockwell E may be bent over a very small radius; however, the 16 pct Zn alloy requires a bend radius of more than 8T. The hardness relationships illustrated in fig. 1 can be explained by the partial phase diagram shown in fig. 2. The zinc-free magnesium-lithium alloys are entirely body-centered cubic (100 pct beta phase) when the lithium content of the binary is 10.3 pct or higher. When zinc is added, the boundary between the beta and alpha-plus-beta fields at 700°F is shifted to lower lithium contents. In addition, the solubility of zinc at 700°F decreases with decreasing lithium content. It is shown by a study of micro-structures that the limit of solid solubility of zinc in the 6Mg/Li* matrix at 700°F is about 19 pct. It is believed from a study of the aging curves that this limit is about 2 to 3 pct at 200°F. Zinc additions up to about 2 pct increase the hardness and strength of the magnesium-lithium base solid solution. Larger additions of zinc effect further hardness increases, but precipitate during prolonged aging at 200°F. Alloys having 14 to 20 pct Zn precipitation harden extremely rapidly during quenching, even when quenched in toluene at —105° F. The high-zinc alloys overage at 200°F but are capable of maintaining reasonably high hardnesses for periods up to 1000 hr.

Jan 1, 1951

By Carlos G. Valenzuela

The value generally accepted for stacking-fault energy, of copper has been approximately 40 ergs per sq cm based on Fullman&apos;s2 value for the coherent twin-boundary energy and the assumption that is twice the twin boundary energy However, Thornton and coworkers8 determined that the lower limit of for copper is approximately 60 ergs per sq cm, based on measurements of dislocation-node radii. They suggested that the assumption of = 2t is invalid. It is the purpose of this note to present results which indicate that the values of obtained by measurement of twin-grain boundary intersections and the values obtained by measurement of dislocation-node radii are actually compatible. The most reliable values for of the a brasses, based on electron-microscope observation of dislocation nodes, are probably those values reported by Smallman and Green6 who applied the Siems correction (1961) to data obtained by Howie and Swann.3 These values shown in Fig. 1 give an extrapolated value of approximately 70 ergs per sq cm for pure copper. In the present work, Fullman&apos;s method for determining the stacking-fault energy of copper was extended to the a brasses. High-purity copper (99.999 pet) and high-purity zinc (99.999 pet) were mixed in proportioned amounts and melted in sealed and evacuated quartz tubes. The alloys were homogenized for a week at 750°C and chemically analyzed by means of X-ray fluorescence. These alloys, along with a specimen of pure copper, were rolled to 98 pet reduction and a thickness of 0.009 in., resealed, and annealed for 40 hr at 715°C. Values for the ratio of twin-boundary energy to the grain-boundary energy, it gb, were obtained from measurements of dihedral angles formed at the intersections of twin boundaries and grain boundaries by using Fullman&apos;s2 mechanical analogy of surface tensions acting at the intersection of an annealing twin and a grain boundary. The angles between the twin traces and the grain boundaries were measured for a large number of twin-grain boundary intersections at a magnification of X500 using a rotating mechanical stage on a Reichert metallograph. The rotary stage has a calibrated angle scale with vernier so that measurements can be made to 0.1 deg. The mean twin-grain boundary energy and standard deviation were calculated for copper and each of the brasses by the use of an IBM 7072 computer. It was found that the mean value of gb stabilized after approximately 100 twin-angle measurements. This was determined by plotting the mean against the number of angles measured. Since the measured angles deviate from true dihedral angles, a correction factor for grain orientation, discussed below, was applied. The stacking-fault energy was then calculated from these values and the values of grain-boundary energy derived by Taylor.7 The data obtained are tabulated in Table I. Values for stacking-fault energy are plotted in Fig. 1. The value of gb for the specimen of 1.03 pet Zn is close to the value obtained by Fullman2 for OFHC (99.98 pet) copper, 0.045. It is believed that the purity of the copper affects gb significantly. The 99.999 pet purity Cu used in this investigation yielded a value of yt/ygb, 0.76, which is much higher than that obtained by Fullman. Additional evidence suggesting that the purity of

Jan 1, 1965

By G. R. Speich, Morris Cohen

The growth rate of bainite has been determined by hot-stage metallography in five hypereutectoid high-purity iron-carbon, iron-carbon-chromium, and iron-carbon-nickel alloys. The studies have been confined essentially to lower bainite. The growth rate is independent of time at constant temperature, but both the edgewise and sidewise growth rates increase with increasing temperature. Increasing the carbon content, or adding chromium or nickel, decreases the growth rate without greatly affecting the temperature dependence. The results lead to separate diffusion-controlled models for the edgewise and sidewise growth rates. ALTHOUGH bainite has been subject of many detailed investigations,1,2 the growth mechanism of this intermediate transformation product of steel remains unclear. One difficulty has been that practically all the kinetic measurements have been restricted to studies of the overall reaction rate. Only a limited amount of information3, 4-6 is available on the growth process itself. The purpose of the present work was to investigate the effect of time, temperature and composition on the growth rate of bainite using hot-stage metallography. This method makes it possible to observe continuously the isothermal growth of individual bainitic units because of the surface upheavals accompanying their formation.3 This information is needed to test the existing growth models and to obtain a better understanding of the factors controlling the bainitic transformation. EXPERIMENTAL PROCEDURE Alloys—The compositions of the alloys used in the present work are shown in Table I. The five alloys were vacuum-melted and cast, and were prepared from high-purity materials. The three iron-carbon alloys were available from the work of Roberts et al.7 in the form of 3/8-in. diam rods.* To facilitate machining, the rods were ing. The rods were then tempered for 3 hr at 650°C to allow machining. The iron-carbon alloys in Table I were selected for investigating the effect of carbon on the bainitic growth rate. Due to the rapidity of the transformations involved, it was not feasible to measure the growth rates in iron-carbon alloys having carbon contents much less than 0.9 pct C. The iron-carbon-chromium and iron-carbon-nickel alloys were selected to study the influence of chromium and nickel on the growth rate at a carbon level of about 1.1 pct C, since this carbon content was intermediate among the iron-carbon alloys. The concentrations of chromium and nickel were chosen to match isothermal trans formation diagrams in the literature.8&apos;9 Hot-Stage—Since the iron-carbon alloys had such low hardenabilities, it was necessary to quench the hot-stage specimens drastically from the austentiz-ing temperature to the isothermal transformation temperature to prevent the formation of pearlite or proeutectoid constituents. A rapid-quenching metal-lographic hot-stage was built for this purpose. A maximum temperature of about 1100°C and quenching rates up to 500°C per sec could be attained with this equipment. The details of the apparatus are described in a recent publication. After being polished and mounted on the hot-stage, the specimen (0.020 in. thick) was protected from oxidation and decarburization during austenitizing by a vacuum of 10-4 to 10-5 mm. The quench to the reaction temperature was accomplished with a helium blast, and the isothermal run at this temperature was conducted in a helium atmosphere. A fine-wire thermocouple spot-welded to the sample and a high-speed

Jan 1, 1961

By Donald E. Grimes

In conjunction with Inland Steel&apos;s development of lead-bearing steels possessing improved machin-ability because of tellurium and/or selenium additions, it was decided to determine liquidus and solidus temperatures in the Pb-PbTe-PbSe sub-ternary system. With the exception of alloys in the PbTe-PbSe system, it is believed that no previous study of this subternary has been performed. Thermal analysis was employed in a general survey of the subternary. In addition to PbTe, PbSe, and pure lead, ten ternary compositions were selected at intervals of ten at. pct. Sixty-gram alloys were prepared by sealing an appropriate mixture of the elements in quartz crucibles with a central thermocouple-well under a vacuum of less than 10 p. All three elements were 99.999+ pct pure with only trace impurities detected by spectroscopic examination. After the alloys had been heated at least 20°C above the liquidus in a Kanthal furnace, cooling and heating curves were obtained. Two or more cooling curves were employed both for the determination of each alloy liquidus and for the solidus of those al- loys containing greater than 50 at. pct Pb. Cooling rates were 0.5° to 3.5°C per min during the 5 min immediately prior to the start or end of solidification. For those ternary alloys containing 50 at. pct Pb, the solidus was determined from heating curves. Temperatures were measured with a Pt/Pt-10 pct Rh thermocouple which was calibrated in the same apparatus against the freezing points of zinc (A. D. MacKay—99.999 pct), antimony (A. D. MacKay-99.999 pct), and copper (ASARCO—99.999+ pct) both before and after the experimentation. The only interruptions in the continuous strip-chart recording of the temperature occurred for brief periods at significant points of interest when direct readings were made with a Rubicon Type B potentiometer sensitive to * 1 µv. The average liquidus and solidus temperatures obtained in this investigation are listed in Table I together with probable errors based on the accuracy of the thermocouple calibration and the reproduci-bility of the data. No chemical analyses of the alloys were performed because the synthetic or as-charged compositions were felt to be reliable. The melting points obtained for PbTe (924.7° ± 0.7°C) and PbSe (1084.0° ± 0.6°C) compare favorably with recent findings of other investigators.&apos;-&apos; As indicated in Table I, both the liquidus and solidus temperatures increase as selenium replaces tellurium for a constant atomic percent lead. As a result, the ternary liquidus and solidus temperatures for a given percent lead lie between the corresponding binary temperatures published in the literature. It should be noted that those ternary alloys containing 50 at. pct Pb exhibit a relatively narrow liquid-plus-solid region (<80°C) when compared with alloys containing greater than 50 at. pct Pb. Alloys with 60, 70, or 80 at. pct Pb not only have a much wider liquid-plus-solid region (>500°C) but also exhibit considerably lower and approximately constant solidus temperatures which thus form a virtually isothermal solidus "plane" slightly below the melting point of pure lead (327.3°C). For these alloys

Jan 1, 1965

By Caudle B. H., Cooper H. E. Jr., O. K. Kimbler

The results of studies of areal sweepout behavior in nine-spot injection patterns are presented in this paper. The ratio of the production rates of the two types of producing wells in a nine-spot pattern is considered in its effect on breakthrough. A model study was used to develop a method to predict the production histories of both side and corner wells and to develop the production history of the pattern or the field. INTRODUCTION The importance of areal sweepout behavior in injection operations has been recognized for a number of years. We now know that the fraction of a reservoir which will be reached by an injected fluid is a function of the geometric arrangement of the production and injection wells and of the mobility ratio of the fluids. Of these two, the mobility ratio (which is a measure of the relative ease with which the oil and the injected fluid can move through the reservoir) appears to have the greatest effect on recovery. The effect of mobility ratio on production history has been reported for most of the dispersed injection patterns (i. e., five-spot, staggered and straight-line drives).4-6 ere has been very little published on the nine-spot injection pattern. This may be because the two types of producing wells in the nine-spot pattern can—and sometimes should —be produced at different rates. This adds a second variable (the fist being mobility ratio) to be covered in a study of the nine-spot flooding network. Muskat1 has reported the sweep pattern efficiency at breakthrough for a mobility ratio of one at various ratios of producing rates for the two types of wells. For these conditions he found maximum oil production at breakthrough to occur when the corner well (the producing well farthest from the injection well) is produced 10.7 times as fast as the side well. Other investigatorsa2,3 have studied a few of the many possible operating conditions possible with this injection pattern. This paper presents the results of studies which are strictly applicable to a nine-spot injection pattern surrounded by other nine-spots in a homogeneous reservoir and which has no flowable gas present (no oil bank is formed). Although the full ranges of the variables mentioned above have not been covered, the results reported here should allow reasonable estimates of field operations to be made. EXPERIMENTAL The well spacing geometry of the nine-spot pattern is shown in Fig. 1. Here we see that each injection well is surrounded by eight production wells arranged in a square. Four of these producing wells are located at the corners of the square; the other four are in the midpoints of the four sides. These two types of producing wells are called "comer wells" and "side wells" respectively. It is the ratio of the producing rates of these two types of wells that affects the breakthrough recovery, as calculated by Muskat.&apos; This ratio is defined as the total producing rate of a corner well divided by the total producing rate of a side well. The model used in this study represented one-eighth of a nine-spot pattern, as shown in Fig. 1. It contained the equivalent of one-fourth of a side well, one-eighth of a comer well, and one-eighth of an injection well. Because of these proportions, the actual producing rate ratios in the model were one-half of the ratios of producing rates as

Jan 1, 1965

By Harvey T. Kennedy, Charles R. Olson

In many investigations of the performance of petroleum reservoirs the assumption is made that the liquid, if below its bubble-point pressure, is at all times in equilibrium with gas. On the other hand, observations by numerous investigators have indicated that gas-liquid systems including hydrocarbon systems, may exhibit supersaturation to the extent of many hundred psi in the laboratory. Up to the present, there has been no reliable data on which ti judge the actual extent of supersaturation under conditions approaching those existing in petroleum reservoirs. The work reported here deals with observations and measurements on mixtures of methane and kerosene in the presence of silica and calcite crystals. Bubbles were observed to form on crystal-hydrocarbon surfaces in preference to the glass-hydrocarbon interface or to the body of the liquid. Statistically, it was found that the number of bubbles formed per second per square centimeter of crystal surface was a function of the supersaturation only. and the function was evaluated graphically. Supersaturations were observed up to 770 psi, under which condition bubbles formed quickly and with considerable violence. With decreasing degrees of supersaturation, the frequency of bubble formation became less, until at 30 psi supersaturation and lower, no bubbles were observed to form, even though the observation at 30 psi was continued for 138 hours. It was found that silica and calcite crystals had identical effects, within experimental error, in accelerating the formation of bubbles, and that small amounts of water and crude oil had no effect on the results. It is shown that the maximum supersaturation that can exist in a reservoir may be calculated from the data presented and from the area of the rock surface. It is also shown that the number of bubbles formed in the reservoir, in order of magni- tude, may be calculated for any rate of pressure decline imposed on the reservoir by production. The bearing of the number and distribution of bubbles on reservoir performance is discussed. INTRODUCTION A liquid system is supersaturated with gas when the amount of gas dissolved exceeds that corresponding to equilibrium at the existing pressure and temperature. The degree of super-saturation may be conveniently expressed as the difference between the bubble-point of the mixture and the prevailing pressure. Thus, if a mixture having a bubble-point of 1,000 psi at a given temperature exists in single liquid phase at 700 psi at the same temperature. it is supersaturated to the extent of 300 psi. There are many examples of high supersaturations, mostly in aqueous solutions, reported in the literature. Thus, Kenrick, Wismer and Wyatt1 showed that water may be saturated with oxygen, nitrogen or carbon dioxide at 100 atmospheres, and the pressure reduced to one atmosphere without producing bubbles immediately. When liquids are in a state of tension, they may be considered as supersaturated at least to the extent of the tension. The tensile strength of water has been reported as 30 atmospheres by Meyer,1 60 atmospheres bv Budgett. 30 to 50 atmospheres by Temperley and Chambers,4,5 200 atmospheres by Dixon6. and 223 atmospheres by Briggs.7 Vincent8,9 determined the tensile strength of a mineral oil as 45 psi. Gardescu1 maintained pressures for short times in a model reservoir at 115 psi below the bubble-point. It should be noted that the high supersaturations observed were obtained on systems carefully purified to remove particles or surfaces which might promote the formation of bubble; These "nuclei" were considered as contaminants which interfered with the determination of a property of the liquid. In

Jan 1, 1952

By David J. Mack, T. V. Philip

The effects on the Cu-A1 eutectoid transformation of the addition of a third element from the second long period and from Group IIB of the periodic table, were studied by isothermal transfomation techniques. The valency of the third element shows the most pronounced effect on the eutectoid decomposition. With some exceptions, the atomic size factor of the third element shows some consistent effects on pearlite nucleation and growth. The atomic concentration or the electronegative valency of the third element shows wo consistent effect on the eutectoid decomposition. Addition of the third element helps spheroidization of pearlite. SINCE the pioneering work of Davenport and Bainl on the eutectoid decomposition in steel by the isothermal transformation technique, an enormous amount of data has been accumulated on the eutectoid transformation characteristics of commercial steels. While the eutectoid reaction in steel is of tremendous industrial importance, it appears to be quite unique among the eutectoid reactions. Though the metal-lographic structures developed in the Fe-C and Cu-A1 eutectoids are similar, it is now evident that the two eutectoid reactions are quite dissimilar. The eutectoid decomposition in the Cu-A1 system is more complicated partly due to the appearance of transitional phases in addition to the equilibrium phases. * The first isothermal studies of aluminum bronzes were made by Smith and Lindlief2 and later by Mack,3 Klier, and Grymko,4 and recently Hayne 5,6 A few other systems, structurally analogous to the above, have been studied by the same technique.7-10 Kasberg and Mack1&apos; studied the effects of iron on the transformation of commercial aluminum bronze. The effects of manganese and nickel on this aluminum bronze and those of iron, manganese, and nickel on the binary Cu-A1 eutectoid have been recently studied.12 The object of the present investigation was to study, by isothermal transformation techniques, the effects (with respect to the fundamental factors of alloy formation) of the addition of a third element on the transformation of a Cu-Al eutectoid alloy, 11.8 pct Al. The third elements chosen for the purpose were silver, cadmium, indium, tin, and antimony from the second long period, and beryllium, zinc, and cadmium from group 11B of the periodic table. They were added in nominal amounts of 0.5, 1.0, and 2.5 pct by weight to a eutectoid Cu-A1 alloy. These third elements were expected to show the effects of electron valency, atomic size factor, and electronegative valency effects on the binary eutectoid transformation. PFLEPARATION OF ALLOYS AND PROCEDURE All alloys were made as 400-g heats by induction melting in a graphite crucible with a graphite lid. The molten alloy with a layer of graphite powder on top was stirred at regular intervals by a graphite rod. When the melt was judged to have acquired sufficient superheat, a pinch of common salt was sprinkled on top and any crust scraped off to one side. It was then chill cast into a 5/8 in. rod. The alloys with silver were prepared by remelt-ing the high-purity Cu-A1 eutectoid alloy used by Mack3 with high-purity silver (99.99 pct pure from Hardy and Harmon, Inc.). In the preparation of all the other alloys, polished electrolytic copper shot (from Belmont Smelting and Refining Co.) and high-purity aluminum (99.99 pct pure from Aluminum Co. of America) were used.

Jan 1, 1962

By R. J. Stokes

This paper compares the room-temperature mechanical behavior of magnesium oxide crystals containing &apos;fresh&apos; and &apos;grown in&apos; sources. &apos;Fresh&apos; dislocation sources introduced by cleavage or mechanical contact move and multiply to generate slip bands at 3000 psi. Macroscopically the crystals yield smoothly at 6000 psi and can be quite ductile. When &apos;fresh&apos; sources are eliminated by chemical polishing the crystals have to rely on &apos;grown in&apos; sources to initiate slip. They then deform elastically up to extremely high stresses (-30 to 50,000 psi) yielding with a sharp stress drop down to the level at which Ifresh&apos; sources operate. Grown in&apos; sources are considered to be associated with impurity wecipitate particles or inclusions. Annealing crystals at 2000°C dissolves these particles thereby eliminating sources for slip. The crystals then become consistently stronger (> 70,000 psi) approaching within 1/10 of the theoretical strength. Dislocations of the grown-in network do not move under stress to nucleate slip. It is proposed that they are locked electrostatically. DISLOCATIONS were originally conceived to resolve the large discrepency between the theoretical and real strength of solids. The idea that slip propagates by the movement of dislocations is now well confirmed both by electron transmission and etch pit studies. But this by itself is not sufficient to explain the low yield strength of crystals for there is still the need to understand where slip dislocations originally come from. Theoretical estimates place the stress to generate dislocations homogeneously in the lattice at approximately 1/30 of the shear modulus,&apos; a value 104 to 105 times greater than the stress at which the very first manifestations of plastic deformation have been observed. Only an special cases can the theoretical strength be approached; in crystals of high perfection such as whiskers2 where dislocation sources do not preexist and in covalent crystals where the dislocations present at room temperature are almost completely immobilized by the bond character of the solid.3,4 For the most part it is necessary to assume that the yield strength of ionic and metallic solids corresponds to the motivation and multiplication of dislocation sources present beforehand. The question as to their origin appeared to be answered by the suggestion of Frank and Read5 that dislocations forming part of the grown-in structure could operate as a mill for the large scale production of dislocations. The Frank-Read mechanism is still widely accepted as the source of dislocations but a number of observations have been reported which are in serious disagreement with it. One of the most intriguing of these is that under normal testing conditions dislocations of the grown-in network appear to play no role in the plastic deformation of rock salt structure ionic solids. This was first reported in the etch pit studies on lithium fluoride by Gilman and Johnston6 and is true also for magnesium oxide. To explain the comparatively low yield stress of lithium fluoride it was proposed by a number of authors7,9 that small unresolved prismatic loops formed by vacancy condensation were acting either directly or indirectly as the dislocation sources. This proposal led Gilman10 to perform a series of detailed and careful experiments on lithium fluoride to try to identify the sources responsible for the initiation of slip. He concluded that prismatic loops played no general role and that other sources were more important. Dislocation sources in ionic crystals can be divided into two general categories. First, there

Jan 1, 1962