Search Documents

By W. C. Hagel, J. H. Westbrook

THERE has been a recent revival of interest in the intermetallic compound AgMg as an experimental material for study of the physical and chemical properties of simple ordered structures. Studies of mechanical behaviors,1-4 diffusion,5,6 and thermo-dynamic properties7'8 have been reported. In several of these studies, heat treatments have been carried out in argon-filled silica capsules at temperatures as high as 750°C with no apparent adverse effects. The present authors were, therefore, startled to discover in the course of some yet unpublished work, that gross melting of near-stoichio-metric AgMg compositions occurred in such samples more than 100 deg below their melting point of about 800°C. This note is to report a brief series of experiments carried out to establish the reason for this behavior. Gross errors in sample composition and failure of furnace temperature controls were quickly eliminated as causes of melting. The first tangible lead came from chemical analysis of an AgMg sample which had melted during treatment at 750°C. A silicon content of 3.3 wt pct was found. Since satisfactory analyses had been obtained on the original as-cast ingot, contamination by diffusion and/or reaction with the fused silica capsule seemed a distinct possibility. A perplexing fact, however, was the apparently capricious incidence of the effect. Not only was it previously unknown, even in the experience of the present authors; but, in the early part of the present study, melting sometimes occurred and sometimes not with specimens treated under constant conditions. Indeed, one sample successfully survived a 750°C heat treatment and yet melted completely during the course of a subsequent anneal in an identical capsule at a lower temperature. To obtain evidence that silicon contamination could lower the melting point to the extent observed, the following experiment was performed. A series of ternary alloys was made up with a stoichiometric AgMg base and containing 0.1, 0.2, 0.4, 1, 2, and 4 wt pct Si. Melting was done in MgO crucibles under a cover of argon gas. After holding 10 to 20 min in the temperature range 850° to 900°C, the alloys were allowed to solidify in the crucible and the temperature during cooling automatically recorded with a Pt/Pt-10 Rh thermocouple. Results from the cooling curves are shown in Fig. 1. Checks within 2 to 5C° were obtained upon repeated melting, cooling, and freezing. The whole series of cooling curves as well as metallographic examination of the melted alloys established that the AgMg rich portion of the AgMg-Si quasibinary is an eutectic-type system. The melting point of AgMg is lowered from approximately 820°C in the pure stoichiometric binary9 to about 710°C in the saturated intermetallic phase. Since second phase was observed in all samples on cooling to room temperature, the solid solubility of AgMg for silicon evidently falls rapidly with decreasing temperature as indicated schematically by the dashed solvus in Fig. 1. It is thus established that a silicon content

Jan 1, 1963

By Charles Luner

ALTHOUGH the kinetics of the atmospheric oxidation of tin have been studied,1-3 the kinetics in pure oxygen have not been reported. This note presents some results of the kinetics of the oxidation of tin foil in pure oxygen. The tin foil used in this investigation was 99.78 pct pure, the two major impurities being Pb (0.17 pct) and Sb (0.024 pct). The foil was degreased and air-dried prior to oxidation. The air-formed film was estimated by coulometric reduction4 of the surface oxides to be about 25A. The samples, which were in strip form and had a total geometric surface area of about 300 sq cm, were first evacuated at room temperature in an oxidation bulb to 1 X 10 -5 mm Hg and subsequently degassed for 1 hr at the temperature of the experiment. Spectroscopically pure oxygen was then introduced into the bulb. The rates of oxidation were measured by following the rate of pressure change due to oxygen consumption in a closed system, the volume of which was sufficiently large so that the pressure change during an experiment was 10 to 15 per cent of the total pressure. An oil-mercury manometer,5 with a sensitivity of 3 X x mm Hg (which corresponds approximately to 5 X 10 -7 gm of oxygen) was used to measure the pressure change. The oxidation bulb was heated by an oil-bath and controlled to within -10.3 C. The reproducibility of the rates was good, as determined by the coincidence of rates at 190oC for duplicate experiments. Fig. 1 shows the oxidation curves in the temperature range 168 to 211.5oC at 8 mm Hg pressure. The effect of pressure on the rate of oxidation at 190°C is also shown. The rate of oxidation was not markedly affected by changes in pressure in the range 4 to 9 mm Hg, except perhaps at the lowest pressure, 4 mm Hg, where after about 70 min there appeared to be a decline in the rate, as compared with the rate at the higher pressures. At the lower tem- perature, 168oC, and for short reaction times, it is difficult to distinguish between a linear relationship and a slight curvature in the oxidation rate. However, for longer times, there was a somewhat larger indication of curvature. The samples after oxidation were gold-colored in appearance. The oxide that was formed at 170°C was identified as a-SnO by reflection electron diffraction. This is in agreement with results obtained by other workers.6, 7 The rate data best fitted the logarithmic-oxidation rate law, w = K1n ln(1 + -t/to) [1] where w is the weight of oxygen consumed, t is the time, and K In, and to are constants. First estimates to were obtained according to the method of Taylor Thon8 and were then employed to obtain the best simuItaneous estimates of to and K In, that would fit the logarithmic expression. These estimates were found numerically, so that the residual variance could be minimized. The calculations were performed on an

Jan 1, 1961

By Dwight K. Smith

A new pozzolanic composition has been developed for cementing oil wells where moderate to high temperatures prevail. This material is an entirely different concept to other oil well cementing materials, such as portland cements, cements containing additives, or liquid resins. Its characteristics are such that it is not, at present, recommended for use at temperatures less than 140º F. It can he either accelerated or retarded across a wide range of well conditions. This new cement is composed of a pozzolanic material, hydrated lime, and a chemical activator to give it early initial strength. This material can be used in wells from 6,000 to 18,000 or more feet where temperature conditions are similar to those along the Gulf Coast. This cement, when set, has no soluble portion subject to leaching or any compounds that should be attacked by sulfate waters or brines. For this reason, it should be permanent when placed adjacent to formations carrying any type of fluid. The compressive strengths in 24 hours are more than adequate for wells where temperatures are 140°F and higher. These values ore in excess of many other types of cementing composition presently in use in the field. This pozzolanic composition does not retrogress in strength at high temperatures as do some other types of cementing materials. The slurry weights of this material will vary slightly according to the specific gravity and water requirements of the pozzolnn itself. The materials covered herein will mix from 13.5 to 14.3 lb/gal, and will have a waiting-on-cement time comparable to other materials used under the same conditions. Economically speaking, this composition is less expensive than either portland cements or retarded cements presently being used under deep well conditions. INTRODUCTION Pozzolans are siliceous material which, though not cementitious in themselves, contain constituents which at ordinary temperatures will combine with lime in the presence of water to form compounds which have a low solubility and possess cementing properties. The use of pozzolanic materials dates back many hundreds of years and both the ancient Greeks and Romans were aware that certain volcanic deposits, if finely ground and mixed with lime and sand, yielded a mortar which possessed special properties. Generally, the early strengths of such materials were rather weak and were considered insufficient for modern commercial usages. Pozzolanic materials have been used extensively with portland cement in mass concrete to obtain special properties. In recent years, large quantities of certain pozzolanic materials have been used successfully admixed into portland cements for oil well cementing. Pozzolans, being reactive silicates, will combine with the free lime that is an inherent component of set portland cements and thereby. becomes cementitious themselves. POZZOLANS FOR OIL WELL CEMENTING There are many types of pozzolans, some of which are more reactive than others. The quality of the pozzoIan depends on the degree of reactivity, chemical composition, fineness, and other less well understood factors. Some of the more widely accepted pozzolans are those classified as fly ashes, while others are certain materials of volcanic origin. pozzolans which require large vol-

Jan 1, 1957

By Kenneth Cottingham

The number of wells completed in Ohio during I940 was about 20 per cent more than during the preceding year, the comparative totals being 1020 and 1228. Of the 1940 completions, 327 were oil wells, 491 gas wells, and 410 dry. The completions for the past five years, divided into oil wells, gas wells, and dry holes, are shown in Table 2. Wells drilled deeper and input wells in water-flood areas are not included in the tabulation. The annual production of oil has decreased steadily in Ohio from the maximum of 23,941,000 bbl. produced in 1896. Table 3 shows the quantities of oil produced in the last five years. In 1940, the total was 3,052,000 bbl., produced by about 25,500 wells. The number of wells and the approximate quantities by grades are shown in Table I. Table i ,—Tabulation by Grade Grade 1 2 Barrels __________________________________________________________________________________________ Pennsylvania ............. . 1,198,000 Lima.................... . 325,000 Corning................... 3,730 1,159,000 Lodi...................... T,040 350,000 Cleveland................. 30 1:1,000 Total................... 25,500 3,052,000 The prices paid for Ohio crude oil in 1940, together with dates of changes in posting, are shown in Table 4. The production of natural gas in 0hio has declined from a maximum of 79,510,032 M cu. ft. in I9I5 S to 36,469,000 M cu. ft. in 1939, the most recent year for which a figure is available. Consumption reached its peak in Ohio in the year 1916, when it was 169,480,01r M cu. ft., declining to 114,720,ooo M CU. ft. in 1939. The produc-tion and consumption of natural gas in Ohio for the past five years are shown in Table 5. TAble 2.—Completions in Ohio during Past Five Years Numbs of Wells Drilled during Year YearI, ] Oil Gas Dry Total 1936............. 263 570 324 1,157 1937............. 317 503 45I 1,271 1938............. 189 433 288 gro 1939............. I70 501 349 1,020 19391940............. 327 491 410 1,228 Total.......... 1,266 2,498 1,822 5,586 Table 6 shows the number of oil wells and the number of gas wells completed by sands during 1940, with the average initial production per well for each sand. Table 7 shows the total number of wells drilled—oil, gas and dry—by sands. Development during 1940 Szth-Trenton.—For several years, considerahle interest has been shown in a horizon lying some 500 to 700 ft. below the top of the Trenton, known to the driller in western Ohio as the "green sand," and in eastern Ohio as the St. Peter. In 1939, ten 'lgreen sand" tests were drilled, all in western Ohio and all dry- In 19401 eight wells were drilled to this horizon, one of which was a small oil well (one barrel) in Men county- Of the remaining seven—all of which were dry-—one in Franklin County, in central Ohio, was drilled to a depth of 2903 ft. .Another was in Medina

Jan 1, 1941

By R. M. Brick, J. T. Richards

Tests have been conducted to determine the mechanical properties of several beryllium copper alloys down to liquid air temperatures. The materials investigated include beryllium copper, beryl-lium-cobalt-copper, and beryllium-zinc-copper in the wrought and cast conditions. As a means of evaluation, the influence of cold work and age hardening treatment upon subzero behavior has been observed. The effects of temperature upon both elastic and plastic deformation are also considered. THE low temperature mechanical properties of beryllium copper are of current interest in view of the increasing number of subzero applications. At extremely low temperatures, beryllium copper components are employed in temperature control and gas liquefaction equipment. At more moderate temperatures, such as those encountered in arctic regions, these alloys find use in a wide range of civilian and military applications. Although several previous subzero investigations have included beryllium copper,'-' none have been complete with respect to test temperatures or materials employed. As indicated in Table I, the alloy: used by Colbeck and MacGillivray,1 Walle,2 and Kostenets' were nonstandard and were not representative of present commercial practice. In addition, Kostenets4 did not test age hardened specimens, while the temperature in the other investigations", "-' were not carried below —100°F. These tests, however, indicate that beryllium copper offers interesting possibilities in subzero atmospheres, since the increase in strength with decreasing temperature is not accompanied by a reduction in ductility or impact resistance. As a means of checking and extending this earlier work at subzero temperatures, an investigation was undertaken at the University of Pennsylvania. In addition to testing the standard 2 pct beryllium copper, other alloys were also considered in wrought and cast forms. Charpy impact and tension tests were included with particular emphasis on the elastic characteristics, since beryllium copper is frequently selected for its spring qualities. Nominal test temperatures were +80°, —75", —200°, and —300°F. Test Materials Wrought beryllium copper, beryllium-cobalt-copper, and beryllium-zinc-copper specimens were machined from 0.560 in. diameter rod. These alloys were tested in the solution treated, cold drawn, or age hardened conditions. In the case of solution treated beryllium copper, some specimens were aged (3 hr at 600°F) for maximum hardness and others were overaged (1 1/2 hr at 750°F) to determine the effect of heat treatment. The compositions and average room temperature properties of these wrought alloys are presented in Table 11. The casting alloy versions of beryllium copper and beryllium-cobalt-copper were prepared as sand-cast cylinders, roughly 3/4 in. diameter x 6 in. long. Test specimens were machined from these cylinders. Conditions tested included as cast as well as solution treated and age hardened. Table 111 lists compositional and room temperature property data for the cast alloys. Test Methods Tension tests were conducted on specimens having a 0.25 in. diameter reduced section over a 1 in. gage length. To insure axiality, specimens were loaded by means of hardened chains. The yield strength at 0.2 pct offset was obtained from autographically recorded stress-strain curves resulting from a spe-

Jan 1, 1955

By Kendall E. Born

Production of crude oil in Tennessee during 1940 was slightly more than 15,000 bbl., a decrease from 1939 of about 36,000 bbl. This sharp decline has been caused largely by curtailed activities in the shallow pools in Clay County, where approximately 3000 bbl. was marketed off the lease during the year as against more than 37,000 bbl. in 1939. The flashy production found in 1938 in the Celina area has been short-lived and the area is essentially abandoned. Failure to find steady production has been the major factor retarding developments in the northeastern Highland Rim area. The Mississippi lime production in Scott and Morgan Counties continued to show a steady decline. The Tennessee production by counties is shown in Table I. Table i.—Oil Production in Tennessee it1 1940 Production. Bbl. Number of County Wells Pumped 1939 1940 Scott............ 4 4,332 3.596 Morgan.......... I: 6,479 5,751 Fentress.......... 3 I,2XX 1,5xz Pickett........... 1 1.2XX Clay............. 8 37.200 3,XXX Developments There were 32 wells spudded in during 1940, four of which were drilling or only temporarily suspended on Dec. 31, 1940. Twenty-eight wells were completed during the year, four of which were commercial producers. The total footage drilled was 3I,214 ft. The more important wildcats are listed in Table 2; the distribution of 1940 oil and gas tests according to physiographic divisions is given in Table 3. Cumberland Platenu.—Thcre was one completion in the coal area of the state, a test that attempted to extend the Mississippi lime production in the Coon Hollow pool to the southeast in Morgan County. This test encountered only slight shows of oil in the producing horizons of the near-by Coon Hollow and Boone Camp pools. Some surface work was carried on by private interests during the year in Scott and Morgan Counties and two wells were spudded in early in 1941 The revival of interest in the Kentucky portion of the plateau will probably result in increased activity in this part of Tennessee during 1941. Several sizable blocks of acreage, some by major oil companies, are held in Scott, Morgan, and Cumberland Counties. Middle Tennessee.—The northeastern Highland Rim continued to be the most active area in the state with 20 completions, although this figure is about one third of the number drilled in 1939. Four oil wells, none with initial productions of more than I00 bbl., were completed in Clay, Fentress, and Pickett Counties. The producing horizons discovered in Pickett and Fentress Counties were in the "Sunny-brookJ' pays of Trenton age. The Clay County producer was an old test drilled deeper in which oil was found at 671 ft. in the upper part of the Stones River group of limestones, a common pay in this area. All four wells were drilled in or close to old shallow production. Deeper testing into the Knox dolomite group in this area was not particularly encouraging, although one well in Fentress County encountered some saturation at 1860 to 1869 ft. in the upper

Jan 1, 1941

By Kendall E. Born

Production of crude oil in Tennessee during 1940 was slightly more than 15,000 bbl., a decrease from 1939 of about 36,000 bbl. This sharp decline has been caused largely by curtailed activities in the shallow pools in Clay County, where approximately 3000 bbl. was marketed off the lease during the year as against more than 37,000 bbl. in 1939. The flashy production found in 1938 in the Celina area has been short-lived and the area is essentially abandoned. Failure to find steady production has been the major factor retarding developments in the northeastern Highland Rim area. The Mississippi lime production in Scott and Morgan Counties continued to show a steady decline. The Tennessee production by counties is shown in Table I. Table i.—Oil Production in Tennessee it1 1940 Production. Bbl. Number of County Wells Pumped 1939 1940 Scott............ 4 4,332 3.596 Morgan.......... I: 6,479 5,751 Fentress.......... 3 I,2XX 1,5xz Pickett........... 1 1.2XX Clay............. 8 37.200 3,XXX Developments There were 32 wells spudded in during 1940, four of which were drilling or only temporarily suspended on Dec. 31, 1940. Twenty-eight wells were completed during the year, four of which were commercial producers. The total footage drilled was 3I,214 ft. The more important wildcats are listed in Table 2; the distribution of 1940 oil and gas tests according to physiographic divisions is given in Table 3. Cumberland Platenu.—Thcre was one completion in the coal area of the state, a test that attempted to extend the Mississippi lime production in the Coon Hollow pool to the southeast in Morgan County. This test encountered only slight shows of oil in the producing horizons of the near-by Coon Hollow and Boone Camp pools. Some surface work was carried on by private interests during the year in Scott and Morgan Counties and two wells were spudded in early in 1941 The revival of interest in the Kentucky portion of the plateau will probably result in increased activity in this part of Tennessee during 1941. Several sizable blocks of acreage, some by major oil companies, are held in Scott, Morgan, and Cumberland Counties. Middle Tennessee.—The northeastern Highland Rim continued to be the most active area in the state with 20 completions, although this figure is about one third of the number drilled in 1939. Four oil wells, none with initial productions of more than I00 bbl., were completed in Clay, Fentress, and Pickett Counties. The producing horizons discovered in Pickett and Fentress Counties were in the "Sunny-brookJ' pays of Trenton age. The Clay County producer was an old test drilled deeper in which oil was found at 671 ft. in the upper part of the Stones River group of limestones, a common pay in this area. All four wells were drilled in or close to old shallow production. Deeper testing into the Knox dolomite group in this area was not particularly encouraging, although one well in Fentress County encountered some saturation at 1860 to 1869 ft. in the upper

Jan 1, 1941

By Y. H. Liu, R. Kiessling

The chromium, iron, and tungsten borides have been treated with ammonia at different temperatures. They are attacked, forming metal nitride and boron nitride, and the results are summarized in the tables. In the tungsten-nitrogen system a new phase has been observed, closely related to the known ß phase. THE present investigations were begun to determine whether any ternary phases exist in the transition metal-boron-nitrogen systems for the metals chromium, iron, and tungsten. Attempts to prepare such phases were made by using the borides of the metals as starting materials and ammonia as the nitriding agent. Although no new ternary phases have been found to exist, the results may be of some interest with regard to the technical use of the borides. General Procedure A steady stream of dry ammonia was passed through a silica reaction tube, the central part of which was kept at the reaction temperature while its ends were water-cooled. Weighed amounts of the borides were placed in a silica or porcelain boat and heated at different temperatures for a period of 10 to 24 hr. The boat was then rapidly removed from the reaction zone to the quenching zone, the water-cooled end of the tube, by means of a simple magnetic device. The nitrogen content of the products was determined by the increase in weight of the specimens, and the phase analysis was carried out by X-ray methods. For this analysis a Guinier-type camera, constructed at this Institute, was used with a bent, ground quartz crystal monochromator. The general reaction, which occurred in all the experiments, may be summarized as: metal boride + nitrogen -* boron nitride + metal nitride For the higher temperatures pure metal was formed instead of metal nitride. It is sometimes difficult to Discussi detect boron nitride among the reaction products by X-ray methods. Prolonged exposures of some specimens showed, however, that the strongest reflections of boron nitride were present. Additional evidence for its presence was given by the increase in weight of the specimens after nitriding. This increase was always greater than that corresponding to nitride formation only and was often in close agreement with the formula given above. Finally, a white powder, which was shown by X-ray methods to be boron nitride, was left if the reaction products after nitriding Fe,B at 448°C and FeB at 768°C were dissolved in diluted sulphuric acid. Ch rom iu m - Boron - N itrogen Five phases have been found to exist in the Cr-B system,' , and all were used as starting materials. Investigations on the Cr-N system have shown the existence of two nitrides with ideal composition Cr,N and CrN.".' * The results are summarized in Table I. All the borides are attacked and decomposed into chromium nitride and boron nitride, and the kind of nitride formed depends only on the temperature and not on the boride used as starting material. The lowest reaction temperature, however, is different for the different borides. Thus the 6 phase begins to react at about 735 "C, the r phase at about 800°, the S phase at about 900°, the 7, phase

Jan 1, 1952

By J. Trevor Eyton

This paper addresses some of the financial risk hedging mechanisms available to a corporation contemplating entering the mining business at a significant level of investment. The approach which I have adopted is that of a case study relating to the risk hedging aspects of Brascan Limited's acquisition of 46% of Noranda Inc., formerly Noranda Mines Limited, followed by some remarks on options open to mining companies for reducing financial risks. To appreciate the rationale for Brascan committing over (Can.) $800 million to the natural resource sector, some knowledge of Brascan's parent company, Edper Investments Ltd., is required at the outset. Edper Investments, prior to acquiring a 48% interest in Brascan, controlled Trizec Corporation, one of the world's largest property companies. Edper also was involved in the financial services sector through Continental Bank of Canada and Hees International Corporation. For some considerable time prior to Edper's investment in Brascan, Edper felt a need to provide a better balance to its portfolio of property and financial services. Brascan was rich in cash, relatively unleveraged, and with important existing holdings in natural resources and consumer products. The acquisition of a controlling interest in Brascan provided an opportunity to balance Edper's portfolio of property and financial services with world class acquisitions in natural resources, supplemented by consumer products and financial services. The end result of Brascan's activities over the last few years is illustrated by the following analysis of the book value of Brascan's assets at the end of December 1983. [Can.$% Millions _ Natural Resources81748 Consumer Products 654 38 Financial Services 157 9 Other Operations895$1,717100% ] Source: Brascan 1983 Annual Report. The large emphasis on natural resources came about from the fact that for Canadians operating mainly in Canada, natural resources were attractive. We were impressed by Canada's position in the world natural resource industry as illustrated by some of the following statistics: [CommodityCanadian Estimated Production In 1983 As % of World Total Newsprint 30 Potash 21 Uranium 18 Molybdenum 17 Zinc 17 Pulp 16 Nickel 16 Saw Logs 11 Silver 8 Copper 7 Lead 6 Gas 5 Oil3] Source: U.S. Bureau of Mines and Brascan estimates. In addition, the quality of Canada's reserves looked good to us. The polymetallic nature of many of Canada's orebodies offered a hedge against risk relating to any one metal. Put another way, the by-product metal credits offered a net operating cost advantage with respect to many of the metals mined. Our energy costs also appeared to provide Canada's natural resource industries with an advantage. We considered Canadian mining expertise as amongst the world's finest, as were the exploration equipment and technology developed in Canada. In addition, Canada offered a stable political climate and one we knew. Further, we felt the Canadian Government's future role in the industry would, on balance, be benign, partly because the Canadian content of the mining industry was very high in contrast to the petroleum industry. Granted, we could find cheaper sources of copper; however, to do so would involve venturing into regions where country risks were higher.

Jan 1, 1985

By W. C. Ellis, E. S. Greiner

METALLIC titanium has been prepared in small quantities since the beginning of the century. Hunter1 reported in 1910 that he obtained a malleable product of 99.9 pct purity by the reduction of the tetrachloride by sodium in a closed container. Later Van Arkel2 and Fast3 prepared small quantities of malleable titanium by thermal decomposition of titanium iodide. Another method for producing malleable titanium from tetrachloride was reported by Kroll4 who used magnesium as the reducing agent. More recently Dean, Long, Wartman, and Anderson5 working at the U.S. Bureau of Mines have reported the preparation of the metal on a pilot plant scale by the reduction of titanium tetrachloride by magnesium in an atmosphere of helium. Their product, which is malleable, was used in the present investigation. Early in 1948 after the work of this paper: was completed Campbell, Jaffee, Blocher, Gurland, and Gonser6 described the strength and working characteristics of pure titanium which was prepared by the iodide method on a scale producing 300 to 600 g per run, in the form of 0.3- to 0.4-in. diam rods. Their product is characterized by low hardness and large capacity for cold work which they attribute to a high degree of purity with respect to oxygen, nitrogen, and carbon. Titanium has a melting point of about 1725°C5 it may be classed as a light metal since the specific gravity is 4.5 g per cc-1. The crystal structure is close-packed hexagonal from room temperature t0 885°C. Above this temperature the structure is reported7 as body-centered cubic. The change in crystal structure has been associated with discontinuities in specific heat8 electric resistance9 and thermoelectric force10 at temperatures near 890°C. It is reported11 that annealed titanium has a tensile strength 0f 78,700 psi which can be increased by cold-work to 123,000 psi. In the present investigation, the lattice constants at room temperature, the thermal expansivity between 30 and 800°C, as well as the electrical resistivity and thermoelectric force against platinum between - 200 and 1000°C have been determined. MATERIALS For the measurements, two series of specimens were prepared from titanium furnished by the U. S. Bureau of Mines. The first was lade from an annealed sintered compact, 0.38 in. thick. Sections of the compact were cold-swaged with intermediate anneals in vacuum to the sizes used. Sizes over 0.25-in. diam were annealed at 1000°C and smaller sizes at 800°C. Specimens originating from the sintered compact are designated in this paper as A. The second series of specimens was lade from a rod of titanium, 0.19 in. in dial, which was cold-swaged with the necessary intermediate anneals to the required sizes. This series of specimens is designated B. The impurities in the specimens of titanium, determined by chemical analysis, are given in Table I. Oxygen and nitrogen which were not determined by analysis, are probably present although in small quantities in view of the ductility of the material.

Jan 1, 1948

By Edward E. Hicke, Charles A. Stickels

The dihedral angle of liquid-lead inclusions in solid nickel has been measured as a function of temperature from 371 to 816 C at zero pressure. and as a function of pressure up to 50,000 psi at 317 and 593 C. Thermodynamic expressions are derived for the temperature and pressure coefficients of interfacial tensions in this system. A method is presented for obtaining relative tempmature and pressure coefficients from dihedral-angle data, and the resulting values are used in conjunction with the thermodynamic relations to calculate excess properties of the solid-liquid interface. Defining the position of the solid-liquid interface by the condition that the excess concentration of lead is zero, the excess concentration of nickel and the excess entropy at the solid-liquid interface are: where y(593) is the interfacial tension of the nickel grain boundary saturated with lead at 593C and zero pressure. These values are considered reliable to within a factor of two. While similar calculations are not possible for the nickel grain boundary, it is shown that the expwimental results imply that the excess concentration of nickel at the boundary and the excess entropy of the boundary are negative. THE temperature and composition dependencies of interfacial tensions in metal systems have been reported by several authors in the last 15 years.'-' No measurements of the effect of pressure on inter- facial tensions in metals have been reported, although measurements made on nonmetallic gas/liquid and liquid/liquid systems suggest that a measurable effect should exist.6-l2 The purpose of these experiments was to determine the influence of temperature and hydrostatic pressure on dihedral angles in the Pb-Ni system. The equilibrium dihedral angle is expressed as a ratio of interfacial tensions by2: where 8 is the dihedral angle, yGB is the Ni-Ni grain boundary tension, and SL is the solid Ni-liquid Pb interfacial tension. Three sets of ex- periments were run to determine: a) the effect of temperature from 371" to 816°C on the dihedral angle at zero pressure; b) the effect of pressure up to 50,000 psi on the dihedral angle at 371° and 593°C. THERMODYNAMICS The properties of interfaces of most direct concern are the interfacial tension, excess concentrations of various components at the interface and the excess entropy of the interface, S°. These quantities are defined following Gibbs. Consider an interface separating phases a and 0. Construct two surfaces C, and C such that all properties of phase a remain uniform up to C, and all properties of phase 0 remain uniform up to C. The region between C, and Cp is the interfacial region. Let a "dividing surface", D, be constructed in the interfacial region such that it passes through all points "similarly situated with respect to the condition of the adjacent matter."l3 Surface D divides the interfacial region into a portion a' adjacent to phase adjacent to phase . Let a closed curve, C, enclose an area A in D. Erect normal lines to D along C; these lines and the surfaces C,, Cp, and D then enclose volumes V and V' in the two halves of the portion of the

Jan 1, 1964

By G. B. Craig, H. E. Rosinger, W. J. Bratina

NUMEROUS studies have been reported on how the mechanical properties of a bcc metal are affected by interstitial solute atoms in the temperature range where appreciable diffusion occurs in finite time. Only recently, though, has work on an "interstitial-free" iron been reported, this by Leslie and sober,' on an Fe-0.15 pct Ti alloy. The data was limited to a maximum temperature of 296°K. This work presents a systematic study of the flow stress and the activation volume of a similar material as a function of plastic deformation over the temperature range 253" to 473°K. The material studied was Ferrovac E iron containing 0.01 wt pct C and 0.0002 wt pct N annealed at 870°C for 1 hr, and the same iron with an addition of 0.15 wt pct Ti annealed at 870°C for 80 hr; cooling rates being 75°C per hr. In the latter alloy depletion of interstitials in the a-iron matrix associated with the second phase formation was expected. The temperature dependence of the flow stress was measured at 6 = 3.33 x 10-5 sec-1 from 253" to 473°K as a function of the deformation in 0.01 intervals from 0.03 to 0.12 strain. Results for two strains, 0.03 and 0.09 are shown in Fig. 1. The flow stress increased and reached a maximum in the Ferrovac E iron with increasing temperature, but showed a consistent gradual decrease in the Ferrovac E-0.15 pct Ti alloy. A yield point and Luders region, observed in Ferrovac E, was absent in the Ferrovac E-0.15 pct Ti alloy. Also, the Ferrovac E exhibited a serrated stress-strain behavior in the temperature range 330" to 400°K; dynamic strain-aging characteristics were absent for the titanium alloy. The activation volume was determined over the same temperature range by the method of stress relaxation at constant strain. Results are shown in Fig. 2. At the temperatures of serrated stress-strain behavior in Ferrovac E the activation volume was found to increase toward infinity and, as the temperature rose, to decrease, to about 100 to 200 v/b3. By contrast, the activation volume for the Ferrovac E-0.15 pct Ti alloy tended to increase continuously from the initial value of approximately 300 at 300°K to more than 800 at 473°K. Above 400°K, then, the corresponding activation volume values of Ferrovac E were less than that of the Ferrovac E-0.15 pct Ti alloy. The activation volumes, Fig. 2, appear to depend on dislocation-interstitial interaction in Ferrovac E and on dislocation-dislocation interaction in Ferrovac E-0.15 pct Ti alloy. The gradual increase in the latter metal is associated with thermally activated motion of dislocation segments.' The decrease of the activation volume in Ferrovac E above 400°K is probably related to the diminishing effect of interstitials on dislocations. Here, the interstitials can be moved along with a dislocation without appreciable drag. As indicated in Fig. 1, removal of interstitials

Jan 1, 1970

By C. E. Birchenall, W. Batz, H. W. Mean

AT temperatures between 1095' and 1347ºC, 13 runs have been made on the diffusion of silicon in iron. In two of the runs the couple compositions were entirely within the loop of the Fe-Si system; the base alloys contained 0.0 and 1.0 wt pct Si. The other runs in which the couples consisted of a 2.3 wt pct Si alloy welded to a 3.7 pct Si alloy were a phase throughout. The alloys were made by melting electrolytic iron and commercially pure silicon. Trace impurities were not determined. The butt welded couples were diffused in an inert atmosphere of argon or hydrogen. After cooling, cuts of two mils or greater thickness were machined parallel to the weld interface. The chips were analyzed for silicon. When the concentration and distance data were examined on the conventional probability plot,' no marked variation of the diffusion coefficient with concentration was indicated over the narrow composition ranges employed. Therefore, a single diffusion coefficient is recorded for each run in Table I. The temperatures and atmospheres of the diffusion anneal are listed along with the compositions of the base alloys. For a iron the silicon diffusion coefficient is given by the equation: D = 0.44 e-48,000/RT where R is the gas Constant and T, the absolute temperature. However, since the scatter in the data is fairly large, the activation energy may be in error by as much as 6000 cal per g-atom. The two ? iron points do not permit estimation of the activation energy with any reasonable certainty. They do indicate that the coefficients reported by Smithells2 and Jost,3 based on the work of Fry,4 are much too high. Although very dilute solutions in iron of manganese,5 nickel,8 cobalt,7 and molybdenum8 give dif- fusion coefficients quite close to those obtained for self-diffusion in iron, the silicon values are considerably higher, though of the same order of magnitude. This seems to be consistent with the fact that the silicon atom is the only one of those listed here which is appreciably smaller than iron. The authors are grateful to the Office of Naval Research for their support of this work under Contract N6ori-47, Task order IV, Project NR 031-184, to J. K. Stanley and the Westinghouse Research Laboratories for the silicon alloys used, to several steel companies for the silicon analyses, and to C. Wells, of the Metals Research Laboratory, Carnegie Institute of Technology, for numerous suggestions during the course of the work. References 'C. Wells: Atom Movements (1951) Chapter 2. A.S.M. 2C. J. Smithells: Metals Reference Book (1949) p. 405. Interscience. Pub. Co. 3W. Jost: Diffusion (1952) p. 223. Academic Press. 4 A. Fry: Stahl und Eisen (1923) 43, p. 1039. T. Wells and R. F. Mehl: Trans. AIME (1941) 145, p. 315. "C. Wells and R. F. Mehl: Trans. AIME (1941) 145, p. 329. 7M. F. Hawkes and R. F. Mehl: Trans. AIME (1947) 172, p. 467; Metals Technology (August 1947). .J. L. Ham: Trans. A.S.M. (1945) 35, p. 331.

Jan 1, 1953

By E. H. Crabtree, Neil S. Parker

The custom milling plant of the Eagle-Picher Mining and Smelting Co. is at Sahuarita, Arizona, approximately 20 miles south of Tucson. It is connected by a 2-mile railroad spur to the main line of the Southern Pacific Railroad between Tucson and Nogales. The capacity of the plant is 500 tons per day. The mill is conventional except perhaps in the rather wide variety of ores treated. These vary from straight copper ores, from which only one concentrate is produced, and lead-zinc or copper-zinc ores from which two concentrates are produced, to complex gold-silver-copper-lead-zinc ores, which require the simultaneous production of three or lour concentrates. Custom ores are received in lots varying in size from a few truckloads to several carloads. Similar ores, after crushing and sampling, may be commingled, or individual lots may be milled individually. The ores are first dumped either into one of two 200-ton railroad bins, or into one of the two 75-ton truck bins. From these bins the lot of ore is individually crushed in a 24 by 16-in. jaw crusher to 3-in. size, and then to ½-in. size in a 3-ft Symons shorthead crusher. After crushing to ½-in., the ore is conveyed to the automatic sampling plant. This consists of three Vezin samplers in series, each successively cutting out 10 pct, 10 pct and 5 pct of its feed. After No. I sampler, the material passes through a mixing barrel and is then crushed to -in. in a set of rolls before passing to No. 2 sampler. Between No. 2 and No. 3 samplers, the ore is again mixed in a mixing barrel. The final sample, consisting of one pound per ton of ore, is taken to the laboratory, where it is further crushed to 1/8-in. in a coffeemill, and then riffled down to the size required for grinding in a pulverizer. The capacity of the crushing and sampling plant is up to 100 tons per hour, depending upon the character of the ore. After sampling, the ore is stored in five ore-storage bins, consisting of four 200-ton bins and one 175-ton bin. Each of these bins is discharged by means of belt feeders and conveyor to the ball mills, so that ores may be composited for milling in any required ratio, or milled separately by themselves. Fine grinding is done in one 6 by 4-ft Allis-Chalmers ball mill and one 8-ft by 36-in. Hardinge mill. These two mills both discharge to one 54-in. Akins Simplex High weir classifier. The classifier sands can be returned to either or both mills, so that flexibility in grinding for different ores is easily obtained. Flotation equipment consists of four 66-in. Fagergren machines for copper-lead roughing and six similar machines for zinc roughing. Lead-copper bulk concentrate is cleaned and recleaned in eight No. 18-S Denver machines, and zinc concentrate is cleaned in three 66-in. Fager-grens. Copper-lead differential separation

Jan 1, 1949

By H. C. Gatos, J. T. A. Pollock, V. Sadagopan

PREVIOUS investigations on the effect of neutron irradiation on the superconducting properties of bulk transition metals indicated that little or no change occurred in poly crystalline disordered materials, particularly if cold-worked prior to irradiation. Only the superconducting properties of ordered intermetal-lic A15 compounds were found to be sensitive to irradiation, and the observed reduction in Tc and increased magnetic hysteresis or critical current densities were attributed to the introduction of flux pinning vacancy clusters and disorder in the lattice. Since the former would also be expected to be present after irradiation in disordered alloys, the general conclusion was that the disordering effect of the irradiation was the primary reason for the changes observed. The present note reports some unusual effects of neutron irradiation on cold worked Nb(Cb)-Ti-V alloys. Specimens with nominal composition as given in Table I were prepared by repeated arc melting, taking the usual precautions, and homogenized at 1000°C for 24 hr prior to a reduction of 15:l by cold rolling. Samples of size 1 by 1 by 25 mm were sliced from the rolled strips. The sarmples chosen for irradiating were sealed in a cadmium tube (wall thickness 1 mm) prior to exposure in a fast neutron flux of 3.7 x 1019 neutrons per sq cm in the swimming pool reactor of Union Carbide Corporation&apos;s Sterling Forest Reactor. During irradiation the temperature of the samples was maintained below 70°C. The irradiated samples were stored at room temperature for approximately 1 year allowing the radiation levels to reach a safe handling value. Tc measurements were made employing a self-inductance coil technique. Jc data at 4.2"Kwere obtained using a four lead resistivity method. The latter measurements were made at the Francis Bitter National Magnet Laboratory by setting the perpendicularly applied field and increasing the direct current through the sample until a potential of about 10-6 v was detected. Tc values for the nonirradiated samples are listed in Table I together with the change in Tc after irradiation. A decrease in Tc of 0.25 or 0.3"K was measured for three of the four samples, the exception being the Nb-30 at. pct V-20 at. pct Ti alloy which showed a decrease of 0.5K. Jc vs applied field data are plotted in Fig. 1 for the Nb-20 at. pct V-30 at. pct Ti alloy. These curves are typical of the four alloys and surprisingly indicate that a degradation occurred in all the samples after irradiation. Hc2 values, obtained by extrapolation to zero current, are 8 to 15 pct lower than those measured for the nonirradiated specimens. The reasons for the degradation of Tc and jc ob-served in the alloys on exposure to neutron irradiation are not immediately apparent. The temperature at which the samples were maintained during bombardment (<70°C) and stored (20°C) make it highly unlikely that any significant change in the dislocation density of the materials through thermally activated migration and annihilation would occur. The explanation must lie in the type of damage produced by the bombardment. McEvoy et a1. reported no change in superconduct-

Jan 1, 1970

By H. J. Gluiskoter

The chlorine content of the coals in the Illinois Basin ranges from 0.00% to more than 0.60%. The chlorine content of the Herrin (No. 6) Coal has been mapped on a regional scale and, in general, increases with the depth of the coal. The depth-chlorine correlation exists because the coal is in apparent equilibrium with the composition of the ground water associated with it, and the salinity of the ground water generally increases with depth. At least part of the chlorine can be easily removed from the coal in the laboratory. In a natural weathering experiment, chlorine values decreased markedly during an 8-week period. Results to date indicate that none of the coals studied has a sufficiently high chlorine content to make it unusable in high-temperature steam boilers, although special steps may be necessary in the preparation or utilization of some of the highest chlorine coals. Investigations into the occurrence and distribution of chlorine in Illinois coals have been in progress at the Illinois State Geological Survey for over 35 years. Since 1948, chlorine analyses of face channel samples and of drill core samples of coal have been made routinely. The increased interest in chlorine and alkalies in coal in the U.S. followed that in Europe, where power plants during World War II were called upon to produce at higher levels than previously and with less down time for maintenance. Higher steam temperatures were reached, resulting in increases in the amount of fouling of external heating surfaces and in corrosion of boiler tubes when high chlorine coals were used. Early studies of the problem showed that coals with high chlorine content were more likely than those low in chlorine to cause difficulties in installations fired with powdered fuel. Crossleyl reported that the first rule of thumb developed for British coals was that coals considered to be high in chlorine (more than 0.30%) caused the most trouble, those intermediate in chlorine content (0.15% to 0.30%) were less likely to cause difficulties and those low in chlorine (less than 0.15%) generally were not associated with alkali bonded deposits and corrosion. However, this relatively simple picture was not adequate to characterize the difficulties that could be expected during the utilization of a large number of coals and Crossley1 developed another scheme for assessing the chances of superheater corrosion. This scheme took into consideration the observation that coals high in sulfur as well as chlorine are more likely to cause corrosion and fouling than coals low in sulfur and high in chlorine. Crossley also considered the ash content. When two coals had the same chlorine and sulfur contents, the one with the greater amount of ash would be the less likely to cause difficulties. Knowing only the amount of chlorine in a coal obviously will not give all the answers. Indeed, the significance of the chlorine content has been much discussed and it has been suggested that perhaps the total alkalies are a better indicator of possible troubles. The observation that the deposits that form

Jan 1, 1968

By D. B. Jugle, J. B. Darby

The equilibrium solubility limits of the transition elements Ti, V, Cr, Fe, and Co in liquid tin were determined in the temperature range from 827" to 1211°K. Since the equilibrium concentration of Ti, V, or Cr in liquid tin is moderately dilute in the temperature range investigated, the solubility data were employed to estimate the partial molar enthalpy and the partial molar excess entropy of solution for the three solutes in liquid tin. The reference state s for titanium or vanadium were selected relative to the solute in an intermetallic compound. The thermodynamic quantities for chromium were calculated relative to pure chromium. RECENT experiments1 have shown that the rate of solution of several transition elements in liquid aluminum can be qualitatively predicted from a knowledge of the temperature dependence of the solvent-rich liquidus. In order to extend the analysis to binary tin systems,&apos; it was necessary to know the equilibrium solubility of several of the first-long-period transition elements in liquid tin. Since solubility data for the tin-rich portion of binary systems are meager, the present investigation was undertaken to determine the equilibrium solubility limit of Ti, V, Cr, Fe, and Co in liquid tin in the temperature range from 850" to 1200°K. EXPERIMENTAL PROCEDURE A useful technique3 to determine the equilibrium solubility of a solute in a liquid-metal solvent consists essentially of placing a pure solute in contact with a pure solvent and allowing sufficient time for equilibrium to be attained at the temperature of interest. Subsequently, the solvent is removed and the equilibrium solute concentration in the solvent is determined by an appropriate analytical procedure. The technique can be applied very successfully to relatively simple systems such as the copper-germanium system.3 However, in many binary systems of transition elements with tin, several intermediate phases are known to exist and precipitation of the phases from solution, in solubility experiments, can lead to an erroneously large solubility. The difficulty was avoided in the present work by equilibration of the most solvent-rich intermediate phase with the pure solvent over a range of temperatures. The compounds employed in this investigation, and the temperature range over which each compound is in equilibrium with liquid tin are listed in Table I. No stable intermediate phases are reported in the chromium-tin system4 and, therefore, pure chromium was utilized as the solute. The stoichiometric compounds were prepared by arc-melting on a water-cooled copper hearth in a helium-argon atmosphere. The elemental tin employed in.this investigation was 99.998 pct pure, and typical lot analyses of the transition elements were reported elsewhere.&apos; A sample of an appropriate solute, in the form of a button and in sufficient quantity to exceed the equilibrium solubility, and the pure tin solvent were placed in a high-purity recrystallized-alumina crucible. The crucible and contents were placed in a horizontal furnace under a high vacuum (10-6 torr) and held at temperature for periods varying between 24 and 72 hr. A water-cooled quench tank, partially filled with diffusion-pump oil, was attached close to one end of the

Jan 1, 1970

By W. J. Tait, A. E. Craig, E. P. McCurdy

The Circuitron herein described applies current from the classifier motor circuit and energy from the sound of grinding media to move an oscillating disc. The disc through a photoelectric cell controls the speed of the ore feeder and consequently the amount of ore delivered to the mill. THE Telluride Mines, Inc. at Telluride, Colo., is operating a flotation concentrator recovering lead, zinc, and copper with some gold and silver. The nominal capacity is 500 tons per 24 hr. The ore, which comes from several different mines, is characteristic of the district, changing from extremely tough rhodonite to soft gouge. The ore is crushed and washed, recrushed, and delivered to the mill bin at about % in. to serve as ball mill feed. Details of Grinding Circuit The material from the fine-ore bin is carried over a belt feeder driven by a Reeves vari-speed device. The belt discharges to a No. 86 Marcy ball mill, which operates in closed circuit, with jigs and a 6-ft Dorr classifier. A Massco density controller holds the density of the classifier overflow at a predetermined point. The overflow, which contains about 5 pct + 48 mesh, goes to the flotation section. Manual Operation Before the adoption of automatic control for the grinding circuit, this work was all done manually by the operator. The bin gate was set to deliver 40 to 50 lb of ore per lineal foot of belt, and the speed of the belt was adjusted by the operator to deliver at the rate of about 500 tons per 24 hr. As the ore changed in hardness, specific gravity, or in the amount of moisture, or, as the size of the feed changed due to bin segregation, crusher setting, or other causes, the operator made corresponding changes in the rate of feed by manipulation of the Reeves control. Sometimes these changes occurred so rapidly that they caused sharp, pronounced surges, which created very considerable unbalance from normal conditions in the grinding circuit and, more critically, in the flotation section. Since it is not possible for the operator to anticipate or follow such changes closely, a very considerable unbalance from normal conditions may occur, which will require a drastic change in the rate of feed. These surges upset the fineness of grind and interfere radically with the balance between tonnage and reagent control. All of this tends to reduce the grade of concentrates, increase the loss in the tailing, and thus decrease the recovery of values. The Circuitron Some years ago, The Mine and Smelter Supply Co., in conjunction with the operators at the Telluride Mill, undertook to build a device that would give close control of the rate of feed from the ore bin and to coordinate with this a related device that would regulate the amount of sand load on the classifier rakes. Emphasis was strongly laid on the fact that such a control must apply to the entire grinding circuit and must include the feed to the ball mill, the classifier sand return, and the density of the classifier overflow. If this could be done successfully, we felt that the circuit could be operated under best possible conditions, with compensations

Jan 1, 1951

By J. C. Uy, A. A. Burr

IN the primary solid solutions of zirconium-base alloys, there is a striking regularity of the effect of solute valence on the stabilization of the allotropic phases.1 The valences derived by pauling2 are for elements as they are bonded in the solid metallic state. Effects of variations in isotopes, alloying elements, and allotropes on their valences are difficult to determine and such data are presently unavailable. Pauling&apos;s values are somewhat empirical and approximate, but if some definite correlations can be found between those values and experimental observations, this will lend support to the tacit assumption that the possible variations in valence mentioned above are small. Pauling has amassed a large amount of evidence of such correlations. It is the purpose of this technical note to show another application of the Pauling valences and to offer a possible explanation for this observation. The relationship between the Pauling metallic valence of the solute and the stabilization of allotropic phases in zirconium is shown in Table I, which has been compiled from available data in the literature3 plus the results of work done at Rens-selaer Polvtechnic Institute.&apos; The chemical valences are included for comparison. It can be seen that a solute whose metallic valence is lower than that of the solvent tends to stabilize the a phase while one whose metallic valence is higher than that of the solvent tends to stabilize the 0 phase. It should be noted that, inasmuch as the Pauling valences are periodic with atomic number, this is tantamount to saying that the elements in groups I-A, 11-A, III-A, III-B, IV-B, V-B, and VI-B are a stabilizers while those in groups IV-A, V-A, VI-A, VII-A, VIII-A, I-B, and 11-B are ß stabilizers. The chemical valences do not show such consistency. Although the zirconium-rich end of the Zr-Au diagram is not available, it call be expected that gold, having a metallic valence of 5.56, would stabilize the ß phase. At absolute zero, the Fermi energy level is the criterion of equilibrium, i.e., the structure having the lower Fermi level will be more stable. Conse- quently, allotropic transformation occurs in a metal when thermal excitation raises the Fermi level to a point at which the atoms can be better accomodated by a different structure which yields a lower Fermi level.4-6 Thus in allotropic transformation, a change in structure occurs as a result of the change in the energies of the bonding electrons. Since the Pauling valence is the number of bonding electrons per atom, and these are the only electrons whose energies are affected by thermal excitation,* it can be inferred that the introduction of a solute which has a higher Pauling valence than that of the solvent raises the initial Fermi level; consequently, the transformation temperature is lowered. The converse is also true. The fact that at the transformation temperatures this statement is still fairly valid implies that the contribution due to the difference in specific heat terms of the two allotropes is comparatively small.

Jan 1, 1962

By D. F. Kaufman, E. D. Levine, L. R. Aronin

ThE primary slip plane in hcp metal crystals can usually be inferred from the c/a ratio. Basal slip is the primary system at room temperature for zinc, cadmium, magnesium, cobalt, and rhenium, all of which have a c/a ratio greater than 1.60. Zirconium and titanium, on the other hand, each with a c/a ratio of 1.59, deform primarily by (1010) [ll20] prismatic slip. The increasing tendency toward prismatic slip in these materials is generally thought to be associated with the increase in atomic density on (10i0) as c/a is reduced. Beryllium, with a c/a ratio of 1.57, would, according to the above scheme, be expected to exhibit prismatic slip. However, in beryllium of commercial purity, the primary deformation mode at room temperature is basal slip.&apos; The ratio of critical shear stress for prismatic to that for basal slip at room temperature is approximately 5:l. The critical shear stress for prismatic slip decreases quite rapidly with increasing temperature, however, and at 500°C the ratio is approximately unity. The apparently anomalous behavior of beryllium has led to speculation that prismatic slip in this material may be restricted by an anisotropic effect of impurities,&apos; and that, if beryllium could be purified to a sufficient extent, prismatic slip might predominate at room temperature. In such a case, the conditions under which basal cleavage can occur would be suppressed, and enhanced low-temperature ductility might result. With the advent of the floating-zone method for purification of beryllium,3 it has become possible to determine experimentally the effects of purification on basal and prismatic slip. Tensile tests were performed at room temperature on single crystals oriented favorably either for basal or prismatic slip. The crystals had been purified to various extents by zone-refining, employing procedures that have been described elsewhere.4 Relative purities of the crystals were estimated by measuring the ratio of electrical resistance at 4.2"K to that at 298°K. Typical values ranged from 0.40 for commercial-purity material to 7.7 X 10"4 for crystals prepared from vacuum-distilled beryllium and subjected to six zone-refining passes. The purity dependence of the critical shear stresses for basal and prismatic slip is shown in Fig. 1. In the purity range studied, the critical shear stress for basal slip is decreased from 1.4 to 0.14 kg per sq mm. The critical shear stress for prismatic slip is decreased from 6.7 to 5.3 kg per sq mm. The decreases in critical shear stress for each deformation mode, therefore, are approximately equivalent. No purification anisotropy is observed. Because of the absolute magnitudes of the critical stresses, the ratio of the critical shear stress for prismatic slip to that for basal slip actually increases from 5:l to 38:l at the highest purity level studied. It is evident, therefore, that basal slip is the primary deformation mode in high-purity beryllium. This fact must be accounted for in any rationalization of the deformation behavior of hcp metals. This work was performed at Nuclear Metals, Inc., under the sponsorship of the U.S. Atomic Energy Commission.

Jan 1, 1964