By T. E. Leontis, F. N. Rhines

THE oxide scale that forms upon magnesium at elevated temperatures is nonprotective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth1 and has been verified by Suzuki2 and by Scheil.3 Pilling and Bedworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki,2 the product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavault5 observed that excrescences form upon liquid magnesium and alloys in the course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium7and calcium8 minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.9 Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Scheil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. EXPERIMENTAL PROCEDURE AND RESULTS The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the

Jan 1, 1946

By Nicholas J. Grant, Noboru Komatsu

Metallographic and X-ray studies were made of oxide dispersion strengthened Cu-12 vol pet SiO2 and Cu-3.5 vol pet Al2O3 alloys following time exposures at temperatures approaching the melting. point of the matrix metal. Changes in hardness, oxide particle size and crystal structure were studied to determine the time-temperature stability of these alloys. An interpretation of the mechanism of oxide agglomeration is proposed. One of the most striking features of dispersion strengthened metal-metal oxide alloys is their stability at elevated temperatures, both with respect to recrystallization and maintenance of mechanical properties after exposure at high temperatures. A small amount of work has been done on the re-crystallization phenomenon in dispersion hardened metal-metal oxide alloys'l and several theoretical treatments have been advanced regarding the stability of these alloys by Lenel and Ansell,8 and by Grant and his co-workers.9, 10 This paper reports on metallographic and X-ray studies following various heat treatments of Cu-AI2D3 and Cu-SiO2 alloys at elevated temperatures and the effect of subsequent cold work on the recrystallizalion temperature. An interpretation of the recrystallization behavior of this type of alloy, based on the decomposition and agglomeration of oxides, is proposed. EXPERIMENTAL PROCEDURE Cast ingot bars of copper-1.59 pet Si and Cu-0.77 pet Al, 7/8 in in diam, were annealed in argon for 80 hr at 1000CC for homogenization. The homogenized rods were machined into fine chips and ball milled. Milled particles in the range minus 20 to plus 60 mesh were separated for internal oxidation. The internal oxidation was accomplished by the same method used by Preston and Grant,9 except that the oxidalion temperature for the Cu-Si alloy was 750°C, and for the Cu-A1 alloy was 800°C. These powders were then hydrogen-reduced at 450°C, compacted in a copper container, evacuated at room temperature to 0.04 µ, and sealed for extrusion. They were extruded at 1400°F (760°C) with a ram speed of 55 in. per min for an extrusion ratio of 15.6 to 1 to give a rod 0.38 in. diam by about 3 ft long.

Jan 1, 1962

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

The results of a preliminary study of 113 ternary titanium-base alloys are described. The compositions investigated were as follows: 1. Ternary titanium-carbon alloys containing copper, silicon, vanadium, chromium, manganese, iron, or cobalt. 2. Ternary titanium-nitrogen alloys containing chromium. 3. Ternary titanium-chromium alloys containing additions of vanadium, molybdenum, tungsten, cobalt, or nickel. 4. Ternary titanium-manganese alloys containing additions of silicon, chromium, tungsten, or iron. Tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships for these alloys were determined. THIS is the second in a series of papers describing some of the results of the exploratory work on titanium alloys being conducted at Battelle Memorial Institute for the Wright-Patterson Air Force Base. The work with the binary alloy systems has been described in a previous publication.' This paper describes ternary titanium-base alloys as follows: 1. Ternary titanium-carbon alloys containing copper, silicon, vanadium, chromium, manganese, iron, or cobalt. 2. Ternary titanium-nitrogen alloys containing chromium. 3. Ternary titanium-chromium alloys containing additions of vanadium, molybdenum, tungsten, cobalt, or nickel. 4. Ternary titanium-manganese alloys containing additions of silicon, chromium, tungsten, or iron. As the preparation and fabrication of the 0.5-Ib experimental titanium alloy ingots to 14-ga sheet, as well as the methods of testing used in this work, have been described in the first paper of this series, Titanium Binary Alloys, no further discussion of these techniques will be given. Ternary Alloys Containing Carbon The following alloys of titanium, containing carbon and one other metal, were investigated: 1. 0.25 pct carbon; 1, 2.5, and 5 pct copper. 2. 0.25 pct carbon; 1, 2, and 3 pct silicon. 3. 0.25 pct carbon; 1, 2.5, and 5 pct vanadium. 4. 0.25 pct carbon; 2.5, 3.5, 5, 10, and 15 pct chromium. 5. 0.5 pct carbon; 2.5, 3.5, and 5 pct chromium. 6. 0.25 pct carbon; 1, 1.75, 2.5, 3.5, 5, 7.5, and 10 pct manganese. 7. 0.5 pct carbon; 1.75, 2.5, 3.5, 5, 7.5, and 10 pct manganese. 8. 0.25 pct carbon; 0.25, 0.5, 1, and 2 pct iron. 9. 0.25 pct carbon; 1, 2, and 3 pct cobalt.

Jan 1, 1951

By J. Spotts McDowell

Preparation and Use.-Magnesite is an important refractory in open-hearth, heating, and electric furnaces for steel-making and in many of those employed in the metallurgy of copper and lead. It is sold in the form of brick, finely ground "furnace magnesite" for brick-laying, and dead-burned grains for making and repairing furnace bottoms. The latter are a mixture of granules varying in size from pieces of about 5/8 in. (1.6 cm.) diameter to very fine but sandy particles. Dead-burned magnesite results from calcining 'the crude or lightly burned mineral at a temperature that will not merely drive off practically all the CO2, but will also cause sintering of the particles. During this process the pieces shrink considerably and become hard, dense, and inert to atmospheric moisture and C02; under-burned material, on the other hand, will hydrate on exposure to the air. A small percentage of ferric oxide seems to be necessary for the production of a satisfactory sinter; from 4.5 to 8 per cent. in the dead-burned grains is considered the most desirable amount. Dolomite has been little used for brick-making in the United States, but it is prepared for use in the granular condition calcined or "double-burned" and is the principal ingredient of several materials offered for sale under various trade names for refractory purposes. Dolomitic refractories are almost wholly confined to the open-hearth and electric furnaces, where they are used for fettling and as substitutes for magnesite. Much more magnesite and dolomite are used for basic open-hearth steel-making than for all other refractory purposes. The hearth of the furnace is usually built up of magnesite brick and dead-burned grain magnesite so laid that the brick base is protected by a working bottom of the granular material. The latter is sintered into place in layers 1 to 2 in. (2.5 to 5 cm.) thick to a total depth of 12 to 18 in. (30 to 45 cm.) at the center of the furnace. After each heat, burned dolomite is thrown against the banks as high as it will stick, and all holes in the bottom are filled. At most plants such holes, at the end of each week, are also

Jan 2, 1919

By C. H. Mathewson, Robert Maddin, W. R. Hibbard

A SATISFACTORY mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.1 Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.3 EXPERIMENTAL PROCEDURE Half inch rods of alpha brass (nominally 70 pct Cu, 30 pct Zn) * were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.' In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pct nitric acid solution. The back-reflection Laue technique as described by Greninger5 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buerger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1948

By J. P. Doan, G. Ansel

The important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holubl-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British Patent 5111375 relates to the parent discoveries of Sauerwald, Eisenreich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature5. has been found to the particular characteristics of wrought blg-Zn-Zr alloys, with which the present paper is concerned. The work to be discussed represents essentially an extrusion study of the blg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metallography, and toughness of these alloys. Compositional variations are limited to the ranges 0 to 7 per cent Zn and 0 to I per cent Zr. Experimental Procedure Alloying and Casting Alloying ingredients were cell magnesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl² and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manufacturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zirconium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux-inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold

Jan 1, 1947

By G. Ansel, J. P. Doan

The important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holubl-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British Patent 5111375 relates to the parent discoveries of Sauerwald, Eisenreich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature5. has been found to the particular characteristics of wrought blg-Zn-Zr alloys, with which the present paper is concerned. The work to be discussed represents essentially an extrusion study of the blg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metallography, and toughness of these alloys. Compositional variations are limited to the ranges 0 to 7 per cent Zn and 0 to I per cent Zr. Experimental Procedure Alloying and Casting Alloying ingredients were cell magnesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl² and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manufacturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zirconium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux-inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold

Jan 1, 1947

By Frederick C. Hull, Robert F. Mehl, Robert A. Colton

IT is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth 12 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in 1939 3 Two types of process were described (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures, and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth Both cases are met in the formation of pearlite from austenite (Fig 1),2,3 the former, occurring near the knee of the S-curve has been named "grain-boundary transformation," and the latter, occurring at temperatures near AeI, has been named "group-nodule transformation " In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important''' to obtain data on the rate of nucleation and the rate of growth of pearlite Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the actors that affect hardenability, when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite 2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature,, and the degree of homogeneity of the parent austenite The studies are restricted chiefly to plain carbon commercial steels PREVIOUS DATA ON RAID OF NUCLEATION AND RATE OF GROWTH Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Mehl,1 and by Dorn, De Garmo and Flanigan22 It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc ), austenite grain size, and mode of formation of pearlite at the temperatures given

Jan 1, 1942

By G. F. Jr. Butterworth

THE metallographic structures most frequently encountered in rifle barrels, and which are illustrated by the accompanying photomicrographs, fall naturally into two groups, distinguished by the method used to produce in the stock a physical condition having the requisite properties. The first group consists 'of "rolled" barrels; that is, barrels subjected to hot working by rolling in or near the critical range. In the second group, the stock, which is smaller in diameter than the first, is upset to form the butt end and is then heat-treated by giving it a quench and a draw. These barrels will be referred to as "heat-treated" barrels. The structure of the rolled barrels resembles closely that of the same steel after annealing. There is the same network of excess ferrite outlining the grain boundaries, but the grains themselves are composed of sorbite rather than pearlite. The grain size is closely related to the rolling temperature. The critical-point curves of this grade of steel, which is approximately 0.50 to 0.60 per cent. of carbon and 1.00 to 1.30 per cent. of manganese, show a single very pronounced point between 1300° and 1350° F. (704° and 732° C.). Barrels rolled within this temperature range give an exceedingly fine grain, shown in Fig. 1. In fact, the grains may be so fine that, at a low magnification, they may be confused with the heat-treated structure discussed below, Fig. 6. A magnification of 500 diameters, however, will always resolve a rolled barrel into the characteristic structure, shown in Fig. 2. As the temperature is increased, the grains are found to be larger. If, on the other hand, the rolling temperature is below the critical range, the structure previous to rolling will not be obliterated, the only effect of rolling being to elongate the coarse sorbite grains in the direction of rolling, Fig. 3. This distortion is greatest at the muzzle. Heat-treated barrels are quenched in oil from above the critical range, which should give a martensitic structure, Fig. 4, but the presence of some troostite in the martensite is frequently noted when the quench has not been sufficiently drastic, Fig. 5. The structure brought about by the subsequent draw is not so striking, though quite as typical. It is sorbitic or sorbito-pearlitic, and under- a low magnification appears

Jan 7, 1919

By Frederick Laist, Howard Aldrich

The object of the construction and operation of the 80-ton leaching plant was to test out the leaching of sand tailings on a large scale and, if possible, determine a definite method of operation, and the best construction for the larger unit which is now being built. It was also of importance to obtain some practical data as regards cost items. The 80-ton plant was not expected to be a commercial success. A leaching process on such low-grade material necessitates the treatment of a very large tonnage. Such a cost item as labor, for instance, is entirely out of proportion in such a small plant. The amounts of acid, salt, scrap iron, and fuel for roasting, however, are the same per ton in an 80-ton plant as in a 2,000-ton plant. These costs were definitely established. Also the percentages of extraction and grade of tailings were definitely determined for a large-sized unit. Following will be found the description of the plant, the method of operation and the- results obtained. A general view of the plant is given in Fig. 1. The bins consisted of one coal bin with a capacity of 30 tons, one salt bin with a capacity of 20 tons, and a "mill tailings" or feed bin which held 70 tons. The coal and salt bins were placed with their floor level even with the firing floor of the roasting furnace. The feed bin, to give it greater capacity, discharged about 12 ft. below this point, to a 12-in. conveyor belt, which in turn discharged into a pug mill. This fed another conveyor belt, which discharged into the top hearth of the furnace. The furnace was an ordinary six-hearth MacDougall roaster, 20 ft. in diameter. It was equipped with two fire boxes, on opposite sides, the flames entering on the third hearth. An induced draft was obtained with a Buffalo blower, worked as an exhaust fan. Just above the top hearth was an annular flue around the whole circumference of the furnace. Slots at intervals of about 18 in. led from this flue down into the top hearth. The slots were 2 in. wide by 6 in. long. This annular flue proved rather unsatisfactory, as it tended to fill up with flue dust and choke the dots, thus cutting down the draft. The volume of gas through

Jan 1, 1915

By A. Sutulov

The segregation process, an alternative to benefi-ciation of oxidized and mixed sulfide-oxide copper ores, is studied here with particular emphasis placed on time, temperature, and coke and salt percentage factors. The results show that in a segregated charge, the copper assay of the coarsest fractions normally is of the same order as the copper assay of the tails obtained from grinding and flotation of the same charge. This observation suggests the possibility of limiting or even eliminating the grinding step from the flowsheet of a segregation plant. The segregation process, which offers an alternative to beneficiation of oxidized and mixed sulfide-oxide copper ores, was discovered in 1923 by Moulden and Taplin1,2 who were attempting to apply the Perkins process3'4 to a Chilean ore from the Sagasca mine. After a number of investigations and pilot plant tests,'-' the segregation process became a successful industrial operation.'r9 The process aroused considerable interest in Chile because of the existance of large reserves of oxidized copper minerals which could not be treated by conventional hydrometallurgical methods because of the high consumption and prohibitive cost of sulfuric acid. During the last two years, the Mineral Dressing Dept. of the Institute de Investigaciones Tecnology cas of University of concepci6n (Chile) has carried out a test program on 23 different ore samples representative of the national territory. These tests were carried out on a semi-continuous and batch scale with a rotary, automatically controlled and gas-fired furnace (supplied by Bartlett and Snow, Fig. 1). The results of these tests indicate that out of the 23 samples 20 can be successfully treated by this process with recoveries of copper ranging from 85 to 95%.10,11 The purpose of this paper is to treat some specific problems related to the segregation process. TIME AND TEMPERATURE FACTORS Time and temperature of calcination play an important role in the segregation process. When moderate salt and coke conditions were maintained (each of reagents was added in the quantity of 1 — % wt), systematic testing easily demonstrated the influence of these two factors on segregation and flotation recovery. The pertinent results are summarized in Fig. 2. To determine what specific changes the segregation process made on the ore, the samples, segregated at 700°C for different periods of time and under standard conditions, were granulometrically analysed and

Jan 1, 1963

By J. T. Berling, J. B. Conway

MANY studies have been devoted to the correlation of low-cycle fatigue behavior. Several of these have also been concerned with the identification of an effective approach to the prediction of low-cycle fatigue behavior from short-term tensile data. Perhaps the first such approach was that reported by coffin1 in the form: where is the plastic strain range, Nf is the number of cycles to failure, and c is a constant characteristic of a material. In this analysis by Coffin it was reasoned that in a short-term tensile test the value of Nf could be considered as equal to a , in which case the value of c is interpreted as the tensile ductility, f, measured in such a test. If, therefore, the Coffin equation is assumed to be applicable to a given material, it is a simple matter to predict the low-cycle fatigue behavior. Once the tensile ductility is known, this point is located at Nf = 1/4 on a log-log plot of vs Nf and a line is drawn through this point with a slope of to yield a prediction for the fatigue life. Actually, while this equation is quite useful it is not generally applicable, for experiment has shown that the value of —$ does not reflect the relationship between and Nf for all materials or even for a given material over all temperature ranges. An equation similar to the Coffin equation was prepared almost simultaneously by Manson.2 This expression had the form: In this case the exponent on Nf was not assigned any particular numerical value in accord with the various values of this exponent which had been observed for different materials and at different test conditions. Because of this characteristic it will be recognized that little use can be made of this expression in predicting low-cycle fatigue results. A fairly effective expression for use in predicting fatigue behavior was proposed by Manson3 based on a study of numerous sets of experimental results. This relation (Method of Universal Slopes) makes use of modulus of elasticity, ultimate strength, and tensile ductility, and assumes an exponent on Nf equal to 0.6 in representing the plastic strain range contribution to total strain range. While this equation of Man-Son does not yield completely accurate results it must be recognized as being the best means available at

Jan 1, 1970

By John K. Berry

The handling and disposal of mine water is a much larger problem than is apparent at first glance. Many more tons of water are removed from underground coal mines in the United States each year than tons of coal. In the old anthracite region of Pennsylvania the average was around 36 tons of water for each ton of coal produced, while bituminous mines average about 5 or 6 tons. Water encountered in the mines may come from several different sources. In mines with light cover and without a firm solid roof, rain may seep directly into the workings. This is also true of deeper mines where pillar falls have broken the roof to the surface. The top under creek beds is generally faulty and broken and water comes through the roof at this point. Deeper mines are frequently overlain by water-bearing strata and pillar breaks and faulty top can admit water, while places running to the dip often accumulate water which comes up through the bottom. In all cases, except where passing under a year-round stream, the amount of water made is usually pretty closely connected with the weather-more water during the rainy season, less in the dry, although the deeper a mine is, the longer it is before changes in rainfall are felt. Another source of water, not connected with seasonal changes, is old water, accumulated over a period of time in abandoned workings of the mine, or from flooded adjacent mines. Here the water filters through the coal, the parting, or comes up through cracks in the bottom. Similarly, core holes, drilled to prospect the property, can be a source of unexpected water and modern safety requirements for dust-allaying water at the working faces can turn a pleasant working area into a soggy mess over the weekend if the system is not properly maintained and operated. Why water must be disposed is obvious. If allowed to accumulate, sooner or later the mine will fill up, or at least it will become "roofed" in low places, blocking ventilation and traffic. But it must also be controlled long before it reaches this stage. Water standing in the working faces is unpleasant for the men who have to work there and also cuts down on the amount of work they can do, as they must watch where they step all the time. It is especially unpleasant in low coal.

Jan 1, 1973

By L. E. Young

THE progress of mineral industry education will be limited to the period prior to World War II and will be considered as primarily a division of engineering education. Its relation to progress in the mineral industry and to the activities of the American Institute of Mining and Metallurgical Engineers will be emphasized. The history of mineral industry education has been recorded most completely and authoritatively by Dr. T. T. Read in his recent volume in the Seeley W. Mudd Series of American Institute of Mining and Metallurgical Engineers publications, entitled, The Development of Mineral Industry Education in the United States. Therefore, most of the historical details will be omitted from the discussion and an effort will be made to point out significant developments and to analyze trends. INTRODUCTORY STATEMENT AND SIGNIFICANT POINTS IN PROGRESS Among the significant points in the development of mineral industry education in the United States since 1871, the following deserve particular mention: I. The number of institutions offering undergraduate instruction has increased, particularly during the years 1890 to 1925; the number of students enrolled in undergraduate study has increased greatly, largely on account of the development of courses in petroleum engineering and increasing interest in metallurgy. 2. The selection of students to be admitted to undergraduate courses has been improved through the advisement, counseling, and guidance programs sponsored by the Engineers' Council for Professional Development. 3. Improved instruction methods and the training of the teaching staff have been promoted by the educational institutions themselves, but with the most effective stimulus and guidance of the American Society for Engineering Education and the Engineers' Council for Professional Development. 4. The accrediting of undergraduate curricula through the Engineers' Council for Professional Development, considering both qualitative and quantitative criteria, has done much to improve standards of instruction in engineering education for the mineral industry. 5. Undergraduate curricula and courses are revised currently to meet the needs of the American mineral industry. New curricula are developed currently to permit specialization in technical fields, particularly in the fourth year of undergraduate work. 6. There has been a strengthening of the fundamental courses in mathematics, physics, mechanics, and chemistry, and at the same time these courses are being adapted to the most recent developments in the industry, including metallurgy, geophysics, petroleum engineering, petroleum technology, ceramics and so forth. 7. There has been continuing improvement in plant and laboratory facilities of the educational institutions.

Jan 1, 1947

By B. Chalmers, Stefan Wojciechowski

Rotary oscillation of the mold has been used to produce mechanical stirring of the melt during unidirectional solidification. Al-Cu alloys (1 to 4 wt pct Cu) were solidified to study the influence of alloy composition, temperature at which intensive cooling was initiated, and intensity of stirring on the temperature distribution in the sample, the resulting structure, and the copper microsegregation at the columnar to equiaxed transition. The Proposed explanation for the equiaxed solidification in stirred castings consists of the melting off of dendrite fragments, their partial remelting in hotter liquid, and the subsequent growth of the surviving part when the temperature of the melt is lowered. This may result in the formation of a crystal network, which can stop the growth of the columnar crystals and produce the equiaxed zone. It has long been known and many times affirmed that ultrasonic vibrations or relative motion of liquid and solid can significantly reduce the length of the columnar zone and refine the grains in the equiaxed zone in ingots and castings. Because of the technological importance of these phenomena many investigations have been conducted in which ultrasonic energy or mechanical vibration,1-6 electromagnetic stirring,7"10'17 magnetic stirring,"'12 or mechanical stirring13'14 were used to produce the relative liquid-solid motion. More recently, the question of the importance of natural (or thermal) convection has been raised.15-l7 Several possible mechanisms have been suggested.l,8,18-20 They can be divided into two main groups. The first group includes such nucleation hypotheses as nucleation frequency enhancement due to cavitation at the mold wall or other surfaces; cavita-tion in the body of the liquid resulting from the pressure wave, or an agglomeration mechanism, which involves the formation of nuclei by the accretion of subcritical nuclei. The second group considers the grain-refining action to be due to crystal multiplication phenomena such as the removal of the dendrite fragments by viscous forces or by a high-pressure cycle following cavitation or by a melting-off process. Sbme recent investigations give good experimental support to the melting-off proposa1.21-23 The purpose of the present study was to examine the effect of mechanical stirring during the unidirectional solidification on the structure of alloy samples and on the solidification variables. The motion of the liquid was produced by rotary oscillation of the mold around its vertical axis.

Jan 1, 1969

US 4,134,944-Production of iron oxide ore pellets of uniform size and excellent strength. Small pieces of ore are rolled into nuclei in a first pellet-rolling circuit in the presence of a binder, the nuclei sized and hardened by sintering or cold-bonding of the binder, the nuclei rolled in additional ore to form product pellets, the pellets sized, the suitable size fraction taken as product, and undersize pellets returned to the rolling operation. P. A. Ilmoni and R. Drugge, assigned to Luossavaara-Kiirunavaara AB Jan 16, 1979. 5 pp. (264-37) Filed- 5-25-77 (800,278) Priority: Sweden, 6-2-76 (76/06,¬241). Same British 1,553,763, dated Oct 10, 1979. US 4,145,210-In the induration of pellets of iron oxide ore or iron works dust or sludge, a charge of dried pellets and 2-20% by weight of coke having a size range of from 5 to 30 mm, a drum index of more than 70, a reactivity index of less than 50, and a tumbler index of more than 50 is charged into a rotary kiln The charge is heated and passed through the rotating kiln to indurate the dried pellets without burning the coke Powder-coated coke is recovered from the kiln for reuse. Ring formation in the kiln is substantially prevented. K. Kato and K Kadota, assigned to Sumitomo Metal Industries, Ltd, and Sumitomo Heavy Industries, Ltd. Mar 20, 1979 10 pp (75-3) Filed- 2-22-77 (770,947) Priority: Japan, 2-24-76 (51/19,754) US 4,145,211-Method of cooling hot metallized iron oxide ore agglomerates from a direct reduction furnace Agglomer¬ates ranging from 3/a in to 41/2 in in cross-section and at a temperature of 1000-2000°F are formed into a moving bed while at rest relative to each other Air at ambient tempera¬ture is passed through the bed at a velocity sufficient to cool the agglomerates rapidly to a temperature no greater than about 500°F without substantial reoxidation of the metal in the agglomerates and by using air as the sole cooling gas. C A Czako, A Berzins, and M J Greaves, assigned to Arthur G McKee & Co Mar. 20, 1979 15 pp. (75-34) Filed: 7-18-77 (816,467)

Jan 1, 1980

By D. U. Deere, F. D. Patton

Introduction A close relationship exists between the geologic investigation and the stability analysis of the slopes of an open pit mine. One significant result of this relationship is that the stability analysis is no better than the assessment of pertinent geologic factors that enter into the analysis. In some slope stability problems the engineering solution becomes obvious once the geologic framework is established. In other cases, establishing the geologic framework is only the first stage in the process of analysis. However, even in these cases the geology should not be neglected once the analysis is made. The geology should be periodically reviewed when new slopes are excavated. This will help ensure that the basic assumptions for the analysis have not changed and will permit changes when new conditions are encountered. In recent years improved methods of stability analysis have been accompanied by advances in laboratory testing techniques and new knowledge of the shear strength of rock discontinuities. At the same time there have been improvements in field geological descriptions. As more experience is gained in analyzing and predicting the stability of rock slopes, the importance of certain geologic factors has become more apparent. Some of these factors were described in a paper given at the Open Pit Mining Symposium in Johannesburg, South Africa in September 1970 (I). This paper includes many of the points covered at that meeting but with additional emphasis on the significance of the major geologic structures. Other papers given at the South African symposium also considered geological and hydrogeological factors in slope stability analysis (2) (3) (4) (5) (6). This paper first describes the approach to a slope stability problem including assessment of the relative roles of field geology studies, laboratory testing, stability analyses, and continued slope monitoring studies. Next, is described a framework which has been found useful for classifying or separating the several types of slope stability problems encountered in open pit mines. The principal geologic factors in slope stability problems in rock are discussed and brief comments are made on how these factors distinguish stability problems in rock slopes from those normally encountered in soil slopes. The over-riding control of major geologic structures, especially faults, in most slope stability problems is emphasized. In this regard the relative importance of statistical studies is contrasted with knowledge of the positions of key structural

Jan 1, 1971

By F. H. Kihlstedt

THE Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 6o per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in [ ] Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1946

By R. J. Sullivan

DURING the past twelve months the Loudon pool of the Eastern Interior Coal Basin has become established as one of the two largest discoveries since the revival of exploitation in the Illinois region and now occupies a position among the important pools of the United States. On Aug. 1, 1939, production averaged 54,000 bbl. per day from 990 wells, having accumulated a total of 10,305,000 bbl. Its very active develop-ment promises to continue for fully another year. It is the site of one of the industry's most singular large-scale gas-injection programs. LOCATION AND RESERVOIR CHARACTERISTICS At present the pool embraces an area 15 miles long by 3 ½ miles wide in eastern Fayette County, along the western rim of the now well-known Illinois Basin's deeper part, through townships 6, 7 and 8 north and ranges 2 and 3 east of the Third Meridian. It is the northernmost, and most prominent, productive structure of a group extending over a 50-mile trend southward to the Dix pool of Jefferson County. Three horizons have been proved to carry production-namely, the Weiler sandstone at 1390 ft., the Paint Creek sand at 1460 ft. and the Benoist or Bethel, at 1500 ft. Geologically, they fall in the Chester series of the upper Mississippian system, where much of Illinois' early-day oil was found, having been laid down in shallow off-shore waters as a part of the vast delta deposit underlying central Illinois and parts of Indiana and Kentucky. As a result of this type of sedimentation, followed by repeated uplifts and warping along an anticlinal axis, differ-ential deposition of sands and shales contributing to great irregularity took place. This is further reflected by wide variations in permeability, porosity and thickness of all the sands and, accordingly, in the producing characteristics of wells. Permeabilities range as high as 550 millidarcies, with the average commonly lying between 60 and 100. For the three pay horizons the mean porosity is 18 per cent, at a calculated water saturation of roughly 30 per cent. The Weiler sand has an average thickness of 25 ft., the Benoist of about 23 ft. and the Paint Creek of approximately 18 ft. Of these three productive formations the Benoist

Jan 1, 1940

By John H. Hollomon

THE interpretation of notched-bar impact results has been a matter of controversy since the introduction of more or less standard tests by Fremont,1 Charpy2 and others at the turn of the century. Many investigators3-l1 have contributed to the understanding of the significance of such tests. Several symposiums12,13 have been held with the express purpose of discussing the significance and interpretation of the impact tests. It is not the purpose of this paper to review all these contributions to the development of the knowledge on this subject, but rather to present an interpretation of notched-bar impact tests that appears to be in agreement with the available published data. Fundamentally, the interpretation discussed in this DaDer of the brittle failure of some steels in notched-bar impact test is similar to the qualitative analysis presented by Ludwik3 in the 1920's. Essentially, Ludwik stated that the function of the notch was to increase the tensile stress necessary for yielding, and that brittle failure occurred when the stress necessary for yielding exceeded the normal stress required for fracture (with no plastic de- formation). Ludwik, however, had no means of measuring this normal stress necessary for failure of a plastically* undeformed metal, therefore he could not extend his interpretation beyond the qualitative stage. Kuntze14 and recently MC- Adam15 attempted to determine the effect of deformation on the stress necessary for fracture by testing, in tension, specimens notched to various depths and angles. Because of the uncertainties in Kuntze's (and RlcAdam's) analysis of the stresses (which have been pointed out by SachsI6) and the inherent nonuniformity in the stress distribution in notched bars, the results of such investigations are difficult to interpret. A more direct method of measuring the effect of deformation on the fracture stress was suggested in previous papers17-l8 and has been utilized in the present investigation. The present paper concerns itself primarily with the behavior of notched impact specimens. The effects of strain rate, temperature, and stress distribution, which are discussed with reference to the impact specimen, apply just as well to the behavior of metal at the bases of notches in any engineering structure. All that is necessary is to determine the stress distribution in the structure at the base of the notches.

Jan 1, 1944