By Irving Cadoff, Kurt Komarek, Edward Miller

THE lead-telluride phase diagram as compiled by ansen' has one intermetallic compound, PbTe, with solid-solubility limits extending from 22 to 45 wt pct Te (31.4 to 57.1 at. pct). Pelzel2 redetermined the solubility limits on the lead-rich side of the compound by measuring the relative areas of the two phases in samples annealed in the liquid + compound region, and obtained data that agreed with that of Hansen. Recent studies of the semiconducting properties of PbTe3 however, have indicated that addition of either lead or tellurium to PbTe does not produce samples having carrier concentrations greater than about 10 19 cm-3. Assuming that each impurity atom results in one ionized charge carrier, this carrier concentration corresponds to a solubility range of less than 0.04 at. pct. Fritts and Karrar4 have also observed two phases in samples containing from 0.15 to 3.0 pct excess Pb. To resolve the discrepancy between these data, the solid solubility limits of the compound PbTe were reinvestigated, using several other techniques. Ten 25-g samples with compositions of 1/2, 1, 3, 5, and 10 wt pct excess Pb and Te and two 100-g samples of 15 and 65 wt pct Te were prepared, sealed in evacuated quartz capsules, and melted at 950oC. The 1 pct excess Pb and Te and the 15 and 65 wt pct Te alloys were homogenized for 96 hr at 450°C; the remaining specimens were annealed 50°C below the solidus temperature reported in Hansen. The specimens were polished and etched with dilute HNO,. All the samples were two phase, the second phase appearing at grain boundaries or as spheroidized inclusions in the grains. In the case of the tellurium rich specimens, the second phase could be identified as a eutectic. Debye-Scherrer powder diffraction patterns of the i, 1, 3, 5, and 10 pct excess samples were obtained using CuKa filtered radiation. The films were indexed as the B1 or NaCl structure. The calculated lattice parameter of PbTe was the same for all the specimens, with an average of a0 = 6.460 ± 0.0005A. Lines due to excess lead or tellurium were very faint but could be clearly seen in all the films. The relative areas of the two phases in the 15 and 65 wt pct Te samples were corrected for the differences in density of Pb, Te, and PbTe, and taken as proportional to the relative volumes of the two phases. The corrected relative volumes agreed with a phase diagram having negligible solubility of both lead and tellurium in lead tellurium. The density of the two specimens was obtained to give a third independent determination of the phase limits. The specimens were broken into small pieces to eliminate any internal porosity, and adherent air bubbles were removed by vigorous shaking under water for several hours. The density of lead (11.34 g per cm3) and of tellurium (6.25 g per cm3) was taken from the International Critical Tables and that of stoichiometric PbTe (8.25 g per cm3) calculated from the lattice parameter. For the 15 wt pct Te samples, the density assuming no solubility was calculated to be 9.89 g per cm3; the observed density was 9.86 g per cm8. For the 65 wt pct Te alloy, the density calculated for the case of no solubility was 7.24 g per cm3; the measured density wag 7.22 g per cm3. These results are consistent with those of planimetry and X-ray. SUMMARY Data have been presented which show that the solid solubility of both lead and tellurium in PbTe is

Jan 1, 1961

By H. C. Chang, N. J. Grant

Creep of very coarse grained high purity aluminum was studied at 400°, 700°, and 1100°F at initial stresses of 50 to 1200 psi. Local strain measurements were made across the grain boundaries and in different regions of various grains during creep, thereby permitting the drawing of component creep curves. The relative amounts of elongation as measured across a grain boundary and in the grains adjacent to the boundary depend on the temperature of testing. The significance of creep curve equations and activation energies is discussed. THIS paper presents some of the results of a research program devoted to the study of the mechanism of creep in high purity aluminum. Previous publications have dealt with the cyclic processes of alternating grain boundary sliding and migration, and the deformation in the grains caused by these processes;' the direction and the driving force of grain boundary sliding and migration;' the deformation in the grains and the restricting effects of the grain boundaries on this deformation." These previous papers were based mainly on either microscopic observations or X-ray data, or both. Sometimes creep curves across two closely spaced reference marks (about 0.6 to 0.7 mm apart) were also presented with a view to correlating the elongation values with the optical observations in general, and with certain deformation processes in particular. These curves shall henceforth be referred to as component creep curves. No attempts were made, however, to compare either the component creep curves which were obtained in different regions of a specimen, or those obtained from different specimens subjected to different creep test conditions. It is the purpose of this paper to present these component creep curves. Among the factors influencing the behaviors of these curves, those studied were stress, temperature, and grain arrangements in the specimens. It is proposed to show how greatly the deformation can vary from grain to grain and within an individual grain in a coarse grained specimen. The experimental technique and procedure have been presented.' It remains necessary to emphasize that the reference marks were produced by pressing a thin sewing needle into the surface of the specimen before the final annealing at 900°F for 24 hr and at 1150°F for 12 hr. The cold work around the needle indentations was therefore removed. The depth of these holes after electropolishing the annealed specimens was about 0.01 mm. This depth and area were negligible in comparison with the thickness of the specimens, 2.3 mm, and hence would not affect the creep behavior. Results Fig. 1 shows a development diagram of specimen P-8. The dots on the surface locate the needle point reference marks used to obtain the component creep curves. A curve obtained between two dots across a grain boundary measures not only the boundary deformation but also the deformation associated with boundary sliding occurring in the grains in the region between these indents. The original distance between two reference marks was about 0.6 to 0.7 mm. The maximum error of measurement was 0.01 mm, or in terms of percentage elongation, of the order of & 1.5 pct. Whereas the component creep curves shown in the figures to follow were drawn as a gross average of the points, in view of the fineness of some of the steps of grain boundary sliding and migration, as shown in the previous publications,¹,2 it appears logical to expect that some of the finer cycles of movement have not been delineated for the strain sensitivity of the measuring system. It seems justifiable to say that the curves are not as smooth as shown. 700°F Tests: Fig. 2 shows component creep curves across four of the grain boundaries in specimen P-8, tested at 700°F and 85 psi. These curves clearly show alternate cycles of increasing and decreasing

Jan 1, 1954

By J. P. G. Farr, R. Brownsword

THE role of solute segregation in the formation of cellular solidification substructures in tin and its dilute alloys is well-established, see, e.g., Ref. 1. Segregation has been shown to persist during cooling, enabling solidification structures to be studied from sections taken at some distance behind the interface. In the present work, a single crystal of commercial nickel, 99.965 pct, was examined in this way. The crystal was cut from the center of a rod given a single pass in an electron beam floating zone melter. Polished sections of a nickel specimen taken normal to the growth direction showed a very fine precipitate phase, the distribution of which varied over the section. The identification of the phase proved difficult because of the small amount present and the small particle size, about 1 p: but it was shown by probe microanalysis to contain only nickel and oxygen in detectable concentrations and was probably nickel oxide, NiO. Bulk analysis of the material before melting showed there to be only 3 to 4 ppm of oxygen present, thus demonstrating a very considerable segregation concentration effect. In some areas of the section the precipitate formed a discontinuous hexagonal network suggesting decoration of the cellular boundaries known to be present in the sample2 whereas in a restricted region the precipitate formed small clusters. Occasionally it could be seen that the clusters were at the intersections of an hexagonal network of cellular dimension. It was suggested3 that this was the result of enhanced segregation to the cell boundary intersections whereas general cell boundary segregation was insufficient to give a precipitate. Enhanced nodal segregation has since been demonstrated in a number of systems.1, 4-8 The development of a suitable electrolytic etching technique (perchloric acid 20 pct v/v; ethyl alcohol 70 pct; glycerol 10 pct; current below electropolishing plateau; 1 to 2 sec etching) suggested the association of the phase with regions of solute segregation (where ko < 1); in these regions anodic attack produced grooves or depressions. In a study of the variation of solidification substructures with degree of constitutional supercooling, Biloni et a1.&apos; appear to have used standard growth conditions and varied the solute concentration. They were able to produce in a series of individual tin crystals examples of substructure ranging from planar interface through various cellular structures to den- Fig. 1—Electroetched section taken normal to the rod axis; the center of the rod lies to the left and the periphery to the right of the micrograph. The variation of structure across the section is evident. Magnification 60 times. drites. It was possible in the present nickel crystal to observe a continuous range of substructures varying with degree of supercooling across a single section as shown in Fig. 1. Growth rate, 13 mm per min, and temperature gradient were essentially constant; the variation in structure is thought to be due to a radial gradient in solute concentration ahead of the solid interface. The liquid at the interface is likely to have been richer in solute toward the periphery of the zone, the result of curvature of this interface. The type of substructure was seen to vary with increasing constitutional supercooling as follows: a) region free of precipitate. top left, Fig. 1: 6) region of nodal precipitates which became arranged in hexagons on passing from the center of the rod: c) irregular hexagonal cells with incomplete boundary precipitation; d) regular hexagonal cells of decreasing size with complete boundary precipitation. Fig. 2 shows the transition from stage 6 and Fig. 3 shows the structure in stage d. Within stage 0, the range of conditions over which irregularly positioned nodes occur appears to be small and the nodes are soon recognizable as taking up positions at the intersections of an hexagonal network as the supercooling increases.

Jan 1, 1970

By J. Pinto, F. Galasso

THE current emphasis in preparing boron fibers by reduction of gaseous boron compounds on a resistively heated metal wire substrate has renewed interest in the borides of those metals which have relatively high melting points and are available as fine wires. A knowledge of the structures and properties of the borides, which are formed when boron diffuses into the metal core during boron deposition, can be of assistance in the understanding of the boron fiber formation process and the fiber properties. Many of these borides are well-known and their properties have been measured. However, when an unidentified boride is found in the core, it may be difficult to establish its composition because of the small amount of material available, the preferred orientation effects on the reflections in its X-ray pattern, and the possible overlap of X-ray reflections if several borides are present in the core. For example. the proper indexing of the X-ray pattern of WB4, which was formed in the tungsten substrate core during boron fiber formation, was accomplished only after small single crystals of this boride were grown and X-ray precession investigations were conducted.&apos; This note presents the results of a study of the phases formed in the core when tungsten, tantalum, and molybdenum metal wires were used as substrates in the boron fiber preparation process with particular emphasis on the identification and characterization of a higher boride of molybdenum analogous to WB,. Boron was deposited on resistively heated stationary 0.0012-in.-diam tantalum, tungsten, and molybdenum wires at 1050°C for various times up to 60 sec using boron trichloride and hydrogen as the reactant gases. After 60 sec of boron deposition the fibers were approximately 0.006 in. in diam. Examination of photomicrographs of fiber cross sections showed that the boron had diffused nearly to the center of the tungsten and molybdenum cores in 15 and 30 sec, respectively, and only halfway to the center of the tantalum core in 60 sec. X-ray diffraction photographs of the fibers indicated that it was also after 15 and 30 sec deposition times that the tungsten and molybdenum metal reflections, respectively, had disappeared from the X-ray patterns of the fibers. The patterns of the boron fibers produced using tantalum wire as a substrate showed that amorphous boron, TaB2, and tantalum metal were present after a few seconds deposition time and remained even after deposition times of 60 sec. Until a deposition time of 15 sec was reached, the tungsten substrate fibers contained amorphous boron,273 6WB, W2B5, and WB4 as well as tungsten metal, while the molybdenum substrate fibers contained amorphous boron, MoBa, Mo2B5, and molybdenum metal for deposition times up to 30 sec. Just before the molybdenum metal pattern disappeared, a pattern similar to that of WB, appeared, suggesting that a phase, MOB,, isomorphous with WB,, was present in the fiber. This same pattern was obtained from the product formed by heating a mixture of molybdenum metal and excess boron powder in a boron nitride crucible at 1960°C in an argon atmosphere. As was the case with the WBn pattern, this pattern could best be indexed on the basis of a hexagonal unit cell rather than the tetragonal unit cell Chrktien and Helgorsky reported for ~0~4,~ see Table I. The unit cell parameters for MoB4 were calculated to be a, = 5.214A, co = 6.358A. Assuming the space group P63/mmc and positions5 2M01 in 2b and 2MoII in 2c found for tungsten in WB~,&apos; a logical structure for MOB, was determined using geometrical considerations to place the boron

Jan 1, 1969

By Thomas E. Wayland

AN isopachous map is one on which lines connect points of equal thickness of a given unit. This type of map is used by the Florida Phosphate Project of the U. S. Geological Survey to represent the economic phosphate deposits known as matrix and the waste material, or overburden, that overlies the matrix. The top of the bed on which the phosphate was deposited is known as the basement and a subsurface contour map of this old buried erosion surface is known as a basement map. Recent experiments have been made in preparing maps that show tonnages and grades of the phosphate content of the matrix. Few of the operating companies in the Florida phosphate district have applied isopachous (Greek isos, equal and pachys, thick) to mapping. The writer believes there is a need for the techniques discussed herein and that they can be applied to mapping other geologically similar areas in either economic or scientific investigations. The land-pebble phosphate district of Florida occupies a compact area in the west-central part of the state. It includes mainly the following land survey divisions: Ts. 27 S. through 32 S. and Rs. 20 E. through 26 E. The town of Mulberry, Fla., is in the approximate center of the district. The strata of the area, which is part of the Gulf Coastal Plain, occur in thin formations with broad outcrop belts, and low dips. The topography is subdued and gently rolling with three marine terraces, which are found at 30, 100, and 150 ft above sea level,&apos; accounting for most of the relief. Occasional small sinkhole lakes are present, most of them above the 150-ft shoreline. The phosphate deposits occur in unconsolidated sediments such as clays, sands, and sandy clays. They are overlain by a heterogeneous assemblage of sands, clays, muck, and iron-cemented sand, easily penetrated, in most cases, by a hand auger or drill. Limestone, locally called bedrock, or a calcareous bedclay, thought to be a residue of the limestone, directly underlies the phosphate deposits. General Requirements Most companies and independent prospectors operating in the district have furnished prospecting data to the U. S. Geological Survey. The information is recorded on either field logs or prospecting maps and includes the following information for each hole drilled: location of the hole, thickness of the overburden, thickness of the matrix, phosphate content in long tons per acre, grade of the phosphate content expressed as the percentage of bone phosphate of lime (P2O5 x 2.18) or BPL, and the per- centages of iron-aluminum oxides and insolubles. The phosphate is classified according to size as either pebble or flotation material. The milling processes of the companies vary, and the size classification is necessarily different in many cases. However, pebble may be considered as larger than 14 mesh and flotation material as smaller than 14, but larger than 150 mesh. Some prospecting data include the exact depth at which bedrock or bedclay was reached, and these figures greatly increase the reliability of the data both for isopachous mapping and for mapping the basement. A drilling density of four holes per 40 acres of land furnishes a minimum amount of data for isopachous and related mapping. From the minimum of four, densities up to 32 holes per 40 acres are used. The various drilling densities may influence the choice of the proper scale. Selection of the proper scale is dependent upon the known drilling densities, the subsurface variations to be shown, the extent of the area to be mapped, and the detail desired in the completed map. Scales of 1:24,000, 1:4800, and 1:2400 are used in isopachous and related mapping by the Florida Phosphate Project. The 1:24,000 scale is used most effectively with drilling densities not exceeding eight holes per 40 acres. The subsurface variations should be relatively low and uniform, permitting the use of smaller intervals without undue crowding of the lines. Comparatively large areas can be mapped on this scale, but minute detail is necessarily sacrificed, because the information is drawn from a maximum drilling density of only eight holes per 40 acres. Isopachous and related maps of the 1:4800 scale are made of areas on which the drilling information covers from 4 to 16 holes per 40 acres. Moderate subsurface variations with relatively sharp gradations can be shown accurately. The area represented by the maps is reduced considerably in favor of detail. The 1:2400 scale is most frequently used by the Florida Phosphate Project. It lends itself particularly well to isopachous and related mapping, being easily adapted to the multiform drilling data available. Maps of this scale are prepared with information ranging from 4 to 32 holes per 40 acres; however, use of the minimum drilling density on the

Jan 1, 1952

By Archer Wheeler

The Boston & Montana Reduction Works at Great Falls, Mont., was formerly the reduction works of the Boston & Montana Consolidated Copper & Silver Mining Co., and continued as the reduction plant for the independent company until .June 1., 1910, when the consolidation of a large number of the operating companies of Butte was effected. It then became merged in the Anaconda Copper Mining Co. as the Boston Montana Reduction Department of the Anaconda Copper Mining Co. The history of copper converting at this plant, while not covering the entire period of the commercial use of the process in this country, does cover by far the larger part of it, and as the operations and appliances of the process have undergone many changes during the time, it may, perhaps, be of some interest to put the record of these changes into permanent form. The plan followed in the preparation of this paper has been to give first a brief chronological record of the principal events and changes and then, even at the risk of some repetitions, to give more detailed account, of some of these changes under separate headings. The headings for the complete paper are as follows: 1. General Chronological Review. 10. Development of Different Classes 2. Mechanical Manipulation of Converters After Class I. 3. Casting of Finished Copper. 11. Basic Lining. 4. Tamping of Linings. 12. Number and Size of Tuyeres. 5. Early Acid Linings. 13. Cast Copper Tuyeres. 6. Acid Linings With the Use of Ore. 14. Efficiency of Air. 7. Introduction of Flux Through the 15. Size of Converter Mouth. Tuyeres 16. Height of Converter. 8. Bottom Blast. 17. Summary. 9. Disposal of Converter Slag.

Jan 8, 1913

By Oliver Smalley

EXCEPT for the work of Guillet, who conducted a systematic investigation on the zinc-replacing value of nickel in brass, and extended his investigation with a view to developing commercial high zinc content nickel brasses, the author does not know of any systematic research on the subject. The most promising commercial alloys and their physical properties obtained by Guillet are given below: Maximum Elonga- Reduction Copper Zinc Nickel Stress, tion, of Area, Brinell Tons Per Per Cent. Per Cent. Sq. In. 55.0 41.0 5.0 24.4 46.5 94 Sand cast. 22.6 27.0 90 Chill cast. 56.7 39.74 3.35 30.0 43.0 51.7 97 Casting annealed 2 hr. at 750° C. 33.9 33.0 50.7 144 Cold-drawn bar. 55.15 42.3 2.24 29.8 33.0 116 Casting annealed 2 hr. at 750° C. 32.3 29.0 151 Cold-drawn bar. These test results scarcely justify the use of such quantities of so expensive a metal, and could have been obtained from ordinary commercial brass. For purposes of comparison, the physical properties of ordinary brasses, ranging from 70 per cent. to 50.1 per cent. Cu in both the cast and normalized1 conditions are included in Table 1. These incidentally furnish a useful standard of the properties of castings and of rolled, extruded and forged brass when correctly annealed. A close study of some of the well-known special brasses containing nickel reveals a series of alloys which bewilder by their complexity, and one can only hazard a guess at the function and commercial value of each of the many elements used.

Jan 10, 1925

By R. A. Harrington

THE structure of anodic films formed on aluminum and other metals under varied conditions is not well known despite the wide use of such films both as protective coatings and as the dielectric medium in elec-trolytic condensers. The present work was undertaken as a survey of the possibilities of electron diffraction in the investigation of anodic films, especially in comparing the properties of anodic films formed under dif-ferent sets of conditions and subjected to various subsequent treatments. In addition, an effort has been made to compare surface films formed on aluminum by anodic treatment with surface films formed by heating, immersion in chemicals, etc, The electron diffraction method in many cases has been successfully applied to the study of thin surface films. Its principal advantage is that it can be used without removing the films from the base material upon which they have been formed. The low penetrating power of electrons, in the "reflection" diffraction method which has been used in this work, prevents the appearance of diffraction patterns from substances at depths greater than about 100 Angstrom units (10-6 cm.). Different investigations of the structure of anodic films have shown widely varying results, depending on the methods used in preparing the films. Apparently under some conditions these films are crystalline and under other conditions they are amorphous, and it has been difficult to say which type of structure will be found in any particular case. Schmid and Wassermann&apos;s&apos; X-ray diffraction patterns of eloxal? films show two broad, diffuse bands, which these investigators attribute to finely divided cubic y-Al2O3-§ Burgers, Claassen, and Zernicke3 obtained sharp X-ray

Jan 1, 1940

By R. B. Yerxa, C. F. Green, H. O. Hofman

MASSACHUSETTS INSTITUTE OF TECHNOLOGY, In refining copper, the metal is melted down in a reverbera tory furnace in a more or less oxidizing atmosphere and then further subjected to an oxidizing smelting in order to eliminate the common impurities, most of which have a stronger affinity for oxygen than has copper. In these operations some of the copper is oxidized to cuprous oxide and dissolved by the metal bath. When the quantity of dissolved cuprous oxide has reached about 6 per cent, the metal is said to have been brought to " set-copper." A button-sample will show a depressed surface and, when broken, a single bubble at the apex of the depression; the fracture will be brick-red and dull. It is essential to carry the oxidation to this point in order to know that the impurities have been oxidized as far as it is possible under the given working-conditions. Nearly all the cuprous oxide of the set-copper is now reduced to the metallic state by poling, when "tough-pitch" copper will be obtained. A button-sample will show a flat surface. Upon breaking, it will be found that the former bubble has disappeared and that the fracture has become rose-colored and shows a silky luster. The quantity of cuprous oxide allowed to remain in the copper will vary with the impurities still present in the metal and with the degree of pitch that it is desired to reach. It is essential for the general physical and the mechanical properties of the resulting copper that such impurities as arsenic, antimony, bismuth, lead shall be present in the oxidized state, as they are

Jan 1, 1904

By J. W. Spretnak, G. Sachs

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By G. Sachs, J. W. Spretnak

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By Frank R. Corwin, Selden S. Rodgers

PAGE I. Introduction,........... 383 11. Brief History of Present MacDoUgall Plant,.... 384 III. First Experimental Work on Increasing Capacity of Furnaces, 385 IV. Effect On MacDouRall Plant of IncreaBed Draft from New Smelter Stack,,.......... V. Increasing the Capacity of the MacDouGall FurnaceS,.. 391 (A). Test of Arthur Crowfoot on Increasing Capacity,.... (a). Description of Test,........ (6). Discussion of Results Obtained from Test,... 393 (B). Investigation Carried Out by John A. Church, Jr.,... 395 (a). Advantages of High Speed,......398 (C). Effect on Regular Operation of Department by Applying Results Obtained from Experimental Work ..... 399 (D). Fundamental Principles Involved in Increasing the Tonnage, . 400 VI. Treatment of an INcreased Amount of Ore Screenings,.. 401 VII. Maximum Percentage oF Ore Screenings in a MacDoUGall Feed, 403 VIII. Tests to Further Increase Capacity of Furnaces,... 406 IX. Tests to Decrease PercentaGe of Flue Dust made by MacDouGall Furnaces,............. (A). Repath-Marcy Furnace......... 408 (B). Modified Hepath-Marcy Furnace,....... (C). Crouse Furnace Designed for Dust Prevention,.... 413 (a). Tests on Crouse Furnace,....... X. Concrete Hearths,.......... 419 XI. Conclusion,............ I. Introduction. Since the first installation of MacDougall roasters at the Great Falls smelter of the Anaconda Copper Mining Co., the capacity of the furnaces.has been more than doubled. During the first nine or ten years of the operation of the MacDougall department the tonnage treated by the furnaces remained practically unchanged. Experimental work carried out in 1906, however, showed that increasing the draft of the furnaces would bring about an increase in capacity. In 1909 the MacDougall department was connected to the new smelter stack and

Jan 1, 1914

By Glenn C. Waterman, Scott Hazen

3.1-1. Purpose. Development drilling is directed towards determining the grade, volume, and three-dimensional outline of a mineralized zone previously located by exploration. It is distinguished from exploration or reconnaissance drilling, which has as an objective the discovery of new mineralized areas. A development drilling and bulk sampling program should furnish the following information: 1. Geology of the mineralized zone. 2. Quantitative data on grade and tons of material within pertinent cutoff limits. 3. Physical size and shape of the deposit. Areas underlain by waste as well as ore. 4. Mineralogica1 and metallurgical characteristics of the ore. 5. I1hysical characteristics of the ore. 6. Hulk samples for metallurgical testing and grade check. 7. Data on other factors that could affect mining operations, such as ground water, ground conditions, etc. 3.1-2. Procedures. There are numerous methods and techniques that are used to acquire pertinent data on a potential ore deposit. The total cost and accuracy of a development program depends on significant evaluation of the geology, proper selection of a drilling method, thorough analysis of sample data, and accurate evaluation of all the information. Knowledge of the geology of the mineral deposit is important in planning the development testing program and in evaluating the data obtained from such a program. Exploration work usually provides some significant information on the general size, shape, thickness, grade, and geology of the deposit. In some cases no further data are needed; in many cases geological complexities suggested by the preliminary work require further geological study. Of considerable importance may be the following:

Jan 1, 1968

By H. I. Altshuler

THE mines operated by the Compañia de Real del Monte y Pachuca, Pachuca, Mexico, are in two districts, the Pachuca, and Real del Monte. The principal area of mineralization is within a rectangle roughly 10 miles from east to west and 6 miles from north to south. It contains a number of veins from 2 to 20 ft. wide, which are exploited by this mining company. The scattered position of the producing mines led to the construction of two mills between 1906 and 1908; the Loreto mill, in Pachuca, averaged 2600 tons daily, and the Guerrero mill, in Real del Monte, milled 1270 tons daily. On Feb. 1, 1929, the management decided to enlarge the Loreto mill to take the combined tonnage of both mills at that time. This economic measure required the centralization of ore delivery, which would also afford a material saving in the cost of ore transport. The centralization would give the company the following advantages over the former system of operation: 1. Beneficiation at a single mill, closer to source of materials and supplies than the abandoned- Guerrero mill. The refinery is, also in the Loreto patio. 2. Ore delivery to surface at one point (San Juan Pachuca shaft) instead of at four. 3. Elimination of aerial tramways. To show what would be required to effect this centralization, it is necessary to describe the means by which the ore was delivered to the two mills, prior to centralization. The heart of the Real del Monte district is roughly four miles from that of the Pachuca section. The producing mines in these two districts were: Pachuca district: Santa Ana mine Camelia group

Jan 1, 1934

By C. H. Mathewson

ABOUT fifty pages of Henry M. Howe&apos;s profound treatise, "The Metallography of Steel and Cast Iron," are devoted to twinning with special reference to the origin, nature and general significance of the Neumann bands in ferrite. Howe believed with Osmond and Cartaud1 that the Neumanns are mechanical twins and his careful observations leave no doubt that these straight-sided narrow bands habitually occur parallel to trapezohedral planes of form {211}. Attempt&apos;s to develop the structure of the bands by various methods so that their identity could be established beyond question have not been conspicuously successful. Howe thought that they deflected slip bands. Some of the etching figures which have been developed within and adjacent to Neumann bands support the contention that they are twins. A good example of this effect in ferrite containing 0.6 per cent. of nickel and 1.3 per cent. of phosphorus, originally due to Harnecker and Rassow,2 was reproduced in. the 1928 lecture before the Institute of Metals Division on twinning in metals.3 In this case, the sides of the figures might represent the traces of cubic planes laid bare by etching a properly oriented grain of ferrite, twinned along a plane of form {211}. Our own observations in this direction may be represented by Fig. 1 which shows in a deeply etched cavity in the boundary region between a Neumann band and the original crystal two small crystal surfaces which resemble the faces meeting at a reentrant angle in the simple cube twinned along a bisecting plane of form {211} as sketched in Fig. 2.

Jan 1, 1928

By R. M. Brick

AN increased demand for information in regard to the effect of gaseous elements in steel has accompanied the recognition of the importance of grain size. Attempts to correlate grain-size characteristics with gas con-tent, particularly oxygen in solution or in the form of included metallic oxides, have not been universally successful. Certain definite effects of dissolved gases are recognized; specifically, the role of hydrogen in causing internal cracks or "flakes" and that of nitrogen in preventing excessive grain growth of ferritic chromium steels. When irregular behavior or properties are found in a well-known steel and no definite cause for the abnormality may be assigned on the basis of chemical and metallographic tests, dissolved gases are frequently blamed as the culprits. The solubilities of hydrogen1 and nitrogen2 in pure liquid iron are known but of the ternary systems, iron-alloying element-gas, only the Fe-Si-N3 and Fe-Cr-N systems have received attention and here the study was confined to liquid alloys. Krivobok4 published a curve show-ing the solubility of nitrogen in liquid Fe-Cr alloys but gave no informa-tion on the experimental procedure employed. The considerable experimental work reported on the Cr-N binary alloys has been reviewed by Hansen.5 It is generally agreed that the nitride CrN is a stable phase although the existence of nitrides within limited temperature ranges of stability, viz., Cr3N2 and Cr2N, has been disputed, Adcock6 and others7 have reported a eutectic between Cr and CrN at 1580°C., although the supporting evidence is not complete.

Jan 1, 1940

By Hugh Rose

The properties of the company lie within the Pachuca district, State of Hidalgo, Mexico, connected by three railway lines with Mexico City, 55 miles southwest, and by two lines with Vera Cruz, 250 miles southeast. The ores were formerly divided by sorting into two classes, smelting and milling, the former averaging about 2 oz. gold and 335 oz. silver, the latter 0.12 oz. gold and 23 oz. silver. The smelting ores were sold to custom plants, principally the American Smelting & Refining Co. at Aguascalientes. The milling ores were treated by the patio process at the Guadalupe Hacienda, at Pachuca. This patio was probably the largest in existence at the time and continued in active operation up to March, 1910. In January, 1910, the mines and patio were sold to English interests, represented by Camp Bird Limited. Two new companies were formed, the Compania de Santa Gertrudis, S. A., to operate the mines, and the Compania Beneficiadora de Pachuca, S. A., to build and operate a custom cyanide milling plant. (Pig. 1.) Geology The historical geology of the Pachuca district is described by Fred J. Pope as follows: 1. The most recent sedimentary rooks in the district belong to the Cretaceous period. 2. The Cretaceous rocks were penetrated by large intrusions of ande-site (referred to hereafter as primary andesite) which occur as elliptical dome-shaped masses, striking northwest-southeast. These andesite bodies are from 8 to 15 miles long and from 6 to 10 miles wide. 3. A period of erosion during which the contour of the andesite domes was changed. 4. Andesite flows (secondary andesite) which rest unconformably on the primary andesites.

Jan 1, 1917

By Robert L. Akright

LOCATION AND HISTORY The Candelaria silver mine is located in an arid, isolated desert setting in Sections 3 and 4, T.3N., R.35E., and Section 33, T.4N., R.35E., Mineral County, Nevada (Fig. 1). Silver was discovered in 1863 by Mexican explorers, and high grade silver veins were mined from the early 1870s through the 1880s. Essentially all mining had ended by 1890. The veins were mined by underground methods typical of the period. As is the case in many mining districts, Candelaria was studied and explored by a number of companies. All these efforts were terminated short of mine development because of low silver prices and difficult metallurgy. On March 1, 1976, Occidental Minerals (Oxymin) entered into a Limited Partnership agreement, known as Candelaria Partners, as General Partner with Congdon and Carey Ltd. No. 4. Prior to the agreement, Congdon and Carey had acquired the candelaria properties as part of a bullish silver program and did considerable exploration which indicated the possibility of a large reserve of shallow silver mineralization. GEOLOGY AND ORE DEPOSITS Silver and gold mineralization in the Candelaria district occurs in high-grade fissure veins with silver values ranging from 0.6 to 7.8 kg/t (20 to 250 oz per st). These veins, combined with the low grade disseminated mineralization in the intervening material between the veins, form Manto- like deposits 15 to 46 m (50 to 150 ft) thick. Three such deposits are found in the Candelaria district: the Lucky Hill, Mount Diablo, and Northern Belle deposits (Figs. 2 and 3). The average ore grade of the Lucky Hill and Mount Diablo [ ]

Jan 1, 1985

By H. M. Howe

On commencing the construction of the Orford Company&apos;s copper smelting works, at Bergen Point, N. J., I endeavored to convince our President, Mr. W. E. C. Eustis, by actual tests, that at the pressure of from 15 to 18 ounces per square inch, employed by us in smelting, less power was consumed in delivering a unit of blast by a Baker blower than by a fan blower. I attempted to prove this in the following manner: Across the mouth of a No. 5) Baker blower I firmly fastened a board with two round holes, 6 inches in diameter, cut in it. The board was fastened so tightly that no air could escape except through the holes. I then drove the blower at several differerent speeds, observing the pressure at which the air excaped through the two openings for each different speed of the blower, and also indicating the engine, whose only work at that time was to drive the blower. From this I calculated the quantity of power required to deliver, with a Baker blower, sufficient air to keep the pressure at a given point, while it escaped freely through the two six-inch apertures into the open air; or, in other words, to deliver air at a given pressure through these two openings. From the total power so consumed it was, of course, necessary to deduct the power which was required to drive the engine itself. This was ascertained by removing from the engine the belt which drove the blower, and then noting the quantity of power consumed in simply turning the engine over without any

Jan 1, 1882

By R. C. Hirschfeld, H. H. Einstein, R. W. Bruhn, R. A. Nelson

The objective of the model studies described in this paper is to determine the effect of planar discontinuities on the strength and deformability of a rock mass. A model material was used because it satisfied concurrently three requirements that available natural-rock samples did not: (1) low strength, which was desirable for minimizing the loads that had to be applied in the laboratory; (2) ease of producing test specimens with geometrically regular joint patterns; and (3) uniformity of the test specimens. The model tests were performed on specimens made from a single modeling material and tested under triaxial stress conditions with [u,=u,]. Results are presented in this paper for tests on specimens that had (1) a single joint set inclined at several angles to the major principal direction, including 0º and 90°, and (2) two joint sets that were mutually perpendicular, one set perpendicular to and one set parallel to the major principal direction. Several different joint spacings were used in each series. Future tests will include a series with two sets of joints that make oblique angles with each other and with the major principal direction. The results of model tests and tests on cores of jointed rock by several investigators (e.g., Müller and Pacher,l Moore,2 Krsmanovic and Milic,3 Hayashi,4 Rosenblad,5 Jaeger,6 and Lane and Heck 7, have contributed significantly to the design of these experiments, which are believed to be the first in which a comprehensive study has been made of the combined effects under triaxial loading of joint spacing and joint orientation (Fig. 1).

Jan 1, 1970