By J. A. Snyder, W. L. Finlay

G. Edmunds—Solid solubility is considered to be of either the interstitial or the substitutional type. Is it possible, in a binary alloy as the simplest case, that some of the solute atoms are present in the normal lattice sites (substitutionally or filling lattice vacancies) while simultaneously others are in interstitial positionss One might even ask whether a distribution of the two types may be the normal situation. H. M. Meyer—Metastable states of interstitial atoms occupying vacant lattice sites possibly occur as well as of substitutional atoms squeezed in between regular matrix positions. However (as we know since Hume-Rothery), the solute atoms choose between the two kinds of solutions; consequently, every solute will be unequivocally either substitutional or interstitial in the equilibrium state of the solid solution. M. Balicki—In view of the fact that the authors apparently correlate the analysis of the alloys at the ingot stage with the properties exhibited at the testing stage, I would like to ask whether this is a fully justifiable procedure. In other words, how good are their determinations of solute concentration for correlating them with the mechanical properties. The answer to this question may explain some of the divergencies. Assuming good enough homogenization of the samples and exact determination of mechanical properties the position of the plotted experimental points will depend solely upon the accuracy of composition determination. If this is not accurate, say due to loss or pickup of elements during processing from the ingot to the testing stage, or due to a systematic error in the method employed for obtaining solute concentration data, the points will deviate from their true position and may align themselves along a different curve than the one expected. H. V. Kinsey—We have been studying the creep-rupture properties of titanium-base alloys at 1000°F. In the course of this work, anomalies in behavior of the alloys that would suggest that the material under test was becoming stronger as the test progressed have been observed. If this was so, the most likely explanation that we could think of was that the test bars were absorbing oxygen and nitrogen from the air during the test and were thereby becoming strengthened. In an attempt to determine the strengthening effect of absorbed oxygen and nitrogen the following experiment was conducted. A length of cold-rolled titanium was supplied by the E. I. du Pont Co. Two test bars, having a 1/4 in. diam gauge length, were prepared from this material. One bar was tested in the as-received condition. The second bar was heated in air at 1550°F for 100 hr and subsequently air cooled prior to testing. A testing temperature of 1000°F was employed. The results of these tests are tabulated in table 11. In the author's opinion, is it reasonable to assume that the bar that was exposed to air at 1550°F for 100 hr was stronger because it absorbed oxygen and nitrogen from the air during this heat treatment? W. L. Finlay (authors' reply)—Direct experimental evidence for or against Mr. Edmunds' interesting suggestion will probably never be available. It seems possible, however, that mixed interstitial-substitutional solid solution might well occur with interstitial elements. The less likely possibility of interstitial solution of a normally substitutional element like copper in aluminum was recently discussed at length by the

Jan 1, 1951

By R. V. Colligan

[CONTENTS PACE Educating and Training Economic Geologists of the Future. By C. H. BEHRE, JR. (TP 2278, Min. Tech., Nov. 1948. Discussions by R. V. COLLIGAN and EVAN JUST) ....... I Mercury Industry in Italy. By EDWIN B. ECKEL. (TP 2292, Min. Tech., Jan. 1948. Discussion .............................. by C. N. SCHUETTE) 3 Chert in the Kingsport Formation at Mascot, Tennessee. By ARTHUR T. ALLEN. (TP 2299, ............... Min. Tech., Jan. 1948. Discussion by M. M. BUTLER) 5 Wall Rock Alteration at Butte, Montana. By RENO H. SALES and CHARLES MEYER. (TP 2400, Min. Tech., May 1948. Djscussions by C. D. HULIN, W. D. JOHNSTON, JR., and L. C. ................................... GRATON) 5] Educating and Training Economic Geologists of the Future R. V. COLLIGAN*-I can best illustrate my opinions by drafting another five year plan (Table 2). This plan is set up following the same stipulations outlined by Dr. Behre, namely: (I) the student is preparing himself for commercial work as a mining geologist; (2) he is attending an institution with a sufficiently broad curriculum (that is, engineering school and mining school as well as liberal arts college) to furnish the courses listed; and (3) he is not planning to continue his studies through to a doctor's degree before going into commercial work. A comparison of my study plan (Table 2) and that submitted by Dr. Behre (Table I) will at once point up the basic similarity, due to the obvious fact that there are so many essential courses which must be included in any outline of study. However, a more detailed analysis will show up certain differences, which, in fact, are only certain refinements on Dr. Behre's program. These I plan to discuss in order of their importance. The first and most important change is the addition of 12 hr of optional subjects, making a total of 24 hr of optional subjects as against a total of 12 hr under Dr. Behre's schedule. This of course entails the elimination of certain courses, which I shall discuss later. However, I wish to make it clear that I suggest eliminating these courses not because I feel that they are unnecessary, but rather because I feel the optional courses are more necessary to the complete education of the individual. I appreciate that Dr. Behre recognizes the importance of the cultural side of education, but I take issue with his thesis that the student will get it without credit and in his spare time. I do not think that the average college student, and certainly not the college freshman, is mature enough to know what he needs and where to get it in his spare time. I think it must be "spoon-fed"; he must be oriented through specific courses. University life (or should I say "college life") is too full of athletics, fraternity activities, dances, "bull sessions," and countless other enjoyable distractions, all of which contribute to the "full man." I fail to see how the average young American male can possibly sandwich in a necessary complement of "cultural activities" in his spare time. Since these latter activities do not fall within the pattern set by the "group," and show less promise of immediate return in enjoyment, or increased social status on the campus, they are bound to suffer in competition with the more popular, "group" activities. No doubt much of the criticism levelled against arts colleges, namely, that the cultural courses are useless, is well taken, for the culture

Jan 1, 1947

By P. E. Phillips

INTRODUCTION Rocky Mountain Energy is the mining subsidiary of the Union Pacific Corporation, and has been active m uranium exploration since 1966. Since 1970, RME's uranium activities have been funded 50% by Mono Power, the fuels supply division of Southern California Edision. RME and Mono recognized the need for development of new methods for recovering low grade uranium deposits, and contacted Halliburton Services in regard to in situ leaching, because of Halliburton oil industry experience. As a result, a joint venture between the three parties was formed in 1974. BEAR CREEK The first ISL test was at the Bear Creek deposit in the Powder River Basin of Wyoming, about 60 miles north of Douglas. The mineralized sand is the tertiary Wasatch formation, which is an arkosic sandstone. The sand typically contains about 10% clay. The predominant clay being montmorillonite with some kaolin and illite. The roll front type trends occur along the flanks of old stream channels. This deposit was being considered for exploitation as an open pit mine. Routine amenability testing indicated it was quite amenable to a conventional acid leach, consuming about 50 lbs. of sulfuric acid per ton of ore in an agitation leach, while recovering more than 95% of the uranium. Hydrology testing indicated a permeability of about 1 darcy. The groundwater has a pH of about 8. 0 and TDS of about 1200. Test Facility The Bear Creek test was a summer-only operation, with no effort towards weather-proofing. Uranium was removed from the recovered leach solution by fixed bed ion-exchange columns. Loaded resin was eluted with strong sulfuric acid. The recovery plant was designed for simplicity of operation, with little concern for the grade or form of the yellowcake product. The plant was constructed of PVC piping and valves, fiberglass reinforced tanks, and stainless steel pumps. All waste streams were directed toward a lined evaporation pond. Wellfield The test pattern was a 30 foot radius 5 spot, with wells fully penetrating the 30 foot ore sand to a total depth of about 165 feet. The injection wells were three-inch PVC with slotted casing, while the producer was eight-inch I. D. , with a stainless steel screen. The eight-inch well was necessary in order to accommodate a six-inch stainless steel pump. Wells were cemented using cement baskets, at the top of the sand, to contain a latex acid resistant cement. Leach Conditions The lixiviant generally contained from five to seven gpl sulfuric acid, and about 0. 5 gpl hydrogen peroxide. The pH was generally 1.4 and EMF was usually -550 millivolts. Injection rates were rather variable from well to well, with a total injection rate between 12 and 25 GPM. Production rate was set at 25 GPM, since the production pump could not be throttled more than that. Approximately two pore volumes of solution were injected during the three-month test. Leach Results Injectivity was quite variable, but was generally rather poor, because of poor completion techniques. The problem stemmed from injecting before the injection wells had been completely cleaned of drilling mud. Pregnant solutions averaged about 50 ppm U308, with groundwater dilution varying from 10 to 50%, depending on the injection rate. Injectivity did decline with time, probably as a result of contamination of the well faces. A total of 1000 lbs U308 had been recovered when the test was shut down. This probably represented about 10% of the mineral under leach.

Jan 1, 1979

By R. R. Sayers

THE South African Mining and Engineering Journal recently pointed out that no satisfactory solution of the question of compensation for silicosis can be arrived at by placing further liability of an inequitable nature upon the mines. There are at present 35 scheduled mines liable to contribute to the annual levy of $800,000 and provide for the net outstanding liability of $6,400,000. Several of these mines have, as yet, not been able to set aside sufficient funds against their out- standing liability to the Compensation Fund. The gold producers declare that the gold mining industry today is passing its zenith, and that the production of gold will decline, with a consequent lessening of the spending power of the mines, which in about ten years will be reduced to a great extent unless encouragement is given for the opening of new mines. It is during this period of decline that the mines will be required to meet the large burden already created by miners' phthisis. In England the Workmen's Compensation Act, 1925, was extended to industries involving exposure to asbestos dust.

Jan 1, 1931

By J. S. Kasper, R. M. Waterstrat, B. F. Decker

THE existence of v phase in the Mn-Mo system was discovered in this laboratory several years ago,' but neither the conditions of its formation nor its composition were known, and preliminary attempts to reproduce the phase were unsuccessful. We wish now to specify the information appropriate to phase formation on the basis of experiments performed since that time. The starting materials were in every case electrolytic manganese and high purity molybdenum. Two methods of preparation were employed: l—arc-melting varying combinations of the elements in an inert atmosphere and subsequent heat treating, and 2—sintering compressed mixtures of finely divided powders of the elements. In the latter method, the powders were first passed through 200 mesh screen and then compressed into cylinders of % in. diameter and % in. length, which were sintered at elevated temperatures in an atmosphere of dry hydrogen. For some samples, the sintering temperature was 1200°C (for 1 hr), and these were then heat- treated at lower temperatures for times up to 24 hr. Eventually it was found, for the proper composition, that essentially pure a phase could be produced by sintering at 1125°C for 3 hr. Quenching to room temperature was effected by means of a stream of cold, dry hydrogen in a water-cooled chamber. The arc-melting procedure was found to be unsatisfactory after an investigation of many samples at different compositions and temperatures. Large quantities of manganese were vaporized during melting and none of the products were homogeneous or contained extended regions of pure phase. Nonetheless, these experiments established that no formation occurs in the Mn-Mo system below 1115oC, and indicated, at least roughly, the composition range of interest for further exploration. The more definite results obtained from samples produced by the second method are given in Table I. A portion of sample 2 heated for 16 hr at 1000°C in a Vycor tube transformed to molybdenum plus unidentified phases of complex X-ray pattern. From these few results it appears that the region of phase is quite narrow in composition. It is of interest that the composition is such as to make for difficulties in correlating this structure on an electron atom basis with other a structures of iron, cobalt, and nickel. In that respect Mn-Mo shows the same anomaly as Mn-Cr and Mn-V systems.' A second feature is that in common with the two other known molybdenum (Fe-Mo and Co-Mo), Mn-Mo v exists only at elevated temperatures. The X-ray powder pattern of the pure a phase of Mn-Mo is given in Table 11. It agrees well with the patterns established for other structures, especially with that for Fe-Mo as given by Goldschmidt.An attempt is being made to establish whether an ordering of the respective atoms occurs and such information will be reported in a future publication. Acknowledgment The authors acknowledge gratefully the assistance of Mrs. J. R. Belanger in some portions of this work. References 'J. S. Kasper, B. F. Decker, and J. R. Belanger: Journal of Applied Physics (1951) 22, p. 361. 2 A. H. Sully: Journal Inst. Metals (1951) 80, p. 173. H. J. Goldschmidt: Research (1949) 2, p. 343.

Jan 1, 1954

By Alfred Siegel

Mineral pigments give color, opacity, or body to paint, stucco, plaster, mortar, cement, linoleum, rubber, and similar materials. They must be finely divided, substantially insoluble, and generally inert for such uses. Inorganic pigments may be grouped somewhat arbitrarily as follows: A. Natural mineral pigments dug from the earth. 1. Those consisting mostly of iron oxides, such as hematite and limonite. 2. Those containing large amounts of clay or noncoloring matter, such as ocher, sienna, umber, and colored shales. 3. Those whose color is not due to iron oxide, such as Vandyke brown (including sap brown, an alkali extract of Vandyke brown), graphite, and terre verte. B. Synthetic pigments. 1. Those containing iron oxide as the essential coloring matter, such as "pure" reds, yellows, and blacks, and Venetian reds. 2. Those not containing iron oxide, but rather such compounds as lithopone, zinc white, titanium white, ultramarine, Prussian blue, and the like. Only groups A and B-1 are discussed here. All the pigments in those two categories, except Vandyke brown, sap brown, and some of the carbonaceous slates, contain, as their essential color constituents, one or more compounds of iron; namely, an oxide-limonite (2Fe2O3.H2O to Fe2O3.4H20), hematite (Fe2O3), or magnetite (Fe2O3.FeO). Man's first permanent coloring materials were earth pigments-the ochers, iron oxides, and various iron-stained clays. The caves occupied by prehistoric man and the arts of the ancient Chaldean, Egyptian, and Cretan civilizations bear mute witness to this and also testify to the beauty and permanence of earth colors. As the Roman era developed, earth pigments were pushed from their pre-eminent position by white lead and red lead and in the Middle Ages by zinc oxide. Today, of course, the number of acceptable pigments is very large and on a value basis the group of natural and synthetic earth pigments stands forth with $16,000,000 per year; it is surpassed by titanium, lead and zinc pigments. Of this sum,21 natural pigments supplied 31 pct of the tonnage and 16 pct of the value of the total finished pigment in 1957, the remainder representing the tonnage and value of sales of the synthetic iron oxide colors. The average value of finished natural pigments in 1958 was $80.62 per ton. The average value of manufactured pigments in the same year was $202 per ton. Of the 60,000 tons of manufactured colored pigments sold in 1958, the reds comprised 76 pct of the market and the yellows 20 pct. The reds furnished 68 pct of the value and the yellows 24 pct. Of the finished iron oxide pigments (natural and manufactured) sold in 1958, the reds dominated the market with 66 pct of the quantity and 63 pct of the value; yellows supplied 17 pct of the quantity and 20 pct of the value, and browns furnished 11 pct of the quantity and 10 pct of the value. The average value of the reds was approximately $152, and the average value of the yellows $190 per ton. The highest valued pigment in 1958, with almost 12 pct of the total tonnage and 21 pct of the value of the iron oxide pigment market, was manufactured red from calcined copperas valued at $286 per ton.

Jan 1, 1960

By John B. Myers

Vermiculite is the commercial name used to describe a micaceous mineral that expands appreciably when heated. This process, called exfoliation, results in a light weight material. The light weight material is also called vermiculite, or more exactly, expanded vermiculite. Practically all uses of vermiculite are for the expanded material. Composition and Properties Vermiculite, in its natural state, has the characteristic micaceous habit and a perfect basal cleavage and readily splits into thin laminae, which are soft, pliable, and inelastic. The monoclinic crystal faces are often marked by triangular lines at 60° and 120°. The hardness varies from 1.5 to 2 or more, depending on the composition. The specific gravity varies from 2.2 to 2.7; specific heat 0.2; fusion temperature 2,000° to 2,500°F; luster pearly to greasy; color amber, bronze, brown, dark green, and black. Feel is like talc and sometimes soapy when wet. When heated quickly at elevated temperatures, vermiculite exfoliates by expanding at right angles to the cleavage into long wormlike pieces (the name vermiculite is from the Latin vermiculari, to breed worms). This important characteristic of expansion is believed to be a mechanical separation of the layers when the contained water is converted to steam. The increase in bulk volume of commercially prepared material is 8 to 12 times, but individual flakes may expand as much as 30 times. There is no expansion parallel to the cleavage. Vermiculite may also be expanded by several chemical processes such as soaking in hydrogen peroxide, weak acids and other electrolytes. The color changes during expansion. Heat-treated material changes to a light golden bronze or cream color depending on composition. The conditions of heating affect color. Heating in an oxidizing atmosphere produces reddish colors and heating in a reducing atmosphere produces dull gray colors. The iron is generally not oxidized during chemical expansion. Vermiculite is hydrated magnesium-aluminum silicate. Although there has been much research on the chemical and structural composition, there is not yet complete agreement on the exact formula and composition. This is to be expected since vermiculite is not a mineral of fixed composition and different workers have examined different varieties. It has been proposed that vermiculite is not a single species but a family of related minerals. This has also resulted in many names for the particular vermiculite found in a certain deposit. All of this difficulty arises from the very nature of its crystal chemistry. Unlike most minerals, certain crystal structure properties and the chemical composition can be changed by the ordinary forces of nature or in the laboratory. This would suggest that vermiculite be thought of more as a variable mineral rather than a group of related species. It was stated on page 261 of this volume in the chapter on Clay Minerals by H. H. Murray of the Georgia Clay Co., that vermiculite is an equidimensional, expandable clay mineral. Gruner (ref. 14, Chap. 12) showed that the structure consists of a layer made up of two silica tetrahedral sheets with a central magnesium, iron octahedral sheet separated by two layers of water molecules and adsorbed magnesium and calcium ions. Mathieson and Walker,2a in a recent publication, agree that vermiculite must be regarded as a true clay mineral. The characteristic properties of the mineral, such as high cation ex-

Jan 1, 1960

There were present twelve- Directors, the Secretary and the Assistant Secretary of the Institute, and fifteen guests. A committee of three was appointed to draft a suitable resolution of memorial of the services of Joseph Esrey Johnson, Jr. The committee consists of Joseph W. Richards, Chairman, J. V. N. Dorr and Allen H. Rogers. William R. Walker was elected a Director in place of J. E. Johnson, Jr., and Edwin Ludlow was elected a member of the Executive Committee in his stead. George C. Stone was appointed Chairman of the Committee on Membership in place of Mr. Johnson. The following resolutions were then adopted: RESOLVED, That a special business meeting of the Institute be and the same hereby is appointed to be, held at the office of the Institute, No. 29 West 39th Street, Borough of Manhattan, City of New York, on the 27th day of June, 1919, it 8.30 o'clock in the P. M. to consider and take action upon the proposal to change the name of the Institute to "American Institute of Mining and Metallurgical Engineers, Incor-porated," and the further proposal to extend the corporate purposes of the Institute so that it shall, in addition to its other powers, be empowered to promote the arts and sciences connected with the economic production of the useful minerals and metals, and the welfare of, those employed in these industries, by all lawful means.

Jan 6, 1919

By AMY F. JENNINGS

TO give a concise history of the Woman's Auxiliary of the A. I. M. E. is a difficult task and much interesting information must needs be omitted. The organization has grown and evolved so much from its early simple beginning that it seems best to adopt the technique of some of our modern novelists and begin with the latest development. As the headquarters of the A. I. M. E. is in New York, it follows that the Woman's Auxiliary to the A. I. M. E. necessarily has also its central office and government there. The affairs of the organization are administered by a duly-elected president and five vice- presidents, a treasurer, recording secretary, and corresponding secretary and a board of directors, the personnel of which includes each chairman of a section or an elected or nominated representative who is able to attend the monthly meetings of the board and correspond with the section for which she acts, and the chairmen of the five standing national committees, i. e. Educational Fund, Library, Emergency, Membership and Hospitality. The chairmen of these committees are all responsible to the president and board of directors and their activities must be indorsed with their approval.

Jan 1, 1929

By Shiou-Chuan Sun

SHIOU-CHUAN SUN (author's reply).-Thanks are extended to Professor Hassialis for his recognition of the usefulness of a new tool, the cataphoretic cell, as an adjunct to the bubble machine and the abstraction test. His questions concerning adsorption, dielectric constant, floatability, activation, and depression are interesting and worthy of discussion. I According to Mueller,28 it is questionable that any of the present formulas gives absolute values of zeta potentials which are completely accurate. The problem is further complicated by the question" of whether the "dielectric constant" has any meaning at all for such a microscopically thin layer. With these in mind, the results in this paper should be considered in the relative sense as a first approximation and not as absolute quantities. Adsorption Referring to item a of Fig. 8, the dielectric constant and the viscosity of the xanthate solutions are the same for galena, sphalerite and quartz. If dielectric constant and viscosity (but not the adsorption) were the first-order variable of the cataphoretic system, as claimed by Professor Hassialis, then the magnitudes of zeta coefficient of galena, spha)erite and quartz would have been similar to each other. These are not. The big difference of zeta coefficient of these three minerals in the same xanthate solutions is not altogether unjustified to be attributed to their difference in adsorption of xanthate ions. This is supported by the results of chemical abstraction tests reported by Ince.14 Again, the big difference of zeta coefficient between wollastonite, calcite, and fluorite in the same laurylamine hydrochloride solutions (p. 118, Figs. 58, 59, and 60 of ref. r5) also indicates that the cataphoretic system is not governed chiefly by the dielectric constant. Beside the data shown in Fig. 8, other experimental evidences15 which support the idea of correlation between adsorption and zeta coefficient are: (I) there is a qualitative parallelism between the zeta coefficient curve and the chemical abstraction curve of sphalerite in solutions of various concentrations of sodium cyanide, (2) there is a qualitative parallelism between the zeta coefficient curve and the chemical abstraction curve of sphalerite in solutions of constant concentration of copper sulphate at different pH values, and (3) there is a qualitative parallelism between zeta coefficient curve and chemical abstraction curve of quartz in solutions with constant concentration of barium chloride at different pH values. The above mentioned experimental results are generally in agreement with Gouy's double layer theory,1-5 and support this idea that the concentration and the kind of ions adsorbed at the mineral surface and in the adjacent surrounding liquid chiefly govern the electrokinetic phenomena. Dielectric constant and viscosity of the liquid medium may be of somewhat lesser importance. It follows that the correlation between the coefficient and adsorption as claimed in this paper is justified. Dielectric Constant The term "dielectric constant " was first introduced into the electrokinetic equations by Perrin.30 In a footnote of his publication he states that Holmheltz has forgotten to include the dielectric constant. The conversion of the moment29 to the zeta potential involves an additional difficulty and confusion not involved for the moment, namely, assigning a value to the dielectric coefficient. This is conventionally assumed to be constant and equal to the dielectric constant of the bulk liquid. 21 The published literature 10, 12 indicates that the values of dielectric constant for dilute chemical solutions have been assumed as those of pure water.

Jan 1, 1947

By Stanly A. Easton

SEVEN years ago there was installed in the hospital of the Bunker Hill & Sullivan Mining & Concentrating Co. at Kellogg, Idaho, an ultra-violet ray quartz lamp, the standard equipment which is found everywhere in the offices of physicians and among usual hospital equipment. The use of this lamp was con- fined largely to treatment of pathological cases, still treatment of under-nourished children, run-down anemic people, both men and women, and, as a general tonic, was part of the routine hospital procedure. At the latitude of the Ceur d'Alene district and especially because of the position of the towns in deep canyons, with much overcast and cloudy weather, sunshine is not plentiful at any time of the year; for many of the winter months there is scarcely any. Underground workers, particularly during the winter, have little sun- shine; it is not unusual to have none at all for weeks at a time. Treatment by the ultra-violet ray lamp in the hospital has resulted in many extraordinary benefits but the use of the lamp is expensive and limited. Some weeks ago attention was directed to the automatic solarium equipment of the Burdick Corporation. The doctors strongly recommended the increased use of the ultra-violet lamp for its curative powers and tonic effects, urging that it be made accessible to all employees. Real interest was . . also displayed by employees with the possibility of securing ultra-violet ray treatment for themselves and families under better conditions than it was possible to have by the limited use of the lamp at the hospital. This resulted in the installation of the so-called sun room or automatic solarium as an adjunct to the mine change-house. An annex was built to the change-house, with dressing rooms for women, children and men from other departments, and the outfit put into use on Sept. 5, 1929. The installation consists of an escalator, or

Jan 1, 1929

W. H. Blauvelt, New York, N. Y.—One thought lias been running through my mind during the wholc of this meeting and that is that the scientific and the practical men must recognize very clearly their interdependence. The value of scientific classification of coal is going to be of the very greatest importance to the users, the practical men. Is not the scientific investigation and the great amount of work that is being done in a measure at least lost to the world? Therefore the scientific investigations and the practical needs of the users should bo brought as close together, and the work should be done as closely together, as possible; that is, the scientific man should know what the practical man needs, and the practical man should not feel that the scientific man is merely a theorist. Scientific investigation is going to have a great effeet and be of great valuc to the practical man who is trying to solve his problems. In the subject which I discussed' for instance, we must look to the scientific man to tell us why coal cokes in one way and not In another and why certain coals will do certain things and others, which appear on the surfacc to be generally similar, do not act in the same way. Need or Physical Data on Coal H. J. Rose, Pittsburgh, Pa.—There is a subject which is a sort of hobby of mine; that is, the need for what might be called critical tables of constants for coal. The chemist has big volumes giving constants, such as the density, solubility, specific heat, thermal conductivity and all other physical and chemical data that have been determined for chemical compounds. Data arc also available on many common materials, for example, the density, hardness, modulus of rupture or maximum crushing strength of swamp white oak as compared with some other wood. In fact, physical data for practically cvery hype of wood commercially produced in the world can he found. In the same way the metallurgical man has handbooks giving the properties of alloys, etc., but we havc very little tabulated information about coal. Our principal reference works are the volumes published by the U. S. Bureau of Mines on the proximatc and ultimate analysis and calorific values of coals of the United States. That is 3 pioncer work of enormous value, but we have reached the point where we need more diversified information. Mr. Fulweiler raised the question of the relative strength of the different coals and cokes. Dr. Campbell and Dr. Ashley wanted to have some information on the resistance of coal to air slacking. It was brought out in the discussion that we want to know something about the coking properties of coal. There are any number of physical tests that we need, such as the thermal conductivity of certain coals, the coefficient of expansion, or the coefficient of friction; or other constants. A smattering of such information is scattered through the literature; for instance, a research worker in Wales will report a coefficient of expansion on Wclsh coals and one in South Africa will report something else for one or two kinds of African coals, hut it is difficult to find the information that is needed on our own coals. Would it not be worth while to consider collecting reliable critical

Jan 1, 1930

By Harold Margalin, Elmars Ence

M. H. Mueller, M. V. Nevitt, and H. W. Knott (Argonne National Laboratory)—We have reported1 the crystal structure of Ti2CU as body centered tetragonal with a. = 2.944A and co = 10.786A, six atoms per unit cell, and space groupl4/mmm(MoSi2 type). This cell is larger but definitely related to the unit cell reported by the authors. It permits definite positions for the titanium and copper atoms in the cell located as follows: 2 Cu (a) 0 0 0; 1/2 1/2 1/2 4 Ti (e) 0 0 z; 1/2 1/2 1/2 + z; 0 0z; 1/2 1/2 1/2- z where z = 0.341 The face centered tetragonal cell reported by the authors can be transformed to a small body centered tetragonal cell with flo (small bet) = ao(fct)v2 Both unit cells have the same CO. Neither the face centered tetragonal cell with four atoms per unit cell nor the small body centered tetragonal cell with its two atoms per unit cell lend themselves conveniently to an orderly arrangment of the 2 to 1 ratio of titanium to copper atoms. When the co of this small body centered cell is tripled, however, a large body centered tetragonal cell results with six atoms per unit cell as described above. We had also noted that the X-ray patterns of Ti2Cu indicated that the structure could be approximately described by the face centered tetragonal cell as reported by the authors; how- ever, there was evidence for a few additional very weak lines whose positions indicated a larger unit cell. Since the X-ray scattering amplitudes of titanium and copper are nearly equal, it is evident that it is difficult to distinguish their positions especially from X-ray powder patterns. It was therefore decided to look at a powder pattern obtained by neutron diffraction since the scattering amplitudes of the two elements are considerably different in magnitude and opposite in sign. The sample used for neutron diffraction was selected from a group of three alloys prepared by arc melting using crystal bar titanium of 99.92 pet nominal purity and 99.999 pet pure Cu. The alloys designated as A, B, and C had the following respective compositions: Ti-32.8 at. pet Cu, Ti-33.3 at. pet Cu, and Ti-33.8 at. pet Cu. On the basis of the melting losses incurred, it was established that the actual concentration of either component in any of the alloys probably did not deviate from the intended value by as much as 0.1 at. pet. The alloys were annealed for 5 days at 700°C in evacuated Vycor capsules and quenched in tap water. The metallographic structures of these alloys are shown in Fig. 1. None of the alloys contained sufficient second phase to permit its positive identification. Since alloy B contained the least amount of second phase and since its composition placed it closest to the ideal stoichiometry, it was chosen for the neutron diffraction study. The oxygen content of alloy B was found by chemical analysis to be 0.06 at. pet. This particular intermetallic compound is especially suitable for investigation with neutron diffraction since if the titanium and copper atoms have a random statistical distribution, a near null-matrix would result in which there would be practically no coherent scattering of neutrons, and hence no Bragg diffraction peaks. Such a condition could come

Jan 1, 1962

By Joseph J. Becker

RECENTLY the "oriented growth" hypothesis of recrystallization textures has been receiving considerable attention. According to this view, "whenever a new generation of grains is growing in a highly oriented matrix . . . one may assume . . . that from among available nuclei of a great variety of orientations those with suitable orientation relationship with respect to the matrix have by far the highest rate of growth (oriented growth) and will, therefore, predominate."' This statement includes primary recrystallization of single crystals and of polycrystalline materials showing strong deformation textures as particular cases. While the phenomenon of oriented growth undoubtedly does operate, and may be of importance in coarsening or secondary recrystallization, the writer feels that its extension to primary recrystallization is a different matter. Several aspects of this phenomenon may be pointed out which are difficult to rationalize on the basis of oriented growth. In recrystallizing deformed single crystals of alpha brass, Maddin, Mathewson, and Hibbard2 found that the twin composition planes of the recrystallized grains were parallel to the three operative slip planes they observed, and not to the fourth octahedral plane. The writer's current work seems to indicate further that when only one or two slip systems can be seen to operate, the recrystallized grains are aligned only with those slip planes actually observed. This behavior could hardly be accounted for by oriented growth, because on the latter basis the recrystallized texture of a deformed single crystal should certainly have the same symmetry as the crystal itself. Growth rates could not be expected to distinguish between crystallogra- phically equivalent directions, unless the presence of a visible slip system vastly increases the growth rate in the appropriate direction. This seems unlikely. These relationships were observed by the writer only when considerable care had been exercised before annealing to etch away the effects of cutting out the centers of tensile specimens with a jeweler's saw and to etch off the ends of compression specimens. When these.precautions were not taken, nu-cleation inevitably appeared to occur at the saw cuts or at the ends, and the resulting orientations never showed a [111] rotation but appeared quite random. The provision of many nuclei of many orientations did not enhance the correlation, but destroyed it. Recrystallization textures are sometimes strongly dependent on annealing temperature, which would imply that the anisotropy of growth rates is a suddenly varying function of temperature. This might be regarded as unlikely. Recrystallization textures can be strongly dependent on the degree of deformation. If textures are to be explained by selective growth from among nuclei of all orientations, it is difficult to see how the recrystallization process could have any dependence whatever on the manner or degree of deformation. It is felt that the above points should be considered before the oriented growth hypothesis is applied to primary recrystallization, with the necessary complete divorce of the mechanism of recrystallization from the details of the deformation process. References 1P. A. Beck and H. Hu: Reply to discussion of their paper on Recrystallization Texture and Coarsening Texture in High Purity Aluminum. Trans. AIME, 188, 1057; Journal oF Metals (Aug. 1950) TP 29083. 'R. Maddin, C. H. Mathewson, and W. R. Hibbard, Jr.: The Origin of Annealing Twins in Brass. Trans. AIME, 185, 655; Journal of Metals (Sept. 1949) TP 26763.

Jan 1, 1952

By Jay N. Fairbanks, Richard G. Robinson

This paper discusses a computer program and related formulas for fire fighting responses by coal mine personnel. The computer will interpret the mine air analysis, print reports, and provide relevant graphs allowing quick and accurate responses to coal mine fires.

Jan 1, 1983

By Charles L. Mantell, Kurt Straler

The hydrogen reduction of Cr2O3 to chromium metal was found to be feasible at very low water-vapor concentrations, corresponding to dew points of -38° to -24°C, over a temperature range of 1130" to 1490°C. Hydrogen reduction under these conditions was predicted by the calculated equilibrium curves which also indicated that CrzOs is reduced directly to chromium without forming the intermediate oxide, CrO. This reduction path was confirmed by X-ray diffraction analysis. The percent reduction of Cr2O3 at each reaction temperature was constant with time, suggesting an inhibiting effect of water vapor. A small increase in the residual water-vapor concentration of a single temperature, 1490°C, strongly retarded the rate of reduction This effect was expressed by an empim'cal equation which indicated a direct relationship between "distance from equilibrium" and the rate of reduction. me effect of temperature over the range of 1130" to 1490°C was expressed in an Arvhenius plot of log rate vs reciprocal absolute temperature. From this curve the apparent enthalpy of activation was found to be 29,600 cal. Based on the hypothesis that the rate of reductiun is contvolled at the oxide-metal interface, an over-all rate equation consistent with the experimental data and the thery of absolute reaction rates was formulated. A simplification of this expression to an Arrhenius equation was justified by the overriding effect of temperature on the rate of reaction for the minimum water-vapor concentration range. MOST of the metals in Subgroup V1 of the periodic table can be prepared commercially by direct reduction of their oxides by hydrogen or carbon monoxide, at temperatures considerably below the melting points of both the metals and their oxides. Chromium is an exception, being generally reduced from its ore, Cr2O3 . FeO, by silicon in an electric arc furnace which operates above the melting point of the Fe-Cr alloy or above the melting point of chro- mium if a chromium oxide be the starting material. In reduction of chromium oxide by hydrogen, either reduction does not occur at all or the rate of reduction is extremely slow. Theoretical considerations based on the high, exothermic, free energy of formation of Cr2O3 compared to the oxides of the other Subgroup VI metals, molybdenum, tungsten, and uranium, would also suggest a slow rate of reaction and a high activation energy. Interest in the direct gaseous reduction of fine-powdered ores in fluidized beds was considered justification for examination of this reaction. In order to develop a basis for a continuing study of the commercial feasibility of the direct gaseous reduction of chromite, a study of the kinetics of the reduction of Cr2O3 with hydrogen was undertaken. To the authors' knowledge no accurate kinetic data for this reaction have been obtained. Neither has an activation energy been determined nor has an attempt been made to establish a mechanism of reaction. LITERATURE Maier10 compared the data of I. Y. Granaat,6 H. von Wartenburg and S. Aoyama, and G. Grube and M. Flad7 with that derived from calorimetric and ther-modynamic properties for the equilibria for the reduction of Cr2O3 with hydrogen. These results, plotted as the log of the equilibrium constant vs absolute temperature for the reduction of Cr2O3 and the intermediate oxide, CrO, to chromium, show agreement between the differently derived data. In both cases the equilibrium constants were extremely low. Maier showed that, over a temperature range of 1000° to 2000°K, Cr2O3 is more readily reducible than CrO. Granat assumed that CrO was preferentially formed from Cr2o3 above 1100°C. Grube and Flad's analysis of their reaction products in the 895" to 1000°C range indicated the coexistence of only Cr2O3 and chromium. The hydrogen reduction of the other Subgroup VI metals, molybdenum, tungsten, and uranium, shows that reduction of the higher oxide proceeds through all of the intermediate oxides before being reduced to the metal. Since evidence pointed to an anomaly in the reduction behavior of Cr2O3, the authors investigated the reduction path of Cr2Os.to chromium. This was done theoretically with more recently available free-energy data and experimentally by X-ray diffraction analysis. This work reinforces Maier's conclusion.

Jan 1, 1964

By J. Lewis, J. Harper, M. F. Ashby

A grain boundary in a metal interacts with second-phase particles, which exert a pinning force (first estimated by Zener) on the boundary opposing its motion. We have computed the shape of boundaries which interact with more or less spherical second-phase particles and have constructed a soap-film model to reproduce the shape of the boundary surface. An important result is that measurement of this shape allows the pressure, or driving force, on the boundary to be measured. We hare applied this technique to grain boundaries in two alloys and hate measured the pinning force exerted by single second-phase jwrticles on the boundaries. It is in good agreement with Zener's estimate. J\. boundary between two grains, or two bulk phases, interacts with small inclusions or particles of a second phase, whether they are gas or solid. This interaction means that the boundary, forced to migrate by a difference in free energy between the material of the two grains or phases which it separates, exerts a force on a particle which it touches, tending to drag it forward. (The movement of inclusions through metals under the influence of this force, has, in fact, been observed. 1-3) Equally, the particle can be thought of as exerting a pinning force on the boundary, tending to hold it back. Zener (in a celebrated private communication4) first realized that this interaction, and the resulting pinning force, existed. His calculation of its magnitude was crude but adequate: a spherical inclusion of radius r blanks off an area nr2 of the boundary on which it sits; since the boundary has an energy of rMM x per unit area, the blanlung-olf decreases the energy of the system by MM: this energy is returned to the system if the boundary is pulled free from the inclusion— a forward movement of the boundary by a distance r will do this—so that the maximum pinning force is Trrym.M- A similar argument can be made for inter-phase boundaries. The nature of the particle itself did not enter this, or two subsequent treatments.5,6 When it is considered, tic leifthe energyoftheb a) The boundary may enter and pass through the particle if the energy of the boundary is lower within the particle than in the matrix. Fig. l(r/). Certain coherent precipitate particles behave like this. h) More usually, the boundary will bend round the particle, enveloping and bypassing it. Fig. l(b). In doing so, it changes the structure and energy of the interface between the particle and its matrix. This means that the boundary does not touch the particle surface at right angles, as early treatments assumed,5'9 but at some angle a which depends on this change in surface energy of the particle, and can be calculated from the equilibrium of surface tensions. Most precipitate particles and inclusions behave like this. Gas bubbles or liquid drops can be regarded as belonging to either group. The progress of bypassing is conveniently measured by the angle shown in Fig. 1. When the nature of the particle is ignored, its maximum pinning force is exerted when - 45 deg. When it is considered, this critical value of is found to depend on a and thus on the nature of the particle. The maximum pinning force lies between nryMM and 2jtjMM (Appendix 1). not very different from Zener's result. In reality, a boundary between crystals has a specific energy and tension which varies with the orientation of the boundary. Furthermore, recent experiments7 indicate that such a boundary is not atom-ically smooth, but has steps on it: migration of the boundary corresponds to the sweeping of these steps across the boundary surface, like the Frank model of crystal growth from the vapor. This means that the interaction of a boundary with particles should really be considered in terms of the way in which particles hinder the movement of these steps. To suppose a grain boundary or interphase boundary to be smooth, and to ignore the variation of its energy with orientation, is to liken it to a soap film. The advantage of this soap film approximation, which we have used throughout this paper, is that interaction energies and boundary shapes can be calculated easily. We have done this by numerical computation and by using a soap film model, and have compared the results with grain boundaries in an aluminum-based and a copper-based alloy. It turns out that the shape of the boundary which bulges between particles allows the pressure an it to be calculated; that is, the local driving force an the boundary can be measured. This has allowed us to check the Zener relationship experimentally.

Jan 1, 1970

By P. C. Johnson, B. A. Stein

This paper describes a study of the effects of combined heat treatment and explosive loading on the mechanical properties of high-strength steels. nis program investigated two distinct areas: 1) the effect of shock waves, without gross irreversible defmmution, on a 3-Cr steel at various stages of heat treatment; and 2) the effect of rapid deformation (explosive forming) on H-11 and D6-AC steels in the metastable austenitic state. The mechanical properties of these steels were improved, in some cases markedly, as a result of these treatments. ,AUSFORMWG, which requires the plastic deformation of metastable austenite, is a process which can appreciably improve the properties of selected alloy stee1s.l,2 The Ausform process significantly increases the strength of these steels without decreasing their ductility. The properties at high temperatures are also improved through a change in the response of the steels to tempering. Although the mechanism by which ausforming alters the properties of these steels is not fully understood, it appears that the dislocation arrays produced by deformation of the metastable austenite influence the structure of the martensite on subsequent transformation. This, in turn, affects the strength, ductility, and tempering response of the martensite. This research used chemical explosives to deform steels at various stages in their heat treatment in order to improve the properties of these steels. The explosive energy is used in two ways; 1) high-pressure shock waves are propagated through the steel to produce extensive microscopic shear strain without causing a large irreversible change in shape, and 2) explosive energy is used to cause extensive macroscopic plastic strain in the metastable austenitic state (explosive forming). I) AUSFORMING WITH INTENSE SHOCK WAVES The steel used in this phase of the research was an alloy having a nominal composition 0.43 pct C, 3.0 pct Cr, 1.5 pct Ni, and 1.5 pct Si. The steel was subjected to intense shock waves in three conditions: 1) in the metastable austenitic state, 2) in the tempered mar tens itic state, and 3) in the tempered martensitic state after ausforming by conventional techniques. The specimens were in the form of disks 2.75 in. in diam and 5/16 in. thick. These were incorporated into a specimen assembly consisting of two disks pressed into a 5 by 5 by 1 in. block of stainless steel, Fig. 1. Spalling (or scabbing) is confined to the front disk. The specimen is protected from oxidation and decarburization by the surrounding metal. The temperature of the assembly is monitored by a thermocouple inserted into one side of the stainless steel block. The assembly is positioned over an oil reservoir which serves both as a means of catching the disks and as quenching medium for the disks shocked under ausforming conditions. Plane shock waves are introduced into the assembly by a metal driver plate impacting the top surface of the block. The driver plate is accelerated by a chemical explosive sheet supplied by E. I. du Pont de Nemours & Co. All the specimens were subjected to plane shock waves having a peak pressure of approximately 430 kbar. The pressure is that quoted by G. E. Dieter for the plane wave generator used in this work.' The driver plate used was 1/4 in. thick, so that the initial pulse was essentially a l/2-in.-wide square wave. The attenuation of the peak pressure during the subsequent 1/4 in. is estimated to be less than 5 pct. The shock front induces a temperature rise, a portion of which is irreversible. Rough estimates (+25 pct) of this temperature rise have been made for iron shocked at room temperature.4 For a 500-kbar shock wave, the temperature rise in the shock front is about 700°F, and is held for a time of the order of microseconds. The irreversible temperature rise, which remains after the shock wave passes, is about 450°F.4 The disks are quenched to room temperature within a few seconds of the shock treatment. It should be emphasized that the temperature rises given above are estimates for pure iron at room temperature, and are not necessarily true for the tests made in this work. The disks shocked at temperatures in the metastable austenitic range were austenitized in the stainless steel assembly in a furnace protected from the firing area. The assembly was removed from the furnace and placed over the recovery reservoir. The plane wave generator was then positioned and

Jan 1, 1963

By W. M. Wojcik, R. F. Kowal

Oxygen and sulfur distributions in commercial, 5-ton ingots of killed, medium carbon steel are described. Oxygen distribution is found to vary with deoxidation practice. Irregular distribution of oxygen within ingots makes necessary special precautions in sampling of rolled products for analysis of oxygen. Oxygen distribution is discussed in terms of recently published solidification concepts which had been successfully applied to simpler cases of segregation. These concepts have been found inadequate to explain observed oxygen distributions. Convective movements of the liquid metal, as determined by tracer elements, are shown to be capable of accounting for the observed distributions of oxygen. IN an effort to explore the origin of surface and subsurface imperfections in pierced steel products, a study of oxygen and sulfur segregation was made on ingots cast in open-top and hot-top molds. The results of our previous investigations1"3 have indicated the importance of the location and amount of oxide inclusions in an ingot. Inclusions close to the surface of the ingot have been found to contribute greatly to the formation of imperfections in the surface of finished products. This study of the effects of deoxidation and casting practice on segregation and the resulting oxygen distribution in ingots was initiated to determine the parameters controlling the location of inclusions in an ingot. Segregation of solute elements during solidification of low-melting binary alloys has been studied in the past.1, 5 Formation and growth of inclusions in iron melts have been studied under specific conditions."- In spite of these and other recent studies,10-12 segregation during solidification of commercial, killed steel ingots is not well understood. Consideration of solidification rates, of segregation during solidification of the chill, dendritic, and central zones, and of material balances for the segregated elements has indicated that a simplified theoretical solidification model is not adequate. However, the observed high oxygen contents in localized volumes of the dendritic zone can be rationalized if additional effects of convection currents in the ingots, precipitation, and rapid growth of new phases are considered. EXPERIMENTAL PROCEDURE Steelmaking and Processing. A group of nine killed. medium carbon steel heats having compositions listed in Table I have been studied. The deoxidation and mold practices used were varied to give a wide range of steel oxygen contents. The amounts of aluminum added to the ladle and the ingot casting practices (hot top and open top) were the main variables. The steel was made by a duplex practice in 160-ton tilting basic open-hearth furnaces. All nine heats were top-cast into 24 by 24 in. big end down, fluted molds, to a height between 60 and 76 in., using both open tops and exothermic hot tops. The deoxidation practice and the tapping and teeming details for each heat and ingot studied are given in Tables II and III, respectively. Hot-top practice is indicated by the letter H following the heat designation. Furnace and ladle temperatures were measured by standard disposable-tip, Pt/10 pet PtRh thermocouples. Teeming-stream temperatures were obtained as described by Samways et al.,13 by immersing a Pt/10 pet PtRh thermocouple, covered by a silica sheath, into the teeming stream under the nozzle. The output of this thermocouple was recorded with Leeds & Northrup Speedomax potentiometer. Calibration of the latter thermocouples was based on the freezing point of a pure iron/oxygen alloy (2795°F). The accumulated errors of measurements were within ±10°F. The thermocouple measurements were supplemented in this investigation by continuous recording of a ratioing, two-color pyrometer (Shawmeter), protected from smoke by a blast of clean air within the sighting tube, and calibrated to read with better than ±10°F accuracy. Following teeming of three heats, P, R, and T, tracer elements were added to the steel in the molds to obtain a record of the progress of solidification. As soon as the teeming stream was shut off, a 0.010-in.-thick steel can containing a mixture of crushed standard ferro-titanium and ferro-vanadium (0.05 pet of each alloy element) was plunged into the middle of the steel pool to a depth of 6 in. In about 30 sec no indication of the can or its contents remained. The surface of the open-top ingots solidified in 20 to 30 sec. A study of liquid metal movement and the precipitation of oxides was facilitated materially by use of the tracer technique as titanium has a low distribution coefficient between solid and liquid steel while vanadium has a high distribution coefficient.

Jan 1, 1965

By E. Buehler, H. J. Levinstein

The temperature ranges in which the three inter-metallic phases in the Nb-Sn system form have been determined and the composition and structure of two of the three phases has been established. The kinetics of the formation of Nb3Sn in cored wire samples has been studied in the temperature range of 800° to 1050°C. From 800°to 950°C the rate of formation increases by four orders of magnitude. The rate-controlling step for the formation process in this temperature range appears to be the diffilsion of tin through NbSn. At higher temperatu~es a change occurs in the mechanism of the formation process such that up to a temperature of 1050°C the rate of formation of Nb3Sn does not increase above the rate observed at 950°C. For temperatures helow 950°C the current-carrying capacity of the wire increases with increased percent reaction reaching a maximum value when the formation process is 90 to 95 pct complete. The maximum current-carrying capacity obtainable in this temperature range is independent of the temperature. Above 950°C tlze current-carrying capacity obtainable in the wire decreases with increasing temperature of formation. A model is proposed which accounts for the ohserved behavior. RECENTLY, Buehler et a1.l reported the results of an investigation of the process variables which influence the superconducting properties of Nb3Sn-cored wire. These results indicated that at least four variables affect the properties of the manufactured wire. These include composition, particle size of the starting powder mix, temperature of heat treatment, and time of heat treatment. In order to understand completely the role of these variables, it is necessary to have an accurate knowledge of the phase equilibria in the Nb-Sn system. At the present time, phase-equilibrium diagrams for the Nb-Sn system have been published by a number of investigators.2-5 The diagrams differ as to the number of phases present, the composition of the phases, and the temperature range of stability of the phases. The present investigation was undertaken in order to resolve these differences. Since the investigation of Buehler et al. demon- strated that the length of time at the temperature of heat treatment affected the superconducting properties of Nb3Sn, it is apparent that it is necessary to understand the kinetics of the formation process as well as the equilibrium conditions before a complete understanding of the system is possible. As a result, the kinetics of formation of the various phases in the system were also studied in this investigation. EXPEFUMENTAL PROCEDURE Diffusion couples and sintered powdered compacts were employed in the phase-diagram investigation. The diffusion couples were made by filling 1/8-in.-ID monel-sheathed niobium tubes with tin. The monel sheath was employed to facilitate drawing.' The tubes were then drawn to a tin-core diameter of 32 mils. Samples approximately 3 in. long were then cut from the drawn composite. The tin was drilled out of the ends to a depth of 1/4 in. and niobium-wire plugs were inserted into the ends and peened over. The monel was removed by etching in concentrated nitric acid, after which the samples were sealed in evacuated quartz bulbs and heat-treated in a resistance-wound tube furnace. The samples were quenched into ice water upon removal from the furnace. The diffusion couple samples were examined metallographically employing a chemical etching solution consisting of 10 ml of saturated chromic acid per g of NaF. In addition, two anodizing solutions were used for phase-identification purposes. The first was the picklesimer7 solution; the second consisted of equal parts by volume of 30 pct H2O2 and concentrated NH4OH to which 1 g of NaF was added per 25 ml of solution. The anodizing conditions for the second solution were 2 v and 100 ma with a tin cathode. The powdered compacts were made by pressing previously mixed powders of 99.9 pct pure Sn and 99.6 pct pure Nb supplied by the United Mineral Co. into cylinders 3/8 in. in diameter by 1/2 in. long. The cylinders were then sealed in quartz tubes and heat-treated in the same manner as the diffusion couples. The samples were examined metallographically and by X-ray diffraction techniques. Since it was desirable to be able to correlate the kinetic data with current-carrying capacity, the type of specimen chosen for this part of the investigation had to be a compromise between the optimum system for studying kinetics and one which was suitable for making current-carrying capacity

Jan 1, 1964