Search Documents

By J. Philip Neal, Carroll P. Rogers

Feldspars, the most abundant minerals of the igneous rocks, occur in numerous forms and mixtures. The feldspars of commercial significance are found in widely distributed pegmatites as large crystals usually free of iron- bearing impurities and thus suitable for hand-cobbing, and also in larger bodies where the ore contains various types of feldspar inter- mingled with quartz and relatively free of iron- bearing impurities, or at least readily unlocked from impurities present at relatively coarse mesh. The latter type of ore includes some pegmatites, and the ''alaskite" bodies so common in the Spruce Pine district of North Carolina. On the west coast of the U.S. and in Oklahoma there is-r has been--commercial recovery of natural feldspathic sand as a source of alumina in glass and ceramics. "Aplite" in commercial terminology is a light-colored igneous rock with a granitic composition and a fine sugary texture, often banded with readily removable iron impurities. Two areas in Virginia produce aplite for the glass industry: one located in the vicinity of Piney River, Amherst County, and the other near Montpelier in Hanover County. According to Deer et al. (1966) the word feldspar derives from the Swedish feldt or falt (field) and "spath:" chunks of rock appearing in tilled ground overlying granite. Castle and Gillson (1960) indicate a Germanic origin, citing "spat," which is said to refer to any transparent or translucent material which is readily cleavable. The term "spar" has in the past been applied to minerals other than feld- spar, such as barite, calcite, and fluorite. It is correct to call the latter "fluorspar." There is a true barium feldspar, but it is rare and of no present economic importance. What is recognized as feldspar or "spar" by present producers and consumers consists of three silicate minerals which, if pure, would have the formu- las KAISi,O, (microcline or orthoclase), NaAlSi,O, (albite), and CaAl,Si,O, (anorthite). These are almost never found in pure form in nature, but occur together in great abundance in a three-component system. A considerable number of different combined ratios of these three exists, with the exception that isomorphism between potassium spar and calcium spar is very limited. User specifications for feldspar products are largely built around the prevalent naturally occurring ratios. Pas- sages following will refer to "K-spar," "Na- spar," or "Ca-spar." Nomenclature and Descriptive Terms Relating to both the mineralogy and the economics of feldspar are certain terms whose coverage it is useful to specify. Commercially, aplite is a feldspathic rock mined and beneficiated in two locations in Virginia, in which both titanium and feldspar minerals are present-the latter now being the major, if not the only, economic product. Technically, the term aplite when applied to this rock is of questionable accuracy. But, in light of accepted commercial usage, the term will be here used to designate it. Regarding the Virginia rock, Ross (1941) is cited.

Jan 1, 1975

By E. A. Anderson

In another paper' the writer has shown that the low permissible maximum fiber stress in a loaded zinc sheet demands a much closer support spacing than is used for steel. The limiting fiber stress in 13-gage (0.032 in.) sheets having a 1-in. depth of corrugation was found to be about 5000 lb. per sq. in. on a 37-in. span under a load of 40 Ib. per sq. ft. Corrugated steel sheets are commonly laid with spans varying from 48 to 60 in. In order to increase the span in 13-gage zinc to 54 in. (a common spacing) the metal must be capable of withstanding, under long-continued loading, a maximum fiber stress of about 10,000 lb. per sq. in. This is known to be impossible with unalloyed zinc. In this paper the writer describes a series of experiments leading up to the development of an alloy capable of safely sustaining this fiber stress. The effect of alloying on the slow creep of zinc was studied by means of static tensile tests, accurate determinations of apparent elastic limits and finally by means of loading tests on full-size roof sections. Two industrial buildings roofed with alloyed zinc sheets on spans involving fiber stresses in excess of 10,000 lb. per sq. in. have been under observation for over two years without signs of sagging. Experimental Work Two methods of increasing the maximum permissible fiber stress in zinc were considered. Cold rolling, which' increases the stiffness and tensile strength, was found to decrease the resistance to slow flow. Alloying, therefore, provided the only feasible means of obtaining the desired result, It was recognized that the improvement secured by the solid solution of natural impurities was insufficient. A series of alloys was outlined, therefore, in which a number of metals were added separately and together. The sheets rolled from these alloys were tested under

Jan 1, 1930

By M. H. Sommer

Many attempts have been made to develop a relation between the tensile properties and the deep-stamping qualities of metals commonly used in deep drawing. These operations are generally performed cold and the metal is always stressed beyond the elastic limit. However, the problem cannot be readily solved without a proper investigation of: (1) the relation between actual stress and actual strain in the plastic range and (2) the stresses that are set up in the metal during the process of deep stamping. Much work has been done in recent years to add to our knowledge on plastic deformation of metals and the shortcomings of the ordinary tensile test, particularly in the plastic range, have been sufficiently recognized. It has been widely acknowledged that the local contraction, which appears in a tensile test after the maximum load is reached, is not a general characteristic of the material but is peculiar to this form of testing. The plastic deformation of materials is explained by the slip of their crystals along certain planes and this rearrangement should be similar whether observed in a tensile, compression or torsion test, and if the results of any of these forms of testing show deviations, it must be due to other influences, as for example the local contraction in a tensile test. For this reason the tensile-test curve as obtained from the measurements taken on a tensile-test machine or registered by an autographic device has been supplemented by the so-called "actual stress-strain curve," which is constructed from the observed tensile-test data by eliminating the effect of local contraction and is in complete alignment with the stress-strain values obtained in a compresison or torsion test. The actual stress-strain curve shows the increase of actual unit stress in relation to unit elongation beyond the yield point and beyond the point of maximum load and indicates clearly the extent of strain-hardening which the ordinary tensile-test curve does not reveal. The following metals have been investigated in this paper and their actual stress-strain curves and, further, their char-

Jan 1, 1934

By G. C. Bateman

The Workmen's Compensation Act of Ontario was passed in 1915 and Miners' Phthisis was added to the list of compensable industrial diseases in 1916. Under this provision of the Act only about two cases were compensated per year. In 1924, The Department of Public Health made a survey of miners in the four principal camps—Sudbury, Porcupine, Kirkland Lake and Cobalt—and the survey indicated that an alarming proportion of the men exposed to dust had silicosis in one or other of its several stages. A number of conferences were held between representatives of the Department of Mines, the Department of Public Health, the Compensation Board and the mine operators. The operators were advised that in the earliest stages of silicosis there was no physical disability and if men in that stage were removed from underground there would be little danger of permanent disability. They were further advised that if active steps were taken at once to compensate men that had some real disability and remove from the mines men in the early stages of silicosis, the first cost would be the greatest and thereafter their liability should decrease. As a result of this advice, and having at that time no reason to doubt the findings of the survey, the operators agreed to do all that was asked of them and cooperate with the Government in the steps believed necessary to meet the situation, and to provide compensation for the men affected. Amendments in 1926 Arrangements were made for the necessary amendments to the Mines Act and the Workmen's Compensation Act and these amendments were passed in 1926. The Amendment to the Mines Act provided that all underground employees must be the holders of certificates certifying that they were free from tuberculosis of the respiratory organs and further provided that the certificates must be renewed annually. The Government, however, at that time refused to adopt a form of certificate for applicants certifying as to their physical fitness for underground work. The Amendments to the Compensation Act defined both silicosis and

Jan 1, 1937

By Robert U. King

The Climax Molybdenum Company's mine is situated on the Continental Divide at Fremont Pass in Lake County, Colorado. Elevations at the mine range from 11,000 it. to over 12,000 ft. The ore body is on the south flank of Bartlett Mountain, a prominent peak in the Ten Mile Range. A horizontal section of the mine, such as the Phillipson level (Fig. I), shows the outer ore zone as an annular ring varying in width from 300 to 800 ft., surrounding barren silicified rock. In vertical section the outer ore zone is dome shaped (Figs. 2 and 3), the apex of which is truncated at the surface by glaciation, exposing part of the ore body. The outer ore zone overlies the barren core and is itself overlain on the flanks of the dome with unmineralized rock. An ore zone of similar shape underlies the barren core of silicified rock, known as the Central Ore Zone (Figs. 2 and 3). Molybdenite is distributed uniformly through a zone of moderately silicified granite, schist and quartz monzonite (early) porphyry, around a highly silicified core. The molybdenite occurs in veinlets associated with fine granular quartz and pyrite, replacing altered and fractured granite, schist, and porphyry, and as coatings on numerous fractures cutting these rocks. Intense fracturing of all rocks is a characteristic feature of the Climax ore body. Most fractures are mineralized and no longer represent planes of weakness. Much fracturing is postmineral, however, and these fractures are generally filled with sericite or gouge, or remain as unmineralized joints separating otherwise massive rock into blocks of various size. Study and Mapping of Caving Characteristics Important differences in the behavior of caving of various blocks of ore at Climax have been recognized, involving arching of the rock over caved stopes, tendency of caved rocks to funnel, and size of caved rocks. Also, new problems have arisen associated with future mining on the Phillipson level, and may occur with proposed development of lower levels, such as excessive stress on mine pillars caused by large masses of overlying stable rock, and higher costs in maintenance of mine workings in soft, weak rock. To explain the differences and to provide solution for these problems, a study of geologic structure was undertaken early in 1944, to determine whether it would be possible to map cavability of rock from physical features exposed in mine workings and in diamond-drill cores. A comparison of known caved areas was made and rocks were classified structurally according to strength or degree of cavabil-ity. As nothing of this nature had been done before at Climax, the approach to the problem was rather indefinite. Several trials were made with negative results, but collectively indicated a suitable method. This was to examine all mine workings and diamond-drill cores, record-

Jan 1, 1946

By John L. Lamont, Walter Crafts

THE principle formulated by Grossmann1 for calculating hardenability of steel by multiplying the ideal diameter of "pure" iron-carbon alloys by factors for grain size and alloying elements has been confirmed on many steels and has proved useful in designing substitute alloy steels. Grossmann found that the typical behavior of the multiplying factors was to increase directly in proportion to the amount of the alloy present in a steel. However, the multiplying factor for the effect of silicon on hardenability was found by Grossmann to increase to a lesser degree as the amount of silicon was increased. In view of the in¬creasing use of silicon in heat-treating steels, the effect of silicon on hardenability is becoming more important. Calculation of the hardenability of high-silicon steels made at the Union Carbide and Carbon Research Laboratories, Inc., indicated that the multiplying factor for silicon increased directly in proportion to the amount of silicon present. A more extended study of high-silicon steels covering fairly wide ranges of grain size, carbon, manganese, and aluminum has confirmed that up to 2 per cent silicon the multiplying factor is directly proportional to the silicon content. Manganese and aluminum factors have also been determined. The results of the study offer strong confirmation of the general validity of Grossmann's multiplying principle. TESTING PROCEDURE Steels on which the study of the effect of silicon on hardenability was based were made in high-frequency induction furnaces using Armco iron and standard alloying materials. The ingots were forged to bars, and sections were normalized prior to machining Jominy hardenability test specimens. The Jominy test was carried out under standard conditions.2 The depth of hardness penetration for determination of ideal diameter at "half hardness" was taken at the hardness level indicated in Fig. 20 in Grossmann's paper by the solid line for 50 per cent martensite in plain carbon steel. The depth of penetration of hardness on the Jominy specimen was converted to ideal diameter by the relation given in Fig. 28 of Grossmann's paper. Chemical analysis was determined on a sample taken adjacent to the Jominy specimen. Aluminum was determined as "acid-soluble aluminum" rather than as total aluminum, as it is probably more representative of the aluminum that is effective as an alloying agent. In addition to the elements nominally present in the steels, analyses were made for residual phosphorus, sulphur, nickel, copper, molybdenum and chromium on one heat of those made with the same materials during the same period. Actual grain size was determined by microscopic examination of small samples quenched in water after receiving the same thermal cycle as the Jominy hardenability specimens. Chemical analyses, heat-treatment, grain size, and hardenability are shown in Table I representing three ranges of composition.

Jan 1, 1943

By Sylvan Z. Beer

The factors that determine the yield and crystal size in the two-temperature synthesis of A lp were examined. Low yields and small crystals were associated with low temperatures and pressure. Attempts to grow large crystals in the critical and supercritical region of phosphorus were unsuccessful. Crystal size increases markedly at elevated temperatures. Crystals grown at temperatures as high as 1450° C fluo-resced, under uv excitation, at energies close to the estimated band gap of about 2.4 ev, while crystals grown at lower temperatures tended to fluoresce in the red region of the spectrum. Those grown in the supercritical region showed no ALP fluorescence. Heating the high-temperature-grown ALP under vacuum greatly increased its fluorescence efficiency and moved the emission peak to higher energies. I HE III-V compounds, with few exceptions, have been prepared by the two-temperature method. In its classic form this technique is applicable to closed systems where at least one of the components, in this case the column V element, is a liquid or a solid with a high vapor pressure. One advantage of this method over flow systems is in its simplicity. In addition, because it is a closed system, it can, under the circumstances to be described later, be run at higher pressures of the volatile species than in flow systems. In instances where the III-V compound is soluble in the parent III metal to about 1 mol pct or higher, solution growth can be made to take place by slow cooling. This, for instance, is one way in which single-crystal GaP1 and Inp2 have been grown. Initial attempts to synthesize and grow A1P by this technique were not too successful; the yield was low and the crystals obtained were exceedingly small. The conditions required for improving the yield and growth by this technique were, therefore, sought. Two obvious conditions which could be controlling were examined. These were the temperature of the aluminum and the pressure of the phosphorus. The range of temperatures studied extended from about the melting point of aluminum, 660° to about 1450°C. The latter is dictated by the vapor pressure of aluminum which reaches about 1 Torr at that temperature and the limitations of the materials of construction as described in the next section. The pressure range of interest covers from below 1 atm to above the critical pressure of phosphorus, 82.2 atm. EXPERIMENTAL The Temperature of Aluminum as a Variable. A series of experiments were run in the conventional two-temperature manner. All refractories and quartz were dried by heating at 800° to 900° for a minimum of 24 hr, and usually much longer, before use. The aluminum

Jan 1, 1969

By Howard Clarke, Cyril Stanley Smith, Clarence Zener

The importance of cold-working in the fabrication of metals is in marked contrast with our ignorance as to the nature of the accompanying internal changes. The failure of the usual methods of testing to provide a consistent picture of these internal changes has given the incentive for the present program of investigating the effect of cold-working upon the internal friction of metals measured at small strain amplitudes. It has previously been shown1,2,3, that the internal friction introduced by cold-work is removed by annealing at comparatively low temperatures. In the present paper the following additional factors are investigated: (I) frequency of measurement, (2) amount of cold-work, (3) temperature of measurement. Special care was taken to minimize the internal friction due to causes other than cold-work. The present paper is purely experimental, the authors believing that any conclusions drawn from this work as to the nature of the internal changes accompanying cold-work would be premature.'l PrEpaRations oF Specimens In this study of cold-work it was desirable to eliminate as far as possible all other sources of internal friction. One disturbing source is the lack of temperature equilibrium between adjacent crystallites of a vibrating specimen.4 Temperature equilibrium is aided by small grain size and by the use of low-frequency vibrations. Unless unduly long specimens are used, low frequencies can be obtained only in transverse vibrations. But in transverse vibrations a second source of internal friction is present, that arising from transverse thermal currents.5 The effect of these may be reduced by increasing the transverse dimensions. The grain size and transverse dimensions of the specimens were thus so chosen as to render the vibrations simultaneously nearly isothermal with respect to intercrystalline thermal currents, and nearly adiabatic with respect to transverse thermal currents. The material for this investigation was a 70-30 brass, part of the same lot of material that was used for some earlier studies on the effect of strain on proportional limit.10 It had the following composition: copper, 70.59 per cent; zinc, 29.39; lead, 0.01; iron, 0.01. This material was received from the brass mill in the form of 3/4-in. rod, cold-drawn to final size by a 65 per cent reduction of area from material that had been annealed to give a grain size of 0.060 mm, Rods of appropriate length were annealed for 2 hr. at 400°C. and cooled in air. The annealed rods (grain size, 0.012 mm.) were then stretched in a tension-testing machine, using special grips1' to ensure axial application of the load. The rate

Jan 1, 1942

By Walter Crafts, C. M. Offenhauer

IN a previous study' of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is a more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about r1to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, 1 per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to 1-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudomartensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously' that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By L. D. Woodworth, E. E. McGinley

During the past several years has occurred what, in the light of future events, may aptly be called the rebirth of the acid Bessemer process. The increased attention given to the technical and metallurgical details involved in the production of Bessemer steels has been exceedingly fruitful, and indicates the value of further research and p1ant development. In times like these, when the steelmaking capacity of the country is operating at a maximum rate to supply materials for the national defense program, it behooves the Bessemer operator not only to strive to increase production but also to maintain a high standard of quality. The opportunity is ripe, it seems, to recapture fields of application once considered the birthright of Bessemer steels, but supplanted in recent years by open-hearth grades. This involves cooperation all along the line, from the blast-furnace operator to the metallurgical contact man and salesman. The metallurgist's part in this program involves the study of the many steelmaking variables and the measures necessary to ensure constancy in the finished product. It is equally important that the knowledge gained be disseminated widely to ensure the wise application of Bessemer steels in new fields. The merits of Bessemer steels for certain work are well understood. The combined properties of good weldability, machinabil-ity and stiffness are unique and fully explain the strong entrenchment of Bessemer steels in certain fields; e.g., skelp for small butt-weld conduit, screw steels machined in automatics, and certain tin-plate applications. It is the purpose of this paper to review briefly the physical properties of Bessemer steels as contrasted with those of open-hearth steels, to discuss control measures now employed in the making of Bessemer steel, and to consider the advantages derived from the use of these control measures. Physical Properties oF Bessemer vs. Open-hearth Steels A number of Bessemer blows and open-hearth heats were tested for tensile strength, ductility and impact strength. The steels selected were confined to sections from 3/4 to 1 1/4-in. diameter, inclusive, and the carbon content covered was sufficient to yield parallel ranges in ultimate strength for the comparison. Other factors, such as the extent of deoxidation of the steel and variations in chemistry, were kept as comparable as possible. Machined test pieces of 0.505-in. diameter with an 8-in. gauge length were pulled. The data obtained are shown in Fig. I, ultimate strength being plotted against carbon content. This graph shows that for equivalent carbon content Bessemer steel has on the average 15,000 lb. per sq. in. greater tensile strength and, conversely, for the same tensile strength Bessemer steel requires on the average 0.14 per cent less carbon. The average phosphorus content for the Bessemer steel was 0.090 per cent,

Jan 1, 1941

By W. A. Ver Wiebe

The year 1939 in Kansas, with a production of 57,944,300 bbl. from 19,669 wells, shows a slight recession from the peak of oil production reached the previous year, when slightly over 59,000,000 bbl. of oil was marketed. The previous peak had been reached in 1917 with 45,451,000 bbl. marketed. Another still earlier peak had been reached in 1904, when slightly less than 5,000,000 bbl. was produced and sold. The production of gas probably reached a new peak during 1939 with a total of over 69 billion cubic feet. Between the peak of the year 1908, when over 80 billion cu. ft. was produced, and that of 1939 the production dropped to 16 billion cu. ft., in the year 1921. During the year 1458 wells were drilled. This figure is somewhat lower than that given in several trade journals, because it does not include wells that were deepened or recompleted in a different geological horizon. Nearly 75 per cent (1029) of the total number of wells were completed as commercial oil wells (824 in western and 205 in eastern Kansas). The commercial gas wells completed number 71, of which 24 are in eastern Kansas and 47 in western Kansas. The remaining completions include 154 dry holes in eastern and 204 dry holes in western Kansas. Based on daily potential capacity the new discoveries of the year accounted for a cumulative initial production of 264,000 bbl. in eastern and 1,158,827 bbl. in western Kansas. It is interesting in this connection to note that the number of wells completed in the state rose gradually to a first peak in 1904, when 2782 were drilled. The number dropped off rapidly to 368 three years later, but rose to the second and highest peak in 1918, when 4671 wells were completed. In the period between 1904 and 1912 more gas wells than oil wells were completed. Between the high peak of 1918 and the somewhat lower peak of 1937, the low point was reached during 1931 with the completion of only 470 wells. In the matter of new pools discovered, Kansas again ranks high. The exact number depends somewhat upon the interpretation of a "new" area—whether it should be called a new pool or a long extension of an older pool. In some places this determination cannot be made until more wells are drilled within the area. Therefore, the figures given

Jan 1, 1940

By C. R. Dale

The need for instruments to measure the movement of fluids and gas in wells has been recognized by engineers for many years. Information regarding flow in the producing interval has a direct bearing on completion practices in new wells and also provides information on the production characteristics of the well. Many hours of engineering time are spent in planning and completing wells but knowledge as to whether or not the original planning has produced the desired results has not always been complete. Many questions such as the following often arise: Why is it that two wells are completed under supposedly identical conditions, yet one well is a good one and the other is a poor one? Are the sands that look the best on the electric log contributing to the production? These and many other conditions in the producing well need to be under- stood in order to develop more efficient production practices and to improve on methods of completing new wells. It is the purpose of this paper to briefly describe one type of instrument, outline the methods of running the equipment and show the results of surveys made under various conditions. With an understanding of the use of this type of survey its importance can be evaluated in relation to the problems encountered by the operator. DESCRIPTION OF INSTRUMENT The instrument is a velocity recorder employing a clock-controlled 16mm film for recording the rpm of an extremely sensitive rotor which is rotated by the flow of fluids or gas in a well. The helical-vaned rotor and shaft, weighing one-half of one ounce are an integral unit exposed to the well fluids and are the only moving parts not enclosed in the fluid-tight housing. No packing or fluid seal of these parts is necessary and the shaft is mounted top and bottom on special jeweled bearings. Fig. A is the lower part of the instrument showing rotor and shaft with the protecting housing sleeve removed. The rpm of the rotor is recorded on the moving film by a combination electrical and optical system. The record is a series of dashes on the film, each dash and space representing twenty (20) revolutions of the rotor. (Film record of survey made in California well showing station recordings at various depths.) As the movement of the film is controlled by the clock the number of dashes and spaces in one minute of film travel represents the rpm of the rotor. The range of the instrument is from 0 to 2,500 rprn. The barrel or housing is 1-11/16 in. OD and seven feet long. Various types of expanding fluid traps are attached to the lower end of the instrument to direct the flow through the 1 in. orifice containing the rotor. The fluid trap for upward flow is shown in Figs. B and C. This assembly consists of eight arms with light spring

Jan 1, 1949

By A. J. Miles, A. D. Topping

in this paper, the theory of elasticity has been applied to the rock about a deep well, It is assumed that the rock has a modulus of . elasticity and a Poisson's ratio and that the theory of elasticity applies. It is necessary to know or assume the state of stress existing in the rock before it is penetrated by the well drill. The application of this theory indicates that stress concentration of shear, tensions, and compressions about the bore hole are of a high order. This is particularly true when a horizontal compressive stress exists in one direction only in the formation before drilling. If such an initial state of stress exists before drilling, then the rock will have stress concentrations of both tension and compression at the same elevation and of such magnitude that failure of the rock is likely. Accompanying these is a shearing stress of large proportion which is likely to produce spalling of the well walls. Internal pressure applied to the well bore will relieve the extreme compression but not the tension and has little effect upon the shear. Plastic deformation of the rock through a geological time tends to mitigate the stress concentrations. IntroductioN It has long been known that the stresses about holes and re-entrant corners of elastic solids under the influence of loads are different and generally more intense than those imposed upon the body else- where. Stress concentration at a re-entrant corner can be reduced by increasing the radius of the fillet at the corner. Stress concentration at the end of a crack in a plate undergoing either tension or compression Can be relieved appreciably by drilling a hole at the very end of the crack. Also, stresses can be increased in an elastic body in tension or compression by making a hole in it. The stress concentration is greatest at the edge of the hole. Considerable knowledge of the stresses which exist about the bore hole of a deep well may be had by applying our knowledge of engineering mechanics; or more particularly the theory of elasticity. It is, of course, necessary to make the assumption that the rock is elastic and behaves as an elastic solid, that is, that it obeys Hooke's law, has a modulus of elasticity, and a Poisson's ratio. It is also necessary to know, Or assume, the state of stress which exists in the rock prior to the penetration of the drill. With this knowledge it is possible to compute the stresses about the bore hole. The problem can be simplified by considering several simple cases separately and then by applying the principle of superposition to solve the more complex cases which are made up of the simpler ones. Case i—Rock Strata in Compression Penetrated by a Hole This case was first worked out by G. Kirsch* for structural material, but applies equally well to a horizontal rock strata in a state of in in one direction

Jan 1, 1949

By M. S. Burton, H. H. Kranzlein, G. V. Smith

The influence of up to 2 at. pct of Ni and Pt on the yield strength of mono- and polycrystalline high-purity iron has been evaluated at temperatures from + 25° to -196°C. Current theories of solid -solution strengthening fail to explain the experimental observations. The temperature dependence of yield stress was found to be less in the alloys than that in high-purity iron. The room-temperature yield stress increased with alloy content, but at —78°C the yield strength first decreased with increasing a1loy content. AS a result of many studies, a number of theories have been proposed for solid-solution strengthening. The purpose of the present study was to evaluate these theories, as applied to the solid-solution strengthening observed in Fe-Ni and Fe-Pt alloys. Of various theories of solid-solution strengthening, those of Cottrell,1,2 Fisher,3 Suzuki,4 and Mott and Nabarro5 are most prominent, and have been discussed widely in the literature.'-' Of the recent concepts of solid-solution hardening the work of Fleischer9 is notable. Each of these models has been applied to particular alloy systems with some success, but in general none has proved generally applicable. In many of the previous studies to assess the effects of alloy additions in ferrous systems, lack of adequate control of the purity and grain size of the materials has obscured strengthening effects, so that few comprehensive data relating composition, temperature, and change of lattice parameter have been determined. In the present investigation an attempt was made to obtain data which would be meaningful in evaluating the theories of strengthening. Materials of high purity were used to minimize extraneous impurity effects, and both single crystals and polycrystalline materials were studied to evaluate the effect of grain boundaries. Nickel and platinum were chosen as alloy additions, because both belong to the same chemical group and have the same crystal structure and valence, with markedly different atomic diameters. It appeared that some conclusions regarding atomic size effect on strengthening might be made. MATERIALS AND PROCEDURES Fe-Ni and Fe-Pt alloys containing 0.5, 1.0, 1.5, and 2.0 at. pct alloy additions were prepared from high-purity materials. The iron was supplied by the American Iron and Steel Institute from a stock of 99.98 pct zone-refined iron prepared by Battelle Memorial Institute. The minimum purity of the nickel and platinum used for alloying was 99.98 and 99.999 pct, respectively. Alloys were prepared by levitation melting, cast into cylindrical copper molds, and cooled, all under a partial pressure (0.3 atm) of purified helium. Samples were 0.375 in. in diameter and weighed 20 to 25 g. Chemical analyses of the alloys are given in Table I. A sample of unalloyed iron also was cast as a control specimen.

Jan 1, 1965

By B. L. Averbach, E. E. Underwood

The vapor pressure of zinc in equilibrium with solid ß AgZn alloys has been measured by the dew-point method. The thermodynamic activities of silver, and the molar heats of formation have been calculated. Similar measurements have been made for the ternary alloys formed by adding gold to AgZn. An apparent particle size effect has been observed for AgZn filings. The vapor pressure of zinc over filings is 15 to 20 pct higher than over the solid alloys. STATISTICAL methods have been used to inter pret the thermodynamic activities of the components of a solid solution in terms of average equilibrium atomic configurations. In some cases, the atomic arrangements can be measured by X-ray methods, and the results are usually expressed in terms of short range order parameters. Only in the cases of Cu³Au and AgAu have there been sufficient X-ray and thermodynamic data to verify the assumed correlation between the X-ray and the thermodynamic measurements. In Cu³Au the agreement is good; negative deviations from Raoult's law are observed and the number of Cu-Au nearest neighbor pairs predicted on the basis of the thermodynamic treatments agrees quite well with the number of such pairs observed by the X-ray methods. The ß brass alloys present a different set of conditions. The ordering is so rapid in these alloys that the disordered state cannot be retained on quenching. In contrast, the disordered state in CuAu is easily retained on quenching. On heating, the ordered ß brass loses its long range order continuously as the critical temperature is approached; in Cuau the order decreases slightly on heating and then drops discontinuously to zero at the critical temperature. These differences indicate that the short range order configurations in ß brass systems may be of a different character than in Cudu systems. However, X-ray measurements of local order cannot be made in the Cu-Zn alloys because of the similarity in scattering factors. The alloy AgZn is isomorphous with CuZn, however, and recent experiments have indicated that there is a good possibility of observing short range order in this system. Another complication arises in the case of ß AgZn. The disordered body-centered cubic structure exists above 280°C. On quenching from above this temperature an ordered structure of the cesium-chloride type is formed. On slow cooling, however, a complex hexagonal structure, the 3 phase, is produced; and if an ordered quenched alloy is reheated the phase begins to form above 80°C. It is thus difficult to study local order by X-ray methods in single crystals of AgZn since the C phase formed on heating does not necessarily return to a single crystal of the original orientation. This problem has been met, however, by adding a few percent of gold to the AgZn. The gold suppresses the formation of the c

Jan 1, 1952

By Corliss R. Kinney

Since the first atomic bomb exploded over Japan, a great deal of speculation has been published about the use of atomic energy instead of coal for the production of power. Atomic energy, in time, may displace coal for this purpose, but atomic energy will not displace coal in supplying chemical raw materials to the rapidly expanding carbon-chemicals market. Modern civilization demands large quantities of carbon compounds and the logical source of many of these is coal. Consequently, many progressive operators are considering the possibilities of the utilization of coal as a chemical raw material as never before. Furthermore, the demand for clean, smokeless, and ashless fuels will continue to increase and the only way to handle coal under those conditions is to take it apart, just as crude petroleum is taken apart. One can readily imagine where the petroleum industry would be now if it had insisted on selling customers only crude oil, perhaps emulsified with a little salt water to correspond to the moisture and mineral matter in raw coal. The time seems to be coming at an accelerated Dace when mine operators will find that competing for a highly selective fuel market by producing a larger tonnage at smaller cost will be less profitable than to increase the value of a smaller tonnage many fold by producing something more valuable to industry and civilization than raw coal. For example, about 750,000 tons of carbon black selling for $50 to $60 per ton was produced in the United States in 1945. This tonnage is insignificant compared with the total production of coal in the United States, but a very tidy tonnage, together with the coal necessary to operate the process, for any mine operator fortunate enough to obtain a method of producing a better carbon black from coal. From the point of view of tonnage, the manufacture of coke of various kinds and its by-products is at present the most important source of carbon chemicals from coal. Nearly 20 per cent of the coal mined in this country is used for this purpose. A large proportion of the coke is used for the production of iron and steel, but even in this operation a considerable part of the coke is used for a chemical purpose; that is, the reduction of the ore to metallic iron. In addition, large quantities of coke are used in manufacturing many important products that find their way into the market. Possibilities of Acetylene One of the important chemicals manufactured from coke is calcium carbide, from which many products are made. One of these is acetylene. This hydrocarbon can also be manufactured from natural gas or from waste oil-refinery gas and these industries will probably offer competition for the manufacture of acetylene. Coke-oven gas can be used for making acetylene and should receive consideration

Jan 1, 1947

By George M. Rigg, Samuel M. Cassidy

During 1937 a program was begun to mechanize and modernize the then 28-year old Isabella mine of the Weirton Coal Co., which is on the Monongahela River, in Fayette County, Pennsylvania, at one edge of what is generally known as the Coke Region. Weirton Coal Co. is a subsidiary of the National Steel Corporation, and produces metallurgical grade coking coal for the Weirton Steel Co., Weirton, W. Va. Improvements subsequently made included a cleaning plant for washing the entire mine output, shovel-action track-mounted machines for mechanically loading all the coal, universal-type track-mounted cutting and shearing machines, post drills, 8-wheel mine cars of 10 tons capacity, cable-reel gathering locomotives and other auxiliary equipment. This paper presents the factors, reasons and results of decided changes from the mining system generally prevailing in the region, as well as abandonment of selective mining practices in favor of complete seam extraction. Coal-seam Conditions Fig. 1 illustrates the Pittsburgh coal seam on the property. Cover over the seam averages 450 ft., and 675 ft. is the maxi- mum. Main roof varies from very weak to medium strong; usually it disintegrates rapidly on exposure to air. The "wild" coal makes a fairly strong immediate roof if supported by crossbars and if unbroken affords a seal to the main roof. The draw slate is very weak and treacherous. The floor is characterized by numerous irregular bottom rolls, or "horsebacks," protruding from a few inches up to 3 ft. into the coal. Some are soft, but many are hard and flintlike. Although the bottom slate usually is hard, the underlying fire clay causes it to buckle and heave readily with any moderate increase in roof pressure or where damp. As a whole, the bottom is weaker than the main roof. The coal is characterized by numerous closely jointed face and butt cleats and a woody, springy nature when shot, both having a decided influence on face practices. As shown in Fig. I, at both the top and bottom of the main coal seam is a layer of coal of higher ash and sulphur content than the body of coal in the middle. Factors That Influence the Mining System Equipment was bought and organization for mechanical loading was made on the basis of working each mechanical unit as near its full capacity as possible, to lessen investment cost and obtain best operating efficiency. This led to combination double and triple-shift operation at the start, and, very shortly, to all sections being triple shifted.

Jan 1, 1947

By Herbert H. Kellogg

In 1930, Taggart, Taylor and Knoll1 found that addition of various electrolytes to suspensions of ground minerals resulted in the stopping or starting of Brownian movement of the suspended particles. On the basis of the many new facts found, they rejected the " classical"† theory of Brownian movement and proposed an "ioniza-tion " theory. This new theory was further supported in later publications by Taggart.3,4 The acceptance of the ionization theory by men in the field of flotation may be judged by the mention given this theory in Gaudin's "Principles of Mineral Dressing,'16 Wark's "Principles of Flotation,"8 as well as in a recent paper by Fitt, Thomas and Taggart.7 The proponents of the ionization theory have gone further than the mere statement of the new theory. A parallelism between the Brownian movement of mineral particles and their behavior in flotation was reported.1,3,4 Likewise, the correlation between flocculation-dispersion of mineral particles and the Brownian movement of these particles has been investigated.' Bankoffl5 has suggested that "slime-coating" can also be directly correlated with the Brownian movement of the slime particles. In each of the instances mentioned it is the ionization theory of Brownian movement that has been used to "explain" the correlations that were found. The essential conflict between the kinetic theory and the ionization theory can be understood best by a brief description of each. The kinetic theory* proposes that Brownian movement is caused by the impacts of liquid molecules against the solid particles. At any instant of time, the molecular impacts on all sides of the solid particle will not balance, and the particle will receive a push in some direction. According to this theory, dl particles suspended in a liquid are in Brownian movement. However, if the particle is very large, the impacts on all sides will very nearly balance and the motion will not be noticeable. Another factor, besides the size of the particle, that affects the magnitude of the Brownian movement is the viscosity of the liquid—the greater the viscosity, the less the displacement of particles by Brownian movement. This theory has been verified experimentally by measurement of the velocity of Brownian movement, and by measurement of the compacting of suspensoid particles under the influence of gravity.2 The originators of the ionization theory found that he addition of various electrolytes to slime pulps caused cessation or commencement of Brownian movement, depending upon the chemical nature of the particle and the electrolyte. The Brownian movement of quartz particles was observed to stop upon the addition of Certain electrolytes, where the conditions of the experiment prevented flocculation

Jan 1, 1947

By W. K. Hardy, H. H. Stadelmaier, L. J. Huetter

The ternary system Co-Sn-C was studied in the cobalt-rich region. The liquidus projection ulas established and two fonr -phase reactions were found. An isothermal section at 950°C was worked out. In the region studied the following phases were observed: cobalt-rich solid solution, graphite, binary compound y -cobalt-tin, and a ternary compound. As a result of the limited solubility of carbon in liquid cobalt-tin alloys, the investigation was limited to the cobalt-rich region. Tin contents up to 32 at. pct were studied. Cobalt of 99.99 pct purity, tin of 99.97 pct purity and synthetic graphite of 99.93 pct minimum purity prepare the alloys. Carbon determinations of all alloys were obtained by gas volumetric analysis. Samples were investigated microscopically and by X-ray diffraction using CoK, and FeK, radiation. Cooling curves were obtained with a number of alloys to determine the temperature of the four-phase reactions. The thermocouple was calibrated with the melting points of high-purity silver and copper. In the region studied the following phases were observed: Cobalt-rich solid solution (face-centered cubic) Graphite. Binary compound y (solidifies congruently at composition Cop~n)'. Ternary compound k which is face-centered cubic with superlattice and nonferromagnetic.' In Fig. 1 the fields representing the projections of the liquidus surfaces were determined by microscopic investigation and are labled by their primary phase. In the field labled C graphite is the primary phase. During solidification in this field much of the primary graphite was expelled through the surface of the melt. It could not always be established microscopically whether the remaining graphite was primary or purely eutectic. Therefore it was not possible to determine accurately the boundary curve which drops from the binary eutectic el at 1309 "~~ to the point of the four-phase reaction at F. The ter-nary carbide is the primary phase in the field labled k. To the right of this field the primary graphite is consistently nodular whereas flake graphite is observed at tin contents somewhat below F. The ternary carbide does not appear to solidify congruently. The graphite is attacked in a peritectic reaction along the boundary between k and C. Thus no graphite is observed in alloys in the k field. In alloys right of the boundary between k and C the graphite nodules are located in the center of the k crystallites, further documenting the peritectic nature of the reaction with the graphite. A four-phase reaction was found at F and 1120 &3"C. The most likely reaction is L+ CY-Co + C — k. Below the temperature of the binary eutectic ez at 1112" a second four-phase reaction was observed at E and 1100 lt3"C. It is the ternary eutectic L — CY-Co + k + y. Figs. 2(a ) to (e) show microstructures of the ternary alloys in the as-cast condition. Fig. 2(a) shows the eutectic a-Co + C (with some primary graphite) with the carbide k in the grain boundaries. Fig. 2(b) shows primary cobalt (dark areas) and the eutectic a-Co + k which is formed along F-E.

Jan 1, 1961

By J. Buchwald, R. W. Heckel

THE DeHoff method' of analysis of ellipsoids of constant shape provides a quantitative metallo-graphic technique whereby the actual size distribution of the ellipsoids may be determined from polished and etched random planar sections. This method provides a useful metallographic tool since it appears to be the only method available for determining the size distribution of nonequiaxed second-phase particles. This method, however, assumes that the type of particle being studied is known to be either oblate or prolate of a fixed minor to major axis ratio, q. This, in general, means that one assumes either oblate or prolate ellipsoids of a given q and checks the total volume and surface area of the second phase as determined from the particle size distribution to values of these quantities determined by other techniques. Suitable check methods may be point counting, lineal fraction, and areal fraction methods for obtaining the total volume and the Smith and Guttman2 method of intercepts for obtaining the total surface area. If the initial guess at particle shape and q were incorrect, i.c., the volume and surface information obtained from the particle size distribution data does not agree with those values obtained by other techniques, another assumption must be made and the particle size dist distribution must be recalculated. A current study in this laboratory has involved a large number of these calculations. To facilitate the handling of the calculations, the DeHoff method was programmed in the FORTRAN language for an IBM 1620 computer. The purpose of this note is to briefly describe this program. The complete program along with a list of variable names, a sample input, and a sample output may be obtained from the senior author. Basically, the program provides for the calculation of particle size distributions for a series of q values for both oblate and prolate ellipsoids for each set of input data. The total volume of second-phase particles per unit volume are calculated for each calculated particle size distribution. The output of the program is arranged to allow a rapid comparison of the calculated volume and surface values to data obtained by independent check measurements. A condensed flow chart of the program in the notation of DeHoff1 is given in Fig. 1 The calculation of the number of particles per unit volume in the jth size class, Ni, according to the DeHoff method' is: where k(q) is the shape-correction factor given by DeHoff as a function of q for both oblate and prolate ellipsoids, A is the size-class increment, k is the number of size classes, ni is the number of particles in the ith class on the planar measurement surface, and B(j,i) are the saltykov3 coefficients which correct for measurement surfaces which do not pass through the major and minor axes of the particles. The values of /3(j,i) are included as a two-dimensional array in the program. Particular values of k(q) are included in the program in increments of q of 0.05. The first calculation is carried out for q = 1 (spheres), the second for q = 0.95 oblate, the third for q = 0.95 prolate, and so forth. The number of q values chosen for the calculation is determined by a control card in the input for each set of data.

Jan 1, 1965