By Shuqiang Guo, Dingsheng Tan, Weizhong Ding, Zunyu Hu

"The mixture of hydrochloric acid and magnesium chloride is a good lixiviant for leaching of laterite. The solution can enhance the leaching ability because of the proton activity deviated positively from ideal. Otherwise, the existence of magnesium chloride in the lixiviant affects the dissolution behavior of magnesia, which may be an advantage of the process with less hydrochloric acid consumption. An investigation of magnesia particle dissolved in strong hydrochloric acid solution has been conducted. Influences of concentration of the magnesium chloride and hydrochloric acid and temperature on magnesia dissolution were studied. The dissolution mechanism was also discussed in this paper.IntroductionThere has recently been much interest in the use of hydrochloric acid leaching processes for recovering metal from ores or secondary resources [l-41_ Compared with sulfuric acid, the use of hydrochloric acid as lixiviant offers significant advantages including faster leaching kinetics even at atmospheric conditions, higher leaching rate and greater solubility for most metal chlorides [5-61 .With the gradual decline of the nickel sulfide supply, the extraction of nickel from laterites has become increasingly attractive [7-s1. Nickel may be co=ercially recovered from laterites both by pyrometallurgical and hydrometallurgical processes. The drawbacks of pyrometallurgical processes include the requirement of high grade ores, substantial energy input and loss of cobalt bound within ores. The extraction of Ni from lower grade nickel laterites ores is suited by hydrometallurgical routes, which play an increasingly important role with depletion of higher grade deposits."

Jan 1, 2014

By Wiraseranee. Chompunoot, Kazuki Morita, Toru H. Okabe

"Aiming at the development of more effective recycling processes, dissolution behavior of rhodium into molten slag was investigated. Using a pure rhodium crucible and Na2O-SiO2 slag system, equilibration experiments were carried out for 18 h at 1423-1623 K under various oxygen partial pressures of 0.005-1 atm with varied slag basicity. Rhodium solubility increased with increasing oxygen potential, slag basicity, and temperature. Rhodium dissolved into slag as rhodate ion ([RhO2]-) by the endothermic reaction: Rh(s) + 3/4O2(g) + 1/2O2-(in slag) = [RhO2]-(in slag). In the dissolution reaction, the “rhodate capacity” of slag is newly-defined. The correlation between rhodate capacity and optical basicity is reported.IntroductionDue to its high chemical resistance and outstanding catalytic properties, rhodium (Rh), one of the platinum group metals (PGMs), is utilized in various applications such as catalysts, molten glass vessels and containers, and electronic devices. Owing to the rarity of Rh resources in nature, recycled Rh from scraps such as spent automobile catalytic converters is currently considered as an important source of Rh supply [1]. According to the recycling practices, Rh is currently mainly recovered from scraps along with other PGMs such as platinum (Pt) and palladium (Pd) by a dry process (e.g., smelting), a wet process (e.g., leaching and subsequent separation of PGMs from aqueous solution), or a combination of both processes [2]-[4]. Among these processes, smelting is commonly applied because PGMs can be effectively separated from a relatively large amount of various impurities coexisting in scraps. In the smelting process, Rh and other PGMs are collected in the collector metal (e.g., iron and copper), and impurities in scraps are removed into slag [4]-[6]. The process may be carried out at a temperature range of 1573-1973 K, in either an oxidizing or reducing atmosphere. Due to the high oxidation resistance at high temperatures, Rh is expected to be collected efficiently in the metal collector rather than being oxidized and forming RhOx in a molten slag. However, Rh loss into slag does occur in this process [7]."

Jan 1, 2011

By K. N. Han, N. S. Kim, H. Yoon, J. S. Sohn

The leaching behavior of silver and silver oxides in ammonical solutions has been studied. The current study is concerned with an effective recovery of silver from secondary sources such as spent silver batteries. Silver associated with these batteries appears in various forms including metallic silver, argentous oxide, Ag2O and argentic oxide, AgO. The leaching behavior of metallic silver in ammoniacal solution has been studied using an electrochemical mehtod. Oxidants used in this study include hyperchlorite, hydrogen peroxide, bromine and iodine. Results on cyclic polarization and Tafel plots on the silver anode in ammoniacal solutions are presented and the results are discussed. The dissolution rate of metallic silver in ammoniacal solutions is also compared with those of silver oxides.

Jan 1, 2002

By Chao Du, Xiaohui Ning, Hongmin Zhu, Qiuyu Wang, Shuqiang Jiao

"TiCxOl-x solid solutions were synthesized by sintering a mixture of titanium carbide and titanium monoxide at 1600 °C. The corresponding structures and morphologies of the TiCxOl-x solid solutions were characterized by XRD and SEM. A series of tests has been performed on the electrochemical dissolution behavior of TiCxOl-x solid solutions in NaCl-KCl molten salt. The influences of synthesis time and electrokinetic parameters on the anodic dissolution behavior were also investigated. The results showed that TiCxOl-x solid solutions can dissolve as Tin+ into alkali chloride melt. Titanium ion species dissolved from TiCxOl-x solid solutions changes between Ti2+ and Ti3+ depending on the applied potential. The tail gas on the anode was monitored by a mass spectrometer. It was found the synthesis time significantly affects the components of the anodic gas.IntroductionTitanium and titanium alloys have been desired greatly because of their many uses. The critical factor that restricts the range of uses for Ti is its high cost of extraction. The primary titanium metal, sponge titanium, is still produced industrially worldwide by a process invented by Dr. Kroll in the 1940s[1] •Since the early 1970s, the research focus of the titanium industry has been directed towards developing a continuous process to produce high purity titanium at low cost. [2-10] Of the many alternative methods that have previously been investigated, the electrolytic process has been considered a promising method for titanium metallurgy [4-10]. Recently, several electrolysis and related methods such as the PFC-Cambridge process[11-15], calciothermic reduction[16-18], USTB [19,20] and MER[21] process were extensively investigated.The USTB process is a new approach where the pure titanium can be directly obtained by the electrolysis with an anode of titanium oxycarbide in molten salts[19, 20]. The titanium oxycarbide was produced by carbothermal reduction of titanium dioxide under vacuum at a temperature"

Jan 1, 2011

By E. Uzun

"In this study, H2SO4 and HCl leaching behaviour of an ore sample containing 1.87% of Ni, obtained from the Karaçam (Eskisehir-Turkey) lateritic deposit that started operation recently was investigated. Acid concentration, temperature and reaction time were investigated as variables by comparative leaching tests and the optimum leaching conditions were selected on teh basis of Ni, Fe, Co and Mg behaviour. For H2SO4 leaching, optimum leach parameters were 95°C, a 12 normal H2SO4 concentration and 90 minutes of reaction time, and under these conditions Ni and Fe dissolutions were 97.6% and 95.4% respectively. On the other hand, 70°C, an 8 normal HCl concentration and a reaction time of 90 minutes were found to be the optimum parameters for HCl leaching, and Ni and Fe dissolutions found were 97.1% and 97.8%, respectively.INTRODUCTION Today, nickel and various nickel compounds are obtained from sulphide and lateritic nickel ores (Moskalyk & Alfantazi, 2002). Even though about 72% of the world's nickel reserves constitute lateritic ores, only about 42% of nickel is produced from these ores. The decrease in production from sulphide deposits, on the other hand, and increases in the use of nickel in the iron and steel, and battery production sectors, and especially the production of nickel cast irons in recent years, have accelerated the importance of making use of lateritic deposits (Luo et. al., 2010; Chang et. al., 2010). In the beneficiation of sulphide nickel ores, mostly pyrometallurgical methods are used. On the other hand, about 39% of lateritic ores are beneficiated by pyrometallurgical, and 61% are beneficiated by hydrometallurgical methods (USGS, 2009). In laterite beneficiation, the ore properties are of significance; that is to say, limonitic ores are eneficiated by high pressure acid leaching or via the Caron process, nontronitic ores are beneficiated by high pressure acid leaching or heat treatment (smelting), and ores containing serpentine by pyrometallurgical methods (Berezowsky, 2004; McDonald & Whittington, 2008a; Dreisinger et. al., 2015)."

Jan 1, 2017

By Xiaohui Li, Lianyun Liu, Hongmin Zhu, Chunfang Zi, Kai Huang, Hongjie Li

"The dissolution kinetics of steelmaking slag in pure water was studied, and the relative influential factors were investigated. The dissolution behavior of slag particles in water was well described by Noyes–Whitney equation, and for this kind of sparingly soluble rigid mineral this simple model was extensively applicable to describe their dissolution process. Experimental data were also obtained to confirm the significant promotion effect on the growth of some algae.1 . IntroductionIt has been found that the population of phytoplankton distributed in the ocean was significantly related to the concentration of some elements [1]. For example, silicon and iron were very low in the high-nitrate low-chlorophyll (HNLC) areas, which was the main factor limiting phytoplankton and other biomass growth in these open ocean surface water [7]. The silicon and iron-rich test also confirmed that the supply of these elements had the direct effect on the growth of phytoplankton processes at HNLC areas [2-8]. So in order to promote the growth of phytoplankton in these ocean areas, providing some of these elements into these ocean areas is a natural idea for choice. Steelmaking slag is a good resource for consideration because it usually contains silicon, iron, phosphorus and other elements that are necessary for the growth of phytoplankton [8-10].Haraguchi has proposed the following idea that [5-6], if steelmaking slag can be spread to the open ocean, the trace components like silicate, iron and phosphate as the indispensable nutrients for the growth of phytoplankton, will be leached into the sea water, not only promoting the growth of phytoplankton, but also making good use of these huge amount of steelmaking slag produced every year. Based on this idea, they have carried out studies in recent years and they found that silicon and iron in the slag could be extracted into seawater effectively and play a positive role in the growth process of many algae. About the dissolution of the steelmaking slag, the Japanese scholars' research work mainly focused on the thermodynamic analysis of its dissolution possibility, and in the process of dissolution they tried to adjust the pH value of the seawater by continuously adding hydrochloric acid, which was deviated from the natural conditions of dissolution, and so the laws drawn under these special conditions can not give the identical guide to the practical application. Therefore, it is quite necessary to investigate the dissolution behavior of the steelmaking slag in the seawater at the normal pH range without adjustment to simulate the dissolution possibility under the natural conditions. In the present study, the silicon extraction behavior from the steelmaking slag was investigated and the dissolution kinetics in this process was also discussed in detail. Further studies were also performed here to evaluate the promotion of steelmaking slag on the growth of algae."

Jan 1, 2011

By Mustapha A. Raji, Alafara A. Baba, Christianah O. Adeyemi, Aishat Y. Abdulkareem, Rafiu B. Bale, Malay K. Ghosh

The increasing demand for pure aluminum and aluminum compounds of industrial quality from kaolinite ore cannot be overemphasized. Nigeria is one of the African countries endowed with abundant solid mineral resources that have not been sufficiently exploited to assist its indigenous industries. A wide array of applications of pure aluminum and its compounds are available, such as paper filling, refractories, adsorbent, catalysis, and paint additives. In this study, the upgrading of a Nigerian biotite-rich kaolinite ore by a hydrometallurgical route was investigated in oxalic acid media. During leaching studies, the effects of parameters including reaction temperature, lixiviant concentration and particle size on the extent of ore dissolution were examined. At optimal conditions (1.0 mol/L C2H2O4, 75 °C), 92.0% of the initial 10 g/L ore was reacted within 120 min. The dissolution curves from the shrinking core model were analyzed and found to conform to the assumption of surface diffusion reaction, and the calculated activation energy of 33.2 kJ/mol supported the proposed model. The unreacted product (~8.0%) analyzed by XRD was found to contain siliceous impurities and could serve as a valuable by-product for certain industries.

By Mustapha A. Raji, Alafara A. Baba, Christianah O. Adeyemi, Aishat Y. Abdulkareem, Rafiu B. Bale, Malay K. Ghosh

The increasing demand for pure aluminum and aluminum compounds of industrial quality from kaolinite ore cannot be overemphasized. Nigeria is one of the African countries endowed with abundant solid mineral resources that have not been sufficiently exploited to assist its indigenous industries. A wide array of applications of pure aluminum and its compounds are available, such as paper filling, refractories, adsorbent, catalysis, and paint additives. In this study, the upgrading of a Nigerian biotite-rich kaolinite ore by a hydrometallurgical route was investigated in oxalic acid media. During leaching studies, the effects of parameters including reaction temperature, lixiviant concentration and particle size on the extent of ore dissolution were examined. At optimal conditions (1.0 mol/L C2H2O4, 75 °C), 92.0% of the initial 10 g/L ore was reacted within 120 min. The dissolution curves from the shrinking core model were analyzed and found to conform to the assumption of surface diffusion reaction, and the calculated activation energy of 33.2 kJ/mol supported the proposed model. The unreacted product (~8.0%) analyzed by XRD was found to contain siliceous impurities and could serve as a valuable by-product for certain industries.

By W. D. Cho

The slag chemistry in steel processing plays an important role in terms of the removal of impurities including alumina particles. In the present study, the dissolution of solid alumina particles in CaO-based fluxes at the temperatures between 1450 and 1550 °C has been investigated to determine dissolution kinetics and mechanism. Alumina particles were added directly in the slags and the size of alumina particles was measured as a function of time using optical and scaru;ling electron microscopes. The dissolution rate has also been obtained as a function of Si02, CaF2, MgO and MnO contents in the slags. The diffusion boundary layer between alumina and bulk slag phase has been observed and analyzed using SEM and EDX. In addition, some experiments have been performed for the dissolution of alumina in BaO-based fluxes.

Jan 1, 2003

By W. D. Cho

The slag chemistry in steel processing plays an important role in terms of the removal of impurities including alumina particles. In the present study, the dissolution of solid aluimina particles in CaO-based fluxes at the temperatures between 1450 and 1550 °C has been investigated to determine dissolution kinetics and mechanism. Alumina particles were added directly in the slags and the size of alumina particles was measured as a function of time using optical and scanning electron microscopes. The dissolution rate has also been obtained as a function of Si02, CaF2, MgO and MnO contents in the slags. The diffusion boundary layer between alumina and bulk slag phase has been observed and analyzed using SEM and EDX. In addition, some experiments have been performed for the dissolution of alumina in BaO-based fluxes.

Jan 1, 2003

By Batric Pesic

Recovery of gold from refractory ores was studied by pressure oxidation as the method of ore pretreatment followed by bromination of oxidized residues. Three different ores were examined, Au-Ag, Au-Ag-Te, and Au-silver free ore. Pyrite was the major host mineral for gold in these ores. The effect of pressure oxidation parameters (temperature, pressure of oxygen, time, and pulp density) on subsequent bromination under standard conditions was examined. Bromination of residues produced under standard pressure oxidation conditions was examined as a function of: temperature, bromine and sodium bromide concentration, and time. Recovery of gold on activated carbon, from the pulp after bromination, was studied too. Recovery of gold from silver containing ores was lower (87-91%) than the recovery of gold from silver free gold ore (97%). In each studied case, the presence of activated carbon in the pulp further increased the recovery of gold.

Jan 1, 1992

By H. Kaffash

Ferromanganese is a ferroalloy with high manganese content which finds many uses for example as deoxidizer in steelmaking industry. However, there is very little data on the dissolution rate of carbonaceous materials in Mn containing metals. In this paper, the kinetic analysis of carburization reactions is investigated for Mn–Fe alloys. Dissolution rate of graphite in pure iron and four different alloys with 10 wt%, 40 wt%, 60 wt% and 85 wt% manganese at 1823 K was studied. Results showed that the dissolution rate of carbon from graphite increased with increasing time for all alloys. The dissolution rate constant increased with the increasing manganese content from 6.5 × 10−3 cm/s for 0%Mn to 23.6 × 10−3 cm/s for 85%Mn.

By M. Clotilde Apua, A. F. Mulaba-Bafubiandi

"The efficiency of hydrochloric acid (HCl) leaching of gold from low grade gold-bearing material has been investigated in the presence of sodium hypochlorite (NaOCl) to produce in situ chlorine gas which is an oxidizing agent able to oxidize gold metal to its soluble forms. The effect of concentrations of HCl, NaOCl, and mixtures of HCl + NaOCl was sought. Iron and potassium present in the feed were leached and consumed all the HCl. Gold found as inclusion in pyrite was not exposed to the lixiviant. Therefore, leaching of gold from low grade gold-bearing material in aqueous chlorine solution is not an effective process for now.INTRODUCTIONHydrometallurgy of gold is commonly based on cyanide leaching solution. Due to the environmental concerns related to cyanidation and mercury processes, and inefficiency of cyanide gold leaching to dissolve refractory ores, sustainable alternative lixiviant systems, capable of generating gold (I) and gold (III) complexes must be studied. Amongst non-cyanide gold lixiviants there is the chloride/chlorine system (Hilson and Monhemius, 2006; Senanayake, 2004; Pilsniak and Trochimczuck, 2007; Wang et al., 2007; Reeves et al., 1999; Khodadad et al., 2008).In practice, the most oxidizing agents utilized for the leaching of gold as chloride, are chlorine (Cl2) or hypochlorite (HOCl) which are either generated in situ by suitable reaction or added in solution (Adamson, 1972). The dissolution of gold concentrate using hydrochloric acid, sodium chloride and sodium hypochlorite (Cl-/HOCl system) were studied (Puvada and Murthy, 2006). The effect of NaOCl and NaCl concentrations were also investigated. The leaching was performed under the following conditions; time: 4h, solid–liquid ratio = 1:4, at room temperature. It was found that the increase of the NaOCl concentration from 25 to 75 g/L did not have any meaningful effect on the recovery of gold which was about 30% (experimental conditions; S/L ratio = 1:4, NaCl concentration: 25 g/L, HCl concentration: 0.35 M). It was also found that from 25 g/L to 200 g/L NaCl, the recovery of gold rose from 30% to 40% (experimental conditions; S/L ratio: 1:4, NaOCl concentration: 25 g/L, HCl concentration: 0.35 M)."

Jan 1, 2012

By Kenneth N. Ham

Hydrometallurgy covers a wide spectrum of areas and its knowledge base is enlarged and enhanced by contributions from many other fields. Dissolution of metals and alloys in aqueous media will be used to illustrate how rich the field of metal extraction can be. Comprehensive understanding of the fundamentals of metal and alloy dissolution in aqueous systems requires creative application of thermodynamic principles, solutions chemistry, ligand complexation theory, electrochemistry, transport phenomena and heterogeneous kinetics. In addition, recent developments in instrumentation in the fields of interfacial phenomena and corrosion have tremendously advanced the field of metal extraction in aqueous system. The close relationship between metal extraction in aqueous systems and various physicochemical phenomena occurring in corrosion and interfacial systems will be discussed and illustrated with examples.

Jan 1, 2002

By R. C. Hubli

A panial equilibrium model? to simulate the dissolution of millerite (NiS) in aqueous solutions containing copper(II) chloride as the oxidizing species has been developed. The predominant copper(I) and copper(II) species are CuQ3 and CUO2 respectively. The model computes the initial concentrations of the species present in the aqueous phase under the specified input conditions, prior to the simulation of dissolution. During the dissolution of millerite, nickel enters the leach liquor as NiH and it has been found that the H+ decreases as a function of NiS dissolution. The simulation has been accomplished under conditions prevailing during actual dissolution, with only one mineral undergoing dissolution. The model can be applied for the simulation of co-dissolution of two or more sulfides. Under the given conditions, the precipitation of Cu1(OH»)O is negligible but loss of Cu(1l) could be significant if the initial H+ is lower than 0.03 M. The results of the simulation compare favorably with experimental observations.

Jan 1, 1996

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By Luiz A. Teixeira

A process is described whereby worn, deffective or crystallized photoconductive Se-As layers can be stripped off from aluminium photocopier drums, using hydrogen peroxide solutions in conditions such that the aluminium substrate is preserved from chemical attack. The process allows the stripped drum to be recoated with a new photoconductive layer, and to be put again in use.

Jan 1, 1990

By S Jayakumari, E Ringdalen, V Canaguier

Silicomanganese (SiMn), containing approximately 16–30 per cent Si, is produced in submerged arc furnaces using various Mn sources and quartz as the primary raw materials, along with fluxes and reductants. In the high-temperature zone known as the coke bed, a silica-rich slag is formed. SiMn is produced through the reduction of SiO2 from the slag. Dissolution of quartz into slags with different compositions, the primary slag formed from the Mn sources and flux before any MnO reduction occurred, representing conditions at the top of the coke bed, and dissolution of quartz into a partially reduced slag to simulate conditions inside the coke bed has been investigated. Experimental investigations were carried out to study the dissolution of quartz particles of varying sizes, 5 mm and 25 mm in synthetic slags with different compositions at temperatures between 1400°C and 1600°C, with varying holding times. Observed results are compared with liquidus compositions and equilibrium phases for original and formed slags. Particle size has been shown to be of little importance for the dissolution. Quartz dissolved more easily in slag at top of the coke bed than slag in the coke bed. Complete dissolution was observed after 30 mins at 1600°C in all cases, but not after 0 mins.

Jun 19, 2024

By Kazutoshi Haga, Ariunbolor Narankhuu, Ariuntuya Battsengel, Yasushi Watanabe, Altansukh Batnasan, Akita University

"Rare earth minerals are usually concentrated by flotation, magnetic or gravity separation methods to produce concentrates that are subsequently leached with hydrochloric (HCl), sulfuric acid (H2SO4) or nitric acid (HNO3). About 75 % REEs are lost in gypsum by-product when apatite is dissolved in H2SO4, whereas more than 80% of REE can be extracted from the apatite using HCl and HNO3 leaching processes, respectively. Therefore, the main aim of this study was to find an efficient process of dissolution of rare earth elements (REEs) from apatite ore by sulfuric acid solution due to its lower cost. In order to optimize the dissolution process, effects of different parameters, namely, concentration of H2SO4 (0.05 – 6 M), solid/liquid phase ratio (1:50 – 1:100), temperature (20 – 80 ºC), agitation speed (300 – 900 rpm), and leaching time (0.5 - 6 h) on the dissolution of REEs from apatite ore were examined in various intervals. The contents of main REEs in the apatite ore used in this study were (as % wt): 3 % La, 6 % Ce, 0.6 % Pr, 2.1 % Nd, 0.2 % Sm and 0.3 % Y. X-ray diffraction (XRD) analysis identified fluorapatite and phlogopite as main minerals in the ore. The results obtained from leaching experiments showed that more than 85% of REEs were dissolved from the apatite ore under the optimized conditions, which were: 1 M H2SO4, particle size of -150 + 100 µm, S:L phase ratio of 1:50, agitation speed of 500 rpm at 20 ºC for 1h. The XRD analysis revealed that main mineral compositions of the residues from 1M and 6 M H2SO4 leaching are gypsum (CaSO42H2O) and hemigypsum (CaSO40.5H2O), respectively.INTRODUCTIONThe term rare earth elements (REEs) denote the group of 17 chemically similar metallic elements consisting of the 15 lanthanides, plus yttrium (Y) and scandium (Sc) in the periodic table. These metallic elements are generally divided into two sub-groups; (1) the cerium sub-group, which is called “light rare earth elements” (LREEs), includes the elements from lanthanum (La) to europium (Eu), and (2) the yttrium (Y) sub-group elements, which are known as “heavy rare earth elements” (HREEs), are the remaining lanthanides from gadolinium (Gd) to lutetium (Lu) plus yttrium (Gupta and Krishnamurthy, 2005). The REEs occur together in the minerals due to their chemical and physical similarities, which cause problems of separating them from one another (Abreu and Morais, 2014). Although REEs are relatively abundant in the earth’s crust, they are typically dispersed and rarely occur in concentrated forms, making them economically challenging to obtain. There are a wide variety of rare earth minerals, however economic deposits of REEs in mining are bastnasite (La, Ce) FCO3, monazite (Ce, La, Y, Th) PO4, and xenotime YPO4 (Binnemans, 2013; Xie, et al, 2014). Due to the unique physical, chemical, catalytic, electrical, magnetic and optical properties of REEs, demand of these elements has increased dramatically with the advent of new technologies in electronics, communication, construction, energy and medicine (Jordens, et al, 2013). Since 1990, China has provided about 90 % of REEs worldwide. Japan and United States are the largest consumers of China’s REEs. In 2010, China announced to reduce REEs exports to Japan, as it tended to increase prices of REEs and to reduce a stable supply of REEs in the world market (Humphries, 2013). Therefore, there has been an increase in recent exploration activities intended to reveal new commercial sources of REEs and to bring them into production (Antico, et al, 1996). Apatite is an important host mineral for REEs in igneous and metamorphic rocks and can be used as an ore for those metals (Kanazawa and Kamitani, 2006). Apatite is also the main source of phosphate fertilizers and phosphoric acid (Habashi, 2013; Emsbo, 2015)."

Jan 1, 2016

By Fumito Tanaka

In the Mitsubishi Continuous Copper Smelting & Converting Process, the heat for the dissolution of scraps is effectively supplied from the melts strongly stirred by top injection. Various kinds of shape of scraps not only powder but also lump, sheet, cube and so on can be treated without any emission of dust and fugitive gas, and no additional furnaces for scrap processing is necessary. Therefore, this process is much suitable for recycling. The authors have investigated the melting rate of ice sphere into a water bath equipped with top blowing lances as a basic study for the dissolution of scrap. Hydrodynamic experiments were carried out, and mathematical models were applied to the results. The results show that the melting rate of ice sphere strongly depends on the standing waves at the bath surface.

Jan 1, 2001