Search Documents

By L. Diaz, J. Serp, L. Massot, P. Chamelot, M. Gibilaro

The discovery of NdFeB permanent magnets helps to perform technologies with reduced weight and gives them access to miniaturization. The industrial process of production of the Nd-Fe alloy by electrolysis used to manufacture NdFeB magnets consists in reducing Nd3+ ions dissolved in molten fluoride salts. The electrochemical behavior of neodymium is studied in LiCl-KCl and LiCl molten salt systems, examining reduction mechanisms, potential deposition, and faradaic yields.

Mar 1, 2017

By K. M. Parida

The kinetics of dissolution of manganese dioxide in dilute sulphuric acid solution have been investigated using iron pyrites as a reductant. The dissolution rate of manganese is independent of the speed stirring but depends upon temperature, particle size, specific surface area of manganese ore, acid concentration, Fe(II) concentration and amount of pyrite. The activation energy is 43.6 KJ/mol and the linear relationship between the rate of dissolution and lido indicates that the reaction is chemically-controlled. The redox reactions of MnO2 with iron pyrites and Fe(II) are the rate-controlling reactions.

Jan 1, 1990

By Maria K. Kojo

The interaction between various slags and a nickel concentrate containing pyrite, pentlandite, and violarite were investigated by submerging concentrate pellets in molten slags. The slags were contained in MgO-A12O3 spinel crucibles. The slag oxidizes the iron sulfides in the concentrate, resulting in a nickel matte. The amount of S02 gas formed during reaction was measured to determine the oxidation reactivity of the slags. The experimental variables included temperature, the ferric/ferrous ratio of slag, and other slag properties such as the FeO/SiO2 ratio and the MgO and NiO contents. The reactivity of the slag depended in a complex manner on its oxidizing power, viscosity, and interfacial tension. The slag composition for the greatest reactivity was determined to be Fe3+/Fe2+ = 0.3, Fe/SiO2 = 1.3, and % MgO = 2. This slag, however, caused substantial foaming. Increasing the MgO content to 10% or replacing it by 5% MgO + 8% NiO eliminated at a slight decrease in reactivity. The implications of the findings from this work in the bath smelting of nickel sulfide concentrates are discussed.

Jan 1, 1995

By Nobuo Takahashi

Effective solvent extraction media have been investigated for purification of rare earths. At first, a quaternary ammonium compound was studied. The counter anions of rare earths and organic dielectric substances were tested to improve separation factors,. And second, crown ethers were selected for extractant. Several diluents of crown-adducts were tested to improve solubility and distribution coefficient as well as the counter anions of rare earths. Especially, in the presence of strong reducing agents, highly selective extraction of europium from other rare earths was observed. The third extactnts were ß -diketones. Presence of organic dielectric substances was very effective to improve separation factors. Though those. three groups of extractants were suitable for mutual separation of light rare earths, alkyl esters of alkyl-phosphonic acids were suitable for mutual separation of heavy rare earths because of their high separation factors. To keep proper pH value was necessary for acidic extractants, so control method of the solution pH was studied with high molecule insoluble amines or salts of those.

Jan 1, 1995

By Katsutoshi Inoue

Pectic acid gel crosslinked with epichlorohydrin was found to have very high selectivity to lead(II) and iron(III) ions over zinc(II) ion compared with commercial weakly cation exchange resins containing the same carboxylic functional groups, suitable for removing small amount of impurity metal ions from waste zinc plating solutions. In order to lower the cost, new adsorption gel was prepared from orange juice residue containing pectic acid by crosslinking with epichlorohydrin, which was also found to be suitable for removing these impurities. Further, very cheap adsorption gels was prepared not only from orange but also from apple juice residues by a simple method through just saponificating pectin substances contained in these residues into pectic acid by calcium hydroxide followed by water washing and drying. These adsorption gels exhibited excellent adsorption behaviors for removing the impurity metal ions away from zinc.

Jan 1, 2003

By Michael Altepeter

Big River Zinc Corporation, located in Sauget, Illinois, operates a neutral leach residue circuit. The residue produced in the circuit is sold to lead smelters for subsequent recovery of valuable metals. A research program was initiated several years ago to find a means of treating the residue at Big River Zinc to recover the valuable metals. The Ausmelt submerged lance reactor was selected as the best alternative for the first step of the process. Pilot scale tests were conducted at Ausmelt's facilities in Melbourne, Australia. Separations were excellent. 99%+ of the Zn, Pb, Cd, and Ag contained in the residue reported to the oxide fume. 99%+ of the SiO2,, Fe, Mg, and Ca in the residue reported to the slag which passed the EPA TCLP test. Subsequent leaching of the oxide fumes and purification of the leach solutions using conventional procedures produced solUtions suitable for zinc electrowinning and an upgraded lead sulfate cake for sale.

Jan 1, 1992

By Mingchun Lu, Zhe Wang, Mingming Cao, Xiangdong Xing, Shan Ren, Jianliang Zhang, Zhengjian Liu

"The effect of reduction temperature on the vanadium titano-magnetite carbon composite pellets was investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and the discussion has put emphasis upon the enhanced reduction mechanism of additives containing CaF2 and NaF in this paper. The results showed that the reduction temperature of 1350°C was needed for the generation, mergence and growing up of metallic iron as well as monomer dissociation between metallic iron particles and slag phase in the vanadium titano-magnetite metallization pellets. The iron compound was completely reduced into metal iron, and Fe2Ti04 was mainly transformed into metal iron, (Fe,Mg)Ti205 and FeTi03 at 1350°C. The maximum metallization ratio was only 88.5% at 13500 for 30 min without any additive. However, with the addition of 3.0% CaF2 or NaF, the metallization degree of pellets could reach up to 94.8% and 92.5%, respectively.IntroductionVanadium titano-magnetite which is mainly distributed in the area of Panxi, Chengde and Maanshan in China is a kind of complex iron ore which contains various valuable metal elements such as iron, vanadium, titanium, etc. Among the above areas, Panzhihua (Sichuan Province in China) area possesses the largest deposits of vanadium titano-magnetite and the future reserves are more than 100x108t, and the reserves of Ti existing as Ti02 reach to 8.7x108t which occupy over 91% of the whole nation and ranked No.1 in the world[1]. Lots of researches on the comprehensive utilization of vanadium titano-magnetite have been conducted in the world. And many technological processes have been applied successfully in industrial production. Among these processes, the process of rotary kiln-electric furnace is employed to recover iron and vanadium in South-Africa, while the process of blast furnace-rotary furnace is widely used in Russia and China. Besides, many researchers have made efforts on employing new direct reduction process to realize the effective comprehensive utilization of vanadium titano-magnetite[2-4]. However, the direct reduction process is only researched in laboratory and it has not been used in industry."

Jan 1, 2013

By Mariane Costalonga de Aguiar, Carlos Mauricio Fontes Vieira, Sergio Neves Monteiro

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850, 950 and 1050°C. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at 1050°C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antonio de Padua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antonio de Padua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption [3,4]. To avoid this problem, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2011

By Arpad E. Tonna

Recycling of materials from lithium-oxyhalide batteries is a complex task, since the dismantling of batteries is associated with many hazards. The electrolyte and the lithium anode metal are extremely reactive in the presence of water or water vapor. Therefore, the dismantling process is a complex task. In this process, the lithium battery is electrically discharged, then frozen in liquid argon, and cut into small size pieces. These are fed into an incinerator, where the unreacted portion of lithium metal, thionyl chloride, plastic separators and carbon paste are decomposed and burned to gaseous products. The aluminum, iron (steel) and nickel pieces are recovered as saleable scrap metals. The off-gases are scrubbed with an alkaline sodium carbonate containing solution. The clean gases are released to the environment. The particulate mater recovered from the scrub-suspension would be available as additive to the cement industry . The recycling of battery decomposition products improves the economic viability of the disposal processes. Work is in progress to develop safe handling, processing and recycling large size lithium batteries.

Jan 1, 1995

By R. Y. Wan

Low grade sulfidic-carbonaceous refractory ore from Newmont Gold Company's Carlin deposit was microbially pretreated. The biological pretreatment process gave partial oxidation of the sulfidic components of the refractory ore but the preg-robbing carbon continued to be active resulting in approximately zero cyanide gold extraction. A 495 ton pilot plant test heap was conducted using acidic thiourea leach following biooxidation. Activated carbon and cation exchange resin adsorption were tested for gold recovery from the thiourea pregnant solution. The results obtained from the test heap were not satisfactory. Gold extraction was low due to slow reaction kinetics which was caused by relatively large particles and very low winter temperatures. Problems existed in the thiourea-test heap and are discussed in this paper. An alternative heap leach process using thiosulfate has been successfUl at the pilot scale for gold extraction following biooxidation pretreatment of refractory sulfidic-carbonaceous ores.

Jan 1, 1995

By K. A. Brunk

Newmont's research, operations, history and experience with pre-treatment of preg-robbing carbonaceous ores are described, with emphasis on the chemistry, physics and kinetics of chlorine treatment. Present operations, control strategy and projected changes are also described, including a summary of the adsorption of chlorine into pulps and off-gas scrubbing. Conditions of chlorination have been optimized by the use of Eh-pH diagrams of the gold-chlorine-water system, and have resulted in significant increases in gold recoveries and decreases in chlorine consumptions.

Jan 1, 1987

By Shunhong Huang

Thirty-five soils were sampled from three sites at different distances from chromium slag heap of a Iron-alloy factory, namely, nine from site A located under the chromium slag and eighteen from Site B in the vicinity of the factory and eight from site C far from the factory. The contents of total Cr in these soils from site A, B and C were 1666.0±1310.9 mg? kg - 1,1136.2±1844.6 mg? kg - 1 ,300.4 ±165.1 mg? kg ? 1, respectively. The contents of water soluble Cr were 59.3±77.57 mg? kg ? 1,0.6 ±0.3 mg? kg - 1 ,0.5±0.3 mg? kg - 1 , respectively. In order to evaluate soil health, the activities of four soil enzymes (catalase, polyphenol oxidase, dehydrogenase, alkaline phosphatases) were analyzed. The results have shown that dehydrogenase activity was greatly depressed by conditions in the heavy chromium-contaminated sites. Negative correlation was observed between dehydrogenase activity and the distance from the chromium slag heap, however, the activities of catalase, polyphenol oxidase, alkaline phosphatases in soils from the three sampling sites mentioned above did not differ significantly. The result imply that of dehydrogenase activity could be used as an indicator for the chromium pollution level in the area of Iron-Alloy factory and for the stability level of the soil ecosystem.

Jan 1, 2008

By K. S. Izbakhanov

The Chimkent Lead Plant was constructed in 1934 and since that time has undergone many revisions. In 1975 the slag fuming operation was changed from pulverized coal to natural gas fuel. In 1981 the slag fuming furnace water jacket system was converted to evaporative cooling with high pressure steam production. The impact of these changes and the method of their application are described.

Jan 1, 1990

By Qingchun Yu, Baoqiang Xu, Yongnian Dai, Bin Yang, Fulong Zhu

"In this paper, the mechanism of the carbothermic reduction-chlorination process to extract aluminum from alumina in vacuum was investigated. The carbon monoxide (CO) content of the gas, phases of the reduction slag, surface morphology of the reduction slag and the product aluminum were measured by means of gas chromatography (GC), XRD, and SEM. The experimental results indicated that the content of CO in the gas decreased, but Al4C3 increased with time at 1773K during the carbothermic reduction process of alumina. AlCl(g) and graphite (C) were produced by the reaction between Al4C3 and AlCh(g) at 1773K, and then aluminum beads generated after the decomposition of AlCl(g). It implied the mechanism of alumina carbothermic reduction-chlorination process in vacuum involves three steps as follows: the carbothermic reduction of A}z03 to produce Al4C3, the chlorination of Al4C3 by AlCh(g) to produce AlCl(g), and the decomposition of AlCl(g) to produce Al(l).IntroductionAluminum is the basic raw material for many industries [1], and it is used extensively because of various excellent properties such as light weight, good malleability, high strength, excellent thermal conduction, high corrosion resistance and so on [2]. Industrial production of aluminum currently includes refining alumina and electrolytic aluminum processes. However, its development has been effected by some factors such as high energy consumption and heavy environmental burdens [3]. In the past several decades, there had been numerous attempts to produce aluminum by new methods. Extracting aluminum from alumina or bauxite directly by carbothermic reduction-chlorination process had been studied [ 4-6]. Although the alumina carbothermic reduction process [7~9] had been studied, the mechanism of the carbothermic reduction-chlorination process had not been systematically elucidated.In order to investigate the mechanism of the carbothermic reduction-chlorination process in vacuum, GC, XRD and SEM techniques will be used to determine the CO content and to characterize the surface morphology and composition of the slags at various temperatures."

Jan 1, 2011

By Balladares V. Eduardo

Most of the arsenic contained in copper concentrates is removed in the gas phase during the smelting and converting processes and, according to recent environmental regulations, it is required to fix it in a solid stable form. In this regards, ferric arsenate has been reported as thermal and aqueous stable compound. Therefore, various alternatives for treating gas containing arsenic were considered in this work. From data obtained at laboratory scale on fixation of arsenic using iron oxide, a new process to treat copper concentrates containing arsenic was evaluated. The effect of temperature, oxygen potential and the sample porosity on the fixation of arsenic contained in a gaseous stream was studied, and the iron oxide converted into ferric arsenate was up to 10%. The obtained results suggest a new alternative for gas treatment with an interesting and attractive technical development. The arsenic was retained as ferric arsenate with thermal and aqueous stability, and it allows a safe disposal keeping the environmental restrictions. The kinetics parameters are used to scale up laboratory results to higher processing rates.

Jan 1, 2005

By Zhongning Shi, Ramana G. Reddy, Min Li, Zhaowen Wang

Electrodeposition of cobalt from cobalt tetrafluoroborate (Co(BF4)2) was investigated using 1- butyl-3-methylimidazolium tetrafluoroborate (BMIMBF4) ionic liquid. The experiments were conducted at 353 K. Chronoamperometry experiments confirm that the electrodeposition of cobalt on tungsten electrode proceeds via three-dimensional instantaneous nucleation with diffusion-controlled growth process. The average diffusion coefficient of Co(II) was found to be 7.5 × 10-8 cm2s-1 at 353 K, which is in good agreement with the estimated value from cyclic voltammetry. The electrochemical deposit was characterized using SEM-EDS and XRD methods. The SEM image shows formation of a dense and compact deposit at - 0.75 V. The EDS and XRD analysis confirm that the obtained deposit is pure cobalt metal.

Jan 1, 2015

By Yapeng Zhang, Zhiwen Shi, Chaoquan Yao, Fei Wang, Xinyu Li, Jianliang Zhang

A great deal of iron ores which have special elements have been applied in the sintering process with the decreasing of high-grade quality iron ores resources. In this paper, the laterite nickel ores were added into three different kinds of iron ores respectively to make liquid phase formation research by software of Factsage and high temperature characteristic sintering experiments. The results showed that the adding proportion of laterite nickel ores should be less than 15% when the high temperature properties of the mixing ores were well. Increasing the mixing ration of laterite nickel ores in the sintering blending would play an important role in the reduction of the sintering cost.

Jan 1, 2015

By Xiang-dong XING, Zhen-yang wang, Xing-le LIU, Jian-Liang Zhang

Experiments were carried out by adding CaF2 as catalyst in a Ar atmosphere to study the isothermal reduction kinetics of vanadium titano-magnetite carbon composite pellets under high temperature in the range from1473 to 1673K. By analyzing reduction mechanism, it was found that the rate controlling step was gas diffusion, and the activation energy was 178.39kJ•mol-1 without adding any catalysts. Adding CaF2 of 3% to vanadium titano-magnetite carbon composite pellets can decrease the apparent activation energy of reduction, and the decrease extent was 14.95kJ•mol-1. In addition, temperature is an important factor influencing on reaction rate.

Jan 1, 2015

By Carlos Maurício Fontes Vieira, Sergio Neves Monteiro, Diogo Neves Henriques

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850 to 1100oC. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at temperatures above 1000 ° C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antônio de Pádua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antônio de Pádua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption and low mechanical strength [3,4]. To avoid these problems, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2008

By Duclerc Fernandes Parra, Washington Luiz Oliani, Christiano Gianesi Bastos Andrade, Ademar Benevolo Lugão, Danilo Marin Fermino, Francisco R. Valenzuela Diaz

This work concerns the study of the effect of discarded bond paper on the mechanical behavior of polypropylene/organophilic clay nanocomposites. A brown polycationic bentonite from the state of Paraíba, Brazil, was treated with sodium carbonate to transform it into a bentonite that swells in water and then treated with hexadecyltrimethylammonium ammonium chloride to transform it into a bentonite that swells in organic liquids. Polypropylene with 3 % polypropylene graft compatibilizer (PP-g-AM) was mixed with 1 % and 2 % by weight of discarded bond paper and with 1% and 2% by weight of organophilic clay using a twin-screw extruder. The specimens were prepared by the injection process. The clay as received and after organophilization was characterized by XRD, SEM, and capacity of swelling in water and in organic solvents. The nanocomposite specimens were characterized by XRD and thermal analysis. The mechanical behavior of the injected specimens was evaluated by strength, flexural and impact tests. The nanocomposites showed improved mechanical properties compared with the polymer without filler.

Jan 1, 2015