The fire assay process for the quantitative recovery of platinum group elements (PGE?s) prior to subsequent analysis traditionally is a time-consuming process. Samples derive from various ore types and contain PGE?s at the ppm or ppb levels, making concentration of the elements mandatory before assaying. Traditionally sample turn-around times are of the order of 24 hours. The whole sequence of sample preparation, fire assay and subsequent analysis of PGE?s have been automated by Anglo Platinum. Some of the major challenges on the road to automation will be discussed and the novel solutions that were implemented. The engineered solution included robotic automation of the whole sequence, from sample preparation, up to the final element by element assay. The final system allowed for rapid (less than one hour) and accurate analysis of PGE?s even in streams containing very low levels, such as flotation tailing streams and drill core samples.

Jan 1, 2006

By David Arana

The use of gas-water dispersion of a molten material flow onto a vibrating surface is developed as a process to minimize water pumping requirements, minimize the risks of explosions, and minimize the post solidification dewatering and fines handling equipment requirements. The process uses existing vibration transport technologies and common plant utilities. Plant trials using the smaller footprint and the progressive molten particle cooling time have yielded encouraging results. The results are analyzed and reported.

Jan 1, 2006

By Pratheesh George

Solid state galvanic cell with CaF2 as the electrolyte was employed for determining the thermodynamic properties of Nb-Al binary alloys in the temperature range of 973-1073 K. The activities and activity coefficients of Al in NbAl3 were determined. The experimental procedure and the design and construction of the experimental setup have been also explained in detail. Aluminum activity in NbAl3 increased with increase in temperature and shows a strong negative deviation from ideality. The activities of aluminum in NbAl3 were determined to be 0.0165 and 0.0289 at 973 and 1073 K respectively. The stability of NbAl3 has been compared with other available intermetallic systems.

Jan 1, 2006

By Xingjian Gao

The mechanical properties of a low carbon low alloy steel in the austenite and _-ferrite regions have been examined by thermal-tensile tests using a Gleeble-1500D system at temperatures in the range 600oC to 1300oC and at a strain rate of 10-3/s; these being the conditions that apply to the unbending operation during the continuous casting of steel. The yield strength and tensile strength of steel decreased with increasing test temperature and the embrittlement zone occurred in the temperature range 800oC to 970oC. In the embrittlement zone, the fracture surfaces and microstructures of the tensile specimens were examined by scanning electron microscope. The results showed that the cause of the embrittlement at 950oC in which the minimum %R of A was around 36% is the second phase particles precipitated along the _ grain boundary during deformation leading to inter-granular brittle fracture.

Jan 1, 2010

By C. J. Parradies

During injection into a die, semi-solid metal alloys exhibit a shear-rate, history-dependent flow response. Simulating the injection of a thixotropic material requires that empirically determined boundary conditions and viscosity are specified as a function of both temperature and shear rate history. Experiments were performed using an industrial die casting machine that was instrumented with sensors to measure the pressure and temperature during the injection of a semi-solid aluminum alloy through a tube. This benchmark experiment was used to develop a simulation of the die casting process that could then be applied to more complex die geometries. The results of the experiments were analyzed using the exact, steady state solution for a power law fluid and simulations accounting for slipping at the boundary between the semi-solid metal and the die. Results indicated that the no-slip condition cannot be used to simulate the velocity boundary condition, because the measured pressure is much lower than that predicted by the models. An estimated apparent slip coefficient was introduced to account for the reduced pressure. During some of the experiments, a sudden drop in the measured pressured, prior to decreasing the ram velocity, coincided with observations of segregation in the form of concentric rings visible on the polished surface of cross-sections cut from material remaining in the tube.

Jan 1, 1997

By B. P. Sereda

The properties, characteristics and phase structure of chamotte refractories produced with the usage of mullitecorund chamotte and caoline have been given. The comparison of new refractory C-45 obtained by us and refractory C-43 produced by traditional method has done. The physical-chemical properties of refractories is reviewed. The visual porosity, density and pore characteristics of given refractories was calculated. It is established that C-45 has the less gas permeability then C-45 that gives melting units more stability. The petrographical microstructures of refractories have been done. The main phase structures and their influence on refractories properties have been observed. It is established that refractories with mullitecorund chamotte adition has more advantages then refractories gained by traditional method and can be applied to melting units.

Jan 1, 2010

By Emmanuel N. Zevgolis

Energy required for roasting and smelting of a nickeliferous laterite ore by the rotary kiln - electric furnace process is investigated. From this work it comes that thermal energy is about 65% of the total energy needed and the rest is electrical. Also, 61.3% of thermal energy input in the roasting step (of all combustibles fed into the rotary kilns) is used for pre - heating, 11.6% for pre - reduction and the rest (27.1%) corresponds to the energy of the remaining carbon in the rotary kiln products (i.e., calcine, dust and coatings). Carbon entering the system is used as follows: 57.9% for combustion, 37.1% for reduction and the rest (5.0%) remains unburnt. Exploitation of energy from gases of both furnaces, as well as the higher possible reduction degree, the optimum temperature of the calcine and also elimination of the excess air in the rotary kilns, improve significantly energy balance and economics of the process.

Jan 1, 2006

By P. J. Uggowitzer, H. Kaufmann

"New Rheocasting is a novel route of semi-solid casting, in which the globular semi-solid precursor material is produced by controlled cooling of only slightly superheated melts in conventional steel crucibles. The resulting semi-solid slugs are placed into the sleeve of a vertical Squeeze Casting Machine and then filled into steel dies. Solidification occurs under hydraulic pressures up to 100 MPa Due to the reduced cost of precursor material, reduced investment cost and easier recycling, the New Rheocasting process offers cost reductions of up to 25% over conventional semi-solid casting · routes. The New Rheocast products are pore free, pressure tight, weldable and heat treatable castings.In the present work the New Rheocasting Process is introduced and the influence of heat treatment on mechanical properties of the New Rheocast alloy A356 is discussed.The alloy A356 is cast under ideal New Rheocasting conditions into a step die on an UBE HVSC 350 Squeeze Casting machine. As-east, TS and T6 heat treatment conditions with variations in solutionizing and aging time/temperature parameters are applied and the samples are tested by tensile testing. Alternatively, the same heat treatment conditions are applied to conventional Squeeze Casting parts and compared with New Rheocasting.Questions of potential cost savings due to modified heat treatment conditions are also addressed in this paper."

Jan 1, 2000

By Esher Hsu

In Taiwan, around 8,000 tons of batteries are consumed per year but only 17% of which were collected and transported to oversea for recovery. The dumping used batteries have become a potential environment problem. How to increase the collection efficiency of used batteries is an important issue for EPA in Taiwan. Besides, some treatment plants are on process to get permission for recovering used batteries. The objective of this study is to estimate the recycling cost of spent consumer battery and explore the feasibility of recovering used consumer batteries in Taiwan based upon the principle of cost-efficiency. The recycling cost including collection cost and recovery is estimated based on a survey. Results would provide some suggestions to Taiwan EPA regarding feasibility of recovering used batteries in Taiwan.

Jan 1, 2006

By Helfried Nafe

"For about a century thermodynamically absurd facts have been propagated in conjunction with the iron-carbon phase diagram. These facts concern fundamental relationships of chemical thermodynamics. Attention is turned here to the discussion of only one of the relevant aspects of the subject, i.e. the definition of the thermodynamic activity of the solute and its implications for the iron-carbon solution.IntroductionThe view on the iron-carbon solution is characterized by the assumption that the solute may appear in two different forms, i.e. graphite and cementite. Accordingly, two carbon solubilities are differentiated, on the one hand for graphite and, on the other hand, for cementite. As a consequence, two versions of the phase diagram exist simultaneously, the application of which depends on the prevailing conditions, (i) the so-called stable phase diagram with graphite as solute and (ii) the metastable one that is based on the cementite-in-iron solution. These diagrams are joined together in the double phase diagram that originates from Heyn [l ], with the first ideas mainly going back to Stansfield [2] and Charpy [3].Thermodynamically, the most inadequate implication of the Fe-C double phase diagram is that the carbon activity may take values larger than unity. With the standard state of the activity being that of the pure substance, i.e. the Raoultian one, such a value implies the nonsensical existence ofa state purer than pure. The explanation of this physical state, ifthere is any, vaguely refers to supersaturation and, in the wider sense, to the physico-chemical phenomenon of metastability. Other aspects of chemical thermodynamics are likewise involved. Therefore, the comprehensive investigation into the present subject requires more topics to be considered than only one separate issue. Not only should the criticism of the present view be in the focus but also the discussion of new ideas capable of reconciling the experimental facts, known about the F e-C system, with the fundaments of chemical thermodynamics. All this, however, cannot be provided here because of the limited space available. As a consequence, in what follows only a part of the whole problem is under scrutiny, i.e. the definition of the thermodynamic activity and its role for the interpretation ofrelevant experimental facts."

Jan 1, 2014

By Mishark Nnabuchi

A heterojunction of PbS - CuS thin film has been grown on glass slides by SGT. The films were annealed for 1hr at temperature of 373K and 423K respectively. The optical properties were characterized using a UNICO UV - 2102 PC Spectrophotometer at normal incidence of light in the wavelength range of 200 - 1000nm. The minimum percentage transmittance was observed to be 34% for sample A and 25% for sample B within the same optical region. The band gap energy was determined from the spectra to be 2.05eV for sample A and 1.85eV for sample B which gave a band shift of 0.20eV. It can thus be concluded that the optical properties of the films within the VIS - UV - NIR can find application in solar thermal technology, particularly as antireflection coating, window materials and as good materials for selective solar cell fabrication.

Jan 1, 2010

By Jewel A. G. Gomes

Electrocoagulation (EC) has been performed with Al-Fe electrode system with changing polarity for the removal of arsenic from water. The removal process has been studied using ICP-AES and Anodic Stripping Voltammetry with a wide range of arsenic concentration (1-1000 ppm) at various pH (4-10) and residence times (1-60 min). Electrochemically generated by-products have been analyzed using XRD, FTIR, XPS, SEM/EDS and Mössbauer Spectroscopy. Results revealed expected crystalline iron oxides (magnetite (Fe3O4), lepidocrocite (FeO(OH)), iron oxide (FeO)) and aluminum oxides (bayerite (Al(OH)3), diaspore (AlO(OH)), mansfieldite (AlAsO4?2(H2O)), as well as some interaction between the phases. The amorphous or ultra-fine particular phase was also found in the floc. The substitution of Fe3+ ions by Al3+ ions in the solid surface has been observed, indicating an alternative removal mechanism of arsenic in these metal hydroxides and oxyhydroxides by providing larger surface area for arsenic adsorption via retarding the crystalline formation of iron oxides.

Jan 1, 2006

By Felipe Perissé Duarte Lopes

The tensile properties of DGEBA/TETA epoxy matrix composites reinforced with different amounts of curaua fibers were evaluated. Tensile specimens with up to 35% in volume of long, continuous and aligned curaua fibers were room temperature tested in an Instron machine. The fracture was analyzed by SEM. The results showed significant changes in the mechanical properties with the amount of curaua fibers. This was compared to other bend-tested composites with distinct matrices. The fracture analysis revealed a weak fiber/matrix interface, which could be responsible for the comparatively low performance of some properties.

Jan 1, 2010

By Xue Wang, Callie Babbitt, Chelsea Bailey, Matt Ganter, Gabrielle Gaustad, Brian Landi

"Current trends, motivated by fossil fuel dependence and unprecedented greenhouse gas (GHG) emissions, show lithium-ion batteries (LIBs) emerging as a competitive energy storage technology due to higher power and energy densities compared to Pb-acid and Ni-metal hydride chemistries. These trends may be of concern, however, as environmental impacts are not well understood for either the LIB itself, or for the nanoparticles consumed or released during the battery's production, use, or end-of-life. This study combines economic modeling, dynamic material flow analysis, and fundamental material characterization methods in order to quantify some of the economic and environmental trade-offs for LIBs at their end-of-life. As expected, results show that as chemistries transition from Li-Co based cathodes to Li based Fe, Mn, and S cathodes, LIB recovery value correlates to the value of the raw materials used. These initial results aim to inform collection policies being proposed currently as well as enable future deployment of novel recycling techniques.IntroductionGlobal fossil fuel dependence and unprecedented GHG emissions have led to increasing attention on energy alternatives, for both electricity production and personal transportation. However, development of renewable energy systems is contingent on concurrent technological development of energy storage systems, primarily batteries used for power grid load-leveling, renewable energy storage, and hybrid and battery electric vehicles. In this sector, lithium-ion batteries (LIBs) are emerging as a competitive technology due to higher power and energy densities compared to lead-acid and nickelmetal hydride chemistries[!]. LIBs represent close to 20% of the total rechargeable battery market and 75% of the portable rechargeable battery market, which is the fastest growing segment of the rechargeable battery market, with a 20% global growth in 2008 [2].This surge in production ofLIBs indicates a looming waste problem; total waste from Li-ion batteries has likely grown substantially from the 500 metric tons estimated in 2003 [3]. Figure IA shows the substantial increase in world-wide lithium production that has occurred in the last several decades with batteries making up the largest share of applications (Figure lB). California and New York state legislators have attempted to proactively address this looming waste by issuing diposal bans on rechargeable batteries in their states[4, 5]. However, quantification of the costs involved in collection, transportation, and processing of these materials has not been examined in depth."

Jan 1, 2012

By Joner O. Alves

The disposal of scrap tires has been a serious environmental problem. The treatment of this waste by pyrolysis and combustion has advantages since the landfill space is dwindling and the production of fuel becomes of technological interest. However, that processes needs a rigid control of emissions. This work presents a study of the light hydrocarbon gases (HC) generated during the burn of waste tire chips in a two-stage laminar-flow horizontal furnace. Different temperatures in the primary and secondary stage of the furnace were tested, and the oxygen/nitrogen percentage was also varied during the combustion process. A gas chromatograph was used to identify and quantify the components of the gaseous products of combustion and pyrolysis. The results showed the behavior of the gases during the burn of tires, providing valuable information to the control of hydrocarbon emissions.

Jan 1, 2010

By Jeffrey R. Taylor

The distribution of low concentrations of Cr, Mn, Rh, Co, Ni, Ag and Fe between copper matte and bullion phases has been measured at 1200oC. These results. together with values for nine other elements, have been used to develop a simple model to describe the distributions in terms of known thermodynamic properties?. The Temkin model for ionic melts was assumed to apply to the sulphide species in the Cu-S matte? phase and it is shown that the choice of sulphide species is particularly important for successful representation of the experimental .results?. In general, the lowest sulphlde (minimum sulphur :. metal ratio)? formed by the. metal is most suitable, although Ni, Co, Rh and Pd appear to associate with more sulphur in the melt than suggested by the? composition of their lowest sulphide. A correlation between the composition of the metal sulphide species formed in the ternary system and the? position of the minimum in the free energy of mixing curve in the metal-sulphur binary -system is? proposed.

Jan 1, 1983

By Zhouhua Jinag

The attempt has been made to manufacture high nitrogen austenitic stainless steels by pressurized electro-slag remelting furnace with maximum nitrogen pressure of 7MPa. To obtain high nitrogen content in steels, the compound electrodes with different nitrogen sources (FeCrN, Si3N4) were prepared. Using the Si3N4 as the nitrogen alloying source, the silicon contents in ingots were prone to be out of the specification range, and the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved using FeCrN as nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen above 1.0wt% could be obtained. A series of high nitrogen austenitic stainless steels have been successfully developed by this method. The mechanical and pitting corrosion resistance properties of high nitrogen austenitic stainless steels were investigated. The results show that the steels exhibit excellent mechanical and pitting corrosion resistance properties.

Jan 1, 2009

By Chao Du, Xiaohui Ning, Hongmin Zhu, Qiuyu Wang, Shuqiang Jiao

"TiCxOl-x solid solutions were synthesized by sintering a mixture of titanium carbide and titanium monoxide at 1600 °C. The corresponding structures and morphologies of the TiCxOl-x solid solutions were characterized by XRD and SEM. A series of tests has been performed on the electrochemical dissolution behavior of TiCxOl-x solid solutions in NaCl-KCl molten salt. The influences of synthesis time and electrokinetic parameters on the anodic dissolution behavior were also investigated. The results showed that TiCxOl-x solid solutions can dissolve as Tin+ into alkali chloride melt. Titanium ion species dissolved from TiCxOl-x solid solutions changes between Ti2+ and Ti3+ depending on the applied potential. The tail gas on the anode was monitored by a mass spectrometer. It was found the synthesis time significantly affects the components of the anodic gas.IntroductionTitanium and titanium alloys have been desired greatly because of their many uses. The critical factor that restricts the range of uses for Ti is its high cost of extraction. The primary titanium metal, sponge titanium, is still produced industrially worldwide by a process invented by Dr. Kroll in the 1940s[1] •Since the early 1970s, the research focus of the titanium industry has been directed towards developing a continuous process to produce high purity titanium at low cost. [2-10] Of the many alternative methods that have previously been investigated, the electrolytic process has been considered a promising method for titanium metallurgy [4-10]. Recently, several electrolysis and related methods such as the PFC-Cambridge process[11-15], calciothermic reduction[16-18], USTB [19,20] and MER[21] process were extensively investigated.The USTB process is a new approach where the pure titanium can be directly obtained by the electrolysis with an anode of titanium oxycarbide in molten salts[19, 20]. The titanium oxycarbide was produced by carbothermal reduction of titanium dioxide under vacuum at a temperature"

Jan 1, 2011

By Arthur E. Morris

The primary market driver for improving process technology is innovation, which requires a skilled and educated workforce. However, many Materials Science and Engineering departments have eliminated extractive metallurgy and chemical thermodynamics from their curricula, yet these topics contain the necessary fundamentals for process innovation. As a result, most MS&E students are ill-prepared for careers in processing. The dearth of processoriented MS&E curricula has prompted some Universities to develop a “shared” effort to offer distance education between multiple institutions [1]. A target audience for a shared process simulation course would not only benefit students, but also be a basis for an on-line course for practicing engineers faced with new or changing career choices. To fill the gap, the basics of a process simulation course was developed in an abbreviated form as series of eleven articles and Excel workbooks published in Industrial Heating magazine between July 2012 and July 2013.

Jan 1, 2014

By A. Barba, M. P. Gómez, F. Puertas, M. Palacios, M. F. Gazulla, S. Martínez-Ramírez, I. García-Díaz

"The present study explores the reactivity and burnability of cement raw mixes containing fired red or white ceramic tile wastes or combinations of the two as alternative raw materials. The results showed that the new raw mixes containing these wastes are technically viable. The reactivity and burnability of the new raw mixes have been evaluated; confirming very good results when the particle size of wastes was less than 90 µm. The chemical and mineralogical compositions of the new clinkers were comparable to clinker manufactured with conventional raw materials. The mix of red and white ceramic tile waste was found to perform as well or better than each type of waste separately, a promising indication that separation of the two would be unnecessary for these purposes.IntroductionPortland cement clinker production consumes large amounts of energy (850 kcal/kg clinker) and has a considerable environmental impact. This involves massive quarrying for raw materials (limestone, clay etc), as it takes 1.7 tonnes to produce one tonne of clinker, as well as the emission of greenhouse and other gases (NOx, SO2, CO2) into the atmosphere. Around 850 kg of CO2 are emitted per tonne of clinker produced.The cement industry is looking for solutions to these problems, to attain sustainability and comply with the Kyoto Protocol commitments [1,2]. For that reason, experimental ways are being explored to develop cements whose manufacture is less energy-intensive, less damaging to the surrounding environment and with lower tendency to emit polluting gas. One of the reach this objective is the use of industrial waste and by-products as alternative materials for cement manufacture. Such alternative materials may partially replace fuel [3,4], conventional raw materials [5-8] or clinker in the final composition of the cement [9]."

Jan 1, 2008