By G. Howell Clevenger

FORMERLY great divergence of opinion existed in regard to the influence of copper in steel, as affecting its various physical properties. More recently the investigations of Stead,1 Breuil,2 Wigham,3 Burgess and Aston,4 Ball and Wingham,5 Miiller,6 Dillner,7 and others have shown fairly good agreement in the major points. Copper steel has been shown by these investigators to possess special properties which make it valuable for certain uses. The general range of composition of the useful alloys of copper and iron, and of copper, iron, and carbon, has been quite definitely established, for the former by Burgess and Aston,8 and for the latter by Breuil 9 and Stead.10 Stead 11 has removed one difficulty in reconciling certain of the earlier data by calling particular attention to the influence of carbon in copper steels. Another point which caused confusion in the earlier investigations, particularly in regard to " red-shortness," was the presence of sulphur. Failure to note the presence of sulphur often led to attributing " red-shortness " to the presence of small amounts of copper. Turner 12 has called attention to the fact that where copper exists in an iron ore it often occurs as the sulphide, so that the presence of copper in steel made from such ores might also, necessarily, mean the presence of sulphur. It is evident that the effect in this case might be quite different than where pure copper was added.

Jan 10, 1913

By James C. Word, R. M. McLouski

This paper will describe the development and application of large-scale integration techniques employed in the fabrication of a germanium multielement array. The array consists of 100 by 228 PNP bipolar transistors fabricated on 5 mi1 centers. Back-biased p-n junction techniques are used for electrical isolation of the individual elements. The end use of the array is a high resolution, large area IR sensor. The monolithic array is fabricated in 1 ohm-cm p-type germanium epitaxially deposited on 6 ohm-cm n-type substrate. Epitaxy was accomplished through the hydrogen reduction of germanium te trachloride. Di-borane was used as the dopant. Base regions are achieved by the diffusion of arsenic from doped oxide or arsine sources. Oxide-masking of the arsenic im-pzlvity was achieved by the chemical deposition of a boron doped glass. The emitter is formed by an aluminum alloy diffusion technique. Vacuum deposited aluminum is used for the emitter, interconnections, and for the contact and bonding pads. ALTHOUGH a great volume of literature pertaining to the development of large scale integration techniques (LSI) has been published for silicon and in particular silicon imaging applications,' to date only a small number of similar devices have been constructed using germanium technology.' Since the physical and chemical properties of germanium are vastly different from those of silicon, the fabrication technology for integrated structures in germanium is also different from that of silicon. In particular germanium does not possess a stable oxide as can be grown on silicon by heating in an oxidizing ambient for masking of dopants and passivation. This paper describes the application of germanium LSI techniques employed in the fabrication of a multielement infrared sensor array. The array is used in a high resolution, large area infrared sensor for operation in the 0.8- to 1.5-u spectral range. Back biased p-n junction techniques are used for electrical isolation of individual elements. Discrete germanium devices have been fabricated routinely for some time. However, mainly due to the lack of a suitable mask for selective doping and the high current leakages inherent in germanium p-n isolation, few monolithic germanium structures have been constructed. THE INFRARED MOSAIC A cross-sectional view of the array is shown in Fig. 1. The monolithic structure consists of 12,800 PNP transistor elements in a 100 by 128 matrix fab- ricated on 5 mil centers. The emitters of each line of transistors are connected together using aluminum interconnects while the strip collectors are connected together in series at right angles to the emitter lines. The selection of this structure is dictated by the readout technique involved. Access to each element transistor is obtained by applying a bias voltage to a particular collector strip and separately interrogating each emitter row. A charge storage, i.e., an integration mode is used for reading out this particular array Construction techniques available for use with germanium do not include a selective p-type diffusion capability for surface concentrations greater than 10" per cu cm and junction depths greater than about 10 u. This fact limits the type of structure that may be used. Therefore, an array of PNP transistors that did not employ p-type diffusions was chosen. The structure was fabricated by growing a 1 ohm-cm p-type epitaxial layer on a carefully prepared 6 ohm-cm n-type substrate. N-type dopants were used for the isolation and base diffusions and alloyed aluminum was used to form the emitter junctions. The array was then completed by evaporation of aluminum interconnections and contact pads. SUBSTRATE AND SUBSTRATE PREPARATION Germanium substrates of (111) orientation grown by both Czochralski and zone leveling techniques were utilized for mosaic fabrication. Czochralski substrates were preferred because of the lower dislocation densities available in this type of material. Dislocation densities for the Czochralski material were typically less than 3000 per sq cm, while those for the zone leveled material were typically less than 5000 per sq cm. All substrates were uncompensated to minimize thermal conversion problems in subsequent epitaxial and diffusion processing. Both in-house and vendor polished wafers were used. The in-house polishing technique employed consisted of an initial gross chemical etch in CP4 to remove saw damage from both surfaces. This was followed by a chemical-mechanical polishing operation of one side of the wafer. The chemical-mechanical polishing solution used was Lustrox 1000 (Tizon Chemical Co.), and consists of zirconium dioxide, sodium hypochlorite, water and a surfactant. The wafer thickness before and after polishing was typically 0.020 and 0.010 in, respectively. THERMAL CONVERSION The problem of thermal conversion of both the substrate and epitaxial layer was particularly acute because of the relatively low carrier concentrations employed in both regions. This problem has been encountered by other workers in the past.3 Without special treatment before epitaxial growth substrate conversion (n-type to p-type) and changes in the re-

Jan 1, 1970

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending' upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2'3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn's early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By Thomas M. Price

Sand production for use in hydraulic concrete is probably the most important element affecting the physical characteristics of the resulting concrete in the opinion of most engineers, aggregate producers and contractors of today, who are engaged in the effort to produce stronger concrete per unit of cement used. Their opinion is based on both laboratory and field results. In the past, proper cement production has been the object of most of the study given this subject and while it is still studied by the extensive and well equipped laboratories that are a part of every cement mill, as well as by all governmental laboratories, at the present time the object of most of these studies has been in the field of low heat and quick setting qualities rather than the effect on the strength of the concrete. It is recognized that concrete must have two important qualities; namely, workability with the least water possible, and uniformity. These qualities have been accepted as axiomatic and possible to obtain if the foreman in charge knew his business. Now, however, with concrete produced by plants that mechanically weigh and chart all the ingredients, including water, of a batch of concrete, the foreman cannot cut and fit his aggregates, cement and water to fit his own desires and the secret of the important qualities of workability and uniformity are found to lie largely in the sand, hence the attention given its production at the present time. With this condition in mind the engineers of the United States Bureau of Reclamation and the Six Companies Incorporated in designing the plant for producing the aggregates for the Boulder Canyon Project included every possible means for the production of a sand of a constant and acceptable fineness modulus as well as a constant moisture content, and for attaining these results with as few detrimental ingredients, like silt and vegetable matter, as possible. This aggregate plant (Figs. 1 and 2) is in Hemenway Wash, 7 miles north of Boulder City. It is 4 miles upstream from the low-level mixing plant. At this screening plant 8,234,000 tons of raw aggregate are being

Jan 1, 1934

By W. E. Quist, R. Taggart, D. H. Polonis, C. J. van der Wekken

An intermediate compound that has been identified as Niab is observed to form as a decomposition product from supersaturaled Ni-Nb solid solutions during aging at temperatures between approximately 300" and 500°C. On the basis of data from electron microscopy and selected-area diffraction, the structure of this compound has been determined as fct with a = b - 3a0 and c = a, wlzere a,, is the lattice parameter of the parent solid solution. The compound consists of close-packed layers with triangular ordering, where the niobiutrl atoms are separated by two nickel atoms ([long- close?-packed directions. A nine layer stacking sequence is required to describe the proposed structure. STUDIES of the Ni-Nb binary system have been limited primarily to phase diagram determinations,'-4 investigations of high-temperature equilibrium phases,5"1 and the determination of the influence of deformation on the structure of the equilibrium compound.8 The nickel-rich portion of the binary system is reported to be of the simple eutectic type in which the maximum solubility of 12.7 at. pct Nb occurs at 1282"c.' The two-phase field below the eutectic temperature is bounded by the a fcc solid solution and an orthorhombic Ni3Nb compound. No metastable phases have been reported in previous investigations. In transformation studies of certain nickel-base commercial alloys that contain niobium, two ordered metastable compounds containing niobium have been shown to precipitate from the solid solution, both of which have been identified as y' and have the composition NisNb or Ni,Nb. One compound has been reported to have the bct DOz2 type Al3Ti structure" and the other the cubic LI2 type Cu3Au structure.9,11 In the present work on Ni-Nb binary alloys a metastable y' compound has not been detected after conventional quenching and aging treatments. An anomalous behavior was noted in electrical resistivity measurements. in alloys containing between 7 to 12 at. pct Nb when aging treatments were performed below 500°C after fast quenching from 1250°C. Transmission electron microscopy has shown that this behavior is caused by the formation of a low-temperature precipitate of unreported structure type and composition. EXPERIMENTAL METHODS Several Ni-Nb alloys, containing up to 11.5 at. pct Nb. were prepared by either levitation melting and casting in copper molds or by induction melting in alumina crucibles; both techniques employed purified helium gas as a protective atmosphere. The purity of the nickel and niobium used to make the alloys was 99.98 wt pct Ni and 99.9 wt pct Nb. The composition and homogeneity of the alloys were checked by weight measurements and by electron microprobe analysis. The induction-melted alloys were homogenized for 100 hr at 1100°C. The resistivity specimens were prepared from rods swaged to 2.5 mm and the electron microscopy specimens were cut from sheet that was rolled to 0.4 mm and thinned using a modified Bollmann technique." The elevated-temperature solution treatments were carried out in a purified helium atmosphere followed by direct quenching into a 10 pct NaCl solution at 23°C. Additional protection against oxidation of the samples during solution treatment was accomplished by using tantalum foil as a "getter" in the furnace. The specimens were aged at various temperatures in salt baths controlled to +2oC. A Leeds and Northrup K5 potentiometer was used to make electrical resistivity measurements on specimens immersed in liquid nitrogen. Electron microscopy and diffraction studies were carried out with JEM-7 and Philips EM-200 microscopes operating at 100 kv. RESULTS AND DISCUSSION Ni-Nb alloys containing between 7 and 11.5 at. pct Nb that have been solution-treated in the range 1220" to 1280°C and quenched to 23°C undergo a precipitation reaction when aged in the temperature range 300" to 500°C. Precipitation was detected by selected-area electron diffraction after aging a specimen for as little as 30 sec at 350°C) whereas the reaction was well-advanced after aging for 150 hr at 475°C. Electrical resistivity measurements were used to monitor the progress of the precipitation reaction. In the present experiments the nucleation process for precipitation required a high solution temperature and a rapid quench into brine. The presence of aluminum, iron? and carbon in amounts totaling less than 1 wt pct was found by electron diffraction to completely suppress the formation of the low-temperature precipitate that has been detected in the binary alloy. Electron diffraction techniques were used to determine the structure of the precipitates that formed during the decomposition of the Ni-Nb supersaturated solid solutions. Figs. l(a) through l(d) show electron diffraction patterns oriented to the [loo], [110], [lll], and [I031 zone axes of the matrix. Areas of reciprocal space between these sections were investigated by slowly varying the orientations of the crystal under study; this procedure revealed no reflections other than those depicted in Fig. 1. The presence of super-lattice reflections at points coincident with the matrix reflections was confirmed by the examination of an almost completely transformed structure. On the basis of the accumulated diffraction data, the reciprocal lat-

Jan 1, 1970

By W. G. Woolf, A. Y. Bethune

THE hydrometallurgy of special high-grade zinc as practiced by the Sullivan Mining Co. at its electrolytic zinc plant, Kellogg, Idaho, involves an important filtration step immediately following the leaching process. By means of the filtration the heavy zinc sulphate solution is separated from the residual products which remain after the zinc calcine has been dissolved in the sulphuric acid electrolyte. Because this plant uses the so-called high-acid, high-density process' for the production of First, the strength of the electrolyte (270g H,SO, per liter) results in a saturated zinc sulphate solution, having a specific gravity of 1.510 to 1.540, which must be kept warm during filtration because of its property of "seeding out" small crystals if allowed to drop much below 60°C. Second, the action of the "high" acid on zinc calcine under the temperature conditions of the leach (80" to 102 "C), although favorable to good zinc extraction, causes a considerable quantity of iron to be dissolved (8 to 18. g per liter) along with variable quantities of alumina and silica, depending on the grade and type of original zinc concentrates roasted. These three, iron, alumina, and silica, are almost completely precipitated during the neutralization of the leach (only a few. milligrams per liter of each remain in solution), so that the resulting pulp, instead of being a granular, sand-like product having a particle-size distribution dependent on the fineness of the zinc calcines leached, is in reality a slimy, chemical precipitate whose filtration characteristics constantly change depending on the amounts of iron silica, and other impurities, which are dissolved and reprecipi-tated. Third, the combination of supersaturated solution of high specific gravity plus a dense, semi-gelatinous residue creates a difficult washing problem requiring a positive displacement wash to liberate the zinc sulphate entrapped in the pulp. In a closed-cycle hydrometallurgical operation, such as practiced in this plant, the extent of washing is determined by the volum,e limitations imposed on the intermediate wash waters by the amount of "fresh" (or process) water which may be added. The volume of fresh water used for makeup purposes is limited to the amount which is lost during the closed cycle by evaporation in the leach, sulphate content of the calcines leached, moisture content of the residue, and spillage. The Burt filter as modified and improved by the Sullivan Mining Co. has successfully met and overcome these difficulties under a variety of zinc plant operating conditions since 1928. It might have many interesting applications to metallurgical fields other than that of electrolytic zinc, and its possible usefulness to hydrometallurgists in general warrants its description and discussion. The Burt filter is so named from its inventor who originated it in Mexico for pulp filtration in the cyanide process for gold and silver ores. While retaining the basic principle of Burt's earlier revolving pressure-type filter with internal filtration media, a number of modifications and improvements have been made in Sullivan Mining Co.'s installation. The Burt filter may be classified as a batch-type pressure filter in contradistinction to either the conventional vacuum-type filter, which depends on atmospheric pressure to force solution through a cloth medium, or to the filter-press, which employs whatever pressure is imparted by the pump delivering the liquid being filtered. The Burt consists essentially of a hollow steel cylinder about 40 ft long, 5 ft in diameter, resting horizontally, and capable of rotation about its long axis. It is supported on one end by a hollow trunnion and near the other end by a riding-ring and roller combination. The cylinder is lined with filter units each fastened against the inside of the shell and parallel to the long axis so as to form a hollow cavity into which pulp may be charged. A specific amount of pulp is admitted to the filter and a unique valving arrangement prevents the loss of pulp while air pressure forces the solution through a canvas medium to the discharge port of each filter unit. The residue is left on the surface of the canvas inside the cavity. The remainder of the filter cycle is concerned with washing the residue free of zinc sulphate, discharging it from the Burt, and preparing the filter for the next charge. A more detailed description of Burt filter construction, a typical filter cycle, and its operating characteristics when employed on material encountered in this plant will be given in that order. Description of the Filter: Fig. 1 shows a side elevation view of a filter with riveted shell construction. Since this drawing was made shells have been fabricated by welding, instead of riveting, with complete success. Shells are lagged on the outside to retain heat. Fig. 1 shows a side elevation and plan view of a Burt filter in operating position. The 1/2-in. steel shells are lined with 3/16-in. copper sheet as protection against the corrosive action of the solution (containing about 500 mg Cu per liter) on iron, and the copper is given a thin protective coating of plastic-base paint. Fig. 2 is a view from the discharge end of the filter, with head removed, before filter units are fastened to the periphery. It shows

Jan 1, 1951

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

By A. Szirmae, Hsun Hu

The early stages of recrystallization in a 70 pct cold-rolled Si-Fe crystal of the (110) (0011) orientation were studied with a Siemens electron microscope. Orientation studies based on electron-diffractzotz. patterns confirm the results of previous texture analysis. The driving energy for recrystallizatior and the critical radius for growth were calculated from the dislocation energy and the energy of the subgrain bourzdaries, and it was found consistent with the observed size of the recrystallized grains. The recrystallization characteristics of crystals with different initial orientations are discussed. The recrystallization of cold-rolled (110)[001] crystals of Si-Fe has been widely studied by various investigators.1-4 Their results on both deformation and annealing textures are in good agreement. The rolling texture after 70 pct reduction consists mainly of two crystallographically equivalent (111) [112] type textures and a minor component of the (100) [011] type. The latter is derived from the deformation twins, or Neumann bands, which are formed during the early stages of deformation and later rotate to the (100) [011] orientation upon further rolling reduction. Between the two main (111) [112] type textures, there is some orientation spread, because of which very low intensity areas appear in the pole figure. If these very low intensity areas are considered to be a very weak component in the texture, then a (110) [ 001 ] orientation may be assigned to them. When this rolled crystal is annealed at a sufficiently high temperature for recrystallization, the texture returns to a simple (110) [001]. The purpose of the present investigation was primarily to seek a better understanding of the recrystallization process by using the electron transmission technique. The (110) [0011 type of crystal was selected because orientation data for it are well known from previous studies with conventional techniques. Direct observations on the recrystallization of such a crystal have also been made by using a hot-stage inside the electron microscope, and the results will be reported in another paper. MATERIAL AND METHOD A single-crystal strip of the (110) [001] orientation was prepared from a commercial grade 3 pct Si-Fe alloy by the strain-anneal technique.= The strip was approximately 0.014 in. thick, and was rolled 70 pct at room temperature to a thickness of 0.004 in. Specimens were cut from the rolled strip and were annealed in a purified hydrogen or argon atmosphere. They were then electrolytically polished in a chromic-acetic acid solution to very thin foils. Best results were found by polishing first between two narrowly spaced flat cathodes with the specimen edges coated with acid-resisting paint, followed by polishing between two pointed electrodes until a hole appeared in the center as described by Bollmann.6 It was found that a thin transparent film always formed along the thin edges of the polished specimen. This film was then removed by rinsing the specimen very briefly in a solution of alcohol with a few drops of HF or HCl. RESULTS AND DISCUSSION 1) The Deformed Crystal. From the electron-diffraction patterns taken at various areas of an as-rolled specimen, the texture components as deduced - from ordinary pole-figure analysis were confirmed. Over most of the areas where orientation was examined, a (111) pattern with a [112] direction parallel to the rolling direction was obtained. This corresponds to the main deformation texture of the (111) [112] type. In a few areas the diffraction pattern was (100) [Oil], corresponding to the minor-texture component derived from the Neumann bands. The (110) [001] orientation, which corresponds to the very weak intensity area in the pole figure, was found infrequently. A typical example of the deformed matrix having the (111) type main texture is shown in Fig. 1, where (a) is the microstructure and (b) is the diffraction pattern taken from that area. It was also frequently observed that in other areas more or less continuous rings of weaker intensity were superimposed on the simple (111) diffraction pattern, suggesting the presence of a wide range of additional orientations. Other evidence indicated that the recrystallization characteristics are different in these two different types of areas. The hot-stage observations which provide this evidence will be discussed in another paper. AS shown in Fig. l(a), numerous dislocation-free areas of very small size are embedded in the "clouds" of high-dislocation density. This indicates that the deformation of a single crystal, even after a rolling reduction of 70 pct, is far from uniform on a micro-

Jan 1, 1962

By Charles R. Wraith

The property of the Roan Antelope Copper Mines, Ltd., is situated at Luanshya, north central part of Northern Rhodesia, and is connected with the main line of the Rhodesia Railways, Ltd., by a 24-mile branch line from N'dola. Most of the material and supplies that are not available in Africa are shipped into the country via Beira, on the East Coast of Africa, a distance of 1473 miles from Luanshya and the nearest ocean port. The output of copper is shipped by rail to Beira and thence by boat to the market. Passenger travel is mostly via Cape Town, a distance of 2162 miles from Luanshya. Excellent passenger trains operate on regular schedules between Cape Town and Northern Rhodesia. Luanshya is 13" south of the equator at an elevation of 4000 ft. above sea level, and has a mild healthful climate. During the rainy season, from October to March, the rainfall averages 53 in. The area is profusely covered with vegetation. An ample supply of water for industrial and domestic purposes is available throughout the year. The more important supplies for smelting purposcs, such as wood, coal, limestone, silica, quartzite, and clay for "dolly" mud, are conveniently available. Excellent grades of coal, coke and firebrick are obtained from the Wankie Colliery Co., Ltd., Southern Rhodesia. The Wankie colliery has just completed the erection of equipment for the manufacture of silica brick. An ample supply of quartzite of good grade is available for this purpose. Silica brick is also obtained from the Belgian Congo and from India. Limestone is quarried from a large deposit a few miles from Bwana Mkubwa, which is 30 miles by rail from the smelter. An abundant supply of clay for " dolly " mud and for lining launders is available within a short distance of the smelter. Metallurgy Copper is contained in the ore as chalcocite, chalcopyrite and bornite. Chalcocite predominates in the eastern end of the orebody almost to the exclusion of other copper minerals. The amount of chalcocite decreases with a corresponding increase of chalcopyrite and bornite toward the western extension, where the latter predominate.

Jan 1, 1934

By B. C. Allen, W. D. Kingery

Surface tension and its temperature dependence have been determined for pure liquid Fe, Cu, Co, Ni, and Sn and for Fe-C, Co-C, and Ni-C alloys. The temperature coefficient of surface tension is negative for all these liquids. The surface tension and wetting behavior of tin and tin-titanium alloys on A120,, Si,N,, MoSi,, and Sic, as well as the behavior of titanium-containing nickel alloys on A1 20, have been determined over a wide temperature range. For all the solids investigated titanium additims markedly lower the contact angle. Some limits for the solid-surface energies have been calculated from liquid surface tension and wetting behavior. SURFACE tension and interface energy are important variables in a number of metallurgical and ceramic phenomena, and have been discussed at some length in connection with determining micro-structure of polyphase systems,' solid-state sintering,' thermal etching of grain boundaries, heats of solution and fine powders,'1 grain-growth phenomena,' the mechanical behavior of fine foils and fibers, nucleation, soldering and brazing,' and other phenomenz of academic or practical interest However, until recently few quantitative data have been available for high-temperature systems. Among available data are some indicating positive temperature coefficients for the surface tension of liquid copper,*,11,'2 cast iron,l3 and iron-carbon14 alloys. Although carbon was found to be not surface active in iron at 1570" some preliminary studies had indicated the possibility of a positive temperature coefficient for the eutectic composition at lower temperatures.16 One part of the present study has been largely concerned with determining the temperature coefficient of surface tension for several metals at elevated temperatures, In addition to surface-tension studies, the wetting behavior of alloys containing titanium has been investigated over a wide temperature range. Previous measurements indicated that titanium was selectively adsorbed from nickel at a liquid nickel-solid alumina interface,17 and the use of titanium hydride or titanium-alloy techniques for metal-ceramic soldering is well known. In the present study, previous data have been extended to new alloy systems, and measurements have been carried out with other oxidation-resistant ceramics. EXPERIMENTAL The sessile-drop method was employed to measure liquid surface tension and contact angle between liquid and solid, utilizing apparatus and techniques which have been described previously.'g The shape of a sessile drop depends on equilibrium between forces of surface tension tending to form a spherical surface of minimum area and forces of gravity tending to flatten the drop. Typical sessile drops are shown in Fig. 1. From precise measurements of maximum drop diameter and drop height the surface tension and drop volume were calculated. Four solid materials were employed as supporting plaques for the liquid-metal drops. Aluminum oxide (99.9 pct, J, T. Baker, reagent grade) was pressed and sintered at 1800°C. Molybdenum-disilicide powder (99.0 pct, Electro Metallurgical Co.) was pressed and sintered at 1650°C. Plaques were cut from silicon carbide (99.4 pct, hot-pressed at Alfred University) and silicon nitride (95.1 pct, with Al, Fe, 0 as major impurities, Norton Co.) rods. All plaques were polished, cleaned, and dried prior to use. A number of metals and alloys were employed. Chemical analyses of vacuum-melted ingots of iron, nickel, cobalt (National Research Corp.), commercial nickel-base alloys, electrolytic copper (International Smelting and Refining Co.), and tin (Mal-linckrodt Chemical Works) are given in Table I. Alloys were prepared in the laboratory by vacuum melting the base metal with either titanium hydride (Metal Hydrides, Xnc.) or spectroscopic-grade carbon (National Carbon Corp.). Nickel-titanium alloys contained between 0.001 and 0.005 pct oxygen and the ferromagnetic metal-carbon alloys contained 0.001 pct. Cylindrical metal specimens (1 to 2.5 g) were machined and bevelled at the bottom to insure a uniform advancing contact angle on melting. Before use the samples were acid-etched, cleaned with acetone, and rinsed in petrol ether.

Jan 1, 1960

By Emerson F. Heald

A systematic study was made of new and old data on chemical activities in Fe-Pt alloys at elevated ternperatuves. Experimental results may be expressed in terms of the excess free energy using Least-squares analysis of the data gave the following values for the constants: for the temperature range 1130° to 1350°C, and tentatively to 155O°C, B = -3.326564 and C = 0.221051; for the temperature range 650" to 850°C, B = -2.555690, C = 1.762735, and D =0.097196. In the study of iron-containing silicate systems, it is sometimes desirable to have a direct experimental measure of the activity of iron in the system. The well-known solubility of iron in platinum, often a headache in experimental work on iron compounds under reducing conditions, can be used to advantage in this respect. If the activity of iron in an Fe-Pt alloy in equilibrium with the silicate is known as a function of the composition of the alloy, chemical analysis of the alloy will give a knowledge of the activity of iron in all of the phases in the system. The present study was undertaken in order to elucidate the characteristics of Fe-Pt alloys as iron activity indicators. This work is intended to tie together some previous work, which may be summarized as follows. Larson and Chipman1 determined the activity of iron in Fe-Pt alloys at 1550°C by equilibrating platinum metal with calcium oxide-iron oxide-silica melts of known iron activity. Compositions of the resulting alloys were determined by chemical analysis. A similar study was carried out by Taylor and ~uan,' who worked at 1300°C. They brought the Fe-Pt alloys into equilibrium with iron oxide under conditions of known partial pressure of oxygen, and thus, from the work of Darken and ~urr~,~ conditions of known iron activity. Compositions were determined indirectly, by following the change in weight of the sample. Sundaresen et el* used the electromotive force of cells in which the alloy formed one electrode in order to measure the activity of iron in the alloy at 650" and 850°C. These temperatures were chosen to be above and below the first-order phase transition which takes place upon the ordering of Fe3Pt and the second-order transition which occurs upon the ordering of FePt3. EXPERIMENTAL 1) High Temperatures. The starting materials used were thin platinum foil, about 0.002 mm thick, and Fisher Certified reagent ferric oxide, Fez03, which had been heated for 24 hr at 1000°C. An intimate mixture of 80-mesh Fez03 and platinum platelets was placed in a thin platinum foil envelope. The latter was suspended from thin platinum wires in the hot zone of a vertical-tube, platinum-wound furnace of the type described by Muan and ~sborn.~ A capillary gas mixer similar to that used by Darken and Gurry3 was used to prepare a precisely known mixture of carbon dioxide and hydrogen, which was allowed to flow upward through the furnace tube. The partial pressure of oxygen in contact with the sample was thereby fixed at a value which was calculated from the charts prepared by porter? Temperatures were measured with a Pt-10 pct Rh-in-platinum thermocouple, which was calibrated using the melting points of gold (1062 .@C) and diopside, CaMgSizOB (1391.5"C). Temperature control was maintained to within i3"C with a Geophysical Laboratory proportional controller, using the furnace resistance as the sensing element. Samples were quenched by passing a small current through the platinum suspension wires, allowing the sample to drop into a bath of dibutyl phthalate at the bottom of the furnace tube. Prior to chemical analysis the samples were washed with acetone and dried. 2) Chemical Analysis. It proved possible, in almost all cases, to separate the Pt-Fe platelets physically from particles of iron oxide. The platelets were dissolved in a small volume of aqua regia, evaporated to dryness, and redissolved to 0.1 M HC1. In order to determine iron in the platinum alloy potentiometrically, it is necessary first to remove the platinum. A 10-cm column of Amberlite IR-120 cation exchange resin in the hydrogen form provided separation quickly and quantitatively: The mixture of iron and platinum in 0.1 M HC1 was added to the top of the column, and washed with about 100 ml of 0.1 M HC1. Under these conditions, the iron, principally in the form of cations such as FeC1" and FeCl;, is held quantitatively in the uppermost centimeter of the column. The platinum, in the form of anions such as PtC&- , is washed through without being adsorbed. After a qualitative test with stannous chloride indicated all of the platinum was removed, the iron was

Jan 1, 1968

By B. A. Cheadle, K. P. Steward

Axial tensile, ring tensile, closed end burst, and free end burst tests were done at room tempe.vature and 300°C on three batches of Zircaloy-2 sheathing zuith different textures. Knoop hardness tests were also done on all batches. The mechanical properties of the tubes were largely dependent on the percentages of cold work, but were also markedly affected by the textures, particularly with respect to deformation behavio'r. The deformation behavior observed confirmed Picklesimer's predictions, zuhereas Knoop hardness results could be correlated with texture and yield strength anisotropy after the ,method of Wheeler and Ireland. From the mechanical properties, and from efjectiue strain values deterrlzined at the fractures using a photoqid technique, it zuas concluded that tubing witlz a single preferred orientation of radial basal poles best combines strength and ductility for any given deqee of cold work. THE mechanical properties required in collapsible Zircaloy-2 fuel sheathing for water-cooled power reactors are strength to resist wrinkling deformation by coolant pressure and ductility to accommodate a small amount of deformation in service without rupturing. Zircaloy-2 tubing during fabrication develops pre- ferred orientations of the a Zr grains due to aniso-tropic deformation behavior, and these textures markedly affect mechanical properties. Picklesimer' had predicted the deformation behavior of tubes with various textures, but the texture required to provide the optimum strength and ductility for a given degree of cold work has not been reported. To investigate this problem, tests at three transverse to axial stress ratios were done at room temperature and 300°C on three batches of Zircaloy-2 tubing covering a wide range of textures and percentages of residual cold work. Knoop hardness values were also measured to correlate with preferred orientation and yield strength anisotropy after the method of Wheeler and relland.' 1) MATERIAL For this investigation, three batches of tube-reduced tubing were chosen from the Zircaloy-2 sheathing produced for the Douglas Point Reactor. Individual tubes were 191/2 in. long, 0.600 in. OD, and 0.0165 in. nominal wall thickness. The identities of the batches, together with their textures, are shown in Table I. The tubes had the normal Zircaloy-2 composition3 of 1.5 wt pct Sn, 0.3 wt pct Fe, Ni, Cr combined with the following oxygen concentrations: Batch VII 1140 to 1390 ppm 0 Batch VIII 1400 to 1750 ppm 0 Batch IX 880 to 1320 ppm 0

Jan 1, 1968

By F. W. Schremp, V. L. Johnson

This paper discusses the results obtained from high temperature, high pressure filter loss studies in which field samples of clay-water, emulsion, and oil base fluids were used. High temperature, high pressure tests of some premium priced emrilsion and oil base drilling fluids show filter loss peculiarities that are not predicted by standard API tests. It is recommended that high temperature, high pressure filter loss tests be used to evaluate the performance of such fluids. Apparatus is described which proved to be satisfactory for evaluating filter loss behavior over a wide range of temperatures and pressures. INTRODUCTION The petroleum industry spends large sums of money each year on chemical treating agents for lowering filter loss and on premium-priced low filter loss drilling fluids. While it is an accepted fact that low filter loss is advantageous during drilling operations, it is questionable whether the present standard method of determining filter loss gives a reliable indication of the loss to he expected under bottom hole conditions. The purpose of this paper is to show that high temperature. high pressure filter loss tests Should be used to evaluate filter loss behavior of fluids for deep drilling. Concern over possible effects of filter loss on oil well drilling and well productivity dates back to the early 1920's. During the years 1922 to 1924, filtration studies were reported by Knapp,' Anderson2 and Kirwan." These studies were the first to be reported in the literature on this subject. No further information was published on the subject until 1932 when Rubel' presented a paper in which he discussed the effect of drilling fluids on oil well productivity. In 1935. .Jones and Babson constructed the first laboratory tester designed to study the effects of temperature and pressure on the filter loss behavior of clay-water drilling fluids. In a discussion of their investigations, Jones and Babsons stated, "Performance characteristics of a mud can he evaluated with considerable reliability by a single test at 2,000 psi and 200°F. Exact correlation between the results of performance test5 made under these conditions and the behavior of muds in actual drilling operations is of course impossible." Jones arid Babson apparently were well aware that at best laboratory tests can give only qualitative answers to the question of what is the actual behavior of a drilling fluid when subjected to deep drilling conditions. Jones' presented a paper in 1937 in which he described a static filter loss tester to be used for routine filter loss tests. This instrument subsequently was adopted as the standard APl filter loss tester. In 1938, Larsen7 developed a relationship between filtrate volume and filtrate time that is in general acceptance today. Larsen was cognizant of the danger of estimating bottom hole behavior from filter loss measurements at room temperature. He tried to predict the effect of temperature on filter loss by relating temperature effects through the temperature dependence of filtrate viscosity. This was undoubtedly an over-sirriplification of the temperature dependence of drilling fluid filter loss. In 1940, Byck" published a summary of experimental results of filter loss tests made on six representative California clsy-water drilling fluids. He concluded that "no existing method will permit even an approximate determination of the filtration rate at high temperature from data at room temperature. It is necessary to measure filtration at the temperature actually anticipated in the well, or to make a sufficient number of tests at various lower temperatures so that a small extrapolation of these data to the anticipated well temperature may be applied." Byck's findings were presuma1)ly well accepted and recognized by drilling Fluid technologists, and yet, they did not lead to wide adoption of high temperature drilling fluid filtration equipment. This is evidenced by the fact that no addition information has appeared in print on the subject since 194). Study of Byck's data shows that there was a useful consistency in them. The fluids did not show predictable losses at high temperatures, but they did line up at high temperatures in approximately the same order that they lined up at low temperatures. That is, if a fluid appeared to be a good fluid with relatively low loss at low temperatures, it would also be a good fluid with relatively low loss at high temperatures. In the last decade. the above situation has changed. The drilling fluid art is markedly different from what it was. The outstanding change, as far as the present discussion is concerned, has been the adoption of wholly new types of drilling fluids. Oil base and emulsion drilling fluids have come in to wide use. It is, therefore, necessary- to re-examine previously satisfactory generalizations to see if they are still valid. It turns out. as might have been expected. that Byck's explicit generalization. already quoted, is still true. Filter losses at high temperatures cannot be predicted from filter losses at low temperatures. However, no further generalizations are valid now. Fluids of different chemical types show different general behaviors. No longer do the fluids line up approximately the same at high temperatures as they do at low temperatures. They may line up entirely differently. Special fluids exhibiting very low loss at low temperatures may have losses as high as those of ordinary clay-water fluids at high temperatures. This fact is highly significant, because premium prices are being paid for the special fluids.

Jan 1, 1952

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.' The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5'6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS' on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n', the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,' small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.'-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By H. E. Cline, J. L. Walter

Grain boundary sliding and migration were studied in pure aluminum bicrystal and polycrystal samples with two-dimensional grain structure. Scratches, 50 P apart, were used for measurement of sliding and migration distanceso. Samples were deformed at constant rate at 315C and events recorded continuously on wrotion picture film. Electron micrograPhs of boundary-scratch intersections were obtained. Yield and flow stress values were measured. The sequence of sliding and migration events for a three-grain junction is described in detail. Sliding depended only on the resolved shear stress imparted to the boundary. Sliding was accowmodated by formation of shear zones in grains opposite triple points and adjacent to curved boundaries. These shear zones provided the driving force for grain boundary migration. Migration caused rumpling of the boundaries, decreasing the sliding rate. Sliding and migration generally began at the same time, occurred simultaneously and ended at the same time. In the bicrystal, sliding and migration rates were proportional. Initial sliding rules of 5 X joe cm per sec. were measured for the polycrystal and bicrystal samples. These sliding rates agree wilh the internal friction experirnents of K;. The observations seem consistent with a viscous boundary sliding nzechanism. GRAIN boundary sliding is the translation of one grain relative to its neighbor by a shear motion along their common boundary. Sliding is thought to be an important mode of deformation at elevated temperatures and at low strain rates such as prevail in creep,' and perhaps in the area of superplastic behavior.2"4 Although much work has been done to investigate grain boundary sliding, the effort has not led to the identification of a mehanism. KG showed that grain boundaries in aluminum exhibit a viscous nature under very small displacements of internal friction measrements. Various dislocation mechanisms have been proposed but are without conclusive experimental support. Attempts to relate sliding to 6's viscous boundaries have been unsuccessful in that measured rates of sliding are always several orders of magnitude lower than KG'S results would predict.= In bi crystals7and polycrystalsR of aluminum tested under constant load, the grain boundary sliding was found to be proportional to the total creep elongation which indicated that sliding might be controlled by deformation of the grains. Shear zones were observed to extend beyond grain boundaries at triple points to accommodate the sliding.8 Surface observations brought forth the opinion that sliding and migration occurred alternately, in sequence.' Measurements of sliding at the surface have been criticized because they might not be representative of the interior of the sample. Generally speaking, it seemed that much of the previous work and knowledge was based on observations made at relatively low magnification and examination of samples after deformation had been accomplished. Thus, it was the purpose of the present study to continuously record, at high magnification, the events occurring during the deformation of pure aluminum. Samples with two-dimensional grain structures were used to simplify interpretation of the results. The sliding and migration of small areas of many samples were continuously recorded by time-lapse motion pictures. Replicas of the surface were used to provide high-resolution electron micrographs. These observations, coupled with tmsile strength data, provide sufficient information to arrive at an understanding of the phenomenon. EXPERIMENTAL PROCEDURE An ingot of 99.999 pct A1 was rolled to sheet, 0.127-cm thick. Tensile specimens, with a gage length of 0.85 cm, were machined from the sheet. Bicrystal tensile specimens, of the same dimensions, were spark cut from a large bicrystal ingot. The grain boundary was oriented at 45 deg to the tensile axis. The surfaces of the tensile samples were ground flat on fine metallographic paper and were then electropolished in a solution of 75 parts absolute alcohol and 25 parts of perchloric acid. The solution was cooled in an ice-water bath. Using a weighted sewing needle suspended from a small pivot on a precision milling machine, a grid of fine scratches, 50 p apart, was scribed on one surface of the sample. The polycrystalline samples were then annealed in hydrogen for 15 min at 350" to 400°C to produce a two-dimensional grain structure of about 0.2-cm average grain diameter which would not undergo further growth at the test temperature, 315OC. Examination of both surfaces of the samples showed that the grain boundaries were perpendicular to the surface of the polycrystal and bicrystal samples. A hot-stage tensile machine was constructed for use with an optical microscope as shown in Fig. 1. The specimen is shown mounted in the grips. The grips ride in V-ways so that the sample can be mounted without damage. The rear grip is free to slide so that when the sample expands during heating it is not put under a compressive stress. When the grips and samples are at temperature, the rear grip is locked in place by two set-screws. The other grip is connected to a synchronous drive motor which, through a worm gear and a fine-threaded rod, deforms the

Jan 1, 1969

By N. J. Grant, H. Brunner

This paber is concerned with the determination of equations relating elongation to the amount of shear taking place both along grain boundaries and in slip planes of poly crystalline aggregates during creep. Certain discrepancies with previously used equations are pointed out. Grain boundaries were observed to become serrated during creep, but it is shown that this does not necessarily prevent further grain boundary sliding. Direct obser-vations of subgrain boundary ingration lead to the conclusion that this migration facilitates sliding along serrated grain boundaries. It is bointed out that the state of stress at triple boints is still unknown. MOST of the mechanisms of deformation contributing to elongation are shear processes, such as slip, kinking, grain boundary sliding, and twinning. For quantitative investigations of individual deformation mechanism it is necessary to know the equation which permits the calculation of speci-tnen elongation from measured amounts of shear. This calculated elongation must then be compared with the observed total elongation. The authors' special interest concerned grain boundary sliding during creep. Although this subject has already been investigated quantitatively by McLean,' Rachinger,' and Fazan, Sherby, and Dorn, calculations indicated that none of the equations used thus far to relate shear with elongation were sufficiently well founded. A basic study of this relationship was thus made and the results of this study (which do not entirely agree with those previously used) are presented. Most of the ideas set forth apply not only to grain boundary sliding but to other mechanisms of shear as well. THE SPEAR-ELONGATION RELATIONSHIP Basic Models—The relationship between shear and elongation is trivial in the simplest case of shear, which is shown in Fig. l(a). The vector A; designates the displacement across the shear interface, and Au, and Aut are its components parallel and normal to the tensile direction, respectively. It is evident that the specimen elongation due to shear is equal to the longitudinal component of the shear vector, and it should be noted that the normal component does not contribute to the elongation of the specimen (there are, of course, two normal components in a three-dimensional model). The model shown in Fig. l(b) may be applied to mechanical twinning and to subgrain boundary tnigration. In this case the width (h) of an already existing shear band increases by the migration of an interface, but the shear angle y (angle of mis-orientation in the case of a subgrain boundary) remains constant. The geometrical relationships indicated in Fig. l(b) permit this case to be reduced to the one shown in Fig. l(a). For the resulting elongation A6 we find: where AV/V = fraction of the volume of the specimen swept by migrating interfaces , and 1 = length of specimen. Thus, assuming for example that the angle of mis-orientation is 1 deg, and that P = 45 deg, we find that the specimen elongates 0.87 pct of its length if the entire volume of the specimen is swept once by such a subgrain boundary. An example of deformation by migration of subgrain boundaries is shown in Fig. 2. The specimen shown was repolished after 9.8 pct creep strain and the test then continued for another \ pct. Since the shear vector has, in general, a component normal to the surface, subgrain boundary migration results in the formation of an inclined band delineating the region swept by the subgrain boundary. These inclined bands become clearly visible when observed with oblique illumina-

Jan 1, 1960

By O. J. Hassel, W. T. Maidens, J. H. Calbeck

The rotary gas fired reheating furnace used by the American Zinc Oxide Co. at Columbus, Ohio for Therotarygasfiredreheatingfurnacerefining lead-free zinc oxide is described. The outstanding features of this operation are that the color of the zinc oxide is greatly improved, sulphur is eliminated, and cadmium arethatrecovered without densifying the product to an objectionable degree. IN 1919 Leland S. Wemple obtained a patent for a process of reheating zinc oxide wherein the "coarsening of grain due to excessive heating was avoided." He taught in his specification that if solid carbonaceous material, such as lamp black, was added to the zinc oxide in proper amounts prior to reheating, objectionable sulphur compounds could be removed and the color would accordingly be improved and no objectionable densification would occur because of the relatively low temperature required. The situation that made this invention imperative was the newly opened zinc oxide plant of the American Zinc, Lead & Smelting Co. in Hills-boro, Ill. This was one of the early Western Type American Process zinc oxide operations. Characteristic of all of these early Western operations using Tri-State and Western ores was the great difficulty encountered in obtaining a product low enough in sulphur to compete with the Eastern Type American Process zinc oxides which were made from ores containing very low sulphur percentages. Wemple demonstrated that the refining process of his invention produced a superior color and although this was true and a most welcome feature, the primary purpose of the early refining operations at Hillsboro was to reduce substantially the high sulphur content of the crude zinc oxide. Although many and varied attempts had been made for refining zinc oxide none of the processes had a commercial history of any consequence until Wemple's invention became standard practice for the American Zinc, Lead & Smelting Co. in 1919 and their operations have been unique in that substantially all of their lead-free zinc oxide has been reheated since the first installation at Hillsboro. This process has become known in the industry as refining. The furnace developed by Wemple and continued in use by the company from 1919 until 1943 was unusual and merits some consideration by way of review in this paper. The furnace was essentially a double hearth coal-fired muffle furnace with a mechanical raking system consisting of a central shaft supporting six rabble arms in each muffle. The untreated or "crude" zinc oxide was fed onto the outer rim of the top muffle, moved to the center where it dropped to the lower muffle and progressed to the outer rim where it was discharged into an alloy screw conveyor. The retention in this furnace was extremely short, about 5 min, and the shallow zinc oxide bed on the hearths of the muffles was being continuously turned by the fast moving rabbles. Soft coal was burned on the grates below the lower muffle and the long yellow flame necessary to carry the heat around both muffles resulted in a very inefficient combustion of the fuel. The temperature of the top of the lower muffle seldom exceeded 65 °C although the oxide itself often reached 700°C before discharge. The capacity of this furnace was approximately 1/2 ton per hr. In our plant at Columbus it was necessary to keep four of these furnaces running in parallel to take care of the production because, as mentioned above, every pound of zinc oxide produced during these 24 yr passed through one of these refining furnaces. An essential part of this refining operation was the use of carbonaceous material admixed with the zinc oxide fed to the furnaces. Between 1 and 2 pct of a bran produced in the processing of cotton seed was added to all zinc oxide charged to the furnaces. The bran ignited on the top hearth and was still burning when the charge fell from the top hearth to the bottom hearth making a cascade of sparks. The rapid turning of the zinc oxide caused these particles of bran to flash on the hearths behind each rabble; but the combustion, of necessity, had to be complete by the time the charge reached the outer rim of the bottom hearth, otherwise the finished product would be contaminated with the charred particles of bran which would give the zinc oxide an unsatisfactory color. Although this operation was initiated to reduce objectionable sulphur percentages, as time went on new properties of the product were appreciated which made advisable continuing the refining process long after other methods of sulphur reduction became known in the industry. The particle size and particle size distribution, the absence of colloidal fines and perhaps a unique surface condition gave this product an outstanding performance when used in paints. The Wemple furnaces installed in Columbus in 1919 had to be rebuilt frequently and were extravagant in the use of fuel. The raking mechanism and the muffles required excessive maintenance expense and as the furnaces wore out the problem arose whether to continue along this line or to explore the possibilities of obtaining similar or better results in the simpler and more commonly used rotary furnace. To this end special research was initiated in 1941 on a small laboratory rotary

Jan 1, 1951

By T. E. Leontis, F. N. Rhines

THE oxide scale that forms upon magnesium at elevated temperatures is nonprotective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth1 and has been verified by Suzuki2 and by Scheil.3 Pilling and Bedworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki,2 the product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavault5 observed that excrescences form upon liquid magnesium and alloys in the course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium7and calcium8 minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.9 Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Scheil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. EXPERIMENTAL PROCEDURE AND RESULTS The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the

Jan 1, 1946

By Robert Maes, Robert de Strycker

The Fe-Ni-As phase diagram has been established by the study of about a hundred alloys, by microscopic observation, and by thermal analysis, with arsenic contents up to 50 pct. The iron and nickel arsenides present extensive solid-solution fields, owing to the substitution of nickel by iron and vice versa; the extent of the solubility field of each compound has been determined with an accuracy of ±1 pct. In the investigated range of compositions, the solidification reactions were established, and the temperatures of the invariant reaclions detevmined with a preciston of iZ°C in the most favorable and ±5°C in the least favorable cases. The isothermal lines of the liquidus surface have also been drazum, with an accuracy estimated at i5°C. Reactions in the solid state, which take place for the formation or the decomposition of certain phases , were investigated in detail. ThE constitution diagram of the Fe-Ni-As system is fundamental for the understanding of the properties of nickel speiss; these by-products of the extraction of certain nonferrous metals indeed often contain the three elements iron, nickel, and arsenic as main constituents. The Fe-Ni-As system has already been the object of earlier investigations. In 1932, Guertler and Savels-berg' have presented some elements of the ternary phase diagram, for arsenic contents up to 55 pct (all percentages in this paper are given in weight percent), including the vertical section FezAs-Ni&s2. This investigation is, however, incomplete and certain anomalies suggested the necessity to verify the results published by these authors: the section Fe2As-Ni5AsZ, for example, is presented as quasi-binary, with a field of complete miscibility in the solid state, even though these compounds do not have the same structure. Recently, ~useck' established an isothermal section at 800°C in the Fe-Ni-As system by X-ray diffraction and microscopic examination of water-quenched alloys. These techniques are sometimes inaccurate for the determination of the fields where alloys are liquid at the investigated temperature, and they may lead to erroneous conclusions when a compound exists at the investigated temperature but is not stable at room temperature and cannot be maintained by quenching. LIMITING BINARY PHASE DIAGRAMS The Fe-As constitution diagram has been the object of several investigations which have been reviewed by Hansen and Anderko.3 For the Ni-As phase diagram, a recent study has been effected by Yund.4 In this system, Heyding and calvert5 have determined the existence of a compound of unidentified structure at arsenic contents slightly higher than those corresponding to Ni5As2 and at temperatures lower than about 200°C; by analogy with iron and cobalt arsenides, this compound could correspond to the formula Ni2As, as suggested by Kulle-rud; although this is not definitely established. In the region of arsenic contents from 35 to 55 pct, Fried-rich7 detected anomalies in the solidification reactions; an interpretation of these anomalies was given by Hansen ,8 which assumed that the solidification reactions in practice are not in equilibrium, but are meta-stable. The main features of the Fe-Ni constitution diagram are the existence of a complete miscibility field, at least at high temperatures, for the fcc phase (which will be designated by My in the remainder of this work) and of a limited solubility field for the bcc phase (designated by Ma). EXPERIMENTAL METHODS The fundamental technique used in this investigation was microscopic observation, which allowed the determination of the reactions occurring during solidification of the alloys, and possible reactions in the solid state.

Jan 1, 1968