By P. W. Rainier

The Chivor emerald field is situated on the eastern slope of the Andes in the Department of Boyach, at an elevation of about 8000 ft. above sea level. It overlooks the Llanos (plains) of the Orinoco and is watered by many streams flowing into the Rio Meta, the Orinoco's largest tributary. The Rio Meta is navigable from the Orinoco to a point within about 50 miles of the Chivor district and may eventually prove to be the reasonable outlet for the future development of this part of the country. The topography of the district is extremely rugged and mountainous (Fig. I), the difference in elevation between two points on a mining claim 1 km. square being sometimes as much as 4000 ft. The ground is covered with dense forest growth and the available timber is suitable and sufficient for mining purposes, but it is becoming gradually depleted by Indian clearings as the country around the mines becomes settled. The many streams combined with the rough topography give good possibilities for hydroelectric power. The center of population nearest to Chivor is Bogoth, the capital of the republic and a city of some 300,000 inhabitants; the distance is two and one-half days' travel. The first stage of the journey from BogotB is accomplished by rail to Choconta, some 4 hr. travel. From Choconth the journey is made in the saddle, one night being spent in Guateque. The latter is a small town and the nearest post office to the mines, being some 10 hr. ride distant. The roads are mere bridle paths, in parts hazardous and almost impassable in the wet season. All supplies brought to the mines, other than those produced locally, are carried by pack mule; mule freight from Choconth costs 3 centavos1 per pound. The climate of the Chivor district is healthful and bracing. The wet season begins in March and concludes in November, the remaining months being dry. The annual precipitation is about 130 in. The temperature throughout the year is nearly constant, varying from about 45" F. to about 65" F. shade temperature. The rains are cold and unpleasant, and for the greater part of each day in the wet season the country is shrouded in dense mist. A fire can with comfort be kept burning in a living room all the year round. There are a few slight

Jan 1, 1931

By Matti J. Saarivirta

The relative machinabilities of the precipitation-hardenable Cu-0.9 pct Cr, Cu-0.25 pct Zr, and Cu-0.9 pct Cr-0.25 pct Zr alloys are improved from 18 to 80 pct by 0.75 to 1.25 pct Pb. The Lead also improves the tensile strength, hardness, ad resistance to softening of the Cu-Cr and Cu-Cr-Zr alloys. When the alloy containing 0.7 to 2.2 pct Cr, 0.10 to 0.25 pct Zr, 0.75 to 1.25 pct Pb, and balance copper is solution-annealed at 1000°C (1830°F) and then aged at 525°C (Y75°F), tensile strength of 65,000 psi, 16 pct elongation, 62Rb hardness, and 84 to 87pct IACS electrical conductivity are obtained. The copper base Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys have high electrical and thermal conductivities, high strength and resistance to softening at elevated temperatures, but their machinability is poor, i.e., close to that of the pure copper. In the manufacture of various components such as welding electrodes or electrical and thermal conductors it is ofter desirable that the alloy have good machinability for high production rates and long tool life. Thus, alloys that combine these properties may be used not only for existing applications, but for new ones where good machinability is a requirement. This investigation was undertaken to improve machinability without impairing other desirable characteristics of the Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys. These commercial alloys contain about 0.4 to 1.2 pct Cr, 0.10 to 0.25 pct Zr, and balance copper. Lead was selected as an element that should improve the machinability and possibly other characteristics of the alloy. WORK PROCEDURE This investigation began with a study of the effect of lead on the hardness, tensile strength, electrical conductivity, and machinability of the binary alloy containing 0.10 to 1.30 pct Cr and balance copper. This was followed by an investigation of the effect of lead on the Cu-0.1 to 0.4 pct Zr and Cu-Cr-Zr alloys. The alloys were made from initially oxygen-free copper and for comparison some castings were made from phosphorus-deoxidized Lake Copper. Commercially pure chromium, zirconium, and lead were used for alloying. In melting the chromium was added to molten copper at 1400°C (2550°F), the heat held for 15 min at temperature, and the temperature then lowered to 1350°C (2460°F) when the other elements were added. The alloys were held for 15 min at this temperature and cast into a cast-iron mold. One-kilogram, 3-in.-diam castings were made. An argon cover was maintained during melting and casting to prevent oxidation. The chemical compositions of the alloys are shown in Table I. The micro structure and properties of the alloys were studied in the cast and wrought conditions prior to and after various solution-annealing and heat-treating cycles. The relative machinability was determined as a function of the lead content and compared with the free-machining Cu-lpct Pb alloy. To determine the machinability, 13/16-in.-diam cast specimens were cut by a machine hack saw using a constant cutting speed of 50 fpm, a fixed feed force, and a new blade for each alloy specimen. Molybdenum highspeed steel saw blades, 0.032 in. thick with 14 teeth per in., were used in all tests. No cutting fluid was used. Five tests were made on each specimen and the average elapsed time per test was taken as a measure of the relative machinability for that alloy. The variation of cutting time for each alloy was less than 110 pct.

Jan 1, 1969

In response to Dr. Ledoux's paper, a large number of metallurgical establishments and individual assayers expressed their willingness to co-operate in the plan he proposed. The necessary samples were prepared as follows : Matte.—A car-load of matte was put through a Blake crusher, then automatically subdivided into tenths by a Taylor and Brunton sampler, and one-tenth passed through Cornish rolls and through a 12-mesh screen. This was again subdivided by an automatic sampler into tenths, and a final tenth, representing 1 per cent. of the original lot, was finished by hand-sampling on an iron floor until 100 pounds remained. This was pulverized to pass a 40-mesh screen and then thoroughly mixed and divided in the presence of my assistant for distribution to the parties co-operating. Copper Borings.—These were taken from a lot of anodes, the dip-samples from several batches having been united, remelted and cast into a plate, which was proved by assay to be of uniform quality in its different parts. Borings from this plate were intimately mixed and divided in the presence of my assistant. Samples were sent out November 1,1894, with the following letter: New York City, November 1, 1894. Samples of matte and copper (about I pound each) carefully prepared in the presence of my assistant and sealed with his seal as below, are sent you by express for assay and report according to the plan of Dr. Ledoux. These samples are constituted about as follows: Matte. Copper. From. To. From. To. Copper, per cent.,.....50 60 ..........., Gold, oz. per ton,.....2 3 0.20 0.50 Silver, oz. per ton,.....100 150 140 180

Jan 1, 1896

By S. P. Kinney, A. J. Boynton

THIS paper is not the result of recent research with regard to any particular feature of iron metallurgy, blast-furnace practice or mechanical engineering. It is rather a series of notes with regard to contemporaneous progress in blast-furnace construction and operation, together with some suggestions as to changes and improvements that seem to be desirable. On April 1, 1930, a committee of the Chicago District Blast Furnace and Coke Association presented to that association a rather ambitious study of blast-furnace equipment, together with recommendations for the design of construction of a complete blast-furnace unit for the production of 1000 tons of pig iron per day. This report represented the result of months of study by members of the committee, all of whom were actively engaged in operation or design of blast-furnace plants. It is natural, therefore, that comments on the present state of the art should take this 1000-tons furnace, as recommended by the Association, as a basis for comparison with corresponding features of construction or design. See Table 1. In looking through this report at the present time, the significant difference is in the nature of the gas-washing equipment that today would be specified. In other respects, the installation would remain generally very much as it was outlined in 1930. The change in furnace dimensions would be very slight and of no especial significance, except with respect to changes in stock-line diameter, of which more will be said hereafter. The high-efficiency stove as developed by various designers is thoroughly described within this report, and few changes have taken place since. Blowing equipment shows refinement and reflects the improvement in steam engineering. Hoisting and charging equipment and ladles for the conveyance of iron and slag remain, in general, as they were in 1930. In accordance with a general tendency

Jan 1, 1935

By B. K. Miller, R. S. Bradley

THE principal producing areas of fire clay in Missouri are: (I) the east central district, which includes Audrain, Callaway, Montgomery, Warren, and Boone Counties [ ] (Fig. I); (2) the St. Louis district, which includes St. Louis and St. Louis County; (3) the north central Ozark district, which includes Franklin, Gasconade, Osage, Maries, Phelps, and Crawford Counties. [ ] Most of the semiplastict fire clay is found in Audrain, Callaway, Montgomery and St. Louis Counties, and in St. Louis. Flint fire clay is found in Callaway, Audrain, and Montgomery Counties and in most of the north central Ozark district. High-alumina [ ] diaspore clay is found only in the north central Ozark district, except a few deposits found in Montgomery County. This paper is concerned with the semiplastic fire clay that occurs in the east central Missouri district near Mexico, Audrain County, Missouri, which is mined by the open-pit method as practiced by the A. P. Green Fire Brick Co. About one-fourth of the semiplastic fire clay in that district is mined in shaft mines, and three-fourths in open pits.

Jan 1, 1941

By Margaret Dienes, Karl L. Fetters

IT is recognized that ingot structure is important in determining the quality of finished steel. Such elements of ingot structure as the size, shape and distribution of primary crystals; the size, shape and distribution of shrinkage cavities; the degree and kind of segregation (both macro and micro); the distribution of nonmetallic impurities and gas cavities are each the result of solidification phenomena. These structural features vary with variations in ingot practice: Their control requires a knowledge of their correlation with the variables of ingot practice. The structures of full-sized commercial steel ingots have been studied extensively by the Steel Ingots Committee of the Iron and Steel Institute.1 This work has contributed much to our knowledge of ingot structure and the factors that control it. These investigations of necessity have been limited in scope because of their costliness and the great amount of time required. Studies of the structure of small steel ingots have not been very satisfactory because of the rapid rate of freezing of the ingots. Their structures are thus difficult to resolve and to interpret. Medium sizes of steel ingots in the ranges of 150 to 500 lb. do offer opportunity for study, but their cost also becomes greater and their use less expeditious. Experimental models for the study of steel-ingot structure have been made of nonferrous metals. Gathmann2 used lead-tin alloys and reported that they were satisfactory for determination of the location of the major shrinkage cavities and the "planes of weakness" resulting from the pattern of crystallization. Certain features of mold design have been illustrated by these results. Bezdenezhnihk3 has used copper and aluminum ingots similarly and has shown the effect of mold-wall thickness on the depth of columnar grains. These studies of nonferrous models have been useful, but their results have been limited because the analogy with steel ingots obviously is not a close one. Model wax ingots have also been useful in pointing out important features of mold design. Gathmann4 watched the solidification of wax ingots, through a glass-walled mold, and has reported the effects of mold type on the location of the shrinkage cavities. Segregation was simulated by using a mixture of paraffin and stearine and adding a red dye that on freezing segregated preferentially to the stearine. Brearley5 also used wax models to determine .the effects of some of the principal features of mold design. Carlsson and Hultgren6 used stearic acid to show that the columnar crystals of ingots tend to slope upward progressively from the mold wall toward the center of the ingot. As with the nonferrous ingots, the wax ingots have

Jan 1, 1943

By Robert E. Green, Kenneth Reifsnider

A microscopic X-ray diffraction technique was employed for the simultaneous study of the behavior of several families of lattice planes, whose local orientatiotz changes are manufestations of internal distortions resulting from specimen deformation. Photographs taken using aluminum were single crystals 1/64 in. In diam are presented which illustrate the appearance of various types of deformation- or growth- induced structural variations. Slip and lattice bending were detected in tensile tests for strains as small as 0.1 pct. Evidence of deformation bands, lineage structure, and void formation wns also shown. AmONG the most important methods of studying internal stresses in metals is the utilization of various X-ray techniques. The general subject of X-ray metallography has been treated in a most excellent manner by Taylor,1 and the use of X-rays for the direct observation of imperfections in crystals has recently been reviewed in an article by Newkirk2 and in the book edited by Newkirk and Wernick.3 Since the inception of metallographic X-ray analysis, there have been numerous technological developments and refinements, each with its particular advantages and disadvantages and, acrording to these, its particular applications. X-ray diffraction techniques can be divided into two general categories, that of X-ray diffraction microscopy and that of X-ray diffraction macroscopy. In the former are included such methods as those of Berg-Barrett, Lang, and Schultz2,3 which are concerned with microscopic imperfections such as dislocations. The second category includes all work concerned with the study of the condition of a crystal lattice structure as indicated by the marroscopic detail in its diffraction patterns. An example of this is the study of the diffraction manifestations of inhomogeneous plastic deformation as manifested by formation of deformation bands and inhomogeneous lattice rotations. The method used in the present investigation was an X-ray diffraction macroscopy technique. The geometry and analytical aspects of the method were similar to those of Julien and Cullity.4,5 The source was collimated with a single slit in a manner simi- lar to the "parallel beam'' method of Barth and Hosemann6 except that a continuous spectrum of radiation was employed. The apparatus produced large-beam transmission Laue patterns of thin cylindrical aluminum-wire crystals, which were deformed either in tension or torsion. Although the conventional X-ray target and interposed slit were not capable of the high resolution obtainable with a fine-focus X-ray source as employed in a microfocus apparatus, resolution was a secondary consideration in our technique, and was sacrificed to obtain sufficient intensity along a sizable length of the specimen. By using a grid indexing technique similar to that of Barth,7 we were able to study several diffraction lines from various planes simultaneously. The results of these tests give additional information with regard to the inhomogeneous deformation of single crystals, and the indexing procedure used provides a correlation between portions of the test specimen and portions of a diffracted beam. EXPERIMENTAL TECHNIQUE The experimental arrangement used is shown schematically in Fig. 1. A source of continuous X radiation from a vertically mounted Machlett X-ray tube possessing a copper target and operated at 20 kv and 10 ma was passed down a horizontal lead tube 80 cm long which terminated in an adjustable vertical brass slit. The slit opening was adjusted to correspond with the diameter of the test specimen. In front of the brass slit it was possible to place a screen wire mesh, one horizontal strand of which was a lead wire which served as a fiduciary mark, the screen itself serving as an indexing system as will be described later. Behind the screen was the test specimen which consisted of an aluminum single crystal wire 1/64 in. in diameter and 3 in. long. These 3-in.-long crystals were cut from

Jan 1, 1965

By Arthur Knapp

No oil territory in the world has been so rich in large producing wells, in a comparatively small area, as the Baku field. Particularly is this true of the Bibi Eibat field, which formerly produced millions of "poods," of " gusher," or as it is called in Russia, " fountain " oil. The Bibi Eibat and Balachany fields have been exhausted of gas and ruined by water, but the Surachany and Benegadi fields are still fountain territories and many outlying districts that have only been prospected produce rich fountains. The method of controlling fountains, or gushers, is the result of growth, along with the Russian system of drilling, where large diameters and riveted casing have been in vogue. The screw casing is seldom used except to exclude water. Formerly the method of finishing wells and the condition of the casing at the top of the well would not permit the use of gates, manifolds, and connections as is standard elsewhere. The life of the flowing wells is very short, particularly those 10 in. (25 cm.) or more in diameter, which produce large quantities of sand and often flow for but a few days and are then a complete loss. More than 1,000,000 poods in 24 hr. have been claimed in several instances, but in no case was the flow for more than a few days. The oil sands of this district are free uncemented sands and vary in thickness from paper thin to a maximum of 10 ft. (3 m.). The sands are interlaid with strata of soft clay. In spite of this, the practice has been to drill into such sands and produce from the open hole without screen or liners. Sometimes the casing is set below the oil sand but in this case holes from 2 ½ to 3 in. in diameter are drilled opposite the oil sand, which would not have the effect of a screen.

Jan 1, 1920

By G. R. Speich

A cellular precipitation reaction in which cells consisting of an Ni3Ti (DO24) phase and austenite are formed has been studied in an austenitic Fe-30 Ni-6 Ti alloy. The variation of the growth rate and interlamellar spacing of the Ni3Ti cells with temperature has been determined m the range 400" to 975°C; the interlamellar spacing is proportional to the degree of undercooling; the growth rate can be expressed by an equation of the form G = K?T)2 exp(-Q/RT). The habit of the Ni3Ti lamellae is (001)Ni3Ti (111)y;[010]Ni3T2 [010]y. An almost perfectly coherent interface is formed between Ni3Ti lamellae with this orientation rela -tionship and the intervening austenite. This first Ni3Ti cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. CELLULAR precipitation reactions have been studied in copper-base,1,2 Au-Ni,3 pb-sn,4 and iron-base ferritic5,6 solid solutions, and this mode of precipitation has been treated theoretically by smith," Turnbull,8,9 cahn,10 and more recently by bohm.11 In the case of substitutional austenitic iron-base alloys little or no data are available, Cellular precipitation reactions are well known in austenitic nickel-base alloys12,13 but usually these reactions do not proceed to completion because of general precipitation occurring in the matrix, and they have not been studied in detail. Precipitation from an austenitic Fe-30 Ni-6 Ti alloy was studied as part of a larger investigation of the mechanisms of precipitation from substitutional iron-base alloys. This alloy, austenitic at high temperatures, decomposes at lower temperatures by a double cellular precipitation reaction. The first decomposition product consists of alternate lamellae of an Ni3Ti(DO24) phase and austenite. The reaction proceeds to completion, consuming all of the original austenite. This first cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. The first cellular reaction was studied in detail by light and electron microscopy, hardness measurements, and by X-ray and electron diffraction. Interlamellar spacings and growth rates were measured during isothermal aging in the range 400" to 975°C. The orientation relationship between the Ni3Ti and austenite lamellae was determined and indicates that an almost perfectly coherent interface exists between the two phases. This first Ni3Ti cellular reaction is of particular interest because it occurs over such a wide temperature interval. This allows cellular growth rates and interlamellar spacing data to be obtained for much larger degrees of undercooling than reported hitherto. MATERIALS AND EXPERIMENTAL PROCEDURE The Fe-30 Ni-6 Ti alloy was prepared from electrolytic iron, Mond nickel shot, and sponge-purity titanium* by vacuum melting in a zirconia crucible

Jan 1, 1963

By E. Gregory, A. Coucoulas

Carbm dioxide, which exists metastably as a constantly subliming molecular solid in a normal room-temperature environment, has been shown to exhibit many microstructural features which are similar to those observed in metals and ceramics at temperatures approaching their melting points. An examinution has been made of some of the factors affecting a brittleness condition known as "smzdiness" which occurs in solid carbon dioxide. It has been shown to be highly dependent on manufacturing and storage conditions and is thought to be a marked intergranu-lay brittleness which results from a combination of excessive grain growth and a concentration of gas-filled pores at the grain boundaries. In the course of an investigation carried out to explain certain physical and mechanical properties of solid carbon dioxide, observations were made of the microstructure and fragmentation of samples after fabrication and storage under varying conditions. Many similarities between the structures of solid carbon dioxide observed under ambient conditions and those existing in metal and ceramic systems at temperatures approaching their melting points have been observed. There are, however, important differences between solid carbon dioxide and the common metallic and ionic solids which result primarily from the differences in the nature of the bonding forces. Despite these differences, the relative ease with which certain microscopic observations can be carried out, may make solid carbon dioxide a useful material model for the physical metallurgist and the ceramist. It could also prove a valuable material for educational purposes where it is required to illustrate grain phenomena which normally can only be seen with the aid of a high-temperature microscope, and after prolonged chemical or thermal etching.

Jan 1, 1963

By E. T. Turkdogan, P. Grieveson

Molten silver is equilibrated with silicon nitride at 1400°C in nitrogen + hydrogen gas mixtures, and from the solubility data the activity coefficient of silicon is found to be 1.76 at silicon concentrations below 1 pct. Using this value, and that available from the silicon cmbide solubility measurements, together with those derived from the phase equilibrium diagvam, the activities of silver and silicon are estimated for the entire composition range. The main feature of the activity data is that there is a pronounced positive deviation from ideality. The activity of silver in molten silver containing up to 5 pct Si was determined by Schadel, Derge, and Birchenall1 by measuring the vapor pressure of pure silver and of the alloy over a temperature range of 850º to 1050°C. They deduced from their results that there is a positive deviation from Raoult's law and that the activity coefficient of silver increases with decreasing temperature. However, as pointed out by Kubaschewski and Catterall,2 their activity coefficients are much too high, giving silver activities greater than unity. At a later date McCabe and Birchenal13 showed that the previous vapor pressure data on silver4 were high by a factor of about 1.3; presumably a similar error must have occurred with the vapor pressure measurements on the Ag-Si alloys. The activities of silicon and silver calculated by tager' from the phase diagram and by Gibbs-Duhem integration, respectively, show a positive deviation from Raoult's law for silicon activity and positive and negative deviations for the silver activity. According to these computations, at infinite dilution of silicon ygi = 1.12 at 1420°C. d'Entremont and chipman6 measured the solubility of silicon carbide in molten silver at unit carbon activity; the equilibrium silicon content is found to be Nsi = 0.017 ± 0.002 atom fraction for 1420°C. Using the data of Grieveson and Alcock7 for the free energy of formation of silicon carbide from pure silicon and graphite, the activity of silicon for unit activity of carbon and of silicon carbide is asi = 0.0308 at 1420°c; therefore for the above solubility data on silver, YSi = 1.81, which is somewhat higher than that given by Hager. Use is often made of silver alloys in the measurements of activities of solutes in metals where silver has a very low solubility; in fact, Ag-Si and Ag-A1 alloys have been used in the past for such purposes. In an attempt to gain more thermodynamic data on molten Ag-Si alloys, measurements have been made in the present study on the solubility of silicon nitride in molten silver; the results on these solubilities are given in this paper together with a detailed discussion of activities of silver and silicon. SOLUBILITY OF SILICON NITRIDE The standard free energy of formation of silicon nitride is known with a reasonably high degree of accuracy. According to the measurements made by Hincke and Brantle8 and by Pehlke and Elliott,' the following are the free energy data for the standard states of solid Si3N4, liquid silicon, and Nz at 1 atm pressure:

Jan 1, 1963

By H. D. Kessler, R. J. Van Thyne

Phase diagrams of the titanium-rich portion of the ternary systems from 0 to 10 wt pct Al and 0 to 1 wt pct 0, N, and C were determined. Micrographic analysis of annealed high purity arc melted alloys was the principal method of investigation and was supplemented by X-ray diffraction. TITANIUM-ALUMINUM alloys exhibit excellent properties, particularly for elevated temperature use. For this reason, the Materials Laboratory, Wright Air Development Center, sponsored an investigation of the effect of the interstitially soluble contaminants, oxygen! nitrogen, and carbon, on the Ti-A1 system. Using high purity arc melted alloys and micrographic analysis of annealed samples as the chief method of investigation, titanium-rich partial phase diagrams were determined for the ternary systems. Experimental Procedure Materials: The titanium used in the preparation of the alloys was iodide crystal bar (99.9+ pct pure) produced by the New Jersey Zinc Co. and Foote Mineral Co. The aluminum was obtained from the Aluminum Co. of America in the form of sheet. The given analysis was: Si, 0.0006 pct; Fe, 0.0005; Cu, 0.0022; Mg, 0.0003; Ca, <0.0006; Na, <0.0005; and Al, 99.99. High purity titanium dioxide purchased from the National Lead Co. was used in the preparation of the oxygen-bearing alloys. The spectrographic analysis of this material was as follows: SiO,, 0.07 pct; Fe,O,,, 0.002; A1,0,, <0.001; Sb,O,, <0.002; SnO,,, <0.001; Mg, <::0.001; Cb, <0.01; Cu, 0.0004; Pb, 0.002; Mn, <0.00005; W, <0.01; V, <0.002; Cr, <0.002; Ni, <0.001; and Mo, <0.002. Special spectroscopic graphite rod purchased from the National Carbon Co. was used in the preparation of the Ti-A1-C alloys. Alloy Preparation: Alloy ingots weighing 10 grams were melted in a nonconsumable tungsten electrode arc melting furnace using water-cooled copper hearths and a helium atmosphere. The arc was struck on a tungsten stud in the copper block to minimize contamination from the electrode. Details of the techniques have been reported.&apos;, &apos; Each ingot was inverted and remelted a minimum of four times to insure homogeneity, without opening the furnace. Remelting small control ingots of iodide titanium under similar conditions resulted in no measurable hardness increase, indicating contamination-free melting conditions were used. The alloy charges and resultant ingots were weighed to the nearest milligram. Only small weight losses were obtained upon melting, indicating that the actual compositions were very close to the nominal compositions. Check analyses substantiated this. Oxygen and nitrogen were added during ingot preparation as master alloys. An oxygen master alloy containing 25 wt pct 0 was prepared by melting iodide titanium and pressed titanium dioxide (40 pct 0) powder. The Ti-25 pct 0 alloy is more easily handled during weighing and charging than the pressed TiO, powder. Chemical analysis indicated that titanium-nitride received from an outside source contained large amounts of impurities (2.7 pct Ca). Therefore, a master alloy containing approximately 12 pct N was prepared by melting nitrided sponge titanium. As the sponge melted with difficulty, the alloy was diluted by addition of titanium to lower the melting point. The chemical analysis of the final alloy was 6.69 pct N. Both master alloys are friable and were used as —8 +16 mesh lumps resulting from crushing the ingots. NIelting the Ti-A1-0 and Ti-A1-N compositions five times produced homogeneous ingots. The preparation of homogeneous carbon-bearing alloys caused considerable difficulty. Alloys containing less than 1 pct C were prepared using spectrographic graphite rod, 1/8 in. diameter by 1/8 in. long. However, the graphite did not dissolve even with long melting times and many remelts. The ?/s in. pieces of graphite were used rather than powder because the low density powder is troublesome in arc melting.

Jan 1, 1955

By B. Ancker, E. R. Parker

The small-angle dislocation-boundary density of nickel and some of its alloys was investigated as a function of strength. It was found that the strength is a linear function of the density for pure nickel and for Ni-Ti alloys, but not for Ni-Co alloys. The results are interpreted in terms of dislocation theory. THE processes by which metals deform are still poorly understood, even though there has been a concentrated research effort in this field during the past fifteen years. Single crystals and individual grains in polycrystalline aggregates often develop a subgrain structure when deformed. Substructure formation occurs as a result of local plastic bending and its development is augmented by annealing at moderate temperatures.&apos; Investigations made to date, largely qualitative in nature, have shown that the substructure is composed of a network of small-angle boundaries. The purpose of the present paper is to present some quantitative data on substructure (obtained by X-ray techniques) and to correlate the results with the strength of the metal in which the substructure existed. Nickel and some of its alloys were used for the experiments. The presence of certain kinds of foreign atoms greatly alters the formation and effect of the substructure. Polycrystalline tensile specimens were prepared from high purity nickel, two Ni-Ti alloys, and two Ni-Co alloys; the composition of these materials is given in Table I. Tensile specimens having a reduced section 1/4 in. diam by 3 in. long were machined from materials which were refined, cast, forged, and swaged in the authors&apos; laboratories. The specimens were annealed for 1/2 hr at 1150°C, a treatment which produced grains having a diameter of approximately 0.5 mm. This rather large grain size was used to facilitate later examination of the substructure. Duplicate specimens of pure nickel and of each alloy were strained various controlled amounts in tension at room temperature and recovered for 1 hr at 800°C. (This strain induced prior to recovery will be referred to hereafter as the "prestrain.") One of each of the recovered specimens was pulled in tension at room temperature to obtain the stress-strain curves. The other bar was cross-sectioned in the gage length, carefully polished, and deeply etched to remove all cold-worked material. This specimen was then examined by the X-ray microscopic technique2 to determine the nature and magnitude of the substructure. The use of duplicate specimens permitted a direct correlation between tensile properties and substructure characteristics. X-ray microscopic studies were made with an apparatus constructed to have an average resolving power of about 4 microns. The monochromatic radiation reflected from grains which were oriented favorably was recorded on fine-grain photographic plates. These were examined at Xl00 which represents the true magnification, since there was essentially none in the X-ray system. This permitted detection of angular differences between subgrains of as little as 10 min. A very large number (over 100) of grains for each specimen was examined at this magnification and the number of substructure boundaries per grain was tabulated. An accurate relative measure was obtained under fixed experimental conditions, e.g., same grain size, resolving power, magnification, etc. The greatest source of error lay in counting the subboundaries, but this proved to be surprisingly small when repeated counts were made by different investigators. Furthermore, as the subsequent analysis indicates, whatever human error was introduced was not significant. Analysis of the Substructure Data When the number of substructure boundaries per grain was plotted against the frequency, skew (asymmetrical) distribution curves of the type shown in Fig. 1 were obtained. These are smoothed curves for the 1 atomic pct Ti in nickel alloy subjected to various prestrains and are representative of the curves obtained with all the metals. Since skew-distribution curves cannot be analyzed by elementary statistical methods, detailed investigations were undertaken in order to 1—test the consistency

Jan 1, 1955

By C. R. Holmgren

A large consolidated sand core was used in this investigation. Four groups of experiments including gas drives, water drives, and water drives combined with gas injection, were made. The results of the gas-drive experiments indicate that greater ultimate recovery may be obtained by higher pressure gradients. However, other considerations challenge the absolute veracity of this conclusion. Results indicate that with connate water present and a low pressure gradient during a gas drive, less gas is required to produce a given amount of oil. The saturation gradient determined during a gas drive is presented. Results of the water-drive experiments indicate that the recovery of oil is not a function of either gradient Or input rate. The presence of initial gas saturation resulted in a slightly lower final oil saturation. Injection of sufficient gas to maintain the initial gas saturation during a water drive resulted in lower final oil saturation. Introduction With the demand for petroleum products reaching an all-time record high and the location and exploitation of new reserves becoming more difficult and expensive, the oil industry must look to more thorough and efficient methods of producing the petroleum already located. Much of the previous work along these lines is exploratory and suggests a more complete investigation. For example, a great amount of laboratory work has been done on flooding sands initially saturated roo pct with oil. Since sands saturated roo pct with oil rarely, if ever, exist in nature, and because the water content is a vital factor in the ultimate recovery from the sand, laboratory investigations on cores without water must be supplemented by comparable work on cores with water present.1&apos;2 Other investigators have done a considerable amount of laboratory work using gas and water drives.3 Krutter and Day4 have reported results of investigations using cores saturated IOO pct with oil and have concluded that " the ultimate recovery obtained, using air drive, from a completely oil-saturated core depends on the pressure gradients used. The higher the pressure gradient, the greater will be the recovery until a certain Pressure range is reached above which the reward of increased recovery is much smaller for similar increments in pressure." Yuster and Day6 conclude that less gas and less time are required to produce a given quantity of oil at high pressure gradients than at low pressure gradients; they also conclude that an increase in the viscosity of the oil requires a proportionate increase in the gas needed for recovery. Their results indicate that the gas required to produce a given quantity of oil is greatly reduced by the presence of connate water. R. C. Earlougher2 concluded, based on results of water-flooding a large number of

Jan 1, 1949

By K. E. Brown, F. W. Jessen

It is deemed feasible to store atomic reactor fuel wastes in salt dome cavities when the differential pressure acting on the cavity does not exceed 3,000 psi and the temperature is less than 400°F. Tests at pressure increments of 1,000 psi were conducted on a 2-in, cylindrical cavity contained in a 6-in. long X 6-in. diameter salt core. The cavity exhibited stability under pressures up to 3,000 psi and temperatures to 300°F. At temperature ranges of 100 to 400°F and with pressures of 5,000 psi and above continuous deformation of the cavity resulted. Initial movement of the salt was observed at all pressares. This was evidenced by vertical deformation and cavity size reduction. INTRODUCTION The development of storage techniques for safe disposal of atomic reactor fuel wastes is a goal of the Atomic Energy Commission. Salt domes have been used successfully for storage of liquefied petroleum gases and hence should prove to be suitable for liquid waste products of atomic reactors. The purpose of the following work is to evaluate the practicability of utilizing salt dome cavities for such wastes and to de-termine particularly the effect of pressure and temperature on a salt cavity. This work represents a part of a comprehensive study covering the over-all problem of storing re- actor fuel wastes in salt domes and/ or salt beds. The problem of accurately determining the stresses which exist in rocks in the earth&apos;s crust is indeed a complex one. Theoretical studies have differed widely in many of the basic assumptions about the physical properties of the rock itself. Some solutions of problems in underground stress analysis assume that rock is elastic, homogeneous and isotropic in character; others assume that rock possesses plastic, viscous, elasticovis-cous properties, or a combination thereof. Experimental evidence has shown that salt possesses plastic, viscous and elasticoviscous properties.&apos; Recent work has shown that salt becomes more plastic with temperature.&apos; APPARATUS AND PROCEDURE For experimental study a cylindrical cavity was chosen for analysis since it provided maximum volume per unit of depth with constant diameter. This particular cavity shape, allowing for irregularities, can be easily leached out of salt domes in field operations. For the purpose of approaching underground storage conditions as nearly as possible, the following factors were considered: (1) control of pressure and temperatures, (2) measurements of temperature gradients throughout salt mass, and (3) measurement of structural stability of salt cavities. In order to obtain triaxial pressure on the salt cavity without resorting to the application of fluid pressure directly on the salt mass, a system was designed whereby the same effect could be produced through axial loading only. By cutting a core to close dimensions to fit a steel test cylinder and applying axial pressure, a lateral pressure was obtained. This equipment is shown in Figs 1 and 2. A steel cylinder was made from

By R. G. Schaal

The Magma Mine at Superior, Arizona had an unimpressive beginning as a. worked out silver mine that was purchased in 1910 for $130,000 and then incorporated into the Magma Copper Company which has been continuously mining the deposit since 1915. Copper is the principal metal produced. However, zinc, gold, silver and iron have also contributed to the total metal product. Prior to 1973, the production rate of 1500 tons per day was maintained by hoisting 4 and 5 ton pay-loads at speeds up to 1100 FPM through four small hoisting shafts. The hoists used included 8&apos; and 7&apos; diameter double drum, double clutched doc. and a.c. motor driven geared units built as early as 1917. One old timer that did yoeman&apos;s service for many years was an 8&apos; Bollen Pulley with a.c. geared drive that utilized an endless rope system with mechanical grip and release mechanism built into the pulley&apos;s throat. Primary power for all of these old production hoists was 25 Hertz. Exploration that was completed in 1967 developed a reserve of 10 Million tons of 5 per cent copper which was sufficient to justify new capital expenditures for enlargement of productive facilities to 3300 tons per day. To reach the new reserves a 22&apos; I.D. concrete lined vertical shaft was sunk to an initial depth of 48431. A 12 ½ diameter adit was bored from the mill side of the mountain to intercept the shaft at a point about 1100&apos; below the collar. This 9200&apos; long adit provides the right-of-way for the mine to mill railway and egress for heavy supplies from rail head as well as a conduit for potable water, electric power, compressed air and mine drainage. Mine operating levels begin 3582&apos; below collar and thereafter have been cut at 100&apos; vertical intervals. Skip loading stations have been installed 4282&apos; and 46821 below collar with an in-shaft skip dump station located 800&apos; below collar. This provides for 4500 tons of storage above the mine to mill train loading station located 1100&apos; below collar. Ore and waste are moved horizontally from stope chutes and drift headings by rail haulage to transfer raises which channel all material to the two mentioned skip loading stations. The 22&apos; diameter shaft crossection is arranged with the two skip compartments on the south side separated from the manway and utility compartments by the cage compartment. The cage counterweight operates in a portion of the southwest quadrant of the shaft. The hoisting plant consists of two conventional Nordberg double drum, single clutch, geared, d.c. motor driven units that are identical except for the drives and automatic controls. The drums are 15&apos; diameter x 105" face with LeBus grooving for 2-1/8" diameter wire rope wound in three layers. Mechanical design emp1o::ed is the same as has been used for the past twenty- five years. One drum is attached to the main shaft by 2 large bolted integral shaft flenge. The loose drum is engaged by a 4-arm positive tooth clutch meshing with radially cut teeth of the clutch ring which is bolted to the drum. The drums are one-piece steel plate weldments having a finished weight of 60 tons each and are mounted upon a 36" diameter shaft that also weighs 60 tons. With the addition of brake rings, clutch, bull gear and rope, the total dead weight adds up to nearly 250 tons that is supported by just three double row spherical roller pillow block bearings. There is no bearing between the drums. All pinion shafts as veil as all head sheave journals are supported in the same type of antifriction bearings.

Jan 1, 1975

By Michael Hoch, Seong Kwan Rhee

The ternary system Zr-Cr-0 was investigated at 1200°, 1500°, and 1700°C. The isotherms at these temperatures were determined by metallographic and X-ray diffraction analysis of carefully selected alloys. AS a part of a series of investigations1-4 of the ternary and quaternary phase diagrams on refractory metals and their compounds, the ternary system Zr-Cr-O was investigated at 1200°, 1500°, and 1&apos;700°C. The binary diagrams Zr-Cr, Zr-O, and Cr-0 as reported by Hansen5 and Levin et a1.&apos; and the existence of a ternary coompound ZrsCrsO (q-carbide structure a. = 11.96A) provided a good base for this investigation of the Zr-Cr-O phase diagram. MATERIALS The materials used and their suppliers were: Zirconium powder, 99.4 pct pure, Charles Hardy, New York; Zirconium dioxide, Fairmount Chemical Co., Newark, N.J.; Chromium powder, 99.85 pct pure, Fairmount Chemical Co., Newark, N.J.; Chromium sesquioxide, 99.86 pct pure, J. T. Baker Chemical Co., Pillipsburg, N.J. Though the materials used were not "hyperpure", the impurities present do not affect the results (lattice parameters, phase boundaries) within the experimental accuracy. EQUIPMENT AND PROCEDURE The detailed procedures and equipment used for this investigation were similar to those described elsewherel&apos; "ith the exception that in this study an induction-heated argon-atmosphere furnace was used. The latter furnace was used to prevent the vaporization of chromium metal in samples in the higher temperature range (above 1200°C). The tungsten crucible was induct ion-heated in a vertical quartz tube filled with argon gas. The quartz tube was 1-1/2 in. in diameter and 10 in. long; it was connected at the top and bottom to water-cooled copper plates. The argon gas of a purity 99.995 pct was further purified by being passed through zirconium metal chips which were maintained at 800°C in a silica tube 1 in. in diameter and 30 in. in length. The furnace was flushed with argon gas for an hour before starting heating; during heating, a slight (3 cm oil) overpressure of argon was maintained in the system. Power was supplied by a 20-kw Ther-Monic Induction Generator. The samples rested on a tungsten-wire basket; the wire basket was connected to a tungsten wire which passed through the tungsten crucible lid, and entered the system on top through a Wilson-type seal. By pulling on the wire, the sample was removed from the crucible and dropped to the water-cooled copper base of the furnace. Because of the presence of argon gas, the cooling of the sample was even more rapid than in the vacuum furnace.&apos; EXPERIMENTAL RESULTS AND DISCUSSION 1) Isothermal Section at 1200°C. The compositions investigated have been numbered within the phase diagram, Fig. 1, and all the pertinent information about the samples can be found in Table I. This table lists the composition of the samples, the phases present in the room-temperature diffraction patterns, the phases detectable in the microstruc-ture, and calculated lattice parameters of the a-zirconium phase. The shapes of the various phase

Jan 1, 1964

By O. R. Bergmann

Two approaches were taken to obtain direct experimental evidence jar the existence oj a jet in the explosion-cladding pvocess: 1) direct observation of the claddirg jwocess by rtzeans ojf kig-h-speed photography using a fvartziiy catnera and 2) use of a plated-surface experiment in contribution with clzetrzical analysis. The framing-camera records showed clearly the presence of a jet it1 the form of what appears to be a line spray. The jet velocity is considerably highev than the detonation velocity arid in vacuum it is almost twice as high as the detonatiou velocily. The results jrorrz the plated-surface experiment also corzfivtned the preseizce of- a jet. The artzoutlt o,f etzergy dissipated in the jetting process was foundd lo be consislent with the basic theovetical model o/ the cladding mechanism.. MaNY reports on metal working with explosives have appeared in the literature during the last few yearsThis paper describes experiments concern- ing the mechanism of the explosive metal-cladding process. It has become increasingly important as a unique method for bonding metals and a typical cladding arrangement is shown in Fig. 1. A theoretical analysis of the mechanism of explosive bonding and a description of the nature and types of bond zones obtained was given by Cowan and oltzman." A further discussion of the basic principles of the process, a detailed description of the different bond-zone types, and extensive information on the properties and the applications of explosively bonded metals was recently published by Holtzman and cowan. " The process is now in commercial use by E. I. du Pont de Nemours & Co. The concept of the existence of a jet during metal bonding with explosives forms a central part in the theoretical analysis of the cladding mechanism described by Cowan and Holtzman When a layer of explosive is detonated on a metal plate that is separated from a second metal plate by a small distance the metal plate in contact with the detonating explosive is accelerated by the detonation pressure. An angle is established between the undeflected and deflected portions of the plate. Subsequently the deflected portion of the first plate collides with the second metal plate.

Jan 1, 1967

June was the month in which AIME was founded in the year of 1871. For some reason, February was selected as the month for the legal Annual Meeting. One can&apos;t help thinking wistfully of Annual Meetings in June but of course this is not the reality. Because the Centennial Ceremonies are taking place in February, that month has been chosen as the one in which MINING ENGINEERING, the monthly magazine of the Society of Mining Engineers, a constituent society of AIME, is publishing its Commemorative is- sue to celebrate the event. SME and ME take a proprietary air about AIME. This is mostly because AIME started as the American Institute of Mining Engineers. Metallurgy was added to the name in 1919 and Petroleum in 1956. The official abbreviation of "AIME" has been retained, however.

Jan 1, 1971

By H. L. Gilbert, C. Travis Anderson, W. J. Kroll

IN a previous paper,1 the use of a split graphite tube resistor as a heater element for high-temperature furnaces has been described. The principal advantages of this type of construction are: I. The quadruple resistance or voltage compared with the top-bottom clamp resistor furnace. 2. Free expansion of the resistor. 3. The ease of protection from oxidation by air. 4. The firmness by which it may be held in the compact split clamp. This construction appeared to be well adapted for the fusion of high melting metals which require fusion in a vacuum. Zirconium metal had previously been melted at the Albany Laboratory of the Bureau of Mines in a vacuum arc furnace on a water-cooled plate, using a movable tungsten top electrode.2 When larger furnace capacities were desired, this type of construction proved to have its limitations as the largest tungsten rods available were about 7/8in. in diameter. The supply of direct current of high amperage for producing the . desired arc characteristics was also not available. Considerable difficulty was also found in compensating the atmospheric pressure on the flexible tubing of the movable electrode, at the same time keeping its movement sufficiently free to enable the striking of an arc on any part of the metal briquet. Among the various materials used for the electrodes in conducting experiments in the vacuum arc furnace was graphite. It was found that zirconium fused in a graphite cup with a carbon arc was contaminated to only 0.2 pct carbon. It was therefore decided to melt zirconium directly in graphite crucibles. A high-frequency furnace was first used in the attempt to melt the zirconium in graphite crucibles. The high-frequency heating coil was placed outside a silica tube which was evacuated by means of an oil diffusion pump backed up by a mechanical pump. The graphite crucible was thoroughly degassed at 1900°C before use. Considerable difficulty was experienced in operating at such temperatures in vacuo because, as shown by Zintl,3 carbon vapor formed and reacted with silica according to the reaction: Si02 + C = SiO + CO. The silicon monoxide which is volatile at these high temperatures reacted with the zirconium, thereby contaminating it with silicon and oxygen. The presence of carbon monoxide was detected by means of a gas discharge tube placed in the vacuum system as indicated by the pale blue glow of the tube as soon as carbon vapor started to react with the hot silica. The reaction between the carbon vapor and hot silica was avoided by the use of split cylindrical molybdenum shields which were inserted between the graphite crucible

Jan 1, 1948