By Axel Hultgren, B. Herrlander

THE original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between At and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880° was free from veining. Bannister and Jones4 considered veining in ferrite to be a manifestation of microscopical and submicroscopical inclusions. Northcott,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berglund. Tritton (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling.

Jan 1, 1946

Page Laboratory Methods...........................127 Special Analytical Methods.......................127 Improvements in the Accuracy of the Vacuum-fusion Method for the Determination of Oxygen in Steel....................127 Quantitative Spectrochemical Analysis of Mixtures of Gases.......131 Oxygen Samples from Open-hearth Bath...............133 Rapid Analysis of Sample for Alumina.................139 Accurate Carbon Analyses in Low-carbon Steel.............139 Laboratory Technique for Study of Reactions Involving Liquid Metal. . . . 142 Rotating Liquid Crucibles......................143 Stationary Crucibles.........................145 Jones and Laughlin Experimental Furnace...............148 Vacuum Melting..........................149 Measurement of Temperature of Liquid Iron and Steel;..........149 Pouring and Teeming Temperatures..................149 Bath Temperatures.........................151 Plant Methods.............................154 Methods of Studying Slags.......................154 Sampling Slag in the Open Hearth..................155 Viscosity of Open-hearth Slags....................155 Petrographic Examination of Slag...................156 Statistical Methods Applied to Study and Control of Chemical Relations in Bath...............................166 Rapid Method of -Correlation Applicable to Study of Steelmaking Reactions............................166 INTRODUCTION On Thursday morning, Feb. 16, 1939, a round table discussion was held on the subject of Experimental Methods in the Study of Steelmaking. Dr. John Chipman, Professor of Metallurgy at the Massachusetts Institute of Technology, and chairman of the A.I.M.E. Committee on Physical Chemistry of Steelmaking, presided. In opening the meeting, the chairman said: "The purpose of this round table is to discuss methods of study by which more and better information on the fundamentals of steelmaking can be obtained. It was thought that a round table discussion rather than a symposium would furnish the best opportunity for those actually using various methods of study to get together and discuss their common problems. For this reason attention will be focused upon methods of study rather than upon their results. We want new and current and up-to-date discussion.

Jan 1, 1940

By B. S. Norris, Charles R. Austin

The stresses which initiate deformation processes in metals are fundamentally important in the study of the mechanical properties of metals. A point of inflection in the load-elongation curves obtained for single crystals' has been rather too readily interpreted as a true yield point, and the critical resolved shearing stress on the plane of slip taken as a material constant. Even early work showed that the stress at this point varies with rate of loading, but it has not been generally appreciated that creep tests under static loads alone are suited for determining the existence or nonexistence of a yield point.* It has now been shown by Miller that single crystals of zinc3 when loaded statically begin to yield at loads too small to measure; as a result there is no case now known, apart from that cited in the present paper, in which a true critical stress for yielding has been demonstrated for single crystals of metals. The case of iron has especial interest: the existence of an upper and lower yield point and of an elongation at the yield point in ordinary iron and steel marks this substance as unusual, though the effects have been found to a very minor degree in other metals and alloys. $ Most alloys do not show such marked phenomena when appreciable yielding begins, and accordingly modern practice is to speak of the yield strength of such materials, a stress read from the load-elongation curve after elongation has begun, rather than yield point. The special behavior of iron suggests that it is more likely that single crystals of iron should have a true yield point than other metals. The study of the mechanical properties of metals and alloys requires a determination of the crystallographic mechanism of deformation, wlletller deformation proceeds by slip, twinning, or cleavage, or a combination of these, and a determination of the stresses that induce these modes of deformation. With this information, a study of the rates of work-

Jan 1, 1938

By A. W. Fahrenwald

The physics and chemistry of the flotation process are not well understood. Many papers dealing with the theory of flotation have been published but most have been narrow in their viewpoint. No theory advanced has done more than explain, more or less satisfactorily, various isolated phenomena. Scientists have done little with the problem, doubtless because they have not seen sufficient of the practical side of the subject to have their interest aroused. Any attempt to explain the mechanism of flotation that considers only contact angles, surface tension, adsorption, the floating of needles, flocculation, or any other single and narrow phase of the question is sure to be disappointing. Flotation is a problem of colloid chemistry and must be studied as such. In a broad general way, flotation is a process involving and operating by virtue of surface reactions. The term "surface reactions" may be open to criticisms. Many chemists give the term "reactions" a definite and restricted meaning and to such the term may connote change in atomic grouping in strict stoichiometric ratios. While Langmuir looks upon adsorption as a reaction, and there is much evidence in support of this view, we may look on adsorption as a physcial process as far as this paper is concerned. The term seems well suited to the work in general. Presumably these reactions are reactions between the same kinds of forces (electrical) and differ only in degree and in the surface manifestations produced. This premise seems logical if we accept the theory that the atoms of dl elements are made up of grains of electricity, having mass and charge, called electrons; and that atoms differ from one another only in the number and arrangement of the electrons about a positive nuclear

Jan 1, 1924

By Nathaniel Arbiter, Norman L. Weiss

Factors now accelerating the trend to larger concentrators and larger equipment units are reviewed. After almost 40 years of stability with unit sizes less than 100 cu ft, 200 and 300-cu-ft flotation-cell units are now operating and a 500-cu-ft machine is being built. The design of these cells is considered, as is the design and operation of flotation circuits against the background of the need to achieve greater process efficiency while holding down operating and investment costs. Particular attention is paid to the scale-up problem. With the newer cells having five to ten times higher unit capacities, the advantages resulting from this in sampling, mill operation nnd control, testing and plant layout are indicated, as well as the broad direction for changes in the overall design of 50,000 to 100,000-tpd concentrators. A comparison is given of the available larger cells of U.S. manufacture with analysis of differences and similarities. After almost 60 years of application in this country, froth flotation is still by far the most important process for concentrating metallic ores as well as a number of nonmetallic ores including fluorspar, phosphate rock, and potash. Its use on iron ores and coal is increasing. In the metals groups, the largest plants and the greatest progress are found in copper and molybdenum mills, and the section of this paper that deals with applications will be found most pertinent to that field. During its long reign, the flotation process has passed through several phases of evolution and has achieved progress in economy, efficiency. and simplicity of operation. Much of today's success in the flotation of low-grade ores can be attributed to that progress. Even more important to us than our ability to cope with today's conditions are tomorrow's problems, which we can contemplate with some prescience and confidence. Our annual production of copper, lead, zinc, and molybdenum—to mention only the most important metals occurring in the U.S. as sulfides- must be held at a high level in the face of a declining grade of ore. It is probable that the tonnage of such ores mined and processed will double in this country before the turn of the century. Not only will many of the existing flotation mills be enlarged again and again, but larger mills will be built here and abroad to meet our needs. At this moment, in fact, there are at least three proposed new foreign mills or expansions that envision 100,000-tpd milling rate on copper ores. Table 1' shows the trend in copper ore grades in U.S. in recent years. Table 2' shows the projected annual growth rate of consumption 1966-1985. A study by one of the authors 25 years ago showed that of 32 copper mills in North America with more than 100-tpd capacity, only eight had capacities exceeding 10,000 tpd. The average for these eight was 25,000 tpd. These included the three giants of that day, Magna, Arthur, and Morenci; the other five averaged a little over 10,000 tpd. Today instead of the eight mills with capacities exceeding 10,000-tpd capacity we have 25, and the mill with less than 1000-tpd capacity is fast becoming extinct. Much less range is found in lead and zinc mills, which are still generally small except for the few with over 1000-tpd capacity in Missouri, Utah, and Idaho, and a few zinc ore mills in the same size category. Molybdenum and potash operations are the fastest growers in North America today, but when one considers the projected increase in consumption of copper together with the projected decrease in grade of ore (3% annually), he can foresee that copper ore milling will soon lead the list. Technological improvements to meet the challenge of lower-grade ores have taken the wholly predictable path toward bigger equipment. In mining, shovels, draglines, scrapers, and trucks have led the way; in ore processing, we have seen a rapid increase in size of grinding mills, flotation cells, and pumps. Twenty-five years ago, for example, the 10-ft-diam ball mills treating 2000 tpd at Morenci were considered the giants, but today some grinding mills in similar service have five times that capacity. The specific matters to be dealt with in this paper are 1) the underlying principles that affect flotation-machine design, and the conditions required to produce

Jan 1, 1971

By I. H. Silberberg, R. L. Reed, O. K. Kimbler

interfacial films have frequently been observed at interfaces between certain crude oils and water. Several investigators have postulated that the presence of these films should influence the efficiency of oil recovery in water drive or waterflood operations. They may also influence the stability of emulsions which are sometimes a problem in petroleum production, and may be a factor in the fonation of paraffin deposits in oil well tubing and flow lines. This paper presents a technique with which a modified Langmuir film balance may be used to study the compressibility and collapse pressure of these natural interfacial films. Experimental data are presented for several nude oil-water systems. Data developed are used to infer the phase state of the film as a function of such variables as rate of reduction of interfacial area, ionic composition of the subtrate and pH of the subtrate. A film of known physical characteristics is shown to have a sinnificant effect on oil recovery from an unconsolidated sand pack. Possible applications of these results to petroleum production are discussed. INTRODUCTION The use of water to displace petroleum from reservoir rocks is of major importance both as a primary and a secondary recovery process. As water invades the rock, oil is completely displaced from some pores and left as a discontinuous phase in other pores. The manner in which water moves from pore to pore is strongly influenced by capillary forces. In view of the complexity of reservoir fluid systems, there can be little doubt that complicated interactions take place at both the liquid-solid and oil-water interfaces. One of the more interesting, and least understood, of the phenomena which take place at the oil-water interface is the formation of interfacial films. These films are believed to result from the adsorption of high molecular weight polar molecules at the interface.l.2 Presence of such molecules may cause a striking alteration in interfacial tension. When the oil-water interfacial area of certain crudes is rapidly reduced, a thin region (film) about the interface assumes the appearance of a solid membrane, and striations, wrinkles and gross distortions may occur. If such a film is solid, it should greatly alter the interfacial tension normally assumed to exist between the oil and water phases. If the membrane is continuous, a solid phase would separate the oil and water. Interfacial films between crude oil and water were observed in 1949 by Bartell and Niederhausers who commented upon the apparent rigidity of the films and their possible importance in the petroleum industry. Morrell and Egloff4 had earlier attributed the extreme stability of emulsions of sea water in fuel oil to very stable asphaltic films. Numerous investigators have observed rigid films in the course of crude oil-water interfacial tension determinations by the pendent drop method. Several investigators5,6,2 have separated inter-facially active materials from crudes and attempted to characterize them chemically. Reisberg and Doscher,2 using Ventura crude, showed the interfacial tension against water (as measured by the pendent drop method) to be affected by aging, contraction and expansion of the interface, and the pH of the water. These investigators attributed the adhesion of oil to a water-wetted surface and the distortions of flow paths in glass capillaries to the presence of rigid films. Dodd7 has studied the interfacial viscosity of adsorbed films and found them to be non-Newtonian in behavior. Craighead and Harvey8 reported a series of displacements in tubes packed with 60 mesh glass beads. They interpreted the results as indicating an effect of stearic acid films on waterflood recovery and imply that natural films may produce similar results.

Jan 1, 1967

By B. S. Norris, Charles R. Austin

The stresses which initiate deformation processes in metals are fundamentally important in the study of the mechanical properties of metals. A point of inflection in the load-elongation curves obtained for single crystals' has been rather too readily interpreted as a true yield point, and the critical resolved shearing stress on the plane of slip taken as a material constant. Even early work showed that the stress at this point varies with rate of loading, but it has not been generally appreciated that creep tests under static loads alone are suited for determining the existence or nonexistence of a yield point.* It has now been shown by Miller that single crystals of zinc3 when loaded statically begin to yield at loads too small to measure; as a result there is no case now known, apart from that cited in the present paper, in which a true critical stress for yielding has been demonstrated for single crystals of metals. The case of iron has especial interest: the existence of an upper and lower yield point and of an elongation at the yield point in ordinary iron and steel marks this substance as unusual, though the effects have been found to a very minor degree in other metals and alloys. $ Most alloys do not show such marked phenomena when appreciable yielding begins, and accordingly modern practice is to speak of the yield strength of such materials, a stress read from the load-elongation curve after elongation has begun, rather than yield point. The special behavior of iron suggests that it is more likely that single crystals of iron should have a true yield point than other metals. The study of the mechanical properties of metals and alloys requires a determination of the crystallographic mechanism of deformation, wlletller deformation proceeds by slip, twinning, or cleavage, or a combination of these, and a determination of the stresses that induce these modes of deformation. With this information, a study of the rates of work-

Jan 1, 1938

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By A. S. Richardson

AIR conditioning, or air cooling, for the improvement of ventilation in the Butte mines has come into increasing use during the past 10 years. In part, the methods practiced have been described in previous publications of the Institute, but some improvements on earlier methods have been made and a number of new features have been developed. This paper is presented as a record of progress made, and for the sake of completeness describes all general features of the work. The need for air conditioning in the ventilation of mines in the district arises from the fact that the temperature of the ground and mine water has shown a very great increase with increase in mining depth, and has now reached a maximum of slightly over 130°F. The most difficult part of the ventilation problem is the maintenance of temperature and humidity of a satisfactory standard in the working places, especially on the lower levels. Although ordinary ventilation is adequate to maintain good conditions in most of the working places it is subject to a number of limitations at great depth. Most important among these limitations is that with increase in depth the air becomes heated before it reaches the working places, both by compression from increase in atmospheric pressure and by heat transferred to it from rock at high temperature, so that its capacity for lowering temperatures is greatly reduced before it reaches the operating zone. Increasing depth of mining also increases the distance traveled by the air in its passage through the mine, and this causes a corresponding increase in resistance to air flow, so that there is greater difficulty in maintaining even the same volume in circulation. Thus, in the face of a demand that the ventilating system have a very much greater capacity to remove heat from the mine, the tendency is for that capacity to diminish. The only evident alternatives were (I) the opening of additional air shafts to increase the volume of air in circulation, (2) an extension of the existing system that would be subject to the same limitations, or (3) the adoption of an entirely different method such as air cooling. Fortunately for an economic solution of the problem, the mean annual temperature of the surface atmosphere at Butte is about 40°F., with very low relative humidity in summer, so that there is unlimited natural cooling power at a temperature range adaptable to air-conditioning methods. METHODS Two similar methods of air conditioning are used, as necessitated by service requirements and dependent upon the equipment available. In one, which is the more important and has the greater cooling capacity, water is circulated in a closed circuit, and, alternately, first absorbs heat from warm mine air and then dissipates it in the surface atmosphere by cooling at a cooling tower. The second

Jan 1, 1941

By Frank Woolley, John F. Elliott

The high-temperatzrre solulion calorimeter has been modified and an extension dynamic analysis of i/s transient behavior has provided an improved basis for interpretation of the experimental data. The partial molar heats of mixing, Him, of aluminum, copper, and silicon in the corresponding binary liquid-iron alloys haz,e been measured directly at 1600°C. The resulls in kcal per g-alom are: THE high-temperature1,2 solution calorimeter was planned and designed to obtain directly the partial molar heat of solution of solute elements in a variety of liquid metals that might serve as solvents. Results obtained in the temperature range of 1000° to 1200°C were described in the two earlier publications. However, a long-term goal in the program has been to obtain measurements at 1600°C of the heats of solution of elements in liquid iron. Hence, subsequent to the work last reported,2 and based on the experience of the first two studies, the calorimeter system has been modified and operated at 1600°C to obtain measurements on the Fe-Si, Fe-A1, and Fe-Cu systems. This paper reports the results of the work. THE MODIFIED SYSTEM It was clear from the earlier results that the most precise measurements can be obtained with the high-temperature solution calorimeter when the solution time is less than approximately 30 sec. This can be achieved only when the bath temperature, Tb, is above the melting (liquidus) temperature of the solute material being dropped. A second point of importance is that the refractories used earlier liberated considerable water so that, although the oxygen potential of the atmosphere in the system was satisfactory for work with nickel and copper, it was too high for work with iron, silicon, and so forth. Third, for work at 1550" to 1650°C, an improved temperature-sensing unit is needed. The modified calorimeter in its latest form is shown schematically in Fig. 1. The refractory brick and the Kanthal-Super heating elements which formed the furnace for heating the solute addition have been replaced by a smaller resistance-heated tube furnace which is insulated with bubble-grain alumina. A more elaborate gas purification system was installed to maintain a satisfactorily low oxygen potential in the atmosphere of the calorinieter chamber and of the solute addition furnace. As was the case in the earlier work, at the beginning of a run the calorimeter chamber is evacuated and then filled with purified argon so that a total pressure slightly in excess of 1 atm is maintained during the run. When either of the furnaces within the enclosure attains a red heat, 6 pct H2 is added to the atmosphere. Throughout the run, gas from the calorimeter is circulated through a de-oxidation system at the rate of approximately 5 standard liters per min; the changeover time for the gas within the calorimeter enclosure is approximately 1 hr. The essential stages of the deoxidation system are: a copper furnace at 600°C, a drying tube of anhydrite, and a titanium furnace at 800°C. The oxygen potential of the gas stream in the purification system can be monitored at several points by a stabilized zirconia oxygen cell. This cell is invaluable in detecting the development of leaks in the container vessel and the gas circulating system. The installation of the solute-addition furnace allowed either of two types of temperature-sensing units to be mounted on a water-cooled probe. The first was a small optical device using a silicon diode that was

Jan 1, 1968

By C. S. Smith

It is the policy of The Metallurgical Society to provide, in the TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, a prompt and accurate medium for publication of reports of significant new research in both the scientific and engineering aspects of metallurgy. Papers submitted to the Society are judged by competent reviewers according to established criteria for technical merit, accuracy, originality, and presentation. STAFF: Editor, Dr. Gerhard Derge; Editorial Assistant, M. A. Redmyrski; Staff Coordinator, James J. Burke. THE METALLURGICAL SOCIETY: W. R. Hibbard, Jr., President; J. C. Kinnear, Jr., Post-President; John Chipman, Vice President; T. D. Jones, Treasurer; R. W. Shearman, Secretory. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: A. W. Thornton, Chairman- Dennis Carney John Chipman J. C. Fulton J. H. Hollomon H. H. Kellogg, A. E. Lee, R. Moddin, J. D. sullivan, and D.&apos; Swan. Review and selection of manuscripts is under the supervision of the following Publications Committees: Extractive Metallurgy Division: T. B. King, Chairman; S. J. Dickenson, R. P. Hermsdorf, R. Schuhmann, Jr., and P. T. Stroup. lnstitute of Metals DM lion: Robert Maddin, Chairman. F. Lincoln Vogel, Jr.. Vice chairman. W. A. Backofen R. W. Boliuffi J. H. Bechtold&apos; M. B. Bever R: S. Busk C 6. Goetzel poul Gordon C. D. Grobom, Jr., Robert F. Hehe-mann R. I. Joffee F. i. Joumot Jr. lrvin R. Kromer, A. J. Leno. Horold Morgolfn, C. J. McHargue, Russell A. Meussner, J. B. Newkirk, H. W. Paxton, G. E. Pellissier, I. S. Servi, Alon U. Seybolt, A. J. Shaler, and Jack Washburn. Iron and Steel Division: J. C. Fulton, Chairman. T. B. King, F. C. Laogenberg, W. O. Philbrook, and T. 0. Winkler. Publishod bimonthl by the American Institute of Mining Metollurgicol and Petroleum Engineers Inc., 29 West 39th Street, New York 16, N. Y. Telephone: PEonylvanie 6-9220. Subscription $20 par yew for non-AIME members in United States and North, South and Control Americo $25 foreign; $5 for AIME members. Single copies, $4.00, single copios foreign $5,00. The AIME is 1958 by the Amarican mode or opinion axpressed in it* publications ... Copyright by the Amarican lnstitute of Mining, MataIlurgicol, and Petrolum Engineers, Inc,. . . Reg. istered cable address AIME New Yark ... Indexed in Engineering Inderx, Industrial Arts ...Index and Chemicol Number5. Absrtracis . . . Second class postage paid at New York,Indor. N. Y., Industrialond Ann Arbor, Mich.

Jan 1, 1959

By Charles Clayton

CAST-STEEL runners, while not interesting from a commercial standpoint, furnish valuable material for microscopic study. Foley1 found not only the usual ingot structure, but zones of Widmannstattian structure, which he explains as due to differential crystallization. The writer, in examining nickel-steel runners, found a type of pro-eutectoid ferrite that is unusual and most probably new. The runner in question was 8.75 cm. (3.5 in.) in diameter and analyzed at its center 2.69 per cent, nickel and 0.350 per cent. carbon and at its edge 2.62 per cent. nickel and 0.359 per cent. carbon. The macrostructure, which is the usual type, is shown in Figs. 1 and 2, which are a cross-section and the longitudinal surface, respectively. Slight segregation of ferrite can be seen near the center of the segment and at other points near the edges of polyhedral grains. Stead&apos;s reagent brings out the dendritic structure within the grains as shown in Figs. 3 and 4. This texture is what would be expected of such a steel. Figs. 5 to 10 show the peculiar swirls of pro-eutectoid ferrite, the finding of which prompted this paper. These swirls, or eddies, if such a term can be applied, occur in all parts of- the runner and in all parts of the individual grains. I he tipper left-hand figure shows this ferrite at a grain boundary; the middle left-hand figure shows the inner portion of a grain; and the lower left-hand figure shows these swirls at the edge of a grain which is also the outer edge of the runner. Straight-lined ferrite associated with swirls is found in the areas of Figs. 11 and 12. The texture of the carbon-bearing constituent of the runner is shown to- some extent in Fig. 12, the pearlite being very fine or sorbitic. Higher magnification does not bring out any new features either in the peculiar ferrite or in the pearlite. Figs. 13 and 14, at 240 diameters, show the curved and straight-lined ferrite.

Jan 3, 1920

Page Laboratory Methods...........................127 Special Analytical Methods.......................127 Improvements in the Accuracy of the Vacuum-fusion Method for the Determination of Oxygen in Steel....................127 Quantitative Spectrochemical Analysis of Mixtures of Gases.......131 Oxygen Samples from Open-hearth Bath...............133 Rapid Analysis of Sample for Alumina.................139 Accurate Carbon Analyses in Low-carbon Steel.............139 Laboratory Technique for Study of Reactions Involving Liquid Metal. . . . 142 Rotating Liquid Crucibles......................143 Stationary Crucibles.........................145 Jones and Laughlin Experimental Furnace...............148 Vacuum Melting..........................149 Measurement of Temperature of Liquid Iron and Steel;..........149 Pouring and Teeming Temperatures..................149 Bath Temperatures.........................151 Plant Methods.............................154 Methods of Studying Slags.......................154 Sampling Slag in the Open Hearth..................155 Viscosity of Open-hearth Slags....................155 Petrographic Examination of Slag...................156 Statistical Methods Applied to Study and Control of Chemical Relations in Bath...............................166 Rapid Method of -Correlation Applicable to Study of Steelmaking Reactions............................166 INTRODUCTION On Thursday morning, Feb. 16, 1939, a round table discussion was held on the subject of Experimental Methods in the Study of Steelmaking. Dr. John Chipman, Professor of Metallurgy at the Massachusetts Institute of Technology, and chairman of the A.I.M.E. Committee on Physical Chemistry of Steelmaking, presided. In opening the meeting, the chairman said: "The purpose of this round table is to discuss methods of study by which more and better information on the fundamentals of steelmaking can be obtained. It was thought that a round table discussion rather than a symposium would furnish the best opportunity for those actually using various methods of study to get together and discuss their common problems. For this reason attention will be focused upon methods of study rather than upon their results. We want new and current and up-to-date discussion.

Jan 1, 1940

By H. I. Aaronson, H. A. Domian

ELectvon-probe analgsis has been used to in7:estigatr the partition ot alloying- elements between aus-tenite and proeutectoid ferrite (or the Jerritic component of bainite) in high-purity Fe-C-X alloys, lsuully at tzco levels of carbon content fca 0.1 and 0.4 pct in ntost steels) at temperatures between the M, and the Ae3 in Si, mn, Ni, mo, Co, Al, Cr, Cu, and PI steels. No partition ous found during the early stages of transformation at any temperature studied in the Si, ,mo. Co, Al, Cr, and Cu steels. Partition did take place, Jrowel&apos;er, in Ihe Mn, ATi, and Pt steels, occurring in lewtperature. regions below the Ae3 of ca 130°, 65", UNDERSTANDING the mechanisms through which alloying elements influence the kinetics of austenite decomposition reactions which proceed by nucleation and 35c respectively. A break was discovered in the TTT curve for the initiation oj the proeutectoid ferrite reaction in the latter steels at the temperature at which partition began. The alloy content in ferrite at the a:y bondavy remained at constart lecels, shown experimentally to be significantly above those corresponding to eqiilib+iu??l, e&apos;en at the longest reaction times investigated (ca 1o6sec). The partition and the TTT curve observations foere rationalized on the basis of the thermodynamic treatment developed in an accompany ing paper. and diffusional growth has been a major research objective of physical metallurgy since the latter part of the 19th century. The measurements made on the dif-fusivities of carbon and of substitutional alloying elements in austenite during the 1930&apos;s and 1940&apos;s seemed to provide a useful clue as to the nature of these mechanisms. These measurements showed that the diffu-sivity of carbon is several orders of magnitude higher than that of the alloying elements at a given tempera-

Jan 1, 1967

By Ralph D. Parker

The Frood mine (Fig. 1) is 2½ miles north of Sudbury, at a general elevation of 1000 ft. above sea level. It includes the original Frood location, which was the No. 3 mine of the Canadian Copper Co., and the adjoining Frood Extension, which until 1929 belonged to the Mond Nickel Co. Mine Openings The mine is operated from two vertical shafts and one underground incline shaft. No. 3, for men, supplies and ore, is a vertical six-compartment shaft in the footwall of the south mining area and extends froin surface to a depth of 3045 ft. No. 4 is a vertical three-compartment shaft, 2500 ft. north of No. 3 and adjacent to the north mining area. It extends from surface to a depth of 3345 ft., and is used exclusively for hoisting ore. No. 5 shaft, inclined at 65&apos; to the horizontal and of three compartments, is near No. 4 and extends from the 2600-ft. level to 77 ft. below the 3100 level. It is used for development below the 2800 level. The ventilation shaft, No. 1, with which this paper is directly concerned, will be described fully in the following pages. Mining Methods The orcbody is laid out in 80-ft. sections at right angles to the gcneral strike and numerically indicated from the southern extremity toward the north. Each section consists of a 45-ft. stope and a 35-ft. pillar, extending the full width of the orebody. Pillars and stopes are superimposed from level to level. The present mining territory is divided into two vertical areas, a north and a south area. Both areas have the same number of stopes on each level, the two areas being separated by 10 sections to be mined later. In a few instances, at the ends of the south area, where the orebody has narrowed, longitudinal stopes are used, of more than the usual 45-ft. width. It will thus be seen that mining operations hare been concentrated in two relatively small areas, offering

Jan 1, 1934

By E. V. Crane

A tremendous volume of the metal rolled annually into sheets strips and coil stock finds its way to a host of stamping and manufacturing plants which are the quantity production units of the country. Considerable in volume, too, are the rolled and extruded rods which go into forging and manufacturing plants for conversion into the same general line: those widely sold metallic necessities and luxuries of the household, the office, transportation, farming and building construction. Yet, in spite of its age and its importance, the stamping trade has been doing its "engineering" largely by trial and error. Its distinctive method is shearing out and plastically working metal to finished shape in a few quick strokes with high loads and expensive tools which are warranted only by large quantities to be produced. The principal operations have many features In common with rolling and wire-drawing methods. Combinations of stresses are diffcrent, however, and details of operations are infinite in variety. An engineering study of the subject begins with stress analysis, but must go back to metallurgy for its foundation. A grouping of pressed-metal working operations according to whether the metal is (1) sheared, (2) bent, (3) drawn or (4) squeezed has proved useful. All of these groups include instances of both hot and cold operations. For discussions of metal working properties, the division between hot and cold working is taken as the recrystallization range of temperature. This, of course, brings tin, lead and often zinc into the hot-work range at or near room temperature. The outstanding hot-working press field is in forging: particularly of brass; all of which is included in the squeezing group. Shearing Operations The shearing group of operations, including blanking, piercing, trimming, shaving, slitting, shearing, notching, parting and numerous variations and combinations of these enters once or more into the production schedule of practically every stamped or forged article. The transverse stress, set up in shearing, as shown in Fig. 1A, is a combination of an angular compressive thrust and a tensile stress which is also at an

Jan 1, 1931

By M. H. Harris

A solution has been obtained to the problem of calculating flow into a cased and perforated well. Equations describing the idealized system were solved by numerical analysis techniques on a high-speed digital computer. Computer experimentation indicated that the results are within 3 per cent of the exact solution. Computed results are presented as an apparent skin effect, on a series of dimensionless working curves. Productivity ratios can be rapidly calculated from these data for the wide range of wellbore and reservoir properties actually encountered in field practice. Any reasonable vertical unisotropy ratio can be included in the computation. Productivities can be calculated for wells perforated in a regular pattern, a single horizontal plane or a vertical line on one side of the casing. Solutions for asymmetrical perforation patterns can he easily obtained from the working curves. Solutions for flow into sells completed with a horizontal notch are also provided. Results show that productivity can be increased by extending perforation penetration. This is especially true for shallow penetrations. The highest productivity is obtained when perforations are arranged in horizontal planes, as opposed to a vertical line on one side of the casing. Four or five perforations in one plane will approach the maximum productivity. The effect of perforation hole diameter is small, and is rioticeable only in shallow penetrations. INTRODUCTION The perforating method of well completion has been successfully and widely used in most producing areas. In the past, the desired perforation results were achieved by simply shooting numerous large holes in the casing. A perforating scheme for an area, or particular well, was established by evaluating two types of experimental data: the well flow index and the productivity ratio.&apos; 3 The well flow index test is a means of determining the relative flow capacity of perforations in a linear system. This test also gives information on the perforation size, shape and hole damage which can be expected under well-bore conditions. However, relative flow data from this test cannot be accurately tarnsformed into the radial wellbore system. Thus, no true indication of the productive capacity of a perforated well can be obtained from the well flow index test. A well productivity ratio is derived from electrolytic models built to simulate perforated wells. Available productivity ratio data 2,3 are limited in that all important variables are not extensively evaluated. For example, data are limited to well radii of 3 and 6 in., and to maximum perforation penetration of 1 ft. Practically no information is available on the pattern of flow into a perforation. The effect of various perforation patterns on well productivity has not yet been determined and the effect of perforation diameter has not been thoroughly studied. Also, it will be shown that this type of electrolytic model data is probably in error by as much as 10 per cent or more. Modern completion techniques such as limited-entry perforating, single-plane fracturing, steam and hot air injection and chemical consolidation of incompetent formations all rely on injection and/or production from a limited type of completion. These completions may consist of several high-capacity perforations or a horizontal notch which is equivalent to an infinite number of perforations in one plane. Proper design of these new completion techniques requires, in part, accurate estimates of a well&apos;s productive capacity. Data on perforated and notched well productivity have been determined in this investigation. Results are presented as a function of the pertinent variables. Equations describing the idealized system were solved by numerical analysis techniques on a high-speed digital computer. DESCRIPTION OF PROBLEM PRACTICAL APPLICATION The computed results can be applied to wells which meet several general specifications. An external drainage radius of the well must be known or assumed, but the well need not be drilled on a regular pattern. The well must be cased and cemented through the entire producing interval. And, the casing must be perforated with one or more horizontal planes of perforations. The perforation pattern itself must conform to three geometrical requirements. 1. The perforations in a plane must divide the plane into equal angular segments (Fig. 1). Four perforations per plane would be 90" apart. 2. Perforations in a plane must be directly above or beneath perforations in adjacent planes. For two shots per plane, perforations would lie in the BB&apos; plane (Fig. 1). 3. Horizontal planes must have equal vertical spacing and be separated from the top and bottom of the formation by one half the spacing interval. Single planes of perforations should be in the middle of the formation. This is shown in Fig. 2 where h is the formation thickness in a single plane conlpletion or the spacnig interval in a multiple plane completion. The spacing interval at the top and bottom of the formation may vary somewhat without causing an appreciable error in the productivity calculation if the formation is reasonably thick and there are many horizontal planes of perforations. A special provision has been made to calculate the productivity ratios of wells with uneven spacing intervals, or for the case where a single plane of perfora-

Jan 1, 1967

By B. S. Norris, Charles R. Austin

IN a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000° C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallographic characteristics. The data, which related specifically to tempering temperatures of 550°, 650° and 710° C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650° C. to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at subeutectoid temperatures. 4. The node of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hr. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Determination of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000° and 850° C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938

By R. E. McNulty, R. D. Heidenreich, C. H. Gerould

TIIE electron microscope techniques and their application to magnesium alloys that are to be discussed in this paper are the result of research at The Dow Chemical Co. over the past three years. The view- point underlying the work is not wholly metallurgical, but has evolved through a variety of problems related to the physics and chemistry of surfaces. It can be said that the interest and stimulus were closely associated with a desire to employ effectively the electron microscope in research concerning the properties of solids as related to their physical structure. Only a portion of this work will be described here, and, consequently, many points of interest and debate are of necessity either only briefly recognized or are completely omitted. As has been pointed out by Desch,1 a great deal of the knowledge of the structure of metals has been obtained through microscopic studies of the surfaces of metallic specimens prepared in a particular manner. This information, when added to that obtained by means of thermal, electrical, X-ray, dilatometric and other methods, has been of great value both from a theoretical and a practical view- point. With the introduction of new instruments such as the electron diffraction camera and the electron microscope, it would be expected that still more information could be obtained. These two instruments have in many instances been very effective when directed toward the investigation of metallic surfaces, provided the proper methods of surface preparation were employed. Experience shows that the problems of surface preparation greatly limit the general application of these instruments to metallographic studies. It was found necessary to discard the standard metallographic procedures in applying the electron microscope to magnesium alloys and to work out new methods, which were required to satisfy certain conditions. These methods are unique to magnesium only in the specific chemical reactions occurring during etching. The presentation of the methods and results will be ordered as follows: I. Electron Microscopy of Surfaces. 2. Surface Preparation of Magnesium Alloys. 3. Discussion of Microstructures. a. Pure Magnesium and Single-crystal Studies. b. Types of Precipitation. c. Some Common Structures. d. Special Micrographs and Techniques. e. Structure of Mg-A1 Solid Solutions. 4. Correlation of "Fine Structure" with Corrosion Behavior of Magnesium Alloys.

Jan 1, 1946

By C. O. Burgess, W. D. Forgeng

DESPITE the increasing interest in and the technical importance of iron-chromium-manganese alloys, very little published information is available regarding their constitution. F. M. Becket&apos;s paper1 in 1930 represents the first correlated effort in the field of these alloys. The paper served particularly to draw attention to the commercial possibilities of iron-rich alloys containing chromium and manganese in balanced proportions. The duplex structure of alloys within the commercial range was briefly discussed, but exposition of their structural constitution was necessarily limited because the physical properties and corrosion resistance of the alloys were the main subjects of the paper. Both prior to and following the publication of F. M. Becket&apos;s paper, and at his instigation, an extensive investigation of the constitution of iron-chromium-manganese alloys of commercial purity was in progress at the Union Carbide and Carbon Research Laboratories, Inc. The present paper is based on the results of that investigation. In the last few years, investigations covering various portions of this alloy system have also been made in Europe. W. Koester briefly mentioned the effect of annealing on chromium-manganese steel2 and later3 constructed approximate sections of the iron-chromium-manganese equilibrium diagram. M. Schmidt and H. Legat14 even more recently studied this system, and their article and conclusions are of interest as representing an entirely independent study of a number of iron-chromium-manganese alloys. Koester&apos;s sections are shown in Fig. 1. The figures summarize the effect of manganese additions to iron alloys containing 5, 10, 15 and 20 per cent Cr as well as the effect of increasing chromium content on iron alloys containing 3, 8, 20 and 30 per cent Mn. These diagrams, within their composition limits, substantiated in some measure the results of our investigation. However, in our work some differences as regards the position of the mixed alpha-gamma fields were found as compared to Koester&apos;s work, and we were able to detect the presence of

Jan 1, 1938