Organization Place Date 1919 American Chemical Society Philadelphia, Pa. Sept. 2-6 National Assn. of Stationary Engineers Huntington, W. Va. Sept. 8 American Peat Society Minneapolis, Minn. Sept. 22-24 American Iron, Steel Electrical Engineers St. Louis, Mo. Sept. 22-26 American Institute of Min. and Met. Engineers. Chicago, Ill. Sept. 22-27 American Steel Treaters' Society, First Annual Convention Chicago Ill. Sept. 22-27 National Exposition of Chemical Industries.... Chicago, Ill. Sept. 22-27 National Safety Council Cleveland, O. Sept. 29-Oct. 2

Jan 8, 1919

By J. Spotts McDowell

Ackowledgments........................... 5 Introduction............................. 5 The Silica Minerals. Stability Relations......................... 6 Optical Properties........................ 9 Density.............................. 10 Melting Points....;..................... 10 Thermal Expansion..................,..... 10 Solubilities............................ 12 Identification of Cristobalite and Tridymite.............. 12. The Silica Refractories. Raw Materia1........................... 13 American Deposits....................... 13 Properties Determining Usability................ 15 Expansion on Heating..................... 16 Texture........................... 17 Silica Brick............................ 17 Manufacture........................... 18 Properties of Silica Brick .................... 19 Analysis ......................... 19 Density......................... 19 Porosity......................... 20 Strength....................... 21 Melting Point....................... 22 Specific Heat....................... 22 Thermal Conductivity................... 23 Expansion........................ 24 Effect of Rapid Temperature Change.........:... 26 Constitution......................... 26

Jan 1, 1918

By ALFRED T. BARR

In certain areas of the New Cornelia pit, considerable secondary blasting is necessary to reduce oversized boulders, formed from primary blasting, to pieces which will pass the 41/2-cu yd dippers on the shovels. Some of the boulders are 'dobied, but when time permits they are blockholed and blasted. In most instances one hole drilled to a depth of 2 to 3 ft and blasted with 1/3 to 1/2 of a stick of powder will break a boulder satisfactorily. Blockholing is normally done by using a jackhammer of the 55-lb class, 1-in. round drill steel, and detachable steel bits, 2-in. gauge when new. A bit change is usually made after the completion of each hole. The use of light drilling equipment in blockholing is desirable, both from the standpoint of safety and ease of doing the work, and when it was seen there was a possibility of using a lighter jackhammer through the use of tungsten-carbide bits and at the same time get at least the same drilling efficiency as with the standard equipment, it was decided to test tungsten-carbide bits. The claims for long life of the bits and footage drilled before resharpening gave hopes of eliminating much of the delay time in changing bits which is unavoidable with the use of steel bits. and thus gain in actual drilling time.

Jan 1, 1949

By H. J. Wasson

WITH the close of 1932 and the third year of the depression, the activity of oil production presents, amidst the general wreckage and chaos of industrial society, a somewhat unique picture of rationalized economic effort. East Texas still dominates the contemporary horizon, but it has become, at least for the time being, a definitely known factor. With its 9500 wells it is approximately 90 per cent drilled up. So long as production control obtains, it is merely one important factor of the national oil reserve. Each succeeding month of stabilized production tends to lull the industry's fears and the menace, both actual and psychological, of this giant field becomes ever more remote.

Jan 1, 1933

By AIME AIME

THE following paragraphs, constituting the concluding portion of the Annual Report of the Council for 1903, have been withheld from publication until now, in order to make them as accurate and complete as possible. They will be published in Volume XXXV. of the Transactions in their proper place at the end of the said Annual Report. Franklin Ballou was born in Pittsburg, Pa., May 29, 1845. He was the son of an old resident, Arthur Ballou, a manufacturer and wholesale dealer in vinegar. In early youth Franklin attended the Western University of Pittsburg, but left school at the age of 16 to become book-keeper for his father, upon whose retirement from business, in 1868, he associated himself with Walter C. Childs, of Pittsburg, in the manufac¬ture of furnace-grates and asbestos-cement for blast-furnaces. This firm was known as W. C. Childs & Co., and did a success¬ful business for several years. In 1869 Mr. Ballou married Miss May S. Wilson, daughter of Judge Wilson, of Lewistown, Pa. In 1876 he spent several months traveling in the West and studying the mining industry, which greatly interested him. In consequence of this journey, he wound up his business in Pittsburg and removed in 1877 to Georgetown, Colo., where for several years he conducted a sampling-works, and built up an extensive business as an agent for the sale of ores, besides engaging to some extent in mining enterprises. , It is said that he controlled at one time about one-eighth of the output of the Leadville mines. In the early 80's, he became Vice-President and General Manager of the Bimetallic Smelter at Leadville, of which Mr. David H. Moflat was the principal owner. This was practically the first successful demonstration of pyritic smelting in Colorado. Upon the sale of the works in 1897 to the American Smelting and Refining Co., Mr. Ballou retired

Jan 1, 1905

By W. T. Olsen, R. Ulcer

WHEN a liquid alloy freezes, the solid first formed usually differs widely in chemical composition from that last formed, so that there is segregation in the alloy as cast. For example in the copper-nickel system (fig. 1) the first solid formed from a liquid containing 55 atomic pct Cu may contain as little as 38 pct Cu, while the last must contain well over 55 pct. Three factors may act to decrease segregation from the maximum possible. 1. Diffusion in the cooling solid tends to make the phase homogeneous, decreasing segregation. This may be important at slow rates of cooling. 2. Segregation is impossible without diffusion in the liquid. At extremely rapid rates of cooling there may not be enough time to allow maximum segregation. 3. Supercooling delays nucleation to temperatures well below the liquidus thereby decreasing segregation. Hence the first nucleus in the copper-nickel system may contain well over 38 pct Cu. At sufficient supercooling the first nucleus may form below the solidus, in which case there is no reason to expect any segregation whatever. From these considerations, we could predict that at sufficiently low rates of cooling the alloy would be unsegregated because of factor 1 and at sufficiently high rates of cooling there should also be no segregation because of factors 2 and 3. Considerable segregation should occur only at intermediate rates of cooling. We have demonstrated experimentally that segregation can be completely suppressed by rapid rates of cooling. For the alloys studied, however, these rates are too great to be attained in any commercial practice. An alloy of 55 atomic pct Cu, 45 atomic pct Ni was frozen by cooling at varying rates. The degree of segregation in the solid was determined by X-ray diffraction photographs. Slow rates were obtained by slowly cooling the furnace containing the liquid alloy; fast rates by pouring or ejecting droplets of the alloy into water or iced sodium hydroxide solutions. The cooling rate of the droplets can be cal-culated from their dimensions by assuming reason- able values of thermal conductivity.' The experi-ments were repeated with an alloy of 16.5 pct Cu and 83.5 pct Au. A single experiment also showed a 50 atomic pct Bi-Sb alloy had no segregation at the most rapid quench. The position of back-reflection X-ray diffraction lines is a highly sensitive function of the lattice constant, which in turn depends on the chemical composition of the phase. A phase of varying composition will give broad diffraction lines. By measuring the edges of these lines and making suitable corrections for intrinsic line width, it is possible to determine the range of lattice constants represented. These can be converted to chemical compositions from a lattice constant vs. composition curve. Results are shown in table I. In the copper-nickel system the greatest segregation is found at the slowest cooling rates, where the lowest percentage of copper theoretically possible is found. In the copper-gold system, on the other hand, the degree of segregation is decidedly less at the slowest rates of cooling, being greatest at 11,100°C per sec. At no rate is the theoretically lowest percentage of copper (12 pct) found. At the rates of cooling found in sand and die castings the degree of segregation is large and depends little on the rate of cooling. Acknowledgment Most of the material in this paper is abstracted from a thesis presented by William T. Olsen, Jr. in 1948 in partial fulfillment of the requirements for the degree of Master of Science at the University of California.

Jan 1, 1951

By OWEN H. PERRY

One of man's primary tools is the ordinary screen. Whether of mesh or punched plate, it is fundamental in principle, primitive in its origin, and common in its application through all the world; and yet the screen goes only a part of the way toward the completion of its job of separating materials according to size. It will give a practical and continuous separation according to "size," as generally understood (accurate according to the breadth), but the accurate and continuous separation as to thickness is not a practical function of the screen. Still, all through history, the thickness of particles of material must have been important to many people; therefore, one would expect that some standard method of sizing for thickness would long since have been evolved and that equipment applying that method would be readily available to any in¬dustry. This, however, seems not to be so.

Jan 1, 1949

By Floyd C. Kelley

The literature of the last decade is rich with information relating to the cause and means of control of grain growth in pure metals, but is deficient concerning the role diffusion plays in grain growth, although during this period many new products that depend on diffusion for their properties and success have been developed. Among these are cementation products, produced by calorizing, chromizing, and carbonizing, or by mixing, pressing, and sintering powdered metals such as Syke's iron-molybdenum die material, Genelite, and Elcon Metal (copper, tungsten) etc. This is a fertile field for new developments, but before it can be utilized to the fullest extent there must be a thorough invest,igation of the processes by which diffusion and grain growth take place. Grain growth plays no small part in the process and certainly the physical properties of these products depend largely on the grain size and state of equilibtiuni produced. The field of investigation does not end here, but may be extended to the effect of diffusion on impurities, segregations and dendrites in the broad field of ferrous and non-ferrous metallurgy. A number of years ago the author investigated several of these cases and noted, with striking regularity, the pronounced effect of diffusion in promoting recrystallization and grain growth. An example of this phenomenon is given in his paper on chromizingl which contained photomicrographs of large radial or columnar crystals produced by diffusion of chromium in the solid state. Another manifestation of this effect was discussed by Austen,2 who showed the part hydrogen plays in the decarburization of steel and the effect of diffusion upon the grain structure. Diffusion of Metals in Iron It seems to be a general law, whenever two metals are brought into intimate contact at a temperature at which diffusion takes place, that a comparatively rapid, or abnormal, grain growth results. The grains

The problems confronting the development of Latin America's mineral resources have hinged largely on the political and economic climates-in short, the investment climate--existing and often changing in each nation. .The attractions and risks confronting today's investors in such mineral developments have been described and debated to considerable length during the past two decades, the arguments pro and con colored by the previous experiences incurred by the would-be investor, whether company or individual. In an effort to shed light on the investment climates existing today throughout Central and South America, the Council of Economics brought four experts together at the AIME Annual Meeting last March to give their views on this subject.

Jan 7, 1966

Mr. Tays (communication to the Secretary): Mr. Wynne's criticism of my paper* brings forward a few points which are really important, and might properly have been considered in the original paper. By calling attention to them he has rendered me a service. It is quite true, as Mr. Wynne says, that, in the tests reported by me, the Bryan mill was always working at a relative disadvantage, and my comparison of the work of this mill with that of the stamp-battery should be interpreted, therefore, so much the more favorably to the mill. Of course, wire screens can be used to advantage on the Bryan mill, if they are not of smaller size than 30-mesh; but

Jan 1, 1902

By W. R. Ingalls

In reviewing the history of the metallurgy of zinc, I shall pass hastily over what is only of antiquarian interest. That has been excellently treated by Dr. Bernhard Neumann in "Die Metalle" (1904) and has been described briefly in my "Production and Properties of Zinc" (1902), in my "Lead and Zinc in the United States " (1908), and in other metallurgical works of more or less the same date. In this present monograph, I have it in mind to confine myself mainly to technical practice, especially to that of the last 75 years, prior to which period advance was slow and of no great moment. The ancients made brass by the cementation process, i.e., embedding copper in a mixture of calamine and carbon and heating, whereby zinc oxide was reduced and zinc was vaporized and combined with the copper. Zinc was isolated by some of the alchemists, who named it and knew something of its properties, but made no use of it. Long before then, however, zinc was produced in India. Later it was produced in southern China. Possibly the Chinese obtained their knowledge from India. The Chinese in remote places still produce small quantities of zinc. I have seen photographs of their furnaces; or pots, for they hardly deserve the dignity of being called furnaces. I imagine that they are the same that were used centuries ago, for I cannot conceive of anything more primitive. Anyway, it is certain that the idea of a commercial production of zinc in Europe was imported from the Orient, where the metal was known in commerce as Speauter and Spiauter, whence speltrum and finally our term spelter. Tutanego and Tuteneague are other old names. Dr. Isaac Lawson went to China about 1730, expressly to discover the method of its production. What connection there was between Isaac Lawson and John Champion we do not know, but the latter obtained in 1739 a patent for a process of distillation downward and at some time between 1740 and 1743 erected a works at Bristol and actually began the manufacture of spelter. A production of 200 tons per annum is mentioned. In about the year 1766, Rishop Watson visited the Champion works and saw the process in operation, which previously had been

Jan 1, 1937

By H. M. St. John

THE melting department is the heart of the foundry. From it clean metal flows to the molding floor, in the right quantity, at the right time and at a sufficiently low cost-or, if not, the foundry fails to thrive. Since it is our purpose here to discuss present-day melting practice in the foundry, it may be well at the start to emphasize the wide differences in foundries and the conditions under which they must operate in order to reach the goal stated in the first paragraph. In every foundry, large or small, jobbing or captive, the same factors must be dealt with but they are of varying consequence and must be dealt with in varying ways in different foundries. Particularly in the nonferrous industry, there is so wide a variation in the composition of alloys used and in the character of castings made that no one type of furnace, nor any one method of operation, can be expected to produce the best results at all times. The present discussion will not attempt to include all nonferrous metals. It is intended to cover only the copper-base alloys in which copper is the dominant element, most of which are commonly known as brass or bronze. The discussion is further limited to the melting of these copper-base alloys for use in sand-casting foundries. Die-casting plants, the brass-rolling mills and certain other metal industries have melting problems peculiar to those industries, which will not be considered here. The following considerations are elemental in all foundries and are listed in what is believed to be the relative order of their present-day importance: I. The melting department must meet the foundry's requirement for dean, fluid metal, of specified composition and purity, at a temperature suitable for the work the foundry has in hand. This is the prime consideration in any foundry, at any time, anywhere. 2. Working conditions surrounding the melting furnaces and attending their use must be good. 3. The cost of molten metal at the mold must be as low as possible. 4. The operating characteristics of the furnaces must be sufficiently flexible, to meet normal variations in foundry requirements. 5. The operation and maintenance of the melting equipment must not require more skill and experience than is available in the particular foundry in question. METAL QUALITY It is not a function of the melting furnace to refine or improve the quality of the metal but simply to melt it without impairing its quality. Good practice requires, therefore, that care must be taken to supply the melting department with metal of inherently good quality, assured by specification or otherwise, having all the properties necessary to produce the castings desired. An alloy contains a number of primary elements, which must be present in definite proportions if the castings made from it are to have the desired properties. If the castings are made to a customer's specification, this will state the range within which these principal elements (for example, copper, tin, lead and zinc) are permitted to vary.

Jan 1, 1946

By Jack Green

Within three major tectonic time frames of earth history: Microplate (±3.8 - ±2.6 billion years), intraplate (±2.6 - ±1.3 b.y.), and macroplate (=1.3 b.y. - present), precious - metal deposits are confined to specific structural, depositional and physico-chemical environments. Precambrian primary gold deposits are localized in two microplate greenstone episodes (±3.7 and ±2.7 b.y.); secondary gold in Witwatersrand placers (±2.6 b.y.). Precambrian primary platinum group metals are in anorthositic facies of layered mafic intrusions (±2.8, ±1.8 and ±1.0 b.y.). Most radioisotope mineral dates cluster - at these times and are coincident with inflections on polar wandering curves. These coincidences may reflect episodicity in lunar tidal disruptions and global deceleration effects in crust and outer core during micro- and intra- plate phases. Macroplate tectonics and an oxygenated atmosphere created favorable conditions for strata-hosted and plate suture gold and silver deposits. "Black smokers" at constructive plate margins and calc-alkalic calderas at destructive plate margins are loci for hydrothermal gold and silver.

Jan 1, 1984

By Floyd C. Kelley

THE literature of the last decade is rich with information relating to the cause and means of control of grain growth in pure metals, but is deficient concerning the role diffusion plays in grain growth, although during this period many new products that depend on diffusion for their properties and success have been developed. Among these are cementation products, produced by calorizing, chromizing, and carbonizing, or by mixing, pressing, and sintering powdered metals such as Syke's iron-molybdenum die material, Genelite, and Elcon Metal (copper, tungsten) etc. This is a fertile field for new developments, but before it can be utilized to the fullest extent there must be a thorough investigation of the processes by which diffusion and grain growth take place. Grain growth plays no small part in the process and certainly the physical properties of these products depend largely on the grain size and state of equilibrium produced. The field of investigation does not end here, but may be extended to the effect of diffusion on impurities, segregations and dendrites in the broad field of ferrous and non-ferrous metallurgy. A number of years ago the author investigated several of these cases and noted, with striking regularity, the pronounced effect of diffusion in promoting recrystallization and grain growth. An example of this phenomenon is given in his paper on chromizing1 which contained photomicrographs of large radial or columnar crystals produced by diffusion of chromium in the solid state. Another manifestation of this effect was discussed by Austen,2 who showed the part hydrogen plays in the decarburization of steel and the effect of diffusion upon the grain structure. DIFFUSION OF METALS IN IRON It seems to be a general law, whenever two metals are brought into intimate contact at a temperature at which diffusion takes place, that a comparatively rapid, or abnormal, grain growth results. The grains

Jan 1, 1928

On the Art of Metallography (Howe Memorial Lecture), by F. F. Lucas; Beneficiation of Iron Ore. Abstract of paper by C. E. Williams followed by Round Table Discussion; A Statistical Analysis of Blast-furnace Data, by R. 8. McCaffery and R. G. Stephenson; Air Discharge of Circular Tuyeres, by R. S. McCaffery and D. E. Krause; Open-hearth Steel Process as a Problem in Chemical Kinetics. by E. R. Jette; Carbon-oxygen Equilibrium in Liquid Iron, by H. C. Vacher and E. H. Hamilton; A Thermodynamic Study of the Phasial Equilibria in the Bystem Iron-carbon (Abstract), by Yap, Chu-Phay; Influence of Dissolved Carbide on the Equilibria of the System Iron-carbon (Abstract), by Yap, Chu-Phay; Inclusions and Their Effect on Impact Strength of Steel, I and 11, by A. B. Kinzel and W. Crafts: Method for Electrolytic Extraction of MnO, MnS, FeS and Si02, Inclusions from Plain Carbon Steels, by G. R. Fitterer; Permanent Growth of Gray Cast Iron, by W. E. Remmers; Some Notes on Blue Brittleness, by L. R. van Wert; Austenite-pearlite Transformation and the Transition Constituents, by A. Sauveur; Age-hardening of Austenite, by F. R. Hensel; Transformational Characteristics of Iron-manganese Alloys, by H. Scott; Composition Limits of the Alpha-gamma Loop in the Iron-tungsten System, by W. P. Sykes; Magnetic Properties Versus AUotropic Transformations of Iron Alloys, by T. D. Yensen and N. A. Ziegler; Dilatometric Study of Chrome-nickel-iron Alloys, by V. N. Krivobok and M. Gensamer; Low-carbon Steel, by H. B. Pulsifer; Bright Annealing of Steels in Hydrogen, by F. C. KeUey; Development of Continuous Gas Carburieing, by R. J. Cowan. Transactions, Institute of Metals Division, 1931. 500 pages. Index. Papers and discussions presented before the Division at Chicago, Sept. 22-26, 1930 and New York, Feb. 16-19, 1931. X-ray MetallograpIhy: X-ray Determination of Alloy Equilibrium Diagrams (Annual Lecture), by A. F. Westgren; Suppressed Constitutional Changes in Alloys. by G. Sachs; Texture of Metals after Cold Deformation; by F. Wever. Theoretical Metallurgy: Studies upon the Widmanatitten Structure. I.—Introduction. The Aluminum-eilver System and the Copper-silicon System; by R. F. Mehl and C. S. Barrett; Studies upon the Widmanstatten Structure, 11.—The Beta Copper-einc Alloys and the Beta Copper-alumnum Alloys, by R. F. Mehl and 0. T. Mareke; Application of X-rays in the Manufacture of Telephone Apparatus, by M. Baeyerts; Thermal Conductivity of Copper Alloys. 11.—Copper-tin Alloys; 111.—Copper-phosphorus Alloys, by Cyril Stanley Smith; Thermodynamic Study of the Equilibria of the Systems Antimony-bismuth and Antimony-lead, by Yap, Chu-Phay. Ganeral: Cemented Tungsten Carbide; a Study of the Action of the Cementing Material, by L. L. Wyman and F. C. Kelley; Influence of Casting Practice on Physical Properties of Die Castings, by C. Pack; Fabrication of the Platinum Metals, by C. S. Sivil; Effect of Certain Alloying Elements on Structure and Hardness of Aluminum Bronze, by 9. F. Hermann and F. T. Sisco. The WorkinG oF Metals: Metal Working in Power Presses, by E. V. Crane; Forming Properties of Thin Sheets of Some Nonferrous Metals, by W. A. Straw, M. D. Helfrick and C. R. Fischrupp; Die Pressing of Braas and Copper Alloys, by J. R. Freeman. Jr.; Plasticity of Copper-sina Alloys at Elevated Temperatures. by A. Morris: Directional Properties in Cold-rolled and Annealed Copper, by A. Phillips and E. 9. Bunn; Effect of Combinations of Strain and Heat Treatment on Properties of Some Age-hardening Copper Alloys by W. C. Ellis and E. E. Schumacher; Constituents of Aluminum-iron-silicon Alloys, by W, L. Fink and K. R. Van Horn; Equilibrium Relations in Aluminum-antimony Alloys of High Purity, by E. H. Dix, Jr., F. KeUer and L. A. Willey; Equilibrium Relations in Aluminum-magnesium Silicide Alloys of High Purity, by E. H. Dix. Jr., F. Keller and R. W. Graham; Constitution of High-purity Aluminum-titanium Alloys, by W. L. Fink, K. R. Van Horn and P. M. Budge; Experiments on Retarding the Age-hardening of Duralumin, by E. H. Dix. Jr. and F. KeUer; Aluminum-silicon-magnesium Casting Alloys, by R. S. Archer and L. W. Kempf; Modulurr of Elasticity of Aluminum Alloys, by R. L. Templin and D. A. Paul; Quenching of Alclad Sheet in Oil, by H. C. Knerr.

Jan 1, 1931

By H. J. Rose

SIXTY-FIVE million net tons of coal were carbonized in the by-product and beehive coke ovens1 of the United States during 1924. This tonnage represented 13.4 per cent. of the bituminous coal which was mined in that year. Table 1 shows production and disposition.2 TABLE 1.-Production and Disposition of Oven Coke in 1924 BY-PRODUCT BEEHIVE TOTAL Coal charged into ovens, tons 49,061,339 15,914,310 64,975,649 Coke produced (exclusive of screenings and breeze), tons 33,983,568 10,286;037 44,269,605 Average yield of coke, per cent 69.3 61.6 68.1 Disposition of coke: PER PER PER CENT. CENT. CENT. Blast furnace 82.5 82.8 82.6 Foundry 4.6 13.3 6.6 Domestic 8.3 1.4 6.7 Water gas manufacture and all other uses 4.6 2.5 4.1 Cokes having somewhat different combinations of chemical and physical properties are desired for the various uses listed above, and these properties depend primarily upon the types of coal used. American coals have a wide range of purity and coking quality, and the chief subject of this paper will be the selection of coals for the manufacture of blast furnace, foundry, domestic, and water-gas coke, in by-product coke ovens. It will obviously be necessary to include a discussion of those physical and chemical characteristics that are generally considered essential or desirable for each type of coke.

Jan 7, 1926

By P. Pietrokowsky

lntermediate phases in the binary metal alloy systems Ti-Zn, Ti-Hg, Zr-Zn, Zr-Cd, and Zr-Hg have been investigated by X-ray powder diffraction methods. Gamma-TiBHg and Zr3Hg have a beta tungsten structure; TiHg and ZrHg are analogous to ordered AuCu (L l0 type); delta-TixHg and ZrHg, are isomorphous with ordered AuCu,, (L l2 type); ZrZnz is face-centered cubic (C 15 type); TiZna crystallizes in a C 14 type structure; and Zrll-, occurs in cubic and tetragonal modifications in which a random distribution of atoms exists. Additional information for the intermediate phase TiZn, is presented. THE physical metallurgy of titanium and zir-conium when alloyed with elements in subgroup 11-B of the periodic table has received comparatively little attention in the literature. Laves and Wallbaum' reported the existence of several intermediate phases in the system Ti-Zn. They identified TiZn as a CsCl (B 2) structure and described TiZn, as an ordered Cu,Au (L 1, type) crystal structure. Gebhardt' investigated very limited zinc-rich regions in the systems Ti-Zn and Zr-Zn. Phase relationships in these partial constitution diagrams were deduced from the results of thermal analysis and metallography, X-ray results being inconclusive. The first zinc-rich intermediate phase in either system was not identified. More recently, Anderson, Boyle, and Ramsey" have had occasion to refer to a partial Ti-Zn phase diagram (unpublished data) covering the region 0 to 10 atomic pct Ti, wherein two intermediate phases corresponding approximately to TiZn,, and TiZn,, were indicated. The metals used in this investigation and typical analyses as determined by the suppliers are given in Table I. The iodide-process zirconium which was used was not hafnium free. Experimental Methods Alloy Preparation: The relative ease with which titanium and zirconium combine with other elements places extensive restrictions on the methods by which alloying can be achieved. The direct current electric arc melting procedure was found to be unsatisfactory for preparing these binary alloys and for this reason solid state diffusion methods were utilized. The iodide process titanium and zirconium rods were filed by hand. Fines were subjected to a magnetic separation and classified as to size as either finer than 200 mesh or coarser than 200 but finer than 80 mesh. Powder mixtures of various binary combinations of titanium and zirconium with zinc and cadmium were compacted in a 12 mm diameter die and then placed in Vycor or quartz vials which were evacuated and sealed. The mercury alloys were prepared in a similar manner; the proper weight of liquid mercury being placed in a vial with minus 200 mesh titanium or zirconium. These ampoules were then heat treated at various temperatures and times depending on the characteristics of the particular alloy system. Upon completion of the heat treatment the ampoules were cooled rapidly and the specimens weighed. The loss in weight varied from 1 to 3 pct (except as noted in the text) and for this reason the calculated compositions were accepted as a fair measure of the actual alloy compositions. X-Ray Dif raction Techniques: Powder diffraction experiments were conducted at room temperature with a 143.2 mm Debye-Scherrer X-ray camera in which the film was placed in the Straumanis arrangement. When copper radiation was used, a nickel filter was employed, and for the cobalt target a filter of iron oxide was used. In both cases, the /i? filter was placed between the X-ray target and the powder specimen which was mounted on a glass fiber. The lack of information based on optical metallography placed reliance on the results obtained from the X-ray experiments for determination of

Jan 1, 1955

By H. C. Jennison

Two distinct types of defects occur at times in copper wire as a result of the use of dies of improper design or undesirable wire-drawing practice. The conditions under which these defects may be produced, as well as precautions to be taken in order to prevent them, have been known to The American Brass Co. for many years. The quality of the copper wire bars and rods has too often and unjustly been held responsible for these particular defects and it is to correct any such belief that this paper is presented. An extremely high quality of electrolytic copper has been supplied to the trade by all refineries for the last 20 years at least. The purity of the copper would average well above 99.900 per cent. The casting of the wire bars has been handled in a generally satisfactory manner. The bars have been cast sound, with a flat to slightly crowning set and have been free from sloppy edges, cold sets, etc. In other words, the wire bars have met A. S. T. M. specifications and have been generally satisfactory. For the most part, they have been everything that could be desired from a quality standpoint yet most of the wire mills in this country and in Europe have at times held the quality of the copper responsible for the two types of defects described in this paper. As a matter of fact, these defects are produced entirely in the wire mills. The author has visited many of the large wire mills in the United States and in Europe to investigate these defects. In some cases the trouble has been so serious that the wire mill has ceased operations. At times the wire mills are reluctant to believe that they are responsible for the defective product. The effect of die design, wire-drawing practice, etc., upon the quality of copper wire has received little study on the part of wire mills, particularly those that have commenced operations in the last few years. Two Types of Defects One type of defect is generally known in this country as "check marks;" in Europe it is termed "crowfeet" (Fig. 1). This defect occurs in the surface of the copper wire, in the form of V's, which are always

Jan 1, 1930

By B. L. Landrum, P. B. Crawford

The rise of a new laboratory model for studying tran-sient fluid flow problems, is described. The theory of he model is based on the analogy between the equa-ions which describe the flow of compressible fluids in porous media and the conduction of heal m solids. The "thermal model" is used to study the Iransient Pressure distributions during fluid displacement in five Standard well patterns. The studies indicate quantita-ively how die pressures change with lane at any poit in the reservoir. It was found that, in general, the equipressure contours are more radial about the wells early in the program than after steady-state conditions are established. In addition two studies of fractured five-spot patterns are presented to illustrate the opplicability of the model for a wide range of reservoir conditions. INTRODUCTION In reviewing the oil recovery techniques involving fluid displacement it was found that a very considerable quantity, if not all of the fluid within the pattern, mav be displaced (during a time-dependent or transient period rather than the usually applied steady-state conditions. Since the oil is displaced during a transient period, it was believed desirable to study the nature of the transients for several of the commonly used fluid displacement patterns. A literature review indicated fairly complete studies of the streamlines and isopotentials for steady-state: yet few data were available on the transient displacement process. Several simulated steady-state multiwell displacement programs were carefully mapped by Foster and Lodge on an electrical conducting sheet as early as 1875, hut the more recent work of Muskat provides the best source for steady-state phenomena having direct petroleum production applications. In order to study the transient phenomena a new lab-oratory model was developed which is based on the similarity of the equations that describe the flow of fluids and the conduction of heal. The equations describing heat flow were developed early in the nineteenth century. Regorous solutions tor most transient problems are in gcneral complex and usually limited to fairly restricted houndary conditions.2 the thermal model may be used to obtain approximate solutions for many transient problems without some of the restrictions required for analytical solution. The application of the analogy between heat conduc-. tion in solids. electrical flow and fluid flow, in a porous media has long been recognised. Techniques originally developed for the solution of heat conduction prol?lems have in many instances proved useful in ohtaining solutions to fluid flow prohlcms. Ir is not surpri5ing then that a heat conduction or thermal model might bf usefull in sludying transient fluid flow. As an example ol the problems suitable for the study with the thermal model, transient pressure distributions during fluid displacement programs are studied for the five-spot, line-drive, staggered line-diibe. seven-spot 211 two fractured patterns. A model was constructed of an iron plate of geometry similar to the reservoir patterns under study. The principle of mirror images as suggested by Bryan was employed in shaping the model. A temperature differential was obtained by soldering two sections of copper tubing to the plate at points analogous to the well location in the field. Hot and cold water was passed through the tubing. The temperature distribution, analogous to the pressure distribution in the field. was obtained a a function of time from thermocouplcs distributed over the plate.

By W. P. Sykes

ThiS investigation was undertaken primarily to establish the relations existing between temperature and mechanical properties in molybdenum, nickel, and an aluminum-copper alloy. Mlolybdenutn (m.p. 2500" C.) was chosen because it is partly similar to tungsten and partly similar to the common ductile metals. Also it is known to furnish, by proper treatment, a desirable material to use in studying relation of grain size and physical properties. The molybdenum used was of the quality that is drawn into wire 0.003 in. in diameter for use as filament supports in incandescent lamps; Chemical analysis shows less than 0.1 per cent. of impurities. Nickel belongs to the same class as iron. Its melting point is 1450" C. and an allotropic change at about 370" C. results in a loss of magnetism above that temperature. This feature made nickel doubly valuable for the purposes of these tests. The nickel used was obtained from the Driver-Harris Co. as 0.090 in. (2.3-mm.) wire, annealed; analysis showed 99.8 per cent. nickel and 0.150 per ccnt. iron. Aluminum is one of the low melting-point metals. Some tensile tests at clevated temperatures have been reported by Bengough but the possibility of learning more with the low temperature and sensitive apparatus available rccommendcd this metal. The samples marked A1 arc an aluminum-copper alloy that contains 3 per cent. copper, 0.42 per cent. iron, and 0.21 per cent. silicon. The presence of the copper somewhat coniplicates the analysis of the results; but the action of copper in aluminum has been studied so that its influence might have been foretold, in part at least. The material and analyses were furnished by the Aluminum Castings Co. The nickel wire, which was deformed at 400" C., was drawn under a bath of molten lead and through a die, which also was immersed in the bath. A thermocouple was suspended in the molten metal to indicate the temperature. Hot oil was uscd as the heating bath for drawing the

Jan 1, 1921