Search Documents

By Zhaohui Xie, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

A high carbon low-grade gold ore, in which gold mainly occurs in carbonaceous matters, is a typical refractory gold ore whose conventional cyanide leaching extraction is only 12.9 %. In this paper, by the process of flotation-roasting-leaching, gold was effectively enriched and extracted. The flotation results showed that the enrichment ratio of gold was relevant to that of carbon, indicating that gold occurred in close association with carbon. A concentrate containing gold 7.26 g/t and carbon 12.37 % was obtained, with gold recovery 83.10 % and carbon recovery 90.24 %. Subsequently, the roasting of flotation concentrate favorably made the removal rates of carbon and sulfur reach 99.81% and 98.79%, respectively. After roasting, the gold in the roasted product was further enriched to 29.70 g/t and the optimal gold cyanide leaching extraction reached 93.66%.

Jan 1, 2015

By Peng Lv, Shiqian Liu, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

The treatment process of a low-grade refractory gold ore containing sulfide minerals and carbonaceous matters was studied in this work. The gold extraction of this ore by all-sliming cyanidation was only 11.75%. Hence, a pretreatment was necessary. In this paper, a flotation-preoxidation-cyanide leaching process was developed. The concentrate from the flotation procedure was processed using different preoxidation methods. A concentrate containing 34.08g/t of gold with the gold recovery ratio of 81.20% was obtained by flotation. After roasting, microwave heating or alkaline pressure oxidation, the gold cyanidation ratio reached 82.37%, 81.26% and 71.09% respectively. Roasting was an effective, reliable and mature technique to oxidize sulfide minerals and carbonaceous matters. Roasting and microwave heating both produced dangerous environmental pollutants while alkaline pressure oxidation was eco-friendly.

Jan 1, 2015

By H. H. Kellogg

The thermochemical properties of molten solutions in the binaries Cu-Bi, Cu-Sb and Bi-Sb, as well as the ternary Cu-Bi-Sb, have been correlated and described in mathematical form by use of the associated species concept combined with the three-suffix Margules equations to account for the non-idea 1 behavior of the solution species. Agreement of the correlations with experimental data is excellent (relative deviation of less than 2.5% in the values of the activity coefficients) in most cases. The correlations are applicable over the entire composition range of each system, and in the temperature range 700°-1250°C.

Jan 1, 1985

By Rainer Schmid-Fetzer

"Isothermal solidification can be used to form strong bonds at low temperature which remain solid at much higher temperatures. The exploitation of this principally known technique for new high temperature processing steps and applications in electronic assemblies is the aim of this study. Three basically different variants of this bonding process are given. A comprehensive metallurgical screening is performed and the feasibility of binary material systems is given on a quantitative scale. Very attractive systems are spotted that have never been studied before. Detailed examples for the realization of bonding with complex ternary and multilayer systems are given. A highly innovative example is the chip stack or wafer to wafer bonding of unmetallized Si or SiC at 250°C. The proposed bond remains stable above the melting point of Si and enables entirely new semiconductor manufacturing steps. An improved die bonding process was proposed and verified experimentally.1. IntroductionIsothermal solidification can be applied to form strong bonds at relatively low temperature which remain solid at higher temperatures. The general principle of this type of joining processes is illustrated in Fig. 1. An interlayer of a low melting component, Lo, is provided as a foil or a thin film coating between the high melting joint components, Hi. The assembly is heated under moderate pressure to the bonding temperature, T 8 , and a liquid filler forms, either because the melting point of Lo is exceeded or due to a eutectic reaction between Lo and Hi. This molten filler initiates a rapid interdiffusion or reaction diffusion between Lo and Hi and the subsequent approach to an equilibrium state results in isothermal solidification. The solid phases formed at T 8 in the joint region exhibit a remelt temperature above T8 •"

Jan 1, 1996

By R. T. Seaman

Pressure oxidative treatment of whole ores and/or mineral concentrates is used to leach or liberate metals of value for downstream recovery. Silver, when present, is often lost in processing, precipitating as a cyanide-insoluble jarosite in the residue. Depending on pressure oxidation conditions, the degree of silver loss to jarosite can vary dramatically. Batch bench-scale testwork is often performed to define that loss, and then assess the implications in continuous operations. This paper focusses specifically on the impact of CESL pressure oxidation conditions on silver recovery, and discusses limitations of batch bench-scale testing as well as means of overcoming these limitations to better predict silver recovery in the scale up from bench-scale to continuous operations. Since silver is only partially soluble in both sulphate and chloride media, it will gradually leach and deport to a jarosite as oxidation progresses. When a silver-insoluble anion, for example iodide, is dosed prior to oxidation, there is a marked improvement in silver recovery from batchgenerated residue; however, that benefit is not consistently seen in continuous operations. The difference has been attributed to the dynamic solution conditions in the batch test, specifically the first few moments of oxidation. Using these principles, a predictive correlation has been established between initial leach concentrations of iron and acid and ultimate silver recovery with iodide addition.

By O. Norman Lotter

The formulation and use of mixed collector suites in sulphide flotation can be traced back as far as 1957 with the work of Glembottskii and his co-workers in Moscow. The subject was reviewed by Lotter and Bradshaw in 2010, and proposed a synergy between ideally-selected different reagent types to deliver improved performance, in particular the in situ catalysis of a xanthate to dixanthogen by a dithiocarbamate. Correctly formulated for a particular application, an optimally arranged mixed collector suite delivers the following improvements to the flotation process: • An increase in the flotation kinetics • Improvement in coarse, or middling, particle recovery • Reduction in total dosage requirement • Best results are found from testing the ratios of the collectors. This is of critical importance. In all an optimally formulated mixed collector system usually delivers an increase in paymetals recovery of 1–4% absolute, with a gain in concentrate grade in the range 10–20% relative. In recent years, the addition of semi-conductor theory and associated electrochemistry has contributed significantly to this toolbox by way of identifying optimum domains of Eh and pH for the flotation of individual minerals. In the case of mixtures of minerals, this is where the mixed collector system delivers significant value by way of presenting a mixed set of collector radicals and dimers in a common Eh and pH domain for overall performance. This calls on a fundamental understanding of organic chemistry, mineralogy, semiconductor theory, and electrochemistry. Whereas the selection of grinding media type effectively influences the Eh, the pH can be easily controlled by pH modifiers. The theory of this system, and some industrial case studies, are discussed.

By Sunil G. Warrier

A rapid infrared forming technique has been developed to fabricate titanium matrix composites. This technique applies infrared heating to infiltrate titanium alloys into carbon and silicon carbide prepregs. The entire process typically takes 1-2 minutes in an inert atmosphere. The advantages of this technique are that the process is fast, simple, does not require a vacuum or a high external pressure. The process is very economical both in energy conservation and operation costs. This technique has been used to produce void free composites with limited, well controlled fiber-matrix reactions and mechanical properties comparable to currently available titanium matrix composites.

Jan 1, 1993

By C. P. Broadbent

The process metallurgy of many nickel laterite smelting operations is controlled largely by the physical chemistry of the slag system. Consequently, accurate phase diagram information and physicochemical property data are essential to interpret and predict the behaviour and optimisation of the overall process. The system (SiO2 - MgO - FeO) first described by Bowen et al. between 1914 and 1935 and the system (SiO2 - MgO - FeO - Fe2O3) determined by Muan and Osborne in 1956 are of particular relevance to the study of nickel laterite smelting slags as these systems form a reasonable approximation of many industrial slags. This paper will review the literature for these (and other relevant) phase systems. In addition data available from the ternary and (quasi)ternary phase diagrams will be compared with data obtained from industrial slags. The physico-chemical properties under consideration will include; melting and crystallisation behaviour (solidus and liquidus temperatures), viscosity - temperature relationships, heat flux considerations, electrical conductivity, surface and interfacial tension.

Jan 1, 1993

By M. Friák, L. G. Wang, M. Šob, V. Vitek

"The paper gives an account of applications of quantum-mechanical (first-principles) electronic structure calculations to the problem of theoretical tensile strength in metals and intermetallics. First, we briefly describe the way of simulating the tensile test and the electronic structure calculational method. Our approach is then illustrated on calculations of theoretical tensile strength in W, NiAl and transition metal disilicides MoSi2 and WSi2 with C11b structure. In Wand NiAl, we consider uniaxial tension along [001] and [111] directions. Although tungsten is elastically nearly isotropic (C44 = C”), theoretical tensile strength exhibits a marked anisotropy (oth/001 = 29 GPa, o'th/111 = 40 GPa). Calculated results compare favorably with experimental value of 24.7±3.6 GPa obtained for tungsten whiskers grown along the [110] direction. Similarly, in NiAl, the 'hard' orientation [001] differs very significantly from the [ill] orientation (oth/001 = 46 GPa, oth/111 = 25 GPa). This anisotropy is explained in terms of higher-symmetry structures present or absent on the calculated deformation paths. In disilicides, the theoretical strength is calculated for [001] loading (oth/001 = 37 GPa and 38 GPa for MoSi2 and WSi2 , respectively). The role of relaxation of internal structure parameter is discussed and changes in bonding conditions during the tensile test are analyzed.IntroductionIn most engineering applications, the strength of materials is limited by the presence of internal defects. If there were no defects, then, for example, the tensile strength could be several orders of magnitude higher and its value would be comparable with that of shear modulus. Therefore, the strength of ideal (defect-free) crystal represents an upper limit of attainable stresses, which is called the ideal strength. While it may not be possible to achieve the ideal strength in practice, it is not possible to exceed it. However, the ideal strength is already approached in situations which are technologically relevant. These include the low-temperature deformation of inherently strong materials, such as diamond, Si, Ge and some of the transition-metal carbonitrides, deformation of whiskers, nanoindentation of materials with low defect densities, hardened thin films and coatings etc. The ideal strength sets the limits of elastic stability of a solid. Its knowledge is useful for estimation of the ideal work of fracture stresses needed for homogeneous nucleation of dislocations and for modelling of crack propagation."

Jan 1, 2001

Several processes are now available for the recovery of free and WAD cyanide from gold plant solutions and pulps. In the past, the incentive for evaluating cyanide recovery in gold plant flowsheets has been economic. In many cases, it has been possible to demonstrate (at least in the laboratory and on paper), an improvement in process economics by; (i) reducing the costs of tailings detoxification, (ii) recycling cyanide at lower cost than the purchase/delivery price of new cyanide, and (iii) generating additional revenue via by¬product sales. Despite these convincing arguments, few cyanide recovery plants have been built at operating gold mines. Also, there is arguably an even more compelling reason for mining companies to consider cyanide recycling. With the growing storm of negative public opinion that the use of cyanide in the mining industry is attracting - following several highly publicized spills over the last couple of years - the time has come for the gold industry to demonstrate environmental diligence and stewardship in the use of this commodity that is so vital for their industry. There is no doubt that the widespread implementation of cyanide recycling will reduce the impact of the cyanidation process on the environment, both by reducing the risk of spills (with less cyanide being transported from manufacturing plants to gold mines), and by reducing the loading of toxic and non-toxic metals and ions in the tailings. In this paper, the various processes that are available for cyanide recovery are discussed, along with the process chemistry. Results of several laboratory and pilot plant trials that have been conducted over the last few years are also presented.

Jan 1, 1998

By Mingming Zhang, Marshall S. Coe, Marcelo W. Andrade

To supply iron units and flux burden in blast furnaces, sinter basicity is one of the vital parameters for sinter plants. The sinter basicity also plays an important role in sinter quality since it imparts the formation of different mineral phases in sinter. Pot-grate sintering tests were carried out with low and high basicity to investigate the effects of sinter basicity on sinter mineralogy, properties and productivity. It was found that with an increase in sinter basicity, both sinter productivity and reducibility (RI) increased. Tumbler index (TI) and low temperature degradation index (LTD) of high basicity sinter were comparable to low basicity sinter. Softening and melting tests showed that sinter with 3.5 C/S basicity had slightly higher softening temperature comparing to lower basicity sinter with C/S 2.6, acid and fluxed pellets. XRD analyses confirmed the formation of silico-ferrite of calcium and alumina (SFCA) and calcium ferrite (CF) in the tested sinter samples.

Jan 1, 2015

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn't favor the economic metals' recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By Zhonglin Ye, Yifeng Shi

"This paper has outlined forms of Au & Ag losses in copper smelting process and methods for increasing Au & Ag recovery, analyzed factors influencing Au & Ag recovery in copper converting process, presented Au & Ag behavior in copper electrorefining process, and reviewed effect of current density/electrolyte circulation rate during electrolysis and surface finish of cathode on Au & Ag losses. Measures and research direction for decreasing Au & Ag losses in electrolysis have also been introduced. Based on Au & Ag behavior in copper electrorefining process and previous studies by others, new approach for increasing Au & Ag recovery in copper smelter has been discussed. And brief comparison has made between continued multiplication method and equilibrium method application in the case of calculation of Au & Ag recovery in copper smelter.IntroductionAs gold and silver are the major by-products from copper smelting process, efficient Au & Ag recovery has become one of the key approaches for copper producers to increase economic efficiency. With similar physicochemical properties, Cu, Au and Ag belong to the first subgroup of elements in the same periodic table. Au and Ag will be enriched into Cu phase firstly when both matte-slag phase and copper-matte phase appear in copper smelting process. However, great changes have taken place in Au & Ag proportions into individual phase due to changes of physicochemical conditions in each smelting process. Metallurgists at home and abroad have carried out a great deal of pilot plant tests and laboratory tests in order to increase Au & Ag the former Soviet Union with regard to Au & Ag losses in copper smelting process in the 1970s and 1980s, and he proposed solutions to increase Au & Ag recovery in copper metallurgical plants. As more than 20 years passed, Jingchun Lu's paper, Discussion on Increasing Au & Ag Recovery in Copper Smelting System, remains as a literature of the most comprehensive study. Based on Jingchun Lu's literature, the authors of this paper discussed new approaches to increase Au & Ag recovery in copper metallurgical plants with combination of many researches done by other researchers for over 20 years."

Jan 1, 2013

By Ivan Imris

The iron production has generated many tonnes of very fine residues with high concentration of iron. In addition, during the recycling of galvanised steel scrap in the steel making processes the zinc and lead are largely concentrated in the dust. These kinds of dusts are usually dumped beside the metallurgical plants and cause environmental problems. Therefore the metal recovery from the metallurgical residues has become a major interest not only from the viewpoint of metals recycling but mainly from the viewpoint of environmental land protection. The thermodynamic analyses and laboratory experiments suggested that the metals could be recovered from metallurgical wastes by reduction roasting and by plasma smelting processes. The iron rich pellets with very high metallization may be obtained from metallurgical wastes by the reduction roasting and the inert slag and pig iron could be produced by plasma smelting processes. In both cases the iron rich products are suitable for the steel production. During the reduction roasting or plasma smelting the high volatile zinc and lead metals were removed and enriched as a secondary dust, Zn-Pb concentrate, which is suitable for processing in zinc and lead smelters. Suggested processes are commercially feasible and environmentally friendly without any solid or liquid waste.

Jan 1, 2003

By Zvi Rivlin

Classical nucleation theory states that in first order phase transformations, such as liquid to solid transition, nucleation of the product phase starts with the formation of small, unstable clusters (embryos). When the thermodynamic barrier to nucleation is overcome, the embryos grow and attain a critical size, beyond which they are stable, i.e. they become nuclei. If nucle- ation does not occur, the parent, liquid phase remains in metastable equilibrium. At temperature lowers, undercooling increase and atomic mobility decreases. The viscosity change in the undercooled liquid may result in the formation of glassy state. As demonstrated in previous papers [I-21, in solidification involving surface nucleation of the product phase, as the case is in rapid quenching by melt-spinning, both nucleation temperature and nucleation time depend upon the number of atoms available at the isothermal surface in contact with the substrate. As a result of the thinness of the melt-spun ribbons, the embryo clusters that form at the freezing temperature may not be supplied by the amount of atoms necessary for their growth to critical nuclei sizes. In such extreme conditions, the liquid does not crystallize, it forms a metallic glass. A numerical simulation method is proposed for the reactions involved in embryo cluster formation and growth, at the atomic level. The simulation enables the caIcuIation of either the nucleation or the glass transition temperatures. Calculations made for the well-known glass forming CuZr and FeB systems afford prediction of the geometrical and thermodynamically conditions necessary for the formation of either crystalline or amorphous ribbons in melt-spun ribbons.

Jan 1, 1994

By H. D. Freeman

The occurrence of gold in refractory gold ores varies widely and affects the recovery process. The determination of gold and the composition of the associated minerals are important in selecting an appropriate processing scheme. However, locating the gold in an ore sample is a difficult task which requires perseverance, luck, and experience. Our experience has led to the development of a relatively fast and reliable means of deter-mining the mineralogy of ore samples through analysis combining an energy-dispersive x-ray analyser coupled to a scanning electron microscope (SEM). In some cases, a wave length dispersive spectrometer or microprobe is used to further quantify the various mineral compositions. The SEM/microprobe analysis identifies the source of problems that may arise during the recovery of gold from refractory gold ores.

Jan 1, 1981

By Michael S. Moats, Scott C. Campin, J. Brent Hiskey

"Electrochemical techniques are a valuable means of analyzing the passivation of commercial copper anodes. Electrochemical impedance spectroscopy (EIS) provides information concerning transport and reaction phenomena occurring at an electrode surface. Commercial. copper anodes of varying compositions have been examined using EIS. Experiments were conducted in a flat cell with an electrolyte of 40 gil Cu2 + and 160 gil H2S04 maintained at 65 DC. Impedance spectra were obtained at the potentials characteristic of the open circuit voltage and passive region for each anode. The spectra of the passivating films exhibited a flattened resistive/capacitive loop at middle to high frequencies and an inductive loop at low frequencies. An equivalent· circuit utilizing an inductor-resistor series in parallel with the double layer capacitance and charge transfer resistance was adequate in modeling the impedance data. The influence of anodes impurities on the components of the equivalent circuit is discussed and correlated with a hi-layer passivation model.IntroductionPassivation of copper anodes during industrial electrorefining has received considerable attention in the past few decades. Great strides have been made in understanding the roles of anode impurities [1-25], electrolysis parameters [20,26], and electrolyte chemistries [20,26]. Even so, passivation still occurs even in the most modem of refineries. The exact cause of passivation is not fully understood. It is known that the anode surface becomes covered by a passivating film. This film has been proposed to be CuS04'&5H20, Cu20, or mixed oxides. The localized concentrations of Ft, Cu+, and Cu2+ ions determines which phase is more favorable. The presence of these ions is controlled by the reaction kinetics and diffusion of species through the slimes layer.Reaction kinetics between Cu, Cu +, and Cu2+ are based on the dissolution mechanism of copper. There exists four different models to describe the dissolution of pure copper. The classical model of Mattsson and Bockris [27] involves two single electron transfers with the cuprous-cupric reaction being the rate detennining step. More recently, Wong, Collier, and MacFarlane [28] used ac impedance to elucidate a more complex mechanism involving the affect of pH and anions. Their findings indicate that the formation of cuprous ions in solution, Cu(I)so~ is favored over Cu(1I) ions adsorbed to the electrode surface in the presence of sulfate and as pH increases from pH 1 to pH 5."

Jan 1, 1997

By Randall M. Gennan

Generally sintering is focused on the bonding of particles at high temperatures; possibly with simultaneous densification. However, an important aspect of sintering occurs during heating at relatively low temperatures where polymer processing aids are removed via control of the atmosphere, heating rate, or hold time at intennediate temperatures. New insights into burnout processes show impact from the polymenype, particle size, amount of polymer, atmosphere, part geometry, and thermal profile. This presentation focuses on the key parameters to demonstrate improved mechanical property levels are available in traditional powder metallurgy alloys by proper selection of the processing polymer and proper care in its thermal extraction. The focus is on mechanical property, where gains up to 40% are demonstrated due 10 changes in the processing polymer. Further, atmosphere control during polymer burnout provides a benefit by allowing formation of desirable carbonitrides, giving strength levels over 3 GPa (over 400 kpsi). Insight is? gleaned from powder injection molding, where high polymer contents mandate proper processing control.

Jan 1, 1996

By F. F. Lins

There is a large use of mercury in Brazil by the gold miners in the so called "garimpos" (non registered mining operations), where it is usual to recover the gold contained in the gravity concentrates by amalgamation, which is highly deleterious to environment if not conducted properly. Unfortunately, this is a common practice there. After presenting in brief the modus operandi generally practiced in the garimpos and the environmental problems, this work reviews some of the research conducted in CETEM according to two approaches: (i) replace amalgamation by other processes and (ii) develop technology to treat mercury-contaminated soils and effluents. Conventional processes like froth flotation, to recover gold from gravity concentrates, and centrifuges were considered. Also as alternatives to amalgamation, innovative process like the recovery of gold by coal-oil agglomerates and a technology that is currently under development in our laboratory, called gold-paraffin process, are described in brief, some results presented and their potential use assessed. To reclaim sites already polluted a technology was developed to float mercury selectively from contaminated soils. The potential use of centrifuges to pre-concentrate the mercury is also discussed. The scope for applying the last techniques is to concentrate the pollutants in a small volume of mass which would be suitable for recycling or isolation from the environment. A prospective technology to treat contaminated soils, or mercury concentrates, is the immobilization of mercury by adding inorganics. Concerning the ionic mercury which may be present in effluents, precipitation of the ions and flotation of the precipitates are being studied.

Jan 1, 1994

By Edgar Peek

"The two dominant metallurgical problems in treating most base metal sulphide concentrates in both the chloride and sulphate system are iron removal and sulphur elimination, respectively [1-3]. In this paper the opportunities, limitations and fundamentals of the chloride metallurgy system are described against this background. Only the treatment of oxide and sulphide ores is considered. Both hydrometallurgical and pyrometallurgical unit process operations are highlighted, since most successful base metal processes are based on a combination of the two. Hence, an overview of the technical and also some economical aspects of chloride metallurgy are presented.This overview summarizes the successful applications of chloride metallurgy, but it will not give exhaustive process and plant descriptions. It predominantly focuses on the essential technical features of the metallurgical unit process operations, while providing numerous references separately."

Jan 1, 2011