By W. S. Steele

Vermiculite is a nonmetallic mineral of the mica family, probably related to biotite mica. Its occurrence has been noted at numerous places in the United States and in some foreign countries, but it can be said that vermiculite is of only moderately wide distribution. A laboratory and field survey of over 60 deposits in the United States by F. 1;. Schundler & Co., of Joliet, Ill., indicates that the purest deposit represented in this survey is on the property of the Zonolite Company at Libby, Montana The Zonolite Company is commercially active and the vermiculite it produces is sold as Zonolite. Hereafter, in this report, the word "Zonolite " will be used to designate the vermiculite produced by the Zonolite Company. Values given herein to Zonolite are peculiar to the vermiculite produced from the Zonolite Company's deposits. References to " vermicullite," are to he interpreted as covering the broad field covered by the Schundler survey. Composition and Characteristics of Vermiculite Vermiculite is an aluminum-nmgnesium silicate. The following typical analysis is published by the United States Bureau of Standards: silica, 41 per cent; iron oxide, 7; aluminum oxide, 18; magnesium oxide, 21; calcium oxide, 1; alkalis (sodium and potassium), 1; moisture, 11. Vermiculite breaks down into platelike formation in crushing and grinding operations. Its cleavage is basal. Crude, screened, dry Zonolit,e weighs between 80 and 90 Ib. per cubic foot; its specific gravity is 2.8 and its specific heat is approximately 2. The fusion point of Zonolit'e is 2462" F. Crude vermiculite contains between 7 and 9 per cent of chemically combined moisture. The instantaneous introduction of crude Zonolite into an expansion furnace at a temperature of between 1800" and 2000" F. transforms the combined moisture into steam, which in an effort to liberate itself forces all explosive expansion of the platelike crude material

Jan 1, 1934

By Nathaniel Arbiter

T. M. Morris (School of Mines and Metallurgy, Rolla, Mo.)—Rate studies promise to help quantify flotation operations. The author's exposition of rate studies is therefore laudable. However his exposition of a second order rate equation rather than a first order rate equation is not convincing. It is important to use the correct equation, otherwise erroneous conclusions may be drawn. The data assembled by the author and plotted according to a second order rate equation can be plotted according to a first order rate equation. As a matter of fact much of the data used reveals that a second order rate equation is not applicable. According to the method used by the author for plotting data, the reciprocal of the slope of the line is the maximum possible recovery. Physically this cannot exceed 100 pct, yet several graphs yield maximum recoveries greater than 100 pct. For example: l—Curve 2, Fig. 1 yields a value of 120 pct; 2—Curve 2, Fig. 2 yields a value of 115 pct; 3—Fig. 7 yields a value of 110 pct. The real test of the graphical method is, as the author points out, whether or not the earliest points agree with a straight line. The second order rate plot does not fulfill this requirement. Fig. 10 shows the data used by the author to obtain Curve 2 in Fig. 1, plotted according to both a second and first order rate equation. Fig. 11 shows the two rate plots made from data published by Ludt and DeWitt.19 In Fig. 10 the first order rate plot gives a very good fit and obeys the boundary condition of passing through the origin. For the second order rate plot a straight line can be drawn through the last three points but the earliest points are not in agreement with this line. The reciprocal of the slope of the straight line gives a value of maximum possible recovery of 112 pct. The maximum possible recovery according to the first order rate plot is 78 pct. In Fig. 11 the first order rate plot again fits all of the points very well and passes through the origin. The second order rate plot shows wide deviation of the earliest point, indicating that the second order rate equation is not applicable. The reason for the fit of data to the second order rate equation during longer flotation times is that R, the cumulative percent recovery, changes slowly toward the end of the flotation operation, so that when t/R is plotted against time, one is, in effect plotting t against t and one would certainly expect a straight line. The author attempts to show that the second order rate equation is correct by citing evidence which shows that recovery is a function of initial concentration. This is a debatable point especially since, in the author's original presentation of this paper at the St. Louis

Jan 1, 1952

By C. V. Corless

WE are living at a period of the world's history in which social phenomena are on so vast a scale, are of so profoundly soul-searching a nature, and are occurring in such rapid succession in the great world drama in which we are both actors and spectators, that, in our efforts to obtain a rational point of view in relation to them, our minds may fail to discern the simple in the complex and our understanding is liable to be-come confused or even overwhelmed. To the social student whose scientific training has convinced him of the truth of the evolutionary law, Natura non facit saltum, it is neither the vast scale of the events; their deeply soul-stirring nature, nor their rapid succession that matters so much, as the discovery of the underlying principle or law in accordance with which the disintegration and reintegration, which are the two aspects of social evolution, or indeed of evolution everywhere, are occurring. He is most deeply concerned in seeking an answer to the question: Have we in the present great and perplexing upheavals in human society, whether regarded in Central Europe, in Russia, in Great Britain, or in America, a really new cause at work, or, have we, though on a very- large scale, merely new manifestations of the working out of an old principle? When we think of the appalling struggle in Europe, into which the world's greatest exemplar of democracy was finally drawn, no one has any hesitation in admitting that the great conflict was fundamentally a life-and-death struggle for self-preservation and self-propagation on the part of autocracy. The variations we meet with in the statement of the cause of the war arise mainly from differing distances of perspective: but in the last analysis all agree that the autocratic system of political government, which found its very soul and center in Prussian despotism, was consciously arrayed in a final "world-power-or-downfall" struggle against a love of freedom which was steadily widening and-deepening throughout the world, and particularly throughout those parts of the world where this love of freedom and justice has found expression in democratic institutions. It is not irrelevant to our discussion to recall in passing that this most imposing structure ever conceived by the human mind as an instrument of tyranny is lying today an irretrievable mass of ruins, completely over-

Jan 4, 1919

By M. J. Marcinkowski, K. S. Raghavan, A. S. Sastri

A detailed transmission electron microscopy investigation was carried out in connection with a manganese Hadfield Steel. At small plastic strains, numerous individual intrinsic stacking faults are observed. With increased plastic deformation, the stacking faults thicken into twin lamellae which in turn subdivide the original austenite matrix into smaller domains. The twin boundaries act as strong barriers to subsequent dislocation motion and is in a sense equivalent to grain refinement. It is this "grain refinement" which is believed to be the cause of the very high work hardening rates in the Hadfield Steels. In many cases, especially where an hcp phase is the stable one at low temperatures, the stacking fault energy in fcc metals and alloys decreases with decreasing temperature.' Since stacking faults of the intrinsic type are precursors of both twins as well as the hexagonal close packed structure, both of these entities should become more frequent as the temperature of a fcc crystal is lowered. In the case of the twin, there is no chemical driving force for its formation and it is generally necessary to provide the required driving force by an applied stress, i.e., strain energy. In the case of the hcp structure the transformation from the fcc modification can occur spontaneously (marten-sitically) since a decrease in chemical energy does in fact occur; however, an applied stress will provide an even greater driving force toward complete transformation. Since the transformation products mentioned above occur in an inhomogeneous manner throughout the crystal and since these can act as potential barriers to further plastic deformation2 marked strengthening effects can be anticipated. Also because metal and alloy strenghening is in general proportional to the shear modulus, these effects should be greatest in steels of the austenitic type (y), i.e., the fcc types. Perhaps the two most important steels in this category are the austenitic stainless steels and the Hadfield manganese steels. Both may be quenched from elevated temperatures so as to retain the austenitic states characteristic of those temperatures. The effect of subsequent deformation at lower tem- peratures has a profound effect on the stress-strain curves of these alloys. In particular Fig. 1 shows the compressive stress-strain curves obtained with an 18-8 stainless steel which was quenched from 1850°C after annealing for 1 hr so as to produce all y. As the temperature is lowered, the work hardening rate increases markedly. Although some hcp or c mar-tensite can be generated by plastic deformation as the temperature is lowered,~ it is believed to be a transition phase4 and most of the martensite produced is of the bcc or a variety.3 It is this stress induced martensite which gives rise to the very low initial work hardening at 77°K as can be seen in the stress-strain curve in Fig. 1. Similar low initial work hardening rates have been observed in the stress induced Ni-Ti martensites.5 Fig. 2 shows that an even more rapid rate of work hardening occurs in the Hadfield steels treated in the same way as that described for the 18-8 stainless steels a; the temperature is lowered. It is this ability to work harden to such high stress levels that makes the Hadfield steels particularly suitable for armor plate and heavy construction equipment. However, unlike the case of Fig. 1, no initial low rate of work hardening is observed in any of the curves in Fig. 2. Thus the stress induced formation of any low energy martensite phase in any significant quantity must be ruled out. This observation is in accord with the X-ray findings of Otte.~ On the other hand, small quantities of the E phase have been observed by other investigators using transmission electron microscopy (TEM) above Even more significant was the fact that large numbers of deformation twins were observed in the deformed Hadfield steels,678 which were postulated to be one of the reasons for the high work hardening ability of this class of steels.8 It is the purpose in what follows to discuss a series of experimental observations pertaining to the stress induced transformation in a Hadfield steel and to formulate a dislocation mechanism which adequately accounts for the observed results. EXPERIMENTAL PROCEDURE The stainless steel used to obtain the curves shown in Fig. 1 was of the AISI Type 303 containing approximately 18.0 pct Cr and 8 pct Ni. On the other hand, the Hadfield manganese steel used to obtain the curves shown in Fig. 2 contained between 1.00 to 1.25 pct and 11.5 to 13.5 pct Mn. In all cases the samples were in the form of compression cylinders 0.220 in. in diam and 0.370 in. long. Prior to testing the samples were annealed for a hr at 1050°C and rapidly quenched into a brine solution. This treatment was sufficient to preserve the y phase for subsequent testing at lower temperatures. All samples were compressed in an Instron testing machine using a cross head speed of 0.02 in.

Jan 1, 1970

By AIME AIME

A MODERN copper reduction works has both a genera1 chemical laboratory for control work and a research laboratory for the study of improvement of present processes and better working-up of by-products. The division of work in the general laboratory would naturally differ in different plants. The following statement to the writer from a chemist in one of the works will give a good idea of the type. of work in the general laboratory :

Jan 1, 1929

By D. Harrington

One of the main functions of the United States Bureau of Mines is to obtain and disseminate information that will promote safety in and around mines, and the health and safety of employees engaged in mining. Serious health and safety conditions arising out of contamination of air in metal mines by dust, fumes from explosives and fires, and absorption of oxygen by timber and other causes, led the Bureau of Mines to cooperate with the United States Public Health Service in the study of dust occurrence and ventilation in metal mines in various parts of the country. A. J. Lanza, of the U. S. Public Health Service, and Edwin Higgins, mining engineer of the U. S. Bureau of Mines, in 1915, made a detailed study in the mines around Joplin, Mo.; their reports1 are now available. In 1916, 1917, and 1918, a similar study was made in the Butte, Mont., region by Doctor Lanza and D. Harrington, mining engineer of the Bureau of Mines; the reports of this investigation will be available soon. In 1919, the study was continued in some of the Arizona mines by D. Harrington, of the Bureau of Mines, and G. E. McElroy and R. A. Koronski, of the U. S. Public Health Service, the underground work being completed in June, 1920; these reports are now being prepared for publication. In the spring of 1920, the scope of the work was extended, with D. Harrington in charge as supervising mining engineer, and short studies were made in the mines of the Coeur d' Alenes in Idaho and around Oatman, Ariz. It is hoped soon to extend the work into mines of California, Nevada, Colorado, Michigan, and Minnesota, and ultimately to other states should the mining companies be willing to coöperate. While the coöperation of the mining companies is necessary, the companies are put to practically no expense other than supplying a guide to accompany the investigators underground, the length of time spent

Jan 1, 1922

By P. W. Gilles, B. D. Pollock

THE pioneering work of Steinitz1 and Steinitz, Binder, and Moskowitz2 has shown conclusively the existence at high temperature of two additional phases in the molybdenum-boron system and thus brings to a total of six the number of structures appearing in this system. To the structures Mo2B, MOB, and Mo2B5 they have added MO3B2, a new -MOB form, and have shown that MOB,, which has the same range of composition as Mo2B5, is only a high temperature structure of the latter. This solid solution, interestingly enough, includes neither of the compositions corresponding to the stoichiomet-ric compounds, MOB, or Mo2B5, but rather at all temperatures has intermediate values of composition. These workers have also, in the course of their work, measured melting points, transition temperatures, eutectic and peritectic points in the system and have shown that Mo3B2, because of its dispro-portionation at low temperature to Mo2B and MOB, is stable only in a limited high temperature range. During the course of the present work on the vaporization properties of the molybdenum-boron compounds, a few transition temperatures were observed. When the report of the other workers appeared, it was decided to repeat, in part, their study of the system. As a result, considerable evidence has been obtained that substantiates the specific kinds of melting processes they report as well as the general features of their diagram. However, a marked difference was found between the temperatures they report and the ones observed in this study, with the latter being higher. The purposes of this paper are to present the evidence obtained in this laboratory that verifies their diagram of the system, to give some important temperatures in the system, to compare them with those previously published, and to seek an explanation of the difference. Samples The metal starting material was 400 mesh molybdenum powder with a purity stated by the manufacturer to be 99.9 pct. The initial treatment, designed to remove volatile contamination, consisted of heating in a vacuum for 10 min to a temperature of from 800" to 1000°C during which a loss of 0.3 to 0.4 pct occurred. An assay following this treatment showed it to be 99.4 pct pure, with the principal impurity probably being oxygen. The boron starting material was obtained from the Cooper Metallurgical Laboratories and the Fair-mount Chemical Co. as 325 mesh powder with manufacturers' analyses of 99 pct or better. Initial treatment consisted of heating in molybdenum in a vacuum at about 1700°C for 10 min. During this time a loss of 3.5 pct occurred. An assay following this treatment showed the different samples to have purities ranging from 95.5 to 99.0 pct with iron and carbon as the principal impurities. Following the initial treatment, the elements were combined to form stocks of Mo2B and MOB by heating pressed mixtures in a vacuum to 1100" to 1200°C to accomplish reaction and to 1500" to 1900°C for a few minutes to evaporate the more volatile impurities. Analysis of the two compounds for boron by a modification of the method of Blumenthal3 and for molybdenum by the lead-molybdate method indicated them to have purities greater than 99 pct. The individual samples to be studied had compositions in the Mo2B-MOB range and consisted of mixtures of the stock compounds. Procedure As is usually the case in high temperature work the selection of containers for the samples posed some problems. For vapor pressure studies tantalum crucibles, allowing little contact with the pressed samples, were used and some of the observations made during these experiments are pertinent to the study of the phase diagram. Most of the experiments, however, were performed in graphite containers, as were those of the previous authors. Two kinds of spectroscopic grade graphite crucibles were used. One was a % in. cylinder, 3/4 in. high, containing seven 3/16 in. holes drilled 1/2 in. deep into which were packed samples of the different mixtures weighing 250 to 500 milligrams. The other, consisting of separate crucibles, was prepared by drilling 3/16 in. holes, 1/2 in. deep into 1/4 in. graphite rods % in. long. The 7/8 in. cylinder was heated directly by induction while the small crucibles were packed in a tantalum heating element for induction heating. All heating was done in a high vacuum system in which the pressure was generally less than 1x10-5mm and never rose above 2x10-5mm when the samples were hot. The general pattern of the heating in graphite was to heat rapidly to a temperature somewhat below the desired one, then to raise the temperature slowly. The samples were held for 2 to 5 min at the maximum temperature, which in all cases was far higher than that needed to produce reaction. The short time was employed to reduce possible contamination by the crucible material and to reduce composition changes that would occur because of vaporization. After examination following the heating, the samples were reheated to a higher temperature. Temperatures were measured with a Leeds and Northrup disappearing filament optical pyrometer, certified by the National Bureau of Standards, by sighting through a window at the top of the vacuum

Jan 1, 1954

By Lewis E. Dr. Young

MINING engineers in the United States understand that mining conditions in the British coalfields are much more difficult than in most of the mines now being operated in the United States. We realize also that in the near future we must face some of these same difficult problems. Early Mechanization The progress made in mechanical loading in the United States is the result of a long struggle in many coalfields to mine with power tools safely and to increase output per man-shift. Attempts to use power to loosen coal and to transport broken coal in the U. S. may be said to date from the Stanly Header, or Entry-Driver brought from England in 1888. The principle of this boring machine was used in the McKinlay Entry-Driver, almost continuously used in the U. S. since 1920. Since 1888 experimental loaders, scrapers, and conveyors were installed with more or less success. Beginning in 1918, considerable progress was made with mobile loaders, and in 1920 the first wage agreement for the operation of mechanical loaders was made in Indiana. In 1923 the Pocahontas Fuel Co. loaded nearly 1 million tons of coal using 23 Coloders. Labor Policy The United Mine Workers of America have never officially opposed the Mechanization movement. On December 10, 1945, in a statement before the House of Representatives Labor Committee, John L. Lewis said, regarding the policy of the United Mine Workers of America: "We have welcomed progress; we have welcomed machines. We have told our people that they had to accept that condition; that it was the process of progress, and that they would have to take their chances." Recent Development In 1951 about 71 pct of the tonnage mined underground was mechanically loaded. Over 4000 shuttle cars are in service and it is estimated that much more than half of the tonnage loaded underground is produced by trackless mining. In 1947 roof-bolting was introduced extensively and it is estimated that more than 2 ½ million bolts are now being used per month in about 600 mines. The use of roof bolts has permitted the more effective and safer use of loaders and shuttle-cars. Continuous Mining The McKinlay Entry-Driver could have been used for continuous mining, but for many years it was used only .for entry driving. In 1946 the Silver machine was developed in Colorado, and in 1947 this was acquired by the Joy Mfg. Co. and called the Joy Continuous Miner. Other types of combination mining-loading machines which eliminate drilling and blasting operations are the Marietta Miner, the Colmol, the Lee-Norse Miner, the Junior Miner, the Goodman and the Konnerth machines. There are several other types in the process of development. Probably by January 1953 there will be about 250 continuous miners in operation in the U. S. Payment of Mine Labor One of the most important problems in mechanizing was the establishing of rates of pay that would be attractive to the best men. Prior to the installation of mobile loaders the hand loaders and cutters have been paid by the ton. It was felt that a system of a day's pay should be established and that piece and tonnage rates should be abolished completely. Without exception, all coal loaded in mines equipped with mobile loaders is prepared and loaded by men paid an hourly rate. Trends in Mining Research There are two diverse approaches in coal production research; to try to design a mining machine to fit current methods, or to adapt mining practice to take advantage of proven machines. A great deal of credit must go to the mine operators who have been enterprising and dynamic enough to use available equipment intensively and to discard it as soon as an improved or new machine is available. Effect of Changing Markets Formerly there was an important demand for lump and prepared coal in the larger sizes for domestic use. The use of bituminous coal for house heating has decreased so that not more than 19 pct of the annual tonnage goes to retail trade, only 12 pct is used by the railroads, and much of the retail and most of the railroad coal is in stoker size. As a result of this decline in the market for coarse coal most of the large mining operations have crushers installed in the tipples or preparation plants. Mass production at the face requires increased preparation facilities. Another important trend is in connection with complete seam mining with mechanical loading. In many mines where the immediate roof is apt to fall with the coal no effort is made to separate roof material from coal prior to

Jan 1, 1952

By K. G. Kreider, J. H. Brophy, J. Wulff

The technology of nickel-activated sintering of tungsten powder has been successfully applied to the densification of plasma-sprayed tungsten. Nickel was added by infiltration in a zinc solution followed by evaporation of the solvent. After sintering one hour at 1300°C density 95 pct of theoretical and transverse rupture strength of 74,000 psi were obtained. Shrinkage was found to be anisotropic and the mechanism of densification was comparable to that found in the nickel-activated sintering of tungsten powder. 1 HE use of a plasma spray gun for the fabrication of massive tungsten parts has become increasingly interesting. Applications now exist where a deposit in the as-sprayed condition is satisfactory. However, these deposits are generally characterized by a lamellar anisotropic microstructure containing 15 pct porosity of which, typically, two-thirds is open to the surface. Mechanically, the as-sprayed deposits fail at relatively low stress levels with a biscuit-like fracture. As a result of these problems the possibility of improving structure and strength by sintering treatments subsequent to spraying is particularly attractive. Preferably this sintering treatment should be adaptable to large bodies of sprayed metal. The similarity between the as-sprayed tungsten structure and that of a powder compact suggests that the relatively low-temperature activated sintering technique1 might be profitably employed in the densification of plasma-sprayed tungsten. It was the purpose of the present investigation to develop a technique for introducing the nickel-activating agent into the sprayed structure, to evaluate the amount and mechanism of densification obtained as a function of time and temperature, and to obtain an indication of the relative strength before and after sintering. EXPERIMENTAL PROCEDURE Powder used for spraying was purchased from the Wah Chang Corp. in several size fractions ranging from an average size of 4 to 150 . These powders were sized further for an explicit study of the influence of average feed size on densification. All powders were dried at 200°C before use. Spraying was accomplished with a Plasma Flame unit manufactured by Thermal Dynamics Corp. Several modifications of the unit were helpful in conducting the investigation. A variable speed auger feed mechanism coupled with the carrier gas mecha nism facilitated the use of fine particle sizes. A coil of ten turns of copper tubing in series with the arc power and concentrically would around the nozzle improved nozzle life and extended the range of operating currents available. The function of the auxiliary coil was to cause the arc to spin and to prevent impingement at only one point in the nozzle. Normally air sprayed deposits were made with an arc maintained at 400 amp at 50 to 70 v. The arc was blown by a gas mixture containing from 5 pct H, 95 pct N for the finest powder feed sizes ranging to 20 pct H, 80 pct N for the coarsest size. The flow rate was maintained at 100 cu ft per hr NTP through a nozzle of 0.25 in. ID. When apraying in air, the powder stream was directed toward an aluminum substrate for ease of mechanical removal of the deposit. The substrate was cooled by diverting the plasma flame with an air jet, and a second jet was directed on the deposit surface. In this configuration a gun-to-work distance of 2 to 3 in. was found to be satisfactory. Fig. 1 represents a typical as-sprayed deposit micro-structure. Laboratory studies of protective atmosphere spraying were carried out in cylindrical chamber 8 in. in diam by 18 in. in length. In operating the nozzle attached to such a chamber, particular care was required to avoid nozzle burn out due to reduced gas flow. The structure and density of the chamber sprayed deposits varied over wide ranges depending on substrate temperature. For the purposes of this investigation, flat deposits were made approximately 2 in. sq by 3/8 in. thick. From these deposits individual samples were cut an ground to a rectangular shape typically 1 1/2 in. by 1/8 in. sq such that the long dimension was perpendicular to the spraying direction. For the study of shrinkage anisotropy deposits up to one inch thick were produced. From these, rectangular samples were cut having a longer dimension parallel to the spraying axis. Prior to the addition of activating agent, the samples were deoxidized in hydrogen at 800°C for 20 min. No detectable dimensional or microstructural change was observed after this treatment. The addition of nickel was accomplished by infil-

Jan 1, 1963

By AIME AIME

T HE appointment of Herbert Hoover to the portfolio of Commerce in the President's Cabinet is to engineers the fulfillment of a long deferred hope to have an engineer in high political office and is a matter of congratulation to us for three reasons; because he is a mining engineer who represents the highest type of idealistic engineering effort; because he is a past president of the Institute; and because he has probably a broader grasp of world problems than any other living engineer. Frank A. Vanderlip in the preface to his book "What Happened to Europe" tells of the many interviews he had with the most prominent men in Europe which were made possible for him by his eminence as a banker and by the courtesy of the American ambassadors. He cites by name such well known figures as Austin Chamberlain, Sir Auckland Geddes, Monsieur Delacroix, Monsieur Briand, Mr. Padkrewski, Mr. Venizelos, Colonel House, General Pershing, Mr. Baruch, and many others and says :

Jan 1, 1921

By J. B. NEALEY

MANY nonferrous smelting plants have recently adopted natural gas as fuel with resultant economies, both in cost and efficiency of utilization. Not only has this fuel been used for roasting, reduction, sintering, drossing, and smelting, but also for power. All of the three big smelters near Salt Lake City, Utah, have been changed over from coal and oil firing to gas. Among these is the plant of the International Smelting Co., Tooele, an Anaconda subsidiary, smelters of both copper and lead ores. In the roasting division at Tooele are 32 MacDougall six-hearth roasters, each 16 ft. in diameter and 19 ft. high. Two gas burners are installed on each furnace. These burners are of the single-valve, automatic gas-air proportioning type using high-pressure gas at 10 lb.

Jan 1, 1933

ALBERT SAUVEUR, Chairman. A. A. STEVENSON, Vice-Chairman. HERBERT M. BOYLSTON, Secretary, Abbot Bldg., Cambridge, Mass. John Birkinbine, William Kelly, J. S. Unger, William H. Blauvelt, Charles Kirchhoff, Felix A. Vogel, James Gayley, Richard Moldenke, Leonard Waldo, Henry D. Hibbard, Joseph W. Richards, William R. Walker, Henry M. Howe, C. F. W. Rys, William R. Webster, Robert W. Hunt, E. Gybbon Spilsbury, Frederick W. Wood. J. E. Johnson, Jr., The innovation of a special meeting under the auspices of the Iron and Steel Committee was well justified, if we accept as a criterion the number of papers presented at the meeting held on Oct. 16 and 17 in New York and the attendance at that meeting. Twenty-four papers were read, and most of these were widely discussed orally, while doubtless the written discussions will be even larger in extent. Discussions will be received up to Dec. 1, 1913. The attendance at the meeting of 106 members and 75 guests is an evidence of the wide anti growing interest in the Institute of men interested chiefly in iron and steel. It is especially interesting to note this large attendance at a meeting where very little of a social nature was introduced into the program. An informal dinner for the men at the Engineers' Club closed the meeting. At this dinner were present about 70 members and guests. One of the Vice-Chairmen and the Secretary of the new Committee on Petroleum and Gas told of the important plans in prospect of that Committee. Brief impromptu speeches by a considerable number of the members and guests were enjoyed. Professor Marburg reiterated his previous assertion that he believed that the Institute and the American Society for Testing Materials, as well as some of the other technical societies, were all fighting for one good cause; that there was room in the field for all of these societies with their various points of view; and that they should march shoulder to shoulder. The success of this dinner was due largely to the efforts of Mr. Johnson who had the affair in charge.

Jan 11, 1913

By P. G. Winchell, R. J. Russell

The distribution of displacements of originally plane surfaces by an invariant-plane strain has been analyzed statistically. The displacement ratio (the magnitude of the displacement of a point originally a unit distance from the invariant plane) can be determined from an analysis either of tilts of random surfaces or of displacements of random scratches scribed on a randowz surface. In either case the mean of the tangent of the observed displacement angle is related to the displacement ratio, and the number of observations used in determining the mean is related to the confidence limits placed on the estimate of the displacement ratio. In estimating the effect of applied stress on a phase transformation whose displacement effects can be approximated as an invariant-plane strain,* the dis- placement ratio of the invariant-plane strain is of primary importance. Two procedures for determining such displacement ratios are considered here. In the tilt method the measured quantity is taken to be the angle through which a random polish plane is rotated by the invariant-plane strain. In the scratch method the measured quantity is taken to be the angle between the original direction of a random scratch in a random polish plane and the projection of its final direction in the polish plane. In order to obtain precise results from either of the methods, it is necessary to measure the relative volume change associated with the strain in a separate experiment. TILT METHOD A locally homogeneous invariant-plane strain, P, with displacement ratio, S, may be written&apos; where ; and < are unit vectors indicating the displacement direction and invariant-plane normal, respectively, as pictured in Fig. 1. Eq. [I] describes a uniaxial strain if the direction of displacement is parallel to the invariant-plane normal and a pure shear strain if the displacement direction is perpendicular to the invariant-plane normal. The original orientation of the random polish plane relative to the invariant plane and to the displacement direction is shown in Fig. 2. The angle 03 between < and u is related to the relative volume change, ?V/V, and to the displacement ratio by As a result of the invariant-plane strain, the polish plane is rotated about its intersection with the invariant plane by the angle y, which is always taken to be positive. The tangent of this angle in terms of the above parameters is

Jan 1, 1967

By R. S. Archer

THE name molybdena was employed by Pliny to denote various substances resembling lead. Later this name was applied to galena-the naturally occurring sulfide of lead-or substances of similar appearance. By the middle of the eighteenth century, it was applied to graphite and to the mineral sulfide of molybdenum (MoS2) now called molybdenite. This confusion is quite understand- able inasmuch as these substances look and feel very much alike. In 1778, the Swedish chemist Scheele published a treatise in which he pointed out essential differences between graphite and molybdenite. On treatment with nitric acid, molybdenite, unlike graphite, produced a peculiar white earth with acidic properties which he called molybdic acid. Since the same mineral gave off sulfurous fumes on heating, he concluded that it was a sulfide of molybdenum. In 1790, there appeared an account of the isolation by P. J. Hjelm of the new element molybdenum, as a metallic powder, by heating the oxide with carbon. It was not until Bertelius conducted the necessary experiments, about 1818 to 1825, that the foundation of the chemistry of molybdenum was laid. The only recorded use of molybdenum during the first century after its isolation was as a chemical reagent, primarily for the determination of phosphorus. It was not until the last decade of the nineteenth century that the use of molybdenum in steel appears to have been investigated. A

Jan 1, 1953

By Robert H. Richards

The adaptation of European methods of concentrating ores to suit the conditions of this country has followed the lines that simplify machinery, diminish labor and increase capacity. Noteworthy instances are the substitution of hydraulic classifiers for the last one or two trommels in the series, and the substitution of a distributing-tank for the slimes in the place of the Spitzkasten. The question may be fairly asked, At what point do losses become serious in consequence of these changes? It is to study this question that the investigation herein described has been undertaken. After the losses are located and the methods of stopping them are pointed out, it will then lie with the individual mill to decide whether or not the plans proposed will save suficient value to warrant their adoption. In the discussion of sorting followed by sizing, as the terms are used in this paper, me have to deal with the preparation of slimes by the Spitzkasten for subsequent washing upon the slime-table. The Spitzkasten, or pointed box, is an inverted hollow pyramid, generally of wood, usually with four faces or sides coming together in a point below. The sides can have, according to Rittinger, a minimum angle of slope of 50" with the horizontal. The feed-water carrying fine slimes (less than 0.01 inch, or 0.25 mm. in diameter) for treatment is fed at one end and carefully distributed over the whole width. The outlet is over the opposite end. The water-current passes direct from inlet to outlet, and has usually been regarded as a surface-layer pass-

Jan 1, 1898

By C. R. Johnson, R. A. Greenkorn, R. E. Haring

Three confined five-spot miscible displacements at unity, favorable, and unfavorable mobility ratios were conducted in a shallow, water-saturated sandstone of Pennsylvan-ian age near Chandler, Okla. These studies, plus associated laboratory experiments, were designed to measure miscible displacement performance in a controlled natural system, using known scaling criteria to develop an approach to modeling the heterogeneous field system. We have concluded from these studies that: (I) displacement efficiency in the field is a pronounced function of mobility ratio, indicating that miscible fingering observed in simple laboratory models occurs in the field: (2) field displacements can be quantitatively predicted by scaled laboratory models if the degree and location of field permeability variations are preserved in the models: and (3) arbitrary simplifications of heterogeneity will not necessarily predict observed displacement efficiency, and the simpler the model, the more optimistic the prediction. INTRODUCTION Many processes to achieve miscible displacement of reservoir oil by injected fluids have been conceived and field tested by the oil industry. Among the better known are high-pressure gas, enriched gas, and LPG banks. The simplest form of miscible displacement—one fluid miscibly displacing another fluid of different viscosity but the same density—has been studied extensively in homogeneous laboratory models. Observations of unstable fingering have been made which explain the significant decrease in displacement efficiency as the mobility ratio (ratio of displacing fluid mobility to displaced fluid mobility) increases. General industry experience with field tests of miscible displacement projects, mostly LPG banks, has been premature solvent breakthrough and lower than predicted production rate increases. These results have been attributed to either unstable fingering, unusual or unexpected permeability stratification, or both. Miscible displacement data in a controlled natural system have never been reported, however. Also, it has not been shown that properly designed and constructed laboratory models quantitatively predict field-scale behavior. The purpose of the combined field and laboratory ex- periments reported in this paper is twofold. The first was to measure miscible displacement performance at different mobility ratios in natural rock approaching field size under precise, controlled conditions. The second purpose was to utilize known scaling criteria plus several approaches to heterogeneity to model the field. Comparison of model and actual field results should then determine whether or not the laboratory phenomena (manifested by miscible displacement efficiency) are exhibited in large, natural rock systems. We carried out our program by first locating a shallow, water-saturated reservoir whose rock properties were representative of oil-bearing reservoirs. Detailed reservoir description by core analysis and interference testing showed the field site to be heterogeneous. A sequence of controlled, aqueous-phase miscible displacements was conducted at unity, favorable and unfavorable mobility ratios. A central, confined pattern was used to obtain the displacement data. A laboratory program using sand-packed models was conducted to determine the modeling criteria necessary to simulate field behavior of miscible displacement in a heterogeneous system. SCALING THEORY The detailed derivations and descriptions of the scaling laws that apply to laboratory models of reservoirs are adequately described elsewhere, so the following discussion will be restricted to facets of importance in this study. For a displacement in which one liquid miscibly displaces another, the following dimensionless groups are required to have the same numerical value in the model as in the field: The model also must be geometrically similar to the field, be spatially oriented the same as the field (same dip angle), and have the same initial and boundary conditions as the field (same initial fluid saturations and same injection-production well arrangement). When these conditions are satisfied, the theory predicts that at dny dimensionless time (pore volumes of produced fluids) the dimen-sionless flow potential and dimensionless fluid concentrations will be identical at all dimensionless spatial locations within the model and the field. If this prediction is correct, then the local dimensionless velocities must be identical, thus the instantaneous fraction of displaced fluid produced and the cumulative recovery expressed as fraction of original fluids in place must be identical at all dimensionless times. The theory outlined above has been obtained by either dimensional analysis or inspectional analysis of differential

Jan 1, 1966

Attention! Engineers! Geologists! Here is your Opportunity to be of Professional Service The war has interrupted the supply of many minerals, which were normally imported. In view of present transportation conditions, a serious shortage exists in certain materials and will soon develop in others. Some immediate action is imperative. The first thing is to take a careful inventory of American resources. We must know where the ore deposits are, what has hitherto hindered their utilization, what methods must be used, and what equipment will be needed if an emergency demands their rapid development. Many properties must be re-examined from a new point of view, that of present necessity rather than of normal profit. When the shortage is realized, the preliminary steps for relief should have been completed. It is a necessary and patriotic form of mineral insurance. Will you have a part in it? Do not forget that these are war times, and that what may have been valueless a year ago may be a "life-saver" now; an abandoned copper prospect of 1913 might make a successful pyrite mine in 1917. We are fighting an autocratic enemy who knows his resources to the last pound, and uses them with most efficient organization. We have no Kaiser, so each of us must do his share to put our Government in the same situation. The Government needs your facts.

Jan 8, 1917

By A. R. Kinkel

Robert T. Walker and Woodville J. Walker (Walker Engineering Corp., Salt Lake City)—Mr. Kinkel&apos;s article embodies, in condensed form, the results of the first detailed and complete geological survey that has ever been made of the long neglected but potentially very important West Shasta Copper-Zinc district, in Shasta County, California. In view of the difficulties of the terrain and the complexity of the geological structure, this represents a notable achievement, and it is with regret, therefore, that the writers find it necessary to differ from Mr. Kinkel&apos;s conclusions on two important points. The first has to do with the interpretation of two members of the stratigraphic column of formations in the district; for purposes of comparison, the description of these two members according to Mr. Kinkel is shown parallel to the description of these members according to the writers, see Fig. 14, Mr. Kinkel&apos;s nomenclature being used. The first member, which Mr. Kinkel terms the upper unit of the Balaklala rhyolite, consists of a single, massive, homogenous body of very silicious igneous rock, consisting almost wholly of quartz and albite, and averaging about 80 pct silica. Most geologists of the U. S. Geological Survey who have previously inspected the district have called it an alaskite. It is not a pile of several members, but is a single unit, without internal subdivisions. It has the form of a recumbent lens, approximately flat on the bottom and arched on top, several miles in diameter, and attaining a maximum thickness of 1000 to 1200 ft. It varies in texture from porphyritic to holocrystalline, and contains unusually large quartz phenocrysts up to 4 mm diam. Mr. Kinkel considers this formation to be a thick lava flow that is older than the overlying Kennett shale, while the writers interpret it as being intrusive, constituting a domed sill or laccolith that is younger than the Kennett shale. Their reasons are as follows: 1) This formation shows none of the features which within the writers&apos; experience invariably accompany very silicious lava flows. Nowhere is it vesicular; nowhere does it contain any glass or its devitrified equivalent; nowhere does it contain flow breccia; and nowhere has it a ragged top, in spite of the fact that there is no evidence of surface erosion, which might have removed such a top.

Jan 1, 1957

Butte Meeting. It is expected that the technical program of the Butte meeting will be a sufficient attraction to draw to that point every member who can possibly get away long enough to attend. Attention is particularly called to the papers already sent in by the Committee on Precious and Base Metals, and the papers which they are undertaking to secure for the meeting, as published on pp. ix and x. In addition to these papers, and in addition to those published in this Bulletin, the office of the Institute already has in hand several papers, which will be published at an early date, and presented in abstract and discussed at the meeting. Of the discussion of these papers a special feature is being made. Therefore, let every member come to Butte who can do so. A meeting of the Board of Directors of the Institute will also be held at Butte. In the May Bulletin, we stated for the information of members the railway excursion rates for two suggested tours in connection with the meeting, which included Glacier Park before the meeting and Yellowstone after it. The itineraries there given and rates quoted were planned and offered by the railway agent bureaus in New York. Circulars have been sent to the members of the Institute by A. E. Vaughan & Co., a tourist trip agency of New York City, containing details of tours nearly identical with those outlined in the Bulletin, and quoting rates covering, the expenses of the whole trip. Members can easily compare these rates with the rates offered by the railroads, and published in the last Bulletin. In order that no misapprehension may exist, the statement is here made that the Institute and its officers have no connection whatever with Vaughan & Co.&apos;s proposals and that any such tours will be strictly personal matters between said company and the members of the Institute who take them. Nevertheless, the Board of Directors calls to the attention of members the circumstance that tours such as these will afford an opportunity for members to travel together to the meeting.

Jan 6, 1913

By Dilip K. Paul, Charles H. Jacoby

The economic importance of salt domes has been recognized throughout the world, primarily because of oil and gas accumulations on their flanks, and to a lesser degree, for the value of their salt and potash. Recently they have become of value as hosts for cavities used to store hydrocarbons. In the near future we believe that their main value will be a source of geothermal energy. Although tremendous effort has been expended on the understanding of the geology and physical characteristics of the strata intruded by salt domes, relatively little energy has been exerted in the comprehension of the salt dome itself. Salt domes have long been recognized as a geological heat anomaly. With respect to other sedimentary rocks, salt is a good conductor of heat. Expressing values in 10-3cgs units, sedimentary rocks vary from 1.0 to 8.0; metamorphic rocks from 5.2 to 8.4 and igneous rocks from 3.1 to 9.8. Rock salt in its pure form has a thermal conductivity of 17. Thus a salt dome can be expected to act as a conduit bringing heat vertically from deep within the earth&apos;s crust.

Jan 5, 1974