By W. L. Saunders

THE world's greatest producing area is, geographically, in the midland region of North America about the Great Lakes. This area, with but one- third of the nation's population, produces, with the exception of tobacco and cotton, three-quarters of the principal staples. It provides the surplus or export grain, meats, dairy products, steel and leading minerals. The social and political condition of a nation is determined by its industrial efficiency, and the share of the commerce of the world obtained by a nation is fixed more by the economy of its transportation than by any other factor. It is an economic maxim that: The total cost is the cost of production plus transportation cost. The cost of carrying 1000 tons by water or 100 tons by rail is equal, over the same distance

Jan 1, 1921

By Messrs. von Jonstorff

Continued Discussion of the Paper of Messrs. von Jonstorff, Blair, Dillner and Stead, presented at the New York Meeting of the Iron and Steel Institute, October, 1904.* (Bethlehem Meeting, February, 1906.) CLEMENS C. JONES, Richmond, Va. (communication to the Secretary+) :-In the chapter of this paper entitled "Method for the Determination of Phosphorus," by Andrew A. Blair, a form of the reductor used by Mr. Blair is illustrated. This form was employed by me in my earliest experiments, and abandoned after my adoption of the final apparatus described in my paper on the subject in 1889. The results reported by Mr. Blair are very closely accordant; but my experience was that, in the use of this form, a loss of the solution, amounting to almost a cubic centimeter, was occasioned by minute bubbles of hydrogen rising to the surface, and there exploding. My final reductor was designed to prevent this loss; and the most satisfactory results were obtained with a reductor having the open cup replaced by a bulb-shaped receptacle, provided with a glass stopper, similar to that of a separatory funnel of similar capacity, as suggested in a foot-note in my original paper. In my experience, the use of this later form of reductor repeatedly gave duplicate results which were, coincident to the fourth decimal place. R. W. RAYMOND, New York, N. Y.:-The. remarks of Mr. Jones recall to my mind an interesting part of the history of the Institute, and, of its relation to modern progress in the department covered by this interesting and valuable paper. In

Mar 1, 1906

By H. L. Marcus, P. W. Palmberg

As can be seen from the phase diagram A1-W1 the equilibrium solubility of tungsten in aluminum is practically nil at room temperature. By quenching from the liquid state (50,000°C per sec), Varic, Burov, and Kolesnicenko2 obtained A1-W solid solutions up to 0.15 at. pct W. The quenched alloys were in the form of foils, 0.2 to 0.3 mm thick. Considering the results of Duwez and Willens,3 it is obvious that this thickness, which makes impossible a sufficiently rapid quenching, was the main reason for the relatively low content of tungsten dissolved in aluminum found by Varic.2 he present note shows that the metastable solubility of tungsten in aluminum can be appreciably extended in aluminum-rich A1-W alloys. The quenching technique and the procedure employed for the preparation of the alloys have been described previously.475 The resulting quenched flakes varied in thickness from 1 to 20 µm from experiment to experiment. However, the measurements of the lattice parameters were carried out only with flakes thinner than 5 µm. The areas of quenched flakes were between 0.1 and 15 mm2. The quenched flakes were placed into a 0.3-mm glass capillary tube which was then mounted in a 114.6-mm-diam Debye-Scherrer camera. Straumanis asymmetric film position and nickel-filtered CuKa radiation were used. The lattice spacings were computed taking X(CuKa1) = 1.54050A for resolved and ?(CuKa) = 1.54178A for unresolved doublets. All specimens were rotated at room temperature, 26" +2°C. The lattice parameters were estimated from extrapolation against the Nelson-Riley function. It was estimated that the error in the lattice parameter of the measurements on a single film lies within +0.0004A for lower and about +0.001A for higher concentrations of tungsten. The lattice parameters of the metastable solid solutions A1-W are plotted vs the concentration of tungsten in Fig. 1 together with the parameters measured by previous investigators.' Each point of the present measurements represents a determination of the lattice spacing on different quenched flakes, for a given concentration of tungsten. With experimental accuracy, the lattice parameters of the metastable solid solutions fall on the straight line passing through the already known data.' As estimated from the uncertainties in the lattice spacings of the solid solutions, the alloys were homogeneous within 0.1 at. pct W. The solubility of tungsten in aluminum-rich A1-W solid solutions obtained by a very rapid quenching technique is increased to about 0.95 at. pct W. This value is 6 times greater than the amount known up to now. -he lattice parameters of the resultant aluminum solid solutions with higher concentrations of tungsten than 0.95 at. pct W did not remain constant AUGER electron spectroscopy has been used to clarify the role of impurities in the embrittlement of AISI 3340 steel. Analysis of fracture surfaces has shown that the embrittled condition is correlated with appreciable antimony segregation at grain boundaries. The low temperature (400" to 600°C) temper embrittlement of low alloy steels containing various combinations of Cr, Ni, Sb, Mn, P, Sn, and As has been examined extensively for many years. General reviews of the area have been made by McMahon1 in 1968, LOW' in 1959, woodfine3 in 1953, and Holloman4 in 1946. Recent work by Low, Stein, Turkalo, and LaForce5 has done much in separating the alloy and

Jan 1, 1970

By J. E. Forciea, R. W. Salmi

Operating and research personnel at U.S. Steel's Pilotac concentrator have evolved specifications for magnetic separators suitable for use in beneficiation of Mesabi magnetic taconite. These specifications were developed as a result of investigations into the operating and metallurgical problems at the Pilotac concentrator over a period of some ten years. This paper discusses primary magnetic separator specifications, but much of the information is also pertinent to secondary and tertiary magnetic separators. Of particular significance is the proposal of a new basis for specifying the magnetic field which includes consideration of both field strength and field gradient. Other areas of discussion include flowsheet service, operating conditions such as drum speed and pulp level, tank configuration, magnet strength including field gradient, sleeve bearing design, designation of corrosion resistant materials and other details that result in a metallurgically efficient machine that has low repair and maintenance requirements. The mechanical and metallurgical design of magnetic separators at the Pilotac plant, Minnesota Ore Operations, United States Steel Corp. has progressed from the original single-stage, belt-type machines to the present multiple-stage, drum-type units, In ten years of operation, the plant operating and research personnel, in consultation with manufacturers, have made design changes to improve mechanical, electrical and magnetic features to meet process needs as flowsheet designs developed and to incorporate new permanent magnet materials as they became available. Separator specifications were an end result of this effort. The latest specifications which were developed for the Minnesota Ore Operations' plant were not all-inclusive listings; they covered only those points indicated by plant experience. For example, magnet pole piece design and dimensions were not stated. The manufacturers were given freedom to use any design as long as the field pattern was as specified. The selection of the items to be included in the specifications was undoubtedly influenced by particular conditions at Pilotac such as composition of plant water, concentration characteristics of the ore, repair and maintenance facilities available and the research programs that had been conducted. Only the developments leading to the specifications for a primary or "cobber" magnetic separator are presented in this paper. However, the same general concepts are used to specify secondary and tertiary separators. The areas of interest discussed include flowsheet service, tank configuration, magnet design, bearings, materials of construction, and some minor mechanical details. FLOWSHEET SERVICE The primary magnetic separators in the Pilotac Concentrator flowsheet are located after the first stage of grinding as shown in Fig. 1.

Jan 1, 1965

[A Aall, Christian H., M49 D Mgr, American Metal Climax, Inc., 61 Broadway, New York 6, N.Y. Aaroe, S. L., A54 B Sales Mgr, The W. S. Tyler Co. of Can. Ltd., St. Catharines, Ont., Canada Abalos, Teodulo Q., J57 A Foreman, Lepanto Cons. Ming. Co., Mt. Province, Philippines Abbass, G., M55 P. O. Box 680, Hong Kong, China . Abbitt, James M., A54 770 Sole Blvd., Bartow, Fla. Abdullah, M. Y., J53 Dept. of Mines Res. Div., P. O. Box 1016, Tiger Lane, Ipoh Perak, Malaya Able, John F., Jr., J53 A Ming Engr, USA SIPRE 1215 Washington Ave., Wilmette, Ill. Abell, Leo M., M31 B Conct Supt, Phelps Dodge Corp., Morenci, Ariz. Abenius, Hakan Wilhelm, M52 A Mng Dir, Stora Kopparbergs Bergslags AB, Falun, Sweden Abenoroth, Harry F., A57 Natl. Carbon India Ltd., 18A Brabourne Rd., Box 217, Calcutta, India Abercrombie, Harry W., J56 1645 Camphor Dr., Lakeland, Fla.]

Jan 1, 1961

By A. Tonejc, A. Bonefacic

As can be seen from the phase diagram A1-W1 the equilibrium solubility of tungsten in aluminum is practically nil at room temperature. By quenching from the liquid state (50,000°C per sec), Varic, Burov, and Kolesnicenko2 obtained A1-W solid solutions up to 0.15 at. pct W. The quenched alloys were in the form of foils, 0.2 to 0.3 mm thick. Considering the results of Duwez and Willens,3 it is obvious that this thickness, which makes impossible a sufficiently rapid quenching, was the main reason for the relatively low content of tungsten dissolved in aluminum found by varic.2 he present note shows that the metastable solubility of tungsten in aluminum can be appreciably extended in aluminum-rich A1-W alloys. The quenching technique and the procedure employed for the preparation of the alloys have been described previously.475 The resulting quenched flakes varied in thickness from 1 to 20 µm from experiment to experiment. However, the measurements of the lattice parameters were carried out only with flakes thinner than 5 µm. The areas of quenched flakes were between 0.1 and 15 mm2. The quenched flakes were placed into a 0.3-mm glass capillary tube which was then mounted in a 114.6-mm-diam Debye-Scherrer camera. Straumanis asymmetric film position and nickel-filtered CuKa radiation were used. The lattice spacings were computed taking X(CuKa1) = 1.54050A for resolved and ?(CuKa) = 1.54178A for unresolved doublets. All specimens were rotated at room temperature, 26o +2°C. The lattice parameters were estimated from extrapolation against the Nelson-Riley function. It was estimated that the error in the lattice parameter of the measurements on a single film lies within +0.0004A for lower and about +0.001A for higher concentrations of tungsten. The lattice parameters of the metastable solid solutions A1-W are plotted vs the concentration of tungsten in Fig. 1 together with the parameters measured by previous investigators.' Each point of the present measurements represents a determination of the lattice spacing on different quenched flakes, for a given concentration of tungsten. With experimental accuracy, the lattice parameters of the metastable solid solutions fall on the straight line passing through the already known data.' As estimated from the uncertainties in the lattice spacings of the solid solutions, the alloys were homogeneous within 0.1 at. pct W. The solubility of tungsten in aluminum-rich A1-W solid solutions obtained by a very rapid quenching technique is increased to about 0.95 at. pct W. This value is 6 times greater than the amount known up to now. -he lattice parameters of the resultant aluminum solid solutions with higher concentrations of tungsten than 0.95 at. pct W did not remain constant AUGER electron spectroscopy has been used to clarify the role of impurities in the embrittlement of AISI 3340 steel. Analysis of fracture surfaces has shown that the embrittled condition is correlated with appreciable antimony segregation at grain boundaries. The low temperature (400" to 600°C) temper embrittlement of low alloy steels containing various combinations of Cr , Ni , Sb , Mn , P , Sn , and As has been examined extensively for many years. General reviews of the area have been made by McMahon1 in 1968, LOW' in 1959, woodfine3 in 1953, and Holloman4 in 1946. Recent work by Low, Stein, Turkalo, and LaForce5 has done much in separating the alloy and

Jan 1, 1970

By Arthur F. TQggQrt

THE approximate status of education in ore dressing in 1871 is reflected by Rossiter W. Raymond in an article written at that time presenting the curricula and descriptions of the laboratories at the various mining schools in the United States. For the most part, the curricula in which ore dressing was taught were for mining engineering. They comprised courses in geology, mining, and pyrometallurgy about equal in point or credit weights; a short course in ore dressing, and a somewhat longer course in assaying; and courses in surveying, hydraulics, power, and strength of materials-all superimposed on a broad foundation of physics, chemistry, and mathematics. Some curricula contained a fair content of the humanities. Then, as now, the emphasis on fundamentals was greater in the older colleges and universities. The report on the Columbia School of Mines, then relatively young, emphasized that a large percentage of its students were college graduates. As technical and scientific knowledge grew, first metallurgy and then geology were set up as separate curricula. So far as curriculum designation is con-

Jan 1, 1947

By H. E. Exner

This article is a critical review of the influence of surface preparation on crack formation at Vickers indentations in the test used by Palmqvist3-7 to evaluate the toughness of cemented carbides. Experimental results are presented which clearly show that grinding introduces compressive surface stresses into the cobalt phase and thus reduces the crack length. The deformed surface layer is removed by polishing and a stress pattern is approached corresponding to that in the bulk material. Cracks of maximum length are characteristic of this stress state. Deformation stresses can be removed by annealing above 800°C. On the basis of these results , sample preparation for the crack length test can be simplified, the accuracy of measurement is improved, and a simple and significani parameter is found to describe crack resistance of cemented carbides. FOLLOWING suggestions by Ammann and Hinniiber,1'2 Palmqvist3-7 developed a method for testing the toughness of cemented carbides using as a measure the sum of crack lengths at the four corners of a Vickers hardness indentation. This method has several advantages over the bend test commonly used in carbide technology: a) specially formed samples are unnecessary; b) sufficient information can be obtained from one sample; c) the scatter is relatively small; d) the range of actual values for commercial cutting alloys is wide. Thus, this test is both cheaper and more precise than the bend test. Nevertheless, Palmqvist's method is not widely used, mainly for two reasons: a) The relationship between crack length and the technological properties of the material (wear and shock resistance) is not clear. b) The crack length is strongly dependent on surface treatment. It is necessary, therefore, that surface preparation be very precise and reproducible, conditions usually hard to obtain. While any other simple mechanical test has this first drawback, the second became crucial in the application of the crack length method as a practical test. The reasons that this drawback could not be eliminated are, in our opinion, misleading and inconsistent interpretations of the influence of surface preparation on the crack length given in literature. In the following, after a short review of previous experimental results the interpretations given by different authors,4?'-11 cf. Table I, are discussed critically and a consistent explanation is presented on the basis of which improvements of the method of crack length testing are proposed. 1) PREVIOUS EXPERIMENTAL RESULTS In his first attempt to use the cracks at Vickers impressions as a quantitative measure of the toughness of cemented carbides, palmqvist3 calculated the work necessary to initiate cracks by the formula: Sk =k.Pk. [I] where k = numerical constant = 6.49, Sk = critical work to initiate cracks (gf cm), Pk = critical load (load necessary to initiate cracks) HV = Vickers hardness (kp per sq mm). The difficulties involved in experimental determination of the critical load were overcome by the observation that a linear relation holds between the applied load and the sum of the crack lengths at the four corners of the indentation. This linear function, given by Eq. [2] below, was confirmed by Dawihl and Alt-meyer9and by our experiments, see Fig. 1: I = a1.P +a2 [2] where 1 = sum of the crack lengths at a Vickers indentation, P = applied load, al, a2 = parameters dependent on the toughness of the alloy and the surface preparation. The critical load, Pk, is now given by a2, which can be obtained by extrapolating the load vs crack length line to zero crack length, see Fig. 1. This simple relationship, Eq. [2], led Palmqvist1,7 to a parameter which was more reproducible and easier to obtain experimentally than the critical work: the work, S300, put into the sample to produce an average crack length of 300 µm per indentation. This parameter is calculated using the formula: where the load, P3oo, giving a crack length of 300 µm, can be taken from the load-crack length plot, Fig. 1,

Jan 1, 1970

By Dozier Fircley

SOME nonmetallic minerals and their products, such as portland cement, common brick and hollow tile, sand, gravel, crushed rock, vitrified salt-glaze clay pipe, and the like, are a necessity in every community. They are mineral in nature but the establishment of plants for their production is usually a local and elementary problem. Yet it is probable that an economic study of the problem in every locality will show that such nonmetallic mineral commodities are not always obtained in the most economical way, or in the best quality. Other nonmetallic minerals are of such value that they may be shipped for long distances and sold in sufficient quantities to establish prosperous commercial ventures. Among these are phosphates, barium compounds, borates, nitrogen compounds, magnesium compounds, sulfur, asbestos, and potash. Success in marketing such products depends on quality, production cost, transportation, and similar conditions.

Jan 1, 1932

By S. F. Emmons

Br far the greater number of the members of this Institute are men who are engaged in the strenuous work of the technical part of their profession, and find little time for the abstract scientific work which is less distinctly practical and pecuniarily emunerative. There is, however, a small but increasingly numerous class whose members devote themselves to broad geological problems which underlie the systematic development, and whose work, theoretically, ought to precede and form a basis of that of their more practical brethren. These are the so-called mining or economic geologists, who are, for the most part, connected with State or National geological surveys. From the character of their work, the life of these men necessarily follows rather different line's than that of most of their colleagues, and is not generally familiar to them. It seems admissible, therefore, that to the life of a prominent member of this class, who died during the past year, having literally sacrified his life to his work, a more extended notice should be given than the relatively small number of his contributions to the Transactions might seem to justify. George Romans Eldridge, son of Ellery and Sarah (Mathews) Eldridge, was born on Cape Cod at Yarmouth, Mass., Christmas day, 1854. His boyhood education in the public school at Yarmouth was followed by a six years' course in the Public Latin School at Boston, from which lie entered Harvard Uni¬versity in 1872, being graduated with the highest rank in his class in the natural sciences in 1876. During his college course he spent the summers of 1875-6 at Cumberland Gap, Ky., as volunteer aid to Prof. N. S. Shaler, who was then in charge of the State Geological Survey of Ken¬tucky. This vacation work, undertaken by him rather as a pastime, gave him his first leaning toward geology. Soon

Mar 1, 1906

Jan 1, 1917

[†AARONSON, ALFRED E., Vice-Pres., Mid-Co. Petroleum Co., Mid-Co. Bldg. Tulsa, Okla. '18 ABADIE, EMILE R., Min. Engr Address wanted. '76 ¦ABADILLA, QUIRICO A. Geol. Dept. Cia. Mexicans de Petroleo "El Aguila," S. A., Edifico "El Aguila," Esq., Calles Aurora y Comercio,] [ ]

Jan 1, 1925

By JOHN R. SUMAN

IT appears now that the conflict with the totalitarian states will be a long-drawn-out struggle. The course of this war up to now indicates that this may well be the first major conflict where man power has not been the vital and determining factor. Mechanized warfare has made it possible for relatively small, well-equipped groups to outmaneuver and defeat large armies which lack the necessary modern equipment. Under these circumstances, ultimate victory becomes a matter of resources and productive ability. The important question is not how many soldiers can he put into the field, but the volume and speed in producing the armaments essential to ensure a victory. The resources available to the opposing nations and the efficiency of their systems of enterprise and production will be primary factors in determining the ultimate outcome. Germany had a head start of eight years in the armament race, and it is not easy to overcome such an advantage overnight.

Jan 1, 1942

By William Campbell

(Cleveland Meeting, October, 1912.) THE structure of iron and steel, though the object of so much study and research for the past 25 years, is by no means thoroughly understood. In the first place, we have three or more distinct iron-carbon thermal diagrams, each with its own supporters, and each representing a theory of the structure and constitution of cast-iron. In the second place, by reason of the fact that austenite, the solid solution of carbon in iron, decomposes in the solid state into ferrite, or pure iron, and cementite (Fe3C), and that quenching from above this transition-range, no matter how rapid, cannot entirely prevent the change and thus preserve the austenite by itself at ordinary temperatures, it happens that under the microscope we find, in addition to the ferrite, Fe3C, and austenite, which the thermal diagram of steel requires, it series of transition-products with distinctive structures, to which have ,been given the names martensite, troostite, sorbite, etc. Now these transition-products, in addition to the solid solution, austenite, have been the source of much controversy, at times very bitter. One side would insist that, say, troostite was an entity, which the other side would deny, pointing out that it must be a transition-mixture, with a particular structure. That austenite was a solid solution of carbon in iron has been denied by one school ; we have been told that Fe24C dissolved both Fe3C and Fe, and thus gave rise to a whole series of quenching-products-all this in spite of the fact that no matter how the thermal diagrams differ in regard to cast-iron, they all agree in regard to the solid solution, austenite, for Fe24C finds no place on the diagram. Thus it happens that while the authorities fight both in regard to the iron-carbon diagram and the structures met with in hard- * Associate Professor of Metallurgy, Columbia University in the City of New York.

Dec 1, 1912

By E. J. ENGEL

The New York talc deposits of commercial importance are in St. Lawrence and Lewis counties, in the northwest Adirondack Mountains (Fig 1). All of the deposits are of pre-Cambrian age and occur within highly deformed and recrystallized marble of the Grenville series. The deposits in St. Lawrence County, near Gouverneur, are the largest and most productive of their type known in the Western Hemisphere. In 1948 the seven mines which are in operation will produce about 130,000 tons of ground talc. All talc production in Lewis County is from one mine. There the annual production ranges from 15,000 to 30,000 tons. These so called talcs of New York State include earth materials of differ- ent chemical and mineral compositions. In general the mineral talc is sub- ordinate in amount to other minerals in both the Gouverneur and Natural Bridge deposits.

Jan 1, 1949

By H. H. Campbell

The following paper deals almost exclusively with the results of practice at the works of the Pennsylvania Steel Company at Steelton, Pa. From the records of the furnaces at this plant, both acid and basic, large and small, are drawn the data for the various demon strations, and on a long and intimate experience with their opera tions are founded many theories and generalizations. It may seem that universal laws should not be built upon a basis so restricted ; but in reality the condition is the strongest guarantee of validity. Each table investigates some- certain variable, and by virtue of the common origin of the factors, we have good ground for assuming the corresponding agents to be equal. The examples may or may not be instances of good practice, and may be open to criticism if regarded solely as exponents of • metallurgical success. But it must be remembered that the lists are not made up of selected specimens, nor are they chosen to show su perior results; they are gathered to investigate, by strict scientific methods, the formula? of the operation. In such work no untoward results should be eliminated, save those which bear upon their face the stamp of experimental error. If the worst members be omitted, then the best must also be omitted. Only by using every available case can an honest attempt be made to deduce a true average. It is recog nized, however, that with the most careful selection it is difficult, if not impossible, to collect data representing universal conditions. In each table the records tell of a special practice, and all conclusions drawn from them are true only within the limits between which the equations have been integrated. Not assuming the prerogative of speaking for American melters in all the opinions herein expressed, nor acting as a camera in por traying an ephemeral state of national metallurgical development,

Jan 1, 1894

By H. W. Turner

Lying to the east of the Rio Grande, in central New Mexico, is a long N. and S. mountain range, broken into separate ridges at several points. These have received separate names; the mountains at the south end, near El Paso, being known as the Franklin mountains, and then, following successively, to the north, the San Andreas range, Sierra Oscura, Manzano and Sandia mountains. At the eastern base of the Sierra Oscura there are several low ridges, remarkable for their red color. All of these red ridges contain reefs of copper-ore. The eastern flanks of the Sierra Oscura are composed of limestone. Some fossils in the limestone were examined by Prof. J. P. Smith of Stanford University, who says they are Fusulina and indicate an Tipper Carboniferous age. The sandstones and shales containing the copper-reefs directly overlie this limestone (Fig. I), and are very likely of Permian age, like the similar beds in Texas, described by Mr. W. F. Cummins.* Overlying the copper-beds are red sandstones and shales in which very little copper has been found. The cupriferous zone and the red sandstones and shales are everywhere associated, and as one stands on a high point, he will see that these rocks form three main belts or lines of hills. These may be referred to as the northern, middle and southern belts. The northern belt was not visited by me, but is known to contain copper-deposits. The middle belt has a trend of N. of W. and S. of E. The copper-reefs have been traced for a distance of more than 2 miles. The southern belt has a trend of about N. 30' W. and S. 30°

Jan 1, 1903

By A. B. Johnson, J. S. Browning

The USBM has developed new and improved physical beneficiation techniques for economically recovering potash minerals from high-clay and low-grade ore from the Permian Basin of New Mexico. With the depletion of the high-grade ores a need for changes in industry's standard methods of recovery is a must. Technology may be improved in the beneficiation of the ore prior to mineral flotation and in brine clarification from the desliming phase to effect a reduction of losses of fine potash and brine in the disposal of the clay slimes. This report summarizes the results of these tests and demonstrates the feasibility of producing products that meet the requirements of the agriculture market, namely, 95% KCl equivalent to 60% K2O with recoveries ranging between 80 and 90%.

Jan 1, 1973

By Byron B. Morton

NICKEL-BEARING alloys are associated with petroleum in the fields of exploration, production, and refining. In the first- named field the geologist of today makes use of such instruments as the seismograph, torsion balance, and magnetometer, the selection of proper alloys and metals for the manufacture of which is an important matter. Nickel-bearing alloys are useful for parts that require resistance to corrosion or that must have non-magnetic properties. Where special co- efficient of thermal expansion are de- sired, they are obtained by using alloys high in nickel (20 to 60 per cent), since, by varying the nickel contents, alloys can be obtained ranging fro111 "Invar", with a low expansion between -40 and 175 cleg. F., to those with coefficients of expansion exceeding that of steels. The latter are obtained by additions of chromiurn to the alloys. Alloys containing 50 to 80 per cent of nickel, which possess high magnetic permeability, find application in certain instruments where this property is important.

Jan 1, 1935

By Ralph M. Hunter

UNTIL recent years, maintenance of surface coal handling facilities was a relatively simple task. Equipment consisted principally of conveyors, screens and crushers of comparatively simple construction. Electrical equipment consisted of motors and starters, with little, if any, interlocking. In most cases failure of any component affected only the grades of coal loaded so that even a prolonged break-down did not affect mine operation materially. However, with the introduction of modern cleaning plants, the picture has changed. The equipment is much more complex and therefore more difficult to maintain. In many cases failure of any component of the plant prevents loading of coal. Even if provision is made to by-pass, the quality of coal loaded is lowered, affecting markets. In the case of plants designed to permit full seam mining, marketable coal cannot be loaded without operation of the cleaning plant. Under these conditions it is apparent that considerable thought and effort toward better maintenance are justified. In order to assure continuous, efficient and economical operation, maintenance should receive consideration, not only after the plant is in operation, but while it is being designed. It is hardly necessary to say that the designer should strive for sturdiness and wearing qualities. It is sometimes not realized, however, that even the best parts will sooner or later require replacement or repair. The designer should, therefore, give consideration to accessibility. Anyone who has had to do with cleaning plant maintenance is familiar with installations where several hours are required to get at a part that can be repaired or replaced in a few minutes, once it is accessible. As in most cases, experience is the best guide. The men who operate and maintain this equipment know the problems encountered. Whenever available, the opinions of these men should be sought and heeded. As an example, we might consider the refuse elevator on a Chance Cone. Our company is now operating three of these cones, the first of which was installed in 1941, and the latest in 2946. Exact records are not available, but well over 50 pct of delays charged to the Chance Cones have been caused by the refuse elevator. This elevator receives refuse from the cone and carries it to a point above the water level of the cone, discharging onto a dewatering and desanding screen. Since the elevator operates under water and necessarily has close clearances in the lower boot, it tends to jam on large pieces of refuse or tramp iron. The chain, buckets and boot are also subjected to the action of water, sand and refuse, which accelerate normal wear. In case of jamming or chain-breakage it is necessary to drain the elevator and the cone so that even a minor fault in the elevator causes a considerable loss of time for the cone. In our new plant, which will contain two Chance Cones, the refuse elevator has been eliminated. This was accomplished by raising the cone so that the refuse gates could discharge directly onto the dewater-

Jan 1, 1948