Search Documents

By Edmar de Souza Silva, Antonio Augusto Gorni, Emanuelle Garcia Reis, Daniel Bojikian Matsubara

Controlled rolling followed by accelerated cooling, known worldwide as TMCP, aims to increase mechanical properties without toughness deterioration. The process principle is to promote the plate cooling with water jets along the range of the austenite transformation temperatures. The accelerated cooling process is only fully effective when controlled in an integrated manner, as it alone cannot ensure significant improvements in the final properties of steels. Plate surface quality depends on some parameters that must be controlled before the start of the plate accelerated cooling. Good flatness is essential to avoid irregular water accumulations during cooling. After the reheating process, the slab should have uniform temperature, uniform austenitic grain size and easily removable scale. The slab thermal and microstructural heterogeneities are inherited by the rolled plate and tend to increase further during the accelerated cooling. This results in flatness problems, high level of internal stresses and mechanical property variations. The descaling strategy is an extremely important factor and must be determined with great caution. It is important that scale thickness and distribution is uniform to ensure homogeneous cooling over the entire plate surface. Otherwise, there will be an uneven temperature distribution, which can cause serious problems of flatness, surface quality and mechanical properties.

Oct 1, 2019

By K. Adam

Grinding in steel mills adversely affects the flotation of pyrrhotite. The electrochemical nature of inter action between pyrrhotite and active metals was investigated by contacting pyrrhotite with platinum at different applied potentials. Flotation tests, scanning electron microscopy, Auger electron spectroscopy, and X-ray photoelectron spectroscopy were wed to examine the surface properties of pyrrhotite. The formation of hydroxide or oxide and sulfate species of iron through the oxygen reduction reaction at the cathodically polarized surface of pyrrhotite was shown to be the mechanism responsible for the reduced floatability of pyrrhotite.

Jan 1, 1985

By S. Kelebek

DETA exhibits a highly selective depressant action on pyrrhotite without adversely affecting the collectorless flotability of pentlandite and chalcopyrite in nickel-copper ores of the Sudbury region. A simplified Eh-pH diagram has been constructed to illustrate the extended stability of elemental sulphur and to explain the collectorless flotation of pentlandite and chalcopyrite. Cu and Ni ions, which are known to exist on the surface of pyrrhotite, promote the flotation of this mineral whether a collector is present or not. Thermodynamic calculations indicate that the action of DETA involves the sequestration of Cu and Ni ions from surfaces under a wide range of redox conditions; analysis of flotation test filtrate indicates as much as a 20-fold increase in the concentration of Ni and Cu ions. It appears that DETA may enhance the self-hydrophobicity of chalcopyrite and pentlandite by exposing more of the sulphur-rich surface sites for bubble contact in flotation. There are various possible explanations for its depression of pyrrhotite

Jun 18, 1905

By A. Idegami, M. Imamura, S. Heguri, Y. Ozaki

"Nickel powder can be produced by the reduction of a nickel ammine complex solution by hydrogen at high temperature and pressure. To minimize the deposition of fine nickel on the surface of the reactor and other equipment, seed crystals are added to the initial solution to promote nucleation of the nickel powder. Such seed crystals catalyze the precipitation of the nickel particles on the surface of the seed and enhance grain growth. In this study, nickel nuclei were precipitated by the addition of a polymer to the nickel ammine complex solution, resulting in the production of nickel powder. Thus, we herein propose a model that explains the effect of the polymer in the precipitation of nickel nuclei.INTRODUCTIONNickel powder is commonly produced via a hydrometallurgical process from the hydrogen reduction of a solution containing a nickel ammine complex at high temperatures and pressures, and this process was commercialized in the 1950s by Sherritt Gordon (Sherritt International, Canada, Benson & Colvin,1973; The Staff, Research and Development Division, Sherritt Gordon Mines, Ltd., 1958).In the above transformation, upon the injection of hydrogen gas into the solution, nickel is reduced as outlined in Equation(1), ultimately resulting in the production of nickel powder.Ni(NH3)nSO4+ H2?Ni+ (NH4)2SO4+ (n-2)NH3(n:2–6)(1)In this process, seed crystals are added to the reactor to suppress the precipitation of fine nickel (scaling) and to enhance nickel reduction (Benson & Colvin, 1973; Mackiw, Lin & Kunda, 1957). More specifically, iron sulfate and a small amount of dispersant polymer are added, which leads to the formation of nuclei. Upon subsequent hydrogen reduction, the reduced nickel can then be deposited on the nuclei, allowing nickel particle growth to take place. However, this results in iron contamination in the final nickel product, and so the use of pure nickel as a seed crystal is desirable to produce high quality nickel powders."

Jan 1, 2017

By H. Fukushima, T. Ohgai, N. Baba

The electrodeposition behavior of Zn and the morphology of the deposited Zn were studied in electrowinning solutions containing polymer additives such as gelatin and polyethylene glycol (PEG). The cathode potential was shifted in a less noble direction and the polarization resistance for Zn deposition increased with increasing concentrations and molecular weights of both gelatin and PEG added to the electrolytic solutions. However, when the molecular weights of these additives exceeded about lxlO4, the cathode was depolarized and the polarization resistance for Zn deposition decreased with increasing molecular weight. The crystal grain size and the (002) orientation of the deposited Zn became smaller when the concentration and molecular weight of the additives increased, and the cathode was polarized.

Jan 1, 2000

By Ven Mercade

The flotation of calcite has been studied by many investigators, especially in terms of type of collector; pH; and metal ions that activate and, more importantly, depress the flotation of calcite (1)(2). Research was extended to the investigation of the effect of polyvalent metal salts and sodium silicate using these materials added separately or in mixtures (3)(4)(5)(6). Flotation of calcite was also studied with respect to its function as a carrier in the beneficiation of kaolin clays by Ultraflotation (7) (8) (9). The carrier used in Engelhard Minerals & Chemicals Corporation's industrial Ultraflotation operation is calcite. This fact, coupled with the continuing interest in Ultraflotation phenomena, led to a study to determine the effect of polyvalent metal-silicate hydrosols on the flotation of calcite.

Jan 1, 1978

By G. M. Zhao

The gasification of lump coke with CO2 was studied in a fixed-bed reactor. The effective diffusivity of the gas was evaluated from measurements of the reactivity of the lump coke, produced by BHP Steel in New South Wales, and from kinetic parameters that were determined from the reactivity of fine grains. The grain model of effective diffusion in porous media was adopted to express the gasification rate of the lump coke and was found to fit the experimental data well. The relationship between reactivity and textural characteristics of the coke was examined

Jun 18, 1905

By S. S. Rahman, A. Gholami, M. A. Aghighi

"This paper provides a foundation for studying the growth of fractures in presence of other discontinuities and different anisotropies of low permeable hydrocarbon formations and helps to improve the design strategies for multistage fracturing.The multistage fracturing technology has recently been used to exploit low permeable hydrocarbon reservoirs. However, the mechanism of hydraulic fractures interaction and the impact of local heterogeneities on ultimate trajectory of the growing hydraulic fractures are not yet understood in depth. A fully coupled poroelastic Finite Element based model is developed to investigate the mixed mode propagation behaviour of growing hydraulic fractures. This model takes advantage of an explicit representation of the fracture which enables us to take the effects of rock and fluid related parameters into account. Moreover, impact of fracture geometry and leak-off phenomenon is investigated. The refined mesh around the crack provides the added advantage of more detailed stress distribution, pore pressure change and back stress in the vicinity of the fracture and in particular at the fracture tip. The potential deviation propensity of the fractures is evaluated based on the fundamental rule that fractures propagate perpendicular to the direction of the minimum horizontal stress.This study shows that pressurization of transverse hydraulic fractures results in the reorientation of local principal stresses, particularly in vicinity of fracture tips. Variation of flow patterns clearly influences the evolution of shear stress around the fracture tips which will potentially lead to mixed-mode I and II fracturing and consequently, fracture deviation. The presence of local heterogeneities such as preexisting fissures and/or fractures is a main source of such pore pressure induced stress redistribution and reorientation and potential deviation of hydraulic fractures.Most existing models ignore or simplify the effect of pore pressure/stress coupling as well as the fracture geometry and fluid flow within the fracture. Also, the fluid leak-off from the hydraulic fracture into the formation, which is a controlling factor in fracture growth, is often considered using analytical models. Taking advantage of a fully coupled porelastic model along with an explicitly discretized fracture, this study provides a more realistic insight into the complex fracture propagation processes of multistage fracturing operations particularly in presence of reservoir geo-mechanical complexities."

Jan 1, 2015

By J. -P. Tshibangu, M. Ramos da Silva, F. Descamps, C. Schroeder, J. -C. Verbrugge

"The mechanical behaviour of rock materials is largely influenced by the stress state and pore pressure; this needs to be considered in many applications, such as petroleum engineering, tunnelling or stability of underground excavations.Conventional triaxial tests (d2 = d 3) are generally used to assess the influence of confining and pore pressure. In this work, those tests are performed on a porous rock named Sorcy limestone, along with more advanced stress paths like triaxial extension (d 2 = d 1) and purely deviatoric tests with independent pore pressure control. Those tests are combined to a true triaxial study on the dry rock in order to investigate the effect of true triaxial stresses and, hence, build three-dimensional limiting envelopes accounting for the influence of pore pressure.Three-dimensional limiting envelopes of dry Sorcy limestone are built in meridian and octahedral planes. The shape of the octahedral sections changes with the mean stress from triangular to hexagonal and then quasi circular. At even higher mean stresses, the evolution continues towards a triangle with apexes oriented in the direction of triaxial extension stress states. In meridian sections, the deviatoric stress first increases with the mean stress. The transition between this deviatoric mechanism and the cap surface occurs at different mean pressures depending on the Lode angle.Terzaghi’s effective stress is found to govern the yield and plastic behaviour of saturated Sorcy limestone. Triaxial tests show that the limiting envelope does not depend on the loading path (conventional compression and purely deviatoric stress paths). In triaxial extension, the brittle-ductile transition is observed for a higher mean pressure than in triaxial compression, as previously found for true triaxial tests on the dry rock.Finally, it is shown that upon appropriate normalisation, the dry and saturated yield envelopes come very close one to each other. This suggests that only the size of the yield envelope changes between dry and saturated state (pore pressure = 5 MPa); its shape does not seem to evolve."

Jan 1, 2015

By Gheorghe Marin, Franco Chiesa, David Levasseur, Bernard Duchesne

Over the past 20 years, pressure die casting has evolved to a point where structural parts can now be produced by this process. This has been made possible by the development of vacuum die casting and by the development of die-castable, low iron content alloys. This resulted in the production of low porosity, weldable die-cast parts on which heat treatment may be applied. In the present paper, the influence porosities on the tensile properties of as-cast A360 tensile test bars was evaluated. This was done by casting 24 clusters, comprising three 6mm diameter test bars each, in a 280T cold chamber pressure die casting machine after a steady dynamic equilibrium had been reached. Modeling of filling allowed to explain the differences in porosity observed in the 3 samples of a same cluster while the results of solidification modeling were related to the microstructure. Tensile samples were radiographed on a real time X-cube apparatus and separated into 2 lots: samples where no porosity defect were visible and samples with visible defects. By measuring the tensile properties of the 2 lots it was possible to quantify the drop in tensile properties brought about by porosity, which is the most common defect observed in pressure die-cast parts.

Jan 1, 2015

By Chih-Huey Lin

The Au/?-Al2O3 catalyst prepared by AuCl3 impregnation is subjected to the influence of residual chlorine after an oven drying. A post-impregnation NH4OH treatment was able to eliminate chlorine, and to reduce the cluster size of Au moiety. However, the CO oxidation activity was not increased by this post-impregnation NH4OH treatment. This suggests that certain metal-support interaction (MSI) is the determining factor for the activity of Au catalysts. Thermal treatment under H2, O2 or He was attempted to increase MSI of the prepared catalyst with or without the post-impregnation NH4OH treatment. No significant activity enhancement was found but the TPD analysis suggests that a H2 treatment has a higher chance to induce MSI.

Oct 1, 2003

By Yang Hong-ying, Yu Juan

Electrochemical behavior of natural chalcopyrite in electrolyte solution at pH value of 6.97 was studied by cyclic voltammetry, X-ray photoelectron spectroscopy and electrochemical impedance spectroscopy. The results showed that the electrochemical processes occurred on electrode surface were controlled mainly by the growth of sulfur species at lower applied potentials (<0.35Vvs.SHE), and the oxidative dissolution of sulfur species and the hydroxylation of iron at higher applied potential (>0.45V). The EIS spectra of oxide product layers could be illustrated by the equivalent circuit of Re(QdlRct(QfRf)), and the degree of hydrophilicity for chalcopyrite was higher when the value of charge transfer resistance Rct. was greater. The optimum potential range for the floatation of chalcopyrite in collectorless solution at pH value of 6.97 was between OCP (0.165V) and 0.35V.`

Jan 1, 2015

By S. Nakamura, K. Fujiwara, S. Hirosawa, S. Tsukamoto, Y. Koshino, Y. Aruga

"In this study, hardness test, differential scanning calorimetry(DSC)and transmission electron micros copy were carried out to investigate the age-hardening behavior of Al-Mg-Si alloy with a Mg+Si concentration of 1.5mass%, and a Mg/Si ratio of 1.0. Pre-aging treatment was conducted for the solution-treated and then water-quenched specimen at 100, 80, 60, 40, 20 (natural aging), 0 and -20°C for 20min or 5h, followed by artificial aging at 170°C for 20min. It was found that when pre-aging time is prolonged from 20min to 5h, the bake-hardening response is deteriorated irrespective of the pre-aging temperature. In particular, the specimens subjected to pre-aging at 20-40°C for 5 h hardly increased the hardness with the subsequent artificial aging. From the results of DSC measurement, it was suggested that as pre-aging temperature is lowered, the amount of solute clusters formed during pre-aging, i.e. Mg-Si clusters and Si-rich clusters, is decreased, but the ratio of Si-rich clusters is increased, resulting in the deteriorated bake-hardening response.INTRODUCTIONIn recent years, Al-Mg-Si alloys have been widely used forautomotive body panels due to their excellent characteristics such as high strength-to-weight ratio and good formability. Their strength is increased not only by artificial aging during paint-bake treatment; i.e. “bake-hardening”, but also when kept at room temperature(RT);i.e. “natural aging”, in association with the suppressed bake-hardening response. Such a “negative effect of two-step aging” has been a serious problem because Al-Mg-Si alloy coils are unavoidably maintained at RT in the manufacturing process of body panels; e.g. shipping and storage. However, it was reported that pre-aging above 70°C before the two-step aging can restore the bake-hardening response, and such an improvement is related to the formation of solute clusters(Sato, 2006; Abidet al., 2010; Takaki et al., 2014; Zandbergen et al., 2015). From the comprehensive analysis by three-dimensional atom probe (Aruga et al., 2014 and 2015), it is believed that Mg-Si clusters formed during pre-aging transform into the strengtheningß"" phase, whereas Si-rich clusters formed during pre-aging act as a detrimental precursor of ß""phase. In this study, it was aimed to investigate the effect of pre-aging conditions, especially pre-aging temperature and time, on the formation of solute clusters during pre-aging, in order to elucidate the mechanism of the age-hardening behavior of an Al-Mg-Si alloy."

Jan 1, 2018

By J T. Woodcock, G J. Sparrow

A sample of pyrrhotite flotation concentrate pulp assaying 15.3 g/t Au, which had been prepared from an old tailing dump, was treated to extract the gold. Examination of the concentrate with an SEM showed that exposed or free native gold, 5- 40 ¦m in diameter, was present but no locked gold was observed. Direct cyanidation of the concentrate to extract the gold showed that the flotation reagents present inhibited gold extraction. A range of pre-treatments was used to overcome these effects. Direct cyanidation for 48 h extracted only 26 per cent of the gold, indicating possible contamination of the gold in the concentrate with flotation reagents. Pre-treatment of the concentrate pulp by aeration for 24 h, or by 72 h aeration with an addition of 3.65 kg/t of sodium sulphite, gave little improvement in gold extraction by subsequent cyanidation. Pre-treatment by filtration, or by aeration with 12.5 L/t 100 volume hydrogen peroxide, followed by cyanidation for 48 h gave gold extractions in the range 67-77 per cent. Combining filtration and an aeration period with hydrogen peroxide addition raised the subsequent cyanidation extraction of gold to 88 per cent, giving a tailing assaying 1.5 g/t Au. Re-cyanidation of some of the dried tailings from the initial tests extracted most of the remaining gold giving a tailing assaying 0.5 g/t Au. This indicated that most of the gold was available for dissolution by cyanide. The poor dissolution of gold by cyanidation of the untreated concentrate was attributed to the presence of flotation reagents. It was shown by UV spectrometry that xanthate-containing compounds were present in the solids fraction of the original pulp and that they were partly removed by pre-treatment. MIBC was also present, and dithiophosphate, which was used in the flotation step, was also probably present. The results indicated that the improvement in gold extraction after filtration and oxidation of the original pulp was due to partial removal of the flotation reagents, and illustrates the detrimental effects that residual flotation reagents can have on the extraction of gold by cyanidation of a flotation concentration.

Jan 1, 1990

By Sparrow GJ, Woodcock JT

A sample of pyrrhotite flotation concentrate pulp assaying 15.3 g/t An, which had been prepared from an old tailing dump, was treated to extract the gold. Examination of the concentrate with an SEM showed that exposed or free native gold, 5-40 ¦m in diameter, was present but no locked gold was observed. Direct cyanidation of the concentrate to extract the gold showed that the flotation reagents present inhibited gold extraction. A range of pre-treatments was used to overcome these effects.Direct cyanidation for 48 h extracted only 26% of the gold, indicating possible contamination of the gold in the concentrate with flotation reagents. Pre-treatment of the concentrate pulp by aeration for 24 h, or by 72 h aeration with an addition of 3.65 kg/t of sodium sulphite, gave little improvement in gold extraction by subsequent cyanidation. Pre-treatment by filtration, or by aeration with 12.5 L/t 100 volume hydrogen peroxide, followed by cyanidation for 48 h gave gold extractions in the range 67-77%. Combining filtration and an aeration period with hydrogen peroxide addition raised the subsequent cyanidation extraction of gold to 88%, giving a tailing assaying 1.5 g/t Au.

Jan 1, 1990

By Jianping Li, Fei Peng, Yunbo Xu, Jiayu Li

In this study, in order to achieve ultra-high strength without reducing plasticity, a novel heat treatment involving a pre-quenching process prior to conventional intercritical annealing (P-IDP) was proposed in a low carbon low alloy DP steel. It revealed that abundant fraction of banded structure was observed after conventional intercritical heat treatment (IDP) due to the inheritance of cold rolling deformation. However, the banded structure in novel heat treatment was eliminated significantly, whilst the refined microstructure was relatively more homogeneous with ultrafine ferrite grains. Moreover, obvious chain-networked martensite grains along the ferrite grain boundaries were obtained. The optimum mechanical properties with ultimate strength of 1238 MPa, total elongation of 17%, product of strength and elongation (PSE) of 21GPa% were obtained by P-IDP treatment, which was much higher than the values reported with similar composition. As to pre-quenching treatment, all of grain refinement, homogeneous distribution of martensite islands and precipitated strengthening of microalloyed carbides were beneficial to improve the final strength and ductility.

Oct 1, 2019

By A. T. Tye

REGARDING the results of preferential flotation at Cananea, Weinig has stated that "The concentrating mill of the Cananea Consolidated Copper Company at Cananea, Mexico, furnishes an excellent example of modern flotation practice. The complete figures are given because they present so forcibly the advantages of modern selective flotation."&apos; L. O. Howard notes that "Perhaps the outstanding example so far published of improvements in results through the use of selective flotation is that at Cananea, Mexico." The following notes indicate the conditions under which the results were obtained at Cananea; also the effect of preferential flotation at the concentrator and at the smelter. In the majority of cases the full benefit of selective flotation is not fully realized, as the concentrates are shipped from the mill to smelters owned by other companies. The saving made at a certain concentrator by this method of flotation may be well understood but the saving resulting at the smelter from the results of preferential flotation at the mill is not so apparent, as the data are contained in the smelting records of some other company. Even at the smelter the great gains following preferential flotation may not be noted, as a variety of ores and concentrates from various sources are received and the difference from the changed concentrator operations of a certain mill may be obscured. As noted by Professor Weinig and Professor Howard, the results obtained at Cananea brought about a veritable metallurgical revolution at the smelter. There are probably plants at which a better preferential separation is being made than at Cananea. Many ores contain barren iron pyrite which, when depressed, does not carry copper into the tailing. Some concentrators use clean uncontaminated water for milling and in others the ore is ground much finer than at Cananea. All of these items are concerned in perfect separation. The details of preferential flotation at Cananea, therefore, are not presented on account of the perfection of the

Jan 1, 1928

By A. T. Tye

REGARDING the results of preferential flotation at Cananea, Weinig has stated that "The concentrating mill of the Cananea Consolidated Copper Company at Cananea, Mexico, furnishes an excellent example of modern flotation practice. The complete figures are given because they present so forcibly the advantages of modern selective flotation."&apos; L. 0. Howard notes that "Perhaps the outstanding example so far published of improvements in results through the use of selective flotation is that at Cananea, Mexico."2 The following notes indicate the conditions under which the results were obtained at Cananea; also the effect of preferential flotation at the concentrator and at the smelter. In the majority of cases the full benefit of selective flotation is not fully realized, as the concentrates are shipped from the mill to smelters owned by other companies. The saving made at a certain concentrator by this method of flotation may be well understood but the saving resulting at the smelter from the results of preferential flotation at the mill is not so apparent, as the data are contained in the smelting records of some other company. Even at the smelter the great gains following preferential flotation may not be noted, as a variety of ores and concentrates from various sources are received and the difference from the changed concentrator operations of a certain mill may be obscured. As noted by Professor Weinig and Professor Howard, the results obtained at Cananea brought about a veritable metallurgical revolution at the smelter.

Jan 1, 1927

By D C. S M, J Skudder, R F. Sandenbergh

Metallic sulfide minerals present in most gold ores, Morila gold ore included, often decompose under typical gold leaching conditions. The reactions and their products consume oxygen and sodium cyanide, consequently competing for oxygen and cyanide used in gold dissolution. The resultant effect is to reduce both the kinetics of gold dissolution and overall extraction efficiencies. The present paper discusses results obtained from plant data analysis and laboratory work investigating the problem of higher than expected consumption of sodium cyanide at Morila Mine Gold Plant. Cyanide consumption at the Morila Mine Gold Plant had been consistently running at 46 per cent higher than the expected value without any corresponding increase in gold recovery. In fact, plant data analysis showed an inverse relationship between cyanide consumption and grind, as well as cyanide consumption and gold recovery. Experimental and plant data analysis indicated that better control of the [CN-]/[O2] ratio is necessary for the efficient use of reagents and achievement of higher gold recoveries. Careful control of this ratio at a minimum of eight enabled the reduction of sodium cyanide consumption by 200 g/t, that is, from 650 g/t to 450 g/t. Coupling these experimental conditions with the addition of lead nitrate at 100 g/t improved the overall gold recovery to 93 per cent compared to the average plant recovery of 90.2 per cent over a six-month period. This improvement was also reflected in the leaching kinetics where 70 per cent gold extraction was achieved after four hours, as compared to 59 per cent in the absence of lead nitrate addition. Also of great importance is the fact that the combination of hydrogen peroxide and oxygen gave inferior performance relative to either of the two reagents used separately. This scenario presents an opportunity for excluding hydrogen peroxide, an expensive reagent, and focusing on improving the oxygen addition system to boost dissolved oxygen concentration in the plant.

Jan 1, 2007

By David Porter, Nathan Rouse

The implementation of presplit perimeter control in underground mining as a method to decrease dilution yields positive benefits throughout the current and future mining cycles. A case study to understand the benefits of reducing overbreak and underbreak in a cut and fill mining cycle was performed to quantify the reduction in backbreak. The study was performed in a control section of the mine where a presplit perimeter control design was utilized for a length of heading. This control heading was then compared to the existing standard blasting design within the same mining zone. The comparison included multiple aspects of the mining advance including overbreak, dilution of waste, dilution of Cemented Rock Fill, bolt counts, and cycle times. Once mining in the control section was completed and mining commenced in adjacent headings, blast damage due to blast design could be quantified.

Feb 6, 2023