By U .. C. Rojas, J .. C. Gomez

"Fire Refined Copper (EI Teniente Three Stars) has been produced at Caletones Smelter of Codelco Chile since almost the beginning of its operations.Due to changing features of the copper market, together with the targets on technical efficiency and productivity, it has become more and more relevant for copper industry to reach both, good final product quality and a proper environmental control.At present, copper refining process at Caletones Smelter takes place in two cylindrical tilting furnaces, where solid fluxes are injected through horizontal tuyeres into the molten bath. (Fig. N2 1)Solid reagents are pneumatically conveyed and injected into the liquid copper bath attaining excellent solid - liquid contact, so the impurities removal efficiencies are found to be high. Same injection tuyeres are used to introduce both oxidising agent (normal air) and reducing agent (reformed gas) into the molten bath. Air or nitrogen is used as conveying gas for solid reagents, depending on the process stage.This pap~r gives a fundamental description of the process and industrial results related to the injection of blend of sodium and calcium carbonates to remove arsenic and antimony, silica and granulated reverberatory slag to remove lead and a mixture of calcium carbonate and mineral coal to reduce the selenium content of the fire refined copper."

Jan 1, 1996

By Lawrence D. May, Harry Mudgett

"In the course of developing a new industrial process, information produced at the Research and Development (R&D) stage is critical to determining the technical and economic feasibility of the project. Understanding the fundamental operating parameters for each unit operation in a flowsheet typically comes from historical knowledge of similar systems or by technical development through a robust research program. This approach holds true for processes incorporating fluidized-bed technology. In this paper, the authors will present a practical approach for performing a research study that will allow a process owner to determine if the concept of using a fluidized-bed system can become a reality. Included are discussions of key steps required at each level of the R&D program, and the critical information required for advancing the project to the next stage.IntroductionThe conduct of a research and development program typically starts with a process owner identifying a new industrial need or modification to an existing operation. The owner can pursue this need through multiple routes, including initial in-house development, coordination through an engineering firm, contacting suppliers of key equipment envisioned for the process, or through direct contact with research and development organizations. Where and when the project is conducted is as variable as the number and types of owners who pursue them. Factors that can influence the decision of where to conduct a research program can include the type of process desired, the scale and scope of the project, the location of the project site relative to the R&D options, the experience, capability, and availability of the potential research sources, and the costs to conduct the program. Often, the owner may choose a combination of the available resources to achieve their objectives. In the end, the owner's choice should be based on a thorough understanding of their goals and objectives for the program, and a good understanding of how to measure success while achieving those objectives. Herein, the authors will describe the methods we have typically used to develop the information an owner needs to make an educated decision for investing in a new or modified process."

Jan 1, 2014

By Onuralp Yucel, Ahmet Turan, Murat Alkan, Hasan Ozer

SHS (Self-propagating High-temperature Synthesis) is one of the important methods to synthesize B4C powders. The process contains the reaction of boron oxide powders (B2O3) with magnesium reducing agent and carbon black carburizer. SHS products are leached in HCl media to purify synthesized B4C powders in the following step. In the present study, effects of various functional additives (KClO3, KHSO4, MgSO4.7H2O, NaCl, MgO and Na2SO4) in the SHS stage were carried out. Various proportions of the additives were mixed with the initial SHS charge mixtures. Two different molar ratios were employed in the initial SHS mixtures as 1:3:0.8 B2O3:Mg:C and 1:2.5:0.8 B2O3:Mg:C. After the SHS step, HCl leaching process was applied to the SHS products. Filter cakes were dried and characterized by using X-Ray Diffraction Spectroscopy, BET and chemical analysis techniques.

Jan 1, 2015

By Mostafa O. El-Bealy

"To estimate the interdendritic cracking tendency in casting processes, a new model for interdendritic cracking criteria has been proposed. The model combines a concept of the alloying element effect on the interdendritic strain generation and therefore on the susceptibility of interdendritic cracking phenomena. A susceptibility of interdendritic cracking is modeled by using El-Bealy's interdendritic cracking susceptibility function ""BJCSF' and the opening displacement between the dendrites ""EIA "". These concepts are modeled based on the previous experimental observations and ElBealy' approach. The model is implemented numerically for a one-dimensional model problem with some similarities to the casting of steel. The variation of some key parameters that are known to influence the frequency and severity of the interdendritic cracking is then studied.I. INTRODUCTIONInterdendritic cracking ""hot tearing"" commonly encountered in both ferrous and nonferrous castings (1,2]. It is generally believed that interdendritic cracks start to nucleate and develop in the interdendritic strain region within the mushy zone [l-5]. The interdendritic strain region is then definitely coherent, but continuous films of liquid still exit (4,5]. This distinguishes interdendritic cracks from cold cracks forming during the casting process after complete solidification (6,7].Much effort has been put into the understanding of the interdendritic cracking phenomena, and several theories have been proposed. Fellini [8] stated that interdendritic crack ""hot tear"" will result if the material is subjected to too high of accumulated strain within so called vulnerable part of the solidification interval. Kinosita et. al. [9] and Campbell (10] also emphasized the role of tensile stresses in the forming of interdendritic cracks. Most interdendritic cracks criteria simply consider the size of solidification interval, stating that solidification range is associated with a lager interdendritic cracking susceptibility than a short range. Clyne and Davies (11] formulated a more refined such criteria based upon the time spent in different regimes of the solidification interval. They defined a vulnerable region in which thin continuous films of interdendritic liquid exist, and the permeability is low. When thermal strains are induced in this region, the film is not able to sustain the stresses, and an interdendritic crack will form."

Jan 1, 2001

By R. Boom, Y. V. Meteleva-Fischer, B. Kraaijveld, H. Kuntzel

"Segregation of impurities during refining of metallurgical grade silicon (MG-Si) is an option to produce solar grade silicon (SG-Si). Directional solidification is a last step in production of SG-Si effective for removal of metallic impurities. The possibility is investigated to use metallic impurities originally present in MG-Si for removing boron and phosphorus. MG-Si has been treated using two methods: 1) alloying with calcium and 2) refining with Na2O-CaO-SiO2 slag, both by controlled cooling. The microstructure of silicon and the impurities distribution have been studied before and after the treatments. Using EPMA phosphorus and boron have been detected in 1-2 wt% concentration range in several intermetallic compounds in grain boundaries after both treatments. This observation points to a different possible mechanism of silicon refining from boron and phosphorus. Controlled cooling improves migration of phosphorus and boron to the silicide phases in grain boundaries, which can be removed by acid leaching treatment.2. IntroductionStandards for silicon solar cells and growing demand on “green” energy require economical and efficient route to the production of solar grade silicon. Refining of cheap metallurgical grade silicon is one of the promising options, where application of existing metallurgical approaches can result in cost-efficient production on industrial scale. Focus in refining is on impurities, which are most difficult to remove: B, P, Al, Ti, due to their large segregation coefficient in silicon and low vapour pressure [1]. Moreover, more environmentally friendly technology in comparison to the traditional Siemens process [2] will be in accordance with societal needs. Based on properties of common impurities in metallurgical grade silicon, alloying refining and slag refining are suggested as competitive techniques having potential effect on removal of impurities harmful for conversion of solar energy [3, 4]. Alloying with Ca followed by acid leaching was found to be effective for removal of Fe and Ti from silicon [5] and to enhance also removal of boron [6] and phosphorus [7, 8]. In the work of Inoue et al. [8] drastically increasing removal of phosphorus from silicon has been observed with an increase of Ca content and a thermodynamics-based explanation was provided. Since phosphorus has been found to condense in the secondary precipitate mainly composed of CaSi2, it can be removed together with iron and titanium by consecutive acid leaching treatment. Slag refining is one of the metallurgical methods proposed to be effective for refining of metallurgical grade silicon from boron [9, 10]. Slags with additions of the following oxides to silica have shown positive effect on removal of boron: CaO [11-13], Na2O [11,14]. Mechanism of slag refining from boron is based on oxidation of boron followed by its incorporation in the slag network [9,11]; the same mechanism is suggested for refining from phosphorus taking into account that oxides of boron and phosphorus are known as network-formers [15]."

Jan 1, 2012

By A. H. Rhoades

The modern polarizing microscope with such accessories as cameras, infrared devices, reflectance and/or transmission photometers, indention hardness, and heating stage is used to characterize coal, coke, and other carbon forms. It allows characterization of coke by-products, such as tars and pitches and their insoluble residues. A useful product of the microscopic approach is the coal petrographic analysis which permits the prediction of coke strength carbonization pressure and volume change. Carbonization tests are expensive, time-consuming and require large amounts of coal. Tests on the coke show it to be strong or weak but give no indication of why. Petrographic analysis requires grams of coal and yields data that indicates why the coal produces coke of a given quality. Small samples from drill cores are sufficient for petrographic analysis. These data are also used to optimize blends for coke production. When coke-plant problems occur, ~he microscope can be used to check the coal blend proportions, as well as for weathered coal. Microscopy is useful in spore correlation work which may be a prerequisite to sound coal reserve estimates. Dispersed vitrinoid reflectance studies are used to determine the degree of organic metamorphism which serves to establish oil and gas deadlines. Tars and pitches are examined microscopically for the amount of normal solids as well as the size of undesirable carry-over solids resulting from pollution abatement practices in coke works. The microscope is also used to study coals for gasification and liquefaction.

Jan 1, 1981

By T. Nagano

Mitsubishi Metal Corporation started the development work of a new process for continuous production of copper in 1961. After a series of experimental and semi-commercial operations, the first commercial plant of the Mitsubishi Continuous Copper Smelting and Converting Process was put into operation in March, 1974. The new plant, which has a design capacity of 4,000 metric ton copper per month, was built within the premises of Naoshima Smelter, replacing the old No.1 reverberatory smelter there. The SO2-rich exhaust gas from this new plant is blended with the off-gas of the No.2 reverberatory furnace for production of sulfuric acid and the overall emission of sulfur at Naoshima has been greatly reduced. The operation of the continuous plant has been satisfactory and several advantageous features of the Mitsubishi Process have been proven on a commercial scale. This paper first gives a brief description of the history of the development work and the characteristic features of the process. The paper then describes the new commercial plant and operating data obtained so far.

Jan 1, 1976

By Peter R. Sanford

Cyanides are present as a dilute constituent of streams from a variety of metallurgical and mineral-processing operations. In addition, a cyanide concentration in excess of approximately 100ppb is toxic to aquatic life, and consequently these operations require a waste-treatment process to reduce the already dilute cyanide species by several orders of magnitude. Furthermore, the waste streams may have flowrates in excess of a million gallons per day. The paper reports on research conducted with a laboratory?scale electrochemical porous (graphite felt) electrode (anode) flow-reactor, which was conducted in conjunction with a computer-aided simulation of a mathematical model describing the intrinsic rate-phenomena associate with the electrode processes. The laboratory-scale cell, of rectilinear geometry, was found to be capable of reducing a feed-stream anolyte (KCN-KOH and supporting electrolyte of a single salt ? K2SO4) with a cyanide concentration of 10ppm, to less than 100ppb, at current efficiencies in the neighborhood of 50%. The computer simulation of the cell performance based on the mathematical model (and constraints imposed for tractability) was found to provide only for qualitative agreement.

Jan 1, 1998

By Reza Kamali, Mohsen Bashiri, Hadi Fanisalek

"Half of the input energy to aluminum reduction cell will be lost as waste heat which could be studied for possible recovery. Since price of energy is increasing and the main production cost in primary aluminum industry is energy, so waste heat recovery consideration will be interesting. One of the possible choices for recovering is from aluminum exhaust gases that needs minimum modifications for reduction cell and has no influence on cell heat balance which is vital for the operation. By using heat exchangers with in-line and staggered tube arrangements which placed before fume treatment plant (FTP) we will be able to recover enough amount of heat. The main challenging problem which is necessary to overcome will be the heat exchanger material and its design because of corrosive and dusty exhaust gases from potroom. In this paper, a desalination system with six effects of evaporator is proposed for producing distilled water by using recovered heat from hot exhaust gases. The calculated amount of produced distilled water is around 27,000 / in this specific suggested desalination plant. The suggested desalination plant is based on Hormozgan Aluminum Company data (Hormozal) in Bandar Abbas, Iran which is constructed by the Persian Gulf.IntroductionWaste heat losses arise both from equipment inefficiencies and from thermodynamic limitations on processes. The exact quantity of industrial waste heat is poorly quantified, but various studies have estimated that as much as 20 to 50% of industrial energy consumption is ultimately discharged as waste heat [1]. In order to achieve a final decision for establishing the waste heat recovery plant in any type of industry, a strong feasibility study is mandatory. Also, we need to remember that the possible amounts of energy and suggested process plant for recovery have to be investigated before starting any feasibility study. This kind of study which is important to be finished before moving to feasibility step is mainly a theoretical study, and was done for the Hormozgan Aluminum Company (Hormozal). In addition to the exhaust gases from the potroom, the exhaust gases from anode baking plant appear to have a better potential for waste heat recovery compared to potroom exhaust gases. The average temperature of exhaust gases from anode baking kiln is 120°C higher than the exhaust gases temperature in the potroom. This needs further investigation in a different study, because this study is just focusing on potroom exhaust gases."

Jan 1, 2011

By Kan Song, Lin Liu, Hengzhi Fu, Jun Zhang, Haijun Su, Xiaojiao Jia

"Al2O3/YAG/ZrO2 eutectic in situ composite has been regarded as new generation of high temperature structural material due to its excellent performance even close to its melting point. The directionally solidified Al2O3/YAG/ZrO2 eutectic ceramics are prepared by recently developed Laser Floating Zone Melting (LFZM) apparatus in which a splitter mirror is used to obtain two beams with the same quality from one CO2 laser. With the two laser beams irradiate the sample from opposite directions, the sample is zone melted. The apparatus configuration and the solidification processing are described in detail. The solid/liquid interface morphology is studied and the mechanism of microstructure formation especially the characteristic of eutectic cellular is discussed. It is shown that YAG and ZrO2 phases play a leading role during the ternary eutectic growth. Meanwhile, the relationship between the solidification microstructure and the processing parameters are investigated.IntroductionAl2O3/YAG/ZrO2 ternary eutectic in situ composite, due to its excellent high temperature mechanical properties, is now considered to be a promising candidate material as a replacement of nickel based super alloy for new generation aero space engine turbine blade [1]. They exhibit flexural strength of 360-500 MPa from room temperature to 2073K in air atmosphere [2]. The compression creep strength at 1873K is 433MPa with the strain rate of 104/s [3]. However, because of the high melting point and complex physical properties, there remain still many difficulties for its application. One of the bottlenecks is the poor understanding of the relationship between microstructure and solidification conditions."

Jan 1, 2012

By Alexey T. Kovalev, Irina A. Khabarova, Valentine A. Chanturiya, Igor Zh. Bunin, Elizaveta V. Koporulina

"The paper presents new theoretical and experimental results about mechanisms of disintegration of mineral complexes and structural transformations of the sulfide surface under high-power nanosecond electromagnetic pulses (HPEMP). The heated gas outflow from nanosecond breakdown channels of sulfide minerals under HPEMP is considered. It is shown that the gas outflow from channels can be an additional destructive factor in the processes of the electric pulse discharge disintegration of mineral complexes. It is shown that the effect of HPEMP changes chemical surface composition and, respectively, technological properties of pyrrhotite and pentlandite. Morphology and elementary composition of new micro- and nanoformations on mineral surface of pentlandite and pyrrhotite have been investigated using up-to-date methods of SEM/EDX and Scanning Probe Microscopy. Preliminary electropulse effect on mineral products before flotation allows producing optimal conditions for flotation separation of pentlandite and pyrrhotite owing to forming the new nanophases and defects on the surface of sulfides.IntroductionThe effectiveness of High-Power Nanosecond Pulses in the disintegration and liberation of fine disseminated mineral complexes and the recovery of micro- and nanoparticles of precious metals from refractory ores was demonstrated in [1, 2]. Possible mechanisms of selective disintegration were considered in [1-3]. It has been shown both theoretically and experimentally that electric breakdowns can play an important role in the nanosecond pulsed treatment of milled minerals (e.g., semiconductor sulfides and quartz with particle sizes of 100 µm to 2-3 mm) that are carriers of finely disseminated gold and other valuable components. Electric discharges in such minerals are accompanied by a destruction of integrity in the form of breakdown channels and the formation of a system of cracks around these channels [3]. The development of the domains of induced cracks around the channels is determined by the pressure of evaporated material in the breakdown channel. Upon an instantaneous energy release in a channel (nanosecond discharges), the change in its transverse size and in the gas density and pressure in the channel is determined by (i) the radial motion of the evaporation wave, (ii) the radial expansion of the channel, and (iii) the heated gas outflow from the channel. The evaporation wave moves with a speed on the same order of magnitude as the speed of sound (or greater) and travels a distance of around the initial channel radius, i.e., a much smaller distance than the breakdown channel length."

Jan 1, 2011

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By Heikki Tuovinen

The total utilization of raw materials and energy is the most important criterion when planning. industrial processes. The main goal is clearly to use the raw materials and energy as effectively as possible in order to make the desired products directly in the primary process itself', or to recycle unused materials and energy either as such, or after cleaning back into the process. However, few industrial processes are so straightforward. Most processes generate by-streams of materials and energy, which cannot be recycled directly and it is namely these by-streams which tend to remain as wastes. These by-streams are slags, dusts, vaporized metals, liquids, slurries, sludges, gases etc. Most base metal processes produce all these by-products. Waste water and gas emission controls and regulations are tightening all the time, so new processes must be developed to keep pace with these requirements. These processes generate more solid wastes, which must be utilized or at least processed into a harmless form landfilling. Municipal and hazardous wastes also contain valuable materials and energy, which must be used to minimize landfilling. The development of processes for these purposes places even greater demands on research and development. The same principles and methods developed for mining, ore dressing and metal refining processes can also be adapted for research and development work on processes for waste minimization. However, the problems encountered are much more complicated and less familiar, demanding more versatile and accurate tools and equipment. This paper presents principles, examples and some references of R & D work on processes for waste minimization.

Jan 1, 1992

By Ramana. G. Reddy, Haoxing Yang

The electrodeposition of zinc from zinc oxide using urea and choline chloride mixture in a molar ratio 2:1 is investigated in different experimental variables, namely, the concentration of added [BMIM]HSO4, temperature, and applied cell voltage. The additive, [BMIM]HSO4, was determined to have beneficial effect on the current efficiency, energy consumed in the process and surface morphology of the deposits. The highest current efficiency (92.6%) and lowest energy consumption (2.92kWh/kg) was obtained for solution with 20mg/mL [BMIM]HSO4. The morphology showed the formation of absorbed additive layer on the cathode at higher concentration of additives. Experiments were conducted at different temperatures between 343K and 388K and at various applied cell voltages between 2.7V to 3.6V to determine the best experimental conditions. By varying temperature, highest current efficiency (91.3%) and lowest energy consumption (2.69 kWh/kg) was obtained at 373K. The electrodeposition process is enhanced between the applied voltage 3.0-3.3V by achieving lower energy consumption (2.75~3.06kWh/kg) and higher current efficiency (88.4~89.7%). SEM images showed grain size is significantly increased in higher applied voltages. While at higher temperatures, it seemed to generate particle growth as clusters at the outer deposit layer.

Jan 1, 2014

By J. S. Becker

Technology developed and first implemented in the United Kingdom enables very low grade aluminum scraps containing oils, organics, plastics and ferrous metals to be directly charged, without pretreatment, into a unique melting furnace. The system has been in full scale production for over three years. The oxy-fuel-based furnace design incorporates internal afterburning in the furnace's hot zone, producing excellent thermal efficiency and very low emissions. The furnace is inherently low in NOx. This paper will provide both theoretical background and extensive operating results for this new melting concept. Applications describing both purpose built new furnaces and retrofits of existing reverberatory furnaces will be presented. Extensive operating emissions data will be presented.

Jan 1, 1996

By Garrett May

We present a periodic technique for measuring the thermal conductivity of thin, disk-shaped samples. In samples of this type, temperature measurements must be made across the sample faces and are therefore subject to large error due to the interface resistance between the temperature sensor and the sample. The technique uses measurements of the amplitude and phase of the periodic temperature across both a reference sample and the unknown material at several different frequencies. Modeling of the heat flow in the sample allows the simultaneous determination of the thermal parameters of the sample as well as the interface resistance. The technique is demonstrated on nanocomposite samples less than 1.0 mm thick.

Jan 1, 2008

By Onuralp Yücel, Mehmet Bugdayc, Murat Alkan

"In this study, iron based alloys (Fe-Mo, Fe-Cr-Ni, etc.) were produced by using aluminothermic methods starting from Mill Scales obtained continuous casting processes. Mill scales are an oxidised layer of steel alloys containing iron oxide, which includes + 2, + 3 values, on the surface of slabs and billets occurring during annealing in heating furnace at integrated iron and steel milling plant, and continuous casting unit. In the metallothermic experiments, different ratios of starting mixtures and addition of the oxide powders (Alz03, Si02, CaO, MgO) were examined, and their effects on the metal recovery and alloy compositions were carried out. The samples were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques.IntroductionSelf Propagating High Temperature Synthesis process (SHS) has many favour compared to the furnace applications, such as low energy requirement, low cost, very short processing time and simple operation, [l, 2]. In a SHS process, the ignition starts the combustion and propagates throughout the reactant mixture yielding the desired product. However, the disadvantages of the process such as inhomogeneous or unreacted products due to undesirable reaction rates needs to be overcome by changing some parameters such as ignition temperature, particle size, additive, atmosphere etc. [3, 4]. Mill scale is a layer of iron oxide which forms on ferrous materials cooling after being processed in hot rolling or continuous casting plants. Mill scale contains iron (II) and iron (III) oxides, which result in a 70% total iron content in oxide form. Not being able to reuse this material will prevent the raw material entering the production plant from being fully utilized [5]. This study aimed to produce Fe-based alloys via SHS (Self Propagating High Temperature Synthesis) metallurgy which is attractive process technique regarding fast and low-cost production ability of cast alloys by using high metallic iron content by reducing continuous casting mill scale."

Jan 1, 2013

By J. K. Brimacombe

Plant trials have been conducted at the Tacoma Smelter of ASARCO to assess the effect on tuyere blockage and refractory erosion at the tuyere line, of increasing the injection pressure of air into a Peirce-Smith con¬verter. Four tuyeres each having an ID of 19.1 mm (3/4 in) were installed toward one end of the tuyere line of the No. 4 Converter. Air and oxygen-enriched air were injected at 414 kPag (60 psig) through these tuyeres and at the usual 83 kPag (12 psig) through the remainder of the tuyeres in an otherwise normal converter campaign. The test campaign consisted of 88 charges and lasted for 89 days. During this period, punching of the high-pressure tuyeres was found to-be unnecessary; and when, as a precaution, the tuyeres were cleaned by hand at the end of a charge, they were always open. Also it was observed that the flow of high-pressure air remained constant. Accretion formation around the tip of the high-pressure tuyeres varied from charge to charge and was influenced by the matte grade and the level of oxygen enrichment.

Jan 1, 1983

By R. Craig McClung

Contrary to other sulfide minerals, where recovery is principally liberation controlled, the recovery of molybdenite is more complex. It is this complexity that initiated a geometallurgical investigation of molybdenites from Bingham Canyon. The aim of this investigation was to determine the effect mineralogy and/or mineralogical attributes have on recovery. All samples were analyzed using normal mineralogical techniques. The results reveal the presence of two distinctly different types of molybdenite. These have been identified as the two polytypes of molybdenite: i.e. hexagonal (2H); and rhombohedral (3R). The 2H-polytype occurs as textbook-shaped particles in quartz-molybdenite veins that are located in the current pit bottom. The 3R-polytype occurs as disseminated, “ball”-shaped particles with a dull or frosted appearance and are concentrated along the margins of the current pit. Concerning their metallurgical behavior, each type exhibits unique metallurgical properties that are consistent with those reported in the published literature. The 2H-polytype is easily ground and kinetically “faster” floating with surface attributes that are amenable to higher rates of recovery. This results in the production of a high quality concentrate under normal operating conditions. The 3R-polytype, by comparison, is difficult to grind and kinetically “slower” floating with surface attributes that are less amenable to recovery. Therefore, in deposits with higher concentrations of the 3R-polytype, modifications to the normal operating parameters may be necessary to improve recovery. This investigation highlights the necessity for understanding the mineralogical characteristics of any economic mineral(s), as these will have a direct impact on recovery.

By G. Barbery

The models for particle composition prediction that have been put forward are limited to simple textures and lead to an independance of grade with respect to particle size in broken ore. A presentation is made of a modification in texture description; binary textures, in which each subeonstituent has its own breakage characteristics are introduced. The calibration of the textural model can be made using heavy liquid separation results. The application to the case of coal is presented. Coal washability data present spe¬cial difficulty due to the distribution in the specific gravity of coal, which must be taken into account. Coal s.g. distribution is taken as a generalized exponential distribution. Model calibration is then possible and is shown to be in good agreement with experimental data.

Jan 1, 1987