By Yuanbo Zhang, FENG ZHOU, Guanghui Li, Zhengwei Yu, RuijunWang, Tao Jiang

Composite agglomeration process (CAP) of iron ore fines has been proved an effective route for ironmaking burden production, and is characterized by low the fuel consumption and high the productivity compared with the traditional sintering process. Sintering behavior of pelletizing feed in CAP has not been studied fully yet. In this study, individual pellet and simulated CAP cells were roasted under the simulated sintering conditions. The compressive strength, FeO content and microstructures of roasted samples were investigated. The results show that pelletizing feed either from magnetite ore hematite concentrate can be indurated under the conditions of conventional iron ore sintering. Hematite pelletizing feed has better sintering property than magnetite pelletizing feed. Pelletizing feed consolidation in CAP cells is identical to the individual pelletizing feed, but the strength of CAP cells is much higher than the individual pelletizing feed. Higher basicity in both pelletizing feed and matrix feed is beneficial to the strength of CAP cells. Individual strength of pelletizing feed is not the decisive factor in CAP as the pelletizing feed has been embedded into the matrix with high basicity and formed an organic whole. The main chemical compositions and basicity of pelletizing feed and basicity matching with matrix feed is important.

Jan 1, 2015

By M. A. Kader, W. D. Hutchison, M. A. Islam, P. J. Hazell, J. P. Escobedo, A. D. Brown

The effects of post-foaming thermal processing on the quasi-static compressive strength of closed-cell aluminium foam with an average relative density of 0.56 g/cc have been investigated. Samples were subject to one of four material conditions: as-received (AR), warm aged (WA), solution treated (ST), and annealed (AT). X-ray diffraction (XRD) was performed to determine a relationship between each material condition and macro-crystallographic texture of the dendritic α-Al phase. It was found that all heat treated samples contained clear deviations from random texture towards the exterior regions of the samples, indicating non-uniform recrystallization kinetics. The ST and WA samples exhibited the highest yield stresses and energy absorption, with the AT samples exhibiting the lowest. Additionally, it was found that the AR and WA conditions lost 12.8 and 15.6% of their total mass from brittle cell wall crumbling, whereas the AT and ST conditions lost 2.5 and 3.0% of their total mass.

Mar 1, 2017

By H. Castillo

This paper describes the computer simulation of thermal stress fields generated in the quenching of the ns 415 H Steel automotive parts (Valve Lifters), running the ANSYS Multiphysics software of finite element (FEM). Simulation was performed introducing residual stress measurements on specific values areas, like internal pressure condition in the material. The stress condition effect in the material and the properties as temperature function data, were introduced to the FEM software. The thermal stress simulation was made on the 2D system. The parts were austenized to 850 900 °C and then oil quenched, tempered at 150 -200°C, and air cooled. The X-Ray diffraction technique was made to take measurements from residual stresses on valve lifters surfaces. The results analysis showed the ideal stress condition necessary in raw material to reduce the scrap percent in grind operations after hardening heat treating process. Keywords: Thermal Stresses, Temperature profile, Computer Simulation, Finite element analysis, Quenching of steel, Residual Stresses

Jan 1, 2003

By Baokuan Li, Qiang Wang, Zhu He

"A mathematical model has been developed to investigate the magnetohydrodynamic (MHD), thermal, and solidified behavior in electroslag remelting process. Based on the finite volume method, a multiphase coupling MHD approach is employed to investigate the droplet formation as well as movement in molten slag under the action of an alternating current. The VOF formulation is adopted for interface tracking. The electrical potential method is adopted for the electric current and magnetic field. The Electromagnetic force and Joule heating are recalculated at each time step and then is implemented in the momentum and energy equations as a source term, respectively. Moreover, solidification of the metal is described by an enthalpy-based formulation, while the mushy zone is treated as a porous medium with porosity equal to the liquid fraction. The model is used to investigate the effect of electrode tip shape on MHD, thermal, and solidified behavior and provide valuable information.IntroductionElectroslag remelting (ESR) process has been used widely to produce high-performance alloys dedicated to critical application, such as hot work tool steels, nickel base alloys, the manufacture of components in aerospace and landbased turbines, etc. Figure 1 shows a schematic diagram of ESR process including a consumable electrode, a molten slag pool, a liquid metal pool, a solidified ingot, and a water-cooled mold. Alternating or direct current flows from the electrode to the water-cooled baseplate through the high resistivity calcium-fluoride-based molten slag which result in Joule heating and Electromagnetic force (EMF). Part of the Joule heating melts the electrode and the droplets travel through the slag and accumulate the liquid metal pool. The electrode is continuously advanced into the slag as it melts to build up an ingot of improved structure and composition by controlled solidification and chemical refinement. The metallurgical properties of the remelted ingot are really related to the solidification structure, which strongly depends on magnetohydrodynamic, thermal, and solidified behavior in the molten slag, liquid metal pool, and mushy zone."

Jan 1, 2014

By S. G. Kumar

Experimental studies on high carbon steelmaking through LD Converter - Vacuum Arc Degassing - Bottom Pouring route to produce low oxygen steels were carried out. The results indicated that it is possible to produce steel with a total oxygen content of less than 15 ppm. Thermodynamic and mass balance calculations are made on low-carbon steels that are treated by a complex deoxidation practice based on primary deoxidation of aluminum, manganese and silicon additions; followed by secondary deoxidation of vacuum degassing with simultaneous additions of aluminum. The results showed that primary deoxidation is mainly due to aluminum and the effect of carbon under reduced pressures on deoxidation of molten steel that is already killed by aluminum is negligible. The effect of process parameters on total oxygen content of steel, like carbon content, slag composition and inert gas purging, are discussed.

Jan 1, 1994

By Shadia J. Ikhmayies

Polycrystalline CdTe thin films were prepared by vacuum evaporation on glass substrates. The I-V plots which were linear were used to find the resistivity. A value of 2.10×106 .cm was obtained. The transmittance was measured in the wavelength range 400-1100 nm. The bandgap energy was found to be 1.48 eV. X-ray diffraction pattern shows that the material deposits in the zinc blend structure with one strong reflection from the C(111) plane. The scanning electron microscope image shows a uniform surface with a small density of large (mµ1£) grains scattered on the surface.

Jan 1, 2009

By S. Jolivet, A. Klöfverskjöld, P. Latostenmaa, B. P. Wilson, M. Lundström, P. Halli

Doré slag is secondary product of copper electrore fining anode slime treatment. The slag consists mainly of different slag formers, such as borax and silica based minerals together with soda and traces of sealing materials. However, Doré slag also contains metals present in the anode slime, such as Ag, Cu, Bi, Sb and Te. At some plants, slag cleaning has been conducted utilizing conventional grinding and flotation circuits in order to enrich the content of precious metals in the slag [1]. Nevertheless, the routine consideration of the slag as a secondary raw material has so far not been adopted on an industrial scale. The current study presents the preliminary results of the nitric acid and chloride leaching of antimony from Doré slag. Chemical and mineralogical analyses (SEM-EDS, AAS, XRD) were performed for the raw material, leaching residue, and leaching solution in order to ascertain the metal recovery and kinetics during leaching.

Mar 1, 2017

By Xu Zhang, Xuewei Lv, Guibao Qiu

Slag foaming phenomenon is of vital importance to the mass and energy transfer in metallurgical processes. A considerable extensively studies carried out via out-gas in the past cannot simulate well the foaming phenomenon formed in the blast furnace where high TiO2 iron ore is used. A gas reaction was designed in the water-glycerol system to simulate the inner-gas system. This study investigated the influences of solution viscosity, particle concentration and particle size on foaming caused by endogenetic gas. The results show that the foaming height decreases with the increase of solution viscosity, which means reduced foaming ability, more difficult foaming elimination process and prolonged time for natural defoaming. With increasing the solid particle content, the foam height presents a trend which increases firstly and then decreases. Under a certain solid particle content, foaming height decreases with the increase of solid particle size, indicating a weak foaming ability.

Jan 1, 2015

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015

By Jorge Alberto Soares Tenório, Victor Bridi Telles, Denise Crocce Romano Espinosa, Felipe Fardin Grillo, Vicente de Paulo Ferreira Marques Sobrinho, José Roberto de Oliveira

"This research aims to study the process of incorporation of the metal iron in electric arc furnace dust (EAFD), from a steel mill producing long steel by liquid iron in addition to the changing temperature of 1400 degree Celsius altering experimental conditions such as how to add the EAFD (as received and in the form of briquettes), the percentage of EAFD to be added (10, 20 and 30% of initial weight of sample pig iron) and the time of withdrawal of the sample of pig iron and slag (30 minutes after the addition of EAFD). Previously, the EAFD will be characterized using the following techniques: chemical analysis, particle size analysis, X-ray diffraction, scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) microanalysis. After characterization, the eletric arc furnace dust to be added to the bath of liquid iron, will be divided into 2 types: the first order of addition will be in the form ""as received"" from the plant and the second is through the agglomeration of EAFD in the form of briquettes. The achievement of fusion experiments in laboratory scale, will take place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of the metal iron will use graphite crucibles. A flow of inert gas (argon) will be maintained inside the furnace during the experiments. It is expected that the results obtained at the end of the research allow the evaluation of the iron metal incorporation of eletric arc furnace dust in hot metal bath.IntroductionThe steel industry generates a variety of solid wastes, liquid effluents and gaseous emissions at various stages of processing. The electric furnace dust (EAFD), generated in electric arc furnaces, represents a major problem for their content of chemical elements such as zinc, iron, chromium, cadmium, among others, issued to the atmosphere during the manufacture of steel[1]."

Jan 1, 2012

By Susumu Okabe

Injection metallurgy is widely adopted in various fields of metallurgical operations to achieve high productivity. The Mitsubishi Continuous Copper Smelting and Converting Process employs the top blown lance technique for the continuous supply of solid charges and reaction gases into the molten bath, where the agitated bath contributes to enhance the heat and mass transfer and the increased gas/liquid interface area accelerates the reaction. However, excessive splashing of the molten materials accompanied by the injection may cause an unexpected wear of the furnace lining. In order to estimate the splashing rate quantitatively, and to optimize the furnace design and the blowing condition, a physical model study of the top blown gas injection onto the liquid bath was carried out. An equation of the splashing rate was obtained as the function of cavity size, gas velocity and bath properties.

Jan 1, 1995

By Garg. D.

Premixed bronze powders are widely used to produce a wide variety of P/M components including bearings and bushings by the powder metal industry. The physical and mechanical properties of sintered bronze components such as dimensions, strength, microstructural characteristics, and sintered density are well known to change with sinlering furnace design, particle size distribution in powders, green density, preheating and sinlering time" and temperature, and protective atmosphere flow rate. " However, not much is known about the effect of protective atmosphere composition on physical and mechanical properties of sintered bronze components; This paper describes effects of protective atmosphere composition and sintering temperature on physical and mechanical properties of sintered bronze components

Jan 1, 1996

By Zhihao Yue, Honglie Shen, Yahui Teng, Ye Jiang

"In this paper, manganous nitrate [Mn(NO3)z] was used to assist the etching of silicon wafer in hydrofluoric acid (HF) for the antireflective application, and alumina (Al2O3) layer was deposited on the surface of the etched sample by atomic layer deposition method for further antireflection. The surface morphological and compositional studies of these samples were performed by scanning electron microscopy attached with an energy-dispersive X-ray spectrometer. The surface reflectance measurements were carried out using UV-Vis-NIR spectrophotometer. Binary structures of pyramids and nanopores were obtained by etching the alkaline textured monocrystalline silicon wafer in HF and Mn(NO3)z mixed solution for not more than 15 min. But excessive increase of etching time of up to 30 min resulted in the whole destruction of pyramids. The average reflectances of the 5-min-etched sample before and after being coated with 75-nm-thick Al2O3 layer are 4.62% and 3.47% in the range of 200-1000 nm, respectively.1. IntroductionAs we know, the reflectance of silicon wafer after being sliced is so high that the maximal photoelectric conversion efficiency of silicon based solar cells is limited. Therefore, alkaline texturization process was used for silicon solar cell in industrial production. But the reflectance of this alkaline textured wafer is still greater than 10% and this process can only be used for monocrystalline silicon solar cell."

Jan 1, 2013

By T. Johnson, B. Q. Li

"Electromagnetic stirring has found a wide application in metals processing for the benefit of obtaining refined solidification microstructures. This paper presents an experimental study on the melt flow and turbulent behavior in an electromagnetically stirred Woods metal pool. The experimental setup consists of metal bath unit equipped with temperature control to allow both cooling and heating, velocity probe positioning unit and data and signal acquisition and processing unit. The whole measuring system is under the control of an IBM personal computer. Velocity measurements are made using the incorporated magnet probes, which are calibrated using a turntable. The measured results showing the effect of the coil positions, coil arrangements and the applied currents on the melt flow are presented. Both mean flow and turbulence quantities are discussed.1. IntroductionElectromagnetic stirring is widely practiced in the metals industry for melt mixing and for casting microstructure refinement. Industrial examples are taken from induction furnaces where the electromagnetic forces are applied to generate desired melt mixing and also various types of electromagnetic stirrers used in various stages of steel and/or aluminum casting processes to produce fine grain solidification microstructure or to eliminate undesired defects such as TCG (twinned-columnar-grain) structure. For ultrahigh purity aluminum or high strength aluminum alloys containing zirconium or lithium, grain refinement can be difficult with the conventional technique, and electromagnetic stirring provides a particularly powerful means to obtain the refined solidification microstructure [1]. A fundamental understanding of the melt flow and the turbulence characteristics in these magnetically-driven flow systems is of significant engineering importance to both process design and product quality improvement.There exists extensive literature on the magnetically-driven melt flows in material processing systems. Nakanish. et al. [2] were perhaps among the early investigators to mathematically and physically model the magnetically-driven flow phenomena in molten metal systems. Subsequent theoretical and experimental work by Tarapore and Evans [3, 4], Szekely and Chang [5], Hunt and Moore [6] and Szekely and El-Kaddah [7] has contributed very significantly to our understanding of magnetically-driven flow in inductively stirred melts. They have developed mathematical models for the electromagnetic field and turbulent flow in induction furnace and validated the models by either laboratory experiments or direct measurements in the industrial-scale induction furnaces."

Jan 1, 1998

By Young-Sool Jin, Heung Nam Han, Hong Joon Kim, Jae Kon Lee

A mathematical model was developed considering non-symmetric cooling' and stress distribution in both thickness and width direction of strip on a run-out table of hot strip mill. In order to solve a transient heat transfer equation including the heat evolved from phase transformation, a finite element method coupled with thermodynamic and kinetic analyses was applied. The heat capacity of each phase and heat evolution due to phase transformation were obtained from the thermodynamic analysis of the Fe-C-Mn-Si system based on a sub lattice model. The phase transformation kinetics of the steels was derived by using an inverse additivity technique with continuous cooling experiments. Heat transfer coefficients of strips on the run-out table were, by applying an inverse method, determined from the actual mill data under various cooling conditions. As for the stress analysis, the density change of strip due to cooling and phase transformation, and the transformation superplasticity were considered. A 90nstitutive equation for the transformation superplasticity, which is related to the phase transformation kinetics and the internal stress due to the density change of strip, was applied. A finite element method was adopted to calculate the deformation behaviour of strip on a run-out table of hot strip mill. Using the models, the temperature-phase-deformation history and distribution of a strip on the run-outtable was calculated.

Jan 1, 2001

By Grigore Matei

The thermodynamic properties of CU2S-FeS system are important not only in the case of copper smelting but also in the case of general pyro-mctallurgy, However there are not many reported activity data In this study, activities of FeS and CU2S in the CU2S-FeS system were calculated using the Darken's method from the activity data of the CU2S-FeS-Sb2SJ systems measured by the transportation method at 10S0°C. The activities of CU2S and FeS in the CU2S-FeS system showed negative deviation from the ideal behaviour and satisfied the relation of the Gibbs-Duhem equation,

Jan 1, 2003

By R. M. Reynolds

Engitec Impianti, S?.p.A. of Milan, Italy has successfully designed, constructed and has in operation state-of-the-art battery breaker systems at two European locations. A third facility i:s partially completed in Toronto, Ontario, Canada. The CX system crushes whole batteries, separates the various components and desulfurizes the battery paste. The system also produces sodium sulfate from the sulfuric acid and lead sulfate contained in the batteries. Actual plant operating data indicates that the desulfurized paste contains less than 0. 6 percent sulfur and less than 0. 5 percent antimony. The CX system utilizes mechanical screening and an up-flow hydrodynamic separator to accomplish the component separation. Sodiwn hydroxide or sodium carbonate is used for desulfurization. The sodium sulfate brine is evaporated and crystallized to produce clean anhydrous sodium sulfate suitable for use by detergent or glass manufacturers. Plant data also indicates that an increase in furnace productivity of about 25 to 30 percent is achieved using feed from the CX system. The desulfurized paste is very suitable for electrolytic processing as an alternative to pyrometallurqical processing.

Jan 1, 1990

By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By Dumitru Mitrica, Vasile Soare, Elvira Alexandrescu, Mihai Ghita, Marian Burada, Petru Moldovan, Raluca Maria Florea

"Aluminum metal matrix composite Al-Si /SiCp was prepared by reactive gas injection and subsequent remelting. The influence of the remelting process on the microstructure and physicalmechanical properties of the resulted material was investigated. Samples resulted from the synthesis process contained silicon carbide agglomerations in the vicinity of primary silicon and large pore concentrations. In-situ formed silicon carbide presented mostly a polymorphic structure with particle sizes varying from 1 to lOµm. Physical and mechanical properties were largely influenced by the porosity distribution. The remelting process provided a decrease in the composite material porosity and pore size, with significant improvements in the particle distribution and physical-mechanical properties of the composite material. Additions of up to lwt.%Mg in the starting alloy improved the in-situ carbide formation and particles distribution in the solidified material. However, stable and large particle agglomerations were detected in the material in absence of conventional stirring or controlled solidification techniques.IntroductionThe remarkable properties of composite materials (yield strength, stiffuess, hardness and resilience at a reduced specific weight) make them attractive for applications in automotive, aerospace and military industries. Particle reinforced aluminum metal matrix composites (PAMMC) are known for their high strength to weight ratio. The recent development of P AMMC created the possibility to obtain large particles concentrations, exceeding 10% by volume ofreinforcement (SiC, AIN, Al203, etc.). The improvement ofhigh temperature strength and wear resistance made them appropriate for the use in automotive applications, such as the pistons, rotors, disc brakes, and propeller shafts [ 1]. The present main disadvantage of the P AMMCs is their high costs for obtaining and processing related to the final product performance. In order to benefit from the advantages that offer composite materials properties a reasonable production cost - performance ratio must be obtained [2]. Recent innovations in the manufacturing of aluminum-based metal matrix composites provided notable performance improvements but no feasible solutions were found for lowering their present high prices."

Jan 1, 2014

By Jingyuan Wang, Hengyi Zhang, Peng Lan, Ruitian Zhang, Jiaquan Zhang, Yang Li

"For the determination of mould taper and wall thickness, a 3-D numerical model of ingot-mould-hot top system has been made to evaluate the related ingot solidification process and the final soundness. The effect of mould wall thickness and the taper of its hot faces on the thermal history and the as cast structure of steel ingot has been revealed through the numerical simulation. It is shown that the ingot soundness can be improved remarkably by increasing the mould wall thickness, which is possibly beneficial to the mould life as well owning to an improved mould thermal state. The mould taper is vital to the ingot soundness but much less coherent to the mould temperature profiles. Under given casting situations, a larger mould taper can lead to a less intensity of the shrinkage porosities at the top part of ingot.IntroductionIngot casting is still one of important processes for steel production, which is adopted especially for the supply of large-sized semi-products of high quality special steels. The understanding to the solidification process is vital to both the yield improvement of casting production and the quality control of steel ingots, such as their soundness and homogeneity.The ingot processing and service performance are closely related to its defects, such as porosities and pipes[1,2], which are the most common but serious defects during ingots casting. In the late 1960s, Mahadevan and Murthy et al.[3], Irani and Kondic[4] began to analyze criteria for the prediction of shrinkage porosities in light metal casting. In 1980s, Niyama and Uchida[5], Hansen and Sahm[6,7] et al have successfully presented some related porosities and pipes criteria for steel casting. At the same time, numerical solidification simulation was well developed and applied to ingot quality studies[8-10]. However, due to the quick development of continuous casting, less emphasis has been given to the further study on ingot casting process. There leaves much work to be made for the comprehensive understanding to ingot quality improvement and the mould design by the aid of modern solidification technology[11, 12]. In this paper, the effects of mould taper and wall thickness on its thermal history, ingot solidification and the final soundness are numerically studied through solidification simulation, which has been adopted in mould design and industrial production of both the mould and its steel ingot."

Jan 1, 2012