The environmental impact assessment of the Imperial Smelting Process for metallic zinc and lead production in Shaoguan Smelter, China, was carried out by the life cycle assessment method. The detailed inventory analysis of the Input/Output in the process during 1998-2000 was conducted and the allocation was done among the main products of zinc, lead and sulfuric acid, according to the system expansion and substitution principle, The environmental impacts were assessed by using the following five Eco-indicators: Gross Energy Requirement (GER), Global Warming Potential (GWP), Acidification Potential (AP), Heavy Metal Toxicity' (HMT) and Solid Waste Burden (SWB). The results from this study are useful to address the environmental situation of the technology practice in this smelter, and provide a scientific basis for the further improvement.

Jan 1, 2003

By I. D. Reznik

Results of thermodynamic computations have been presented for reactions occurring in the process of segregation roasting of oxide nickel ores to describe more accurately the mechanism of the process. Under conditions of laboratory-scale roasting in combination with close-circuit flotation flow-sheets and magnetic separation, a recovery of 80-82% of nickel into 8 to 10% Ni concentrate and a recovery of up to 66% of cobalt was achieved. Process conditions have been selected for processing of both high-iron and high-magnesium ores. The feasibility of conversion of 94-98% of nickel and cobalt into solution by oxidizing pressure leaching with sulfuric acid has been demonstrated. It has been substantiated that it is reasonable to introduce double-stage segregation roasting.

Jan 1, 2003

By Richard P. Roberts

This paper will discuss the methods for the cooling of aluminum melting furnace? dross .and their impact on the environment. Also discussed will be a case history of an AROS Dross Processor installation, which is designed to maximize the recovery of metal content of the dross in a manner which is not only environmentally cleaner, but which also prepares the output in such a way as to facilitate downstream processes. Handling of the discharged material will be discussed in regards to the recycling of the preserved metal content and deposition of the unusable-materials.

Jan 1, 1992

By Guo Xueyi

The environmental impact assessment of the Imperial Smelting Process for metallic zinc and lead production in Shaoguan Smelter, China, was carried out by the life cycle assessment method. The detailed inventory analysis of the Input/Output in the process during 1998-2000 was conducted and the allocation was done among the main products of zinc, lead and sulfuric acid, according to the system expansion and substitution principle, The environmental impacts were assessed by using the following five Eco-indicators: Gross Energy Requirement (GER), Global Warming Potential (GWP), Acidification Potential (AP), Heavy Metal Toxicity (HMT) and Solid Waste Burden (SWB). The results from this study are useful to address the environmental situation of the technology practice in this smelter, and provide a scientific basis for the further improvement.

Jan 1, 2003

The standard procedure of fire refining consists of sulphur removal via air injected through tuyeres, arsenic slagging via soda-lime flux and oxygen reduction by air or oxygen deficient air or a steam fuel mixtures. The use of porous plugs to stir with an inert gas has been mainly considered as a surface renewing agent that increases the product quality and shorten the refining cycle. In the present study the effect of the bottom stirring by nitrogen gas injection through porous plugs for the treatment of the crude copper in the range of 400-150 ppm sulphur, 3,000-2,000 ppm arsenic and 14,000-7,000 ppm oxygen content was investigated. The combined effect stirring-reducing, by the use of air or a steam fuel mixtures through tuyeres for oxygen removal, follows a kinetics of first order where the constant, K, can be represented by the following polynomial expression: K = A * R2 + B * R + C Where A, Band C are constants that depend on the nitrogen flow rate and R is the air-fuel ratio or the steam-fuel used in the reducing step. Depending on the optimization of the flow of nitrogen and the air-fuel or steam-fuel mixture and only if just the oxidation, complexing and reducing steps are considered, the process cycle might be shortened by 45%.

Jan 1, 2003

By C. Acuna

The standard procedure of fire refining consists of sulphur removal via air injected through tuyeres, arsenic slagging via soda-lime flux and oxygen reduction by air or oxygen deficient air or a steam fuel mixtures. The use of porous plugs to stir with an inert gas has been mainly considered as a surface renewing agent that increases the product quality and shorten the refining cycle. In the present study the effect of the bottom stirring by nitrogen gas injection through porous plugs for the treatment of the crude copper in the range of 400-150 ppm sulphur, 3,000?2,000 ppm arsenic and 14,000-7,000 ppm oxygen content was investigated. The combined effect stirring-reducing, by the use of air or a steam fuel mixtures through tuyeres for oxygen removal, follows a kinetics of first order where the constant, K, can be represented by the following polynomial expression: K = A .* R2 + B * R + C Where A, Band C are constants that depend on the nitrogen flow rate and R is the air-fuel ratio or the steam-fuel used in the reducing step. Depending on the optimization of the flow of nitrogen and the air-fuel or steam-fuel mixture and only if just the oxidation, complexing and reducing steps are considered, the process cycle might be shortened by 45%.

Jan 1, 2003

By Olga A. Gomon, Alexey N. Lozhko

The technology of heat treatment for metal frequently includes multiple fast heating and cooling of the products surface. If the product is heavy-weight or long-size, its moving from a zone of cooling to a zone of heating and return require a long time. Other important condition of ensuring qualitative surface at heat treatment is intensification of cooling phase. It is known that turbulization of a flow activates heat exchange and increases efficacy of cooling without increasing volume flow rate of water. Additional difficulty is to ensure the regularity of heating and cooling on length of a product. The technology of cyclic heat treatment of rolling products, at which mobile zone of turbulent heat exchange is formed on the surface of a product, was developed and realized. The submission of water occurs through to face spray systems. Each of the systems has six long-range atomizers, which are located circularly. Two flows of water move towards one another along a surface of a product. When they collide, the right zone of turbulent heat exchange creates heat transfer in this zone of 10-15 time more intensive than on other surface of a product. The effect of moving turbulent zone on length of a product is reached by changing the proportion of volume flow rate of water, which is created by face sprays. The speed of movement for turbulent zone along a surface of a product is chosen so, that the cooling takes place on a small depth only. Then after passing the turbulent zone over a determined site of a surface, its temperature recovers fast owing to hot internal layers. The parameters of process were determined by mathematical simulation of cooling in an installation. The equations for dynamics of movement of collision point of flows, which were received this way, are interesting supplementary products of research. The experiments show that frequency of movement of turbulent zone is an important technological parameter. It defines mechanical properties of a surface and should be chosen depending on a profile of product and metal grade. The results of comparison of mechanical properties of a surface of various rolling products, which were received by developed and conventional technologies, are described in this report. Dependence of regularity of mechanical properties on frequency of movement of turbulent zone is adduced.

Jan 1, 1998

By W. Mueller

The function of a process mineralogist in the operation of a copper mine and plant is to assist in the identification and classification of the operation's main throughput. These include ore, concentrates, slag and matte, and to a lesser extent, refined products. In addition, a number of other products not normally thought of in association with mineralogy are examined. These include scales from submersible pumps, failed boiler tubes, acid plant, and shaft furnace; characterization of inclusions in failed compressor gear teeth as well as in copper rod; and flue dusts from a smelter, air transported particulates and coatings on passive copper anodes in the refinery. Techniques and equipment required for these studies include simple hand magnets to the high intensity Isodynamic separator, visual examination to electron microscopes, x-ray equipment, DTA, IR, heavy liquid separation, and contracted services of custom laboratories. Several examined products from Magma Copper Company have been selected to illustrate the range of techniques and equipment required by a process mineralogist.

Jan 1, 1981

By Patrick R. Taylor

A novel method for Chemical Vapor Infiltration (CVI) using plasma technology is proposed, Plasma Enhanced CVI (PE-CVI). Due to the low rates at which CVI is currently performed, the use of plasma as a source of heat may be considered to be a faster and less expensive production method. Precursors fed in the hot region of the plasma gas are completely vaporized and forced by the same flow through a porous preform where it condenses as a new material. In this research, silica and methane where used as precursors to form SiC/on a / graphite felt (preform). To enhance the infiltration process, vacuum was used to increase the flow through the preform. Characterization of infiltrated graphite was perfontied using Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). A uniform distribution of Sic was observed along the felt with only twenty minutes of infiltration process, yielding a 178% increment in weight.

Jan 1, 1997

By Ragnhild Aune

In fire refining of copper, the affinities of various impurity elements on dissolved oxygen is of great significance. Further, in the design of oxygen probes in liquid copper, the influence of solute interactions on the activity of oxygen need to be considered in order to evaluate the oxygen concentration in molten copper. The present paper presents a series of measurements of the activities of oxygen in liquid Cu-M-o alloys (where M stands for Mn, Zn, As, Se or Te) carned out by the present group employing the solid electrolyte galvanic cell technique. Extreme care was taken to control the oxygen potentials in the inert gas atmosphere, and to keep the oxygen levels very low in the molten metal. The oxygen content was determined by analysis of the samples taken out from the melt. The results obtained showed that Mn has a strong negative influence on the activity coefficient of oxygen in liquid copper. A similar, but less prominent effect was observed in the case of Zn. Arsenic had no influence on the activity of oxygen in Cu (liq.). Se and Te had slight negative effect on oxygen activities in copper at XQ >10-5, while at lower oxygen levels the interaction coefficients were found to be positive. The results obtained were compared with empirical models for the calculation of interaction coefficients available in literature.

Jan 1, 2003

By C. L. Lin

Transformation of linear grade distribution to volumetric grade distribution has been used to estimate the actual mineral liberation during wet, batch, ball mill grinding of a copper ore. The degree of liberation based on the multicomponent-multisize grinding liberation model using volumetric grade is lower than the apparent degree of liberation estimated from using King's linear intercept model.

Jan 1, 1987

By D. M. Hausen

A refractory siliceous low-grade silver ore (265 g/t Ag) from a prospect in Sonora, Mexico was investigated mineralogically and metallurgically to evaluate extraction of the silver by conventional methods. Approximately half of the silver was recoverable, occurring as coarsely crystalline acanthite (70-300 Am) that was liberated in material crushed to minus 10 mesh. The remaining silver is refractory and occurs mostly as finely locked (-2 to 0.2 Am) acanthite in cherty quartz, and as minor amounts of finely disseminated stylotypite or freibergite in fluorite. The mineralogic data have thus served to explain the 50-60% recovery of silver by flotation and cyanidation.

Jan 1, 1991

By John Norton

"This presentation will cover the physical properties of waste heat recovery. It is a two part presentation. The first deals with actually recovering the heat with new state of the art heat exchangers and applying that heat to the furnace combustion and the second part will cover what other processes you can enhance with this ""free"" heat. It will also talk about converting it to steam, hot air or electricity to be used or sold back to the utility company. The economics of various schemes will be reviewed. A brief discussion on State and Federal grants and subsidies will be presented.IntroductionThere are large quantities of wasted heat in the usual aluminum melting process. And, there are several techniques for reducing and/or using some of that wasted heat as you have seen. Any technique that can make use of wasted heat is a form of recovery. This can range from simply preheating aluminum billets prior to melting, to more complicated processes like air-to-air heat exchangers using the boiling and condensing characteristics of special fluids in “heat pipes.” The objective of this type energy recovery process is to move the wasted heat from the hot and dirty exhaust gas stream into some useful process.Waste Heat Recovery in the Aluminum Melting Furnace.There are considerations, of course:1) What might the value be of the recovered energy?2) Can the recovered energy be used within the process? Within the plant? Or by theneighbors?3) What is the capital cost?4) Is the recovery process complicated?5) Will it take additional staff?6) Will it cause additional downtime on the melting line?7) Will the operations staff need to be licensed?Ideally, the process will be simple and inexpensive, the recovered energy will be very valuable, and the whole effort will cause little distraction to the aluminum melting process itself. These would be ideal."

Jan 1, 2011

By Tingyao Liu, Lihui Han, Qing Liu, Bao Wang, Teng Yang, Yong Sheng

This paper mainly investigates the mass transfer phenomena of rare-earth concentrate from leaching process in Rushton stirred tank reactor with rotate speed of 100-600 rpm. In the research, a certain amount of sphere particles with 50-450 μm in diameter is treated as the mineral particles. Comparison of laboratory experiment data with numerical simulation is performed. The results show that the critical impeller speed for complete dispersion is 300 rpm. And the maximum value of turbulence kinetic energy appeared 15 mm away from paddle, where the mixing time is decreased 55% and 80%, respectively, when mineral particles are injected into stirred tank through one or four filling ports. Moreover, with mixing process going on, the numbers of particles near the paddle region accounts for as much as 58% of the total amount. Meanwhile, following the particle diameter increasing, the particle concentration of the upper part of stirred tank reactor is increased.

Jan 1, 2015

By A. González

Arsenic is one of the main contaminants present in Chilean copper concentrates and its abatement represents a challenge for the process metallurgy, particularly under the strong environmental requirements in the global community. The possibility to form ferric arsenate directly from a gas phase by means of a heterogeneous reaction between an arsenic gas bearing and iron oxide was studied at laboratory scale. A thermodynamical analysis for the system Fe-As-O-S has been initially made, in order to obtain the stability conditions for the ferric arsenate or other FeAsyO2 type compounds. Experiments were made using an hematite sample suspended in a thermogravimetric device. AS4O6 gas generated from solid AS2O3 that was passed through the iron oxide sample and its instantaneous weight change was recorded directly. A kinetic study for the AS4O6 volatilization was made to control the gas composition. A chemical control between 300 and 600°C with an apparent activation energy of around 14 Kcal/mol As2O3 was determined. The samples after the reactions were chemically and XRD analysed. Arsenates detected corresponds to complex compounds. Results shows a dependence on temperature and oxygen content in the gas phase. The kinetics for iron arsenates formation is slow, reaching an arsenic capture of 6% after 80 minutes of reaction when an oxygen content of 50% is fed continuously at 800°C and 3,56% As in the gas. Experiences made at the same temperature but under higher oxygen content in a closed reactor, allowed arsenic capture close to 60%. For higher temperatures the capture is considerably lower.

Jan 1, 2003

By Damien Wagner

To reduce the emission of greenhouse gases by the steel industry, particularly for ironmaking, the production of DRI (Direct Reduced Iron) using hydrogen as the reducing gas instead of carbon monoxide is being considered. In this context, the reduction of pure hematite by hydrogen was studied at the laboratory scale, varying the experimental conditions and observing the rate and the course of the reaction. All the reduction experiments were performed in a thermobalance and supplementary characterization methods were used like scanning and transmission electron microscopy, X-ray diffraction, and Mössbauer spectrometry. The influence of rising temperature in the range 550-900°C is to accelerate the reaction; no slowing down was observed, contrary to some literature conclusions. A series of experiments consisted in interrupting the runs before complete conversion, thus enabling the characterization of partially reduced samples. Interpretation confirms the occurrence of three successive and rather separate reduction steps, through magnetite and wustite to iron, and illustrates a clear structural evolution of the samples. Finally, the influence of the sample type was revealed comparing a regular powder, a nanopowder and a sintered sample. The regular powder proved to be the most reactive despite its larger grain size, due to a more porous final structure.

Jan 1, 2006

Physical and chemical methods were investigated to tower thorium levels in Eneabba Ilmenite from the natural levels of 180-500 ppm to give Becher Process synthetic rutile with less than 100 ppm thorium. Chemlcal treatments, but not physical separations were successful. A pilot plant trial of a sodium hydroxide leach (25M NaOH at 75°C and 40 wt% solids for Ih) followed by a sulphuric acid leach (3M H2S04 at 90°C and 60 wt% solids for 211) confirmed that thorium could be removed to below 100 ppm. However, the activity of the ilmenite was not lowered to the same extent

Jan 1, 1996

By Luis Hoyos-Reyes, Jesus Gonzalez-Trejo, Adriana Cervantes-Clemente, Marco Gutierrez-Villegas, Manuel Palomar-Pardave, Cesar Real-Ramirez

Recent improvements on Peirce-Smith Converters (PSC) have combined numerical and physical simulations. However, most of the physical simulations have been carried out in cold-water models with only one tuyere. Several authors have proved that 2D numerical simulations do not reproduce the hydrodynamic behavior observed in physical simulations. On the other hand, most of the 3D numerical models have used a PSC thin slice with only one tuyere, but symmetric boundary conditions on the virtual walls have been imposed in order to reproduce the behavior of the whole converter. Therefore, there is no coincidence with the rigid walls of the physical models. The aim of this work is to quantify the effect of the virtual walls boundary conditions of a PSC thin slice and to determine the minimum number of tuyeres to characterize the fluid flow behavior of the entire converter.

Jan 1, 2009

By Dian Adisty, Leiv Kolbeinsen, Eli Ringdalen

In Si and FeSi production, the main Si source is SiO2, in the form of quartz. Reactions with SiO2 generate SiO-gas that further reacts with SiC to Si. During heating, quartz will transform to other SiO2 modifications with cristobalite as the stable high temperature phase. Transformation to cristobalite has been investigated and shown to be a slow process where the rate varies between the investigated quartz types. The effect of quartz versus cristobalite as SiO2 source has been studied for reaction (1) 2SiO2 + SiC = 3SiO + CO, by heating of pellets with SiO2 + SiC in Ar-gas. The reaction was faster with cristobalite than with quartz. Initial experiments indicates that this is the case only in Ar and not in CO-atmosphere The higher specific surface area of cristobalite is believed to contribute to the higher rate. The industrial consequences of the observed difference between quartz types are discussed.

Jan 1, 2014

By Brian Lightfoot

Ausmelt technology is a versatile bath smelting technology with application in many waste treatment fields at low capital and operating cost. Heavy metals extracted from wastes may be recycled to mainstream use and the slags produced will be inert and suitable for use as aggregate, shotblasting grit or other applications.

Jan 1, 1994