By H. Masuda

The lijima Zinc Refinery started operation in 1972, and has today an annual capacity of 200, 000+-Zn. The hematite process was employed for the first time and the ideal of waste-free refinery has been pursued for 30 years. In recent years, however, only half of the hematite produced would be sold to the cement industry and hence a reduction of arsenic level has been necessary in order to sell the entire amount produced, The arsenic cementation process with zinc powder, developed through a long time laboratory research was found among some options as the best for the hematite process. The construction work started in 2000 and the facility was put into operation in 200 I. As a result in the same year all hematite were sold to the cement industry. The outline of this project, present operations and technical issue are reported in this paper.

Jan 1, 2003

By J. E. Dutrizac

Mineralogical studies were carried out on nodulated copper cathodes from three primary refineries to characterize the nodular growths and to elucidate the causes of the nodulation. Nodulation is often initiated at the surface of the starter sheet or the stainless steel plating blank, although a layer of smooth copper sometimes is deposited before nodulation commences. In some instances, the "roots" of the nodules exhibit a pronounced dendritic texture that is associated with an abundance of cavities. Slimes particles are not usually associated with these growth features which lead to a globular surface deposit. The globules sometimes develop into larger nodules, and this type of nodulation is likely caused by improper addition agent concentrations. The nodules on most cathodes, however, exhibit "roots" at the contact with the substrate that are associated with microcavities and large clusters (>40 µm) of slimes particles. The slimes constituents are commonly Ag powder, PbSO4 and Cu2(Se,Te) but not AgCu(Se,Te) or Ag,(Se,Te). The size of the slimes clusters, rather than their composition, appears to be the important factor causing the copper to grow into nodules. Tiny individual slimes particles themselves do not appear to cause cathode nodulation.

Jan 1, 1999

By John J. Mahoney, George P. Demopoulos, Matthew T. Bohan

In recent times processing of arsenic-laden complex ores and heightened awareness of the detrimental health effects of arsenic has put an increasing burden on metallurgical operations to remove arsenic from processes for disposal in an environmentally stable form. At present, arsenic is removed and prepared for storage by precipitation of insoluble secondary arsenic-bearing minerals. It has been suggested that Ca(II)-Fe(III)-As(V) phases resembling the natural mineral yukonite, under certain conditions, may have a role in controlling arsenic pore water concentrations in arsenical waste storage facilities. In this study, a previous synthesis method of yukonite (Ca3Fe5(AsO4)4(OH)9⋅4H2O) is revisited and new solubility/stability data is presented based on a modified method.

Jan 1, 2014

By Tsembel Darjaa, Toru H. Okabe, Yoshiaki Umetsu

"With the purpose of extracting molybdenum and rhenium from molybdenum sulfide concentrate; .electrolysis of slurry, solvent extraction and ·precipitation operations were carried out. The slurry of the concentrate in 10 mass% NaCl aqueous solution was continuously circulated into a vertical type 10 stack bipolar electrolytic cell consisted of carbon electrode disks, and, the concentrate was dissolved by electrochemically generated oxidizers at 313 K. The current efficiency for molybdenum dissolution was 73 % after 10 hours electrolysis, and the leach solution was found to contain 0.2 mol/l of molybdenum and 4x10-5 mol/l rhenium. This result shows the dissolution is more than 8 times faster than that obtained using a single cell. The leach solution from electro-oxidation was then subjected to a solvent extraction for rhenium which is then recovered as sulfides. After rhenium separation, molybdenum was precipitated by pH adjustment, and solid MoO3 (H2O)x crystals, free of sulfate, were obtained from the leach solution containing large amount of so42-.IntroductionIn the past, electro-oxidation using a bipolar cell was applied for leaching molybdenite concentrate and ores at U. S. Bureau of Mines [1-3] and also at Bhabha Atomic Research Center [4]. In· these previous studies, Moebious type bipolar cells, in which electrode plates were vertically inserted into the free surface of the electrolyte, were employed and its effectiveness was demonstrated.Recently, the present authors studied on leaching of Mongolian molybdenite concentrate, and the effectiveness of leaching of the concentrate by electro-oxidation in alkaline and acidic NaCl solutions was demonstrated [5]. The leaching reaction during the process can be explained by the 18 electron transfer reaction of molybdenite (MoS2) with the oxidizers produced in-situ by electrolysis of NaCl aqueous solution. Further investigation was made with respect to various process parameters for electrooxidation such as pH, pulp density and temperature of the slurry, and the dissolution behavior of minor elements such as iron, copper, and rhenium [6]. Solubilities of molybdenum in the leach solution at, various temperatures and pH .was · studied, and feasibility of molybdenum recovery by hydrolysis of molybdenum species was demonstrated. By adjusting the pH of the leach solution, molybdenum oxides or hydroxides free from sulfate were successfully obtained from the solution containing large amount of sulfate ion. Rhenium present in the concentrate at a level of several tens of mass ppm was found to dissolve into the leach solution, and co-precipitate with the molybdenum compounds. Rhenium in the leach solutions, therefore, has to be recovered before precipitation of molybdenum, otherwise it is lost in the precipitate."

Jan 1, 2000

By Gennadiy M. Poletayev, Mikhail D. Starostenkov, Alexandra S. Starostenkova

"The process of the combustion synthesis was modeled by computer simulation using the molecular dynamics method. The set of the critical parameters regulating the velocity of the reaction was found from these computer experiments. It was established that the character of structure-energetical transformations at the combustion synthesis in the systems Ni-Al and TiAl depended on the type of boundaries used for the phases delimitation in the bimetal thin films.IntroductionProducing new materials and products, based on the combustion synthesis (CS), is the objective of scientific investigations as one of the most perspective one for industrial applications. But there are several problems connected with theory and experiment. It allows us to forecast the properties of materials. First of all, the main problems are stipulated by structure-energetical transformations taking place at high velocities of the reaction and at high temperatures. It prevents the analyzing of the transformation mechanisms in materials, taking place at microscopic, atomic levels in details.It is evident, that computer simulation allows to decide some problems and to approach to more exact theoretical presentation of structure-energetical reactions taking place at CS. It is known, that the most typical systems, where CS is observed, are bimetals Ni-Al and Ti-Al. The investigation of interphase boundary stability in the systems of Ni-Al and Ni-Fe was made by the method of molecular dynamics in [1]. The bimetal thin film was presented by the packing of atoms in the plane (111) of FCC lattice. It was found that the discrepancy in the sizes of atoms A and B of bimetal was compensated by the formation of 60° top dislocations, set against interphase boundary in the absence of point defects and free volume. The density of top dislocations was proportional to the factor of size discrepancy of atomic components of the bimetal. Diffusional reconstruction of the interphase boundary and areas, situated near it, was observed only at definite concentration of point defects - vacancies, inculcated in the structure of the bimetal at the definite temperature. The atoms of the bimetal component of less size penetrated in the area of the second component with higher velocity. The clusters of intermetallic germs began to form. It led to the growth of the system temperature and acceleration of the process of the diffusional reconstruction of thin film. The following transformations were found: top dislocations splitted into single ones, which climbed from interphase boundary into the zone of more plastic component; the formation of sub grain structures took place."

Jan 1, 2001

By Banqiu Wu

Zirconium carbide powder has been synthesized from zircon concentrate and methane using a high temperature plasma reactor, a non-transferred DC plasma torch was used as heat source. A high temperature filter consisting of graphite felt was designed, built and operated to separate the zirconium carbide from silicon carbide during the process. Characterization of the collected powders was done by wet chemical analysis using Atomic Absorption (AA), Scanning and Transmission Electron Microscopy (SEM and TEM) and by X-Ray Diffraction (XRD). It was found that the zirconium carbide purity was around 95% with silicon carbide being the primary impurity. The powders had particle sizes between 30 and 80 nm. The effect of several experimental variables are presented as well as temperature and velocity profiles calculated in the reactor.

Jan 1, 1997

By C. W. Vierrether

Mineralogical analysis contributes directly to the selection of applicable beneficiation techniques for a given site. Tentative remediation methods for use on the Sharon Steel tailings in Midvale, Salt lake County, UT, were determined in part by mineralogical characterization. A systematic characterization scheme was employed to identify mineral species, mineral associations, and grain size. This paper presents the mineral content and distribution data collected for site characterization. This data was used to determine areas that were representative of the total tailings at the Sharon Steel site. Although this was the main focus of characterization, other useful information was obtained. The approximate location of "old jig tails" was identified and insight on possible arsenic, mobility through the pile was also obtained from the mineralogical study.

Jan 1, 1991

By Alain Jardy, Thibaut Quatravaux, Denis Ablitzer

"A numerical model of the Vacuum Arc Remelting process has been developed and applied to simulate remelting of various metallic materials, such as specialty steels, titanium and zirconium alloys. In practice, electromagnetic stirring is sometimes used, resulting in a complex 3D molten metal flow. After having validated the numerical model for different remelting conditions, we can use it to study the effect of applying a constant or alternated magnetic field on the thermohydrodynamic behaviour of the melt pool. The intensity of flow turbulence, computed with a classical k-E model, is shown to depend strongly on the nature of electromagnetic stirring.IntroductionThe principle of the Vacuum Arc Remelting (VAR) process, illustrated in figure I, consists in melting a consumable metallic electrode of the required grade under a high vacuum, in order to obtain a sound ingot of good structural quality.During remelting, an electric arc is maintained between the tip of the electrode and the top of the secondary ingot, in order to ensure melting of the electrode. The metal droplets fall through the arc plasma and progressively buid up the ingot, which solidifies in contact with the walls of a water-cooled copper crucible. The secondary ingot formed in this way contains three distinct zones, corresponding to the liquid pool, fully solidified metal and intermediate mushy zone. In order to stabilize the arc, it can be confined with the aid of a magnetic field created by an external induction coil. This field can also be used to stir the liquid metal, the rotation induced being in the orthoradial direction. By reversing periodically the coil current, stirring can be alternated."

Jan 1, 2004

By D. P. Cook, M. I. Bloch, J. A. Dantzig

"In this article, we describe a combined experimental and computational program to study the filling of automotive wheels during low pressure die casting. Experiments are performed by placing thermocouples into the mold walls of a production caster for the Ford F 113 wheel to measure the temperature profiles in the die during processing, and to infer the filling pattern. Computational models are also developed using a 36° section of the wheel pattern, taken directly from CAD data files. We use these models to simulate the filling and heat transfer processes. Comparison between experimental and computational results are presented, demonstrating the viability of this procedure.IntroductionAutomotive companies are using increasing amounts of aluminum in production vehicles: While the main driving force is improved fuel economy through weight reduction, replacing steel wheels by aluminum also offers the potential for improved vehicle performance by reducing unsprung mass. For these reasons, many new vehicles are now supplied with cast aluminum alloy wheels, and the aftermarket for these wheels continues to grow.The most common production process for these wheels is low pressure die casting. The process is subject to numerous defects, including microporosity, cold shuts, cold folds, misruns and inclusions. Scrap rates at the caster of the order of 10% are not uncommon. Many wheels also have large production runs, into the hundreds of thousands of wheels per year. Thus, the cost savings from even small reductions in scrap rate have the potential to be quite significant.Most of the defects are associated with the filling and solidification processes in the mold. The molds are air cooled, and the placement and sizing of cooling passages is currently as much art as science. The ultimate goal of this project is to improve that situation, by implementing simulation procedures that enable engineering design methods to be used in die and process specification."

Jan 1, 2000

By Sh. Najisi, O. Lashkari, M. R. Ghomashchi, A. Charette

"One of-the important parameters in casting and foundry technology is the fluidity of molten metal. This parameter becomes particularly important when casting thin wall parts. Therefore, understanding and controlling fluidity plays a major role in fabricating sound and defect-free cast components.Semi-Solid Metai SSM, slurry is a mixture of solid and liquid, mushy zone, with solid volume fractions of 0.1-0.5 and apparent viscosity close to oil viscosity at room temperature. It flows easily under pressure and capable of making complicated shapes with high degree of die filling and integrity.In this study, the ability of the semi-solid slurry to continue to flow is investigated through the effect of different fraction solids and holding temperatures. The results show that in mechanically stirred, MS, semi-solid 356 Al-Si alloy, increasing fraction solid reduces fluidity. Furthermore, the results of MS-alloy are compared with a newly patented Rheocasting route, i.e. SEED, Swirl Enthalpy Equilibrium Device to highlight the differences of the two processes. In addition, the interrelationships between microstructural evolution and fluidity are discussed."

Jan 1, 2004

By Donald R. Sadoway

The viability of treating certain forms of hazardous waste by direct electrolysis in molten oxides is under investigation. Secondary residue or waste mud produced in the course of chromate chemical production is the focus of attention in this study. The goal is to reduce the water soluble hexavalent chromium either to insoluble trivalent chromium or to chromium metal. Electrolysis tests have been conducted in a high temperature cell containing chromate sludge dissolved in an electrolyte composed of Al2O3, SiO2, CaO, and MgO. Oxygen production on a carbon-free anode has been confirmed.

Jan 1, 1992

By Heinz Giegerich

This paper deals with a new development in recycling second generation catalytic converters, namely metal substrate converters (MSC). It describes a patented dismantling process, whereby the MSC is segregated into it's three components outer steel shell, metal substrate carrier foil and ceramic W8shcoat with embedded precious metals.

Jan 1, 1995

By Shunli Zhang

Metals recovery from electronic scrap by physical separation may provide an alternative to the current recycling approach, through which halogenated flame retardants can result in hazardous dibenzo-p-dioxins and dibenzo-furans. On the basis of a complete sink-float analysis of personal computer and printed circuit board scrap, and in view of the advantages of dry processes for electronic scrap recycling by mechanical separation, air table separation is prioritized in an attempt to separate metals from plastics and glass involved. In the present paper, theoretical and practical considerations of air table separation have been detailed. It has been shown that air table separation is effective for recovering copper and precious metals from this specific waste stream. With the feed rate of 60 kg per hour, the combined grade and recovery of copper, gold, and silver attainable for the two heavy products produced by the air table used in the present study was shown in the following table:

Jan 1, 1998

By Minjun Tang, Jianfeng Zhou, Linjiang Qing, Yufeng Guo, Tao Jiang

"For the comprehensive recovery ofV, Ti, Fe in vanadium-titanium magnetite in the process of pre-reduction-electric furnace smelting, it is expected that vanadium oxide is reduced into molten iron and titanium oxide is available in the slag. Thus the effect of slag basicity, the content of MgO, MnO and CaF 2 of slag content on the separation of slag and molten iron and the comprehensive recovery of V, Ti, Fe were investigated. The results show that increasing slag basicity, MgO, MnO and CaF2 are all beneficial to the separation of slag and molten iron. Higher slag basicity and the addition of CaF2 strengthen the reduction of vanadium oxide, and inhibite the reduction of titanium oxide, which are in favour of the recovery ofV and Ti. However, the addition ofMgO, MnO was not efficient for the comprehensive recovery ofV, Ti, Fe. For the vanadium-titanium magnetite of Panxi in China, the recovery of Fe was over 98%, the recovery ofV in molten iron was over 85% and the Ti02 content in slag was about 43% under the optimal conditions of slag phase type.IntroductionIt is well known that there are abundant vanadium-titanium magnetite resources which are located in Panzhihua of Sichuan Province[!]. At present the vananium-titanium magnetite concentrates are smelted in the blast furnace, which just make use of iron and vanadium, but lots of titanium is discarded in the slag. At the same time, the process has a large number of disadvantages, such as low recovery of vanadium, long route, pollutions, large investment and expenditure of energy[2-3]. In recent years, in order to efficiently utilize the vanadium-titanium magnetite concentrates, several new non-blast furnace processes have been proposed, such as pre-reduction-electric furnace, pre-reduction-grinding separation and so on[4]. Especially pre-reduction-electric furnace is operating well in South Africa and New Zealand,However,Du to the high slag basicity of the slag, the grade ofTi02 of slag is Corresponding author:Minjun Tang.E-mail:450435123@qq.com. Tel:13627429224."

Jan 1, 2013

By I. Kim, J. C. Choi, W. D. Cho

"The effect of yttrium addition on the oxidation behavior of Fe3Al intermetallic compound was investigated in the range of temperature 800 to 1100 °C in 0.2 atm 02 in terms of oxidation rate and oxide adhesion. The oxidation rate of alloys, Fe-14.3 wt% Al and Fe-14.1 wt% Al-0.3 wt% Y, was nearly identical and the parabolic rate constant calculated as a function of temperature is Kp=5128 exp[-39506(cal/mol)/RT] mg2/cm4 hr.Rapid cooling and ultrasonic stress tests were carried out to test adhesion of scale formed on the alloys. While the oxide layer formed on the Fe-Al alloy without Y was found to be fragile and detached easily during the tests, the oxide layer formed on the Fe-Al alloy containing Y was protective, dense, and adhesive. The following two mechanisms were proposed to explain the adhesion improvement of Ah03 formed on the Fe3Al containing yttrium : (1) the addition of yttrium decrease generation of growth stress in alumina scale because the preferential diffusion of yttrium through grain boundary in alumina scale prevent internal oxidation of Al, one of main causes of growth stress, and (2) the second phase formed on the oxide scales prevents crack propagation through the scales, leading to better mechanical stability of the oxide scales.IntroductionIron aluminides have attracted the attention of many researchers as a candidate for use at high temperature because of their excellent oxidation resistance due to the formation of protective alumina scale. In order to resist aggressive environments at elevated temperatures, oxide scale formed on iron-uluminum alloy must satisfy the following three requirements : (1) thermodynamic stability (2) slow growth rate (3) adherence on substrate. According to Wallwork and Hed [l], the most suitable alloys for high temperature application are Fe, Ni, and Co alloys with the protection of Si02, Cr203, and Ah03 scales. While chromium oxide can vaporize as Cr03 above 1000 °C and silicon oxide may form low melting silicate [2,3], Alz03 has a high melting point and is the most stable among the three oxides thermodynamically [6]. In this respect, iron aluminides forming alumina seem to be most suitable for use at high temperature. However, alumina scale formed on the iron aluminum alloys tends to be easily spalled during oxidation due to the combination of growth stress and thermal stress."

Jan 1, 1998

By Nagy El-Kaddah, Thinium T. Natarajan

A modeling strategy is presented for computing the electromagnetic field and the shape of the molten metal in electromagnetic confinement systems. This strategy involves the use of a hybrid finite element/integral technique to calculate the electromagnetic field and force distribution in the melt. The free surface shape is determined from minimization of electromagnetic, gravitational and surface tension energies using the Lagrange method of multipliers. This approach was applied to model the electromagnetic levitation melting process. The model was found to accurately predict the measured shape of levitated droplets.

Jan 1, 2014

By Milton Manrique, Edgar E. Vidal, Patrick R. Taylor

"Ultrafine zirconium carbide powder has been synthesized using zircon concentrate and methane in a thermal plasma reactor. The effect of several experimental variables, such as power used and zircon particle size, on the conversion has been studied. A thermodynamic analysis of the possible reactions and stable compounds was performed. A mathematical model that describes the in-flight decomposition of zircon particles was developed based on a description of the temperature and velocity profiles calculated in the reactor. It was shown that the formation of zirconium carbide from zircon and methane is thermodynamically possible. Complete 'vaporization of zircon in the reactor is predicted when the particle size is below 45flm and the effective power entering the reactor is 15 kW. The powders were collected and characterized by XRD, SEM, TEM and chemical analysis using ICP. Results of the product analysis indicated the presence of zirconium carbide, zirconium oxide, silicon carbide and silicon oxide.IntroductionIn recent years there has been an increased interest in the production of nanometric sized powders of ceramic materials for use in advanced materials applications. One possible method to produce these powders is with a thermal plasma reactor, which offers high temperatures and fast quenching rates. This technology has been called - Thermal Plasma Synthesis - [1].Zirconium Carbide (ZrCx) has typical properties of transition metal carbides: elevated hardness - between alumina and diamond - a high melting temperature of 3420°C and high chemical stability at room temperature [2]. ZrCx has a Bl crystal structure with deficiencies in the number of carbon atoms in the cell with x between 0.6 and 1 [3]. Different methods have been used to produce ZrC, one method is by direct reaction of zirconium hydride or halide with carbon. Other methods used are direct reduction and carburization of zirconium oxide (Zr02) and reaction of metallic zirconium with a caburizing gas such as acetylene [3]. Recently small films of ZrC have been obtained using a sputtering device [4,5]. ZrC has been used in nuclear plants as a low neutron absorbing and high mechanical resistant refractory material and also as a constituent in cathodes made of UC-ZrC [6]. It is also used in the form of tubes, boats and crucibles to handle molten metals and as part of electronic devices used for thermoionic transducers. Recently ZrC has been used along with zirconium diboride (ZrB2) to produce composite materials [7,8]."

Jan 1, 1996

By J. E. Wey

Extraction of cobalt from cobalt sulfide and cobaltite flotation concentrate from the Blackbird Mine, Idaho, was investigated using an adapted strain of Thiobacillus ferrooxidans. Cobalt extractions as high as 100% were realized in the inoculated experiments, whereas only 4% extraction was obtained in the sterile run. The influence of pulp density on the rate and extent of cobalt extraction was also determined. It was found that the extraction of cobalt followed predominantly the indirect mode of bacterial activity. In this process, ferric iron oxidizes cobaltite to cobalt sulfate and ferric arsenate while being reduced to its ferrous state; the bacteria continuously re-oxidize ferrous to ferric iron. Electrochemical measurements using cyclic voltammetry suggested that cobaltite oxidation involved a number of intermediate reactions.

Jan 1, 1993

By Vladimir Mindin

Simulation of complex equilibria is usually done in the P-T-X coordinates, where "Xu is the amount of individual chemical components in the system. This approach is not productive in some very important cases: (i) investigation of "open" systems, (ii) determination of coordinates (trajectories) of mono-variant points, among others. To solve these and some other problems, we use the idea of chemical potentials of elements (CPE) of the system. A system of different coordinates axes (CPE-axes ) leads to a new strategy of simulation, observing the results of the simulation, and to efficient technology of compressing and storage the data of the simulation.

Jan 1, 1994

By D. M. Fermino, C. G. Bastos Andrade, V. F. Justo, F. R. Valenzuela-Diaz, M. G. S. Valenzuela, C. Volzone

The present paper presents the study of light green smectite clay, from Paraiba, Brazil, submitted to mild acid attack under moderated conditions. Usually, clays are subjected to treatment with strong inorganic acids at temperatures near the boiling point and at high acid concentrations and then, widely used as bleaching agents. The treatment occurred under bellow boiling temperature and at short times of reaction (90°C, reaction times of 1, 6, 12, 18 and 24 hours in close reactor, concentration of the aqueous solution of hydrochloric acid 1.5 M, clay/acid solution ratio of 1g/10mL). The purpose of these attacks is to reduce the concentration of impurities providing color, with minimal change in the clay minerals structure, aiming at use in products of high value such as cosmetics and polymer/clay nanocomposites. The raw clay and the attacked samples were characterized by X-ray diffraction (XRD), cation exchange capacity (CEC), stereomicroscopy, scanning electron microscopy (SEM) and energy dispersive X-ray detector (EDS).

Jan 1, 2015