By Takuya Shinagawa

After vitrification of the residues from a municipal solid waste incinerator, the vitrified products can be used as a construction material, and the dust can be used as raw materials for the non- ferrous industry. The NKK electric-resistance furnace is operated under a reducing atmosphere, and heavy metals such as zinc and lead in the ash vaporize to form dust. Also, dust from the NKK electric-resistance ash melting furnace is composed of water insoluble zinc and lead components and water soluble NaCl and KCI. This is why, The concentration of zinc and lead in the dust after washing is sufficiently high for the dust to be used as a raw material for the zinc and lead industry. NKK developed a heavy metal recovery process in which zinc and lead in the dust are reclaimed as a raw material for smelting by making the best use of the characteristics of the dust.

Jan 1, 2002

By I. J. Moon

The reduction behavior of hematite by H2 and H2-CO gas mixtures was investigated to elucidate the reduction mechanism at 800-950 °C. The hematite compacts were made by Cold Isostatic Pressing to produce compacts of uniform shape and size. The compacts were sintered at 1000° C for 30min, and showed a contraction of 29%. Mercury pressure porosimeter was used for measuring the total porosity, pore size distribution and pore surface area of the compacts. Reduction was measured by means of weight-loss technique using Cahn Balance (Model : TG-171, capacity log, accuracy f 10pg). Microscopic examination and X-ray analysis were used to correlate the structure of reduced compacts with the mechanisms of reduction. Neither chemical reaction control nor diffusion control is adequate in describing the complete course of reduction of the hematite compact. The reduction of hematite compacts was initially controlled by the chemical reaction at oxidelmetal interface. The reaction goes through a transition phase .where it is undergoing a mixed control, followed by the diffusion control towards the end of the reduction. The values of apparent activation energies for chemical reaction control were 3.48-8.43 kcal/mol depending on the gas compositions.

Jan 1, 1997

By M. Hashimoto

The equilibrium distribution ratios of sulfur between molten copper and CaO-fluxes containing caF2 and caC12 were determined in the range of 1300° to 1400° C under carbon monoxide. The rate of approach to equilibrium is rapid and increases with increasing CaCll concentration. In CaO-CaFl-CaCl2 fluxes, the distribution ratio varies in a complex way with temperature and CaFl concentration. The results are compared with those obtained with the binary fluxes of CaO with BaFZ and MgFl ?

Jan 1, 1983

By Run-bo Wang, Zhe Wang, Fan-yi Meng, Jian-Liang Zhang

The influence of semicharcoal substitution for coke breeze on sintering performance was investigated by pot-grate sintering test. At a fixed fuel ratio, sinter productivity and strength decreased with the substitution increasing from 0 to 100% due to better combustibility. To enhance the utilization efficiency of 100% semicharcoal, sintering parameters (moisture and suction pressure) was adjusted. With the moisture increasing, sinter performance of 100% semicharcoal increased because of the suppression of semicharcoal incomplete combustion. As the moisture further increasing to 9.0%, sinter quality gave rise to a decrease trend. The results also showed that the increase of suction pressure was benefit for the increase of heat transfer rate, leading to the improvement of heat utilization energy. Measures to enhance magnetite oxidation during sintering are discussed based on current understanding of the fundamentals that control the sintering process.

Jan 1, 2015

By Vladimir Mindin

This paper presents results of thermodynamic investigations and experimental' studies of some essential for pyrometallurgy of sulfide concentrates topics. Among them: 1. Thermodynamic simulation and experimental investigations of roasting process, 2. Thermodynamic investigations of sulfur dioxide off-gases treatment technologies. 3. Investigations on "Mind in -Kiknadze" effect of suppression of sulfur dioxide formation during sulfide concentrates roasting in the vapor containing atmosphere. 4. Thermodynamic simulation and experimental investigations of sulfide concentrates and manganese containing materials co-roasting processes. Some essential aspects of thermodynamic simulation techniques are also discussed.

Jan 1, 1998

By Zhucheng Huang, Ronghai ZHONG, Liangming Wen, Tao Jiang

The reduction roasting-magnetic separation and its strengthening of high silicon coal-containing mini-pellets by sodium additives were researched. The results show that the carbon gasification reaction and reduction of fine hematite in high silicon coal-containing mini-pellets with 3% sodium additives were enhanced. Comparing with no sodium additives, the gasification rate of carbon with 3% sodium additives reacting with CO2 for 40 minutes at 950 and the metallization rate of reduced pellets with 3% sodium additives after roasting for 35 minutes at 960 increased from 35.15% and 58.72% to 86.98% and 86.15%, respectively. The analysis of SEM equipped with EDS demonstrates that the inner pore of reduced pellets with 3% sodium additives was more developed and the iron grains size significantly enlarged, meanwhile, the iron grade of concentrate increased from 60.45% to 80.23% and the iron recovery rate decreased from 84.67% to 80.78% after grinding-magnetic separation.

Jan 1, 2016

By James E. Simpson, Suresh V. Garimella, III de Groh

"An experimental and numerical study of the horizontal Bridgman growth of pure succinonitrile (SCN) and of a succinonitrile-1.0 mol. % acetone alloy (SCN-1.0 mol. % ACE) has been performed. Experiments at growth rates of 0, 2 and 40 µmis were investigated. The solid/liquid interface was stable (non-dendritic and non-cellular); however, it was not flat. Rather, it was significantly distorted by the influence of convection in the melt and, for the growth cases, by the moving temperature boundary conditions along the ampoule. For the alloy, the interface was determined to be unstable at growth rates greater than 2.8 µmis, but stable for the no-growth and 2 µmis growth cases. When compared to the pure SCN interface, the alloy interface forms closer to the cold zone,· indicating that the melting temperature has been suppressed by the addition of the alloying element. Two-dimensional computer simulations were performed for the no-growth case for both the pure and alloy materials. These simulations indicate that a primary longitudinal convective cell is formed in the melt. The maximum magnitude of velocity was calculated to be 1.515 mmls for pure SCN and 1. 724 mm/s for the alloy. The interface shape predicted by the computer simulation agrees well with the experimentally determined shape for the pure SCN case. In ongoing work, numerical simulations of the process during growth conditions are being performed.IntroductionIncreasingly, advanced materials used in the aerospace, automotive, optics and electronics fields require low levels of defects and high levels of solute uniformity. Directional solidification by the Bridgman process is widely used for synthesis of these high-quality materials. During Bridgman crystal growth, heat and mass transfer by both thermal and solutal gradient-driven convection and diffusion influence the shape of the solid/liquid interface and dopant segregation levels, and hence, directly determine the final crystal quality. Key process parameters include the applied furnace temperature distribution and rate of translation, ampoule properties and furnace orientation."

Jan 1, 1999

By Ahmad-Bitar¸ Riyad N., Shadia J. Ikhmayies

"CdSi-xTex thin films with O<x<0.3 were prepared on glass substrates by the annealing of CdS:In thin films produced by the spray pyrolysis technique. The annealing was performed in nitrogen atmosphere at 400 --,C in the presence of Te vapor. The compositions of the films were determined by energy dispersive X-ray detection (EDAX) measurements. Scanning electron microscopy (SEM) was used to investigate the morphology of the films. The transmittance of the films was measured at room temperature in the wavelength range 400-1100 nm and used to produce the absorbance of the films. The first derivative of the absorbance was used to estimate the optical bandgap energy Eg by using the minima in the first derivative. The relation between the bandgap energy and the fraction x was found to fit with a parabola and bandgaps in the range 2.196: =Eg: =2.480 e V were obtained. Urbach tailing in the bandgap was also investigated.IntroductionPolycrystalline thin film CdS/CdTe solar cells are promising candidates for low cost and high efficiency photovoltaic applications. The fabrication process of these cells involves the deposition of a p-type CdTe absorber layer on top of an n-type CdS one which acts as a window. The efficiency of the solar cell is affected by the method of preparation of both layers [1, 2].Interdiffusion processes taking place at the CdS/CdTe interface have largely been realized to significantly affect the device performance [3] by changing the bandgap of both CdTe and CdS which modifies the spectral response of the solar cell [ 4]. The formation of a mixed crystal or a graded layer causes a reduction in the lattice mismatch at the CdS/CdTe junction [5] which is about 9% [ 6] and then a reduction in the number of interfacial states and recombination centers, thus enhancing the solar cell performance [7, 8]. A complete understanding of the properties of the intermixed layers CdSxTe1-x that usually constitutes the interfacial region in the CdS/CdTe solar cell is essential. According to our knowledge, a lot of research was devoted to the investigation of the diffusion of S into CdTe [3-5, 9]; but little on the direct investigation of the diffusion of Te into CdS [6]."

Jan 1, 2011

By Jie Li, Zhongliang Tian, Xun Hu, Kai Zhang, Yanqing Lai, Hongliang Zhang

The Al-Sc Alloys show many advanced properties for a wide range of engineering applications. But the metal Sc must be added into the metal Al in the form of the Al-Sc master alloy, which is usually produced by the thermal reduction process. In this paper, the decomposition voltages of Sc2O3 and Al2O3 in Na3AlF6-K3AlF6-AlF3 melt were calculated based on the Nernst equation. And the Al-Sc master alloy was prepared in the melt at 950°C by electrolysis. The results show that the Al-Sc master alloy can be prepared by the co-deposition of Sc3+ and Al3+ at the cathode if the concentration ratio of Sc2O3 to Al2O3 in the melt is more than 2:1 under the condition of the aluminum electrolysis. SEM and ICP analysis of the product indicates that the Al-Sc master alloy is made of the phase Al and the phase Al3Sc.

Jan 1, 2016

By Clemens Schmetterer, Patrick J. Masset

"The surface tension represents an important property for the modelling of high temperature processes. In this study the surface tension of two Al2O3 – CaO – SiO2 model slags and the influence of the admixture of 5 up to 30 wt.% FeO were studied. The surface tension measurements were carried out using the sessile drop technique on BN substrates under Ar atmosphere (10-6 atm O2) up to 1500 °C.IntroductionThe aim of VIRTUHCON1 is the virtualization of high temperature conversion processes, a task that requires thorough understanding of these processes. In many of these conversion processes slag plays an important role to control the properties of the product, to protect the reactor lining or simply as waste. Slag surface tension is one of the materials properties that is needed for the description of such processes, since it influences the interactions between the components in the reactor, e.g. at the slag – Fe interface in the blast furnace.Surface and interfacial tensions have thus received considerable attention in research, but the number of investigations in this particular pseudo-quaternary system is surprisingly low. Furthermore, the literature data are subject to different measurement conditions and techniques which complicates the data analysis and comparison.The slag atlas [1] offers a compilation of the available literature until 1986 (shown in Table I), but literature search has not revealed more recent studies of this system until now. For example, Elliott and Mounier [2] determined the surface tension of ACSF slags using the double tube maximum bubble pressure technique at 1200 °C. They kept their slags in contact with Cu-S-F mattes, and the slag therefore contained a certain amount of sulphur which acts as a surfactant and lowers the surface tension. The compositions of their slags were scattered over a wide composition range and they did not use a common ACS base mixture for their tests, either. The surface tension values vary between 417 and 446 mN/m, but due to the reasons just mentioned no trend in the measurements can be observed and the influence of FeO admixture on the surface tension cannot be deduced. Further information including the temperature dependence is available from Pavlov et al. [3], Ishchanov and Shushkov [4] and Murav’eva and Kaplun [5]; the diagram on page 446 in Ref. [1] has been drawn from these sources. Both positive and negative temperature coefficients are reported in these works. SiO2 is the only pure constituent that has a positive temperature coefficient [6], but a correlation of the temperature coefficient with the SiO2 content was not found to be conclusive."

Jan 1, 2011

By G. A. Irons, D. Colbert

Several electric arc furnace (EAF) shops have increased the zinc and lead grades of EAF dust by reinjecting it into their furnaces; however, the kinetics of this operation are poorly understood. To understand the kinetics, EAF dust was injected into 70 kg heats of iron or steel in an induction furnace. Supplemental additions of carbon and oxygen to overcome the heat load on the system were also investigated. In all cases, the dust was chemically transformed, and the zinc content increased from 16% Zn to 60 - 80% Zn. About 50% of the zinc in the EAF dust dissolved in the iron or steel. The zinc oxide in the dust is thought to be reduced by carbon and the zinc vapour subsequently dissolved in the iron. A kinetic model for the dissolution process is proposed, and the implications for EAF dust recycling are discussed.

Jan 1, 2000

By Chengxian Lui

Detailed mineralogical and metallurgical investigations were carried out on a phosphorous-bearing manganese carbonate ore from the Huayuan manganese mine, Hunan, China. Microprobe analyses indicate that the Manganese occurs mainly in calc-rhodochrosite and in rhodochrosite. The cOll&apos;pOsitional range of these manganese carbonate minerals is 50 -80 % MnOJ3, 0 -35 % CaOJ3, 5-35 % MgC03 and 0 -15 F~. The manganese carbonate minerals are very fine grained, IOOSt are between 4.6 and 9.4 1m in diameter. The small grains are clustered into aggregates that form bands 0.5 to 10 rnn wide. The phosphorous-bearing mineral in the ore is fluorapatite and is in grains that are generally smaller than 6 1m in diameter. Metallurgical tests show that it is possible to concentrate the aggregates of manganese carbonate minerals by high intensity magnetic separation, and to reduce the phosphorous content by rpasting the concentrate to convert the manganese carl::x>nates to insoluble hausmannite, and then leaching the roast product with HCI to dissolve the fluorapatite.

Jan 1, 1989

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By Lu Lin, Yanping Bao, Xiang Li, Linzhu Wang, Xiaobai Yan

The results showed the microinclusions were mainly Al2O3 and sulfide inclusions from tapping to the beginning of LF refining. Al2O3 inclusions were modificated into calcium aluminates after calcium treatment. Lots of spherical calcium aluminates composite inclusions containing MgO, TiO2 and MnS were found after soft blowing and during tundish metallurgy and left in the slab which caused the defects of beam plates. Pure Al2O3 inclusions were observed again after soft blowing 8min. Average sulfur content in inclusions decreased because of the high desulfurization ability of refining slag. Average Ca/Al ratio value in inclusions increased during LF refinging because of the reduction of CaO in slag by carbon and it increased obviously during the process of soft blowing 8min because of the dissolusion of calcium wire.

Jan 1, 2015

By Jorge Alberto Soares Tenório, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Franco Alves Lavacchini Ramunno

"The traditional process for recovery of metals from waste electric and electronic equipment (WEEE) usually involves pyrometallurgical processing. However, the application of this technology to processing waste printed circuit boards (WPCBs) might lead to the formation of dioxins and furans, due to thermal degradation of flame-retardants and polymeric resins present in the board substrate. Therefore, this paper proposes a hydrometallurgical route for the recovery of copper. The acid leaching behavior of copper has been investigated at three different temperatures (25°C, 50°C and 75°C) with and without the addition of an oxidizing agent (hydrogen peroxide - H202). The dissolution kinetics for acid copper leaching was calculated based on chemical analysis by ICP-OES (Inductively Coupled Plasma - Optical Emission Spectroscopy). At 50°C with 1 mol/L H2S04 added 10 mL H202 (30%) each half hour under pulp density of 1 g I 10 mL, 100% of copper was extracted after 3 hours. The dissolution kinetics of copper with H2SO4-H2O 2 followed 1 - (1 - X)113 =Ket, i.e. chemically controlled reaction model.IntroductionThe information regarding the generation of waste electric and electronic equipment (WEEE) are still difficult to obtain because the estimates should take into consideration the historical production and sale of various products and the rate at which they reach the end of their life cycle, whose duration depends on the behavior of consumers [1]. Thus, the estimated overall WEEE generation varies between 25 and 50 million tons each year, which corresponds to more than 5% of all municipal waste generated [2], and this amount will increase at a rate of 3 to 5% per year, approximately three times faster than other individual types of waste [3].Printed circuit boards (PCBs) are essential parts of electric and electronic equipment (EEE), being found in virtually all electronic products, as well as in weapons systems [4]. A PCB is a basic component, which consists of a board where copper tracks are deposited. While the board behaves as an electrical insulator, the tracks connect electrically the various components attached to the board [ 5]. In addition to glass fibers, paper and resins, the PCBs contain significant amounts of metals, such as copper, iron, nickel, lead, stain, silver, gold and palladium [6]. In general, the weight fraction of metal is around 28% and the remainder of the boards is composed of plastic (19%), bromine (as flame retardant - 4%) and ceramic material (49%) [7]."

Jan 1, 2014

By J. D. Miller

Low-level radioactive contaminated soils (10-500 pci/gm) created by defense-related activities at certain superfund sites, such as Nevada Test Site (NTS), is a current environmental concern. Many of these contaminated sites may require appropriate cleanup and restoration, which could cost billions of dollars and put tremendous pressure on our limited financial resources. Therefore, the development of a selective flotation process to separate such radionuclides from contaminated soils should be considered. In this study, both a pure depleted UO2 sample and three synthetic UO2/soil mixtures were used to evaluate surface chemistry features and to examine the possibility for the flotation of fine UO2 particles from selected soils. It was intended that this model system would be a reasonable representation of contaminated soils such as those found at the Nevada Test Site which are reported to be contaminated by PuO2 fallout. The effect of reagent schedule, particle size distribution, and surface charge are discussed with respect to the flotation separation of the UO2/soil mixtures. It was found that both commercial fatty acids and reagent grade sodium oleate are effective collectors for UO2 flotation provided the pH is adjusted to the range of pH 8-9. The bench-scale flotation results successfully demonstrated that froth flotation technology can be used to remove UO2 from such model contaminated soils with appropriate flotation chemistry conditions which depend on the soil characteristics and other pretreatment procedures. In the best case, 90.2% of the UO2 was removed from a UO2/NTS soil mixture (119 ppm UO2) and the soil reduced in UO2 contamination from 119 ppm to 17 ppm in a single stage bench flotation. The impact of clay slimes present in the soil is revealed by the results which show that, for example, for a deslimed soil (28x400 mesh and 100 mg UO2/kg soil) 85¬90% UO2 recovery can be obtained with a reduction in contamination to 4.6 mg U02/kg soil.

Jan 1, 1995

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By I. D. Reznik

On blowing nickel matte in a converter without quartz, first the oxidation of metallic iron and a part of FeS occurs without evolving sulfur dioxide, the formed FeO dissolves in a sulphide smelt and form a homogeneous oxysulphide smelt. On further increasing the FeO content, the oxysulphide separates into 2 layers. Based on the laboratory investigation of FeO-(FeS+Fe°) - (Ni3S2+Ni°) ternary phase diagram we have identified the separation region at 1250°C. The boundaries of the separation region have the form of an arc and the composition of the separated oxysulphide layers is defined by the canodes. In the nickel or copper-nickel matte - silicacalcium oxide slag system at 1250°C three layers, namely sulphide, oxysulphide, and slag may be formed. A high slag basicity due to the presence of CaO can serve to enhance the activity of FeO; a low nickel content in the matte corresponds to a high concentration of FeS therein; FeO from slag and FeS from the matte form a homogeneous FeO-FeS solution, i.e. an oxysulphide layer. The investigation on the "Camebaks" apparatus and by the nuclear gamma-ray resonance spectroscopy method of the phase composition in a slowly cooled oxysulphide layer has shown the presence of four phases: wustite, troilite, ferronickel grains, and calcium oxide-silica inclusions. Knowledge of regularities in the oxysulphides formation makes it possible to use them in pyrometallurgy of nickel and cobalt or preventing their formation.

Jan 1, 1997

By J. R. Sarazin

Density driven convection during solidification has been recognized for some time to result in macrosegregation particularly when lower density alloying elements are rejected into the interdendritic liquid. The resulting segregates are commonly referred to as channels, freckles or A-segregates. Buoyancy driven convection leading to channel formation has been examined in three model systems possessing somewhat different materials parameters. They are the Pb-Sn eutectic system, the transparent aqueous-salt NH C1-H 0 4 2 eutectic system and the transparent organic succinonitrile-ethanol monotectic system. Convection in these systems is controlled by a balance of buoyant and viscous forces, which are strong functions of composition and temperature. Composition, temperature and flow velocity were measured and elimination of channels through heavier ternary additions is discussed.

Jan 1, 1991

By Gervais Soucy, François Quesnel, Pierre Hovington, Wen Zhu, Karim Zaghib, Jocelyn Veilleux

The properties of lithium titanates anodes in Li-ion batteries are highly dependent on their secondary constituents. While their main phase is usually constituted of Li4Ti5O12, significant quantity of lithium titanates compounds of various stoichiometry are often present, due to either the processing, usage or aging of the material. These may go underreported, as many of these spectrums overlap or display low signal in X-ray diffraction (XRD). Samples of nanosized lithium titanates synthetized by inductive plasma were characterized by XRD and scanning electron microscopy (SEM), as they provide a regular yet typical crystallite size and shape including multiple phases. A Rietveld refinement was developed to extract the composition of these samples. Mass balance through further annealing and differential scanning calorimetry (DSC) enthalpy measurements from phase transformations were also used as identification and validation techniques.

Jan 1, 2015