By Qian Li, Li-chen Hou, Yong-bin Yang, Tao Jiang, Jian-jun Hu, Bing Xu

Extraction of gold from refractory gold concentrates usually requires an oxidation step to remove arsenides、sulphides and carbonaceous matter. In this investigation, the gold concentrates were two-stage roasted under different atmospheres and temperatures. Results indicated that at the first stage, under neutral atmosphere, the removal rate of arsenic increases as the temperature rises. Under the oxidizing atmosphere, with the increase of temperature, arsenic content in the residued calcine increases, in addition, the volatilization of arsenic is also affected by the oxidation of carbon that generated CO, which is advantageous to the decomposition of arsenate decomposition. At the second stage of roasting, it is the higher temperature and stronger oxidizing atmosphere, the faster sulfur and carbon oxidated rate is, but at the same time, the calcine appears the phenomenon of consolidation because of the phase of silicate compounds generate.

Jan 1, 2015

By W. G. Davenport

This chapter demonstrates how our matrices can be used for controlling a flash furnace. Specifically, it shows how we can determine the adjustments in industrial oxygen, air, oil and flux input rates that will; (a) correctly alter product temperatures and compositions to newly targeted values (b), maintain set-point product temperatures and compositions with varying feed compositions and feed rates. It also discusses corrective actions that might be taken when furnace temperature and matte grade unexpectedly change.

Jan 1, 2001

By Zachery Zanetell

Flotation circuit performance has become increasingly more challenging due to the complexity of available ore sources. To optimize value mineral recovery, the mineralogical composition of the ore should be evaluated and understood. Utilizing a variety of mineralogical and analytical tools, flotation processing challenges can be overcome and potential limitations understood. In this paper, several case studies will be discussed in terms of the value that has been provided through the use of mineralogical analysis to optimize flotation performance.

By Paponetti B. . A.

Gold is usually recovered by cyanidation, thiourea leaching and amalgamation, however the efficiency of these technologies, in the case of refractory ores, is low ever when fuie grinding is practised. For example, .if the gold particles are included in sulphide minerals, the leachant cannot reach them, so they are often lost in the tailings. Hence .it is first necessary to break the sulphide crystals by preliminary treatment such as roasting, nitric .acid oxidation, pressure leaching and bacterial oxidation and then apply a conventional extractive technique for satisfactory gold recovery. This paper describes the effect of biological pre-treatment with Thiobacillus ferrooxidans) on the? extraction ? and? recovery of gold by conventional cyanidate. leaching from; a refractory arsenopyrite ore from Golcuck (Turkey).

Jan 1, 1991

By A. W. Bryson, K. C. Lenthall

"With the growth in the use of cobalt in industry, interest in its extraction and recovery has increased. With this increased interest comes the need for a fundamental knowledge of the processes involved in the recovery of cobalt metal. This paper examines the effects of cobalt concentration, catholyte pH, operating temperature and current density on cobalt electrowinning with respect to the current efficiency, cell potential and nature of the cobalt deposit. It is found that the cobalt concentration and catholyte pH affect the current efficiency, while current density and temperature affect the cell potential and thus the specific power consumption. Pitting on the deposit is affected by the catholyte pH and the operating temperature. Furthermore, the effect of feed flow-rate on catholyte pH, and thus current efficiency, is investigated. A model to predict the cell performance, which includes the flux of hydrogen ions through the diaphragm, is proposed.IntroductionCobalt metal is a silvery transitional metal found between nickel and iron on the periodic table. Due to its resistance to corrosion and other properties under high temperatures and its good work-hardening characteristics, it is favoured in alloys used in high temperature applications. These include aerospace, aircraft and high speed tools. Other applications include its use as a colourant in glass and ceramics, a drying agent in paints, a nutrient for livestock, a catalyst in the petroleum industry and, in the medical field, in prosthetics and radiology.The main deposits of cobalt are found in Central Africa, specifically Zaire and Zambia, although deposits also occur in Morocco, Canada and Australia. The cobalt is generally associated with other transitional metals including nickel, iron and copper. It is generally extracted by hydrometallurgical means and recovered from solution by electrowinning or hydrogen reduction. Little data [1-2] exists in literature on the electrowinning of cobalt from aqueous solutions. This paper investigates the effects of various operating conditions on the current efficiency, cell potential and deposit nature under continuous operation."

Jan 1, 1997

By W. D. Keller

Scanning electron microscopy (SEM) accompanied by X-ray energy dispersive analysis (XES) is a useful tool in process clay mineralogy. The texture of kaolin, illustrated by SEM, gives a clue to its mode of genesis and probable industrial application. One type of kaolin, originating dominantly by weathering, has an open texture, slakes readily, and is used for filling and coating paper. Another type, in contrast, originates by diagenesis of Al-silicate sediments, and spectacularly resists slaking, thereby enabling it to maintain its bulk density and controlled size and shape of particles after crushing and moistening; this meets an important requirement for the manufacture of refractories. Ratios of elemental Al:Si that may be rapidly determined by SEM and XES yield information on the origin and purity of bauxite and bauxitic clays, and aid in quality control and processing of them. SEM of dissimilar textures of quartz, as in chert and novaculite, are evidence for geothermometry on a stratigraphic scale that is potentially useful in delimiting thermally favorable or unfavorable areas for hydrocarbon exploration, and possibly for unexposed metallic ore deposits.

Jan 1, 1982

By B. C. Blakey

Unlike most hydrometallurgical slurries, those containing significant concentrations of goethite are typically highly viscous and shear-thinning, even at solid volume fractions below 5%. The viscosity may also depend upon time. These characteristics must be taken into consideration in slurry transport and heating. The technical literature is replete with apparent contradictions regarding the viscous behavior of these slurries, which may be due, in part, to variations in viscosity-measuring techniques. We present techniques that yield consistent results suitable for use in process design. A striking degree of time-dependent behavior is demonstrated for a laterite slurry. Reliable methods to design and analyze tubular transport and heating systems for time-independent slurries are summarized. Rules of thumb are then offered to account for the effects of time-dependency.

Jan 1, 2000

By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The clean utilization of the residue containing chloride, CuCl residue, produced from zinc hydrometallurgy is very important for the recycle of valuable metals. And drying is the main process in recycling. In this study, response surface methodology was used to optimize operating conditions of the drying of CuCl residue in a convection oven and desirability function used as the methodology for the optimization. Optimization factors were air temperature (80–100°C), material thickness (10–25mm) and process time (80–120min) while investigated responses was final moisture content. The optimum conditions were found to be the temperature of 95.48°C with the material thickness of 13.47mm for the process time of 89.48 min. Under optimum conditions, the predicted moisture content of CuCl residue was 4.11% while the experimental date was 4.13%. The experimental value after process optimization was found to agree satisfactory with the predicted value. After drying, XRD was used to analyze the main phases of CuCl residue. The CuCl residue is made up of CuCl,Cu2O, ZnS and other compounds.

Jan 1, 2015

By José Brant, Douglas Torres, Rogério Navarro, Rodrigo Souza, Eduardo Brocchi

The steelmaking process requires the input of ferro-alloys to implement the adjustment of some elements composition in the final product. In the particular case of stainless steel production, the high carbon FeCr alloy stands out as one important precursor. However in the production of this material a certain quantity of fine powder with remarkable chromium and carbon content is also generated, which, in turn, could be processed through alkaline roasting in order to selectively recovery this element in a subsequent aqueous route. In the present work, this process is investigated, using excess of NaOH as oxidizing agent, and H2O2 for precipitating chromium as Cr(OH)3, which is next calcinated to Cr2O3. According to the results, the global achieved recovery has shown to be around 98%, suggesting that the proposed route can be seen as a potential process for chromium oxide production from the mentioned fine powder.

Jan 1, 2015

By Eva B. Kisvarsanyi

An Early Proterozoic orogenic terrane of metasedimentary and metaigneous rocks underlies Nebraska, Kansas, and Missouri. Middle Proterozoic epizonal terranes of anorogenic granite and rhyolite, a known metallogenic province partly exposed in southeastern Missouri, overlap the orogenic terrane on the south. These Proterozoic terranes, covered by less than 1,000 meters of Phanerozoic strata, contain a virtually untapped source of mineral wealth and are one of the last frontiers for geologic exploration in the continen-tal United States. Petrographic study of subsurface samples is a powerful tool in the identification of favorable host rocks for a variety of ore deposits.

Jan 1, 1987

By Tianzu Yang, Weifeng Liu, Lin Chen, Xinxin Fu, Shuai Rao, DUCHAO ZHANG

It is well known that the gold ores containing a high content of arsenic and antimony are very refractory. In this paper, the adverse effect of antimony on the extraction of gold by pretreatment-cyanide leaching was discussed in detail. Moreover, these processes of removing and recovering antimony from alkaline sodium sulfide or hydrochloric acid systems were introduced. Last bu not the least, a novel cleaning technology for recovering antimony from refractory gold ores was proposed. Antimony was dissolved into the solution with sodium sulfide and sodium hydroxide as leaching agents. And then pressure oxidation technology was applied to prepare sodium pyroantimonate from sodium thioantimonite solutions. This process is more promising owing to its high removal ratio of antimony, low production cost and environment friendly, which provides a positive guidance for the extraction of antimony from antimonial refractory gold ores.

Mar 1, 2017

By Xi-chang Shi, Yun-feng Fu, Bai-zhen Chen, Hui Xu, Xiang Xiao

"Extracting boric acid from saline brine by boron specific ion-exchange resin was investigated. Effects of resin amount, temperature, time and stirring speed on boron adsorption rate were studied in the experiments. The results indicated that the XSC-700 resin showed excellent boron absorbability and it performed better property for elution. The maximum boron adsorption capacity was 6.16 mg/ml in the optimum conditions: the resin concentration of 5 ml/(100 ml brine), the temperature of 60°C, the time of 5-6h and the stirring speed of 100 r/min. Boron was eluted from the resin with HCl and boric acid was crystallized by evaporating the eluate. The product of boric acid was in pure form as confirmed by XRD and other analysis techniques.1 IntroductionBoron has a number of minerals in nature such as tincal, colemanite, ulexite, and kemite, etc. [1-2]. Boron and its compounds are chemical materials of significant value. The principal industrial uses of boron compounds are in the production of glass, porcelain, enamels and detergents. Other uses include fertilizers, metallurgy, and nuclear shielding [3-4]. In recent years, because of the large-scale mining boron ore, ore resources are drained gradually. With the development of science and technology, the boron mineral resources will be unsatisfied with the future requirement. There exits abundant boron resources in salt lakes which cover about 40% of the total reserves in China. If we can obtain boron from salt lakes, it will produce great economic interests [5-6]. Therefore, actively seeking boron from salt lake and other resources in suitable conditions has become a hot spot in the research organizations of boron resources development and utilization in the world [7].There are many methods such as acid crystallization, solvent extraction and ion exchange processes suggested effective for boron extraction from aqueous solutions. Acid crystallization method has the shortcomings of complicated procedures, the pollution caused by hydrochloric and other ingredients returning to salt lakes during the extraction process. Although solvent extraction process increases the boron acid recovery efficiency, the cost of production is high [8-9]. However, Chelating resin extracting boron has the characteristics of simple process, easy operation and no pollution. It was reported that chelating resins containing functional groups show a high selectivity for boron extraction [10-12]. Therefore, ion exchange technique which is now the most practical application of significance and most extensively used ha"

Jan 1, 2011

By Jun Chang, Jin-hui Peng, Jing Chen, Li-bo Zhang

The leaching of indium from refractory zinc oxide flue dust(ZOFD) is attempted to utilize microwave sulfating roasting process, followed by water leaching. The ZOFD and roasted product were characterized by XRD and SEM/EDS analysis. The effects of various roasting parameters, such as roasting temperature/duration, the proportion of sulfuric acid, as well as the leaching parameters such as the leaching duration and liquid/solid ratio, were assessed. The results indicate that nearly 97% of indium could be leached under the following conditions: mass ratio of concentrated sulfuric acid to ZOFD to be 0.5, roasting temperature of 150 ℃ and duration of 1.5 hours; while the optimal leaching conditions hold at temperature of 25 ℃ for 1 hour, with 4:1 of liquid/solid ratio. The indium leaching rate by the microwave roasting increased by 8% as compared with the conventional roasting process under identical conditions.

Jan 1, 2015

By G. E. S. Lima, I. K. R. Andrade, N. G. Viana, R. O. G. Martins, L. M. Sathler, L. G. Pedroti, C. M. M. E. Torres, W. E. H. Fernandes, C. M. Silva, M. A. Caetano

In Brazil, kraft pulp mills are rapidly expanding and industrial waste generation is increasing. Technical feasibility of using solid wastes from kraft pulp mills as raw material in other industries may be an interesting approach to manage environmental and economic aspects of the industry. This paper proposes the incorporation, in different proportions (0, 2.5, 5 and 7.5%), of alkaline solid wastes from pulp mills, namely dregs and grits, to clinker in the Portland cement industry. The research was carried out in two steps: (i) characterization of dregs, grits and clinker; (ii) laboratory testing (determination of soundness by the Le Chatelier method, determination of setting times, determination of water content of the paste with normal consistency, determination of compressive strength and static modulus of elasticity). The results showed that the addition of dregs and grits to the clinker up to 2.5% were feasible according to the Portland cement Brazilian standards.

Mar 1, 2017

By M. Wenzel, Dang Thanh Tung, Nguyen Anh Duc, Nguyen Huu Luong, Dang Van Sy, N. Kelly, K. Gloe, K. Kretschmer, Phuc Nguyen Le, K. Schnaars, S. Robles M, L. Götzke, J. J. Weigand

The recovery of rare earth metals from secondary sources has attracted much attention due to their ever expanding demand in the high-tech industry. The studies reported here focus on the hydrometallurgical recovery of lanthanum and cerium from spent fluid catalytic cracking (FCC) catalysts in a two-step process: leaching with nitric acid and solvent extraction by tri-n-butyl phosphate (TBP) and di(2-ethylhexyl)phosphoric acid (D2EHPA). The experiments show a high dissolution yield of about 93% lanthanum and 42% cerium in a single leaching step with 2 M (126 g/L) HNO3 at 80 °C; only 11% aluminum has been dissolved simultaneously. In the subsequent solvent extraction step the best results for this leach liquor could be achieved using a 1:1 mixture of 25% (v/v) TBP (0.92 M) and 25% (v/v) D2EHPA (0.76 M) in n-decane without the need for any pH adjustment. In that case La(III) and Ce(III) can be extracted with 60% and 74% yield respectively in one stage from the majority of accompanying matrix elements. In particular no extraction of Al(III) could be observed under these conditions.

Jan 1, 2016

By Gang Qi

The solubility of nitrogen in pure molybdenum was measured over the temperature range 2173 to 2473 K and up to one atmosphere (101 kPa) of nitrogen gas pressure. Both thermochemical and kinetic aspects of this phenomenon were considered in this study. The solution of nitrogen in molybdenum may be expressed by the reaction 1/2N2(g) = {N} (Mo,s), for which the standard Gibbs energy is given by the expression {A}G° = 78,500 + 27.36T Joules/g atom N. The formation of molybdenum nitrides, specifically Mo2N, was considered. Attention was also focused on the mechanism of nitrogen solution in molybdenum. Estimates of the diffusivity of nitrogen atoms in solid molybdenum were derived from the kinetic data.

Jan 1, 1991

By Jaeheon Lee

Gold-copper alloys are shown to form during the cementation of gold on copper in a solution containing 0.25M [S2O32-] at 25oC. The alloy composition is strongly dependent on the initial Cu:Au ratio in solution and ranges from Au3Cu to AuCu3. XPS results for Au, Cu, S, and O are reported as a function of depth through an entire deposited film with an initial solution containing 20 ppm [Au] and 30 ppm [Cu]. The deposit contained about 20 atomic % gold and was predominantly Cu3Au. Underpotential deposition (UPD) theory is discussed as a mechanism for explaining the formation of these alloys. Several other systems that produce alloys during contact reduction/cementation are also discussed.

Jan 1, 2003

By Kenneth S. Coley, Michael Pomeroy, Elaine Chen

Recent work on modeling of BOF steelmaking is reviewed, highlighting the critical aspects of each approach. It is concluded that the most successful models should be based on a deep understanding of the mechanisms and kinetics of the critical reactions. The importance of the decarburization mechanism is discussed with particular reference to its role in droplet swelling or bloating which has a profound influence on the droplet residence time in the slag. Conditions which cause bloating are discussed and the rate determining step is proposed to be primarily nucleation of CO bubbles inside the metal droplet with some influence from growth by reaction at the bubble/metal interface. The discrepancy in the super-saturation ratio required for classical nucleation is discussed and an approach using a surface tension modifying parameter is illustrated. Finally, the role of CO nucleation in controlling the driving force for dephosphorization is discussed.

Jan 1, 2014

By Minting Li, Hailong Yang, ChangWei, Cunxiong Li, Gang Fan, Xingbin Li, ZhiganDeng

The filtration problems on acid leaching sludge of high silicon zinc ore have been paid extensive attention in zinc hydrometallurgy. It was found that soluble silica can be effectively converted into silica precipitate with good settling, filtration and washing properties, and the filtration rate can be in excess of 800 L/m2 · h under certain leaching conditions. According to investigating on the filtration rate, viscosity and concentration of silica of leaching sludge or liquor, the filtering temperature can tremendously improve the filtration property of pulp. At the same time, the experimental data indicated that the viscosity of leaching liquor was the key factor influencing filtration property of leaching sludge.

Jan 1, 2016

By R. C. Hubli

A chemical model has been developed to investigate the dissolution of sulphide minerals in brine solutions containing copper and iron chlorides. The model has been employed to study the dissolution .of synthetic NiS using different initial concentrations of Cu(II), Cu(I), Fe(III) and temperature. The speciation of copper with particular reference to the formation of hydroxy-chlorides as a function of total chloride and H+ has been computed. The model predictions are in agreement with experimental results. It has been found that addition of Fe(III) results in the maintenance of a high Cu(II)/Cu(I) ratio leading to enhanced rates of dissolution and suppresses the loss of Cu(II) due to the formation of hydroxyl-complexes.

Jan 1, 1997