By R. L. Segall

AN unusual thermal etch figure in copper is described and an explanation in terms of twinning is suggested. A flat polycrystalline specimen of OFHC copper cut from a rolled sheet was electro-polished in orthophosphoric acid and annealed at 950°C in a vacuum of approximately 10-3 mm Hg for 2 hr. The specimen was found to be thermally etched, the markings on the surface being consistent with the assumption that they were the traces of the (111) planes which are developed preferentially because they have the lowest free energy. However, on one grain (the grain shown in Fig. 1) the traces formed an almost regular pentagon and at first sight it seemed unlikely that they could all be (111) traces. These traces were studied further because it was thought that they might be a type of growth spiral. A fringe pattern showed that this was not so, the grain being sensibly flat and the only features having steps were the striations and the faint curved line passing out from the center of the pentagons. To obtain some additional information, the specimen was deformed in tension. The effect of the stress was first to cause the appearance of lines running from the centers to the apexes of the pentagons and then to tilt the five segments so formed. At a much greater stress, appreciable slip appeared on the grain; these effects can be seen in Fig. 2. The micrograph was taken at a fairly late stage in the deformation and the tilting is quite marked. The magnification is the same as in Fig. 1, and although some slip can be seen it could be observed better by varying the illumination and using higher magnifications. In each segment of the grain, slip (which takes place on the (111) planes) was parallel to the side of the pentagon in that segment. The marked changes in direction of slip from segment to segment seemed to be incompatible with the presence of a regular array of subgrains. These results suggest that some of the five segments were twins. If this is so, since the twinning plane in copper is the (111) plane, the radial lines must be traces of the (111) planes on the surface. From the symmetry of the striations about the radial lines, these planes must be almost perpendicular to the surface. The angle between <III>directions in face-centered-cubic copper is 70&apos;32&apos;. If, in Fig. 3, OAB (triangle 1) is taken as matrix and OA, OB are (111) planes viewed edge on, then AB is in the correct direction to be the trace of either of the other two (111) planes on the surface. If triangle 2 is the twin (about the (111) plane perpendicular to the surface and containing OB) of triangle 1, then once again it can be shown that all lines are traces of (111) planes. Similarly, triangle 3 is the twin of triangle 2, 4 of 3, and 5 of both 4 and 1. (The sequence is, of course, quite arbitrary.) However, if this were the case there would be a discrepancy of 7&apos;20&apos; to be accounted for. It is suggested that the faint curved line passing outward from the center of the pentagon represents either a low angle boundary or a sixth small twin. The slight step shown by the fringes at this line might be an indication that the former is the case. This explanation does not account for the coincidence of obtaining a grain whose surface must be so close to (110) and obtaining the curious twinning described previously; it would be of interest to find a specific mechanism for this.

Jan 1, 1958

By Wei-Kao Lu

A general rate equation is derived for gas -solid reactions in metallurgical processes by considering the contributions of chemical reaction at inter-phase boundaries and diffusion through the solid product layer simultaneously. This equation takes care of the whole range continuously from purely diffusion control to purely chemical reaction control. The parabolic law,&apos; McKewan&apos;s equationa derived with the assumption of interface area control and the equation derived by Kawasaki et al. with the assumption of purely diffusion control are found as the limiting cases of the corresponding forms of the general rate equation. Many metallurgical processes involving gas-solid reactions have been extensively studied. The common examples of these processes include the reduction of oxides to metallic products, the roasting of sulfides to oxides or chlorides and the oxidation of metals. Gas-solid reactions consist of at least two kinds of steps; one involves the transport of reactant and product to and from the reaction zone and the other is the chemical reaction taking place at the interphase boundaries. In the limiting cases one or the other of the above mentioned steps will be much slower than the other and is then rate controlling. For example, the oxidation of metals is diffusion controlled and obeys the parabolic law.&apos; On the other hand, if the diffusion rate is much larger than the chemical reaction rate then it will be controlled by the chemical reaction rate. This latter case occurs for the reduction of iron oxides studied by McKewan. If the rate of diffusion and of the chemical reaction have the same order of magnitude, a more detailed analysis is necessary. Thus at the beginning of the reaction when the solid and gaseous reactants are in direct contact, the reaction should be chemical reaction rate controlled as no diffusion process is involved. At the other extreme as the reaction zone moves further into the solid, the diffusion distance becomes greater and the diffusion rate continuously decreases. Eventually, therefore, for a sufficiently large sample the rate must become diffusion controlled. As the transition from one controlling step to the other must be continuous, we cannot describe this transition period by either of the two limiting cases. In this paper the author attempts to derive a general rate equation for gas-solid reaction systems. This is effected by considering the rates of diffusion and chemical reaction simultaneously from the state of pure diffusion control to pure chemical reaction control. I) DERIVATION The system under consideration is made of at least three phases, namely the gaseous one, the solid reactant, and the solid product as shown in Fig. 1. The notations are listed at the end of the paper. The mass transfer process involves the diffusion of reactants and products across the solid product layer. It is reasonable to consider that no chemical reaction will take place in the solid product layer with respect to both gaseous reactant and product. For the characteristics of local equilibrium of the system, the diffusion process is really in a quasi-steady-state. It will be proved in the following paragraphs. Then we can invoke the law of conservation of mass valid for all chemical species passing through the layer. The solid reactant sphere has an initial radius, ro, after a fraction of completeness of the reaction, the unreacted core has a radius ri, where r, is in the solid product region. Let Cg be the activity of gaseous reactant in the

Jan 1, 1963

By D. S. Gleason, D. E. Severson, D. R. Skidmore

Pittsburg and Midway Coal Co. has modified the German Pott-Broche process, on which patents date back to 1927, to produce on a bench scale liquid products by solution hydrogenation of coal. A continuing program of lignite solution-hydro gena-tion experiments is directed toward investigating coal solution reactions, determining favorable conditions for the solution refining of lignite by the Pott-Broche process, and investigating some of the uses for the de-ashed product obtained from lignite The German Pott-Broche process1" on which patents date back to 1927, has been modified by the Pittsburg and Midway Coal Co., a Gulf Oil subsidiary, to produce on a bench scale liquid products by solution -hydrogena-tion of coal." The objectives of the present effort are to investigate coal solution reactions, to determine favorable conditions for the solution refining of lignite by the Pott-Broche process, and to investigate some of the uses for the de-ashed product obtained from lignite. This paper is a summary of results to date in a continuing program of lignite solution-hydrogenation experiments. The coal solution reaction program has several principal aims. The first of these is to determine whether lignite can be successfully dissolved in solvents that might be practical for commercial development. The second object is to determine whether the solvents function after successive cycles of use, recovery, and reuse. It seems necessary to the economics of a potential commercial process that the solvent be recycled. Third, it is desired to learn something about the distribution of the ash constituents between cake and filtrate. The extent of ash removal is important. The nature and quantity of mineral matter passing through the filter may determine end-use marketability. For certain use applications, trace quantities of certain minerals can be objectionable, e.g., titanium and vanadium must be very low in electrode carbon for aluminum production. The Solution Reaction The coal solution Process involves an extremely complex system of chemical reactions. An initial solvent such as anthracene oil is a mixture of hundreds of different compounds with a boiling range of roughly 500" to 750°F at atmospheric pressure. The coal macro-molecule is broken down by thermal decomposition and solvent action into myriads of different compounds, some the same as those comprising the solvent. This similarity in structures opens up the possibility of production and subsequent recovery of solvent. Some solvent is inevitably lost by reaction. Regeneration of solvent was not a problem in the early German Pott-Broche plant. The coal refinery was an integral part of a petroleum refinery complex and replacement solvent was readily available. A coal refinery using lignite, however, might be isolated from other hydrocarbon processing facilities and the regenerability of solvent could be vital to the economic success of the venture. Several structural features of the solvent molecules have been cited as important to the coal solution process.&apos;. The first of these is aromaticity of the material, the second, ability to transfer hydrogen to another molecule, as for example the ability of tetralin to transfer hydrogen and be converted to naphthalene. Finally, the presence of hydroxyl groups on aromatic rings within the molecule, i.e., phenolic character, seems beneficial. Mixtures of pure compounds have been tried by various investigators. Mixtures of o-cresol, a phenolic substance, and tetralin were found to dissolve bituminous coal better than either substance alone.3 This maximum solubility was not found with lignite." Hydrogen contributes to the reaction by hydro-genolysis and by combining with free radicals and molecular "loose ends" to stabilize the compounds formed in coal depolymerization. High boiling point, and correspondingly high molecular weight, seems to be a property which improves solution potential for coal with a given type of compound.&apos; The maceral components of the coal appear to have an important bearing on its ease of solution. The fusain portion is quite inert to solvent action, but the an-thraxylon material dissolves quite readily.3 The hydrogenation reaction can be improved by the use of a catalyst; commercial hydrogenation catalysts having been found effective. Although cost is involved in the use of catalyst and catalyst recovery, the resulting saving in time and perhaps lowered temperature or pressure might justify their use in the solution refining process and decrease the total process costs. Apparatus and Procedure The coal solution runs were made in a 1-gal stainless steel stirred autoclave. The autoclave was provided with thermocouple wells and a transducer to permit continuous recording of temperature and pressure. The autoclave stirrer was magnetically driven, eliminating the leakage inherent with a rotating pressure seal. For runs in which a catalyst was used, the catalyst in the form of beads was placed in a wire mesh container mounted on the stirrer shaft. A control system programmed the heatup and reaction cycle. The permissible heating rate was 5°F per min because of the need to minimize thermal stress in the autoclave body. The temperature was raised at that rate until the reaction temperature was attained and then the temperature was held constant for the desired length of time. The maximum temperature seldom exceeded the average run temperature by more than 15°F.

Jan 1, 1971

By D. Weinstein

The high temperature mechanical properties of stainless steels after fast neutron irradiation are discussed in the light of effects caused by lattice dattmage and effects caused by helium generated from n,a transmutations. Embrittlement at high temperatures is due to helium accumulation at grain boundaries and to cavity formation and proPagation along grain boundaries. Following from the embrittlement mechanism, it is suggested that when deformation occurs by mechanisms associated with super plasticity, helium ac-curnulation at boundaries should be attenuated and cavities, if formed, should be nonpropagating. As the mean free Path between interphase boundaries of a two-phase Fe-Cr-Ni alloy was decreased, the degree of superplastic deforrnation at 870°C increased, as vneaszired by total elongation and by the expottent m = a log &apos;a/a log &apos;i. This alloy and type 304 stainless steel were cyclotron irradiated in an a-particle beam to a helium concentration of -1 x 10 atom He per atom. The stainless steel specimen was embrittled, but the ductility of irradiated two-phase Fe-Cr-Ni alloys correlated with the values of. m during &apos;defor-malion. The .finest grained, helium-injected specimens that deforrned with highest m values exhibited the largest elongations to ,fracture. These results could be correlated with metallographic observations of cavity behavior: the propensity for intergranular propagation was lessened as the m value increased. It is concluded that superplastic deformation is ef-fectizle in attenuating helium embrittlement at elevated temperatures. One of the principal problems associated with development of fast breeder reactors is application of alloys such that suitable fuel cladding results. Stainless steels and other Fe-Cr-Ni alloys, because of highly acceptable nuclear characteristics, represent the primary materials for this component, and an exhaustive research and development effort is being conducted. The main deficiency of these materials has been a severe loss of ductility at high temperatures after fast neutron irradiation. An extensive body of mechanical property data and microstructural observations has provided an adequate phenomenological description of embrittlement; in conjunction with transmission electron microscopy studies, a reasonably acceptable embrittlement mechanism has been obtained. Following from this mechanism, it is suggested in the present work that ductility would be enhanced if deformation could occur by mechanisms associated with the phenomenon of superplasticity. Experiments to test this hypothesis have been conducted, and the results are presented and discussed in this paper. IRRADIATION EMBRITTLEMENT AT HIGH TEMPERATURE Austenitic stainless steels have been irradiated to accumulated fast neutron fluences of 1020 to 1022 nvt at temperatures between 60" and 600°C. Specimens that have been exposed to these conditions and subsequently tensile tested at temperatures between 600" and about 900°C exhibit approximately 5 pct total elongation to fracture.&apos;-3 For unirradiated specimens receiving a nearly identical thermal exposure, total elongation at these test temperatures is about 45 pct. Examination of irradiated specimens has shown that fracture propagation is entirely intergranular. These phenomenological aspects of irradiation embrittle-ment at elevated temperatures are well known and are not generally disputed. Although the explanation of this phenomenon has been controversial, a mechanism for ernbrittlement has emerged that accounts reasonably well for the observed mechanical behavior. The controversy resulted primarily from an indeterminate role of neutron-in-duced lattice damage, if any, and a presumed, but experimentally unverified, contribution to embrittle-ment from helium generated by n,a transmutations. Recently, Holmes and coworkers4 have conducted experiments that separate these effects, and the results are instructive in formulation of the ernbrittlement mechanism. Holmes el al.4 irradiated type 304 stainless steel in EBR-I1 to a fluence of 1.4 x 1022 nvt (E > 0.18 mev); the irradiation temperature was 538" * 48°C or, in terms of absolute melting point, 0.49 * 0.03 T,. After irradiation, tensile tests were conducted at temperatures of 21" to 870.C, the specimens first being annealed for 30 min at each test temperature. In addition, thin sections of irradiated specimens were annealed for 1 hr at identical temperatures, electro and examined by transmission electron microscopy. Thus, for a given temperature, it was possible to correlate mechanical properties with the defect structure. At room temperature, the yield stress of irradiated specimens was a factor of 2.5 higher than unirradi-ated specimens exposed to an equivalent thermal history. Electron microscopic examination of the irradiated specimen revealed a high density of lattice damage in the form of Frank sessile dislocation loops and polyhedral voids. Holmes et al.4 concluded that the presence of this defect substructure caused the increase in yield stress and that after irradiation in a fast neutron flux at 0.49 Tm, substantial lattice dam-age persists. Annealing at progressively higher tem-

Jan 1, 1970

By C. M. Means

Considering the hazard involved in mining operations, statistics show that a very small percentage of accidents is chargeable to electricity. These accidents do represent quite a large percentage of those that are preventable and they are the direct result of the introduction, for purely economical reasons, of a dangerous element. The introduction of electricity in mines should decrease the hazard, and in no case should electricity be applied to the mechanical operation of equipment if by so doing the dangers incidental to mining are increased. The greater number of accidents are the result of persons coming in contact with exposed conductors at potentials varying from 258 to 508 volts direct current. The use of alternating current at higher potentials than these is quite common in large mines, but it is very rare that an accident happens from this source. This is explained by the fact that where these high voltages are warranted, proper precautions are taken, and the installations are directed by those who fully appreciate the dangers incidental to the work. Direct current is in much more general use than alternating current because of its adaptability to haulage locomotives and the low cost of installation in small operations. We are, however, coming to a more extended application of alternating current for the operation of mechanical devices used in connection with mining. Our underground direct-current wiring system is an evolution from the surface trolley and feeder systems. This is probably due to the fact that our earlier successful applications were electric locomotives, which required the use of a trolley wire. The trolley current has been almost banished from industrial establishments on the surface because of the hazard involved, yet we use it indiscriminately underground, where the dangers from accidental contact or fire are infinitely greater., This does not mean that the underground trolley systems should be eliminated, but it does imply the proper safeguarding of such equipment as is necessarily a part of the trolley systems. It is a fact that the men now employed in the installation and maintenance of mining equipment may be in many cases incompetent or not thoroughly familiar with the work, but they are the men who must do the work and, in order to do it properly, it is necessary that they be educated

Jan 1, 1915

By B. A. Cheadle, K. P. Steward

Axial tensile, ring tensile, closed end burst, and free end burst tests were done at room tempe.vature and 300°C on three batches of Zircaloy-2 sheathing zuith different textures. Knoop hardness tests were also done on all batches. The mechanical properties of the tubes were largely dependent on the percentages of cold work, but were also markedly affected by the textures, particularly with respect to deformation behavio&apos;r. The deformation behavior observed confirmed Picklesimer&apos;s predictions, zuhereas Knoop hardness results could be correlated with texture and yield strength anisotropy after the ,method of Wheeler and Ireland. From the mechanical properties, and from efjectiue strain values deterrlzined at the fractures using a photoqid technique, it zuas concluded that tubing witlz a single preferred orientation of radial basal poles best combines strength and ductility for any given deqee of cold work. THE mechanical properties required in collapsible Zircaloy-2 fuel sheathing for water-cooled power reactors are strength to resist wrinkling deformation by coolant pressure and ductility to accommodate a small amount of deformation in service without rupturing. Zircaloy-2 tubing during fabrication develops pre- ferred orientations of the a Zr grains due to aniso-tropic deformation behavior, and these textures markedly affect mechanical properties. Picklesimer&apos; had predicted the deformation behavior of tubes with various textures, but the texture required to provide the optimum strength and ductility for a given degree of cold work has not been reported. To investigate this problem, tests at three transverse to axial stress ratios were done at room temperature and 300°C on three batches of Zircaloy-2 tubing covering a wide range of textures and percentages of residual cold work. Knoop hardness values were also measured to correlate with preferred orientation and yield strength anisotropy after the method of Wheeler and relland.&apos; 1) MATERIAL For this investigation, three batches of tube-reduced tubing were chosen from the Zircaloy-2 sheathing produced for the Douglas Point Reactor. Individual tubes were 191/2 in. long, 0.600 in. OD, and 0.0165 in. nominal wall thickness. The identities of the batches, together with their textures, are shown in Table I. The tubes had the normal Zircaloy-2 composition3 of 1.5 wt pct Sn, 0.3 wt pct Fe, Ni, Cr combined with the following oxygen concentrations: Batch VII 1140 to 1390 ppm 0 Batch VIII 1400 to 1750 ppm 0 Batch IX 880 to 1320 ppm 0

Jan 1, 1968

By E. H. Crabtree

Research on the iron ranges begins to bear fruit in big plant construction -Big coppers raise capacity, build at new Arizona, Michigan, Nevada, properties - Hydrometallurgy comes to fore with new uranium ore treatment and the Chemico process for nonferrous metals -

Jan 2, 1953

By W. O. Philbrook, K. M. Goldman, G. Derge

THIS is the third in a series of papers from the Metals Research Laboratory dealing with the transfer of sulphur across the iron-slag interface in a carbon-saturated system. The first paper&apos; showed that the transfer obeyed first-order kinetics. The second&apos; presented detailed evidence in support of the three-stage mechanism: FeS(Fe) FeS(slag) FeS(slag) + CaO(sing) ? CaS(slag) + FeO(slag) FeO(slag) + C ? Fe + CO. This emphasized the role of an iron-sulphur complex as the transfer agent across the interface and as an essential intermediate in the overall process. The present paper shows the influence on the process of the individual elements, carbon, silicon, manganese, and phosphorus, the alloying elements normally present and of interest in commercial blast furnace operations, aluminum, which has a pronounced accelerating influence, and nickel and copper, which are common minor impurities in the raw materials. The experimental methods and procedures for interpretation of data are the same as described earlier.1,2 Induction heated, graphite crucibles were used, and sulphur-free slag was added to the molten iron containing sulphur and the selected alloy. Slag samples were taken at regular time intervals and analyzed for sulphur and other components of interest. The authors wish to state specifically that these experiments were not intended to simulate industrial blast furnace operations. However, they do represent a study of the kinetics and mechanism of sulphur transfer at the slag-metal interface under specified laboratory control of the major variables in the system. It is believed that the results can be usefully applied to the blast furnace if consideration is given to the differences which are known to exist between the two conditions. A rigorous evaluation of the accuracy of rate studies is difficult. Recognized sources of error include sampling and analysis of both slag and metal, temperature measurement and control, selection of zero time, composition of the gaseous atmosphere over the reaction system, and extraneous sources of sulphur from the graphite crucible and reagent materials. In this study carefully standardized procedures were followed consistently in order to minimize the errors. It is believed that the reproducibil-ity of duplicate runs indicates that errors have been rendered negligible relative to the observed effects from intentional variables. For example, original experimental points for duplicate runs are shown in Figs. 1, 2, 7, etc. In most cases in this paper the drawn curves represent an average of at least two heats. The spread in sulphur values at a given time ranges from 0.02 to 0.08 pct, which is a small frac-tioi of the total values ranging up to 2 pct S in slag. In the systematic study of the influence of alloy additions, each element was added over a range of concentrations. The two slags used in this study were designated as "acid" or 1530 and "basic" or 1545. They had the nominal compositions given in Table I. Rates were measured in the temperature range 1500" to 1650°C. Data will now be presented to illustrate the various features of the study. Silicon The first alloying element examined was silicon, because its presence is unavoidable in any silicate slag system through the reaction y/2SiO2(slag) + xM?y/2Si(liq.Fe) + MxOy where M is any reducing agent such as iron or carbon. It is known that the attainment of equilibrium by this reaction is extremely slow and probably not reached in the blast furnace." The influence of silicon on the final stages of the sulphur reaction has also been studied.&apos; It has been shown5 hat silicon increases the activity of sulphur in iron. For such reasons silicon may also be expected to influence the kinetics of the reaction. The observed effects will now be described. The general procedure was to melt 530 grams of ingot iron in a graphite crucible, 3 in. OD, 2 1/4 in.

Jan 1, 1955

By H. M. Strong

Nickel and carbon form a metastable nickel-nickel carbide eutectic system which was ohsen)able by freezing latent-heat arvests at pressures 210 khars. The eutectic freezing temperature Is pressure had a slope of -0.9°Cper kbar. At 50 khars, the nickel-nickel carbide eutectic was at 1297° * 5°C and 0.34 mole fraction Ni3C. The composition of the eutectic increased at an initial rate of 0.004 mol fraction per kbar. The carbon content of the a phase also increased with pressure. Seveval illustrations of nickel carbide microstruc-tures are given and data on the lattice expansion of nickel in terms of carbon content are included. IRON, cobalt, and nickel form a variety of carbides with compositions varying between MeC and MC. Of the three, the carbides of iron are most easily recovered. The nickel carbides are so unstable at temperatures above 900°C that their occurrence in Ni-C alloys is unusual. Under sufficient pressure, however, the temperature range for the stability of the ferrous metal carbides is likely to be increased, or their decomposition suppressed (e.g., see Hilliard&apos; on FesC), providing an opportunity to study the unstable carbides more closely. This was found to be true for nickel carbide which, under pressure, formed a eutectic with nickel. This paper describes the conditions of formation of nickel-nickel carbide eutectic compositions and their subsequent recovery. Despite the comparative instability of the nickel carbides, something is already known about them through various chemical reactions at temperatures not exceeding a few hundred degrees, and from their recovery by the very rapid quenching of molten Ni-C alloys from temperatures of about 1450°C or above. At least four carbides of nickel have been reported: A discussion of the state of knowledge about Ni3C is given by ansen.&apos; The studies of Morrogh and williams7 who obtained Widmanstatten nickel carbide structures and of sidorenko8 who first obtained nickel carbide eutectic structures are also of interest. Sidorenko used short heating times for molten nickel in a graphite crucible followed by very rapid quenching to obtain the eutectic structures. Long heating times produced only the nickel-graphite eutectic probably due to the presence of graphite crystals in the melt which nucleated graphite crystallization. According to the early work summarized by anssen,&apos; nickel carbide may form at temperatures far above the melting point and may be recovered by very rapid quenching. More recently, Giardini and Tydings, working on diamond synthesis, found evidence for "free nickel carbide&apos;&apos; in high-pressure reactions carried to temperatures far in excess of the limit for diamond growth, followed by rapid thermal quench. They stated that nickel carbide was not found in association with diamond growth. In the present work, observations were made on the melting and solidification temperatures of Ni-C alloys as a function of composition, temperature, and pressure. The nickel-nickel carbide eutectic was found at pressures above 10 kbar and its variation with pressure followed up to 60 kbar. Nickel-nickel carbide microstructures were recovered by quenching under pressure from temperatures of about 1400°C and higher. The formation of nickel carbide structures under ordinary diamond-growing conditions was usually observed but the role of carbide formation as an intermediate step in diamond growth needs more study. EXPERIMENTAL METHODS The melting and solidification temperatures of various nickel-graphite compositions were observed by latent-heat arrests in the sample holder illustrated in Fig. 1. The samples were composed of mixtures of carbonyl nickel powder and National Carbon Co.&apos;s SP-1 graphite packed to densities of about 6.4 g per cu cm. They were contained within

Jan 1, 1965

By L. W. Reynolds, R. F. Campbell, K. G. Carroll, S. H. Ballard

Based on metallographic and X-ray data probable equilibrium conditions from 1340" to 2400°F are presented for the composition range investigated. These are correlated with investigations of Takei and Kuo. Provision is made for existence of Mo, C and (Fe, Mo)2,C, carbides heretofore omitted in diagrams in this composition range. These carbides and (Fe, Mo),C, in equilibrium with ferrite and austenite, restrict the austenite and austenite + ferrite fields to lower carbon contents and higher temperatures than in the Fe-C system. OK groups of steel of different molybdenum content, but with approximately the same carbon variation in each group, Table I, were studied. The alloys were melted in an acid-lined 30-lb high-frequency induction furnace, and the ingots forged to l-in. rounds, which were then ground to 0.75-in. diam. To minimize chemical segregations a short length of each bar was given a high-temperature heat treatment as listed in Table I. Specimens 0.062 to 0.125-in. thick were thereafter cut from the homogenized bars for heat treatment to determine phase changes in the alloy. Heat treatments were performed in either a lead bath or muffle-type electric furnace, depending upon the temperature required. Maximum temperature variation was * 2" F in the lead bath and * 5"F up to 1900°F and +8"F above 1900°F in the electric furnace. Adequate protection of the specimen from the oxidizing atmosphere in the electric furnace was obtained by sealing the specimen in either a pyrex or a silica capsule which was evacuated or not as circumstances required. For austenitizing followed by quenching to an isothermal temperature, the specimen was placed in a closed-end refractory tube the mouth of which, extending beyond the furnace, was connected to a vacuum pump. The specimen could be withdrawn from this tube and quenched as desired. IDENTIFICATION OF PHASES The principal method of identification of phases was metallographic examination conducted on surfaces well removed from exposure to lead or atmosphere effects during heat treatment. Hardness measurements (Dph/lOkg) were also made on these surfaces. The etching reagents used and their effects are listed in Table II. Martensite and ferrite were readily recognized by their customary appearance after etching with saturated picral or 1 pct nital. The presence of liquid at high temperature was indicated by curved interfaces characteristic of boundaries between solid and melt, by intergranular pools of dendritic areas in a carbide matrix, and by a black network coincident with austenite grain boundaries. Examples of these structures are shown in Figs. l(a) and (0). The types of carbide which were attacked by the electrolytic chromic acid etch and the alkaline KMnO, etch, Table 11, were identified by X-ray analyses of extracted carbides of five alloys. Carbide residue was obtained from a metallographic specimen by etching the specimen for 24 hr in hydrochloric-picric acid in alcohol (grain-size reagent), after which the carbides, standing in relief, were scraped from the surface of the specimen and mounted on a glass slide. Diffraction patterns were obtained with a Philips spectrometer using iron-filtered cobalt radiation. Figs. 2, 3, 4, and 5 illustrate typical etching behaviors with chromic acid and alkaline KMnO,. Chromic acid attacked Mo,C as shown in Figs. 2(a) and (b)-but not (Fe, Mo),C, Fig. 3(b). Alkaline KMnO, attacked (Fe, Mo),C, Fig. 3(c), and also attacked M0,C. In accordance with these behaviors, a typical differentiation of coexisting Mo,C and (Fe, Mo),~ is shown in Figs. 4(a) and (b). The carbide (Fe, Mo),,C, could not be obtained free of other coexisting carbides for etching experiments. The behavior. however. of coexisting carbides identified by x-ray diffraction as Mo,C ind (Fe, Mo),,C, indicate that (Fe, Mo)23C6 is not etched by chromic

Jan 1, 1961

By M. E. Wadsworth, I. B. Cutler, R. W. Bartlett

The oxidation kinetics of ZrC was studied between 450" and 580°C in oxygen pressures from 6.5 x 10-to 1 atm using a ther mogravimetric apparatus and sized powder samples. Two parallel rate controlling processes were observed. A surface reaction occurring at the ZrC-ZrO2 phase boundary accounted for most of the oxidation and had an activation enthalpy of 46 kcal per mole. The other process, believed to be diffusion of oxygen into the ZrC lattice partially replacing carbon, had an activation enthalpy of 53 kcal per mole. The enthalpy for chemisorption of O2 on ZrC was determined to be —13 kcal per mole. Water vapor in the presence of oxygen accelerated the surface reaction rate. THERE has been little reporting of formal rate studies or attempts to ascertain the mechanism of oxidation of carbides. MacDonald and Ransley1 studied the oxidation of titanium carbide which has the same structure as zirconium carbide, fcc. They observed an initial increase in rate with increasing temperature followed by a rapid decrease through a rate minimum and a subsequent second increase at higher temperatures. The discontinuity in the rate rise was attributed to a phase change in the oxide which changed the rate determining step from the surface reaction at the carbide-oxide interface to diffusion through the oxide layer. Samsonov and Golybera 2 studied titanium carbide and reported that during the initial period of oxidation a dense film of Tic-TiO was formed followed by the formation of less adhering layers of higher oxides. The purpose of this investigation was to study the kinetics of oxidation of zirconium carbide and to attempt to gain some knowledge of the mechanism by which oxidation occurs. EXPERIMENTAL PROCEDURE Measurement of the weight gain associated with the oxidation of ZrC was used to determine oxidation rates. The principal experimental parameters were surface area, temperature, and oxygen pressure. Although moderately sized crystals of ZrC can be grown by the Van Arkel method, the only commercially available ZrC is a powder. In using powders, the surface area must be controlled either by fabricating the powder into a sintered pellet with a measurable surface area, relatively fixed during oxidation, or by using sized unconsolidated powder and applying appropriate geometric considerations to the shape of the grains to correct for their diminishing surface areas as they oxidize. Both techniques involve some difficulties. pellets of binder-free zirconium carbide can be made by hot pressing, but it is difficult to obtain densities greater than 90 pct of

Jan 1, 1963

By Harold M. Feder, Irving Johnson

Tkermodynamic functions for dilute solutions of uranium in liquid cadmium were obtained from galvanic cell measurements. Deviations from Henvy&apos;s law were observed at concentvations down to 2 x 10-3 atom fraction. Unusually large negative values of the pavtial molal relative enthalpy and excess entvopy of uranium, suggestive of the occu,vvenctwe of partial ovdering of cadmium around uranium in these solutions, were found. The negative relative partial molal enthalpy of uranium at the liquidus accounts for the observed retrogvade solubility of metallic uranium between 473" and about 630°C. The standard free enevgy of formation of UCd,, from a-uranium and liquid cadmium is given by F,° THE constitutional diagram of the U-Cd system,&apos; Fig. 1, is unusual in several respects. The near equality of the Goldschmidt atomic radii2 (Cd, 1.52A U, 1.56A) might be expected to give rise to extensive mutual solubility of the elements except for the restrictions imposed by differences in valence and electronegativity.3 The latter factors must be strongly influential because mutual solubilities in the terminal solid phases are probably negligible, and the solubility of uranium in liquid cadmium in the readily accessible range is only about 1 at. pct. Interestingly, the solubility of uranium in liquid cadmium actually decveases slightly with increasing temperature from 473" to about 630°C. Such a retrograde solubility in a liquid phase is a rare phenomenon in metallic systems; no other authenticated examples were found among the nearly 700 binary phase diagrams compiled by Hansen and Anderko.2 These observations suggested the existence of some unusual interaction between uranium and cadmium. Greater insight into the nature of this interaction was sought by measurement of the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE The emf of cells denoted by the scheme was measured. Each cell consisted of two uranium and two alloy electrodes immersed in a molten lithium chloride-potassium chloride eutectic mixture containing uranium trichloride. The physical arrangement is shown in Fig. 2. The potential between any pair of electrodes could be measured with a Leeds and Northrup Type K-3 potentiometer. The measurements were made at points marked in Fig. 1. It should be noted that points on the phase boundaries represent the concentrations of uranium in the saturated liquid phases of heterogeneous alloys. Uranium Electrodes. Uranium, which is not a particularly soft metal, is capable of retaining residual stresses, and its potential may depend upon its physical condition. Electrodes were prepared from 3-mm diam rods of hot-rolled high-purity4

Jan 1, 1962

By F. W. McQuiston

Idarado Mining Company&apos;s mill and surface plant are at the portal of the Treasury tunnel at elevation 10,625 ft, 12 miles south of Ouray, Colo. In 1943 and 1944 this tunnel was extended in a westerly direction to tap the Black Bear vein, and, together with the recently completed 1100-ft inclined Treasury raise, provides access to the Black Bear mine. In 1945 a 250-ton mill was placed in operation to process development ores containing much needed copper, lead and zinc for war requirements, and to serve as a pilot testing unit for larger scale milling operations. In the years 1902 to 1927 some 329,000 tons of ore were produced from mine workings on the Black Bear vein that extended downward from elevation I2,325 ft at the Black Bear tunnel portal to elevation 11,618 ft, the lowest level of the mine. The ores were taken to the Cascade and Smuggler-Union mills near Telluride over two aerial tramways. Gold bullion, a copper-lead concentrate, and a zinc concentrate were produced. Ores The Black Bear is a compound fissure vein that has undergone several stages of mineralization. The first important stage is represented by complex ores of copper. lead and zinc in a quartz gangue. Precious metal content in this stage is low. The galenn is argentiferous and varying amounts of tetrahedrite, freibergite and bornite tend to increase the normal copper content represented in chalcopyrite. The zinc occurs as a true sphalerite with little or no iron. Later re-openings of the fissure took place more or less co-extensively with the successive introduction of (I) abundant quartz gangue containing minor amounts of chalcopyrite, galena and sphalerite; (2) free gold in a fluoritic quartz gangue; and (3) barren, low-grade quartz with minor amounts of pyrite as the only important sulphide. The sulphides show practically no oxidation and little mineralogic inter-growth. Because of the common overlapping of these successive stages of mineralization within a given mining area, considerable dilution of the base-metal content takes place, thus lowering the average mill-head grade. Plant Practice Metallurgical testing was started shortly after the Black Bear vein was encountered on Treasury tunnel level in 1944. Laboratory tests showed good flotability of the minerals in the ore and indicated an economic separation could be made of the copper, lead and zinc minerals into their respective concentrates. The success of the separation is close reagent control to maintain a balance between promotion and depression of the sulphides. To maintain this balance reagent consumption for the three metal separation is considerably higher than in ordinary lead-zinc flotation.

Jan 1, 1949

By A. C. Watts

For several years, a mine in Colorado experienced considerable trouble from small fires caused by the blasting of coal. Although a well-known make of permissible powder was used, it was first thought that the powder ignited gas that might be present and that this, in turn, set fire to line brattices or to the coal. Experiments were, therefore, conducted with another make of powder, but the results convinced the superintendent of the mine, Robt. Williams, Jr., that the fires were not caused by the powder but by the high-voltage electric current used for detonating the shots. The mine "makes" gas very freely, giving off from three-fourths to one million cubic feet of methane every 24 hours. The coal is a good grade bituminous of a very free burning quality. Electric shot-firing from the outside, after all men and animals were outside, had been practiced for a number of years. The shooting circuit was connected with the main power circuit at the mouth of each entry. Shooting circuit switches were mounted in boxes, which were kept locked with the handle of the switch, in open position, showing through the bottom of the box. The door of the box could not be shut and locked when the shooting switch was closed. At the entrance to each room, or working place, a small switch, called the miner&apos;s switch, was placed on the shooting line. It was the duty of the miner, when entering his place at the beginning of the shift, to see that this switch was open and that it was kept open until he left the placc at the end of the shift to go out of the mine. Grounded return was used for main power lines. The current was 500 volts, direct current, with 100 to 300 amp. The nearest working face was 9600 ft, from the shot-firers&apos; switch outside the mine and the most remote working face was 2½ miles. The various working faces were scattered over a wide area between these two points. A description of the main power line would be valueless; the conductors were of sufficient size, the drop in voltage being not more than

Jan 1, 1927

By W. Rostoker, R. F. Domagala, R. P. Elliott

The phase equilibria of the Hg-Th system over the composition range 0-100 pct Th and temperatures up to 1000°C have been studied for a small-volume, closed system. The solubility of Th in liquid Hg is about 5 pct at 300°C and decreases sharply with decreasing temperature. Two intermediate phases occur, Hg3 Th and HgTh. The structures of these are hexagonal (nonideally close-packed) and face-centered cubic, respectively. The HgTh phase decomposes eutectoidally at 400°-500°C. The solubility of Hg in solid thorium seems to be negligible. AFULL-phase diagram for this system would have to be defined on temperature-composition-pressure co-ordinates. This paper describes the pseudo phase diagram of a closed system, that is, where the alloy enclosed in a small volume equilibrates with a vapor pressure of mercury dictated by composition and temperature. Because of the experimental difficulties in studying a system of this nature, many of the phase relations can only be sketched. Alloy Preparation Alloys over the full range of composition were made from triple distilled mercury and one of two grades of thorium. For the bulk of the work, a calcium-reduced metal in sintered pellet form of reported 99+ pct total thorium content was used. Arc-melted specimens of this thorium gave a hardness of 135 VPN. The microstructure showed small primary dendrites of ThO2. A number of alloy compositions were made with a high-purity, iodide-decomposition thorium metal. The are-melted hardness of a button of this material was 35 VPN. Although the microstructure of the arc-melted specimens showed no dendrites of ThO2, there was definite evidence of an unidentified phase enveloping the grain bound-aries. There were no distinguishable differences between the constitution of alloys made with the two grades of thorium metal. Under normal conditions thorium is not wetted by liquid mercury. The film of ThO2 on all thorium metal cannot be penetrated by either liquid or vaporous mercury. It was therefore necessary to comminute thorium in the presence of mercury under such conditions that oxide films could not reform on the newly exposed metal surfaces. This was accomplished by the use of a high-speed, carbide-tipped rotary cutter incorporated in a chamber purged with argon and connected at the bottom to a demountable Vycor bulb containing a weighed amount of mercury. This experimental device is fully described in a separate paper.1 Alloy compositions were calculated by weighing the empty bulb, the bulb containing the mercury, and the bulb containing the mercury and the thorium chips. Many alloys were analyzed chemically for thorium and/or mercury after subsequent homogenization; the agreement between analyzed and calculated compositions was invariably very close. Bulbs containing the requisite amounts of mercury and fine thorium chips were clamped off, removed to a sealing unit, evacuated and sealed. Amalgamation under these conditions proceeded rapidly even at room temperature. To insure homogeneity, the specimens were annealed to 300-400°C. Alloys containing less than 30 pct Th remained pasty after all treatments, indicating an equilibrium condition of liquid plus solid. Alloys with more than 30 pct Th were transformed into a dark powdery product. These latter specimens were annealed for times of up to 1 week to complete interdiffusion. Many of the alloy compositions are pyrophoric. On exposure to air they oxidize with considerable evolution of heat to a mixture of ThO2 and free mercury. It was mandatory that alloy specimens be handled in a "dry box" purged thoroughly with argon. All X-ray diffraction specimens were powdered, screened, and sealed in capillary tubes within the dry box. Experimental Procedures Thermal analysis experiments, useful only in the mercury-rich region of the system, were conducted with the alloys in their original containers. A reentrant thermocouple well formed an integral part of the bulb. These bulbs were heated in a silicone oil bath and cooled in a dry ice-acetone mixture. The rates of heating and cooling were slowed by immersing the specimen bulb in a larger tube containing silicone oil. This provided a suitable thermal lag. In all tests, pure mercury was run as a basic standard. While the invariant reaction at about the melting point of mercury was detected by thermal analysis, the heat effect at the liquidus was not sufficient to produce an inflection in the cooling curve. It was necessary to determine the liquidus temperatures at the mercury-rich end of the system by "breaks" in electrical reslstivity versus temperature curves for individual alloys. The apparatus for this purpose consisted of a pyrex tube about 2 in. diam and 12 in

Jan 1, 1959

By James Boyd

It is obvious that mining has been influenced to a high degree by political and economic events, many of which are of such a nature that the mining industry has relatively little influence in shaping them. I cannot present too optimistic a picture for the immediate future, although I feel that from the long-range standpoint one need not be pessimistic about the future of the mining industry. The population of the United States is continuing to increase and with it has come an expanded consumption of metals on a per capita basis. With this expansion there has and will continue to come the demand for more goods and in- creased products from our mines and our fabricating plants. World War

Jan 5, 1950

By Neil H. Cole

Cost and price inflation and financial gearing through loans are characteristic of modern resources projects. Conventional discounted cash flow and 1P.R analyses, in real terms, and without financing, have inadequacies which can yield misleading results. The degree of improvement in value for project equity owners is limited to the value of the additional tax benefit accorded through the financing instrument used. Debt financing may be low in price and value, but its priority means that the equity owners assume a higher risk, thereby increasing the cost, or price, of their capital. The cost of equity capital, or investment hurdle rate, is related to the Capital Asset Pricing Model. Distortions do occur, with inflation, due to depreciation effects, which can cause the adoption of misleading project rate of return or hurdle rate criteria. For investment decisions, the greatest accuracy possible in forecasting is essential, especially for inflation rates,

Jan 1, 1985

By Charles E. Lundin

The character of the Er-D system was established by determining pressure-temperature-composition relationships. A Sieuerts&apos; apparatus was employed to make measurements in the temperature range, 473" to 1223"K, the composition range of erbium to ErD3, and the pressure range of 10~s to 760 Torr. The system is characterized by three homogeneous phase regions: the nzetal-rich, the dideuteride, and the trideuteride phases. These phases and their solubility boundaries were deduced from the family of isotherms of the system zchich relate the pressure-temperature-composition variables. The equilibrium plateau decomposition relationships in the two-phase regions were determined from can&apos;t Hoff plots to be: The differential heats of reaction in these two regions are AH = - 53.0 * 0.2 and -20.0 *0.1 kcal per mole of D2, respecticely. The differential entropies of reaction are AS = - 36.3 * 0.2 and - 31.0 * 0.2 cal per mole D2. deg, respectively. Relative partial molal and intepal thermodynamic quantities were calculated from the pure metal to the dideuteride phase. The study of the Er-D system was undertaken as a logical complement to an earlier study of the Er-H system.&apos; The primary interest was to compare the characteristics of the two systems and relate the difference to the isotopic effect. Studies of rare earth-deuterium systems by other investigators have been very limited in number and scope. Furthermore, there is even less information available wherein an investigator has systematically compared a binary rare earth-hydrogen system with the corresponding rare earth-deuterium system. The available information consists primarily of dissociation pressure measurements in the plateau pressure region of a few rare earths. Warf and Korst&apos; determined dissociation pressure relationships for the La- and Ce-D systems in the plateau region and several isotherms for each system in the dideuteride region. They compared these data with those of the corresponding hydrided systems. The study of these systems as a whole was very cursory and did not give sufficient data for a thorough comparison of the effect of the hydrogen vs the deuterium in the respective rare earths. The heat capacities and related thermodynamic functions of the intermediate phases, YH, and YD2, were determined by Flotow, Osborne, and Otto,~ and the investigation was again repeated for YH3 and YD3 by Flotow, Osborne, Otto, and Abraham.4 This investigation studied only these specific phases. Jones, Southall, and Goodhead5 surveyed the hydrides and deu-terides of a series of rare earths for thermal stability including erbium. They experimentally determined isotherms of selected hydrides and plateau dissociation pressures for deuterides. These data allowed comparison of the enthalpy and entropies of formation of the dihydrides and dideuterides. To date, no one rare earth has been selected to thoroughly establish the complete pressure-temperature-composition (PTC) relationships of binary solute additions of hydrogen and deuterium, respectively. The objective in this investigation was to provide the first comparison of a complete family of isotherms of a rare earth-deuterium system with those of a rare earth-hydrogen system. This would allow one to determine what differences exist, if any, in the various phase boundaries and the thermodynamic relationships in various regions of the systems. I) EXPERIMENTAL PROCEDURE A Sieverts&apos; apparatus was employed to conduct the experimental measurements. Briefly, it consisted of a source of pure deuterium, a precision gas-measuring buret, a heated reaction chamber, a mercury manometer, and two McLeod gages (a CVC, GMl00A and a CVC, GM110). Pure deuterium was obtained by passing deuterium through a heated Pd-Ag thimble. A 100-ml precision gas buret graduated to 0.1-ml divisions was used to measure and admit deuterium to the reaction chamber. The reaction unit consisted of a quartz tube surrounded by a nichrome-wound furnace. The furnace temperature was controlled by a recorder-controller to . An independent measurement of the sample temperature in the quartz tube was made by means of a chromel-alumel thermocouple situated outside, but adjacent to, the quartz tube near the specimen. Pressure in the manometer range was measured to k0.5 Torr and in the McLeod range (10~4 to 10 Torr) to *3 pct. The deuterium compositions in erbium were calculated in terms of deuterium-to-erbium atomic ratio. These compositions were estimated to be *0.01 D/Er ratio. The erbium metal was obtained from the Lunex Co. in the form of sponge. The metal was nuclear grade with a purity of 99.9+ pct. The oxygen content was reported to be 340 ppm and the nitrogen not detectable. Metallographically the structure was almost free of second phase (<i vol pct). A quantity of sponge was arc-melted for use as charge material. The solid material was compared with the sponge in the PTC relationships. They were found to be identical. Therefore, sponge material was used henceforth, so that equilibrium could be attained more rapidly. The specimen size was about 0.2 gr for each loading of the reaction chamber. The procedure employed to obtain the PTC data was to develop experimentally a family of isothermal curves of composition vs pressure. First, a specimen

Jan 1, 1969

By M. C. Udy, P. C. Rosenthal

The use of minute boron additions to steel has been given considerable attention in recent years. Comparisons made between boron-free and boron-containing heats of otherwise identical analysis have indicated, beyond a doubt, the potent effect of boron for increasing hardenability. The actual hardenability increase has been expressed as a multiplying factor, or in terms of the percentage of other alloying elements boron might replace. The present study presents the results of a systematic survey of the use of boron as an addition to two types of alloyed steels and as a replacement for various percentages of molybdenum in these steels. Both cast and wrought steels of the two basic compositions were prepared. Molybdenum, because of its scarcity at the time the investigation was started, was selected as the element to be replaced by boron. Attention was also given to the effects of boron on other properties of the steels, particularly their notched-bar toughness, to investigate other advantages or limitations of this element as an alloy addition. Experimental Work Steels Investigated The two basic compositions used in this survey of boron as a replacement for molybdenum are given in Table I. The cast steels were higher than the wrought steels in silicon content to improve the casting quality. Table i.—Nominal Composition of the Two Base Alloy Steels composition. Per Cent. steel Mn Si Ni Cr Xi-Cr-Mo Wrought 0.28-0.70-0.15-o.45—o.45-0.32 0.90 0.25 0.55 0.55 Cast 0.28-0.70-0.35-0.45-o.45- 0.32 0.90 0.45 0.55 0.55 hln-&lo Wrought 0.28-I .go-o.0.15-0.32 1.70 0.15 Cast o. 28- I.40- 0.35- 0.31 1.70 0.45 a Sulphur was 0.040 per cent maximum and phosphorus 0.030 per cent maximum. Each of these base steels, both cast and wrought, was made with molybdenum contents of o, 0.10, 0.20, 0.30, or 0.40 per cent, the total comprising 20 steels. In addition, each of these 20 compositions was prepared with boron additions in amounts of o.oo15, 0.003, and 0.006 per cent as ferroboron; and in amounts of 0.002 and 0.005 per cent as two commercial intensifier alloys, designated alloys A and B. The boron-treated steels totaled 100, and the entire series 120. Test Procedure Each steel was melted as an individual heat in a 50-lb., magnesia-lined induction furnace. Ingot iron scrap or mixtures of ingot iron and steel. scrap were used for melting stock. Deoxidation was carried out in the furnace with 0.10 per cent aluminum. The aluminum addition was

Jan 1, 1948

By M. C. Udy, P. C. Rosenthal

The use of minute boron additions to steel has been given considerable attention in recent years. Comparisons made between boron-free and boron-containing heats of otherwise identical analysis have indicated, beyond a doubt, the potent effect of boron for increasing hardenability. The actual hardenability increase has been expressed as a multiplying factor, or in terms of the percentage of other alloying elements boron might replace. The present study presents the results of a systematic survey of the use of boron as an addition to two types of alloyed steels and as a replacement for various percentages of molybdenum in these steels. Both cast and wrought steels of the two basic compositions were prepared. Molybdenum, because of its scarcity at the time the investigation was started, was selected as the element to be replaced by boron. Attention was also given to the effects of boron on other properties of the steels, particularly their notched-bar toughness, to investigate other advantages or limitations of this element as an alloy addition. Experimental Work Steels Investigated The two basic compositions used in this survey of boron as a replacement for molybdenum are given in Table I. The cast steels were higher than the wrought steels in silicon content to improve the casting quality. Table i.—Nominal Composition of the Two Base Alloy Steels composition. Per Cent. steel Mn Si Ni Cr Xi-Cr-Mo Wrought 0.28-0.70-0.15-o.45—o.45-0.32 0.90 0.25 0.55 0.55 Cast 0.28-0.70-0.35-0.45-o.45- 0.32 0.90 0.45 0.55 0.55 hln-&lo Wrought 0.28-I .go-o.0.15-0.32 1.70 0.15 Cast o. 28- I.40- 0.35- 0.31 1.70 0.45 a Sulphur was 0.040 per cent maximum and phosphorus 0.030 per cent maximum. Each of these base steels, both cast and wrought, was made with molybdenum contents of o, 0.10, 0.20, 0.30, or 0.40 per cent, the total comprising 20 steels. In addition, each of these 20 compositions was prepared with boron additions in amounts of o.oo15, 0.003, and 0.006 per cent as ferroboron; and in amounts of 0.002 and 0.005 per cent as two commercial intensifier alloys, designated alloys A and B. The boron-treated steels totaled 100, and the entire series 120. Test Procedure Each steel was melted as an individual heat in a 50-lb., magnesia-lined induction furnace. Ingot iron scrap or mixtures of ingot iron and steel. scrap were used for melting stock. Deoxidation was carried out in the furnace with 0.10 per cent aluminum. The aluminum addition was

Jan 1, 1948