By W. F. Chiao, R. B. Gordon

Tile sharp-yield point found in magnesium crystals in the solulion-treated and aged condition is studied by dislocation internal-friction experiments. The results show that the sharp yield is not file to the sudden release of pinned dislocations hut is movc likely due to the rapid multiplication of an initially small number of dislocations. Recovery or the dislocation internal friction after deformation is also studied. This yecovery results from the re-pinning of dislocations by a solute, presumably nitrogen, which moves with a relatively small activation energy. SHARP-yield points, when they occur, are a striking feature of the stress-strain curve generated during a tensile test. Although commonly associated with steel, sharp yielding has been found in a variety of metallic and nonmetallic crystalline materials. In particular, sharp-yield points have been found in zinc"' and cadmium3 containing nitrogen. With this background, Geiselman and Guy4 investigated the tensile properties of magnesium single crystals containing nitrogen to see if sharp yielding also occurs in this system. They found that sharp yields did indeed occur in solution-treated and aged specimens tested at elevated temperature but were not able to give conclusive proof that the sharp yield was caused by nitrogen, a yield drop being observed even in their purest crystals. Sharp-yield points have also been found in various polycrystalline magnesium alloys.7'8 In the study of the sharp-yield phenomenon it is desired to observe the behavior of dislocations in the earliest stages of the deformation process. Internal-friction experiments are useful for this purpose because dislocation damping is sensitive to the mobility of free-dislocation segments. At low strain amplitudes the damping, A, due to the the forced vibration of dislocation segments of average length L is ? =KAL4 [1] where A is the dislocation density and K, if the applied frequency is well below the resonant frequency of the dislocation segments? is a constant for the sample under observation.5 Dislocation damping, because of the fourth-power dependence on L, is particularly sensitive to the creation of free-dislocation segments during deformation. Since sharp yielding is associated with the sudden release of pinned-dislocation segments, marked changes in the dislocation damping are expected at the yield point.6 The use of the dislocation-damping observations to help elucidate the incompletely understood mechanism of yielding in magnesium is the primary objective of the experiments reported here. PROCEDURE Many investigations have shown that very marked and rapid changes occur in the dislocation damping of of a deformed material as soon as the straining is stopped.5 It was quite essential, then, for the purpose of this investigation, to make the damping measurements during the deformation of the samples. This can only be accomplished through the use of the ultrasonic-pulse method. In this method traveling sound-wave pulses are used and, in contrast to resonating-bar methods, only the sample ends are set in vibration. Thus, the sample can be gripped along its sides in the tensile-test machine without disturbing the damping measurements. In the pulse method, the decrease in the amplitude of a sound pulse is measured as it travels back and forth through the sample. If A is the amplitude after traversing a distance x and A. is the initial amplitude, A=Aoe-ax [2] and a is called the attenuation. It is commonly measured either in units of cm-I or as db per µ sec. The observed attenuation in a metal sample is due to a number of causes. These include scattering by grain boundaries and impurity particles, thermo-elastic damping, diffraction effects, stress-induced ordering of solute atoms, and dislocation damping. The total observed attenuation in a given sample usually cannot be resolved into these various components, but changes in a due solely to changes in dislocation damping can be accurately determined, provided the experiment is arranged so that all other sources of damping are held constant. It is desired to reduce the extraneous sources of attenuation to a minimum and for this reason the experiments are done on single crystals of high purity. Magnesium crystals offer the further advantage that, when properly oriented, only a single set of slip planes is active during deformation. Crystal Preparation. The method of sample preparation is similar to that of Geiselman and Guy.4 The starting material was high-purity, sublimed magnesium rod supplied by the Dow Chemical Co. Melting under Dow 310 flux was used to reduce the nitrogen content of the starting material: the fluxing was done under an argon atmosphere and the

Jan 1, 1965

By R. Gibala

Internal-friction measurements on hydrogen-charged iron over the temperature range 4° to 300°K are reported. Two relaxation peaks, the hydrogen Snoek peak at 48 °K and the hydrogen cold-work peak in the range 145" to 2200K, are observed at 80 kc per sec. The effects of hydrogen-charging, aging, and deformation on the internal-friction results are determined and are used to show evidence of partitioning of hydrogen between solid solution and dislocations. The hydrogen-dislocation binding energy is estimated from the behaviors of the relaxation tiwzes and relaxation strengths of the Snoek peak and the cold-work peak. Its value is approxi,mately 6400 cal per mole. MANY investigators have demonstrated the usefulness of internal-friction measurements in determining the manner in which interstitial impurities interact with dislocations in bcc metals. Part of this success has resulted from the existence in bcc interstitial alloys of two anelastic relaxation peaks—the Snoek peak' and the cold-work or Koster peak2 (designated hereafter by SP and CWP, respectively). The SP has its origin in the redistribution of interstitials in solid solution among sites made energetically nonequivalent by an applied stress. The rate at which the redistribution occurs, measured by the relaxation time for the process, is related in a simple way to the diffusion rate of the interstitial in the free solution. The relaxation strength is proportional to the concentration of interstitial in solid solution. The CWP appears to have its origin in the relaxation of an interstitial-dislocation complex for which the relaxation time at a given temperature is much longer than that for the SP. The relaxation strength depends strongly on the concentration of interstitial and the amount of deformation at relatively low concentrations and deformations.2-8 From the dependence of the relaxation strength on interstitial concentration, the SP and CWP may serve as measures of the concentrations of interstitials in free solution and bound at dislocations, respectively. Thus their behaviors have been used to investigate interstitial-dislocation interactions in Fe-C, Fe-N, and several refractory metal systems.'-' However, the Fe-H system has not been studied extensively,? even though disputes in recent years over the mechanism of hydrogen embrittlement in steels involve argument over the extent to which lattice hydrogen and hydrogen-dislocation interactions play an important role.?-'' Previous work on Fe-H indicates the internal-friction behavior to be qualitatively consistent with that for other systems. Apparently, both a SP and a CWP are observed in the temperature ranges 30" to 50°K and 100°to 140°K, respectively (at 1 cps). However, there is neither sufficient nor accurate enough information to identify convincingly these peaks with their supposed counterparts in other systems. Nor have there been any attempts to make quantitative use of these peaks to study hydrogen diffusion, aging, or interaction processes. In this paper, an attempt is made to obtain more complete information on internal friction of hydrogen in iron than presently available. Internal-friction measurements in the range 4° to 300°K on hydrogen-charged iron show that the two peaks discussed above are in fact the hydrogen SP and CWP. Several effects of hydrogen charging, aging, and deformation on these peaks are observed and are used to determine the partitioning of hydrogen between solid solution and dislocation sites in iron. EXPERIMENTAL Materials. The starting material for this investigation was a high-purity iron supplied by National Research Corp. as a 1-in.-diam rod. The following analysis was given (inwt pct): C, 0.004; N, 0.0003; 0, 0.007; P, 0.002; S, 0.005; Si, 0.006; Mn, 0.001; Cu, 0.002; Ni, 0.005; Cr, 0.001; Mo, 0.001. After an initial vacuum anneal (-5 XTorr) at 700°C, the rod was cold-

Jan 1, 1968

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By M. Metzger, T. A. Read

The strengthening effects of hydroxide and synthetic plastic films in the creep of cadmium crystals were studied. The results were broadly consistent with the naive mechanical model. The dislocation-film reactions and the significance of the macroscopic stresses associated with certain films are discussed in the paper. ALTHOUGH a number of studies have been made of the strengthening of metal single crystals produced by surface films usually less than Ir in thickness, the mechanisms underlying this phenomenon are still not well established. Roscoe' first noted the critical shear stress and the stress-strain curve of cadmium-crystal wires to be raised markedly by the presence of oxide films. Subsequent investigators2-' have confirmed the effect for several metals and films including a number of plated poly-crystalline metal films. Harper and Cottrel1" with a thin film on zinc presumed to have formed as a result of etching and washing treatments) did not detect a strengthening at a rate of extension of 10 ' sec-' although at lo-' sec-' the film raised the flow stress by 7 pct at 0.0005 extension and by 22 pct at 0.01. The marked strengthening at moderate strains thus appeared to be the result of a dynamical effect dependent on the rate and amount of plastic flow. Other observations'. " are consistent with this view. The large effects of films on the tensile creep rate of single crystals were demonstrated when the observation of Andrade and Randall," that the creep rate of cadmium crystals increased on immersion in aaueous solutions of certain cadmium salts. was shown' * to hold only when a film was present initially and was explained by the attack of the solution on the film and the removal of its strengthening effect. Changes in the creep rate interpretable in terms of the removal or formation of various films have been observed by other investigators.3,8,10,31 Certain other experiments have been reported in which surface films or liquid environments have affected the plastic behavior of metals, but these are not within the scope of the present work which deals with the effect of solid films on single-crystal slip. Possible Mechanisms—The film does not significantly reduce the load on the crystal in the elastic range (the elastic moduli of film and crystal are not too greatly different and the area of the film is so small that its share of the load is negligible) so that the initial operation of internal Frank-Read sources is not affected. However, as Fisher" has pointed out, a source terminating on the crystal surface requires only half the critical stress for activation as an internal source of the same length and a relatively strong film (even a very thin one) would pin the free ends of the surface sources so that, if surface sources are responsible for plastic flow in a clean crystal. such a film would increase by roughly a factor of 2 the stress necessary for generation of dislocation loops at a given rate. The other general possibility is that the film resists the passage to the crystal surface of internally generated dislocations. If the film is adherent and if the specimen is to exhibit slip of the same general character as a film-free specimen, the film must deform or fail in shear at the active slip planes. The naive mechanical model, where shear-stress relaxation across the active slip plane in the metal transfers load to the film until it deforms and slip can

Jan 1, 1959

By Clyde E. Williams

MODERN steelmaking has gradually evolved from an inefficient small-scale operation, utilizing tiny units, to a highly efficient one utilizing large units almost completely mechanized. The leading position of the United States in the steel industry is due to the possession of easily assembled high-grade raw materials and large-scale highly developed plants. Modern integrated steel operation is largely one of material handling. Mining and transportation of iron ore, coal, and fluxes, coking the coal in by-product ovens, smelting the ore with coke and limestone in blast furnaces, converting the resulting pig iron into steel in the Bessemer, or in the open hearth when supplemented with scrap, and fabricating the resulting steel ingots in the shapes of commerce all are done on a huge scale, mostly by machinery, most of the labor being employed either in operating the machine or keeping it in repair. At the same time the quality and uniformity of the product have been greatly increased by the development of scientific knowledge and operating skills. Thus, the steel industry in this country is highly developed both mechanically and technically.

Jan 1, 1942

By H. A. Bourne, E. L. Haden, D. R. Reichmuth

A circumferential-toothed bit with novel tooth form gave improved penetration performance. In this design the exterior flank of all teeth were vertical when in rolling contact with the hole bottom. Rock chips were generated by the interior flank of the tooth displacing the rock inwardly and downslope toward the center of the hole. A unique two-cone laboratory bit assembly enabled evaluation of numerous cone and tooth configurations. Some of the variables investigated, in addition to weight on bit, rotary speed and rock type, were tooth interference, percent tooth, hole bottom angle, attack angle and relief angle. Most tests were conducted dry on a brittle synthetic sandsone or a ductile quarried limestone. Tooth configurations were found to be more significant in the ductile material. This was attributed to the deeper tooth penetration before rock failure. These studies showed that the attack angle (angle beween interior flank of the tooth and rock surface) was the controlling variable; changing the tooth configuration from the assymetric or semi-wedge to the more conventional symmetric or wedge form reduced penetration performance; and penetration performance of circumferential-type cutters was directly proportional to rotary speeds up to 200 rpm. INTRODUCTION Much of the published literature on rock-chisel interactions describe experiments wherein symmetrical wedges are vertically loaded or impacted against a smooth rock surface.1-6 are is usually taken to insure that the indentation is not made near the edge of the rock specimen less erroneous data be obtained. The literature describes relatively few studies in which the investigator deliberately attempted to take advantage of an edge or free surface. In contrast, anyone who chips ice or breaks up a concrete sidewalk almost always works near an edge. Chisel "indexing," which has been considered by some investigator1,2,6,7 makes limited application of an edge or free surface. Probably the best documented investigation into applying this idea to drilling was that of Drilling Research Inc. at Battelle Memorial Institute.' Their "annular wing" percussion bit consisted of paired asymmetric chisels oriented so as to produce and move chips to the center of the hole. They predicted that the lowest energy requirement for chip generation would be achieved with a stepped hole bottom having a median angle of 45" to the horizontal. Results from limited tests showed that approximately 50 percent of the rock fragments were large and semi-circular in shape, as would be expected by a chisel impact near an edge. The remaining 50 percent were fine chips produced by the chisels in re-establishing the steps or ledges. Initial penetration rates with this bit were high, but they rapidly decreased. This was the result of excessive tooth wear caused by the constant friction on the gauge surfaces. The basic idea — circumferentially placed asymmetric chisels — still appears to have merit. If the concept could be applied to a rolling cutter bit, two of the shortcomings of the fixed chisel design could be overcome: (1) reduction in tooth friction, and (2) greatly increased cutter surface. Adapting asymmetric chisels to cutters rolling on an inclined hole bottom is restricted by bit geometry. The basic elements of roller rock-bit construction prevents the practical attainment of a 45" hole bottom angle. Nonetheless, experimentally it was considered desirable to investigate the influence of hole bottom angle to at least 40". This paper describes the laboratory studies conducted in evaluating the circumferential-toothed roller cutter rock bit. EXPERIMENTAL APPARATUS AND PROCEDURE BIT ASSEMBLY The cost of constructing a sufficient number of conventional three-cone rock bits to investigate circumferential cutter performance was prohibitive. Instead, a novel two-cone laboratory assembly which used an external bearing system was designed and constructed. The external bearings made it possible to alter the journal bearing angles and thus allow a wide flexibility in cutter configuration. Fig. 1 shows the laboratory bit assembly, the various bearing mount plates and the appropriate roller cutters for drilling shallow holes having hole bottom angles of 0, 10, 20, 30 or 40". The bit was limited to a drilling depth of 1 1/2 in. at the gauge teeth and a hole diameter of 43/4 in. This more or less intermediate size bit was chosen because it gave a more realistic match between bit teeth and the rock than would a microbit. Also, the rock sample size required was convenient and easy to obtain. CIRCUMFERENTIAL CUTTERS The tooth configuration used in our initial studies is shown in the upper half of Fig. 2. All cutters used in this series had the same tooth form — 43" included tooth angle, 2" positive relief angle and a horizontal tooth flat width of 1/32 in. Each cone cuts alternate rows except for the gauge row. The row-to-row spacing in view was 1/4 in. Static loading tests conducted earlier with asymmetrical chisels had been used to establish this spacing. These tests showed energy requirements for chip production increasing rapidly as the distances to the edge increased beyond

By Jan M. Mutmansky, Y. J. Wang

Mine ventilation analysis is an engineering discipline that can be considered a branch of the body of science known as network analysis. Likewise, the group of engineering procedures known as the critical- path method (CPM) is considered a branch of network analysis. It is therefore not surprising that mine ventilation network analysis and CPM have many similarities. These similarities are useful in analyzing several types of mine ventilation problems and will be utilized in this paper. The analogy between the free split in a ventilation circuit and the critical path in a scheduling network has been recognized by Owili-Eger (1973). While this was recognized as a property of a general ventilation network, many important applications to controlled- splitting problems also exist. The mathematical procedures necessary to apply CPM and network methods have previously been presented (Wang, 1981; Wang, 1982). This paper will illustrate the implementation of these methods by application to mine ventilation networks.

Jan 1, 1982

By E. G. Banks

THIS paper is presented in the belief that metallurgists and chemists will be interested in the practice of grinding in tube-mills in connection with stamps, especially since the records of working here given extend over a lengthy period of time (since May, 1905). The ore from the Waihi mine-more especially that produced in the upper levels-contains a large proportion of hard, chalcedonic quartz, and the gold exists in an exceedingly fine state, conditions which necessitate very fine crushing in order to ob¬tain a high extraction of the precious metal. Before the introduction of tube-mills at the 90-stamp Waihi mill, it was found necessary to stamp through 40-mesh (1,600 holes per sq. in.) woven wire-screens, having a fairly high discharge. The pulp then graded

Jan 1, 1907

"The greatest mining center in the state of Utah is the incorporated town of Bingham about twenty-five miles southwest of Salt Lake City. The principal industry of this vicinity, prior to the early fall of 1 863, was lumbering and the first saw-mill in the state was built near the mouth of Bingham Canyon. Early in the fall of that year, George B. Ogilvie discovered gold and shortly afterward the first mining district in the state was organized. Some writers place the discovery of gold in the canyon in the late fifties. If this be so, however, the matter was kept extremely quiet because no mining was engaged in until after Ogilvie's discovery.Bingham was a placer mining camp, producing about one million dollars' worth of dust and nuggets from placers up and down the canyon and in Bear Gulch until early in the seventies, or about ten years after the discovery of gold, when a large body of argentiferous lead ore was discovered and soon after heavy shipments were made from a half dozen or more properties.In 1 8 74, A. H. and George L. Bemis erected the first concentrating plant in the state for the treatment of sulphide lead ores.The history of the camp as a producer of copper begins in the summer of 1 88 7, when Enos A. Wall noticed, in observing prospecting drifts and inclines driven some years before, the discoloration caused by the coppery solution. As a large part of the adjacent ground had been abandoned, he located two claims, which he called the ""Dick Mackintosh"" and the ""Charles Reid,"" after two of his friends.Late in 1896, the Highland Boy Mine produced sulphide ore rich in copper, causing a revival of interest in the copper potentialities of the camp, and during the next seven years a number of new claims were located ."

Jan 1, 1925

By MERLE HOWARD GUISE

WHEN I was a boy I walked into Fairbanks in 1905. I was but a soft chechako, and arrived with blisters covering my feet, as a result of "mushing" the 400-mile trail on foot. Because of them, the display windows of the trading posts were first to catch my eye-dog and horse collars, harness and sled parts! And because of my enthusiasm for things adventurous, I looked long upon the prospectors' gold pans, shovels, rifles, camp equipment, and what not. Today those windows are filled with motor car accessories, tires and repair parts; yes, even thermos bottles and vacuum cleaners! There were many chance meetings with little parties of prospectors in my youth, and it always set my blood to tingling. Sometimes it was a 70-year-old sun-baked son of the Arizona desert, wrangling his stubborn, faithful jenny away from some outfitting store, at others a shovel-ended poling b0at in northern Canada, \vith the partners and the dogs towing upstream along the bank, or an old sourdough, with tug-rope around neck and hand on the spruce sapling gee-pole, mushing along behind his two or three old, plodding malamutes, dragging a little Yukon sled piled high with rusty sheet-iron stove, pick and shovel, cross-cut saw and axe, rifle, bales of dog salmon, and other paraphernalia. These meetings envisioned the panning of old creek beds and draws in the search for as yet undiscovered pay-channels; they meant the toughest kind of work sinking a hole to bedrock in some far-away valley of promise; they suggested wood fires to thaw the frozen muck and gravel and crude windlass and hand-made tub to hoist the water and the mud; but loudest of all they spoke of Adventure.

Jan 1, 1929

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700' and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag' HZ =-6600(1 - xA1)' + 4400(1 - XMf cal SCHNEIDER and toll' have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,' however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1' that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA 'A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By Edward Hanrahan

September 1981 I'm here today to report on a revolution -- a revolution in the way the Federal Government looks at energy. I'm not talking about a simple change in the relative emphasis on sources -- such as more recognition for coal and nuclear power, with less rhetoric about "soft- technology." Nor am I describing a mere change in focus -- from the demand side to the supply side. And I am not referring exclusively to our obvious goal of budget cuts. No, I'm here to discuss a fundamental change in Federal direction -- one that started as soon as President Reagan was inaugurated, and one that is articulated in the National Energy Policy Plan he sent to Congress in July. That brief policy document was backed up by three volumes of supporting data; but I think I can catch it's flavor for you in just three phrases: * First, various energy forms complete with each other and complement one another. * Second, fair competition among them (which includes honest pricing) will give us the best "energy mix." • And, finally there may be ligitimate arguments about where Federal responsibility in regard to energy spills over into Federal interference; but it's about time we drew the distinction -- and eliminated the latter. This Administration's national energy policy is quite different from any we have had in recent years. It is tuned to human nature and changing times. We are seeking the best practical solutions in the energy -a lot better than the ones we have been offered before, but still something less than perfection. One way we do that is by counting on a fully informed public to guide it's own destiny. And, instead of treating energy as an isolated entity, we recognize it as part of the overall economy. The President's Program for Economic Recovery is as much a factor in energy policy as the specific actions of the Department of Energy. One striking difference from the past energy policy 1s that this policy plan does not say: "In 1985 we will -produce so many hundreds of millions of tons of coal: . . . or . . . "By the end of this century the Nation will be deriving X percent of it's electricity from wind generators." Unfortunately, targets like these are what many people have come to expect from the Federal Government -- and what they think of as energy policy, whether the figures hold up in the long run or not. But . . . think about it! Nether the Department of Energy nor any other part of the Federal Government produces coal, or mines uranium, or manufactures solar collectors. There are only a few sections of the country where the Federal Government generates and sells electricity. So it does not take any great insight to recognize that the amount of energy we will produce or consume as a Nation In the future depends on many factors beyond direct government action. And those future totals cannot be predicted precisely, anyway -- by the Government or by anybody else. According to our way of thinking, the choices should be up to the people. When the free market works within a healthy economy, individuals express their preferences in the marketplace -- adjusting the balance of all energy factors continually in a way that no computer could be programmed to reflect perfectly. So, instead of having the Government issue a rigid set of numerical goals, our main concern simply is that there be enough energy. We want the Nation itself to decide how much that should be, what form it should take, and how that energy should reach consumers. The marketplace decides. Considering the recent past, this is indeed a revolutionary idea. It has some pitfalls, and we won't reach this ideal of free choice overnight. But that is where we are headed. And I'll offer some evidence in a few minutes that the policy has already started working. First, let me give you some of it's highlights: 1) Nobody who appreciates the philosophical underpinnings of this Administration will be surprised that the energy policy shows faith In domestic energy production and the supply side of the economy; but it also recognizes the important role of energy conservation -- the wise and efficient use of energy resources.

Jan 1, 1982

By AIME AIME

INSTITUTE members attending the Annual Meeting in New York who want to see one of the mining engineers' newest aids, photoelastic stress analysis, are due for an interesting afternoon on Thursday, Feb. 15, when open house: will be held at the Columbia University mining laboratory. Information as to the direction and distribution off stresses in mine structures, which has been developed by Professor Bucky, associate professor at the Columbia School of Mines, and David Sinclair, research assistant, is useful in the design of pillars and in the placing of openings relative to working places such as gangways and haulage levels.: This work has been sponsored during the last ten years by the Engineering Foundation.. It is fully reported in T. P. No. 1140.

Jan 1, 1940

By J. L. Tomlinson, B. D. Lichter

Electrical resistivities 01 liquid Cd-Bi, Cd-Sn, Cd-Pb, In-Bi, and Sn-Bi alloys were measured using an electrodeless technique. The resistivities ranged from 50 to 160 microhm -cm, temperature dependences were positive, and no sharp peaks in the composition dependence of the resistivity were observed. On the basis of these observations, it was concluded that the alloys are typical metallic liquids. The electron con-cent9,ation was calculated from the measured resis-tizlity and available thermodynamic data using a model which attributes electrical resistivity to scattering by density and composition flzcctuations. A correla-tion was shown between the departure of the electron concentration from a linear combination of the pure component valences and the value of the excess integral molar free energy. Calculation of the temperature dependence of the electrical resistivity showed a need for more detailed thermodynamic data in these systems and led to suggestions for improvement in the concept of residual resistivity in the fluctuation scattering model. THE electrical resistivity of liquid metals provides information regarding interatomic interactions and their effects upon structure. In this experiment an electrodeless technique was used to measure the electrical resistivities of liquid alloys of Cd-Bi, Cd-Sn, Cd-Pb, In-Bi, and Sn-Bi, and the results were used with thermodynamic data to calculate a parameter which reflects the tendency toward localization of electrons due to compositional ordering. It was found that the resistivities of these alloys are generally metallic in magnitude and temperature dependence. The electrical and thermodynamic properties are discussed in terms of the fluctuation scattering model'22 which supposes that the electrical resistivity arises from scattering due to a static average structure and departures from the average due to fluctuations in density and composition. Further, this model is compared with the pseudopotential scattering model of Ziman et al.3-5 EXPERIMENTAL PROCEDURES Alloy samples were prepared from 99.999 pct pure elements obtained from American Smelting and Refining Company (except tin which was obtained from Consolidated Smelting and Refining Company.) J. L. TOMLINSON, Member AIME, formerly Research Assistant Division of Metallurgical Engineering, University of Washington, Seattle, Wash., is now Physicist, Naval Weapons Center, Corona Laboratories, Corona, Calif. 0. D. LICHTER, Member AIME, is Associate Professor of Materials Science, Department of Materials Science and Engineering, Vanderbilt University, Nashville, Tenn. This work is based on a portion of a thesis submitted by J. L. TOMLINSON to the University of Washington in partial fulfillment of the requirements for the Ph.D. in Metallurgy, 1967. Manuscript submitted May 31, 1968. EMD Weighed portions were sealed inside evacuated silica capsules, melted, and homogenized before the resistivity was measured. The resistivity of a liquid alloy was measured by placing the sample inside a solenoid and noting the change in Q. According to the method of Nyburg and ~ur~ess,~ the resistivity of a cylindrical sample may be determined from the change in resistance of a solenoid measured with a Q meter as T7--5--W =R7JT^ ='Kc-lm(Y) [1] where L, R, and Q = wL/R are the inductance, series resistance, and Q of the solenoid. The subscript s refers to the solenoid with the sample inside; the subscript 0 refers to the empty solenoid. Kc is the ratio of the sample volume to coil volume and y = 2 [bei'0(br)-j ber'o(br)~\ br\_bero(br) +j bei0 (br) expressed with Kelvin functions which are the real and imaginary parts of Bessel functions of the first kind with arguments multiplied by (j)3'2. The argument of the function Y is hr where r is the sample radius and b2 = po~/p, i.e., the permeability of free space times 271 times the frequency divided by the resistivity in rationalized MKS units. Since Eq. [I] cannot be solved explicitly for p, values of Kc. lm(Y) were tabulated at increments of 0.1 in the argument by. A measurement of Q, and Q, determined a value of Kc . lm (Y) and the corresponding value of br could be read from the table. From the known r, uo,, and w, the resistivity, p, was determined. The change in Q was measured after letting the encapsulated Sample reach equilibrium inside a copper wire solenoid. The solenoid was contained in an evacuated vycor tube in order to retard oxidation of the copper while operating at high temperatures and heated inside a 5-sec-tion nichrome tube furnace capable of obtaining 900°C. Temperature was determined with two chromel-alumel thermocouples, one in contact with the solenoid 30 mm above the top of the sample and the other inserted in an axial well at the other end of the solenoid and secured with cement so that the junction was 2 mm below the bottom of the sample. Temperature readings were taken with respect to an ice water bath junction, and the voltage could be estimated to the nearest thousandth of a millivolt. The lower thermocouple was calibrated by observing its voltage and the Q of the coil as the temperature passed through the melting points of samples of indium and tellurium. The upper thermocouple reading was systematically different from the lower thermocouple reflecting the temperature difference due to a displacement of 60 mm axially and 6 mm radially. Calculations show that the gradient over the sample was less than 2 deg. Q was measured by reading a voltage related to Q from a Boonton 260A Q meter with a Hewlett Packard

Jan 1, 1970

By George H. Hanna

THE importance of the Donets coal field (the Donbas) to the national economy of the Soviet Union is well known. Great as was the significance of this tremendous deposit of coal in prewar days it is destined to become an even greater factor in the economic life of the country now that the tremendous havoc wrought by the Germans is being remedied. Since the war began, new coal fields have been extended; for example output of the Moscow and Karaganda (Kazakhstan) fields has become considerably larger while new mines are producing coal in several parts of Uzbekistan and Kirghizia. The huge West Siberian coal field, the Kuznetsk Basin, is producing more coal than ever before to supply the industries of that region and of the Urals. But so great has been the development of industry to meet war needs, especially in those districts of the Soviet Union that lie to the East of the Urals, that the coal obtained, eked out by such locally-won fuels as peat and wood, is still barely sufficient to meet industrial requirements. The main burden of the coal supply for the restored industries of the West, therefore, will fall on the Donbas.

Jan 1, 1945

By G. R. St. Pierre, M. J. Pool, R. Speiser

The activities of chromium in solid Cr-Ti solulions contaitning from 10 to 90 at, pct Cr were measured over the temperatutre range 1250" to 1380°C. The Knzudsen effusion technique with direct weighing of the Knudsen cell was used. This was possible because the vapor pressure 0f chromium is about 600 times greater than the capor pressure of titanium so that the amount 0f titanium effusing could be neg-Lected. the activities of titanium were determined by g-raphical integration of the Gibbs-Duhertz equatiotz. The solutio~ls sllcdied exhibited positive deviations from Raoult's law, but they approached ideality as the temperature was raised from 125 to 138t C. The integral free energy of mixing was calclated from the activity values. AF has a maximum value of - 1.66 kcal a1 1390°C and a composition oj 55 at. pcl Cv. The free energy of formation of 'TiCr, is —0.76' lzcal a1 1250°C. The heats and entropies of mixing usere determined using the second law and thus tile mlues could be in error by a considerable amount. The Cv-Ti system is not a regular solution. ThE increasing emphasis on application of various models to alloy formation and solution behavior has led to an intensified interest in the thermochemistry of alloys. In a majority of the cases where different models have been applied the alloy system used was a simple one. However, the amount of data available on more complicated systems is small and in order to fully understand the behavior of metallic solutions more experimental work has to be carried out on these systems. The Cr-Ti system is reasonably complex and even though this system was being investigated as early as 1937 by Kroll,' no previous work has been done on the thermodynamic properties of either the liquid or solid state. This research was undertaken to determine the thermodynamic properties of solid Cr-Ti alloys. EXPERIMENTAL PROCEDURE The experiments on the Cr-Ti system were carried out in a water-cooled metal vacuum system. This system is composed of a brass vaporization chamber wound with copper tubing for cooling purposes, a brass liquid-nitrogen trap, an oil diffusion pump, and a Duo-Seal forepump. The pressure in the system is measured with an ionization gage. The interior of the vaporization chamber is shown schematically in Fig. 1. The Knudsen cell is supported by the molybdenum tripod, and a magnetically operated shutter is provided to protect the Pyrex sighting glass against deposition of metallic vapors in the intervals between temperature measurements. Heating is accomplished by means of a 20-kw 450-kc Westinghouse oscillator. The susceptor in this case is 10-mil tantalum seamless tubing which also forms the outside of the sample container. The remainder of the sample container consists Of an im~ervims re-crystallized alumina crucible and a 10-mil-thick tantalum lid. Two holes are drilled in the lid. The diameters of these holes were measured with the calibrated stage of a "Tukon" microhardness tester. The thicknesses were measured with a micrometer. A Leeds and Northrup disappear ing-filament optical pyrometer was used to measure the temperature. This is sighted through the smaller of the two holes in the lid and corrections for the emissivity of the sample were not necessary since the ratio bf cell length to hole diameter was large enough to insure a hohlraum. The pyrometer was calibrated at the ~~t~~~l Bureau of Standards, and the correction for the Pyrex sighting window was determined in the laboratory. The titanium used in this investigation was obtained from Mallory-Sharon and the chromium from The Union Carbide Metals Co. The reported purities were

Jan 1, 1968

By S. H. McFarlane, K. H. Zaininger, G. W. Cullen, C. C. Wang, G. E. Gottlieb

Heteroepitaxy of silicon on stoichiometric spinel has been studied. Both boron-doped (p-type) and arsenic-doped (n-type) single-crystal silicon films have been grown by the pyrolysis of silane on sioichiometric spinel (MgAl2O4) substrates prepared by a flux technique. The spinel crystals are free from strain and subgrains, and exhibit no thermal instability at temperatures employed for silicon deposition. The growth parameters of epitaxial silicon have been studied. Effects of substrate orientation, surface preparation, and growth conditions on the silicon Properties have been determined. The silicon-spinel composite was characterized by X-ray diffraction, electron diffraction, electron microscopy, and optical techniques. Information on epitaxial orientation relationship, defect structures and film-substrate interface has been obtained. A parallel orientation relationship was found between silicon and spinel. The silicon films exhibit no subgrain structures. However, growth pyramids, microtwins, stacking faults, and dislocations are the prevalent defects. The deformation of epitaxial silicon was measured by an X-ray technique. It was found that the epitaxial silicon is strained under compres-sive stress due to the thermal expansion difference between the film and substrate. The stress was estimated using the classical plate theory and beam equation. Electrical properties of the epitaxial silicon have been measured, including resistivity, carrier concentration, and Hall mobility. MIS and vertical through diffused junction structures have been fabricated wing silicon-spinel composite. Information on MIS characteristics, minority carrier life time, and junction properties has been obtained. THE achievement of single-crystal growth of large area silicon semiconductor films on oxide insulating substrates is of technical importance to many solid state electronic devices. The semiconductor-insulator composite structure is also of scientific interest because the heteroepitaxy is determined by the spatial relationship between the atomic arrangement in the substrate and that of the atoms in the appropriate crystallographic plane of silicon. The degree of crystalline perfection of the silicon deposits depends also on the physical condition of substrate surface. Epitaxial growth of silicon on commercial flame fusion Al-rich spinel (MgO:3.3A12O3) has been reported by several investigators.'-4 The lattice of spinel of this composition is distorted. The material cracks and exsolves the excess alumina in the lattice at temperatures (-1200°C) used in fabricating silicon devices. Stoichiometric MgA12O4 spinel exhibits neither lattice distortion nor thermal instability. Results are given on the epitaxial growth and characterization of silicon on stoichiometric spinel. EXPERIMENTAL Fabrication of Silicon-Spinel Composite Structures. The MgA12O4 spinel substrate wafers were prepared from bulk single crystals grown at about 1200°C by a flux technique5 using a PbF2 flux. The crystals are free from strain and subgrains, and exhibit a typical dislocation density of less than 50 lines per sq cm. The crystals are thermally stable without cracking and exsolution of alumina to at least 1500°C. The spinel crystals were oriented for cutting by the Laue X-ray back-reflection method.6 Substrate wafers (about 25 mil thick) of (Ill), (loo), and (110) orientations have been obtained bu cutting the X-ray oriented crystals using a standard type diamond wheel. An accuracy of better than 1/2 deg is maintained throughout the operation. The spinel substrate wafers were mechanically lapped and polished to produce the flat and smooth surface which is required for silicon epitaxy. Lapping was carried out with about 30-µ boron carbide abrasives to obtain a flat coplanar surface. The lapped surface was further polished using successively finer grades of alumina, ending with the 0.3-µ grade. After polishing the wafers generally have a flatness of ±0.4 µ per cm, as revealed by interferometry. Fig. 1 shows (111) oriented MgA12O4 spinel wafers of various shapes.

Jan 1, 1970

By Eugene S. Meieran

The effects of methods of crystal growing, wafer sawing, polishing, routine handling, diffusion, and epitaxial growth on the defects in GaAs are reviewed and studied using reflection and transmission X-ray topographic techniques. In general, it was found that boat-grown crystals exhibited fewer defects than Czochralski crystals, although all crystals showed large numbers of precipitates visible when examined in the electron microscope. Mechanical surface treatments such as sawing and mechanical polishing introduce damage to a depth of about 5 µ, most of which can be removed by suitable chemical or chem-mechanical polishing. In addition, defects can be introduced through routine handling of wafers, for example with metallic tweezers. These defects can be quite severe, and have been observed 20 µ below the wafer surface. Defects can also be introduced through diffusion and epitaxial growth. These defects, which include precipitates, growth pyramids, stacking faults, dislocations, and so forth, can be detrimental to device fabrication. It is shown that wafers or films which appear defect-free optically can contain defects visible in the X-ray topographs. WHILE the use of GaAs in the semiconductor industry has increased very rapidly in the last few years, due mainly to the recent development of many important GaAs devices,1,2 the major limit to the production of commercial quantities of many GaAs devices remains a severe lack of suitable materials technology. This lack is apparent in two critical areas. First, production quantities of high-quality GaAs crystals, reproducibly doped and precipitate-free, simply are not available commercially, although some reasonable quality material is available on a limited first-come, first-serve basis. Second, in comparison to silicon technology, little is known about the effects of processing variables on the defects either present in as-grown GaAs or introduced through processing and handling of wafers. These areas are now receiving some attention from semiconductor device manufacturers, who are studying defects in GaAs in order to better understand how either to prevent their occurrence or to cope with their existence. Most investigations of the defects in GaAs have been made by optical microscopy3-5 or transmission electron microscopy techniques.'-' Recently, however, the imaging techniques of X-ray topography, electron mi-croprobe analysis, and scanning electron microscopy are being applied to the study of GaAs.9-14 In the case of X-ray topography, a one-to-one image is obtained that must be photographically enlarged. In compensa- tion, the defects within entire wafers may be imaged by simple scanning (Lang technique15) if the wafer is reasonably perfect, or by using the scan oscillation technique developed by Schwuttke16 if the wafer is warped or distorted. The purpose of this paper is to both review and extend the general application of X-ray topographic techniques to GaAs. Emphasis will be placed on the effects of growth and process variables on the quality and perfection of both bulk and epitaxial GaAs. Reference to optical or electron microscopy results will be made when useful. Since the effects on defects of a wide variety of processing variables such as crystal growing, sawing, polishing, diffusion, and epitaxial growth will be somewhat superficially reviewed, a fairly extensive bibliography of the most important recent results in these areas is included. However, for completeness, important defects will be illustrated here, although such defects have been previously shown by others. While this paper is concerned with defects rather than with the physics of X-ray scattering, the mechanisms of contrast formation in the topographs will of necessity be briefly mentioned. EXPERIMENTAL GaAs crystals, both boat-grown18 and Czochralski-grown,'8 containing a variety of dopants of various concentrations, were purchased from outside vendors. Wafers were sliced from the crystals using a Hamco ID saw and were mechanically polished using 1 µ diamond paste. Chem-mechanical polishing was done in bromine-methanol as described by Sullivan and Kolb.18 Chemical polishing was done using a modified sulfuric-peroxide solution, 11 parts H2SO4, 1 part 30 pct H2O2, 1 part DI water.5 Zinc diffusion was carried out in a closed tube, using a 10 pct Zn-In source at 825°C for 1 hr. Oxide masking techniques were used to select the area to be diffused. Epitaxial wafers were either purchased or prepared here. All epitaxial runs prepared here were carried out using a Ga-GaAs-AsC13 source in a closed tube at a substrate temperature of 750°C. Wafers were chem-mechanically polished and gas-etched prior to deposition. The X-ray topographs were taken on a Krystallos Lang camera, operating in the transmission scanning geometry (Lang technique15) or in the reflection scanning geometry (modified Berg-Barrett technique20,21). MoKa, radiation was used for all transmission topographs using a Jarrell-Ash 100-µ spot focus. CuKal radiation was used for all reflection topographs using a General Electric CA-7 1-mm spot focus X- ray tube. Topographs were printed from an intermediate contrast inversion film, so the contrast shown in all figures here is the same as that of the original 50-µ-thick emulsion L4 Iiford nuclear plate used to record the topograph.

Jan 1, 1969

By H. Rush Spedden, Arvid Thunaes

R. R. Knobler and F. E. Albertson—Following the testwork done by Thunaes and Spedden, a Sullivan deck plant was built for the Colquiri mill. This plant started to operate in April 1945 and continues in successful operation. Since May 1950 the Colquiri mill has operated with a completely revamped flowsheet at a rate of 1000 tons per day. The old Sullivan deck section was retained with this new flowsheet. The "slime plant" in Colquiri consists of one 12-cell Denver No. 18-Sp. Sub-A flotation machine, one 16-ft and one 12-ft hydroseparator, six five-deck Sullivan-frames and six shaking tables for cleaning up the Sullivan deck concentrates, as well as 12 Deister plus three Plat-O tables on which the fine sands, which are not treated on the S-decks, are concentrated. Only —325-mesh fines are treated on the Sullivan decks. The combined hydroseparator overflows are fed to the S-decks. From 1946 to 1949, i.e. with the "old" flowsheet and an average mill feed of 800 tons per day an average of 45 tons per day was treated on four Sullivan rougher frames. The two additional frames were used as cleaners. At times, up to 90 and 120 tons of slimes were treated successfully on this Sullivan deck installation. The average operating data for the S-deck section in Colquiri for the year 1949 were as follows: The tests reported in this paper indicated a tin recovery of 42 pct. The actual plant results for 1949 show a 54 pct tin recovery from the Sullivan decks. The total average quantity of tin produced from the S-deck section in 1949 was 15 tons of tin per month. This corresponds to 3 pct of the total mill recovery. The difference between the 6 pct overall recovery-increase expected after the tests in 1943 and the actual plant results given for 1949 is explained as follows. According to the tests, a total of 170 tons was expected to be routed to the Sullivan decks, but because of certain changes in the flowsheet and mill amplifications,

Jan 1, 1951

By H. Rush Spedden, Arvid Thunaes

R. R. Knobler and F. E. Albertson—Following the testwork done by Thunaes and Spedden, a Sullivan deck plant was built for the Colquiri mill. This plant started to operate in April 1945 and continues in successful operation. Since May 1950 the Colquiri mill has operated with a completely revamped flowsheet at a rate of 1000 tons per day. The old Sullivan deck section was retained with this new flowsheet. The "slime plant" in Colquiri consists of one 12-cell Denver No. 18-Sp. Sub-A flotation machine, one 16-ft and one 12-ft hydroseparator, six five-deck Sullivan-frames and six shaking tables for cleaning up the Sullivan deck concentrates, as well as 12 Deister plus three Plat-O tables on which the fine sands, which are not treated on the S-decks, are concentrated. Only —325-mesh fines are treated on the Sullivan decks. The combined hydroseparator overflows are fed to the S-decks. From 1946 to 1949, i.e. with the "old" flowsheet and an average mill feed of 800 tons per day an average of 45 tons per day was treated on four Sullivan rougher frames. The two additional frames were used as cleaners. At times, up to 90 and 120 tons of slimes were treated successfully on this Sullivan deck installation. The average operating data for the S-deck section in Colquiri for the year 1949 were as follows: The tests reported in this paper indicated a tin recovery of 42 pct. The actual plant results for 1949 show a 54 pct tin recovery from the Sullivan decks. The total average quantity of tin produced from the S-deck section in 1949 was 15 tons of tin per month. This corresponds to 3 pct of the total mill recovery. The difference between the 6 pct overall recovery-increase expected after the tests in 1943 and the actual plant results given for 1949 is explained as follows. According to the tests, a total of 170 tons was expected to be routed to the Sullivan decks, but because of certain changes in the flowsheet and mill amplifications,

Jan 1, 1951