By J. R. Bell, W. J. Childs, J. H. Bucher, G. A. Wilber

A technique for determining recrystallization times as short as 0.10 sec was developed utilizing the "Gleeble", a commercially available testing system designed for the study of short-time, high-temperaLure themal and mechanical processes. The procedure consisted of heating a small tensile specimen to a given temperature of hot deformation, loading to a given reduction in area, unloading, delaying various intervals at temperature, and then reloading- to failure. The magnitude of the ultimate load obtained upon reloading decreased with delay lime as recrys-lallization proceeded. The technique was applied to austenite recrystallization in AISI 1010 and AISI 1010 uith 0.02 pct Cb steels. For each steel the reduction in area given the specimen on the first pull was mainlairred at 30 ± 5 pct and recrystallization times deterntined at various temperatures. The results indicaled a significantly slower rate of recrystallization for the columbium-modified composition, suggested the presence of- a recovery stage in the softening process , and indicated a greatly increased softening rate at a temperatuve where significant allotropic transformation to a partially ferritic Structure could occur. In recent years increasing attention has been paid to the fact that the process of recrystallization of austenite deformed at elevated temperatures is far from instantaneous at many practical hot-working temperatures.1-3 This realization has given rise to such terms as hot cold-working1 or warm-working,2 These terms generally describe processes where the recrystallization rate at the temperature of deformation is slow enough to have an appreciable effect on mechanical properties despite a relatively high deformation ternperature. The mechanical properties of interest can be either the properties at the deformation temperature as in hot-workability studies4 or the room-temperature properties after cooling as in the many recent studies of various thermomechanical processes172 where heat treatment and deformation are intentionally combined to give a unique set of room-temperature properties. Because of this interest in processes where the austenite recrystallization kinetics can be an important variable, the development of quantitative methods of following the course of short-time, high-temperature recrystallization has received increasing attention.l,3,5 The experimental methods to date have, in general, relied upon rapidly deforming the austenite, holding at temperature for various brief intervals, quenching as G.A.WILBER and W. J. CHILDS, Members AIME,are Research-Fellow and Professor, respectively, Rensselaer Polytechnic Institute, Troy, N. Y. J. R. BELL and J. H. BUCHER, Member AIME, are Research Engineer and Research Supervisor, respectively, Graham Research Laboratory, Jones & Laughlin Steel Co., Pittsburgh, Pa. Manuscript submitted March 13, 1968. IMD. rapidly as possible, and then using room-temperature measurements to follow the recrystallization process. Although such methods can be successfully applied to certain alloy steels, the existence of the allotropic transformation during cooling of plain-carbon or low-alloy steels tends to obscure the results. Thus, such room-temperature measurements as hardness and X-ray line widths do not correlate well with the extent of austenite recrystallization before quenching,5 and results based on room-temperature microstruc-tural observations are dependent upon the success in correlating the observed structure with the prior aus-tenitic grain structure.1,3,5 The purpose of the present work was to develop a quantitative method for the determination of short-time, high-temperature recrystallization rates, based on measurements made at the temperature of deformation. EXPERIMENTAL TECHNIQUE The basic technique consisted of heating a small tensile specimen to a given temperature of hot deformation, loading to a given reduction in area, unloading, delaying various intervals at temperature, and then reloading to failure. The data were obtained in the form of traces of load and elongation as a function of time. Due to the high deformation temperature, the strain hardening introduced during initial loading was progressively annealed out with holding time after unloading and the loads obtained upon reloading decreased as this softening proceeded. Although the value of the second load at any Consistent point On the load-elongation curve could have been used as a measure of the degree of softening, the most convenient to use was the ultimate load. The softening indicated by the decrease in the second ultimate load with time is essentially a process of annealing of cold-worked material at a high deformation temperature. Although some recovery grain growth may contribute to such a softening process, it is generally considered that the major softening which must take place to achieve complete removal of substantial Strain hardening will occur by the formation of new, stress-free grains. As the results of this work indicate that essentially complete removal of strain hardening did in fact occur. the primary softening process will be attributed to recrystallization, and specific reference made where it appears that other mechanisms may be contributing to the total observed softening. It would, of course, be of interest to attempt to correlate the results of this work with the actual austenite fraction recrystallized as determined by other techniques. This was not attempted in the present work because it would have required running a large number of additional specimens and, as discussed previously, there is limited assurance that the results would accurately reflect the prior austenite fraction recrys-

Jan 1, 1969

The pressure of the gas in equilibrium with sphalerite has been determined in the temperature range of 680' to 825°C, using the Knudsen orifice method. A comparison of these experimental pressures with those calculated from thermal data and from other equilibrium measurements shows that the vapor above sphalerite is predominantly dissociated ZnS. Equations have been given for correctly calculating dissociation pressures using the Knudsen orifice method. It has been shown that the experimentally determined pressure is the same, whether the zinc sulphide is sphalerite or not, or a mixture of wurtzite and sphalerite. CONFLICTING points of view appear in the literature on the constitution of the vapor in equilibrium with solid zinc sulphide in the vicinity of 800°C. By comparing the dissociation pressure calculated from thermodynamic data and the vapor-pressure determination of ZnS by Veselovski,1 Lumsden2 has concluded that the vapor consists largely of dissociated ZnS. Sen Gupta,' however, concludes from his spectroscopic determinations that the vapor is largely ZnS molecules. In view of the fact that the thermodynamically calculated' dissociation pressure is higher than that experimentally measured by Veselovski, it seemed in order to repeat Veselovski's measurements. Experimental Procedure The method used for the determination of the pressures in this papel- is the Knudsen effusion cell. The apparatus and procedure were described in a previous paper- from this laboratory on the determination of the vapor pressure of silver. The only difference is that the Knudsen cell in this work is made from platinum and there is no external cover around the cell. The cell is an ordinary platinum crucible of 2.2 cm top diameter with a capsule cover. It was thought that platinum might stand up at these temperatures to the solid and gaseous ZnS, since it was found that the weight of the platinum cell itself did not change appreciably on heating ZnS in it at the working temperatures. To insure that reaction of the zinc sulphide with the cell was not giving' a false value, a stabilized zirconia cell was employed for check runs. Fig. 1 shows the comparison, which is satisfactory. Veselovski previously had measured the vapor pressure of ZnS using a silica Knudsen effusion cell. On repeating his experiment in this laboratory, it was found that ZnS at-tacked the silica cell, giving it a marked frosty appearance. This led to the belief that Veselovski's result:; may be in error. Also, he was operating at pressures above the range ordinarily considered safe for the Knudsen method. The effusion rate was measured by weighing the cell before and after each run. The weight loss during heating to temperature and cooling down was measured and subtracted from the weight loss during the actual run. The zinc sulphide used in this investigation was from two sources: Fisher cp grade, and a sample of pure sphalerite supplied by Mr. E. A. Anderson of the New Jersey Zinc Co. Before and after the series of runs with Fisher ZnS, X-ray analysis showed that both wurtzite and sphalerite were present. However, the ratio of sphalerite to wurtzite increased. All measurements were made below the transition temperature which has been reported" to be 1020°C. The data obtained in this investigation are tabulated in Table I. The pressure was calculated by the usual Knudsen formula" on the assumption that ZnS molecules were effusing. From these data, using pure sphalerite in the platinum Knudsen cell, the vapor pressure of ZnS, in mm of Hg, as a function of temperature is given by the solid line in Fig. 1. The best straight line, as determined by the method of least squares, is given by 14405 logpzns =-14405/T +11.032. A comparison of these results with Veselovski's shows that his results are about 50 pct lower. Discussion The vapor in equilibrium with solid zinc sulphide in the temperature range of this study will consist of Zn, S2, and ZnS mol, since other species of zinc and sulphur' are relatively unstable. The question to be settled is whether or not ZnS is largely dissociated. The derivation8 which follows gives the method of calculating the pressure of zinc and sulphur over solid ZnS, assuming complete dissociation, from Knudsen cell data. The free energy of the reaction 2 ZnS(solid) ? 2 Zn(gas) + S2(gas) is given by ?F?° = -RT In K = —RT In p12p2 where p1 is the zinc pressure and p is the sulphur pressure. If dissociation occurs in a closed system,

Jan 1, 1955

By J. D. Vincent, Pierre R. Hines

INTRODUCTION OF FROTH FLOTATION INTO THE UNITED STATES "The introduction and development of the flotation process have proved to be of such momentous importance to the mining industry of the United States that they deserve to be considered historically ." T. A. Rickard l James M. Hyde installed the first froth flotation process in the U. S., about Aug. 1, 1911, at the Basin Reduction Co. plant, Basin, Mont., which was then under lease to the Butte and Superior Copper Co.2 Two months later, the Minerals Separation Ltd.. filed suit in the U. S. District Court of Montana against Mr. Hyde char& him with infringement of their Patent 835, 120/1906. The U. S. District Court decided in favor of Minerals Separation Ltd. on July 28, 1913. This decision was reversed by the Ninth Court of Appeals in San Francisco on May 4, 1914. Then the U. S. Supreme Court, on Dec. 11, 1916, upheld the patent on three counts only but restricted it to 'the use of less than one percent of oil.” The Miami Copper Co. was sued by Minerals Separation on Oct. 10, 1914, for infringement of Patents 835,120 and 962,678, and 1,099,699. The Miami Copper Co. was operating under John M. Callow's froth flotation process Patent 1,104,755/~uly 23, 1914. Miami lost this suit in the District Court of Wilmington, Del., and appealed to the Court of Appeals, Third Circuit, Philadelphia. The Third Court of Appeals decided against Miami, May 24, 1917. The case was referred to a Master and hearings to determine profit and damages were not settled until 1923. Nevada Consolidated Copper Co. was sued Sept. 9, 1919, and Magma Copper Co. was sued Jan. 10, 1920. Thus, the first ten years of froth flotation in the U. S. were beset by patent litigation. This litigation suppressed the free circulation of new discoveries or useful information that might be cited in a patent suit against the originator; it accounts for many of the blank spaces in the historical record. T. A. Rickard3 has reviewed the history of flotation and has given the chain of discoveries, patents, and processes that resulted in froth flotation. He has re- ported also on the patent litigation beginning in 1911 and ending in November 1923, when Minerals Separation's Patent 835,120 expired. He comments on

Jan 1, 1962

By M. E. Wadsworth, K. C. Bowles, H. E. Flanders, R. M. Nadkarni, C. E. Jelden

The kinetics of precipitation of copper on iron of various purity were carried out under controlled conditions. The rate of reduction has been correlated with such parameters as copper and hydrogen ion concentration, geometric factors, flow rate, and temperature. The character of the precipitated copper as a function of flow conditions and rate of PreciPitation has been observed under a variety of conditions. ThE precipitation of copper in solution by cementation on a more electropositive metal has been known for many years. Basile valentine' who wrote Currus Triumphalis Antimonii about 1500, refers to this method for extraction of copper. Paracelsus the Great2 who was born about 1493 cites the use of iron to prepare Venus (copper) by the "rustics of Hungary" in the "Book Concerning the Tincture of the Philosophers". Agricola3 in his work on minerals (1546) tells of a peculiar water which is drawn from a shaft near Schmölnitz in Hungary, that erodes iron and turns it into copper. In 1670, a concession is recorded4 as having been granted for the recovery of copper from the mine waters at Rio Tinto in Spain, presumably by precipitation with iron. Much has been published in recent literature on the recovery of copper by cementation, the majority of the articles being on plant practice.5-24 The rest include articles on investigation of the variables involved25-28 and a review of hydrometallurgical copper extraction methods." This literature has established: a) The three principal reactions in the cementation of copper are Cu + Fe — Fe+4 +Cu [ 11 One pound of copper is precipitated by 0.88 lb of iron stoichiometrically. In actual practice about 1.5 to 2.5 lb of iron are consumed. 2Fe+3 + Fe — 3Fe+2 [21 Fe +2H'-Fe+2 + H2 [3] Reactions [2] and [3] are responsible for the consumption of excess iron. Wartman and Roberson'28 have established that Reactions [ I] and [2] are concurrent and much faster than Reaction [3]. b) Acidity control is important in the control of hydrolysis and the excessive consumption of iron. he commercial workable range is approximately from pH = 1.8 to 3." c) Iron consumption is closely related to the amount of ferric iron in solution. Jacobi" reports that, by leaving the pregnant mine waters in contact wi th lump pyrrhotite (Fe7S8) for 3 hr, all the iron was reduced to the bivalent condition and scrap iron consumption was cut to 1.25 lb scrap per pound of copper precipitated. He also reported that SO2 has been used successfully to reduce ferric iron to the ferrous state. d) The ideal precipitant is one that offers a large exposed area and is relatively free of rust. e) High velocities and agitation show a beneficial effect upon the rate of precipitation, as it tends to displace the layer of barren solution adjacent to the iron and also dislodges hydrogen bubbles and precipitated copper to expose new surfaces. Little work, however, has been published on the reaction kinetics of copper precipitation on iron. Cent-nerszwer and Heller20 investigated the precipitation of metallic cations in solutions on zinc plates. They found the cementation reaction to be a first-order reaction. The rate constant was independent of stirring for high stirring rates and they concluded that the rate is governed by a diffusional process at low stirring speeds and by a "chemical" process at higher stirring speeds where the rate reaches a constant value. This conclusion has been challenged by King and Burger30 who could not find any region where the rate was independent of the stirring speed, although the rate constant they had obtained for high stirring speed was greater than the maximum value of the rate constant reported by Centnerszwer and Heller (by a factor of six). King and Burger, therefore, concluded that the rate of displacement of copper was controlled only by diffusion. Cementation of various cations on zinc has been summarized by Engfelder.31 APPARATUS A three-necked distillation flask of 2 000-mm capacity was used as a reaction vessel. A pipet of 10-mm capacity was introduced through one of- the side necks, the sample of sheet iron, mounted in a rigid sample holder, through the other, the stirrer being in the middle as shown in Fig. 1. The whole assembly was immersed in a constant-temperature bath. The stirrer was always placed at the same depth in the solution. EXPERIMENTAL PROCEDURE Reagent-grade cupric sulfate (J. T. Baker Chemical Co., N.J.) was used to make up a stock solution containing 10 g of copper per liter which was then diluted to various concentrations as required. Experimental data were obtained by measuring the amount of copper and iron ions in solution at successive time intervals. The initial volume of the solution was always 2000 ml, 10-ml aliquots being removed each time for chemical analysis. Because the total volume change of the solution was less than 10 pct, no correction was used for solution volume change. Nitrogen was bubbled through the solution before and

Jan 1, 1968

By E. W. Shaw

Continued discussion of the paper of Roswell H. JOHNSON, presented at the New York meeting, February, 1915, and printed in Bulletin No. 98, February, 1915, pp. 221 to 226. See also Bulletin No. 101, May, 1915, pp. 1157 to 1162. E. W. SHAW, Washington, D. C. (communication to the Secretary+). -With the word petrology-literally the science of rocks-being used primarily for igneous rocks, and with geophysics coming to mean the study of lavas and the rocks into which they solidify, contributions to the knowledge of the physical chemistry of sedimentary rocks, even though only ideas which may be used as working hypotheses, become most welcome. The forces which control the formation and subsequent history of the stratified portions of the earth's crust are so little known that no one has yet been able to settle finally the questions as to whether petroleum is of organic or inorganic origin; whether it originated far from its present position, or nearby. Yet both the chemical and physical problems of the rocks in which oil occurs seem to be more simple than those of the igneous rocks. The oil-bearing rocks of western Pennsylvania, for example, have in all probability never been subjected to a pressure exceeding 3,000 or 4,000 lb. to the square inch, nor to a temperature higher than 100° or 200° C. These pressures are considerably below the crushing strength of rocks, and the temperature far below their melting point. The igneous rocks,, on the other hand, have been affected by enormous pressures and very high temperatures and yet steady progress is being made in reproducing in the laboratory the conditions of their formation and subsequent modification within the earth. The solution of the sedimentary-rock problems would seem to be fully as important as those of igneous rocks, and yet we must content ourselves with reasoning backward and our inferences as to what has happened are oftentimes little more than guesses.1 One of the fundamental problems is the origin of the salt water in oil fields. Is the salt water fossil sea water; has it been formed by the solution o-f salts of various kinds from distinct beds, from disseminated par-ticles, and from the weathering of suitable grains in the rock; or is it of deep-seated origin? Its general resemblance to sea water points to the first, but the principles held by some concerning the free circulation of water throughout the earth's crust, and certain peculiarities of composition indicated by the few analyses available, seem out of harmony with such an explanation.

Jan 7, 1915

By H. D. Kessler, R. J. Van Thyne

Phase diagrams of the titanium-rich portion of the ternary systems from 0 to 10 wt pct Al and 0 to 1 wt pct 0, N, and C were determined. Micrographic analysis of annealed high purity arc melted alloys was the principal method of investigation and was supplemented by X-ray diffraction. TITANIUM-ALUMINUM alloys exhibit excellent properties, particularly for elevated temperature use. For this reason, the Materials Laboratory, Wright Air Development Center, sponsored an investigation of the effect of the interstitially soluble contaminants, oxygen! nitrogen, and carbon, on the Ti-A1 system. Using high purity arc melted alloys and micrographic analysis of annealed samples as the chief method of investigation, titanium-rich partial phase diagrams were determined for the ternary systems. Experimental Procedure Materials: The titanium used in the preparation of the alloys was iodide crystal bar (99.9+ pct pure) produced by the New Jersey Zinc Co. and Foote Mineral Co. The aluminum was obtained from the Aluminum Co. of America in the form of sheet. The given analysis was: Si, 0.0006 pct; Fe, 0.0005; Cu, 0.0022; Mg, 0.0003; Ca, <0.0006; Na, <0.0005; and Al, 99.99. High purity titanium dioxide purchased from the National Lead Co. was used in the preparation of the oxygen-bearing alloys. The spectrographic analysis of this material was as follows: SiO,, 0.07 pct; Fe,O,,, 0.002; A1,0,, <0.001; Sb,O,, <0.002; SnO,,, <0.001; Mg, <::0.001; Cb, <0.01; Cu, 0.0004; Pb, 0.002; Mn, <0.00005; W, <0.01; V, <0.002; Cr, <0.002; Ni, <0.001; and Mo, <0.002. Special spectroscopic graphite rod purchased from the National Carbon Co. was used in the preparation of the Ti-A1-C alloys. Alloy Preparation: Alloy ingots weighing 10 grams were melted in a nonconsumable tungsten electrode arc melting furnace using water-cooled copper hearths and a helium atmosphere. The arc was struck on a tungsten stud in the copper block to minimize contamination from the electrode. Details of the techniques have been reported.&apos;, &apos; Each ingot was inverted and remelted a minimum of four times to insure homogeneity, without opening the furnace. Remelting small control ingots of iodide titanium under similar conditions resulted in no measurable hardness increase, indicating contamination-free melting conditions were used. The alloy charges and resultant ingots were weighed to the nearest milligram. Only small weight losses were obtained upon melting, indicating that the actual compositions were very close to the nominal compositions. Check analyses substantiated this. Oxygen and nitrogen were added during ingot preparation as master alloys. An oxygen master alloy containing 25 wt pct 0 was prepared by melting iodide titanium and pressed titanium dioxide (40 pct 0) powder. The Ti-25 pct 0 alloy is more easily handled during weighing and charging than the pressed TiO, powder. Chemical analysis indicated that titanium-nitride received from an outside source contained large amounts of impurities (2.7 pct Ca). Therefore, a master alloy containing approximately 12 pct N was prepared by melting nitrided sponge titanium. As the sponge melted with difficulty, the alloy was diluted by addition of titanium to lower the melting point. The chemical analysis of the final alloy was 6.69 pct N. Both master alloys are friable and were used as —8 +16 mesh lumps resulting from crushing the ingots. NIelting the Ti-A1-0 and Ti-A1-N compositions five times produced homogeneous ingots. The preparation of homogeneous carbon-bearing alloys caused considerable difficulty. Alloys containing less than 1 pct C were prepared using spectrographic graphite rod, 1/8 in. diameter by 1/8 in. long. However, the graphite did not dissolve even with long melting times and many remelts. The ?/s in. pieces of graphite were used rather than powder because the low density powder is troublesome in arc melting.

Jan 1, 1955

By R. Sprycha, J. Szczypa, W. Janusz, J. Neczaj-Hruzewicz

INTRODUCTION Because large aqueous suspensions of various fine solids originate during the beneficiation of ores, the Mining Industry constantly requires efficient and feasible dewatering methods. Among the techniques currently in use (1,2), filtration (vacuum, press) and centrifugation are fairly expensive and thus are limited to use with more valuable materials. Furthermore, installations of reasonable size produce only moderate outputs. Therefore, tailings from ore dressing plants are usually treated by sedimentation or settling techniques with a tailings dam as the ultimate sedimentation basin (3). Apart from growing environmental and economic questions, the solid product obtained from the tailings dam basin has in most cases, a rather high moisture content and a persistent semi-fluid consistency. Thus, it is difficult to transport and use further. On the other hand, the solids may be utilized as a filling material, fertilizer, etc. providing they are dry enough and properly granulated. Demands for an improved technique are met to a great extent, by the technique presented in this paper. AGGLOMERATION OF FLOCCIJLATED SLIMES Origin and Qualitative Description of the Process Phenomena of consolidation and pellet formation in flocculated fines were first observed by Yusa and Gaudin (4) while studying rheological properties of flocculated kaolinite. On this basis, methods of separating liquid from solids have been worked out (5-7) and many possibilities for application have been suggested (5,6). Yusa termed the technique "wet pelletization&apos;&apos;.

Jan 1, 1980

By A. H. Larson, R. J. McClincy

The activity of Sb,03 in PbO-Sb,03 slags containing less than 50 mol pct Sb,03 was determined by the inert-gas saturation method at 700°C. In this composition range, the activity gf SbzO3 shows a strong negative deviation from ideality. The activity of PbO in these slags was calculated by application of the Gibbs-Duhem iniegration to the Sb203 activity data. The calculated activity of PbO in slags containing more than 63 mol pct PbO was found to deviate in a positive direction from ideality uthile a negative deviation was found for slags containing less PbO. The standard Gibbs free energies of formation of Sb,03 and PbO. Sb203 have been calculated and compared with existing data in the literature. The activity of Sb203 in PbO-Si0,-Sb203 (PbO/SiO, = 2) slags containing less than 25 mol pct Sb,03 was also determined by the inert-gas saturation method at 700°C. In this composition range, the activity of Sbz03 shows a very large negative deviation from ideality. VERY little experimental work has been published in the past to determine equilibrium data in the oxide systems connected with the refining of lead. These data are of value since impurities such as antimony, arsenic, and tin must be removed from lead and recovered for further treatment. Equilibrium studies on antimony and arsenic systems are also of interest for the design of new processes for lead refining and lead dross treatment. Maier and ~incke&apos; first determined the liquidus curves for the PbO-Sb203 system and identified the compound PbO . Sb203. They found the phase diagram for this system to be two simple eutectics located on either side of the congruent melting compound. They also determined a very limited amount of vapor pressure data for Sb406 abbve PbO-Sba3 melts at 697"~. A second phase diagram investigation on this system was reported by Hennig and Kohlmeyer&apos; who confirmed the existence of the compound PbO . Sb203 as well as the form of the diagram. A disagreement was noticed, however, in that their liquidus temperatures over nearly the entire composition range were higher than those reported by Maier and Hincke. Barthel~ and pelze14 redetermined the liquidus curve at the PbO-rich end of the PbO-Sb@, system and agreed very closely with the results of Maier and Hincke. None of the investigators mentioned above reported any mutual solid solubility in the PbO-SbD3 system. Zunkel and Larson5 have determined the phase diagram for the PbO-rich end of the PbO-Sb203 system by slag-metal equilibrium studies in the Pb-PbO-Sb203 system and by thermal analysis studies in the PbO-Sbz03 system. A maximum solid solubility of 5.6 mol pct Sb203 in PbO was observed at the eutectic temperature of 604°C. Their results for the phase diagram agree favorably with those of Maier and Hincke. The vapor pressure of Sb2O3 in the temperature range from 470" to 800°C has been determined by Hincke, using a modification of the transportation meth~d.~ His results for temperatures below the melting point of Sba3 are the only data reported in the published literature. The predominant vapor species has been shown to be Sb,06 by Norman and staley.? Myzenkov and Klushin,8 using the boiling-point method, have determined the pressure of Sb406 above liquid SbD3 in the temperature range from 715" to 1025°C. The agreement between these two studies is not very close. A portion of the discrepancy lies in the fact that Hincke used silica crucibles, which were attacked by the liquid Sbz03 at high temperatures. This fact does not account, however. for the large difference observed at the melting point. ~aier&apos; gives a brief summary of vapor pressure data for Sb,O, above pure liquid Sbz03 which agree quite well with the data of Myzenkov and Klushin at temperatures near the melting point. This paper describes the determination of Sb2O3 activity data in the PbO-Sb203 and Pb0-Si02-Sb203 (PbO/SiOz = 2) systems by the inert-gas saturation method. These activity data are compared with the data calculated by Zunkel and arson. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade PbO (99.8 pct PbO, 0.14 pct insoluble in CHsCOOH, 0.02 pct not precipitated by HB, 0.1 pct CaO, and 0.08 pct SiOz), Sbf13 (99.6 pct Sb203, 0.004 PC~ C1-, 0.005 PC~ SO;-, 0.15 p~t AS, 0.001 pct Fe, and 0.03 pct other heavy metals such as Pb), and SiOz (chromatographic grade). Apparatus for Vapor Pressure Determinations. The apparatus used in this investigation consisted of a transportation reaction system with two separate gas trains. The argon transporting gas was first mixed with a small amount of hydrogen, metered, and dried by passage through silica gel and anhydrone drying tubes arranged in series. After this preliminary drying, the argon was passed through copper wool at 500°C to convert the residual oxygen to water vapor which was removed by three anhydrone drying tubes. A second stream of argon was metered and dried and then passed around the outside of the alumina reaction tube to flush away the volatile species to pre-

Jan 1, 1970

By Elliot P. Rexford

B. C. Burgess-—Prior to hearing this paper presented at the San Francisco meeting, I travelled by car from Yuma, Ariz., across south-central California and up through the San Joaquin Valley. After hearing the paper I returned by the coast route to San Diego then along the Mexican border to Yuma. The striking feature of these trips, related to this paper, was the dry river and creek beds at a time of year not the dry season. Contrasted with this was the wasteful use of water in irrigation canals and laterals. Poland says "at least 90 pct of the ground water pumped is used for irrigation." That being the case, it would appear that first consideration should be given to conservation of this use. Probably a small part of this is actually reaching the plants. Some measure of this loss between pump and crops would be revealing. Methods that might be employed to reduce this loss are pipe lines and spraying of some crops such as the banana planters are using in Central America. Another idea which might be investigated is to line canals and ditches with some water-repelling mineral like pyro-phyllite. Perhaps a comparatively thin sprayed-on

Jan 1, 1951

By Elliot P. Rexford

B. C. Burgess-—Prior to hearing this paper presented at the San Francisco meeting, I travelled by car from Yuma, Ariz., across south-central California and up through the San Joaquin Valley. After hearing the paper I returned by the coast route to San Diego then along the Mexican border to Yuma. The striking feature of these trips, related to this paper, was the dry river and creek beds at a time of year not the dry season. Contrasted with this was the wasteful use of water in irrigation canals and laterals. Poland says "at least 90 pct of the ground water pumped is used for irrigation." That being the case, it would appear that first consideration should be given to conservation of this use. Probably a small part of this is actually reaching the plants. Some measure of this loss between pump and crops would be revealing. Methods that might be employed to reduce this loss are pipe lines and spraying of some crops such as the banana planters are using in Central America. Another idea which might be investigated is to line canals and ditches with some water-repelling mineral like pyro-phyllite. Perhaps a comparatively thin sprayed-on

Jan 1, 1951

By N. Van Wingen, Norris Johnston

Laboratory flood pot testing of California sands has progressed to a considerable extent in the past 18 months. Flood evaluations have been carried out on over 200 large core samples. Many of these were heavy oil sands of high permeability and completely unconsolidated in nature. The oil frequently formed a bank, though some of the oil was recovered in the subordinate phase of the flood, by viscous drag. Flood pot recoveries as high as 1400 bbl/acre ft have been recorded. Reservoir analysis suggests a conformance factor of 0.4 to reduce laboratory recovery to probable field practice. Oils with viscosities up to 1800 cp have been successfully handled in flood pot evaluations. The shallow, loose sands are not well adapted to the application of- high pressures to offset the high viscosities. INTRODUCTION Secondary recovery may be said to have started 60 years ago when accidental floods occurred in the Bradford sand in Pennsylvania. About 1921 artificially conducted water drives came into extensive use and since that time the great Bradford field has been almost completely subjected to water flooding. During the last 30 years, most of the known medium and deeper production in California has been discovered and is being exploited by primary recovery methods supplemented in some instances by high pressure gas injection. The California area is just beginning to feel the need for secondary recovery in view of an unprecedented market demand and the rapidly rising cost of new pool discoveries. With the presently recognized desirability of secondary recovery in California, there must also be appreciated a number of serious differences between the water flooding problems here as compared to the territory east of the Rockies. California sands are generally thicker, and are frequently soft and argillaceous. The oils are often heavier and asphaltic. Much of the oil is below 15°API, occurs at shallow depth, is cool and free from appreciable dissolved gas, which results in relatively high reservoir oil viscosity. Secondary recovery is particularly beneficial where primary recovery has been poor and where no natural water drive exists. These conditions apply particularly to the heavy, shallow, clean production from soft, often argillaceous California sands so abundantly found at depths less than 1500 feet. Often, too, there is a totally insufficient supply of water of satisfactory quality to inject at a reasonable cost. Also, the crude oils are priced far below the premium Bradford crude. Although these and a number of minor problems beset the operator desirous of starting secondary recovery, great progress has been made in the past few years in finding how to adapt previous Mid-Continent and Eastern experience to water flooding in California. There are about nine projects for subsurface injection of water which can be said to classify as secondary recovery operations. Subsurface water disposal would so classify when the sand receiving the water is a nearby oil producer, as is often the case. When water is injected subsurface into a barren sand, the operation does not classify as secondary recovery. Several of the most active operators avail themselves extensively of preliminary engineering and laboratory work to guide their decisions, while others enter small scale flooding operations directly in the field. It is the laboratory work pertinent to several of the California secondary recovery projects that this paper discusses. PURPOSES OF LABORATORY FLOODING TESTS Experience in areas where water flood operations have been carried out has indicated that careful engineering planning is an important requisite for subsequent economically successful field operation. Floods that fail are more frequently those where operations were instigated without a prior engineering investigation to determine the effectiveness of the injection fluid as an oil displacing medium. Laboratory data are essential in the evaluation of an oil property for secondary recovery possibilities. Success or failure of secondary operations can under certain special circumstances be determined directly by cores and their subsequent routine analysis. This is particularly the case where flushing of the cores in the course of coring is negligible and where the results of the analysis can be compared with existing secondary recovery operations. Where these conditions cannot be&apos; fulfilled, the application of core analysis is more limited. In such event, the results obtained by water flooding core samples in the laboratory have been found to be of prime importance. Cores may be flooded "raw" as taken from the well or in the event flushing and depletion of the cores in the process of drilling are major factors the fluid content may be artificially restored prior to the flooding. Laboratory studies should also be made to determine the suitability of the water selected for injection. Thus interaction between injected and formation water may cause precipitates to be formed which may plug the sand. Even more important, especially to California operations, is the possibility of the hydration of formation clays by the injection water. The aims of flood pot and associated tests are basically to determine the residual oil saturation after flood, the water-oil throughput ratio and to establish whether an oil bank is formed. Additional information which can be obtained from flood pot tests pertains to the pressure differential required to effect displacement, the relative permeability to oil in the oil bank and the relative permeability to water in the watered out region behind the bank.

Jan 1, 1953

By G. S. Brooks, L. G. Duncan

During the past few years, the Mineral Point Zinc Co. has had under consideration the improvement of various types of gas-filtering apparatus used in the removal of dust from crushing and milling plants, in the manufacture of oxide, and on blast-furnace fume and sintering furnaces. The original equipment of the various plants of the company was, of course, along lines of the standard stationary bag house. These houses required large surfaces, hand shaking, and varied only in the manner of the collection of solids and in the distribution of the gas. , Early in 1908, the first trial of a mechanical bag house was made at Nassau Plant at Depue, Ill. The duty of this installation was on dust-laden gas from a fine-crushing mill. The Printz and Rau bag machine was finally adopted and put into operation. This ingenious machine embodied what were then to us two novel features in bag-house practice: 1. An intermittent crinkling and snapping of the filtering fabric to free the meshes of solids. 2. A reversal of gas flow for a short period by a temporary connection with the suction trunk. This equipment worked fairly well except in cold weather, when we ran into condensation troubles. Had we at that time understood more fully some of the limitations of fabric filtering work, these might well have been remedied. We were impressed by this experience, however, with the efficiency of sudden tension on the fabric under suction. After a study had been made of some of the western blast-furnace houses using the reversal-of-flow feature, experiments were started early in 3 914 with a view to developing an automatic equipment along the best lines of our past experience. The objects sought were: 1. Keeping labor out of the houses for hygienic reasons. 2. Reduction of labor costs. 3. Reduction in size of bag houses. 4. Accessibility. 5. Ability to handle relatively hot gases where required.

Jan 1, 1918

By C. D. King

The advances in basic open-hearth practice which have occurred during the past decade have been principally in the direction of the physical development of larger units, decreased fuel consumption and increased length of furnace campaigns. However gratifying the economies which have resulted from these improvements are, it must be granted that like advances in chemical, physical-chemical and metallurgical knowledge pertaining to open-hearth practice would have added greatly to these already attained reductions in costs and it is the purpose of this paper to stimulate the discussion and study of these phases of cooperation and their relation to ingot yields. Definition and Calculation oF Losses In discussing basic open-hearth yields, the writer refers to the ingot yields obtained in the process of converting pig iron, scrap and ore to steel. In this conversion some scrap is produced. The difference between the total weight of ingots and scrap produced and the original metallic charge constitutes the loss. Basic open-hearth yields vary considerably, and while some of the divergencies can be explained metal-lurgically because of differences in slag analysis, proportion of pig charges, and character of steel made, there often remain differences that apparently do not readily disclose themselves. In reconciling yields by the usual accepted methods of calculation, one is often forced to evaluate large losses as ((unaccounted for." Such a system is prone to accept these large losses as inherent to the operat.ion and not, susceptible of appraisement and correction. It is obvious that if the ingot yield plus the scrap recovered subtracted from 100 per cent. determines the loss, a drop in yield may increase the loss or the scrap, and both contribute to a monetary loss. To be sure, one can subdivide these unaccounted for losses into various components, such as metallics in slag, free Fe in slag, spillage, etc., and thereby reduce the amount of losses considered as "unaccounted for." If empirical methods could indicate with some degree of accuracy all losses, however slight, the undetermined losses become appreciably smaller and resultant calculations will check actual

Jan 1, 1929

By P. E. Doherty, B. Chalmers

Subboundaries may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits do not form in the vicinity of high- or low-angle boundaries. They are attributed to the condensation of vacancies from a super saturation produced during coolirzg. Using the vacancy pit and Schulz X-ray techniques for observing low-angle boundaries, a study was made of the transition from the nearly perfect seed to the striated structuke characterist-ic of aluminum crystals grown from the melt. It was found that the individual striation boundaries develop by the coalescence of very small-angle boundaries, as well as by the addition of individual dislocations. Several mechanisms for the formation of striations are discussed. Evidence was found suggesting that a super-saturation of vacancies exists near a growing interface, and it is proposed that the resulting climb of existing dislocalions produces "half&apos;-loops" at the interface, which combine to form the low-angle striation boundaries. LINEAGE, or "striation" boundaries, have been studied in detail by Teghtsoonian and Chalmers 1,2 in crystals of tin grown from the melt, and by Atwater and Chalmers3 in lead. They found that single crystals grown from the melt consist of regions which are separated by subboundaries that lie roughly parallel to the growth direction. A difference in orientation of 0.5 to 3 deg exists between the striated regions; the misorientation is such that the lattice of one region could be brought into coincidence with the lattice of its neighbor by a rotation about an axis approximately parallel to the direction of growth of the crystal. They observed an incubation distance for the formation of striations which increased with decreasing growth rate. They also found that in any crystal, the sum of all rotations of the lattice in one sense, in going from one striation to the next, is very nearly equal to the sum of all the rotations in the opposite sense. A striation boundary, which is a low-angle grain boundary, can be described as an array of dislocations. If it is assumed that suitable dislocations are introduced into the crystal during solidification, the formation of striation boundaries can be explained as a result of the migration of the disloca- tions into arrays. The formation of arrays is energetically favorable since the energy of an assembly of dislocations can be reduced by the interaction of the stress fields when a suitable array is formed. This investigation presents and interprets new information concerning the nature and origin of striation boundaries in aluminum. EXPERIMENTAL TECHNIQUE Single crystals of high-purity aluminum (Alcoa 99.992 pct) were prepared by horizontal growth from the melt.&apos;&apos; The specimens were subsequently electropolished in a solution of 5 parts methanol to 1 part perchloric acid kept between -10° and 0°C in a bath of dry ice and alcohol. The current density was approximately 6 amps per sq in. Doherty and Davis9 have shown that in aluminum sub-boundaries with misorientations of not less than several seconds of arc may be revealed by the vacancy pit technique. During cooling from elevated temperatures pits form on electropolished surfaces of aluminum crystals as a result of the condensation of vacancies.11 Pits do not form in the vicinity of small- or large-angle grain boundaries, presumably because such boundaries act as sinks for vacancies. Boundaries of misorientations down to 3 sec of arc are revealed as pit-free regions, see Fig. 1. The Schulz X-ray technique12 was used to determine the angular misorientations of subboundaries. In this method, white radiation from a micro-focus X-ray tube is used to produce an image of a fairly large area of a single crystal surface. Subboundaries cause splitting in the diffracted image, see Fig. 2. Misorientations down to about 15 sec of arc may be observed with this technique. OBSERVATIONS AND DISCUSSION Figure 1 shows a striated aluminum crystal grown at 10 cm per hr etched by the vacancy pit technique. An incubation distance of about 1 cm is observed before the initiation of striation boundaries. Fig. 2 is a Schulz X-ray photograph of a striated crystal similar to that shown in Fig. 1. A large area of the crystal was studied by means of a series of photographs. Fig. 2, which is a reflection from the (100) plane, included about the first 4 cm of crystal to freeze. There is an incubation distance of about 1 cm, and a distance of about 2 cm over which the angle of misorientation builds up to its final value of approximately one degree. Some twist component can be seen in Fig. 2 at the right side of the photograph. From Fig. 2 it can be seen that the sum of all rotations of the lattice in one

Jan 1, 1962

By A. L. Marshall, F. J Norton

The object of this investigation was to make a comprehensive study of the degassing of molybdenum in order to determine how rigorous a treatment was necessary to completely remove sorbed gases from molybdenum electrodes in vacuum tubes. Some work has also been done with tungsten, nickel, iron and carbon. As a logical development of this work it has been shown that the gas is present throughout the body of the metal and a study has been made of the solubility of nitrogen in molybdenum and tungsten and the rate, of diffusion of nitrogen through molybdenum has been calculated. Tests were made on molybdenum from all the commercial sources and no difference was discovered in the nature of the gases present, the amounts or the ease of removal. The reason for this was apparent when a study was made of the manner in which gases are absorbed by gas-free molybdenum. It is necessary to heat molybdenum to 1760°C. in a vacuum of the order of 0.001 micron for a time which varies lineally with the thickness, in order to obtain a condition in which no further gas is evolved by the sample. A sample so degassed can be handled and subsequently assembled in a tube and then degassed readily. The gases obtained from molybdenum are carbon monoxide and nitrogen, the nitrogen being the more difficult to remove. Apparatus and Technique The apparatus is shown in Figs. I and 2. It consisted of two units, a degassing system and an analytical system. Each had a bake-out oven, as shown surrounding the systems in the sketches. The system , will be traced, starting from the sample in the degassing system. A water-cooled quartz chamber surrounded the sample. The high-frequency coil, which heated the sample, extended only around this chamber and was cooled by an air blast. High-frequency power of 1800-meter wave length was obtained from a self-rectifying oscillator circuit with a maximum power input of 20 kw. A graded seal connected the quartz to the rest of the apparatus, which was of hard glass. The temperature of the molybdenum sample was observed by an optical pyrometer through an optical window about 40 cm. distant from the sample. Since the object viewed under these conditions was not a black body, true temperature was not observed, but the so-called "brightness temperature." The correction of this to true temperature is discussed in a later section. The apparatus was taken apart just above the graded seal; the quartz chamber was slipped off, washed with nitric acid, water and alcohol, and dried by an air stream. The old sample was removed by unscrewing the lower nut, and the new

Jan 1, 1944

By A. L. Marshall, F. J. Norton

The object of this investigation was to make a comprehensive study of the degassing of molybdenum in order to determine how rigorous a treatment was necessary to completely remove sorbed gases from molybdenum electrodes in vacuum tubes. Some work has also been done with tungsten, nickel, iron and carbon. As a logical development of this work it has been shown that the gas is present throughout the body of the metal and a study has been made of the solubility of nitrogen in molybdenum and tungsten and the rate, of diffusion of nitrogen through molybdenum has been calculated. Tests were made on molybdenum from all the commercial sources and no difference was discovered in the nature of the gases present, the amounts or the ease of removal. The reason for this was apparent when a study was made of the manner in which gases are absorbed by gas-free molybdenum. It is necessary to heat molybdenum to 1760°C. in a vacuum of the order of 0.001 micron for a time which varies lineally with the thickness, in order to obtain a condition in which no further gas is evolved by the sample. A sample so degassed can be handled and subsequently assembled in a tube and then degassed readily. The gases obtained from molybdenum are carbon monoxide and nitrogen, the nitrogen being the more difficult to remove. Apparatus and Technique The apparatus is shown in Figs. I and 2. It consisted of two units, a degassing system and an analytical system. Each had a bake-out oven, as shown surrounding the systems in the sketches. The system , will be traced, starting from the sample in the degassing system. A water-cooled quartz chamber surrounded the sample. The high-frequency coil, which heated the sample, extended only around this chamber and was cooled by an air blast. High-frequency power of 1800-meter wave length was obtained from a self-rectifying oscillator circuit with a maximum power input of 20 kw. A graded seal connected the quartz to the rest of the apparatus, which was of hard glass. The temperature of the molybdenum sample was observed by an optical pyrometer through an optical window about 40 cm. distant from the sample. Since the object viewed under these conditions was not a black body, true temperature was not observed, but the so-called "brightness temperature." The correction of this to true temperature is discussed in a later section. The apparatus was taken apart just above the graded seal; the quartz chamber was slipped off, washed with nitric acid, water and alcohol, and dried by an air stream. The old sample was removed by unscrewing the lower nut, and the new

Jan 1, 1944

By F. C. Newton

RefineRs of lead by the Parkes process have always been solicitous of recovering the zinc used in the desilverization, and justly so, as the loss in zinc constitutes one of the heavy costs in this method of refining. Part of this loss is due to the absorption of zinc by lead, and in the present state of knowledge is not recoverable as metallic zinc. The remainder of the zinc, which finds its way into the precious-metal-bearing crust, is recoverable and naturally engages the operators&apos; most exacting attention. Careful elimination of the impurities in base bullion has enabled the refiner to produce a zinc crust better adapted to retorting, which reflects favorably in the zinc recovery;- and to produce a richer crust, thereby lowering the zineking cost, as the increased efficiency of the zinc results in less of it being in circulation. It is obvious that if the ratio of concentration be increased, a lessening of the amount of crust formed will ensue, throwing less work on the retorts and diminishing the amount of retort metal sent to the cupels, thus making an actual money saving in all these operations. In the effort to obtain a rich crust, the metallurgist has increased the heat to a considerable degree, upon the assumption that at the higher temperature the zinc-dver alloy could be squeezed free from the adhering lead. A further possibility for improvement suggested itself in the freezing-point curve of Prof. H. C. Carpenter, upon zinc and silver. Study of this curve disclosed the existence of a definite chemical compound, Zn3Ag2, with a freezing point of 665" C., a promising compound for practical application. In the experiment undertaken it was endeavored to force this compound into the crust, hoping thereby to obtain a higher concentration than formerly. It was recognized that in bringing a large kettle of lead to such a heat, more fuel would be used, the life of the kettle would perhaps be shorter, and other disadvantages would be experienced. AS a commercial operation, the project would have to stand on its own feet,

Jan 1, 1915

By Howard R. Hughes

In drilling for water and oil to reasonable depths through the generally soft yielding clay and sand formation of the Coastal Plain of Texas, Louisiana, and Mississippi, the rotating method of drilling was adopted, principally on account of the easy and quick penetration, and the low cost of the drilling plant. In favorable ground, free of heavy gravel and rock strata, as much as 1,600 ft. has been drilled in less than 36 hr., although such performances were of course rare. Hydraulic rotary drilling, or, as it is now called, rotary drilling, was used in the above States as early as 1880. The plant consisted of an ordinary derrick, a 25-h.p. boiler, a small hoist, a steam pump, and a water swivel with hose attachment, and an ordinary flat diamond-pointed bit. The successful drilling in of a phenomenal oil well by this process on Spindletop, near Beaumont, Texas, on Jan. 10, 1901, and the ascertained impracticability of drilling subsequent wells in the same locality by other methods (owing principally to heavy quicksand under pressure from below), brought rotary drilling into great prominence, practically to the exclusion of any other process throughout the Coastal Plain, and later on elsewhere. The method, as its name implies, involves the rotation of a pipe by means of machinery placed on the derrick floor. A drill bit attached to the lower end cuts a clearance for the drill pipe, with much the same motion and effect as an auger. Water forced through the drill pipe by means of a pump, and escaping through the bit, removes the cuttings and returns to the surface outside the drill pipe. In this manner the hole is kept open, permitting the drill stem to rotate freely. The pressure of the column of muddy water holds up the walls of the hole until it has been cased. Practically all the wells of the Gulf coast region, numbering nearly 10,000, have been drilled with this system. During the last five years its use has been extended to many other States and countries.

Jan 1, 1915

By W. L. McMorris

The Convertol process was first described in Germany by Muschenborn&apos; in 1952. In the U. S. Fraser&apos; reported this new process in 1953, and Brisse and McMorris" presented the results of a Convertol pilot plant at the Alpheus preparation plant in Gary, W. Va., illustrating the mechanics of the process by a series of sketches. The purpose of the present investigation was threefold: 1) to determine the relative effectiveness of various oils and hydrocarbons for recovering coal by the Convertol process, 2) to ascertain the behavior of coal pulps in this process under various operational conditions, and 3) to compare Convertol with flotation in the recovery of fine coals. APPARATUS, PROCEDURE, AND COAL SAMPLES In laboratory work with the Convertol process a Waring Blender equipped with a speed-regulating rheostat was used for wetting, conditioning, inversion, and retention of the coal pulp. A 5-in. International centrifuge was adapted to dewater the agglomerated clean coal product by installation of a 100-mesh screen inside the regular bronze basket of the centrifuge. Except where otherwise stated, the Convertol testing was performed by the following steps: 1) A 450 to 500-cc coal slurry, containing 24 pct by weight of solids, was agitated in the blender for 10 min at 100 rpm to insure complete wetting and mixing. 2) Eight percent by weight of oil was added to the coal slurry in the blender and agitated for 1 min at 11,000 rpm to result in the phase inversion or agglomeration of oil-coated coal particles. 3) The agglomerated coal slurry was poured onto a 100-mesh sieve and wet-screened for about 2 min to remove most of the ash and some of the water. 4) The material remaining on the screen was transferred into the centrifuge for final dewatering. 5) A portion of the clean coal was immediately weighed out for moisture determination, while the

Jan 1, 1960

By Auguste J. Rossi

We cannot expect, within the limits of this paper, to treat this subject exhaustively, but will endeavor, in the following, to present it in as concise a manner as is consistent with a clear exposition of its importance. Ores of titanium, titaniferous iron-ores (that is, iron-ores containing a notable amount of titanic acid, TiO2,, say not less than 5 per cent., generally 10 to 20 per cent., and frequently more, up to 40 per cent. or thereabout), occur all over the world in immense quantity, " in mountain masses," constituting in some localities, as in Sweden, Norway, Canada, the Adirondacks (N. Y.), in North Carolina and other States of the Union, the geological formation itself, the igneous rocks having, in many places, been so permeated with the metallic oxides as to justify their being called iron-ores. As a rule they are Bessemer ores, quite free from phosphorus and sulphur, though not invariably so. When the percentage of titanic acid is very high, that of the iron is low, but the proportions do not necessarily vary in the same ratio; that is, a rich ore may contain more titanic acid than one lower in iron. The percentage of iron varies, being as low as 35 to 36 per cent. in real ilmenite. It is more generally not less than 50 to 55 per cent., reaching often an average of 58 to 60 per cent., and as high as 63 to 65 per cent. It is obvious that if these ores were to be considered in the same light as other iron-ores, equally rich in iron, they would form an excellent stock for blast-furnaces for years to come, as their supply might be called inexhaustible, and they could

Jan 1, 1903