Jan 1, 1891

By J. Kitagawa

INTRGDUCTION The Paragsha concentrator is the largest of Cerro de Pasco Corporation's base metal beneficiation plants operating in Peru. At present, this plant is treating an average of [ ]

Jan 1, 1970

By W. F. Cloud

The data and information compiled under Part I of this report are the results of experiments performed in the petroleum engineering laboratory under the supervision of W. F. Cloud, Associate Professor of Petroleum Engineering and William Schriever, Professor of Physics, University of Oklahoma. Problems Being Studied Most of the time has been spent in trying to determine the rate of flow and pressure gradient in a 4-in. flow tube 10 ft. long, which was packed with sand of various grain sizes. To date, only two kinds of sand have been packed in this tube: 60 to 80-mesh Canadian river sand, 60 to 80-mesh and 80 to 100-mesh Simpson sand. The original intention was to follow the same procedure and use the same types of crude under identical saturation pressures of both air and gas, as well as unsaturated (dead) oil, flowing the various crudes through several different sizes of both Canadian river and Simpson (Wilcox) sands, but lack of time has prevented such an intensive study of the problem. Some additional time has been spent flowing saturated and unsaturated crudes, similar to those used in the 4-in. tube, through 1-in. tubes, one of which was 2 ft. long and one 5 ft. long. The results obtained have been checked against those obtained by using the 4-in. tube, to obtain the relation of diameter and length of tube to rate of flow in similar sands. Laboratory Equipment Saturation Tank.—A heavy steel cylindrical saturation tank, capacity about 42 gal. was mounted on a platform of bricks, then a galvanized tin temperature bath was built around the saturation tank. This contained

Jan 1, 1930

America.-Foreman, J. T. Ashland.-Sturdevant, J. C. AItalIa. Henderson, R. M. Bessemer.-Ball, E. M. Maschmeyer, W. L. McKenzie, W. C., Jr. Birmingham.-Abbott, C. E. Aldrich, T. H. Aldrich, T. H., Jr Aufderhaar, H. C. Berg, H. A. Blair, C. S. Bush, M. W. Clark, G. H.

Jan 1, 1923

By H. C. George

THE Wisconsin. Zinc District, or the Upper Mississippi Lead and Zinc District as it is often called, lies in the southwestern corner of Wisconsin, in, Grant, Iowa and Lafayette Counties, and it includes adjoining parts of Illinois and Iowa. The district is about 70 miles long, north and south, and about 40 miles wide, east and west. It lies wholly within what is geologically known as the non-glaciated area of the Upper Mississippi Valley. HISTORY OF THE DISTRICT The district was first opened up as a lead producer in 1822. From this time until 1860, about 205,000 tons of cog lead (galena) and washed lead (galena) was produced from shallow crevices and openings. From 1860 to 1900, about 74,500 tons was produced, and since that time, from 5000 to 7000 tons has been produced annually. Since-1900, most of the lead concentrate produced has been as a byproduct of the zinc mines. The first zinc ores were mined about 1862. These were the carbonate ores, locally known as " drybone." Very little zinc blende was mined in the district, previous to 1875. The zinc blende ores mined from 1875 to 1900 were mostly of the high-grade, hand-cobbed, sheet-ore class, which usually contained from 45 to 60 per cent. metallic zinc. Such nines as the "Sallie Waters," ? Quinlin," "Lead Mine," "Benton Blende" and "Ida Blende," located near Benton, Wis., were mines which produced ores of this type, during this period. The mines located at Highland, the "Coker Mine" located at Livingston, Wis., and the "Opencut Mine" located at Shullsburg, Wis., were mines that were heavy zinc carbonate producers, previous to 1900.

Jan 12, 1917

By J. W. Halley, T. S. Washburn

Rimming steels derive their name from their action during solidification in the molds. As a result of incomplete deoxidation, gas is evolved during freezing, and the metal has a characteristic rolling action. The metal rises along the mold walls and descends in the center of the ingot. This action keeps the top of the ingot open and the advancing rim of solid metal can be seen. The rim grows until the rolling action is insufficient to prevent the top of the ingot from freezing or until the action is stopped by capping the ingot with a heavy plate. The violence of the reaction and its characteristics, such as growth or drop in the molds, are determined by the composition, the furnace practice, and the deoxidation in the ladle and in the molds. Though rimming steels represent a large proportion of the amount of plain carbon steel made, they have received comparatively little attention in the technical literature. The manufacture of rimming steels has been described by Hibbard,1,2 Fleming,3 Pierce4 and Jackson.5 The reactions occurring during rimming have been considered from the theoretical point of view by Chipman and Samarin.? The structure of rimmed-steel ingots has been discussed by Nead and one of the present authors6 Meyer: in studying segregation, investigated the distribution of carbon, sulphur and phosphorus in rimmed-steel ingots by analyzing the rim and core of blooms. In their studies of segregation, the Joint Committee of the Iron and Steel Institute and the British Iron and Steel Federation9 studied distribution in one billet and one ingot of rimmed steel. A detailed study of the distribution throughout the ingot has not been published. The present investigation was undertaken to determine accurately the distribution of carbon, manganese and sulphur in normal rimmed ingots and the general distribution of other common elements present. The study included some work on the effect of pouring conditions and furnace practice on the distribution, though there is still much to be done in this direction. The structure of a rimmed ingot that has been split by dynamiting and a schematic diagram of the zones in the ingot are illustrated in Fig. 1.

Jan 1, 1938

By J. W. Halley, T. S. Washburn

Rimming steels derive their name from their action during solidification in the molds. As a result of incomplete deoxidation, gas is evolved during freezing, and the metal has a characteristic rolling action. The metal rises along the mold walls and descends in the center of the ingot. This action keeps the top of the ingot open and the advancing rim of solid metal can be seen. The rim grows until the rolling action is insufficient to prevent the top of the ingot from freezing or until the action is stopped by capping the ingot with a heavy plate. The violence of the reaction and its characteristics, such as growth or drop in the molds, are determined by the composition, the furnace practice, and the deoxidation in the ladle and in the molds. Though rimming steels represent a large proportion of the amount of plain carbon steel made, they have received comparatively little attention in the technical literature. The manufacture of rimming steels has been described by Hibbard,1,2 Fleming,3 Pierce4 and Jackson.5 The reactions occurring during rimming have been considered from the theoretical point of view by Chipman and Samarin.? The structure of rimmed-steel ingots has been discussed by Nead and one of the present authors6 Meyer: in studying segregation, investigated the distribution of carbon, sulphur and phosphorus in rimmed-steel ingots by analyzing the rim and core of blooms. In their studies of segregation, the Joint Committee of the Iron and Steel Institute and the British Iron and Steel Federation9 studied distribution in one billet and one ingot of rimmed steel. A detailed study of the distribution throughout the ingot has not been published. The present investigation was undertaken to determine accurately the distribution of carbon, manganese and sulphur in normal rimmed ingots and the general distribution of other common elements present. The study included some work on the effect of pouring conditions and furnace practice on the distribution, though there is still much to be done in this direction. The structure of a rimmed ingot that has been split by dynamiting and a schematic diagram of the zones in the ingot are illustrated in Fig. 1.

Jan 1, 1938

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.' This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.'" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson' as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, ''p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler's saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By H. Kenyon Burch

PaQe Introduction.............................................................. 708 Plant Sites................................................................ 709 Type of Construction...................................................... 710 Mine Plant............................................................... 710 Dual Arrangement.................................................... 711 Underground Haulage............................................. 711 Tipples........................................................... 712 Underground Pockets............................................. 712 Automatic Measuring and Loading Devices......................... 712 Shafts ............................................................. 716 Ore and Spillage Skips............................................ 716 Automatic Hoists................................................. 716 Man Elevator..................................................... 717 Crushing Plant....................................................... 718 Storage Bin........................................................... 720 Sampling Plant....................................................... 720 Motors and Other Equipment.......................................... 721 Compressor Equipment................................................ 721 Concentrator............................................................. 722 600-Ton Test Mill..................................................... 722 The 15,OO0-Ton Concentrator...................................... 726 Grinding Section.................................................. 726 Floor Arrangement........................................... 726 Marcy Ball Mills............................................. 729 Performance of Crushing Machines............................ 730 Flotation Section.................................................. 780 . Flow-Sheet with Callow Flotation Cells....................... 731 Flow-Sheet with the Inspiration Flotation hfachines............. 731 Flotation Air Supply.......................................... 733 Concentrates Filter Plant.......................................... 733 Drag Classifiers................................................... 733 Tailing Settling System........................................... 735 200-Ft. Dorr Thickener ...................................... 736 General Equipment and Supplies.......................................... 737 Water Supply......................................................... 737 Power Supply......................................................... 737 Transformer Stations.................................................. 738 Shops and Railroad Facilities.......................................... 739 Conclusion................................................................ 740

Jan 1, 1917

By W. B. Finkeldey, C. H. Mathewson, C. S. Trewin

This paper was prepared upon request as a contribution to a symposium covering the manufacture, properties, and uses of the important non-ferraus metals. In approaching a subject as broad as this, there is a natural desire to build up a comprehensive and finished production which shall constitute a dependable source of information on all questions properly belonging to this branch of metal technology. There are, however, a number of circumstances, apart from the mere routine of labor and thought involved, which operate rather effectively against the possibility of completing such .an ambitious program at the present time. First of all, as far as any public record of results is concerned, the commercial rolling, drawing, and forming of zinc with relation to changes of structure and properties—and this we consider to constitute the clement~ of metal technology—might as well be an unpractised art. We have never seen a published photomicrograph showing the structural characteristics of either hard or soft sheet or strip, although the structure of castings has been frequently described, and other coarse-grained structures resulting from hard-hammering and annealing have been reproduced. Thus, an author in this field must proceed to his task without much assistance from the literature, and the outcome can represent only a personal estimate of principles, facts, or findings, and not a summary or survey of progress in the entire field as determined by varied experience, practice, and settled opinion.

Jan 1, 1921

By Shueling Woo, Charles S. Barrett, Robert F. Mehl

When one solid phase is generated from another, fixed and rational orientation relationships are observed to subsist between the parent and the new crystal. The principle has been proposed1 that the relationships obtaining between the same two phases are identical whatever the type of phase change involved, or whichever of the phases may act as parent. Many types of phase changes have been studied: allotropic transformations in pure metals, precipitation from solid solutions, eutectoid decompositions, peritectic reactions, the formation of oxide layers, and others2 Phase layers generated by diffusion of one metal into another constitute an additional type of reaction. This report provides new data on the orientation relationships occurring between phase layers formed by diffusion, in the Cu-Zn system,§ and furnishes further evidence in support of the principle. Materials and Methods The Cu-Zn system is especially suitable for these studies since the high vapor pres- sure of Zn provides an opportunity readily to create one phase poorer in Zn upon a parent phase richer in Zn by removing Zn by vaporization, or to reverse this process by adding Zn from Zn vapor; e.g., the beta phase can be found as a layer upon gamma by dezincing, or gamma can be found on beta by addition of Zn from Zn vapor. Since orientation relationships are to be sought, requiring crystals large enough for orientation determinations, it is convenient to prepare single crystals or large grains of the parent phase. The samples were prepared from oxygen-free high-conductivity copper and Horse Head zinc by melting under a borax flux in a graphite crucible. Large crystals of beta brass were grown by the strain-anneal method, in plates sectioned from the cast ingots, by the following procedure. Rockwell-hardness indents were made at I cm. intervals and with various loads, then the plates were annealed for 4 days at 700°C. in Nichrome boxes packed with beta-brass chips and graphite. Surface layers were removed by grinding and etching to a depth of about 1.0 mm., and individual grains were cut out. Crystals of alpha and gamma brass were prepared by freezing, by lowering a graphite crucible at speeds less than one inch per hour through a furnace held at a constant temperature above the melting point. Single crystals were cut out with a jeweler's saw, ground, polished and etched. Care was taken to remove cold-worked layers from the finished crystals

Jan 1, 1944

By Charles S. Barrett, Robert F. Mehl, Shueling Woo

When one solid phase is generated from another, fixed and rational orientation relationships are observed to subsist between the parent and the new crystal. The principle has been proposed1 that the relationships obtaining between the same two phases are identical whatever the type of phase change involved, or whichever of the phases may act as parent. Many types of phase changes have been studied: allotropic transformations in pure metals, precipitation from solid solutions, eutectoid decompositions, peritectic reactions, the formation of oxide layers, and others2 Phase layers generated by diffusion of one metal into another constitute an additional type of reaction. This report provides new data on the orientation relationships occurring between phase layers formed by diffusion, in the Cu-Zn system,§ and furnishes further evidence in support of the principle. Materials and Methods The Cu-Zn system is especially suitable for these studies since the high vapor pres- sure of Zn provides an opportunity readily to create one phase poorer in Zn upon a parent phase richer in Zn by removing Zn by vaporization, or to reverse this process by adding Zn from Zn vapor; e.g., the beta phase can be found as a layer upon gamma by dezincing, or gamma can be found on beta by addition of Zn from Zn vapor. Since orientation relationships are to be sought, requiring crystals large enough for orientation determinations, it is convenient to prepare single crystals or large grains of the parent phase. The samples were prepared from oxygen-free high-conductivity copper and Horse Head zinc by melting under a borax flux in a graphite crucible. Large crystals of beta brass were grown by the strain-anneal method, in plates sectioned from the cast ingots, by the following procedure. Rockwell-hardness indents were made at I cm. intervals and with various loads, then the plates were annealed for 4 days at 700°C. in Nichrome boxes packed with beta-brass chips and graphite. Surface layers were removed by grinding and etching to a depth of about 1.0 mm., and individual grains were cut out. Crystals of alpha and gamma brass were prepared by freezing, by lowering a graphite crucible at speeds less than one inch per hour through a furnace held at a constant temperature above the melting point. Single crystals were cut out with a jeweler's saw, ground, polished and etched. Care was taken to remove cold-worked layers from the finished crystals

Jan 1, 1944

By Charles S. Barrett, Robert F. Mehl, Shueling Woo

WHEN one solid phase is generated from another, fixed and rational orientation relationships are observed to subsist between the parent and the new crystal. The principle has been proposed' that the relationships obtaining between the same two phases are identical whatever the type of phase change involved, or whichever of the phases may act as parent. Many types of phase changes have been studied: allotropic transformations in pure metals, precipitation from solid solutions, eutectoid decompositions, peritectic reactions, the formation of oxide layers, and others.2 Phase layers generated by diffusion of one metal into another constitute an additional type of reaction. This report provides new data on the orientation relationships occurring between , phase layers formed by diffusion, in the Cu-Zn system, § and furnishes further evidence in support of the principle. MATERIALS AND METHODS The Cu-Zn system is especially suitable for these studies since the high vapor pressure of Zn provides an opportunity readily to create one phase poorer in Zn upon a parent phase richer in Zn by removing Zn by vaporization, or to reverse this process by adding Zn from Zn vapor; e.g., the beta phase can be found as a layer upon gamma by dezincing, or gamma can be found on beta by addition of Zn from Zn vapor. Since orientation relationships are to be sought, requiring crystals large enough for orientation determinations, it is convenient to prepare single crystals or large grains of the parent phase. The samples were prepared from oxygen-free high-conductivity copper and Horse Head zinc by melting under a borax flux in a graphite crucible. Large crystals of beta brass were grown by the strain-anneal method, in plates sectioned from the cast ingots, by the following procedure. Rockwell-hardness indents were made at I cm. intervals-and with various loads, then the plates were annealed for .4 days at 700°C. in Nichrome boxes packed with beta-brass chips and graphite. Surface layers were removed by grinding and etching to a depth of about 1.0 mm., and individual grains were cut out. Crystals of alpha and gamma brass were prepared by freezing, by lowering a graphite crucible at speeds less than one inch per hour through a furnace held at a constant temperature above the melting point. Single crystals were cut out with a jeweler's saw, ground, polished and etched. Care was taken to remove cold worked layers from the finished crystals

Jan 1, 1944

By P. G. Shewmon

A novel technique for determining the surface energy (?) and its derivative with respect to orientation, (?') is described. Essentially it involves the 'floating" of a wedge on the substrate, said wedge being made of a material which is not wet or only slightly wet by the substrate, i. e., as a greased needle "floats" on water. A thermodynamic analysis of a system in which the wedge is supported entirely by surface energy is given. If the original suyface is not at a cusp orientation, the surface tension is directly measurable from the groove angle formed. If the original surface is at a cusp orientation, there may or may not be a groove depending on the relative value of ?' and the weight of the wedge. Experiments primarily on copper and silver showed that sapphire, quartz and refractory metal wedges were wet while graphite wedges were not. The technique was demonstrated to work using graphite wedges, but the results obtained were not as eccurate as those obtained by other workers using the wire-creep experiments. It is concluded that the technique might prove most useful with non-metals where ?' is large and filament creep experiments would be quite difficult. If an absolute value of the surface free energy (?) of a metal is to be determined, the most reliable methods used to date measure an average over the various orientations exposed on a polycrystalline sample. For example, ? for silver, gold, and copper have been measured by determining the force required to just keep a thin wire,' or foil,' specimen from contracting under the influence of ?. Herring 3 has predicted and experiment confirms, that the sensitivity of this method is inversely proportional to the grain size.' Thus it cannot be used to measure ? for a particular orientation by using a foil single crystal or a very coarse-grained specimen. An accurate value if ? for tungsten averaged over a range of orientations has been determined using a field emission technique. The same techniques cannot or have not been used to measure ? for non-metallic solids, and as a result the values available are much less accurate.4 This Paper resents a means of making an absolute determination of ? for a particular surface orientation on any solid, as long as the given surface orientation does not break up into other orientations during an anneal. Experimentally ? is found to vary with orientation and at a few low index orientations it is found to have a cusped minimum, i.e., the derivative of ? with respect to the orientation of the surface changes discontinuously at the low index orientation, see Fig. 1. The slope of a plot of ? vs orientation (herein designated ?') is called the torque on the surface, since it tends to rotate the exposed surface toward the low index orientation, or if the surface is at the cusp orientation it opposes any force tending to rotate the surface out of the low index orientation. The ratio ?'/? has been determined for a few metals, but in cases where this ratio is high there is presently no means of determining either ?'/? or the absolute value of ?' for the orientations present on an annealed surface. The technique discussed herein also provides a means of determining an absolute value of ?' for those orientations which deviate only infinitesimally from a cusp orientation. It should work best on surfaces where ?'/? is large; that is, for cases where no other technique is available for measuring ?'. Aside from trying to learn more about surfaces through measuring ? and ?', the primary reason for wanting values of ? or ?' is to study adsorption. From measurements of the variation of ? for a particular orientation with the concentration of an impurity, one can obtain the number of impurity atoms adsorbed per unit area (Ti) on that orientation using the Gibbs adsorption equation.' where µi is the chemical potential of the adsorbed impurity. Thus, if absolute values of ? could be obtained for the free surface of a given surface orientation as a function of µi, ri could be determined for the given orientation. Furthermore, by equilibrating a grain boundary with the given surface at various values of ki, one could also determine ri for the grain boundary. Similarly Robertson 6 has pointed out that if y is taken to be a continuous function of and µi, then a2 ?/a @a µ2 = a2 ?/a pi a +. Thus, at all orientations away from cusps the following equation holds From a measurement of ?' vs ki, it is thus possible

Jan 1, 1963

By W. T. Turrall, M. J. Cook

A discussion of modern developments in beneficiation of fine sizes of anthracite, this paper includes a description of the plant flowsheet, an analysis of operating results, and a summary of fundamentals of mineral separation relative to plant operation.

Jan 9, 1953

GENTLEMEN : Herewith are submitted reports for the calendar year 1933 of your Treasurer and the Chairmen of the following standing committees: Finance, Admissions, Membership, Papers and Publications, Library, and MINING AND METALLURGY. TO these reports you are referred for additional details of the year's activity. Finances.-Income for 1933 from all sources totaled $121,690 com- pared with $138,331 in 1932. Incidentally, this exceeded the income as estimated in the budget by $7,190; the largest item being a "surplus" of $3,316 over the budget expectancy as to member dues. As compared with 1932 the most important items of shrinkage in income were $9,000 from dues and initiation fees; $5,500 from the magazine, MINING AND METALLURGY; and $2,500 from sales of publications other than the magazine.

Jan 1, 1934

By Rclssell Gibson, F. S. Turneaure

The tin deposit of Monserrat; Bolivia, consists of one major vein 1600 m in length. The ore is unusual because of the notable quantity of teallite, even though cassiterite is the principal tin mineral. The deposit, formed at shallow depth under a wide range in temperature, may be classed as xenothermal. Polished sections reveal a complex history of replacement, with low-temperature minerals deposited before high-temperature minerals.

Jan 1, 1950

THE illustration below shows the design of the face of the clock to be erected as a memorial to the American engineers who gave their lives overseas in the World War. It will be placed in the tower of the library at Louvain, which has been rebuilt through contributions from America. Large clocks seldom have figures on their faces, and each hour on this one will be marked by a gold star, the four faces containing 48 stars, one for each State of the Union. Contributions toward the memorial have been received from every one of the States, and from Alaska and Hawaii as well, but additional subscriptions are invited by the Com-mittee which is arranging for the memorial.

Jan 3, 1928

By D. H. Polonis, Gary A. Dreyer

This investigation involved a study of the reactions occurring during aging of supersaturated a phase in a CIL-Si alloy. The aging processes at temperatures below 552°C were studied by means of metallography, microhardness, and electrical resistivity measurements. During the initial stage of aging in the temperature range 275o to 525oC an anisotropic phase, which is visible in the form of striations in the micro-structure formed prior to the appearance of the -phase. This transition phase has been designated k' due to its structural similarity to the k phase. The rate of K' formation during aging increased with aging temperature. At 450o and 525°C the reaction appeared to reach completion before significant amounts of precipitation were observed. The overall precipitation reaction in this system involved four stages: formation of formation of at a grain boundaries, growth of particles in 7-egions, and coagulation of into large particles. The relative role of each of these processes is dependent on the temperature of aging. The formation of phase from supersaturated a during aging increases the electrical resistivity and slightly increases the hardness of a 4.9 pct silicon alloy. The formation of during aging decreases the electrical resistivity and increases the hardness until coalescence of particles begins during the final stages of aging. The coalescence of results in a decrease of both electvical resistivity and hardness. THE available literature does not record a detailed analysis of the aging processes in Cu-Si alloys. Such an analysis has been difficult due to both the limited data available and misleading microstructural observations which have been reported. Previous work suggests that a rather complicated series of processes may be involved in the aging of supersaturated a. The present investigation is concerned with an analysis of the sequence of these aging processes in a 4.9 pct Si alloy. The currently accepted version of the Cu-Si equilibrium diagram, Fig. 1, was published by C. S. Smith in 1940.' This diagram shows a eutectoid at 5.2 pct Si with the high temperature phase, having its composition range entirely to the right of this value. By quenching alloys in the composition range 4.6 to 5.2 pct Si from the region, Smith was able to retain the phase. However, this phase exhibited a striated microstructure which was anisotropic to polarized light. These striations were suggested by Smith to be duplex twins. Using an oscillating crystal X-ray method Barrett2 studied alloys containing 4.0 to 5.4 pct Si quenched from the and regions. The striations observed in quenched specimens were attributed by Barrett to quenching stresses. He found that striations could also be formed by deformation after quenching and identified them as stacking faults in alloys containing 4.0 to 5.0 pct Si. Barrett related the striations in alloys containing 5.0 to 5.4 pct Si both to stacking faults and to a metastable phase which he called The striated structure reported by smith' was also obtained by Hoffmann, et al. 3 By deeply etching their specimens the anisotropic phase on the surface was removed, leaving a structure which was microscopically similar to pure copper. By means of X-ray analysis before and after deformation at room temperature it was concluded that the anisotropic phase was metastable This conclusion has been questioned by Barrett who attributes the discrepancy to superposition of k and lines on the powder patterns of Hoffmann, et alm3 The decomposition of supersaturated according to smith' and Anderson,4 is very sluggish. However, Nony and Dreyer,5 and Hoffmann, et al.' found that deformation increases the rate of decomposition. X-ray studies by Hoffmann, et al on

Jan 1, 1962

By Frederick Rhines

THE investigations of Wyman1 have demonstrated that copper deoxidized with several of the commonly used agents that confer immunity to ordinary hydrogen em-brittlement can still be embrittled if it is annealed alternately under oxidizing and reducing conditions. During the oxidizing cycle, oxygen diffuses into the copper and frequently deposits a subscale composed of the oxide of the residual deoxidizing agent. Upon subsequent reduction with hot hydro-gen, the copper becomes ruptured along the grain boundaries to a depth sharply limited by the previous penetration of oxy-gen as delineated by the inner boundary of the subscale. Obviously the sensitivity to this kind of hydrogen embrittlement is engendered by the introduction of oxygen during the oxi-dizing anneal, but beyond this the mecha-nism of the process, and hence the controlling factors, remain obscure. There are several possibilities: (I) oxygen dissolved in the copper matrix of the subscale may, upon cooling prior to the hydrogen anneal, precipitate as cuprous oxide which is subse-quently reduced by hydrogen as in the familiar case of hydrogen embrittlement; (2) oxygen in solid solution in copper may itself confer susceptibility to embrittlement by hydrogen; (3) the normally refractory oxides such as those of aluminum, silicon and titanium may themselves he reduced by hydrogen when in contact with copper; or (4) the precipitated oxides of the sub-scale may be complex compounds such, perhaps, as Si02-Cu20, which are partially reduced by hydrogen. These possibilities have been examined, and it has been con-cluded that the first three and possibly the fourth are operative collectively or indi-vidually under more or less predictable conditions.

Jan 1, 1940