Search Documents

By Robert Goodrich

THERE is a small area about Murray where bedded gold quartz veins occur in Prichard slate. The ore taken from the upper levels, during the early days, was free milling and was treated by stamp milling and amalgamation. There was likewise a considerable placer working. The report is current that tungsten (scheelite) was encountered, which interfered with the amalgamation in the stamp mills and which, in placering, collected in the riffles in the sluice boxes and. clogged them. Consequently, in the quartz mines, the scheelite, when encountered, was rejected, being thrown into the waste, sometimes inside the mine and at other times outside on the clump. The free surface ores became worked out and as the ore in depth became pyritic and rebellious to amalgamation the mines closed down. Last spring tungsten ore brought a high price, near $80 per unit, 60 per cent. W03 and up. This so stimulated the output of tungsten ore that old clumps were explored and waste stored in the mines was gone over. Tungsten was likewise mined from virgin ground. So the district produced quite heavily for a time. The condition now is different. The price is not so high, about $20 per unit W03, which makes profits questionable when mining in new ground. The accumulations from early clay mining have been exhausted and the output has greatly declined. The Golden Chest mine was the heaviest producer of tungsten. The months of June and July were spent at this mine studying the problem. Since the mine had produced both gold and tungsten, we looked forward to the problem of recovering both from what might be called a gold-tungsten ore. A study of the Golden Chest vein showed this not to be so there. While gold ore and tungsten ore come from the same vein, the tungsten ore is confined to a more or less disturbed or distorted portion

Jan 8, 1917

By Charles Barrett

SINCE 1925, when the preferred orientations in compressed aluminum were first determined1, 2 the orientations have been described as a fiber texture in which a face diagonal, [110], of the face-centered cubic lattice is parallel to the compression axis. Subsequent experiments have seemed to confirm this texture,3-5 and a number of theories (recently summarized in references 6 and 7) have been proposed to explain it and to relate it to the behavior of single crystals during compression. 3,8-11 The experiments reported in this paper prove that the orientations are not adequately described as quoted above-i.e., as a [110] fiber texture-although this is a first approximation to the actual texture. They also show that the texture cannot be thought of as a stable orienta-tion that is reached and maintained after a sufficient amount of deforma-tion. The actual texture, when studied in detail at successive stages of compression, indicates that a hitherto unsuspected range of orientations is present, both in the polycrystalline metal as a whole and in various individual grains in its interior, and that a state of dynamic equilibrium exists within this range. The reasons for the failure of previous theories to predict the actual texture become obvious when the heterogeneous nature of the flow is considered. In addition to the deformation texture, the manner of its develop-ment, and its theory, this paper presents data on the following related subjects: the identity of strain markings in aluminum; the orientation changes in aluminum single crystals during compression and a com-parison of these with the conditions in individual grains of a polycrystal-line specimen; the origin of asterism in deformed single crystals, which heretofore has been regarded as a distortion localized at the surfaces of slip planes; and the relation of plastic strain in individual grains in an aggregate to the strain of the whole.

Jan 1, 1939

By D. R. Mitchell

FOR the second consecutive year, attendance at the Coal Division sessions far exceeded exoectations. Those in charge were continually faced with problems of finding seats and space for attending members. 115 seats were set - II~ for the annual luncheon meeting of the Division and approximately 175 members showed un. Since the hotel management would not serve more than the 115 it meant that 60 members were forced to eat elsewhere. This created hard feelings with some members. How- ever, officials of the Division were not able to obtain in advance any indication of this overflow crowd, but are suggesting to the New York Office that some means other than ticket sales be adopted to obtain an estimate of Division luncheon and dinner attendance. Members could be circularized prior to he meeting or they could be checked when registering as to the events they expect to attend. Under the inspiring leadership of Cadwallader Evans, Jr., Chairman, the Coal Division had a phenomenal growth during the year. Reporting at the luncheon meeting, Newel1 Alford stated that approximately 190 new members had been obtained. A few more years of continuing increase at this rate will make the Coal Division one of the largest Divisions in the Institute.

Jan 1, 1944

By A. K. Chakravarti, A. Lihiri, G. G. Sarkar

One primary objective of India's third Five Year Plan is the expansion of coal production. The goal: boost present output of 45 million tons to 95 million tons by 1965--an increase of more than 100 pct!

Jan 7, 1961

By J. Handin, S. J. Bauer, M. Friedman

Deformation mechanisms in room-dry and water-saturated specimens of Charcoal Granodiorite, shortened at 10-4s-1, at effective pressures (Pe) to 100 MPa and temperatures to partial melting (?1050°C) are documented with a view toward providing criteria to recognize and characterize the deformation for geological and engineering applications. Above 800°C strength decreases dramatically at effective pressures ? 50 MPa and water-weakening reduces strength an additional 30 to 40% at Pe = 100 MPa. Strains at failure are only 0.1 to 2.2 percent with macroscopic ductility (within this range) increasing as the effective pressures are increased and in wet versus dry tests. Shattering (multiple faulting) gives way to faulting along a single zone to failure without macroscopic faulting as ductility increases. Microscopically, cataclasis (extension microfracturing and thermal cracking with rigid-body motions) predominates at all conditions. Dislocation gliding contributes little to the strain. Precursive extension microfractures coalesce to produce the throughgoing faults with gouge zones exhibiting possible Riedel shears. Incipient melting, particularly in wet tests, produces a distinctive texture along feldspar grain boundaries that suggests a grain-boundary-softening effect contributes to the weakening. In addition, it is demonstrated that the presence of water does not lead to more microfractures, but to a reduction in the stresses required to initiate and propagate them.

Jan 1, 1982

By C. H. Mathewson

CONSIDERABLE progress has been made during the last few years in analyzing the action of plastic deformation in metallic crystals. This is due largely to the development of X-ray spectrographic methods for studying changes in the orientation of single crystals, or of conglomerates, as they occur during the process of plastic deformation, but partly to the widespread knowledge of suitable technique for preparing large (single or variously combined) crystals for direct crystallographic observation under stress or in various conditions of strain. These two methods of studying changes in the crystalline structure of metals may of course be used in conjunction with features of mutual support, but unfortunately the advantage of direct crystallographic observation is lost when we proceed to the study of severely cold-worked structures, owing to the occurrence of real or apparent crystalline discontinuities which become more and more complicated as the amount of plastic action increases. Furthermore, the X-ray methods do not appear to be adequate, at least in their present stage of development, to fix definitely the character of structural alteration in the parent crystal lattice by plastic deformation. The principal question at issue concerns the nature of the crystalline particles that remain after plastic deformation. These are generally known in our American metallurgical literature as crystalline fragments,1 and they seem, indeed, to diffract as individuals causing the Hull pattern of a, severely cold-worked metal to resemble the pattern of a fine powder,2 with certain features of preferred orientation among the particles determined by the manner and intensity of cold working.

Jan 1, 1927

By W. F. NETZZEBAND

THE long-hole drill has been used for prospecting underground in the tri-State district for several years, and its value has been pretty thoroughly proved. An attempt was made to get a statement of their experience with the machine from all the operators who were known to have used the machine. The majority of them replied to the questionnaire so that this paper is practically a summary of the experience of the district, together with some practical details taken from the experience of the Eagle-Picher Lead Company. When the drill was first used by the Eagle-Picher Lead Co., it was put in low headings and was mounted on a cross-arm supported by two drill columns. This was found to be a rather awkward method of mounting, because fairly long moves were made and the same drill columns could not be used on any two successive set-ups. The machine was later moved to a mine with high headings so that this type of mounting was found to be impractical. A heavy tripod was tried and found satisfactory, provided care was taken to see that the set-up was solid. The Evans-Wallower Lead Co. and the Century Zinc Co. report using the double post set-up, but the headings are low in these mines. The Commerce Mining St Royalty Co. first used the double-post mounting in high headings by cutting a niche in the wall and setting the post in it. This proved to be a slow and expensive method and was later abandoned for the tripod. The Federal Mining & Smelting Co. has used a tripod throughout its operations. Great care must be taken in using the tripod to see that the set-up is solid. Wherever possible it is advisable to sludge in the legs and let them set a short time before the machine is put into use. Where high bottom is encountered the Eagle-Picher operator found it advisable to drill jack- hammer holes in the bottom and drive the legs into them.

Jan 1, 1930

By L. S. Castleman, R. K. Hotzler

We are currently studying the effects on recrys-tallization of impurities diffused into dispersion-hardened alloys. Our interest in this phenomenon was originally aroused by the observation that the recrystallization temperature range of tungsten "doped" with alumina and silica, or with thoria, is lowered drastically if nickel is plated onto the tungsten prior to heat treatment.' In this note, we report a similar effect that sulfur has on the recrystallization behavior of thoriated nickel. The experimental procedure for this exploratory phase of the investigation has consisted simply in heating commercially obtained stress-relieved samples of thoriated nickel for varying temperatures and times in sealed capsules containing air and small quantities of sulfur. The samples contain 2.4 vol pct thoria and initially less than 18 ppm S by weight; they are prepared either from 0.5-in.-ciiam rod stock or from 0.092-in. sheet and are in the "as-received" (stress-relieved) condition prior to exposure. In an atmosphere free of sulfur, such samples do not show evidence of recrystallization after being annealed for 1 hr at a temperature of 2500°F (1372C).2 The photomicrograph in Fig. 1 shows the microstructure of one of our samples annealed for 75 hr at 1000° C (1832°F) in a sulfur-free capsule. The grain structure is hardly evident (if at all) at 465 times magnification. In contrast, the photomicrograph of Fig. 2 shows the recrystallization that has taken place in a sample exposed to sulfur for 5 hr at 1000°C (1832°F). A nickel sulfide phase is visible at the grain boundaries of the light-appearing grains. We have also observed recrystallization to occur in a sample annealed at 600°C (1112°F) for 25 hr. This temperature is below the 637°C (1178°F) eutectic in the Ni-S system. In the latter case, no nickel sulfide phase is evident in the microstructure. Moreover, we have noticed the occur-

Jan 1, 1969

By C. W. Crispell

The four nomograms presented in this article were designed to simplify and make more rapid the calculations connected with the compression and transmission of air. The formulae involved are rather complicated, but the graphic solutions are simple; their use requires an ability to follow explicit directions and to interpolate values on a logarithmic sca1e. † For the sake of convenience, the nomograms will be divided into two classes, and the purpose and accuracy of each will be discussed. Power foR CompREssion It is frequently desirable to determine the horsepower necessary to compress a given amount of free air from atmospheric pressure to a certain final pressure. The nomograms in Fig. 1 and 2 present a rapid method of calculating the horsepower required to compress 1 cu. ft. of free air per minute by single or two-stage compression. The general formula for the horsepower required to compress air adiabatically is: S X 144 PVn [(P')n-1/sn -1 (1) where: P = absolute atmospheric pressure at compressor, in pounds per square inch. P' = final absolute pressure of compressed air, -in pounds per square inch. V = volume of free air compressed per minute, in cubic feet. S = number of stages. n = exponent of the compression curve.

Jan 1, 1918

By Philip S. Mathews

THE tremendous stimulus given to the mining industry by the gold and silver policy of the present administration has found the capital market for mines ill prepared to afford practical means of financing. Particularly has this been true of the host of abandoned high-cost producers and prospects which increased gold and silver prices have made potentially profitable. In a comparatively short time, experience has demonstrated abundantly that valuable properties have frequently failed to secure capital, while questionable properties have drawn to themselves and their promoters more of the public moneys than their prospects justify. Singularly enough the fault is usually attributable to faulty financing. Discussion and study of this problem are vital to the industry.

Jan 1, 1936

By Daryl R. Tweeton, William H. Engelmann, Orin M. Peterson, Jon K. Ahlness, Gregory R. Anderson

The Bureau of Mines measured the geochemical changes as H2SO4 was used for in situ uranium leaching by Rocky Mountain Energy Company near Casper, Wyoming. Cores and ground water were analyzed before leaching. Water samples were taken from observation wells located between injection and production wells as the leach solution was brought up to full strength in several steps. Measurements were made of pH, Eh, temperature, conductivity, total dissolved solids, dissolved oxygen,HC03, U. V, Na, K, Ca, Mg,S04, CI, Mo, Mn, Fe, AI, Si, F, P, As, and Se. The data were gathered to assist in geochemical modeling of leaching and to study the potential environmental effects of acid leaching. Environmental considerations appear favorable. For example, the concentration of Se, a toxic element often found in uranium deposits, stayed below the EPA standard for drinking water.

Jan 1, 1979

By T. Fraser, F. F. Giese, R. L. Sutherland

Under a cooperative agreement between United States Bureau of Mines and the Truax-Traer Coal Company, some operating-scale experiments have been made with the cyclone thickener in the preparation plant of the Shamrock No. 1 mine at Kayford, West Virginia. These tests were made with a 14-in. cyclone of the type developed by the Dutch State Mines in Limburg. It was applied experimentally to the thickening of solids in washery water to obtain performance data to show the range of sizes that may be recovered and other operating characteristics that would indicate the field of usefulness of this device in coal preparation practice. This is a progress report only. It covers results obtained in a series of 17 tests of the operation of what has been considered a unit of commercial size operating on suspensions of fine coal mixed with a relatively small amount of free impurities. The underflow material, after further dewatering in centrifuges, is a marketable grade of coal. The coal at Shamrock No. 1 is mined from the No. 2 Gas seam. It is made up essentially of a low ash coal suitable for byproduct use with one or more bands of splint coal of higher ash content suitable for industrial fuel. The washing plant was installed for the two-fold purpose of removing the free impurities incident to mechanized mining and to separate the run of mine coal into the two types. To accomplish these results it is necessary to make a separation at a specific gravity of about 1.4 to recover the byproduct coal and to separate the splint coal from refuse at a higher gravity. The coarse coal section of the washing plant was put into service about 10 months before the fine coal section was completed. Inadequate screening capacity in the raw coal preparation plant resulted in a portion of the fine coal being fed to the jigs. No provision for preliminary dedusting of the raw coal feed was incorporated in the design. Under the conditions in the initial operating period, separation at the desired lower gravity was not realized, apparently because of the presence of an excessive amount of fine solids in suspension in the wash water. Difficulty in wetting the fine coal may also have been a contributing factor. Additional facilities for the removal of the fine solids from the wash water was indicated. Information then available on the Driessen cone for this purpose was studied and a cooperative agreement with the Bureau of Mines for experimental work with a unit of standard size as developed by the Dutch State Mines was arranged. During the time required for construction of the cone it was found the addition of a small amount of wetting

Jan 1, 1950

By Leonard Grimshaw

THE idea of bonding two dissimilar ferrous metals, and making use of both, is an old one. Tips have been brazed onto tool shanks for many years. The bonding of larger pieces to form whole bars and sheets has also been accomplished, but has received little attention in the technical literature, although a number of patents have been issued covering various methods for its accomplishment. There are three main motives behind the manufacture of composite steels. One is that the physical properties of one steel may supplement those of another; a useful, but at the same time, hard, brittle steel may be backed by a soft ductile one, or a stainless steel may be backed by a steel possessing greater strength. Another motive is direct lowering of cost; an expensive steel may be backed by a less expensive one, bringing down the cost of the piece as a whole. The third motive is an indirect lowering of cost, as when a useful steel is backed by a steel that is easier to machine, so that machining cost on a finished product is lowered considerably. Often more than one of these motives lead to a decision to use a com-posite steel.

Jan 1, 1936

H. Van F. Furman, Denver, Colo. (communication to the Secretary): There are some statements in Dr. Carpenter's interesting paper which appear to require explanation, if not modification.

Jan 1, 1901

By Eugene A. Alexandrov

The Minister of Geology of the Soviet Union P.Ya. Antropov, recently visited China and claims that this country occupies one of the foremost places in the world in reserves of tin, tungsten, molybdenum, antimony, iron ore, coal, and phosphates. Occurrences of economic value of chromite, nickel, gold, beryllium, tantalum, niobium, rare earths, and asbestos have also been reported. MINERAL RESOURCES Coal: The inferred reserves of coal are estimated at at 1,500 billion tons. A considerable part of the coal reserves is represented by coking coal, 80% of which is bituminous. Thicknesses of coal seams range up to 150 ft in the principal deposits located in northern and northeastern China. The total output of coal in 1958, 270 million tons, was produced by an army of 20 million people mainly in small mines operated by the agricultural communes. Modern hydraulic mining is applied besides primitive, obsolete methods and equipment

Jan 3, 1960

By Norman D. Fitz Gerald

THE growth of domestic requirements for motor fuel has been phe-nomenal, rising year after year in a fashion almost unique among com-modities, resisting depressions and forging rapidly ahead in times of prosperity. Consumption advanced from 226 millions of barrels in 1925 to 522 millions of barrels in 1938; or 130 per cent. The economic influ-ences generating and sustaining this demand are of vital concern to the petroleum industry. The general factors affecting utilization of motor fuel are well known but it is the purpose of this paper to employ the recently developed technique of economic dynamics to describe them mathematically. Such problems in economic analysis are complicated by the freedom of all the variables to fluctuate, their mutual interdependence, changing incidence upon one another, and the nonquantitative character of some of them. Economic quantities and relationships, unlike those of the physical world, are continuously changing and this dynamic characteristic is both a distinguishing and confusing feature in economic research. The com-plexities of the problems require application of the analytical devices of mathematical statistics to uncover the probable relationships between factors. The procedure employed is to formulate a logical relationship linking the dependent to the independent variables, and then simul-taneously, rather than sequentially, determine their separate effects by multiple correlation. This transformation of common knowledge to quantitative terms makes it possible to measure the probable effects of changing conditions upon requirements, assisting in the sound interpreta-tion of economic policies. The utility of the results of such dynamic analysis is in sharp contrast to the sterility of the trends and other simple empiricisms of descriptive statistics. It is not intended in this study to throw light on the reasons why any motor fuel at all is consumed; but to discover relationships explaining why more was consumed at one time than at another. Specifically the prob-lem is confined to the measurement of the influences of statistically

Jan 1, 1940

By P. K. Lucke

ONE of the interesting features connected with the great continental uplift, which formed the table land of Mexico, is the great depth to which oxidation and secondary enrichment of orebOdies occurred. This table land lies at altitudes ranging from 4000 to. 7000 ft. (1219 to 2133 m.) above sea level. Several cases could be cited of oxidized zones in copper and lead mines which reached depths of upward of 1500 ft. (457 m.) below the surface, and it is universally admitted that the oxidized zone in a mine is limited by the permanent water level. FIG. 1. Mexico, however, like many other countries in which deserts occur, is visited at rare intervals by tremendous floods, which sometimes cause variable water levels over long periods. The following cases bear out the idea, and lead to interesting conclusions of commercial value. My paper demonstrates that carbonates of ores may occur below water level and sulphides above, and I will endeavor to explain the causes of the phenomena in certain specific instances.

Jan 6, 1918

By P. K. Lucke

One of the interesting features connected with the great continental uplift, which formed the table land of Mexico, is the great depth to which oxidation and secondary enrichment of orebodies occurred. This table land lies at altitudes ranging from 4000 to 7000 ft. (1219 to 2133 m.) above sea level. Several cases could be cited of oxidized zones in copper and lead mines which reached depths of upward of 1500 ft. (457 m.) below the surface, and it is universally admitted that the oxidized zone in a mine is limited by the permanent water level. Mexico, however, like many other countries in which deserts occur, is visited at rare intervals by tremendous floods, which sometimes cause variable water levels over long periods. The following cases bear out the idea, and lead to interesting conclusions of commercial value. My paper demonstrates that carbonates of ores may occur below water level and sulfides above, and I will endeavor to explain the causes of the phenomena in certain specific instances. Case I.—Fig. 1 in this case shows that sulfides of lead remained

Jan 1, 1920

By L. S. Darken

It has been known for sometime that in an ionic lattice, such as that of Ag,S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulphide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulphide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall' support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffdsion proposed by several authors, most recently by Bir-chenall and Mehl.2 This theory has, however, also been questioned3v4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however. Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz, who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a Similar mechanism, whatever it may be, at a greater Or lesser rate, thus giving rise

Jan 1, 1949

By L. S. Darken

It has been known for sometime that in an ionic lattice, such as that of Ag,S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulphide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulphide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall' support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffdsion proposed by several authors, most recently by Bir-chenall and Mehl.2 This theory has, however, also been questioned3v4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however. Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz, who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a Similar mechanism, whatever it may be, at a greater Or lesser rate, thus giving rise

Jan 1, 1949