Search Documents

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By G. R. Love, C. C. Koch

The changes in superconducting properties with aging time have been studied ,for the pecipitation reaction in a Tc-30 at. pct V alloy. Superconducting critical temperature, upper critical field, and relative critical current density were determined by ac susceptibility techniques. Aging produces changes in critical temperature of both matrix and precipitate which can be rationalized by compositional effects. maximum flux pinning (critical current density) occurs at a time during aging when subgrain boundaries are completely decorated with precipitates and the subgrain centers remain precipitate -free. The particular effectiveness as barriers to flux motion of planar defects which enclose regions of low deject density is discussed. THE precipitation of a second phase can dramatically modify the superconducting properties of type I1 super-conductors. According to Livingston and Schadler1 one might expect changes in the primary, secondary, and tertiary superconducting properties of the material. Changes in matrix chemistry caused by precipitation can alter the fundamental superconducting parameters; critical temperature, Tc, and thermody-namic critical field, Hc. The concimitant changes in electron mean free path (reflected in normal state resistivity) can affect the critical fields Hc 1, IIc2, Hc3. Finally, the presence of precipitate particles may hinder the motion of flux lines and may considerably improve the current-carrying capacity in high-field superconductors. The influence of precipitation on superconducting properties has been studied in a number of systems.2 Magnetization measurements have been used to study the influence of precipitates on flux pinning in lead-base alloys by Livingston3 and Evetts et al4 In these alloys precipitates induced magnetic hysteresis and flux trapping. The amount of hysteresis increased with the volume fraction of precipitate and decreased with coarsening of the precipitate. Jn an Al-Zn alloy5 and an A1-Ag alloy6 the initial precipitate size was presumably smaller than a coherence length and coarsening increased magnetic hysteresis5 and critical current density.6 The influence of precipitation on superconducting properties has also been studied in several of the commercially interesting Ti-Nb7-10 and zr-Nb11 alloys. The maximum in critical current density for these alloys was confined to a narrow range of either isothermal aging time" or isochronal aging temperature7 during the precipitation reaction. Thus, experimental evidence and theoretical considerations suggest there is an optimum precipitate size, spacing, and density, and a critical composition with respect to the matrix for flux pinning. What these "optimum" values might be and the relative importance of each is still not clear, although a few generalizations can be made. It is generally accepted1' that particle sizes smaller than the coherence length or larger than the inter-flux line spacing are poor pinning centers. In high Hc2 materials, precipitate sizes for maximum values of critical current density lie in the range of 50 to 2000Å,9,7 and there are indications that increasing dissimilarity between precipitate and matrix produces increasing pinning force.13 Because of several interesting features of the aging reaction in a Tc-30 pct V alloy, we have chosen to study the influence of precipitation on the superconducting properties of this alloy. The physical metallurgy14 and a survey of the superconducting properties" of the Tc-V alloy system have been reported. The Tc-V phase diagram is presented in Fig. 1. At 1500°C the Tc-30 pct V alloy is in the single phase 6 field. Samples quenched from the 6-phase field have a CsCl structure X-ray diffraction pattern at room temperature and it has been proposed that the 6 structure is closely related to the bcc lattice.14 When held isothermally below the eutectoid temperature, 115O°C, the 6 phase decomposes into the CsCl and hcp phases.

Jan 1, 1970

By B. H. Caudle, W. J. Bernard

Factors which influence the success or failure of a waterflood can seldom be determined in the laboratory. For this reason pilot waterfloods are initiated in a repreventative portion of the oil reservoir in question. For a pilot flood to predict quantitatively the recovery to be expected in a field-wide waterflood operation, the pilot area must behave as though it were confined (surrounded by similar areas). In this study, laboratory fluid-flow models were used to determine the simplest pilot pattern, for particular conditions of mobility ratio and initial gas saturation, that would behave as though it were confined. Pilot patterns studied ranged in complexity from a single inverted five-spot to a grouping of nine regular five-spots. Only the innermost producing well in each pattern was studied. Model results showed that the optimum number of wells in the pattern depends upon the oil-water mobility ratio and the expected oil-bank size. Unfavorable mobility ratios will, in general, require more wells in the pilot pattern than will favorable mobility ratios. Pilot patterns in reservoirs which contain a dispersed, flowable, free gas saturation will require fewer wells than for the under-saturated case. The single inverted five-spot pattern was found to be unsatisfactory for predicting behavior of fully developed waterfloods. In particular, it is possible that, in reservoirs which contain a flowable, dispersed gas phase, the oil bank will never be observed at the producers due to the large amounts of free gas which continue to be produced with the oil. INTRODUCTION One method which has been used to predict the performance of a waterflood is the pilot flood. The pilot waterflood is a flood which involves only a small cluster of the reservoir wells and is located in a small, representative portion of the reservoir. The object is that oil produced from the pilot can, in some way, be related to the oil recovery to be expected from a field-wide expansion of the waterflood. However, these field pilot waterfloods have often been unreliable in the prediction of oil recovery in a fully developed waterflood. This unreliability has also been demonstrated in several laboratory studies of pilot floods. Some of the investigators have shown that there are situations in which the pilot flood oil production is far too optimistic with respect to the oil recovery in the fully de- veloped flood. Others4-G have shown that the pilot results can also be pessimistic, especially if the pilot waterflood is initiated in an oil reservoir which has been depleted by primary recovery and is at very low pressure. The major reason for this unreliability of pilot water-floods is the migration of fluids into or out of the pilot area. By the well-known method of images, if straight lines can be drawn to represent vertical planes of symmetry in a porous medium which contains pressure sources and sinks (injectors and producers), then these lines are invariant streamlines, or lines across which there is no potential gradient, and therefore no flow. In an actual reservoir, these lines of symmetry can never be established exactly because of reservoir inhomogeneities and irregular reservoir boundaries. However, if the reservoir is relatively large and contains wells in repetitive patterns, these lines of symmetry are commonly assumed to exist for the pattern units sufficiently far removed from the reservoir boundary. Lines of symmetry for the five-spot injection pattern are shown in Fig. 1. Each five-spot unit in this figure can be considered confined with respect to flow across its boundary. In pilot floods this is not the case. The lines of symmetry for the pilot patterns investigated in this study are shown in Fig. 2. It is obvious that the fluid within these pilots is not confined and is therefore able to migrate into or out of the pilot area. Intuitively, one can see that, if more wells are added to the pilot, the innermost unit tends to behave more and more like the confined pattern. However, there is a practical limit to the number of wells which should be placed in the pilot. This limit is usually determined by economic factors. It was the purpose of this study to use laboratory fluid-flow models to determine which of the previously mentioned pilot patterns will force the innermost producing well to behave as it would in a fully developed waterflood. Since fluid migration is influenced by initial saturation conditions and the mobility ratio, these factors were included in the study. The ultimate objective of this study was to develop data which would allow the operator to choose a pilot pattern and operating conditions that will yield a production history which can be applied directly as an estimate of the performance of each production well of the fully developed waterflood. BASIS FOR THE STUDY The basic problem of field pilot floods is the migration of the reservoir fluids into or out of the pilot area. This problem has been the subject of previously reported model studies on pilot floods. These studies have been concerned mainly with the development of arbitrary "correction factors" to be applied to the simple, unconfined pilot systems such as the single five-spot. The correction factors were intended to adjust the production history of the un-

By J. Hoover Mackin

The iron ore bodies of the Iron Springs district are replacement deposits of magnetite and hematite in Jurassic limestone around the borders of three intrusions of quartz-monzonite porphyry. Production in the period 1923-1965 was about 72,000,000 tons, nearly all of which was direct-shipping ore from open pits. The intrusions are laccolithic in form; all three were emplaced at the same stratigraphic horizon, which had been a zone of decollement gliding during the Laramide orogeny. The intrusions and associated volcanic rocks are post-orogenic. There was no change in the thickness of the limestone during the metallization. Comparison of the composition of the limestone and stratigraphically equivalent replacement ore indicates that, with every million tons of iron, there were additions of 40,000 tons of silicon, 20,000 tons of magnesium, and 10,000 tons of aluminum. The ore-forming fluid was derived from the exposed porphyry. The iron was first incorporated in hydroxyl-bearing mafics, which crystallized in depth and were carried upward in the magma that formed the hypabyssal intrusions. The mafic phenocrysts decayed deuterically in the new environment, releasing iron into the interstitial fluid of a consolidating crystal mush in the interior of the intrusions. Primary tension joints, which opened in areas of late intrusive distention, served as roots through which the ore-forming fluid was drawn from the crystal mush.

Jan 1, 1968

By T. E. Leontis

The specific effect of various rare-earth metals on the room- and elevated-temperature properties of magnesium has been evaluated. Alloys containing didymium exhibit the highest tensile and compressive strengths at room and elevated temperatures. All the rare-earth metals increase the creep resistance of extruded magnesium at temperatures in the range of 400° to 600°F, but the degree of enhancement depends on the temperature and on the concentration of the added metal. THE effects of rare-earth metals on the properties of sand-cast magnesium were discussed in some detail in earlier paper by the author.' The present paper deals with the effect of the same alloying elements on the properties of extruded magnesium. This investigation also had as its aim the development of a wrought alloy having a better combination of room-temperature strength and ductility and elevated-temperature strength and creep resistance than is found in magnesium-Mischmetal-manganese alloys, which have been reported earlier.2-5 The only known attempt to study wrought magnesium alloys containing pure cerium instead of Mischmetal was made by Mellor and Ridley.6 They found that in the form of rolled bars there is a definite, optimum cerium content for creep resistance at 200 °C and that the creep resistance of these alloys at 200 °C is significantly Improved by heat treatment at 550" to 580"C. In the present investigation the compositional variation in mechanical properties of the following alloy systems is presented: I—magnesium-Misch-metal. 2—magnesium-cerium-free Mischmetal. 3— magnesium-didymium. 4—magnesium-cerium. 5— magnesium-lanthanum. Alloys containing predominately praseodymium are not included in this series because of the lack of this material. Experimental Procedures The alloying ingredients used in preparing the alloys described herein are the same as those reported in the earlier paper.' Cerium-free Mischmetal is the rare-earth mixture remaining when the cerium is removed from Mischmetal, which contains all the rare-earth metals as they occur naturally in mon-azite sand, the ore from which Mischmetal is produced. Removal of both cerium and lanthanum from Mischmetal leaves what is commonly called "didym-ium," consisting predominantly of neodymium and praseodymium. Although the composition of the particular batch of each metal used may differ somewhat from the analysis presented previously, these differences are not great enough to warrant repeat- ing the specific composition of each material. The electrolytic magnesium used as the starting material in these alloys has the same typical analysis as that given in the earlier paper.' The alloys were prepared in small laboratory melts applying all the necessary precautions for alloying rare-earth metals with magnesium described by Marande.' Most melts were large enough to cast one 3 in. diam billet 10 in. long. In a few cases, particularly the didymium-containing alloys, the lack of sufficient amounts of the rare-earth metal limited the size of the billet to 6 to 8 in. All billets were scalped to a diameter of 2 15/16 in. and faced to a length of 9 ¼ in. as limited by the size of the extrusion container. The alloys were extruded into ½ in. diam rod on a 500-ton direct-extrusion press using a 3 in. container. The details of the extrusion step are: billet preheat, 925°F (2 hr); container temperature, 900°F; die temperature, 900°F; extrusion speed, 10 ft per min; reduction ratio, 36:1; and percent reduction, 97.3. The lower melting point of alloys containing didymium' necessitated reduction of the extrusion speed to 5 ft per min in order to prevent hot shorting during extrusion. Adequate lengths were cropped from both ends of each extruded rod to assure that all the material used for tests was extruded under uniform conditions. Tensile and compressive properties at room temperature are reported in the several conditions of heat treatment. The ASTM designations are used to distinguish these conditions as follows: T5—Direct age at 400°F (16 hr) T4—Heat treat at 950°F (4 hr) for alloys containing didymium T4—Heat treat at 1050°F (4 hr) for all other alloys T6—T4 + age at 400 °F (16 hr) The lower heat-treating temperature for alloys containing didymium is necessitated by the lower melting point of these alloys. All heat treatments were conducted in electrically heated, circulating-air furnaces. A protective atmosphere containing 0.5 to 1.0 pct sulphur dioxide was used for the high temperature heat treatments. Tension and creep specimens 6 Yz in. long and compression specimens 1½ in. long were cut from the extruded rod. A reduced section of ? in. diam was machined on the tension specimens, whereas on the creep specimens a reduced section of 0.450 in. diam

Jan 1, 1952

By THOMAS LEONBRD WATSON

INTRODUCTION. IN a paper read by title at the Washington meeting of the Institute, May, 1905,1 discussed at considerable length the geological relations, node of occurrence, and the genesis of the lead- and zinc-ores of the Virginia-Tennessee region. The present paper treats of the purely economic phases of the zinc-ores of the district; such as methods of mining the ores, their preparation and treatment. The Albemarle county mines and plant were discussed in the paper referred to above, and will not be considered here. METHODS OF MINING. Until very recently the mining of lead- and zinc-ores in Virginia was limited wholly to the surface belt of weathering. The mode of occurrence and the character of the ores to be mined were such as to demand the employment of methods used in mining secondary concentrated ores. Accordingly, a system similar to that practiced in mining brown iron-ores was employed, being modified to meet the changed conditions. Oxidized or Soft Ores.-Up to the present time practically all the ore mined in the Virginia district has been of the oxidized or soft type;-the silicate, calamine, and the carbonate, smith-sonite; largely the former, which has been localized and concentrated at only slight depths below the surface. Because of the extreme irregularity with which the limestone weathers when stripped of the overlying residual clay, it presents a roughened surface of large and small irregular "chimneys"

Mar 1, 1906

By R. G. Aspden

The cold rolling and annealing textures were studied for 3 pct Si-Fe grains initially (001) [hkl]. A concentration of (001) [loo] primaries were observed only in the annealing textures of crystals initially having [loo] within 8 deg of the rolling direction. Eke annealing textures of the (001) [I101 cold rolling textures were sensitive to the initial orientation of the grains. Single crystal data were used to explain the formation of (001) [loo] in poly-crystalline malerial. CUBE texture formation in 3 pet Si-Fe sheet occurs during the final high temperature anneal. Its formation is dependent on the proper distribution of (001) plane primaries with reference to the rolling direction&apos; and on the growth of these primaries by secondary recrystallization. The selective driving force for these primaries with (001) within 7 deg of rolling plane is derived from the difference in surface energy between the annealing atmosphere and the crystallographic planes exposed at the surface of the sheet.&apos;-= The alignment of [loo] directions of (001) secondaries with the rolling direction is required for optimum magnetic characteristics7 and is dependent on processing.&apos; A high degree of alignment has been observed when the final cold rolled texture has a strong (111) [ll2] type component3 and the normal grain growth texture prior to secondary recrystallization has components with a [loo] parallel to the rolling direction and planes from (001) to (110) parallel to the rolling plane.1,3,8,9 Generally, this (001) component is much weaker than the (110) component. The growth rate of (001) plane primaries to secondaries has been found to be independent of the orientation of the primaries with reference to the rolling direction, i.e., the secondaries have the same degree of alignment of [loo] directions with the rolling direction as the (001) primaries.&apos; Hence, the rolling and annealing textures of individual grains or single crystals are of interest in understanding the development of the (001) [loo] secondary recrystallization texture. (001) components have been observed in the annealing textures of cold rolled grains initially having a [loo] parallel to the rolling direction and an (001) rotated up to 30 deg from the rolling plane. Crystals initially near the (001) [loo] orientation when rolled under the influence of constraints imposed by neighboring grains form deformation bands and ro- tate in both directions toward (001) <110>.10,11 Deformation bands have been reported also for crystals initially with an (001) within 1 deg of the rolling plane and a [loo] within 1 deg of the rolling direction when rolled as a free single crystal.12 These crystals have weak recrystallization textures and contain near an (001) [loo] component.10-12 When near (001) [loo] crystals are rolled as free single crystals no deformation bands form and the crystals rotate by a single rotation toward (001) [110]. Recrystallization after a 70 pct cold reduction yielded near an (001) [loo] component13 and after a 90 pct cold reduction an (001) [I201 component." Crystals initially near (210) [001] had a texture after a reduction of 70 and 84 pct which was similar to the (111) [li2] but rotated 10 to 15 deg in the transverse direction. These crystals recrystallize to (210) [OOl] or (410) [001] and contain an (001) [loo] component.10,13 An (001) component has not been detected in the normal grain growth textures of other single crystals. Crystals initially having orientations between (110) [001] and (111) [ll2] have a cold rolled texture of principally (111) [ll2] .10>16 Other crystals with a [I101 parallel to the cross direction rotate to (111) [112] and/or (001) [110] stable end orientations. Crystals initially having from (001) [110] to (111) [lie] retain this orientation after cold rolling.15 The cold rolled textures having [I101 directions parallel to the rolling direction had components in the annealing textures related to the deformation textures by 25 to 30 deg rotations about common (1 10) poles. Cold rolled textures of the (111) (112) type recrys-tallized to (120) [001] or (110) [00l]. The purpose of the present work was to further the understanding of the alignment of [loo] directions of (001) secondaries with the rolling direction. The cold rolling and annealing textures of grains initially (001) [hkl] were studied. These data were applied to the formation of (001) [loo] by secondary recrystallization. PROCEDURES AND EXPERIMENTAL TECHNIQUES The (001) poles near the sheet normal and rolling direction are given in Fig. 1 for the 10 grains studied. Each of these grains was located in the center of a polycrystalline specimen approximately 25 mm wide and 50 mm long. The lower case lettered grains, a through dl were about 1.2 mm in diam and near the (001) [loo] orientation. Specimens containing these grains were from a commercial 3 pct Si-Fe alloy with the principle orientation of (110) [001] as obtained by impurity inhibition of growth with manganese sulfide inclusions.17,18 Upper case lettered grains, A through F, were about 6 mm in diam and had (001) planes near the rolling plane and [hkl] di-

Jan 1, 1963

By William T. Folwell

The Lucky Friday mine east of Mullan, Idaho, is an outstanding example of a property in the Coeur d’Alene district where a small and insignificant- appearing silver-lead-zinc vein at the surface has changed at depth into a large vein of great importance. The Lucky Friday vein has little if any surface expression and above the 1200 level the ore shoots are small and discontinuous. Between the 1200 level and 2450 level, the lowest developed level, the main ore shoot has shown remarkable improvement on each succeeding lower level, and today the mine is one of the major lead-silver producers in the Coeur d&apos;Alene district. History: The Lucky Friday property is on the north side of the South Fork of the Coeur d&apos;Alene River in sections 25, 26 and 35, T. 48 N., R. 5 E., Hunter mining district, Shoshone County, Idaho. This is about one mile east of the town of Mullan, which serves the eastern portion of the Coeur d&apos;Alene district. The southern part of the property is crossed by a branch line of the Northern Pacific Ry. and by U. S. Highway 10. This highway is the principal road crossing the panhandle of Idaho and connects the district with Spokane, Wash., on the west and Missoula, Mont., on the east. The main portal and surface plant of the Lucky Friday mine is at an elevation of 3365 ft, only a short distance above the valley floor and a few hundred feet from U. S. Highway 10, so the mine is readily accessible for year-round operation.

Jan 12, 1958

By Lyon F. Terry

IN contemplating the prospects of natural gas being transported from the fields where it is produced to such distant points as Philadelphia, New Jersey, New York City, and New England, let us review the advance that natural gas has made and the projects currently scheduled for construction. This may give us a perspective of the point in the long-range development of the natural gas business in which we now find ourselves, and some basis for judging the further expansion of the industry. Authentic statistics of the total marketed production of natural gas in the United States have been compiled by the Bureau of Mines since the year 1906. The growth of the business is indicated by the following data on marketed production for each ten-year interval since 1906:

Jan 1, 1947

By F. C. Frischknecht

Most early development and application of electromagnetic prospecting methods took place in Scandinavia, where geological conditions favor their use. In other parts of the world these methods have aroused cycles of interest, but in Scandinavia they have been used continuously and successfully since the 1920&apos;s. Electromagnetic methods may be classified into two general groups. One group includes methods in which the source of the electromagnetic field remains stationary while the receivers are moved about to explore the area. The other includes procedures in which the energizing and receiving systems are moved together. Other classifications could be based on the size of the energizing source, the particular components of the electromagnetic field which are measured, or the mode of transporting the equipment. The difference between fixed-source and moving-source methods, however, is of such great fundamental importance that it will be emphasized in this discussion. FIXED-SOURCE METHODS Essentially, a fixed-source method consists of the measurement of electromagnetic fields about the source. The mutual coupling between the source and the earth is constant, but the mutual coupling between the receiver and the earth (unless the earth is homogeneous) and also between the source and the receiver changes at each station. The results are usually normalized by relating the field data to the calculated free space or primary field. Turam and Radio Reference Signal Methods: The turam or two-frame* (see Fig. 1A) is probably * Turam means two-coil. the most common fixed-source method. The energizing source is an insulated cable grounded at both ends or formed into a large rectangular loop. Measurements are taken along a traverse at 5 to 50-meter intervals using two small receiving coils, the lagging coil being placed at the position previously occupied by the leading coil. The complex ratio (i.e., inphase and out-of-phase ratios) of the voltages induced in the two coils is measured. Operating frequency range is about 100 to 800 cps. In a typical turam survey a straight, grounded cable several kilometers long is laid out parallel to the probable strike of the ore deposits or conducting strata being sought. An area extending 1 or 2 km on each side of the cable, and within 1 or 2 km of the ends of the cable, is surveyed. Measurements are made at stations 5 to 25 m apart along traverses perpendicular to the cable. Measurements may be made along lines parallel to the cable to serve as base lines for the traverses or for other special purposes. Commonly the receiving coils are oriented with their planes horizontal so that only the vertical component of the field is measured. If additional information is required, one of the hori- zontal components may also be measured by orienting the coils with their planes vertical. In a modified turam technique developed recently for both ground and airborne measurements (Fig. 1B) the amplitude of the complex voltage induced in a single receiving coil is measured and its phase compared with that of a reference signal transmitted from the energizing system by a radio frequency carrier. Thus the un-normalized field is obtained directly, whereas with the turam method it is obtained by calculation from the ratios. The turam method and its modifications have a greater working depth than the other electromagnetic procedures used in ore prospecting. Under favorable conditions conductors have been located at depths of 200 to 300 m. A modified turam method with one of the electrodes grounded in the upper end of a plunging orebody was used to follow the extension of this body to a depth of 200 m beneath a layer of conducting schists. Straight grounded cables are usually preferred to insulated loops because they are easier to lay out and because they often make the method more sensitive. The greater sensitivity of a grounded cable is a result of ground return currents which may flow in the orebodies in addition to the eddy currents caused by induction from the current in the cable. Anomalies in the vertical field due to eddy currents are characterized by a correspondence between high values for the inphase component and positive out-of-phase components and/or low values for the inphase component and negative out-of-phase components. Also the inphase component may approach zero, but it does not become negative. In very long continuous conductors that are parallel to a grounded cable the effect of ground return currents may far exceed the effect of eddy currents. These ground return currents cause a lack of correspondence between the inphase and out-of-phase components and may cause negative inphase or anti-phase components. It becomes difficult to carry out the measurements and often difficult to interpret the results. Such results immediately suggest the presence of graphitic strata, however, since ore deposits are rarely extensive enough to accumulate sufficient ground return current to cause these results. A cable laid out perpendicular to the strike or an insulated loop is sometimes used in areas where graphitic schists and slates are present. Anomalies are then completely or almost entirely due to eddy currents and are easier to interpret. The measured voltage ratios are normalized by either subtracting or dividing by normal field ratios calculated from free space considerations. The normalized ratios are then plotted as individual profiles. When significant anomalies occur in the ratio measurements, the actual normalized fields are calculated by beginning with a measured or an assumed value for the field at a point near the cable and successively multiplying this value by the normalized ratios. There is a similarity between this process and a numerical integration of the ratio curve. Conversely, in many respects the ratio curve is similar to the first derivative of the field curve.

Jan 1, 1960

By J. W. Buch

IN THE FIELD of track haulage, interest has seemed to center on the question of larger mine cars both for handling material from loading point to shaft bottom or surface, and for shuttle service. Saving of time in car changing is obvious if larger cars are used. In addition, shorter trips result where car transportation is from face to opening without transfer. This also brings about side-track and equipment savings. Track shuttle service, using large automatic-dump cars (10 tons) between loading machines and trip loading point, has been a satisfactory solution for the operator who mechanizes a working mine regularly equipped with a large number of small mine cars. This development in track shuttle haulage, has made track installation and maintenance increasingly important, requiring closer supervision.

Jan 1, 1942

By W. H. Class

The embrittling effects of oxygen, ozone, nitrogen, air, and surface residues, on NaCl has been investigated. The embrittlement by ozone and oxygen was found to be associated with the formation of a NaClO3 surface compound. In these cases the initial crack that was responsible for fracture (in a bend test) always nucleated at the corners between the tension and side faces. The behavior of air was very erratic and on certain days did not produce enzbrittlement. During these periods, crystals that had become embrittled by the ozone treatment completely recovered their ductility after a short exposure to the ambient atmosphere, It was established many years ago1 that considerable ductility could be obtained in NaCl single-crystal specimens if the crystal surfaces were dissolved in water either during or immediately prior to the test. The original interpretation of this effect by Joffe attributed the enhanced ductility to the removal of surface microcracks by dissolution. Later investigations2&apos;3 have suggested that the exclusion of air from the specimen surface is the criterion for extensive plastic flow prior to fracture. The air em-brittlement in this later work was attributed to the diffusion of gaseous atoms into the surface layers of the crystal, thereby impeding the movement of dislocations. This model satisfactorily accounts for the reembrittlement observed after further air exposure subsequent to the water dissolution treatment. However, the situation has recently become more complex by the observations in several laboratories4-t that under certain conditions air exposure does not impair the ductility of NaC1. It has also been recognized5 that improper drying operations after water dissolution can leave surface precipitates that lead to embrittlement. Cleavage defects on as-cleaved crystals can often be another source of embrittlement. In the present work the effect of the gaseous atmospheres nitrogen, argon, air, oxygen, and ozone, on the ductility of rock salt was studied extensively. The embrittlement resulting from oxygen and ozone exposures was found to be associated with the formation of a NaC1O3 surface film. It is suggested that certain atmospheres, one of which often can be ambient air, which inhibit the formation or favor the decomposition of this compound, can promote ductility. Thus one aspect of the Joffe effect is certainly related to the removal of surface compounds or complexes by water dissolution. The effect of surface precipitates that remain after drying operations and of cleavage defects were also studied. In neither of the latter cases was the embrittlement as severe as that found with a NaClO3 surface layer. PROCEDURE AND SPECIMEN PREPARATION The nature of the embrittlement produced by the agents mentioned above was studied by means of microscopy, mechanical testing, and X-ray diffraction. Specimens were cleaved from large crystals of optical quality sodium chloride obtained from the Harshaw Chemical Co., and, except for those tested in the as-cleaved condition, were given a 15- to 20-sec immersion in distilled water followed by a rinse in absolute methyl alcohol. The specimens were then blotted on a soft, absorbent paper, and dried by a few seconds exposure to a stream of warm, dry air. Such a procedure was found to give a control surface which was microscopically free of residues. (A few crystals were intentionally painted with a concentrated NaCl solution in order to investigate the effect of surface residues). All specimens were of 0.140 sq in. cross-section. Crystals prepared in the above manner were immediately placed in a gas train where they could be exposed to the desired gases for preselected periods of time. For the oxygen and nitrogen exposures, pure reagent-grade gases were employed. The ozone was provided in the form of an ozone-oxygen mixture (approximately 10 pct ozone) prepared by passing commercial grade oxygen over a strong ultraviolet light source. All gases were dried prior to their introduction into the train. Since argon was found to be completely inert in its behavior (i.e., residue-free specimens that were exposed to argon were not embrittled), it was periodically utilized to check the control specimen surfaces as well as the condition of the gas train used for aging the specimens. After exposure to the gaseous media in question, the crystals to be used for the measurement of the strain to fracture were transferred from the gas train to a protective oil bath (without further exposure to the atmosphere) where the tests were conducted in three-point bending. The apparatus was so adjusted that the load could be applied at a constant, continuous rate. Other Snecimens from the gas train were deformed

Jan 1, 1962

By N. V. Melnikov, L. N. Marchenko

The latest theoretical and experimental study of physical processes initiated by explosions in solid media have made it possible to obtain a deeper insight into the mechanism of the energy transfer to ambient rock from char es of explosives interspersed with various air gaps. As shown in (17, high explosive action causes excessive fragmentation of medium in the vicinity of the charge, while expansion of the process into the massif is negligible. A theoretical outline of a more rational application of explosion energy was given with a view of obtaining more uniform fragmentation of rock convenient for loading and transportation. The proposed idea proven by experimental study consisted of the possibility of explosion control based on redistribution of explosion energy. Practical realization of the above idea was proposed (1) involving charges with air gaps for rock fragmentation. Since the Rolla Symposium on Mining Research (USA, 1961) (2), borehole charges with air gaps have become common practice. This method of rock blasting is applied in open cast and underground mines working the hardest and viscous, hard, medium hard and soft rocks (ore, quartzites, granites, 1 imes tones, sandstones, coals, etc.) as well as at enterprises for extraction of building materials and raw chemical minerals of any strength. Application of charges with air gaps results in an increase of the degree and uniformity of fragmentation (up to 94 percent of the blasted rock mass consists of fragments not exceeding 400 mm), the average fragment size decreases by 1.5-2 times and the amount of lumps is reduced by 2-10 times (in some cases there are no lumps at all ). Besides, the amount of operation for filling boreholes with tamping material is reduced, the specific consumption of explosives

Jan 1, 1971

By S. Warren Hobbs

The section of the Northwestern United States that includes the northern Rocky Mountains and adjacent areas to the west and east is one of large mineral production and important mineral potential. The metallic ore deposits vary widely in age and type and their geologic settings are similarly diverse. A brief resume of the region's physiographic characteristics and geology sets the framework for the selected ore districts that are described in following papers and makes it possible to place these ore deposits in their proper reference to space and time.

Jan 1, 1968

By William Phillips

THE earliest mention of the sulphur deposits in what is now Culberson County, Texas, seems to be contained in "Explorations and Surveys for a Railroad Route from the Mississippi River to the Pacific Ocean, United States War Department, 1853-54." Captain John Pope (he was not commissioned Captain until 1856) had charge of one of the divisions of the Survey. In his report on the geology of the route, William P. Blake noted the analysis of a greenish earthy powder from the bed of Delaware Creek, at the springs, which contained 18.28 per cent. of free sulphur. The report states: "From the chemical examination of the waters of the spring, by Dr. Booth, it appears that chloride of sodium is the principal solid ingredient, but considerable quantities of sulphide of sodium are present. * * * * * The waters from the springs examined by Dr. Booth were alkaline, but it is possible that some of the springs are acid; and in this case the precipitation of sulphur would ensue on the mixture of the acid waters with those charged with alkaline sulphurets and the origin of the deposits of sulphur would he thus explained." This is the first reference to the existence of sulphur in that region, the first mention of the character of the water found there and the first suggestion as to the&apos; origin of the deposits. The possibility of the existence of acid waters was confirmed by E. M. Skeats, nearly 50 years later.1 In this publication, Skeats says that the water from the sulphur deposits in Section 11, Block 114,, Township 5, contains 79.08 grains of free sulphuric acid per gallon. This locality is about 13 miles (21 km.) south of Delaware Creek and about 35-miles (56 km.) east of the Delaware Springs. The next published reference to the existence of sulphur in Trans-Pecos Texas is in the First. Annual Report of the Geological Survey of Texas, 1889, page 226, where W. H. von Streeruwitz mentions that sulphur is found in that region, but gives no further information. In the

Jan 9, 1917

By J. R. McWilliams

Several of the current concepts of brittle fracture involve consideration of the existence of defects or flaws. Griffith 1 observed that the tensile strength of brittle materials was several orders of magnitude less than might be expected from the calculated strength of the molecular bonds. He was able to show that the stress concentration at the tip of an elliptical crack is sufficient to raise the local stress level many fold. He therefore proposed that real materials do contain such stress risers in the form of minute cracks and that this accounts for the rather large difference between theoretical and actual strengths of brittle materials. The degree of stress magnification depends to a great extent upon the orientation of the crack with respect to the general stress system, and to the general geometry of the crack.

Jan 1, 1967

By S. H. Ash

IN no part of the world other than a small area in Pennsylvania is anthracite mining an industry of major magnitude. As the deposits of anthracite in the United States are limited virtually to Pennsylvania, the difficulties of this industry have been commonly considered a state rather than a national problem. However, there is also national interest in the conservation and wise utilization of all the country&apos;s fuel resources and in the control of interstate waterways. The anthracite industry is confronted with a serious problem of water accumulation in many of the mines, a problem that must be solved in the near future if progressively higher mining costs are to be avoided. It cannot be solved by the operating companies without state or Federal aid, or both, owing to the magnitude of the work required, the diversity of interests of the coal and surface ownerships, the hazard to the whole mining community, and interests affected outside the mining region. &apos;The costs of abating the ever-increasing surface seepage to mine workings and of handling this seepage once it has occurred are beyond the eco¬nomic resources of the operating managements.

Jan 1, 1941

By R. F. Lynch, J. D. Wood

The Al-1.0 pct Mg alloy 565 7 was studied using optical microscopy and electron microprobe X-ray analysis. Constituent particles were found to exist inter-dendritically in the as-cast material in a region of precipitate free a -aluminum. Five phases besides a fine precipitate and a-Al were identified in the cast structure: Fel3, Fe2Al7, Mg2Al3, CUMgAl2, and Cu2FeAl7. Thermal treatments conducted for 100 hr at 1180°, 1130°, 1080°, 1030°, 980°, and 880° F revealed a general dissolution and spheroidization of the in-terdendritic constituent network observed in the cast structure. The principal constituents present in the thermally treated structures were FeAl3 and Fe2Al7 with the relative amount of Fe2A17 to FeAl3 increasing with a decrease in the treatment temperature. The phases Present in the wrought structure were identical to those observed after the thermal treatments, with the constituent particles strung out in the direction of rolling. ALLOY 5657 is a nonheat-treatable commercial purity Al-1.0 pct Mg alloy utilized extensively because of its bright finishing characteristics. This investigation was conducted to determine the constituents present in 5657 alloy, and to study the effect of extended thermal treatments on morphology. Numerous studies have been carried out to establish the equilibrium diagrams for various aluminum systems,1-3 with phase identification based on X-ray analysis, morphology, and the etching response of relatively large particles. Phragmen4 conducted a study of the phases in aluminum eutectic systems and compiled a "corrected" table of etching responses, drawing on his work plus that of Schrader,5 Keller and Wilcox,6 and Mondolfo.7 A review of the original work of Keller and Wilcox, and Mondolfo, which was concerned with the constituents found in commercial alloys, reveals that in numerous cases their etching responses differ from those reported by Phragmen and from each other. These inconsistencies may occur because a specific constituent will react to a given etch in a varying manner depending upon its size, the elements dissolved in the phase, the other constituents surrounding a phase, and the solute content of the matrix. Work with a commercial orientation was conducted on alloys 2024 and 3003 by Sperry8,9 and on alloy 3003 by Barker,10 where the relationship between the phase diagram and the nonequilibrium structure of an alloy was examined. Backerud11 investigated the A1-Fe binary system and found that at high cooling rates the equilibrium eutectic reaction forming a-A1 and FeA13 is replaced by another lower temperature eutectic reaction forming a-A1 and metastable FeAl6, a constituent first identified by Hollingsworth et al.12 Most of the above mentioned studies were conducted on materials having a significantly greater alloy content than 5657 alloy, where the relatively small size and sparse distribution of second phase particles hinders the process of identifying constituents. EXPERIMENTAL PROCEDURE Material with a composition as given in Table I was examined in the as-direct chill cast, hot rolled and cold rolled conditions, and after thermal treatment of the cast structure. Thermal treatments were terminated by a water quench. Microscopic examination was conducted under various lighting conditions following the application of standard etchants as specified in Table 11. A semi-quantitative electron microprobe X-ray analysis was conducted for Al, Mg, Fe, Cu, Si, Zn, and Ti. RESULTS AND DISCUSSION Microstructure of the As-Cast Material. Particles of second phase material were found to exist inter-dendritically, principally in regions of precipitate free a-Al, as illustrated in Fig. 1. Adjacent to the ingot edge was a region of inverse segregation, resulting in an increased amount of second phase material containing large sized particles which aided in phase identification. Phase Identification. Cast Structure. Five phases besides a-Al and a fine precipitate were identified using optical microscopy and electron microprobe X-ray analysis, as presented in Tables II and III, respectively. FeA13 and Fe2A17 are often found with Fe2A17 forming a sheath around the core of FeAl3, resulting from an incomplete peritectoid reaction. These phases have a nearly identical appearance under white light, although they are easily differentiated under crossed polarizers, as characteristically illustrated in Figs. 2(a) and 2(b), respectively. Microprobe analysis con-

Jan 1, 1970