By T. B. Counselman

An iron blast furnace of 1000 tons daily capacity will produce a 100,000 cu. ft. per minute of blast-furnace gas. This contains a 25 per cent of carbon monoxide, and has a B.t.u. value of about 95. gas is used primarily for heating the stoves of the blast furnace, secondarily, under boilers, for steam production. Occasionally it is used in gas engines. The raw gas coming out of the furnace carries about 10 grains of dust per cubic foot of gas, under best operating conditions. With furnace "rolling" or slipping, this quantity may temporarily be gre increased. This dust would, of course, deposit on the checkers o: stoves, or plug the burners under the boilers; therefore the gas : be cleaned. Flow Sheet The first step in the cleaning operation, as shown by the flow s Fig. 1, is a dry dust catcher, of which there are several forms, partially cleaned gas next goes to a primary wet washer, where v sprays knock down most of the solid particles. If further cleani desired, the gas may then go to electrical precipitation. Again, the removed is collected in water. Dry dust catchers reduce the dust col from 10 grains to between 4 and 6 grains per cubic foot, and rec roughly half of the total flue dust in the gas. The wet washers rea most of the remaining dust, reducing the dust content to about 1/4 per cubic foot. Electrical precipitators, if used, further reduce the content to about 0.01 grain per cubic foot of gas. The flow sheet s the dust content of the gas at various steps in the treatment and als content of solids in the water. It should be noted that some plant less water on the primary wet washer than indicated, and that ofte solids content of the scrubber water will be 300 grains per gallon, or much higher. Reasons for Recovering Flue Dust.—There are two main incentive recovering flue dust from the scrubber water: (1) the value of the (2) stream or lake pollution, where such a reason applies.

Jan 1, 1937

By R. L. Rickett, N. C. Fick

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By J. M. Cases

Study of the normal interaction between flotation collectors and the silicates through measurement of the electrokinetic potential carried out by the streaming potential and flotation recovery methods indicates that the interaction is wholly 07 partly of electrostatic origin. In some cases, it partly consists of the chemical affinity of the polar head of the collector for the active surface sites. Reagents composed of a polar head and a paraffinic chain and forming micelles in solution were used as flotation collectors. They are sodium dodecylsulfate (anionic collector) and dode-cylammonium chloride (cationic collector). The adsorption isotherms on biotite of alkylamine chloride having 10 to 18 carbon atoms in their chain all show a sharp change in slope relevant to the condensation of alkylammonium ions into bidimensional phase.1-1 Condensation is possible because of the relative homogeneity of the adsorbing surface and of the very strong lateral binding forces through Van der Waals type bonds in the adsorption layer. The different isotherms are seen to coincide when, instead of the equilibrium concentration, the under-saturation ?µ = kT In C/C, is plotted in abscissa, C representing the concentration of the solution with which the adsorbed layer is in equilibrium and C, the saturation concentration of micelles in solution or. critical micellar concentration. More particularly, the undersaturation ?,u1*, corresponding to a surface coverage 6 of 0.5, is equal to Since silicates immersed in aqueous solutions show a surface charge which is a function of pH, it is of primary importance to study the influence of this parameter on the adsorption of collector ions acting as Strong electrolytes in the pH range where they are utilized. The aim of this present paper is to determine by studying electrokinetic phenomena and recovery curves effectuated with a cationic collector and a anionic collector, the nature of the normal adsorbate-adsorbent interaction. Tables 1 and 2 sum up part of the results previously obtained'H11 for the determination of the point of zero charge of the silicate studied by the streaming potential method. Throughout the remainder of this paper, the surface charge will be considered positive for all values of pH below the point

Jan 1, 1971

By N. C. Fick, R. L. Rickett

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By N. C. Fick, R. L. Rickett

DESPITE the large volume of literature on alloys of iron and silicon,1 there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carbon and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in, sheet and strip form, the constitution was determined of a series of commercial silicon steels containing 0.05 to o.08 per cent carbon and 0.20 to 4.31 per cent silicon, over the temperature range 1300° to 2500°F. These alloys were all from regular production heats and of commercial quality. The results of, the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented. MATERIAL AND PROCEDURE All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness-the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. [ ] The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired. range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1946

By P. W. George

This paper presents geological data regarding deposits of over 7,500,000 tons of fine-grained sulphide ore in barite gangue. A series of pyroclastics and arkoses was intruded by sills of quartz porphyry in connection with batholithic intrusions of granite 3 miles from Buchans. Gentle folding, with fracturing and shearing of tuff beds and intruded quartz porphyry, accompanied and followed the intrusion of granite and porphyry. The sulphide-barite mineralization is localized primarily in fractured and sheared tuff beds, but also in the sheared quartz porphyry. Two structures have proved particularly favorable for mineralization-one, the center of an anticline; the other, a series of weak, incompetent tuff beds intruded by thin sills of quartz porphyry and located between strong beds of arkose. During the folding the weak tuff with intruded quartz porphyry was intensely sheared and contorted and subsequently mineralized by sulphides and barite. INTRODUCTION Buchans is 5 miles north of Red Indian Lake, in Central Newfound- land, at an elevation of 900 ft. above sea level and 400 ft. above Red Indian Lake, and is reached by a 37-mile private railway from Miller- town Junction. The first ore body found at Buchans was discovered some 30 years ago in the bed of Buchans River, by Matty Mitchell, an Indian woodsman employed by the Anglo-Newfoundland Development Co. Ltd. In the years following the discovery the ore was developed by shaft-sinking and drifting, with results indicating a lenticular ore body in a shear zone, containing about 100,000 tons of extremely fine-grained sulphide ore in barite gangue averaging about 0.05 oz. Au, 4 oz. Ag, 1.5 per cent Ch, 10 per cent Pb, 18 per cent Zn. Because a profitable metallurgical treatment for the ore was not found, the mine was closed down in 1911. In 1915, Mr. H. A. Guess, Vice President of the American Smelting & Refining Co., learned of the Buchans River ore body, and after metallurgical tests had been carried on from time to time in his company's testing plant a satisfactory separation of the sulphides by selective flotation was finally effected in 1925. Prospecting for additional ore bodies was begun in 1926, utilizing geophysical methods under the direction of Hans Lund-

Jan 1, 1937

By D. A. Thomas, M. F. Comerford

Poly crystalline wires of Fe-3.2 wt pct Si were cold-drawn to 31, 66, and 87 pct reductions of area. Mechanical properties and tnicrostructures were studied after recovery and re crystallization. An initial increase in strength during recovery was ascribed to strain aging, and subsequent softening was largely due to polygonization rather than re-crystallization. No unique actioation energies could be determined for the recovery process. Rather, activation energies ranged from 60,600 cal per mole at 10 pct recovery to 83,200 cal per mole when recovery was 50 pct complete. Sites for the nucleation of recrystallization were found to depend on time and temperature. In the early stages of re-crystallization, nucleation occurred in deformation hands. Later, or at high temperatures, recrystal-lized grains were nucleated primarily al grain boundaries. Polygonized structures did not seem to be preferred sites for nucleation. MUCH of the research on deformation, recovery, and recrystallization processes in bcc materials has been performed on single crystals or lightly worked polycrystals. Little study has been devoted to the relation of mechanical properties to micro-structure in polycrystals after severe deformation and subsequent annealing. This paper presents the results of a study of the tensile properties and microstructures of Fe-Si wires drawn varying amounts and annealed at a series of temperatures. EXPERIMENTAL PROCEDURE The experiments were carried out on an alloy of the following composition: 3.2 wt pct Si, 0.08 Mn, 0.016 C, 0.005 0, 0.0002 N, 0.0001 H, 0.008 P, 0.034 S. The material was received as l-in.-sq bars cut longitudinally from a hot-rolled slab provided by the Armco Steel Corp. The bars were forged to 3/8-in. rounds, centerless-ground to 0.250 in., and swaged to '0.108 in. All subsequent reductions were performed by room-temperature wire drawing at the rate of 2 in. per min. Each preliminary draft gave approximately 30 pct reduction of area and was followed by a l-hr anneal at 1010°C in dry hydrogen. Three lots of wire were made with ultimate cold reductions of 31, 66, and 87 pct reduc-

Jan 1, 1965

By P. W. George

This paper presents geological data regarding deposits of over 7,500,000 tons of fine-grained sulphide ore in barite gangue. A series of pyroclastics and arkoses was intruded by sills of quartz porphyry in connection with batholithic intrusions of granite 3 miles from Buchans. Gentle folding, with fracturing and shearing of tuff beds and intruded quartz porphyry, accompanied and followed the intrusion of granite and porphyry. The sulphide-barite mineralization is localized primarily in fractured and sheared tuff beds, but also in the sheared quartz porphyry. Two structures have proved particularly favorable for mineralization—one, the center of an anticline; the other, a series of weak, incompetent tuff beds intruded by thin sills of quartz porphyry and located between strong beds of arkose. During the folding the weak tuff with intruded quartz porphyry was intensely sheared and contorted and subsequently mineralized by sulphides and barite. Introduction Buchans is 5 miles north of Red Indian Lake, in Central Newfoundland, at an elevation of 900 ft. above sea level and 400 ft. above Red Indian Lake, and is reached by a 37-mile private railway from Miller-town Junction. The first ore body found at Buchans was discovered some 30 years ago in the bed of Buchans River, by Matty Mitchell, an Indian woodsman employed by the Anglo-Newfoundland Development Co. Ltd. In the years following the discovery the ore was developed by shaft-sinking and drifting, with results indicating a lenticular ore body in a shear zone, containing about 100,000 tons of extremely fine-grained sulphide ore in barite gangue averaging about 0.05 oz. Au, 4 oz. Ag, 1.5 per cent Cu, 10 per cent Pb, 18 per cent Zn. Because a profitable metallurgical treatment for the ore was not found, the mine was closed down in 1911. In 1915, Mr. H. A. Guess, Vice President of the American Smelting & Refining Co., learned of the Buchans River ore body, and after metallurgical tests had been carried on from time to time in his company's testing plant a satisfactory separation of the sulphides by selective flotation was finally effected in 1925. Prospecting for additional ore bodies was begun in 1926, utilizing geophysical methods under the direction of Hans Lund-

Jan 1, 1937

By William E. Harris

Time and experience have demonstrated that by means of the Waelz process zinc, lead, cadmium, arsenic, antimony, bismuth and tin can be volatilized satisfactorily. In this way difficult gold ores are being treated to allow for the recovery of the precious metal. Iron ore containing zinc is being treated to remove the zinc and recover the iron. In Germany, thallium is being recovered in commercial quantities from the zinc oxide fume; indium, germanium and gallium are also concentrated to a degree warranting recovery, even though these rare metals are only recognizable in the ore by means of the spectroscope. The physical, chemical or mineralogical condition of the raw material affects very little the applicability of the process. The name Waelz is derived from the German word Waelzen, meaning a "trundling motion," which very aptly describes the movement of the charge through the slowly rotating kiln. The recovery of zinc and lead by volatilization in a rotary kiln has its origin in a process patented in 1910 by Edward Dedolph, of British Columbia. The Dedolph patent was taken over by the Metallgesell-schaft of Frankfurt-on-Main, Germany, which in cooperation with the Griesheim-Elektron, now a part of a large industrial combine, introduced certain improvements (Ohlmer, Specketer patents), but without bringing the process to a state suitable for large-scale operations. The war temporarily stopped all work on the process, and it was not until after the war that the Krupp Grusonwerk, of Magdeburg-Buckau, Germany, quite independently of the Metallgesellschaft, instituted research work in this field of metallurgy, which in 1923 led to the Waelz process proper. The Krupp Grusonwerk and the Metallgesellschaft A.G. later on collaborated, and by their joint efforts further developed and perfected the Waelz process, which they are marketing together as "Waelz-Gemeinschaft." The process is capable of treating a varied type of material; for instance, oxidized and sulphide zinc ores, calamine (zinc carbonate ore) waste dumps, jig tailings, jig slimes, table concentrate slimes, brass ashes, zinc-bearing iron ores (where the iron sinter is the real objective and the zinc oxide a by-product), electrolytic-zinc leach residues, zinc muffle residues and works sweepings, lead-furnace slags, tin ores and slags, anti-

Jan 1, 1937

By F. H. Wilson

Copper base alloys containing various amounts of aluminum and silicon are of considerable commercial interest. In particular the alloy containing 7 pct aluminum and 2 pet silicon shows an attractive combination of high strength with excellent, machinability. Since there is no evidence ill the literature that this ternary system has been studied since the recognition by Smith1 and Anderson2 in 1939 of the kappa phase of the binary copper-silicon system, the determination of the equilibrium phase relationships in the copper corner of the ternary diagram has been undertaken to provide a fundamental basis for understanding the behavior of these alloys. Phase boundaries have been determined by the micrographic examination of quenched samples while points on the liquidus surface have been obtained by thermal analysis. The results, of sufficient precision to serve their major purpose of providing a guide for the control of the manufacture of alloys in the region covered, are presented in a series of both isothermal and vertical sections of the diagram. Alloys StVdied For a rough survey of the copper corner of this ternary system the compositions listed in Table I (Series A) were employed. The results of examinations of these alloys indicated that the compositions listed in Table 2 (Series B) would further clarify regions of greater complexity. All alloys were prepared as 1200 g heats, the copper being melted under charcoal, and then first silicon and then aluminum were added. An excess of 0.05 pet silicon was allowed to cover deoxidation losses. Two small bars 5/8 by 1 1/4 by 5 1/4 in. were cast using Durville type casting equipment. Ailalyses were made on all alloys using material which was hot-rolled at 800 or 850°C and annealed 17 hr at 650°C. All analyses were found to be within 0.05 pet of the nominal composition. Since the precision of analysis is not much better than this, the points of both isothermal sections and vertical sections at fixed aluminum and silicon contents have been plotted at the compositions indicated by the nominal composition.

Jan 1, 1949

By Maurice Cook

NORMALLY the grain size of cold-rolled and annealed copper sheet is of the order of 0.02 to 0.06 mm., and 0.1 min., for example, would, for many purposes, he regarded as undesirably large. The occurrence of very large grain sizes in a few isolated cases of copper sheet led the authors to inquire into the causes giving rise to such unusual results. During the course of this work a very large number of experiments have been carried out to determine the effect of varying the conditions of the final and penultimate rolling and annealing operations, as well as of earlier rolling and annealing treatments. A correspondingly large number of observations have been made, but within the space of one paper it is possible only to outline relatively briefly what appear to be the more important of these experiments and observations. The presentation of the results does not follow chronologically the order in which the experiments were carried out and they have been rearranged for the sake of simplicity. In recent years a considerable amount of work has been done in connection with the recrystallization and grain growth in metals and alloys that take place on annealing, and a number of generalizations have been reached. It is known that the crystal size in wrought material in the annealed condition depends on a number of factors, including the time and temperature of the annealing operations and the nature and amount of cold-work to which the material has been subjected. Results, however, that are not covered by these generalizations can be obtained, which, in some instances, may even appear to he contradictory to them. According to these generalizations gradual changes in grain size are effected by progressive variation of the factors involved in annealing or cold-working. The work recorded in the present paper, however, relates to the development of grain sizes which are far beyond those normally encountered in ordinary annealing operations and far in excess of grain sizes which, according to ordinary standards, would be classified as coarse or large.

Jan 1, 1938

By C. Richards Honeycutt, Frederick C. Langenberg, Guenter Pestel

Solidification in a moving electromagnetic field was successful in altering the as-cast grain structure of steel ingots. The equipment is described and exerimental results are presented for several different alloys. Conditions for optimum grain refinement are described and an empirical design constant presented. The effect of the grain refinement on hot workability is briefly discussed. T HE grain structure of a steel ingot teemed into a metal mold can be defined by macroscopic examination in semiquantitative terms. For example, the relative volume of obviously differing structures can be estimated with the classic definitions of chill, columnar, and equiaxed zones. Experimental evidence has proven that the grain structure of an ingot is affected by changes in such factors as teeming temperature, rate of teeming, degree of turbulence, size of ingot, mold characteristics (including preheat temperature, design and coating), and composition of the metal (especially as it affects the range of solidification). Significant advances have been made in fundamental solidification studies; but the principles which have been developed are difficult to apply tothe complex and changing phenomena that occur simultaneously during ingot solidification. In particular, many attempts have been made to refine the as-cast structure of ingots, with special emphasis on the columnar grains. The formation of large columnar grains is generally considered harmful to the further fabrication of an ingot. It may also result in undesired ani-sotropic properties. However, columnar grains are not undesirable in all grades, or product applications, and caution must be exercised to determine in which grades and applications columnar grains are not desired in the ingot. Although the literature on the refinement of as-cast ingot grain structures is too vast in general to review here, it is noteworthy that such methods are additions of artificial nuclei, mold vibration, mechanical stirring or ultrasonic agitation of the molten metal, and controlled cooling and reheating during solidification have been tried with varying degrees of success. However, it is doubtful that any method of refining the as-cast ingot grain structure has been completely successful on a commercial basis. The purpose of

Jan 1, 1962

THE composition and quality of finished steel depend upon selection and proportioning of the raw materials of the charge as well as on control of furnace practice. This chapter deals only with those raw materials of the basic open-hearth process which are important in determining the composition of the steel or slag. They are the metallic charge, oxygen-bearing materials, fluxes, and alloying and deoxidizing additions. Refractories, which may also affect the slag composition, are discussed in the previous chapter. Wide variations are possible in the type and composition of charged materials, but in all cases certain fundamental relationships among the elements of the charge must be maintained. Since the process consists essentially of refinement by oxidation of undesired elements, a balance must be established between the sources of oxygen and the elements in the charge that are subject to oxidation (see Chapters II and VII). For example, if it is desired to use a high ratio of blast-furnace hot metal to scrap, it is necessary to add an oxygen-bearing material such as ore or mill scale to eliminate the excess carbon and silicon that are present in the hot metal. An example of the opposite extreme would be the use of a metallic charge composed entirely of steel scrap. With this type of charge, it is common practice to substitute burnt lime for limestone as a flux and to charge some carbonaceous material such as coke to avoid an excess of oxygen in relation to the elements of the charge that are subject to oxidation. Elements such as copper and nickel, which are not subject to oxidation or other reactions resulting in their elimination, may be introduced into the charge only to the extent to which they are permissible in the finished steel. An example of adjustment of the charge for elements of this type would be found in the use of steel scrap high in copper. In this case, metallic components of the charge other than the scrap should below in copper, or a sufficiently high ratio of pig iron to scrap should be charged to dilute the copper from the scrap, so that the average copper content of the melt will be below the required maximum.

Jan 1, 1944

OF the many categories into which scientific knowledge has been arbitrarily 'divided, the one that has proved most. applicable in our attempts to gain an insight into the details of steelmaking processes is physical chemistry. To the young metallurgist who has only recently survived a college course in this subject, the application of its principles to reactions in liquid steel should not be difficult. The many excellent textbooks of physical chemistry provide ample material on the principles of this subject for the student of steelmaking processes. It is the purpose of this chapter to provide a concise review of the principles of physical chemistry that have proved useful in studies of steelmaking and at the same time to present some of the data that are essential to the application of physical chemistry to reactions at high temperatures. Certain parts of physical chemistry require rather formidable mathematics for their complete development, but in the main those applications in which we are here interested can be expressed in fairly simple terms. Many of the equations are logarithmic, and we shall use the symbols In X and log X to represent, respectively the natural and the common logarithm of X. The two are related-by In X = 2.303 log X. Logarithms may, be read from a good slide rule with sufficient accuracy for our purposes. In a few spots a knowledge of the calculus will be helpful. MATTER Innumerable forms of matter may, be recognized, and these may be converted by chemical processes into others, as ore, coke, and air are converted into iron, slag, and gas.. Whenever such a change occurs there is a corresponding change in the amount of energy associated with the matter. The process may require an input of energy, as in the electrolytic production of aluminum, or it may result in an output of energy, as in the combustion of fuel. The basic laws of the conservation of matter and of energy tell us that we cannot change the total amount of matter or the total amour t of energy.. When the fuel pile is used up, we realize that it has simply been converted into other forms of matter; .i.e., ash

Jan 1, 1964

By C. H. Wilson, J. W. Daly, J. J. Jakosky

Meteor Crater, Arizona, is a natural wonder which for years has been the subject of considerable discussion and study as to its origin and age (Fig. 1). Of the various theories advanced regarding the origin, two have been considered as most probable by a majority of investigators. The first theory is that the crater was formed by a meteorite or a swarm of meteoric material striking the earth at a high velocity and burying itself. The second theory is that the crater was formed by a "steam explosion" from hot solutions or gases coming from underneath the present sedimentary beds which overlie the area. In order to obtain more detailed information regarding the conditions existing at the crater, the present management decided to have a detailed geophysical examination made. The origin of the crater is of considerable scientific importance and interest. More or less active mining operations have been carried out during the past 20 years by various groups who believed that the crater was of meteoric origin, and who hoped that sufficient quantities of such material had been buried to be commercially valuable. Fragments of meteoric material found on the surface of the ground in the debris around the rim gave analysis of approximately 92 per cent iron and 8 per cent nickel, with some platinum and iridium. The material having a gross value of approximately $50 per ton, mining would be commercially profitable if sufficient quantities of the material existed in condition for mining. In the early work numerous drill holes and shallow shafts were put down, mainly in the northern portion of the crater. Pulverized material and debris caused considerable difficulty, and in an effort to overcome this the present management started a 1500-ft., two-compartment shaft on the south rim of the crater and outside of the fill zone. The intention was to sink the shaft in the solid rock outside of the crater, and then to crosscut toward the crater at a depth of 1500 ft. The work was finally stopped when a depth of 650 ft. was reached, because water poured into the shaft through large cracks and fissures in the rock. The enormous force responsible for the crater had also broken

Jan 1, 1932

By Harry V. Welch

This paper presents a brief discussion of numerous devices and processes which have been utilized for the recovery of values from gases in copper reduction works and describes in greater detail the development and application in recent years of electrical precipitation, more familiarly known as the Cottrell process, to the problems of dust losses with furnace gases in copper-smelting and refining plants. The field for collection of suspended particles in gases is widely extended in our modern complex, congested .and industrialized mode of living, and its satisfactory solution is required by our increasing appreciation of the extravagant waste, unhealthful effects and nuisance which such uncontrolled emission of solid suspensions represents. Much of the special dust-recovery equipment in use today has been developed in one industry and carried over to many others. The early work of Cottrell was with sulfuric acid mists, aimed at the purification problem in contact acid manufacture, but the present uses of Cottrell equipment cover a diversified field—carbon black, combustible gas, oil mists, iron blastfurnace fumes and dusts, cement-kiln gases, as well as the purification of gases in contact and chamber acid plants and its wide and extended use in the nonferrous metallurgical field of copper, zinc and lead, and their associated metals. Dust and fume collection from furnace gases became a problem only with the modern development of large and amply powered auxiliary furnace equipment, which in turn permitted large furnace units, fast driving and large outputs of finished product per unit of furnace capacity. The ancient metallurgist with his small clay pot and hand-operated bellows had too little gas velocity to cause a real dust loss. As furnaces grew in size, flues and stacks were added, and undoubtedly the first observable dust losses were indicated by the deposits in the flue and stack base. Large flues, it was noted, collected more than smaller ones, and the expansion of a portion of the flue into a chamber represented the first serious attempt at recovery of furnace dust losses. For a century or more the settling chamber represented the best of skilled metallurgical practice in recovery of furnace dust, and it may be said to have reached

Jan 1, 1934

By Harmon F. Fisher

In the course of a comprehensive investigation for the development of the electrical process for the dehydration of oil-field emulsions, the writer has had an unusual opportunity to direct and execute a number of related, parallel studies concerning crude oil emulsions and extending over a period of nearly six years. Among these was an investigation utilizing the microscope for studying both the general characteristics of crude oil emulsions, the nature of their electrical charge and the action of an alternating current field in causing coalescence of the finely dispersed, more or less permanently suspended, emulsion particles into larger droplets of such mass that subsequent dehydration would follow by the ordinary process of settling, further agglomeration of the water droplets and, finally, separation into commercially dry, pipe line oil and a clean water discharge. It is not the purpose of this paper to enter into a detailed discussion of the highly specialized subject of microscope technique, nor into a theoretical discussion concerning the origin of the electrical charge on the emulsion particle or concerning the mechanism of the electrical phenomena occurring during the electrical treatment of oil-field emulsions. In a short paper of this character one can hope to touch on only a very limited discussion of the theoretical aspects of crude oil emulsions. The subject of emulsions and colloids is comprised in a comparatively young science in which, however, very rapid progress is being made and consequently it is undergoing many changes; a tentative conclusion valid today may be overthrown tomorrow. Nor would it be a simple science even if it were no longer undergoing this rapid progress; a thorough study of emulsions is based upon a knowledge of such fundamental subjects as molecular structure, ionization and other electrical phenomena, surface chemistry, surface and interfacial tension phenomena, viscosity and other factors too numerous to discuss here and the fundamental theories of which are still undergoing more or less change. Therefore this paper will confine itself largely to a generally descriptive discussion, a sufficiently detailed outline of the microscope technique and a brief comment on

Jan 1, 1931

By A. I. Krynitzky, Henry S. Rawdon

The most commonly used material for terminals in spark plugs is commercial nickel wire, because of its relatively high temperature of melting, excellent heat conductivity, and slow rate at which the metal is oxidized, even upon continued heating at high temperatures. The grade commonly used for this purpose averages 97 per cent. nickel, the remainder being manganese, cobalt, iron, copper, with traces of other impurities always found in commercial nickel. A peculiar and interesting type of deterioration that occurs in these nickel terminals during the service life of the spark plug was recently brought to the attention of the Bureau of Standards. Commercial spark plugs vary greatly in their size and shape and the terminals differ considerably as to their relative size, shape, number, and arrangement with respect to one another. Although this defect was studied in detail in only one form of spark plug, the deterioration is a characteristic of the material, i.e., of nickel wire, rather than of the particular type of spark plug in which it was noted and studied. The mechanical features of the plugs, however, have a considerable bearing on the time required for the deterioration to become serious. The results of this study of the deterioration of nickel terminals in service should be of value to the makers of all types of spark plugs in which the terminals are made of this metal. CharacteR of Deterioration of WIres During Service Macroscopic Appearance and Properties of Changed Wire.—The nickel terminals in which the deterioration was studied were taken from spark plugs having a central terminal with the ground or side terminals attached firmly at both ends to the shell of the plug. In some of the plugs, two side terminals were used, one on each side of the central one. Although both terminals were found to have deteriorated to some extent, the attack of the central one was quite negligible compared to that of the side ones. These latter wires had developed, in service, transverse cracks that, in many cases, were as sharp and definite as a knife-cut. After a separation occurred, the breach widened by loss of material from the

Jan 1, 1921

By N. S. Stoloff, J. N. Mushovic

Age hardening response of a Mg-Th-Zr alloy has been studied at temperatures in the range 60° to 450°C. Transmission microscopy revealed clustering of thorium atoms at low aging temperatures, supporting a previous report of GP zone formation. Peak strengthening, which is observed at 325°C, is due to the formation of a coherent, ordered, DO19 type superlattice structure, of Hobable composition Mg3Th, as plates parallel to the matrix prism planes. These plates later reveal a Laves phase structure of composition Mg2Th. The equilibrium Mg4Th phase begins to precipitate in two different forms at an early stage, competitively with the Mg2Th plates. RECENT work on the Mg-Th system indicated that, unlike most magnesium-base alloys, complex precipitation phenomena may be occurring. The partial phase diagram of the Mg-Th system indicates that an equilibrium phase, Mg5Th, is the sole intermediate phase.' sturkey,' however, has reported, using X-ray and electron diffraction techniques, that a metastable fcc Laves phase, Mg2Th, precedes the formation of the equilibrium compound, which he identified as closer in composition to Mg4Th. Murakami et al.3 reported that the equilibrium phase precipitates preferentially on grain boundaries and dislocations in a Mg-1.7 wt pct Th alloy; Kent and Kelly4 aged a more dilute alloy, Mg-0.5 wt pct Th, for 4 days at 220°C and found similar results. In addition, they reported that a platelike phase with a structure close to that of the magnesium matrix forms perpendicular to the basal plane and is probably ordered. Research on a Mg-4 wt pct Th alloy by electrical resistance measurements and transmission electron microscopy has suggested that GP zones may form at low aging temperatures.3 However, the electron micrographs purporting to show this phenomenon were not conclusive. In view of the fragmentary evidence concerning the nature of the precipitation processes in the various Mg-Th alloys, an aging study was undertaken to clarify the characteristics of the various precipitates which form and to correlate the mechanical properties of the system with the direct precipitate-dislocation interactions. The latter results are presented elsewhere.' The purpose of this paper is, therefore, to discuss the precipitation sequence in this system. EXPERIMENTAL PROCEDURE Sheet stock (0.060 and 0.010 in. thick) of a commercial Mg-3.93 wt pct Th-0.42 wt pct Zr alloy (designated HK3lA) similar to that studied by sturkey2 was supplied through the courtesy of Dr. S. L. Couling of Dow Metal Products Co. Zirconium does not enter into any precipitation reactions,' but is present primarily as a grain refiner. The alloy was chill cast, warm rolled to 0.090 in. thick stock, and then finally reduced by a combination of hot and cold rolling. The alloy chemistry is given in Table I. This material was solution treated at 580°C for 4 hr in a dry CO2 atmosphere, and then water quenched. Material in this condition was fairly clear of precipitate particles and was fully recrystallized. Aging at temperatures less than 200°C was accomplished by immersing the alloy in a silicone oil bath; for higher temperatures, aging was done in a salt pot. Age hardening treatments were conducted at 60°, 80°, 105°, 135°, 160°, 250°, 325°, 350°, and 450°C for times ranging from 5 min to 400 hr. Hardness tests were performed on chemically polished 0.060-in.-thick blanks of solution treated material which were aged at the various temperatures for increasing lengths of time. For aging temperatures above 150°C the Rockwell Superficial 30T scale was employed, while samples hardened at temperatures below 150°C were monitored with the 45T scale. Each data point consists of at least three separate readings. Yield stresses also were measured at room temperature on both 0.060 and 0.010 in. sheet specimens aged at 325°C. The aged foils were thinned by the window method in a solution of 80 pct absolute alcohol and 20 pct concentrated perchloric acid (70 pct) maintained at 0°C. A stainless steel cathode was used and the applied voltage was 10 to 15 v. Thinned samples were rinsed in distilled water and pure methanol. After the me-thanol rinse the thin foils were quickly dried between filter paper. Foils prepared by the above method were examined in a Hitachi HU11B electron microscope operating at 100 kv. RESULTS A) Hardness. The hardness data are depicted in Figs. 1 and 2. Peak strengthening occurs at 325°C after aging about 6 min, see Fig. 1. Significant strengthening is achieved also at 350°C, but aging at 450°C produces only softening. The stepped curve at 250°C indicates that a complicated precipitation process may be occurring at that temperature. Fig. 2 suggests that at least two hardening mechanisms exist since the lowest temperature hardness peaks are displaced to the left of the peaks obtained at 135° and 105°C. A great deal of scatter is observed at long times in all cases due to magnesium surface degradation caused by the silicone oil bath. B) Identification of the Strengthening Precipitates. The structure formed atlowagingtemperatures (c10O°C) was not clearly resolvable by transmission microscopy. The only bright-field evidence for a change in structure was a mottled appearance which could be observed at extinction contours, as shown in Fig. 3(a), and the disappearance of this effect when dislocations produced under the influence of the electron beam passed through the matrix, as noted in

Jan 1, 1970

By H. C. Fiedler

Heats of high purity iron containing 3.1 pct Si and be -tween 0.0003 and 0.0295 pct N were prepared by vacuum melting ad then pouring while in a nitrogen atmosphere with the pressure between 0 and 90 psi. Strip from a heat with 0.0184 pct N underwent complete secondary recrystallization during the final anneal. Heats with less nitrogen had too few Si3N4 particles to restrain normal grain growth, and the heat with higher nitrogen had too many particles to allow complete secondary recrystallization. In the hot-rolled structure, Si3N4 precipitates only at the grain boundaries, with the consequence that annealing after hot-rolling diminishes the ability to subsequently undergo secondary recrystallization. In contrast to this behavior, ALNprecipitates uniformly in the hot-rolled structure. Under 1 atm of nitrogen, Si3N, in 3.1 pct Si-Fe dissociates between 900" and 950°C; the solubility of nitrogen increases from 0.0010 pct at 900" to 0.0030 pct at 1200°C. The solubility of nitrogen in Si-Fe has been the subject of many investigations. Corney and Turkdogan1 heated a 2.83 pct Si alloy in nitrogen and found the solubility, under 1 atrn of nitrogen, to be 0.0019 pct at 900°C. They claimed that Si3N4 did not form in the alloy above 705°C in 1 atrn of nitrogen. Fryxell et al.2 heated samples of 3.25 pct Si-Fe containing 0.0025 pct N over a range of temperatures and then analyzed for total nitrogen by vacuum fusion and for nitrogen in solution by a modified Kjeldahl technique. At 900°C, they reported the solubility of nitrogen in equilibrium with Si3N4 to be 0.0011 pct. pearce9 found the solubility of nitrogen at 900°C under 0.95 atrn of nitrogen to be 0.0017 pct in a 3.06 pct Si alloy. He reported that Si3N4 does not form above 770°C in 1 atrn of nitrogen. Although internal friction measurements have given somewhat higher values for the solubility,4-6 if the solubility of nitrogen is as low as has been reported by most investigators, and if Si3N4 is stable up to at least 945°C at 1 atrn pressure of nitrogen as reported by Seybolt,7 a small amount of nitrogen in properly processed Si-Fe should be effective in promoting secondary recrystallization. The requirement is that in the final heat treatment there be enough small, well-dispersed particles of Si3N4 to restrain normal grain growth. Fast8 has obtained secondary recrystallization by nitriding high-purity 3 pct Si-Fe after hot-rolling to a thickness of 0.118 in., followed by processing to 0.012 in., and annealing. A large amount of nitrogen, 0.076 pct. was introduced during the nitriding heat treatment, but he has since reported9 that "a few hundredths of a percent" is sufficient. Small amounts of aluminum10 or vanadium" nitride are capable of promoting secondary recrystallization. Heats containing as little as 0.010 pct A1 or 0.042 pct V and from 0.006 to 0.009 pct N underwent complete secondary recrystallization at final gage, whereas heats with lesser amounts of aluminum or vanadium did not.l2 To be reported is the behavior of nitrogen in high-purity 3.1 pct Si-Fe, and the relation of this behavior to the ability to undergo secondary recrystallization. PROCEDURE Ingots weighing 1 lb were made by vacuum melting high-purity electrolytic iron (A104, Glidden Co.) and high-purity silicon (Monsanto Co.). The latter was used in preference to ferrosilicon to insure a low aluminum content. The design of the melting furnace permitted pouring with the furnace atmosphere either below or above atmospheric pressure. Accordingly, at the completion of melting, nitrogen was admitted to the desired pressure and the heat then immediately poured. The ingots were sound, with no indication of porosity. In Table I are listed the heats investigated, the nitrogen pressure at pour, and the nitrogen and oxygen contents as determined by vacuum fusion with a platinum bath at 1850°C, a procedure which insures measurement of the total nitrogen.13 In addition, all heats contained 3.1 pct Si and not more than 0.002 pct C, 0.003 pct S or 0.005 pct Al. It was subsequently found that the quantity of nitrogen contained in the heats in Table I does not necessarily represent that obtained under equilibrium conditions. For example, the ingot poured immediately after 1 atrn of nitrogen was admitted to the chamber contained 0.0093 pct N, whereas an ingot poured 3 min after the nitrogen was admitted contained 0.021 pct N and another poured after a 6-min delay contained 0.029 pct N. While some bleeding of the hot top occurred in the latter instance, the ingot when examined in cross section appeared sound. The ingots were heated to 1325°C in hydrogen and rapidly rolled to 0.080 in. in 3 passes. The roll speed of the final pass was reduced so as to increase the quenching effect of the rolls. The hot-rolled pieces were processed both as-hot-rolled and after heating for 3 min at 900°C in hydrogen. After cold-rolling to 0.026 in., the strips were heated for 2 min at 900°C in hydrogen, then cold-rolled to the final gage of 0.012 in. The loss of nitrogen in going from the ingot to cold-rolled strip was no more than 10 pct. The final heat treatment, which was for the purpose of develop-

Jan 1, 1970