By G. R. Love, M. L. Picklesirner

THE use of color adds a new beauty, power, and versatility to metallography. This has been amply demonstrated in a number of public exhibits and on the walls of corporate, government, and university metallographic laboratories around the world. Indeed, in a number of cases, the color not only is of esthetic value but is scientifically essential to the competent examination of particular samples and systems. Optical strain analysis,' determination of true grain size in U-A1 alloys: phase identification in Nb-base alloys,3 analysis of transformation rates in heat-treated Nb-Zr alloys,4 measurement of solidification segregation in cast Nb-Zr alloys,' study of the intermediate phases in Nb/Sn diffusion couples,6 investigation of the oxidation kinetics at various surface orientations in single crystals,7'8 and a number of other research efforts9'10 would have been vastly more difficult without the extra clarity and distinction introduced by color—either the colors resulting from particular polarized light techniques or the interference colors obtained by oxidation. It is unfortunate that the beauty of colored micro-structures cannot be shared more widely, but the economics of publishing a technical magazine apparently prohibits color plates except under extraordinary circumstances. It is doubly unfortunate that no convenient, general method exists for communicating the information available in colored microstructures to the scientific community. True, in some instances the color changes observed are dramatic enough that direct black and white photography is adequate. In photoelastic stress analysis, several orders of interference fringes may be produced and it is frequently desirable to suppress the color effects (use monochromatic light) to simplify interpretation. On the other hand, relatively minute color variations may be readily detectable by eye, be of considerable assistance in interpreting a structure, and yet be enormously difficult to reduce to an unambiguous black and white print. In order to illustrate a possible compromise or solution to the above problems, we wish to show three black and white photographs of the same region of an Nb/Sn diffusion couple whose interpretation depends heavily upon use of color techniques. These micro-structures were obtained from a section through a rod consisting of commercial-purity niobium tubing filled with 99.995 pct Sn (melt-filled in 10"6 Torr vacuum). The composite rod, measuring 500 mm long, was bent into a hairpin shape and inserted into water-cooled copper grips in a vacuum high-temperature furnace. The rod was outgassed for 2 hr at a furnace temperature of 800°C and was further heated by self-resistance using a 2.2-kva ac power supply. The rod was raised to 1910°C over a 4+-hr period, held for 15 min, slow-cooled to 1500°C over a -hr period, and free-cooled to room temperature (all temperatures were measured with W5Re/W26Re thermocouple). Throughout the heat treatment the ambient pressure was kept below 8 x lo-' Torr. Metallographic preparation of the sample was completely conventional except that it was necessary to extend the grinding steps to remove damage in the brittle NbsSn phase introduced by sectioning. No satisfactory chemical or electrochemical etch has been found for these diffusion couples; of those which have been tried, any that attack the niobium-rich phases at all attack the tin-rich phases disastrously. However, the final polishing steps did produce a slight relief effect and this, coupled with anodizing, yielded excellent clarity in the microstructures for direct observation. The anodizing voltage was chosen to give maximum change in color per unit change in composition. In this case, indeed normally, this maximum sensitivity occurred in the blue-to-red color range. The pure niobium tube wall anodized to a relatively bright blue

Jan 1, 1967

By James H. Boettcher, W. Durand Eppler

INTRODUCTION In the second quarter of 1979, Rapid Mining Co., Inc. ("Rapid") inquired whether Crocker National Bank ("CNB") would provide $4 million in term loan financing to help ("Dry Creek") acquire the outstanding shares of the Dry Creek Coal Company ("Dry Creek") in West Virginia. Prior to approaching CNB, Rapid had sought financing with the assistance of a financial advisor from a number of commercial banks without success. A summary of the initial terms requested by Rapid is shown in Table 1 compared with the actual terms on which the transaction closed. It is not difficult to note that the two sets of terms differ significantly. This is often the case when financing requests based on the expectations and vision of a mine developer are juxtaposed with more pragmatic requirements of a commercial bank. The "art" and fund of structuring financing plans for mining ventures (highly leveraged acquisitions or grass roots) comes in working with mine developers to arrive at a final financial structure that meets their objectives and constraints as well as those of the bank or other financial institutions providing much of the financing. Beginning with the terms requested by Rapid and ending with the terms that closed the transaction, this article briefly describes the process we went through with Rapid Mining. The Seller and Buyer The Dry Creek Coal Company was established in 1961, after its owner acquired the coal leases from Republic Steel. Republic has mined the primary coal seam from 1948-1961. Dry Creek was owned as a subchapter S corporation (i.e., for federal income tax purposes, income is taxed at the shareholder level) and had been run on a low key basis. Since the company had virtually no debt and limited cash needs, the owner produced primarily when rail cars were available and income was required. Output was therefore erratic as is shown in the top of Table II, but the result was a profitable little company with an attractive free cash position. Because the owner wished to retire and enjoy his wealth in a more readily spendable form, he had put the mine, with stated recoverable reserves of approximately 13 million tons, up for sale. In contrast, Rapid Coal's investors consisted of a number of investors of disparate financial situations. They had agreed upon a primary objective of income maximization and planned an annual production rate of 120,000 TPA which they and the current owner believed realizable. The Formulation of a Financing Structure Figure 1 presents a simplified overview of the sequence of steps taken in the financing process which lasted approximately three months from start to finish. Since banks see many requests for funding and considerble time is required to follow up on each, an important step was determining, after a brief review of the materials provided to us, whether the basic "eonomic entity" was viable. In this case, the size and quality of the reserves, the inherent operating cost characteristics, the sales arrangements, the management/labor situation and Rapid's principles all appeared to be sound enough to warrant investing the time necessary to do a thorough analysis of the project. Once this decision was made, the evaluation and analytic process shown in Figure 2 was initiated. The first and most fundamental concern of any banker is whether the loan will be paid back as scheduled from the cash flow generated by the project. The amount of debt relative to the owner's equity is of course crucial in such a determination. Before the debt/equity issue was addressed, however, a number of more qualitative factors had to be studied and if

Jan 1, 1985

By A. K. Mukhopadhyay, B. Sikdar, V. P. Arora

Introduction During the past several years, persistent concerns about an economic slowdown in India have tempered capital-expan¬sion plans. This has encouraged companies to find methods of increasing the capacity of existing production equipment. One of the more cost-effective methods of increasing produc¬tion capacity without major capital investment is to improve equipment maintenance to prevent needless machine down¬time. This can have a significant financial impact because of reduced maintenance costs and increased machine availabil¬ity. The maintenance program employs different techniques, but the analysis of the vibration behavior of machine compo¬nents to assess their condition was found to be the most accurate technique for monitoring various machine disorders. A dragline that handles overburden in open pit mines is one of the more capital-intensive pieces of production equip¬ment. It is imperative that the machine be run at its optimum capacity under the prevailing environmental conditions. Condition monitoring of the various components of the dragline through vibration analysis not only improves the machines availability but also ensures a long operation time free from sudden failure. This paper describes the application of vibration monitor¬ing and analysis techniques to assess the components of a W2000 dragline. The paper reveals that condition monitoring through vibration analysis can be as valuable in failure prevention as it is in failure analysis. Finally, the paper presents an approach to a knowledge-based expert system to the quick and correct diagnosis of mechanical faults in a dragline. Equipment A dragline is an intermittent-discharge-type excavator having a long boom at one end. Unlike other excavators, the bucket is not rigidly held by the frame structure. In favorable geomining conditions, the intensive operation of these exca¬vators is the least-expensive means of overburden removal. The basic working elements of this equipment are the hoist system, the crowd and retract system, the wing mechanism and the propel mechanism. The walking dragline is accepted as the most economical machine for stripping overburden at depths of up to 60 m (200 ft). They are electrically powered and the various motions are effected by individual drives. The Ward-Leonard system is used to provide the optimum flexibility in controlling different dc-drive motors. To mini¬mize the cost of mineral extraction, the largest such machine in India has a 24-m3 (850-cu ft) bucket with a boom length of 96 m (315 ft). Draglines are very costly, and considerable financial penal¬ties may arise from sudden stoppages due to component fail¬ures. Thus, operational reliability is of the greatest importance. Active measures are now being taken to minimize downtime by adopting condition-based maintenance techniques. Though a number of techniques come under this scheme, it has been observed that assessing the health of the dragline by measuring vibration is the best method of determining the dynamic behavior of its various rotating components to avoid any catastrophic failure. Based on criticality, the vibration-behav¬ior of the following components are studied: • motor-generator unit, • exciter unit, • hoist motor-gearbox unit, • hoist drum-gearbox unit, • drag motor-gearbox unit, • drag drum-gearbox unit and • swing motor unit The approach Increases in the vibration levels in different subsystems of the dragline were observed due to the presence of faults such as unbalance, misalignment, looseness and bad bearings. A vibration behavior study included the measurement of vibra¬tion level, trend analysis of time-domain vibration signals and vibration frequency analysis at bearing points of the components. A vibration meter, a vibration analyzer and a data collector are used. Vibration-level measurement. When the dragline was assembled and put into operation for the first time, vibration data were collected to generate baseline data for the equip¬ment (based on International Standard ISO 2372). After¬wards, the vibration levels were recorded regularly using a vibration meter. The measurements were taken at all bearing

Jan 1, 2000

By A. D. Schwope, L. R. Jackson, K. F. Smith

Burghoff and Blank1 have pointed out that the creep properties of hard-drawn coppers are closely associated with their individual softening characteristics and have further shown that the creep resistance of various types of copper is improved, under certain circumstances, by cold stretching. In the design of certain types of electrical machinery, it is important to have the creep resistance as high as possible; furthermore, short-time creep strength is important since in many cases stresses are large only during warming-up and cooling-down periods. In this paper, data are presented showing the effect of cold work on the short time creep strengths of various types of commercial copper under several conditions. It is shown that trends from short-time creep tests are evident at longer times. Materials Used in the Investigation The coppers used in this investigation were commercial grade and of two basic types, oxygen free high conductivity (OFHC) and tough pitch. Additions of silver in amounts of 15 and 25 oz per ton were added to each of the two coppers. The analyses of these six coppers are given in Table 1. Originally, they started as wire bars 4 X 4 X 54 in. A. square rod was made by hot rolling the wire bars to 9/16-in. rod in 8 passes. This rod was then cold drawn to 0.445-in.-diam rod and annealed for 3 1/2 hr at 1000°F. It was then cold drawn to 0.325-in. rod and again annealed at 1000°F for 3 1/2 hr. Hard square rods were then made by cold rolling to 0.257 X 0.257-in. rod. Soft wire was made from the hard- drawn material by annealing at 650°F for 3 hr. The final rolling was performed using a set of 9-in. grooved rolls revolving at 30 rpm, which produced square wires. Reductions of approximately 5, 20, 30, and 40 pct were obtained using several passes in the same direction for the large reductions. The 5 pct reduction by drawing was accomplished using a steel die having 2 parallel bearing surfaces. The die angle was 7 1/2 degrees and the wires were lubricated with a paste of ceresin wax dissolved in carbon tetrachloride. The speed of drawing was 13 fpm. Since work was done on only two sides of the wire simultaneously, it was necessary to rotate it 90 degrees each pass to insure uniform deformation. The room-temperature tensile properties of the various tempers are given in Table 2. The grain size of the an- nealed 0.257-in. wires was uniform and averaged about 0.035-0.045 mm. Experimental Procedures for Short-time Creep Tests Standard creep-test frames (Fig 1) were used for the testing. Special fixtures were designed to apply axial compressive and tensile loads to the copper wires. The compression specimens were 1 in. long and the ends were ground flat and parallel. The creep in compression was indicated by the movement of reference marks s-ratched on intersliding platinum strips attached to the moving heads of the fixture. The movement was measured with an optical micrometer fitted with a filar eyepiece on which the smallest division was 0.00005 in. The tensile creep specirriens were 4 in. long which provided ample gripping surface for the jaw-type grips. The platinum strips were attached to a one-inch gauge length of the wire and the creep measured as previously described. The single-specimen furnaces were connected to individual power and control sources. The controlling equipment consisted of Foxboro controllers

Jan 1, 1950

By Samuel Tescher

The operation of gaseous mines is a problem, due to the fact that we have not only the ordinary mine accidents to guard against, but have also the ever present menace of a mine disaster involving a large number of human lives, and the destruction of valuable property. In looking over the reports of mine disasters throughout the country in the past several years, we find that methane gas, coming in contact with an ignition agency of some kind, has been the source of at least 75 per cent of our mine explosions. Coal dust, of course, plays its part in propagating the explosive action throughout the mine workings and rendering it more violent and destructive; nevertheless, the initial ignition of a body of explosive gas-sometimes of very small volume-has been the primer for the large majority of our mine disasters. We find also, that the places of initial ignition are most frequently found at the working faces, or in close proximity thereto. This is mainly due to the following reasons: First-The working faces are, as a rule, the places where methane gas is most freely generated. Second: They are places that are most poorly ventilated. Third-They are the places where ignition agencies are most frequently found. The sources of ignition, as a rule, consist of naked lights, the shooting -of shots, defective flame safety lamps, and electrical arcs. The problem, then, in the operation of gaseous mines, is primarily to so ventilate the working faces that an explosive mixture is not likely to occur, and to endeavor to keep away from the working faces all sources of ignition. To do both of these things may seem impossible. Nevertheless, by working along both of these directions, a great many disasters can be avoided. The efficient ventilation of the working faces is paramount. By efficient ventilation, we mean the continuous passing of large volumes of air at the working faces. This can only be accomplished by adequate ventilating equipment, capable of being driven by at least two independent and distinct sources of power, together with large, clean, straight air courses which are free of short turns, constructed areas, and leaky doors and stoppings. In other words, furnish a suitable course for its travel through the mine. Many of us sharpen our pencils and rack our brains to properly estimate the proper size pump and pipe equipment that may be needed to handle a certain amount of water. We estimate the size of copper conductors to a nicety. We immediately rush to repair leaks in our water, compressed air or electric lines. But how many of us give serious thought to the travel of the air through our mines, the health and safety-giving fluid on which so much depends! In driving air courses, a certain economical cross-sectional area should be adopted and maintained as standard. When turns are necessary, they should be made with long radius curves, and the cross-sectional area should be increased on the curves. All entry stoppings should preferably be built of monolithic concrete, with suitable hitches into floor and ribs, and after the concrete has set, they should be examined and leaks due to shrinkage and settling should be eliminated. Overcasts and their approaches should have cross-sectional areas larger than the entries leading to them, to allow for the sudden change of direction, bearing in mind that air wants to travel in straight lines. In the early development of a property, ample provision should be made in the size of the main entry pillars to allow for the driving of additional

Jan 1, 1925

By N. P. Goss

Asterism appearing in X-ray Laue diagrams is an extremely sensitive index of changes in the internal structures of individual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.l-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not conclusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made between mosaic and distorted grain structures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example: has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-l4 to 10-l5 c.c., or 10-15 cm. in size. These crystallites, or blocks, appear to survive the most drastic cold-working, for it has been shown, and more elaborately by Wood's recent work," that cold-working cannot reduce the size of these crystallites smaller than of the order 10-5 cm. The interesting correlation brought out by the experiments of Goetz and Wood is that the block size after severe cold-working is of the same order of magnitude as the groups that formed in the metal just before crystallizing from the molten state. The work of Ewald and Rennenger17 and the now classical experiments of Darwin and James12,13 all strongly suggest the existence of a periodic structure of crystal. lites smaller than the grain itself. Related to this effect is the appearance of veinlike markings in the microstructures. Ammer-man and Kornfeld,16 in their experiments, did not observe any evidence of veining in specimens of alpha iron annealed below A3 and believed that veining was not due to impurities in the iron, as Northcott16 suggested; veining was observed by them only in specimens annealed above A3. Hanemann,16 Schrader and Tangerding found that annealing in hydrogen did not diminish veining and so it could not be caused by oxides. They concluded that veining was due to a slight difference in the orientation of ferrite lattice blocks. This viewpoint is well supported by the evidence presented here.

Jan 1, 1941

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By B. M. Larsen, T. E. Brower

In an earlier paper1 we discussed a simple, rapid method of taking samples of liquid steel and analyzing them for oxygen, which, though possibly not absolutely accurate (as is likewise true of all other methods), certainly yields results that are satisfactorily consistent. Accordingly, samples from hundreds of heats ill different shops were analyzed for oxygen, with results sufficient in number to be handled statistically and permit estimation of some general trends. Measurements were made in acid as well as in basic open hearths, throughout the refining period, to learn how stirring, blocking, adding ore or lime or sand, affects the oxygen content of the bath; we also followed the changes brought about by tapping, teeming, and deoxidizing. Some of these results, discussed in an earlier paper,2 bring out the dominant role of the carbon-oxygen reaction in regulating degree of oxidation both of metal and of slag, also the marked variability of concentration of dissolved oxygen [0] in excess of that which would be in equilibrium with carbon and with carbon monoxide at a partial pressure of one atmosphere. As a logical beginning on this complex problem, we take up in the present paper the variability of this excess oxygen, A[O], when other factors are as constant as they ever are in open-hearth operation; namely, toward the end of the refining period, when the bath may be regarded as in the comparatively steady state it approaches in absence of disturbing factors. This condition was chosen because by that time the significant reactions, except carbon oxidation, between slag and metal have come to substantial equilibrium; this facilitates interpretation of the complex situation and thus perinits more definite conclusions to be drawn. This excess concentration of oxygen, A[O], in the metal is needed, of course, to make the steelmaking process go at a reasonable rate; alternatively it may be regarded as a measure of the virtual pressure increment above one atmosphere, or of the degree of supersaturation, of carbon monoxide in the metal. According to our measurements, the excess concentration A[0] in liquid steel varies from about 0.009 to 0,035 per cent oxygen by weight. It is quite sensitive to change of conditions, being altered temporarily by operations such as stirring with green poles, additions of ore, lime, or sand; but as the disturbance works itself out, it resumes a level within the intermediate range characteristic of the steady state. The conditions most common in average furnace practice are covered by the following: i[O] Usual Per Cent Oxygen by Conditions Weight 1. Vigorous lime boil........... o.oog-0.01s 2. Steady state................ o.or;-0.025 3. Working of ore.............. o.023-0.035 Thus when the bath can be regarded as in a reasonably steady state—that is, when it is boiling normally, is at proper temperature with a well-shaped slag, and has been free from disturbing effects during the preceding half hour—A[0] returns from

Jan 1, 1948

By J. E. Burke, C. W. Mason

IN attempting to study precipitation from a tetragonal lattice using solid solutions of bismuth in tin, it was found that although a Widnmanstatten pattern is observed 1 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process MICROSCOPICAL STUDIES Alloys were made from Chempur tin (Standard samples 42b and 42c, National Bureau of Standards), and bismuth (Kahlbaum C P ) by melting neighed quantities together under palm oil, stirring well, and casting in a heated graphite mold The polishing and etching techniques employed largely govern the visibility of the structural changes The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through BehrManning 3/o abrasive papers, lubricated by a solution of paraffin in kerosene A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution, repeated etching and polishing served to remove disturbed metal For high-power examination better preparation was necessary It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a Heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use A better procedure was as follows The metal lap was warmed slightly, and a 4-in circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C was poured over it, allowed to stand for 1 to 2 min and then washed off It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample The cloth was then charged with a paste of the relevigated alumina in water Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deteriorates after about 24 hr This is not serious, because a new lap can be prepared in about 5 min, and only small pieces of cloth are used Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer For the final etching, the most satisfactory reagent was that of Taffs,7 the formula for which is FeC13 6H20, 2 grams, HC1, 5 c c , H2O, 30 c c , C2H5OH (95 per cent), 60 c c This etchant reveals differences in com-

Jan 1, 1941

By B. M. Larsen, T. E. Brower

In an earlier paper1 we discussed a simple, rapid method of taking samples of liquid steel and analyzing them for oxygen, which, though possibly not absolutely accurate (as is likewise true of all other methods), certainly yields results that are satisfactorily consistent. Accordingly, samples from hundreds of heats ill different shops were analyzed for oxygen, with results sufficient in number to be handled statistically and permit estimation of some general trends. Measurements were made in acid as well as in basic open hearths, throughout the refining period, to learn how stirring, blocking, adding ore or lime or sand, affects the oxygen content of the bath; we also followed the changes brought about by tapping, teeming, and deoxidizing. Some of these results, discussed in an earlier paper,2 bring out the dominant role of the carbon-oxygen reaction in regulating degree of oxidation both of metal and of slag, also the marked variability of concentration of dissolved oxygen [0] in excess of that which would be in equilibrium with carbon and with carbon monoxide at a partial pressure of one atmosphere. As a logical beginning on this complex problem, we take up in the present paper the variability of this excess oxygen, A[O], when other factors are as constant as they ever are in open-hearth operation; namely, toward the end of the refining period, when the bath may be regarded as in the comparatively steady state it approaches in absence of disturbing factors. This condition was chosen because by that time the significant reactions, except carbon oxidation, between slag and metal have come to substantial equilibrium; this facilitates interpretation of the complex situation and thus perinits more definite conclusions to be drawn. This excess concentration of oxygen, A[O], in the metal is needed, of course, to make the steelmaking process go at a reasonable rate; alternatively it may be regarded as a measure of the virtual pressure increment above one atmosphere, or of the degree of supersaturation, of carbon monoxide in the metal. According to our measurements, the excess concentration A[0] in liquid steel varies from about 0.009 to 0,035 per cent oxygen by weight. It is quite sensitive to change of conditions, being altered temporarily by operations such as stirring with green poles, additions of ore, lime, or sand; but as the disturbance works itself out, it resumes a level within the intermediate range characteristic of the steady state. The conditions most common in average furnace practice are covered by the following: i[O] Usual Per Cent Oxygen by Conditions Weight 1. Vigorous lime boil........... o.oog-0.01s 2. Steady state................ o.or;-0.025 3. Working of ore.............. o.023-0.035 Thus when the bath can be regarded as in a reasonably steady state—that is, when it is boiling normally, is at proper temperature with a well-shaped slag, and has been free from disturbing effects during the preceding half hour—A[0] returns from

Jan 1, 1948

By B. G. Reisdorf

This paper describes the microstructural changes that occur when quenched ultrahigh-strength steels containing OA pet C and various amounts of nickel, silicon, and cobalt are tempered. The changes that occur in hardness, yield strength, and martensite diffraction-peak widths when these steels are tempered are related to the precipitation of the carbide phases. An unea$ectedly high silicon content (about 30 pct) was found in the E -carbide phase in a steel containing only 1.5 pct Si. TEMPERED martensitic steels have such wide-spread utility that they have been the subject of numerous investigations, and a sizable amount of literature has developed on this subject.M This investigation, which is a part of a larger program to correlate microstructure with mechanical properties at a variety of strength levels, is limited to the microstructural changes that occur when a quenched 0.40 pct carbon steel (USS Airsteel X-200 steel) is tempered, and to the effects of the alloying elements—nickel, cobalt, and silicon—on these microstructures. Used in this investigation were electron microscopy, electron-diffraction identification of the carbide phases, electron-probe micro-analysis of the carbides, X-ray determinations of retained austenite, and measurements of martensite X-ray diffract ion-peak widths. MATERIALS AND METHODS The chemical analyses of the eight heats examined eats No. 30 through 37) are shown in Table L Heat No. 30 has the chemical com~osition of Airsteel X-200, and the remaining seven heats contain various amounts of nickel, chromium, cobalt, and silicon. The heats were air-melted in an induction furnace and cast into 8 by 8 in. ingots that were subsequently heated to 2300 and rolled to 1-in.-thick plate. Oversize 0.505-in.-diam tensile specimens were rough-machined from the plates and austenitized in air at 1700° F for half an hour and oil-quenched. The specimens were then tempered in air at temperatures of 400° to 1000 for tempering times of 1, 4, and 16 hr, and finish-machined to 0.505-in.-diam tensile specimens. Electron micrographs were prepared from Formvar replicas of the midthickness of tensile-specimen shanks that had been electrolytically polished and etched in nital. Electron-diffraction patterns were obtained from carbon-extraction replicas. The replicas were prepared by etching the sample surface in the same manner as for microscopy, evaporating carbon on the etched surface, and re-etching the sample to free the carbon film and the precipitate particles. Electron-probe microanalysis was performed on some of the extraction replicas. To obtain adequate fluorescent X-ray intensities, several thicknesses of replica were exposed to the electron beam so that the results represent an average composition of the extracted particles rather than an analysis of single precipitate particles. The retained austenite contents of the specimens were determined by an empirical X-ray diffraction

Jan 1, 1963

By N. P. Goss

Asterism appearing in X-ray Laue diagrams is an extremely sensitive index of changes in the internal structures of individual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.l-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not conclusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made between mosaic and distorted grain structures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example: has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-l4 to 10-l5 c.c., or 10-15 cm. in size. These crystallites, or blocks, appear to survive the most drastic cold-working, for it has been shown, and more elaborately by Wood's recent work," that cold-working cannot reduce the size of these crystallites smaller than of the order 10-5 cm. The interesting correlation brought out by the experiments of Goetz and Wood is that the block size after severe cold-working is of the same order of magnitude as the groups that formed in the metal just before crystallizing from the molten state. The work of Ewald and Rennenger17 and the now classical experiments of Darwin and James12,13 all strongly suggest the existence of a periodic structure of crystal. lites smaller than the grain itself. Related to this effect is the appearance of veinlike markings in the microstructures. Ammer-man and Kornfeld,16 in their experiments, did not observe any evidence of veining in specimens of alpha iron annealed below A3 and believed that veining was not due to impurities in the iron, as Northcott16 suggested; veining was observed by them only in specimens annealed above A3. Hanemann,16 Schrader and Tangerding found that annealing in hydrogen did not diminish veining and so it could not be caused by oxides. They concluded that veining was due to a slight difference in the orientation of ferrite lattice blocks. This viewpoint is well supported by the evidence presented here.

Jan 1, 1941

By L. D. Clark, S. S. Saluja

A physical law, governing the rupture of rock by confined explosive charge correspondent to current expressions for determining weight of charge to rupture rock burden, W, was developed in the form Q = cVw3 by two early investigators performing unique experiments with ice. The coefficient C, is found by trial blast. Recent physical tests conducted with rock, synthetic materials and ice to establish the validity of the theory on which it and other related formulae are based indicated: (a) that failure under hydrodynamic impact pressure is by tension rather than shear as was assumed; (b) that the fundamental law of mechanics, enabling the determination of Q = cvw3, modified to the form P = R x Sa x Wb is valid when low velocity explosives are used; (c) that rock breakage under the action of low velocity explosives is entirely due to explosion gas pressure, as was believed; (d) that under the action of high velocity explosive it is due to the joint effects of scabbing and gas pressure; and that further possible modification could make the above equation also applicable to these joint mechanisms. shape could be easily frozen and because large loads would not be required. They found: (a) that the not unfamiliar shearing equation for metals was applicable to ice where P = load in lb; S = periphery of pressure surface, in.; W = burden, in.; K = modulus of rupture by shear in lb per in.2; and (b) that "the form of cavity produced by the application of gradual pressure is similar to that obtained by blasting in rock under similar conditions of free face and pressure surface!" This similarity in crater shapes leads to the conclusion that rock would rupture by shear, as did ice, and its behavior under the force of a blast could be governed by such a relationship as P = S x W x K. Three important interrelated empirical expressions were derived and rock, charging and spacing coefficients C,, C, and e were established and substantiated by trial blasts. In checking the accuracy of the main assumptions, duplication of the ice tests, substituting rock, suggested that K is not constant and that P = K x W x S, though valid for ice, does not necessarily hold for homogeneous limestone.' Conclusions from this later work raised questions making continued investigation desirable because such conclusions do not destroy the practical value of the empirical equations or theory. Further study for the establishment of the relationship between load, burden and periphery of the pressure surface and possible application of these to the mechanism of rock blasting was undertaken by the authors of this paper. MECHANICAL TESTING - EXPERIMENTAL PROCEDURE Certain inconsistencies in the results of the aforementioned tests repeated on three types of limestone suggested these inconsistencies be attributed to rock inhomogeneity. It was also suspected that the loading speed, which could not be held uniform, may have contributed. The earlier work with both rock and ice

Jan 1, 1964

By R. S. Goodrich, G. S. Ansell

The microstructure of three Al-Al2O3 SAP-Type alloys (containing 2.0, 3.0, and 5.7 wt pct alumina, respectively) was studied utilizing transmission electron microscopy. These alloys were fabricated from aluminum powders by powder-metallurgical techniques, cold-rolled into thin strips, and recrys -tallized. Thin foils suitable for an electron-transmission study were then prepared from the strip material by electropolishing. The microstructure of these alloys is shown to consist of small (0.1 mean diameter) plate -shaped alumina particles finely distributed in an aluminum matrix. In the higher-oxide content alloys the platelets are somewhat larger and more irregular in shape. The distribution of oxide particles is not uniform and there is an increasing tendency toward clumping SINCE the discovery by Irmann1 that aluminum alloys produced by compacting, hot pressing, and extruding fine aluminum powders possess remarkable high-temperature mechanical properties, the Al-A12O3 SAP-Type alloys have been utilized extensively as model dispersion-strengthened alloys in both experimental and theoretical invest igations.2-8 The use of the SAP-Type alloys as model dispersion-strengthened alloys implicitly assumes that their microstructure has been completely delineated. This is, however, not the case. with increasing oxide content. In all the alloys studied, the mean center-to-center spacing of particles was quite small (0.2 u) due to the very fine oxide debris present. Selected-area diffraction of the specimen identified the oxide as either y Al2O3 or y' Al2o3. The re crystallized MD-5100 alloy exhibited a mean grain diameter of only 0.7u, while the grain size of the other alloys was several hundred microns. Severe pinning of the grain boundaries by oxide particles was rarely observed, and the grain boundary triple points in the small-grained MD-5100 alloy were often particle -free. Diffraction contrasts visible around the particles are attributed to elastic strain fields set up by differential thermal contraction during cooling from the recrystallization anneal. Early investigation demonstrated that optical metallography did not possess sufficient resolution to observe the microstructure of the SAP-Type alloys.' Later, extensive use was made of replication techniques to study the microstructure by means of electron microscopy.7-9 These studies indicated that the SAP-Type alloys consist of a dispertion of irregular Al2O3 platelets, approximately 150A thick 9 and a micron or so on edge,9 distributed in a matrix of commercial-purity aluminum. These oxide platelets tend to be oriented in the aluminum matrix, with their largest dimension parallel to the extrusion direction. 8,9 A study employing polarized-light techniques1' indicated that the grain size of a series of as-extruded SAP-Type alloys was several microns in diameter, while the grain size after re-crystallization was several millimeters in diameter. A more recent study 12 utilizing surface-replication techniques examined the particle morphology,

Jan 1, 1964

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By W. R. Wilcox

The camphor-anthracene system was chosen as a transparent low-melting analog of the zirconium carbide -graphite system. Camphor and zirconium car -bide both grow nonfaceted, while casting of mixtures yields platelets of both anthracene and graphite. Zone melting of thin layers of organic was observed under the microscope. Irregular lamellar structures were produced at high values of the ratio of the temperature gradient G to the zoning rate V. The anthracene invariably led the camphor, indicating lower kinetic undercooling for the anthracene. The lamellar spacing was an order of magnitude greater than typical spacings for metal eutectic systems. Exact behavior depended on orientation of the anthracene. Oriented dendritic structures were produced at low values of G/V. Transient and oscillatory behavior were also observed—much of it unexpected. A.RC-CAST refractory carbide-graphite mixtures are promising thermal-shock resistant materials. Oriented structures of these materials would be superior to arc-cast materials for many applications. Mollard and Flemings1 and Cline2 have shown that aligned structures can be obtained for a wide range of Pb-Sn alloys. However, these metals both solidify in a nonfaceted manner while graphite yields platelets or flakes. In addition only small diameter samples of Pb-Sn alloys were produced because it was necessary to avoid free convection and to have high temperature gradients. The purpose of the present work was twofold: 1) To observe the solidification of a transparent low-melting analog of carbide-graphite systems and 2) to see if larger diameter samples can be produced. EXPERIMENTAL PROCEDURE When zirconium carbide-graphite mixtures are cast, the resulting structure naturally depends on composition. Carbide-rich mixtures yield metal-like nonfaceted carbide dendrites in a eutectic matrix. Graphite-rich alloys have graphite platelets in a eutectic matrix. Empirically it was found that camphor-anthracene mixtures produce similar structures with camphor being nonfaceted and anthracene forming plates. The organic eutectic melted at 116°C and was composed of 78 wt pet camphor.3 The camphor used was U.S.P. grade from Fisher Scientific Company; the anthracene was 98+ pet fro Aldrich Chemical Co. The impurity content is judged to be on the order of 1 pet. Mixtures ranging from 50 to 88 wt pet camphor were employed for the experiments. All but one of the experiments were performed on the microscope-stage zone melting apparatus described in detail elsewhere.4 The organic mixtures were contained in horizontal cells made of microscope slides or cover glasses. In most of the cells the organic was present as a very thin layer, thus giving almost two-dimensional growth behavior. The cells were moved slowly under a heated wire, which caused a molten zone to move through the solid at rates ranging from 0.01 to 5.4 cm per hr. The temperature gradient was estimated before moving the zone by measuring the distance between the line where all solid was melted (freezing point) and that where solid first began to melt (eutectic temperature). The temperature gradient was found to be 465°C per cm in the thinnest cells used, which were made by pressing together two microscope cover slips in the organic melt and then rapidly withdrawing them. RESULTS The experimental results are described in four parts: simultaneous growth, dendritic growth, irregular growth, and transients and erratic phenomena. Steady state data are summarized in Fig. 1. Except where noted all comments are for the cells containing a thin layer of organic. A) Simultaneous Growth. Simultaneous and roughly parallel growth of anthracene and camphor was obtained over the full range of compositions investi-

Jan 1, 1970

By George P. Chapman

Mica is a platy mineral occurring in a variety of complex hydrous aluminosilicate forms with differing chemical composition and physical properties. Principal minerals in the mica group include: Muscovite-potassium mica (colorless or pale green/ ruby) Phlogopite-magnesium mica (dark brown or amber) Biotite-magnesium-iron mica (black or dark green) Lepidolite-lithium mica (lilac) Selected properties are given in Table 1. Muscovite is most important commercially with phlogopite of lesser use. The laminated structure of mica enables it to be split into very thin films which are transparent and tough as well as having outstanding dielectric and insulating properties. Commercially, mica is used in a number of forms (Chowdbury, 1941; Rajgarhia, 1951; Skow, 1962). Sheet mica consists of flat sheets mined from naturally occurring books of mica, free from defects and capable of being punched or stamped into required shapes. Sheet mica is separately classified into blocks, films, or splittings according to thickness. Built-up mica, or micanite, is made by arranging overlapping splittings in layers , cemented with a binder and pressed together at high temperature. Reconstituted mica, or mica paper, is made by depositing fine flakes of high-quality scrap mica in a continuous film impregnated with binder. Scrap and flake mica are normally unsuitable in quality or size for making sheet mica. Originally the term scrap mica referred to the waste byproduct of mining and fabricating sheet mica, and distinct uses were developed for this material. Subsequently it became economically feasible to mine lower quality mica for these uses, and the term flake mica was introduced. Although the two terms are still used somewhat synonymously, it is considered better, at least in the United States, to use the term flake mica in referring to mica mined for uses other than as sheet mica; and to restrict the term scrap mica to mica mined for or with sheet mica, but which will not meet the specifications. Synthetic mica, such as fluorophlogopite, is produced by slow crystallization of a melted blend of pure raw materials. Mineralogy In the true sense the term mica does not relate to, a particular mineral, but to a group or family of minerals of similar chemical composition and to some extent similar physical properties. These minerals are predominantly potassium aluminum silicates with varying amounts of magnesium, iron, and lithium. The precise formulas and isomorphic relationships of the various group members have been studied, but general agreement has not been reached (Grimshaw, 1971; Hurlbut, 1952; Skow, 1962). The general formula describing the chemical composition of micas is [X2Y4-6Z8020(OH, F)4, where X is mainly K, Na, or Ca; Y is mainly Al, Mg, or Fe; Z is mainly Si or Al (Deer, et al., 1962).] These minerals have an internal structure of the layered lattice type where the silicon atoms are in the center of a tetrahedral grouping of oxygen atoms. The groups are linked together in a single plane by three oxygen atoms that lie within the common plane. Each of these oxygen atoms is shared by two tetrahedra. These linked tetrahedral groups, when continually extended, produce a hexagonal network within the plane. This internal structure of the mica has been used to explain the ex-

Jan 1, 1983

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300' to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By Jei Y. Choi, P. G. Shewmon

Using a scratch smoothing technique, the magnitude and the ratio of the surface diffusion coefficients (D,) in two orthogonal directions have been measured on copper for over 100 different surface orientations. Anisotropy was found for all surface orientations except those lying near the (100) and (111); however, these anisotropies were rarely greater than 2.0. The direction of maximum D, appears to coincide with the direction of step edges on any given surface, and if no such steps exist, no anisotropy is found. Thus the jump frequency along a step edge is shown to be faster than the frequency of a jump over the step. The values of Ds and AH for the (100) and the (111) orientations agree quite well with those obtained earlier by the grain boundary grooving technique. It is proven that the directions of maximum and minimum D, (the principal axes) for any surface orientation are known if the perfectly ordered plane corresponding to the given surface orientation possesses a plane of mirror symmetry. Thus the principal axes of D, for orientations lying along the sides of the unit stereo-graphic triangle are always known independent of the extent of thermal disorder or impurity adsorption. The merits and shortcomings of King and Mullins' recently published equations relating Ds to the rate of scratch smoothing are discussed. 1N an earlier paper the authors have reported the variation of the surface diffusion coefficient (Ds) with surface orientation on copper.' In that study Ds was determined from the rate of growth of grain boundary grooves on symmetric bicrystals. This gave values of Ds from 850° to 1070°C in a given direction on each of the six surfaces. It was found that the activation energy for surface diffusion was essentially the same for all six surfaces. The theory developed to explain these data assumed that the free energy of any given type of surface site depends only on the number of nearest neighbors the atom has. This same theory predicted that on any given surface Ds should be independent of direction. The primary aim of this study was to check the validity of this prediction for a wide range of surface orientations on copper. The growth of grain boundary grooves is ideal for studying Ds in a given direction on a given surface over a range of temperatures, because the same specimen can be repolished and used again. However, there is considerable work involved in growing a symmetric bicrystal, and for a survey of Ds in two or more directions on many surface orientations, the technique would be arduous. A better technique appeared to be the scratch method used primarily by Mykura. 2 If a scratch is placed in a surface whose surface tension is independent of orientation, the surface will smooth out in time under the influence of surface tension. To determine D, from this flattening, Blakely and Mykura2 used an approximate solution which was assumed to describe the rate of flattening. Recently King and Mullins3 (hereinafter K and M) have given a more exact analysis of the flattening of an isolated scratch. A second aim of this paper was to check the validity of this newer analysis and compare the values of Ds determined thereby with the values obtained from grain boundary grooving techniques. EXPERIMENTAL PROCEDURE In an effort to work with a particular predetermined surface orientation, light orthogonal scratches

Jan 1, 1963

By A. M. Adair

The effect of cathodically charging zone-refined iron with hydrogen and the resultant yield stress-grain size relationship has been investigated by tensile testing at -31°C. The resulting Petch plots (using a least-squares analysis) reveal a significant reduction in the slope and an increase in the intercept for specimens cathodically charged with hydrogen, regardless of whether the hydrogen is present during testing or is removed by evacuation. Other than surface blistering, the major effect of cathodically charging this material is to create occasional grain boundary cracks and thus presumably a large number of free dislocations at grain boundaries. These results are consistent with the hypothesis that the slope of the Petch plot is related to the stress required to activate dislocation sources at or near pain boundaries. While there is no significant effect of the presence of hydrogen on the lower yield stress of this material, the ductility is considerably reduced. After hydrogen removal by evacuation, the ductility recovers substantially and almost complete recovery of ductility is experienced by the smaller grain size specimens. THE influence of hydrogen on the mechanical properties of ferritic materials has received much attention throughout the history of the metallurgy profession. This interest has stemmed from the obvious importance of preventing the catastrophic failure of parts in service, and from the desire to determine what mechanism is responsible for the observed behavior. The various mechanisms proposed for hydrogen em-brittlement have been discussed in detail by Tetel-man,'who concludes that a combination of the applied stress and hydrogen pressure within voids best accounts for the many experimental observations reported. From a quite reasonable correlation of the strain aging and delayed-failure behavior of a variety of materials,2-7 Troiano and coworkers are of the opinion that the delayed-failure mechanism (slow strain rate embrittlement as well) is better explained as a lattice effect; solute elements diffuse to regions of high triaxial stress, form uncondensed atmospheres there, and effect a reduction in the cohesive strength of the lattice. Since hydrogen yield points8,9 have been observed in ferritic materials, and since the hydrogen embrittlement process may be related to strain aging, one further contribution to embrittlement could be hydrogen-dislocation interactions which make crack blunting by plastic deformation a more difficult process. The etch" relationship offers a means of comparing the relative ease of initiating and propagating plastic deformation in metals and alloys. In the present study, this relationship was used to compare the behavior of zone-refined iron in three conditions: uncharged, cathodically charged with hydrogen, and cathodically charged with hydrogen and evacuated. These Petch plots and the observed ductility parameters allowed a separation of the effects of the very presence of hydrogen and the act of cathodically charging hydrogen into this material. MATERIALS AND EXPERIMENTAL PROCEDURE An ingot of zone-refined iron was obtained from Battelle Memorial Institute which contained the following (typical) interstitial impurities in ppm: carbon, 10 * 5; nitrogen, 1; oxygen, 22; hydrogen, 0.9. The ingot was cold-reduced to a 1/2-in.-sq cross section, recrystallized 1 hr at 575°C, and then straight-rolled to a thickness of about 0.105 in. Tensile specimens were milled from the strip having a 1-in. gage length

Jan 1, 1967