Search Documents

By Wedam Nyaaba, Samuel Frimpong, Bruno Ayaga Kansake, Irene Akalanyaba Ateng

Haul truck capacities have increased due to their economies of scale in large-scale surface mines. These high-capacity trucks impose dynamic loads on haul roads. A previous study estimated the dynamic forces imposed by ultra-large trucks on haul roads to be more than three times the static load. These dynamic forces exacerbate haul road stresses and deformation. Current haul road response models are 2D and use static truckloads for low-capacity trucks. No models capture the ultra-large truck dynamic effects on haul road structural response. This study uses 3D finite element (FE) modeling to compute the haul road response to ultra-large truck dynamic loading. The dynamic forces were modeled using multibody dynamics (MBD) in MSC.ADAMS. These forces were used in an FE model developed, verified, and validated in ABAQUS, to simulate the response of the haul road to the dynamic truck forces. The road was modeled using an elastoplastic Mohr-Coulomb model. The results showed that road deformation decreases with increasing layer modulus and increases with increasing payload. Increasing the base modulus from 100 MPa to 450 MPa reduced the maximum deformation from 258 mm to 62 mm. When the subbase elastic modulus increased from 100 MPa to 500 MPa, the maximum deformation decreased from 160 mm to 84 mm. Increasing the payload from 0 to 120% of the rated load increased the maximum wearing surface deformation from 131 mm to 216 mm. This study forms a basis for designing structurally competent haul roads for improving haulage efficiency and truck and operator health.

Jan 7, 2023

By Avnulf Muan, Egil Aukrust

Activity-composition curves jor cobalt oxide and manganese oxide in solid solutions with spinel-type structure have been determined by studying the equilibrium between the spinel phase and a coexisting solid-solution phase in the tewzperature range 1100" to 1400"C. Within limits of experimental error, the system displays the behavior of a regular solution. The excess integral free energy of mixing is represented by the equation . The standard free energy of formation of cobalt manganite, CoMn,O,, from the oxide components COO mzd Mn2OS at 1200°C is calculated to be -8.6 kcal. AMONG the technologically and theoretically most important oxide phases are those which crystallize with the same structure type as the mineral MgO . A120,. Although the name spinel originally was used only for this mineral, the term is generally used today to designate the whole group of oxide phases with this same structure type. It is in this wider meaning that the term is being used in the present paper. The previous literature on spinels is very extensive. There are two aspects of spinels which have attracted particular attention: the structure, including the nature and distribution of the cations present, and the physical properties (electric, magnetic). The status of knowledge in these fields has been well-summarized in recent review articles.1'2 By contrast, thermodynamic properties of spinels are virtually unknown. Delineation of the activity-composition curve over the whole composition range of a solid-solution series with spinel-type structure is the objective of the present work. The system at elevated temperatures (>1000"C) constitutes such a series. The activity-composition curves for this system can be calculated from a study of the equilibrium between the above spinel solid solution and a solid solution (Co,Mn)O with sodium chloride-type structure. Data for the latter solid solution have become available recently.3 The system, in contact with metallic CO at 1200°C, obeys Raoult's law. The determination of the activity-composition curve for the spinel phase is based on the following relations. Consider the reduction-oxidation equilibrium for cobalt ions according to the equation: Because it is impossible in practice to measure single activities of electrically charged constituents, we will treat the equilibria in terms of electrically neutral components. Eq. [I] can then formally be written as follows: where and the activities of cobalt oxide in the (Co,Mn)O and the spinel solid-solution phases, respectively, K is a constant at constant temperature, and Pa is the oxygen pressure of the gas phase. The numerical value of K can be determined from a determination of the oxygen pressure P& for the equilibrium coexistence of Cos04 and COO in the binary system Co-0. Under these circumstances be set equal to 1, and hence K = [Po Eq. [3] can therefore be written

Jan 1, 1964

By Richard M. Foose

Five miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. Geology Lower Cambrian Antietam quartzite and the Rilontalto quartzite, stratigraphi-cally older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65" to vertical. The clay crops out at an elevation of about 1000 feet. Origin and Character The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there Are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about loo ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: SiO2, 67.05 per cent; Al2O3, 22.27; Fe2O3, 0.40; CaO, 0.00; TiO2, 1.05; MgO, 0.52; Na20, 0.04; K2O, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1948

By R. A. Stauffer

THE chief ore of lithium is spodumene, a lithium-aluminum silicate containing up to 3 pct lithium. The preparation of lithium salts from spodumene is costly because of the low concentration of the metal and the difficulty of separating it from the other alkali metals present. Dr. Kroll's and Dr. Schlecten's recent paper' has reviewed various methods proposed for preparation of lithium. It will be seen from this paper that the methods proposed to date have required one or another of the lithium salts as a raw material. The high cost of these salts has been the chief item of expense in the lithium metal produced. This situation has made it interesting to investigate the possibility of producing the metal directly from spodumene. When spodumene is calcined at 1000°C in the presence of lime, lithium oxide is replaced in the ore as is evidenced by the fact that it may be leached from the reaction mixture with water.2 Free energy calculations suggested that lithium oxide might be reduced with aluminum or silicon and the lithium produced distilled from the reaction mixture by heating to about 1000°C in a vacuum. These facts taken together suggested that it might be possible to prepare lithium metal directly from spodumene by heating a mixture of the ore, lime, and a suitable reducing agent in vacuum and distilling off the lithium metal as formed. THE REPLACEMENT OF Li20 IN SPODUMENE A series of experiments were undertaken to determine the ratio of lime to spodumene necessary to free substantially all the lithium oxide present in the ore. The spodumene used in these experiments was supplied by Foote Mineral Co. in the form of powder of about 200 mesh. Analysis of the spodumene was as follows: [ ] Lime (cp -200 mesh) was added in various ratios to spodumene and thoroughly mixed in a ball mill. Two hundred gram samples of spodumene-lime mixtures were charged loosely in fireclay crucibles and held at 1000°C in a gas-fired furnace for 5 hrs. The product in each case was ground to pass 140 mesh and then placed in a thimble in a soxhlet extractor. Extraction with water was carried on for 6 hrs. After this period the extract was reduced in volume by evaporation in order to precipitate dissolved lime and was then filtered and titrated with 1/4 normal hydrochloric acid. After correcting for residual calcium oxide in solution, the alkali present was calculated as lithium oxide. The results of these experiments are shown in Table I and Fig I. At lime-spodumene ratios less than 1.5, the products were invariably fused. At the ratio of 1.5 and above, the product was loosely sintered with little evidence of fusion. When the ratio of lime to spodumene was three, replacement of alkali oxides in the

Jan 1, 1947

By K. L. Moazed, G. M. Pound

An investigation was made of the deposition of silver from a thermal beam onto tungsten field-emitter tips at 300°K. "Island"-type nuclei were observed to form and grow. The nucleation of silver crystals occurs preferentially on non-close -packed planes of a tungsten tip at a critical volume free-energy change of about —2900 cal per cc. The adatom population which is critical for appreciable nucleation rate of silver crystals is about 0.2 of a monolayer and is essentially independent of beam flux, time, and source temperature. This result is strong evidence that a metastable equilibrium exists between adatoms and critical nuclei, as assumed in the present theory. SOME of the more significant studies of nucleation in deposition of metals from vapor beams have been conducted by measuring the thermal beam flux which is critical for appreciable rate of nucleation on a substrate surface held at a given temperature.'2 The observed critical supersaturations may be described in terms of Eq. [7] which was derived3'3a on the model of an adsorption, surface migration, and statistical fluctuation mechanism. However there usually made with a low-power optical microscope, a fairly insensitive method of detection. The object of the present study was to overcome some of these difficulties by measuring the critical supersaturation for condensation of a thermal beam of silver onto a tungsten field-emitter tip. Such a tip may be cleaned by electrically heating it to a high temperature in situ, and the high vacuum obtainable in a field-emission tube (10-10 torr) precludes adsorption of residual gases for convenient periods of time. Furthermore, the degree of cleanliness, the orientation, and the state of imperfection of the tip may be ascertained from the field-emission pattern. Detailed explanations of theoretical considerations and experimental procedures relating to the field-emission microscope may be found in a number of excellent review articles12'13 and thus only a brief description will be given here. The electronic work function of a metal is defined as the energy that an electron needs to escape from the potential field of the solid. By applying a large field between the surface of the solid and a suitable collector, it is possible to free the electrons by the tunnel effect. Fields of approximately 30 million v per cm are needed to produce this effect, and such fields are obtained in practice by using microscopic surfaces of high curvature (tips). Because the work function of a metal is a function of surface orientation, the emission from the various planes is different, and thus it is possible to obtain a representation of the surface in the emission microscope. In general, the work function is higher for the more densely packed planes. Fig. 1 shows a pattern for "clean" tungsten in which the central dark region represents the (110)

Jan 1, 1964

By Richard M. Foose

Five miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. Geology Lower Cambrian Antietam quartzite and the Rilontalto quartzite, stratigraphi-cally older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65" to vertical. The clay crops out at an elevation of about 1000 feet. Origin and Character The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there Are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about loo ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: SiO2, 67.05 per cent; Al2O3, 22.27; Fe2O3, 0.40; CaO, 0.00; TiO2, 1.05; MgO, 0.52; Na20, 0.04; K2O, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1948

By J. Philip Neal, Carroll P. Rogers

Feldspars, the most abundant minerals of the igneous rocks, occur in numerous forms and mixtures. The feldspars of commercial significance are found in widely distributed pegmatites as large crystals usually free of iron- bearing impurities and thus suitable for hand-cobbing, and also in larger bodies where the ore contains various types of feldspar inter- mingled with quartz and relatively free of iron- bearing impurities, or at least readily unlocked from impurities present at relatively coarse mesh. The latter type of ore includes some pegmatites, and the ''alaskite" bodies so common in the Spruce Pine district of North Carolina. On the west coast of the U.S. and in Oklahoma there is-r has been--commercial recovery of natural feldspathic sand as a source of alumina in glass and ceramics. "Aplite" in commercial terminology is a light-colored igneous rock with a granitic composition and a fine sugary texture, often banded with readily removable iron impurities. Two areas in Virginia produce aplite for the glass industry: one located in the vicinity of Piney River, Amherst County, and the other near Montpelier in Hanover County. According to Deer et al. (1966) the word feldspar derives from the Swedish feldt or falt (field) and "spath:" chunks of rock appearing in tilled ground overlying granite. Castle and Gillson (1960) indicate a Germanic origin, citing "spat," which is said to refer to any transparent or translucent material which is readily cleavable. The term "spar" has in the past been applied to minerals other than feld- spar, such as barite, calcite, and fluorite. It is correct to call the latter "fluorspar." There is a true barium feldspar, but it is rare and of no present economic importance. What is recognized as feldspar or "spar" by present producers and consumers consists of three silicate minerals which, if pure, would have the formu- las KAISi,O, (microcline or orthoclase), NaAlSi,O, (albite), and CaAl,Si,O, (anorthite). These are almost never found in pure form in nature, but occur together in great abundance in a three-component system. A considerable number of different combined ratios of these three exists, with the exception that isomorphism between potassium spar and calcium spar is very limited. User specifications for feldspar products are largely built around the prevalent naturally occurring ratios. Pas- sages following will refer to "K-spar," "Na- spar," or "Ca-spar." Nomenclature and Descriptive Terms Relating to both the mineralogy and the economics of feldspar are certain terms whose coverage it is useful to specify. Commercially, aplite is a feldspathic rock mined and beneficiated in two locations in Virginia, in which both titanium and feldspar minerals are present-the latter now being the major, if not the only, economic product. Technically, the term aplite when applied to this rock is of questionable accuracy. But, in light of accepted commercial usage, the term will be here used to designate it. Regarding the Virginia rock, Ross (1941) is cited.

Jan 1, 1975

By A.A. Gustafson

In diamond or churn drilling for the prospecting of ore bodies, two products can be used for quantitative analyses; i.e., the core and the cuttings, or sludge. Some operators prefer an assay of core; others insist that the sludge be sent for analysis. Both must recover the sludge for check samples or for assays if there is no core recovery for any particular section of the diamond-drill hole. The Freeport Sulphur Co. found that numerous cumbersome sludge boxes or barrels were inconvenient and delayed drilling. The sludge settled slowly in the ordinary shallow, rectangular diamond-drill boxes and its total removal from the container was difficult, time-consuming and unsatisfactory; and sampling of deposits of which the metal contents are easily concentrated, as in ores containing cinnabar, gold and silver, is subject to error if the boxes are not thoroughly cleaned. Mr. Charles Ballard, dredge superintendent at Freeport's operation at Grande Ecaille, Louisiana, developed a portable cone while he was in charge of prospecting a mercury property near Tonopah, Nevada, in 1940. Ballard later improved the design while the settler was being used at a manganese property in New Mexico. The operation is based on the "free settling" of comminuted particles in a quiescent liquid. The ordinary sludge box discharges over a lip 8 to 12 in. wide and consequently the water has sufficient velocity so that the discharge water is never clear. The cone settler used by Free-port Sulphur Co. discharges over the entire circumference, which gives a discharge ltp of 9 ft. in the size of cone used at the cinnabar and manganese prospects. Consequently, the velocity of the discharge water is slow enough so that all fine material settles and the discharge water is clear. When the drilling of a sample interval is complete, the sludge can be drawn off by the time the driller is ready to cut another sample. Thus, only one cone is needed per drill. The cone has been used by Freeport successfully in churn-drilling a manganese deposit, in diamond-drilling a mercury deposit, and in diamond-drilling a deposit of ore containing tin, copper, gold and silver. The cone is greatly superior to the old methods of collecting sludge and is now used on all Freeport drilling campaigns in the western states, both for surface and underground drilling. Fig. I shows the important details of a cone designed for average operating conditions, 30 in. in diameter and 36 in. high. Abnormal conditions may require some revisions in design. Fig. 2 shows a working drawing. A hose or pipe larger than the one used to convey water from the pump to the swivel head of the string of rods is connected to the stuffing box at the collar of a diamond-drill hole, The usual T-connection is used. It is not necessary to use a stuffing box if the top of the cone can be placed lower than the collar of the hole. Then the return water and cuttings can be made to flow by gravity. This hose or pipe discharges the cuttings of the drill bit and the return

Jan 1, 1943

By R. D. Pehlke, J. V. Gluck, R. L. Louvet

A study has been made of the effect of small additions of bismuth on the activity of zinc in dilute solution in molten tin. Free-energy interactions have previously been determined between zinc and various third elements where the solvents were molten bismuth or molten lead.'-4 In both of these solvents, the activity of zinc exhibits a strong positive deviation from ideal behavior (at 550°C y° for zinc in lead is 11.4 and for zinc in bismuth is 3.0). The present work, using tin as the solvent, is an extension to a case where the positive deviation is considerably diminished (y°Zn at 550°C is 1.63). Several previous investigators have studied the Zn-Sn binary system; however, little data is available in the range below 0.1 mole fraction zinc.5= Previous high-temperature galvanic cell studies in the Sn-Zn-Bi ternary system included the determination by Gluck and Pehlke of interactions in the bismuth-rich corner1 and separate investigations of the central region by Oleari and Fioriani6 and by Ptak and Moser.7 Yokokowa et al.8 conducted Knudsen effusion studies in the central region; however, their experiments at 625°K were conducted somewhat below the present experimental temperature range. Their results indicated an increase in zinc activity with the addition of bismuth. The present series of experiments was conducted in galvanic cells represented as follows: Zn Zn++ in LiCI-KC1 eutectic Zn + Bi in Sn (pure reference (fused salt electrolyte) (molten alloy) standard) The experimental apparatus. a multi-electrode system employing alumina crucibles and contained in a Vycor tube under a helium atmosphere, has been described previously, as have been the experimental procedures, precautions, and the methods of data reduction.1-4,- The experimental measurements were made over the range from 450° to 650°C. Between thirty and forty measurements were made in each run. The linearity of the electromotive force vs temperature relations was verified by linear regression techniques. The correlation coefficients exceeded 0.99. The experimental results summarized in Table I include the interpolated electromotive force at 550°C and the temperature dependence of electromotive force. Only results from stable and consistent cells containing more than 0.025 mole fraction zinc are reported. Attempts to run cells at 0.01 or 0.02 mole fraction zinc were not satisfactory. This is attributed to the closeness of the free energies of formation of the chlorides of tin and zinc. Calculations employing Wagner and Werner's criteria for displacement reactions10 indicated that reduction of the zinc content to 0.01 mole fraction places the cell near the borderline concentration for a 1 pct error in measured potential. The compositions shown in Table I are the actual weighed-in amounts. Previous experience has indicated that compositional changes during the running of a stable cell are negligible.' Over the range of compositions studied for the binary alloys, the activity coefficient of zinc was essentially constant indicating that Henry's law is followed to 0.05 mole fraction zinc. The temperature, OK, de-

Jan 1, 1969

By A. A. Gustafson

In diamond or churn drilling for the prospecting of ore bodies, two products can be used for quantitative analyses; i.e., the core and the cuttings, or sludge. Some operators prefer an assay of core; others insist that the sludge be sent for analysis. Both must recover the sludge for check samples or for assays if there is no core recovery for any particular section of the diamond-drill hole. The Freeport Sulphur Co. found that numerous cumbersome sludge boxes or barrels were inconvenient and delayed drilling. The sludge settled slowly in the ordinary shallow, rectangular diamond-drill boxes and its total removal from the container was difficult, time-consuming and unsatisfactory; and sampling of deposits of which the metal contents are easily concentrated, as in ores containing cinnabar, gold and silver, is subject to error if the boxes are not thoroughly cleaned. Mr. Charles Ballard, dredge superintendent at Freeport's operation at Grande Ecaille, Louisiana, developed a portable cone while he was in charge of prospecting a mercury property near Tonopah, Nevada, in 1940. Ballard later improved the design while the settler was being used at a manganese property in New Mexico. The operation is based on the "free settling" of comminuted particles in a quiescent liquid. The ordinary sludge box discharges over a lip 8 to 12 in. wide and consequently the water has sufficient velocity so that the discharge water is never clear. The cone settler used by Free-port Sulphur Co. discharges over the entire circumference, which gives a discharge ltp of 9 ft. in the size of cone used at the cinnabar and manganese prospects. Consequently, the velocity of the discharge water is slow enough so that all fine material settles and the discharge water is clear. When the drilling of a sample interval is complete, the sludge can be drawn off by the time the driller is ready to cut another sample. Thus, only one cone is needed per drill. The cone has been used by Freeport successfully in churn-drilling a manganese deposit, in diamond-drilling a mercury deposit, and in diamond-drilling a deposit of ore containing tin, copper, gold and silver. The cone is greatly superior to the old methods of collecting sludge and is now used on all Freeport drilling campaigns in the western states, both for surface and underground drilling. Fig. I shows the important details of a cone designed for average operating conditions, 30 in. in diameter and 36 in. high. Abnormal conditions may require some revisions in design. Fig. 2 shows a working drawing. A hose or pipe larger than the one used to convey water from the pump to the swivel head of the string of rods is connected to the stuffing box at the collar of a diamond-drill hole, The usual T-connection is used. It is not necessary to use a stuffing box if the top of the cone can be placed lower than the collar of the hole. Then the return water and cuttings can be made to flow by gravity. This hose or pipe discharges the cuttings of the drill bit and the return

Jan 1, 1943

By R. V. Riley

IN the metallographic examination of the alloys of iron and silicon, several investigators1-' have reported on the occurrence of an unusual type of etched structure, particularly in the alloys of higher silicon content. This, the so-called "barley shell" structure, has been observed with iron-silicon alloys over a wide range of silicon content, and under certain circumstances it can be seen upon the micro-sections of pure iron. The barley shell structure may be demonstrated most easily with iron-silicon alloys in the range 8 to 20 pct Si after etching in a hydrofluoric acid base etchant. Two etchants which produce the structure are: Corson's reagent, which is 2 parts hydrofluoric acid, 1 part nitric acid, and 2 parts glycerol; and picric acid reagent, which is 1 part hydrofluoric acid and 1 part saturated solution of picric acid in alcohol. Both when freshly prepared and used for etching commercial silicon-iron alloys containing 14 to 16 pct Si, invariably produce the barley shell structure shown in Fig. la. It is now well known that the barley shell structure is a pseudomorph and the true structure of an alloy of this composition consists of a single phase of silico-ferrite together with graphite as shown in Fig. lb. Lower silicon alloys and even pure electrolytic iron may also be etched in the above reagents to give the barley shell provided the etchant has been either: 1—Stored in contact with glass or silica, or 2—used previously for etching an iron containing silicon. Pure iron etched in perfectly pure hydrofluoric acid base etchants free from silicon contamination gives a normal structure free from the barley shells. Therefore, although the hydrofluoric acid in the reagent primarily is responsible for the barley shells, silicon, or its compounds, also must be present, either in the etching reagent or in the specimen. It was of considerable interest to the author to read the paper by Wachtell,? in which the barley shell etch was deliberately used for the identification of the boundaries of high and low silicon areas in diffusion experiments made upon laminate bars of compacted and sintered pure iron and ferrosili-con powders. This method of utilizing the barley shell etch is novel and in the hands of the investigator gave a useful differentiation between the high and low silicon areas in those specimens. For the reasons already given, however, the technique is not to be regarded as of universal application. Misleading results might be obtained, for example, if two or more specimens were etched in the same etchant. Fresh pure reagents only must be used each time. Provided this is done and the investigators are well aware of the limitations of the method, then the barley shell pseudomorph can be made of limited use in distinguishing between higher and lower silicon areas in a microspecimen of a ferrous material. The greatest of care must be exercised in the interpretation of the results which may be regarded as qualitative only and may, in fact, not be specific to silicon alloys.

Jan 1, 1952

By John D. Morgan

Introduction The US Bureau of Mines' (USBM) world reserve/consumption ratios (Table 1) indicate that, if the world is relatively peaceful in the next two decades, there should be ample world supplies of minerals to permit rising standards of living for increasing world population. But it must be remembered that most mineral reserve estimates are conservative and that normal mining practice is to develop a ton of ore reserve for every ton mined. It should be noted that "reserve," as used in this paper follows the definition given in US Geological Survey (USGS) Circular 831, 1980; "that part of the reserve base which could be economically extracted or produced at the time of the determination." In addition to accurately determining the geologic parameters of mineral deposits, a judgment as to whether that deposit is a "reserve" per se involves consideration of many other factors. These factors were recognized nearly a century ago by a well-known mining engineer and later President, Herbert Hoover. In "Principles of Mining," 1909, Hoover wrote: "Unfortunately for the mining engineer, not only has he to weigh the amount of risk inherent in calculations involved in the mine itself, but also that due to fluctuations in the value of metals. If the ore is shipped to custom works, he has to contemplate also variations in freights and smelting charges ...In a free market, the law of supply and demand governs the values of metals as it does that of all other commodities. So far, except for tariff walls and smelting rings, there is a free market in the metals under discussion. The demand for metals varies with the unequal fluctuations of the industrial tides. The sea of commercial activity is subject to heavy storms, and the mine valuer is compelled to serve as weather prophet on this ocean of trouble. High prices, which are the result of industrial booms, bring about overproduction, and the collapse of these begets a shrinkage of demand, wherein consequently the tide of price turns back." Current supplies and use There have been ample supplies of most mineral materials to permit several-fold increases of world production of common major mineral based minerals (steel, aluminum, copper, and cement) over the past three decades. Motor vehicle production is a major consumer of mineral materials. However, in the last decade, down-sizing to facilitate improved fuel efficiency and reduce harmful emissions has reduced the weight of the average US-made automobile 15%, to 1.5 t (3200 lbs). Also in the US, there are 92 million dwelling units, or on average, fewer than three persons per dwelling unit. Construction is another major consumer of materials in the industrialized developed countries. It will also be a major consumer of materials worldwide as less developed nations seek to improve their infrastructures by adding roads, bridges, railroads, airfields, ports, and housing. Fortunately, a large number of traditional common materials, many of mineral origin and also many of agricultural origin, are readily available for construction. Traditional construction materials such as steel, aluminum, copper, and cement, are being replaced in many applications by engineered plastic and ceramic

Jan 4, 1986

By L. J. Dijkstra, R. J. Sladek

IN earlier work the effect of manganese on the general behavior of nitrogen in iron was the subject of a careful examination by Fast.' Part of the investigation was made, in collaboration with one of the present authors (L.J.D.), by using the internal friction method. This technique, which has been described elsewhere,' showed some significant changes in the properties of Fe-N alloys by the addition of a small amount of manganese namely: 1—Under standard conditions the maximum of the nitrogen peak in pure iron appears around 20 °C and the half width is about 27 °C. By addition of 0.5 atomic pct Mn a general broadening of the internal friction peak occurs. The half width is increased by about 9°C. Moreover, a shift of the maximum of about 5°C toward a higher temperature takes place, Fig. 2. 2—The precipitation of nitrogen from the supersaturated solution, measured, e.g., at 200 °C, was inhibited by the addition of the amount of manganese given in effect 1. The broadening of the nitrogen peak was confirmed in more recent work3 on samples which were prepared from Westinghouse Puron iron. The effect of manganese on the rate of precipitation, however, was much less striking than in the earlier work' based on Philips high purity iron. Theory To explain the first change in properties just referred to, effect 1, the following two assumptions were made:' First, every manganese atom in sub-stitutional solid solution creates around it six interstices located between an iron and a manganese atom, as is evident from Fig. 1. These interstices, conveniently called Fe-Mn interstices, have for nitrogen a free energy level which is AG* lower than the normal Fe-Fe interstices between two iron atoms. For such low concentrations of manganese as 0.5 atomic pct, the possibility that two manganese atoms will be nearest neighbors can be disregarded. Second, it is assumed that in addition to the normal relaxation time TFe at least one new relaxation time, Mn, Fe, enters in the phenomena which is associated with the elementary diffusion jumps between a Fe-Mn interstice and an adjacent Fe-Fe interstice. Fig. 1 gives schematically the free energy for a nitrogen atom as a function of its position along the line ABC. A tentative analysis of the nitrogen peak in a 0.5 pct Fe-Mn alloy based on these assumptions has been made in Fig. 2. The dotted curve with a maximum at 22°C is caused by jumps between Fe-Fe interstices, the dotted curve with maximum at 32°C by jumps between an Fe-Mn and an Fe-Fe interstice. The two effects added together give the dash-dot internal friction curve for the alloy. In the following these two components will be referred to as the normal peak at 22°C and the abnormal one. (The small secondary peak at

Jan 1, 1954

By E. W. Hough, G. L. Stegemeier

Empirical equations for surface tension of propane and normal butane as functions of reduced temperature are obtained from experimental data. Another correlation relating surface tension to enthalpy of vaporization is given for these two compounds. In addition, new paracbor numbers are calculated for the normal paraffin hydrocarbons. These numbers are utilized for the calculation of interfacial tension of two-component systems as functions of pressure and temperature, using a modified form of Weinaug-Katz equation. The experimental data for two binary systems are approximated by the correlation. From these results it is found that the interfacial tension in the high-pressure region remains extremely low at large pressure decrements below the critical pressure. Thus, it appears that condensate systems may have flow characteristics almost like single-phase conditions even though the pressure is within the two-phase region. Experimental data have shown that interfacial tension divided by density difference approaches zero as the critical pressure is approached. A calculation of wetting-phase saturations indicates that the saturation gradient at the two-phase contact becomes increasingly abrupt as the critical pressure is approached. DISCUSSION Prediction of the surface and interfacial tension of the light hydrocarbons and of two-component hydrocarbon mixtures at various temperatures and pressures may be made if other physical properties are known. Extensive experimental work on single-component and binary systemsl is the basis for the correlations outlined in this paper. Interfacial tension is defined as the specific surface-free energy between two phases of unlike fractional composition, while surface tension is defined as the specific surface-free energy between two phase:; of the same fractional composition. The usual definitions relating interfacial tension to a liquid-liquid interface and surface tension to a gas-liquid interface are not clearly defined when the critical region is included, and there is no sharp distinction between a gas and a liquid phase. Interfacial tension is probably the most important single force that makes one-half to one-third of the total oil actually in place in a reservoir rock unrecoverable by conventional gas-drive or waterflood methods. A rough estimate of this figure for the United States is 100 billion bbl. Interfacial tension presently is used by petroleum engineers in the estimation of saturation gradients at the gas-oil contact and at the oil-water contact. The data in this paper should prove useful for estimates of reserves involving gas-oil contacts. Relative permeability undoubtedly is influenced by interfacial tension, for sufficiently small values. These data should be useful in determining how small the values are In addition, these data should eventually add to our fundamental knowledge of surfaces. At the critical point, all surface excesses approach zero and the thickness becomes very large. SINGLE-COMPONENT SYSTEMS It has been observed1 that the following relationships are good approximations to the physical properties of propane and n-butane.

By V. P. Bhavanandan

The mucus secreted in the respiratory tract provides the first barrier against inhaled particulate and gaseous toxicants. Trachea removed from pathogen-free rats were maintained as organ cultures and used to study the effects of coal dust exposure on the synthesis of mucin. The high molecular weight isotopically labeled (3H-glucosamine, 14Cleucine or 35S-sulfate) mucin could be purified by gel filtration, treatment with testicular hyaluronidase, ion exchange chromatography, delipidation and CsBr density gradient centrifugation. To examine effect of coal dust on mucin production, groups of explant cultures were exposed to media containing coal dust at 100 µg per ml every 2 days for 2 weeks while control cultures were treated with media without dust. Analysis of the spent culture media showed that treatment with dust markedly decreased the production of nondialysable glycoproteins as well as hyaluronidase-resistant acid-precipitable fraction consisting mainly of mucin. Since the synthesis of protein was not affected to the same extent the decrease in mucin production is not entirely due to cell death. In separate experiments rats were subjected to in vivo coal dust exposure in inhalation chambers and tracheae of these and control rats were removed for explant cultures. The incorporation of precursor isotopes into mucin by these explant cultures are being examined. (Supported by U.S. Bureau of Mines through the Generic Mineral Technology Center for Respirable Dust under grant G1135142, project 4210).

Jan 1, 1988

[A session of the Institute of Metals held during the February, 1926, meeting of the Institute, was devoted to a symposium on ''gas" in copper. S. Skowronski, Perth Amboy, N. J., was chairman. On the program were papers by T. S. Fuller; W. H. Bassett and J. C. Bradley; Susan B. Leiter, and W. H. Bassett and H. A. Redworth. These papers follow the chairman's introductory discussion.] S. Skowronski, Perth Amboy, N. J.—There are today two groups of metallurgists, one group who believe in oxygen-free copper and another group who believe that oxygen is absolutely essential in copper; not that the two groups disagree, but that a certain grade of work calls for oxygen-free copper, while another grade of work does not. I can sum up the problem by reading the abstract of an article by Frederick Johnson of Great Britain in The Metal Industry of Sept. 4, 1925. Few, who have watched the trend of things during the last two decades, can have failed to notice the steady growth of opposition to the prevalent use of copper in the "tough-pitch" condition, which for many ages enjoyed an unchallenged supremacy. Broadly speaking, there are two schools of thought in the metallurgical world, one holding the view that copper containing a small proportion of oxygen is an eminently suitable material for users, the other expressing its preference, in no hesitating or uncertain manner, for copper from which oxygen has been removed by means of a deoxidizer. In the old days, before the advent of the converter and the electrolytic refining process, the copper of commerce was so impure that the presence of oxygen was imperative in order to neutralize the influence of impurities which militated against the hot-working properties of the metal. For electrical purposes, oxygen must be present, because sound bars and billets cannot be produced without it, except at the expense of electrical conductivity. For most engineering purposes, however, electro-deposited copper may be used either by itself or with the addition of alloying elements, e. g., arsenic and nickel, which experience has proved to be beneficial, such copper being freed from oxygen by the aid of a deoxidizer, e. g., phosphorus. Such material has positive advantages over "tough-pitch" copper as at present produced from refinery furnaces. It has greater toughness and malleability, and is immune from the action of reducing gases at high temperatures, the destructive action of which, in the case of "tough-pitch" copper, is well known. The reasons why there has been no wholesale replacement of "tough-pitch" copper by deoxidized copper are commercial in nature; copper can be more economically melted in large-capacity furnaces which lend themselves to the poling process and are not so suitable for control of uniformity of action of deoxidizers as the smaller electric or crucible furnaces, whilst they are also more convenient for the production of very large castings. Moreover, the equipment of most large copper manufacturing plants is designed for casting "tough-pitch " copper in open moulds, e. g., wire bars and cakes, and these could not be used for deoxidized copper, which must be cast in vertical moulds as in brass-shop practice. Further, there are still certain impure brands and

Jan 1, 1926

By W. Bleloch

Published in the Journal, September 1970, and presented at a colloquium on 'Future of the Steel Industry', 17th March, 1971. Errata (a) The final sentence in the penultimate paragraph, left hand column p. 34 of the text should read: 'In the hot regions of the bosh and stack the C+CO2=2CO reaction proceeds to CO from coke carbon and carbon dioxide generated by reduction of iron oxides by CO (the so-called solution loss of carbon)'. The italicised words have been omitted in the text. (b) Temperature in Fig. 3 is K not C. (c) In Fig. 9, connection from top plate of column 10 to heat exchanger 9 has been omitted. DISCUSSION J. B. BEEDON AND C. J. JONKER* Dr Bleloch's paper has outlined the advantages of recycling stack-gas of low nitrogen content in the blast furnace. In the first instance it would appear to be extremely beneficial in controlling the hearth temperature and allowing a 100 per cent oxygen-blast to be used. On a second point however we have to disagree. It is claimed that heat is liberated in the combustion zones by the oxidation of CO to CO2 near the tuyeres and in the subsequent reduction of the CO2 by CO. The author has hypothesized as follows, and we quote: 'The C+CO2=2 CO reaction in the outer combustion zone at about 1 700°C is no longer endothermic due to loss of stability of CO2 and its consequent dissociation into CO and free oxygen.' This statement requires closer examination. If we consider the individual events occurring with the CO in the recycled topgas, with the oxygen in the blast and with the coke in the burden, as done by Dr Bleloch, the following heat considerations emerge. All heats of reaction are calculated from the enthalpy values of each reactant and product, as well as the temperature dependence of their molar heat capacities. (a) At the tuyeres: CO+1/2 O2-+CO2 . . . . . (1) CO, CO2 at 500°C; O2 at 25°C. ?H reaction = -65 000 cals/mole CO The reaction (1) is exothermic. (b) In the outer combustion zone: CO2+C?2 CO . . . . . . . . (2) C, CO at 1 700°C; CO2 at 500 0C. ?H reaction = -56 000 cals/mole CO Reaction (2) is endothermic. The overall heat gain of reactions (1) and (2) is ?H=+56 000 - 65 000= -9000 cals/mole CO i.e. the overall reaction is slightly exothermic, the amount of heat liberated is however smaller than suggested by Dr Bleloch. (c) The dissociation CO2+CO+1/2 O2 . . . . . (3) is a highly endothermic reaction at 1 700 0C, requiring 82 000 cals/mole CO2 to proceed to completion. Furthermore, this reaction (3) is energetically not favoured to proceed, as can be observed from the free energy-temperature relationship of figure (3), which favours the formation of CO2 at 1 700 0C. Hence direct dissociation of CO2 at 1 700 0C appears to be unlikely.* The concept of recycling topgas is however still intriguing from many other points of view. Apart from providing a very efficient method of hearth temperature control, it will create a much higher CO partial pressure in the stack. Whether the rate of indirect reduction in the stack will be proportional to this partial pressure or not is un-

Jan 9, 1970

By R. B. Walker, R. Palmer, L. C. Bryner

The purpose of this investigation was to further study some of the factors affecting the air oxidation of sulfide minerals. Data obtained from laboratory studies on the effect of temperature, concentration of iron salts, pH, and other catalysts on the biological and nonbiological oxidation of sulfide minerals are presented. The oxidation of copper sulfide minerals and subsequent leaching of the soluble copper has long been a profitable operation. The chief oxidizing agent is oxygen from the air. This reaction is influenced by a number of different factors such as temperature, light, hydrogen ion concentration, oxidizing agents, and various catalysts. Sullivan1 found that copper sulfide minerals are slowly oxidized by the air and that dilute sulfuric acid and iron (111) increased their solubility. At that time it was not known that bacteria were involved in the oxidation of the sulfide minerals. It has been shown that pyrite, molybdenite, free sulfur, and the copper sulfide minerals found in the waste rock dumps in Bingham Canyon, Utah, are largely oxidized by chemosynthetic autotrophic microorganisms found in the leaching streams.2-6 Similar organisms have been isolated in other mining areas7,8 and from the effluents from coal rnines.9 The following are some of the questions that have arisen regarding the mechanisms of the reactions involved in the leaching process. How dependent is the leaching operation upon the biological reactions? How does the temperature effect the biological and non-biological reactions? How does the concentration of iron (II) and (111) effect the rate of oxidation of copper (II) sulfide? Does the iron act as a catalyst? Does activated carbon act as a catalyst on the oxidation of sulfide minerals? What effect does the hydrogen ion concentration (pH) have on the above reactions? The purpose of this paper is to report the results of laboratory studies on these problems. EXPERIMENTAL The apparatus used in this investigation was an air lift percolator described in our earlier work.' The percolator consisted essentially of an air lift which enabled the leaching solution and microorganisms to pass freely through a suspension of mineral (substrate) in Ottawa sand. The air lift served the additional purpose of maintaining an ample concentration of oxygen and carbon dioxide in the nutrient (leaching) solution. (See Fig. 1.) The percolators were so constructed that they could be immersed in liquid constant temperature baths for temperature studies. The thermostats were controlled to +0.5°C. The reactions were all run in the dark. The percolators were charged with one to three g of mineral, dispersed in 100 g of Ottawa sand and 100 ml of nutrient or leaching solution. The sand was purified to remove traces of iron by digesting with concentrated hydrochloric acid and washng with distilled water until free from chloride. After drying, the sand was ready for use. The compressed air supply was regulated to 5 psi and bubbled through an aerator containing distilled water, which was maintained at the same temperature as the bath used. The air was filtered through cotton plugs to maintain sterile conditions. The tops of the

Jan 1, 1968

By R. A. Stauffer

The chief ore of lithium is spodumene, a lithium-aluminum silicate containing up to 3 pct lithium. The preparation of lithium salts from spodumene is costly because of the low concentration of the metal and the difficulty of separating it from the other alkali metals present. Dr. Kroll's and Dr. Schlecten's recent paper1 has reviewed various methods proposed for preparation of lithium. It will be seen from this paper that the methods proposed to date have required one or another of the lithium salts as a raw material. The high cost of these salts has been the chief item of expense in the lithium metal produced. This situation has made it interesting to investigate the possibility of producing the metal directly from spodumene. When spodumene is calcined at 1000ºC in the presence of lime, lithium oxide is replaced in the ore as is evidenced by the fact that it may be leached from the reaction mixture with water.2 Free energy calculations suggested that lithium oxide might be reduced with aluminum or silicon and the lithium produced distilled from the reaction mixture by heating-to about 1000ºC in a vacuum. These facts taken together suggested that it might be possible to prepare lithium metal directly from spodumene by heating a mixture of the ore, lime, and a suitable reducing agent in vacuum and distilling off the lithium metal as formed. The Replacement of Li2O in Spodumene A series of experiments were undertaken to determine the ratio of lime to spodumene necessary to free substantially all the lithium oxide Present in the Ore. The spodumene used in these experiments was supplied by Foote Mineral Co. in the form of powder of about 200 mesh' Analysis of the spodumene was as follows: PCT SiO2......................... 62.7 Al2O3........................ 29.9 Li2o......................... 4.9 Na2O........................ 0.89 CaO......................... 0.75 MgO........................ 0.49 K2O......................... 0.44 Lime (cp —200 mesh) was added in various ratios to spodumene and thoroughly mixed in a ball mill. Two hundred gram samples of spodumene-lime mixtures were charged loosely in fireclay crucibles and held at 1000ºC in a gas-fired furnace for 5 hrs. The product in each case was ground to pass 140 mesh and then placed in a thimble in a soxhlet extractor. Extraction with water was carried on for 6 hrs. After this period the extract was reduced in volume by evaporation in order to precipitate dissolved lime and was then filtered and titrated with 1/4 normal hydrochloric acid. After correcting for residual calcium oxide in solution, the alkali present was calculated as lithium oxide. The results of these experiments are shown in Table I and Fig I. At lime-spodumene ratios less than 1.5, the products were invariably fused. At the ratio of 1.5 and above, the product was loosely sintered with little evidence of fusion. When the ratio of lime to spodumene was three, replacement of alkali oxides in the

Jan 1, 1949

By E. P. Abrahamson

The effect of transition element binary solid solution additions upon the re crystallization temperature of nickel has been investigated. All additions raised the re crystallization temperature. Both the rate of change of re crystallization temperature with at. pet solute and the limit of initial linearity are found to correlate with the free atom ground state outer electron configuration of the solute element. A comparison of all of the correlations for the transition elements studied has yielded a set of empirical relations, which allows the prediction of the effect of dilute binary transition elements on the recrystallization temperature of other transition elements. The work of Abrahamson, et al.1-7 on dilute binary solution alloys indicated a correlation between the free atom ground state electron configuration of the solute and both the brittle-ductile transition and re-crystallization temperature. Further, it has been shown3,4 that the limit of initial linearity may also be correlated with the solute electron configuration. Since previous studies have dealt with bee and hexagonal base elements, this study is made to note what effect, if any, the fee base structure might have. Nickel also serves to give a solvent configuration which will allow the comparison of all of the transition element solvents. Olsen8 has studied the effect of some trace elements upon the recrystallization of nickel. He included only Ti, Zr, W, Mn, and Co of the transition elements. The differences in change of recrystallization temperature were attributed to the solute atom size and to the solubility of the solute in nickel. PROCEDURE All alloys were made using 99.9 + pet Ni with 0.003 C, 0.015 Fe, 0.007 0, and 0.0007 H. The solute elements were 99.9 + pet pure. According to the published binary phase diagrams9 and metallo-graphic examinations at X750, all solute elements were in solid solution. The alloys were arc melted and remelted four times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot forged at 800oC to 0.750 in. diam, machined to 0.60 in., vacuum annealed for 1 hr at 700°c, swaged to 0.40 in. and annealed at 700oC for 1 hr in vacuum. The grain size was checked and found to be 77 * 20 grains per sq mm. The specimens were then swaged to 0.187 in., yielding 76 ± 1 pet cold work. All alloys were then chemically analyzed for the solute addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The swaged rod was cut into 8.25 in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was maintained at 250" to 850°C over an eight inch length, recorded by twelve thermocouples. Control was ± 3oC, accomplished at the hot end. The recrystallization was determined metallo-graphically over the entire specimen. The criterion chosen was that point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be generally ± 3oC.

Jan 1, 1962