By L. T. Lloyd, H. H. Chiswik

The operative deformation elements in a-uranium single crystals under compression at room temperature have been determined as a function of the compression directions. The deformation mechanisms noted may be arranged with respect to their frequency of occurrence and ease of operation in the following order: 1 — (010)-[I001 slip, 2—{130} twinning, 3—{~172} twinning, and 4bunder special conditions of stress application, kinking, cross-slip, {.-176) twinning, and (011) slip. The composition planes of the (172) and (176) systems were found to be irrational. Cross-slip was shown to be associated with the major (010) slip system, coupled with localized interaction of slip on the (001) planes. The mechanism of kinking was found to be similar to that observed in other metals in that it occurred chiefly when the compression direction was, nearly parallel to the principal slip direction [loo] and was associated with a lattice rotation about an axis contained in the slip plane and normal to the slip direction: the [001] in the uranium lattice. The resolved critical shear stress for slip on the (010)-[100] system was found to be 0.34 kg per mm2 In a single test it was shown that under compression in suitable directions twinning on the (130) also occurs at 600°C. DEFORMATION mechanisms of large grained polycrystalline orthorhombic a-uranium have been studied by Cahn.1 A major slip system identified as the (010) with a probable [loo] slip direction and a minor slip system on the (110) planes were reported; the slip direction of the minor system was not determined. The twinning systems that were identified experimentally included the (130) and the irrational (172) composition planes; observations of other traces which were not as frequent and which did not lend themselves to positive experimental identification led Cahn to postulate on the basis of indirect evidence that twinning also occurred on (112) and (121) planes. In addition to the foregoing slip and twinning mechanisms, Cahn also observed kinking and cross-slip in conjunction with the major (010) system; the cooperative cross-slip plane was not identified. The availability of single crystals to the present authors has enabled them to check these results, particularly with reference to the doubtful mechanisms and the preference of operation of any one mechanism in relation to the direction of stress application. The tests were confined to compression only, primarily because of experimental limitations imposed by the size and shape of the available crystals. The tests were performed at room temperature except for one crystal compressed at 600°C. The compression directions were chosen to obtain a representative coverage of one quadrant of the stereo-graphic projection. To test the existence of some of the deformation elements that were reported by Cahn, but were not found in the present study, several additional crystals were compressed in specifically chosen directions considered most ideal for their operation. Experimental Techniques The single crystals were obtained by the grain coarsening technique described by Fisher? They grinding and polishing on rotating laps, with final surface preparation performed in a H3PO4-HNO3 electropolishing bath. A typical crystal readied for compression is shown in Fig. 1; their dimensions were rather small and depended upon the testing direction. Crystals isolated for compression in a direction close to the [010] axis, which lay roughly parallel to the longitudinal axis of the polycrystalline rod, were about 3 to 4 mm long and 5 mm2 in cross-section, while those prepared for compression in other directions were smaller. Most of the crystals were free from twin markings and showed no evidence of Laue asterism. Several crystals, however, contained twin traces prior to compression; these were identified prior to compression so as to clearly distinguish them from those initiated during deformation. The origin of the twin markings prior to deformation may be ascribed to two sources: thermal stresses and specimen handling during isolation and preparation. Two other types of imperfections in the crystals should be mentioned: inclusions, which were probably oxides or carbides. and three of the crystals contained a small number of spherical included grains (<0.01 mm diam), which were remnants of unabsorbed grains from the coarsening treatment. The volume represented by these imperfections was small, and their presence presented no difficulties in the interpretation of the macrodeformation processes during subsequent compression. Two compression fixtures were employed: crystals A, B, C, E, and G were compressed in a hand-operated screw-driven jig whose compression platens were designed to minimize axial rotation;

Jan 1, 1956

By G. K. Manning, A. R. Elsea, C. R. Simcoe

Boron increases the hardenability of hypoeutectoid steels by decreasing the nucleation rate of ferrite and bainite. It is postulated that concentrations of lattice imperfections, such as exist at the grain boundaries, furnish the necessary energy for nucleus formation. Boron, because of its atomic diameter, will concentrate at lattice imperfections where sites of suitable size are present. Boron will decrease the energy of these local areas by occupying these sites. This mechanism accounts for the large increase in hardenability observed with small amounts of boron. The loss of the boron hardenability effect and the boron precipitate formation are explained on the basis of increased concentration of boron at the grain boundaries either with increasing boron content of the material or with increasing temperature. COMMON alloying elements affect both the nucleation and growth rates of the austenite decomposition reactions.&apos; This effect is largely a result of the slow diffusion rates of these elements. Although a small addition of boron markedly increases the hardenability of steel, the diffusion rate of boron, which is of the same order of magnitude as that of carbon, can hardly account for this effect. An addition of boron in the range of 0.001 to 0.003 pct is about as effective as an addition of 0.30 pct Mo, 0.40 pct Cr, or 1.25 pct Ni in increasing the hardenability of a 0.40 pct C steel;&apos; however, increasing the carbon content of the steel decreases the effectiveness of the boron addition."&apos; The difficulty in understanding why so small an addition of boron can replace much larger quantities of the more strategic alloys, together with the erratic behavior sometimes encountered in boron-treated steels, has interfered with their general acceptance by industry. In the belief that an understanding of the mechanism by which boron increases the hardenability of steel should lead to a more general acceptance of boron-treated steels, a research investigation to determine this mechanism was undertaken at Battelle Memorial Institute under sponsorship of Wright Air Development Center. Experimental Work In order to study the effect of boron on the transformation of austenite to ferrite and bainite, a group of steels was made with a basic composition similar to that of the SAE 8600 series. This base composition was chosen because it has sufficient hardenability to permit accurate measurement of the times required for transformation to start at various temperatures. The chemical analyses of the steels used in the first part of this investigation are listed in Table I. These steels were made as 200 lb heats in an induction furnace. The furnace charge was Armco ingot iron with the alloying elements added as ferroalloys. After the alloy additions were made, the heat was deoxidized with 0.125 pct Al. A 100 lb ingot was cast and an addition of 0.003 pct B, as ferroboron, was made to the metal remaining in the furnace. This metal was cast into a second 100 lb ingot. The ingots were forged to 11/4 in. diam bar stock from which end-quench hardenability specimens were obtained. Part of this material was further reduced by hot rolling to lx¼ in. bar stock from which specimens were obtained for isothermal transformation studies. Studies of Nucleation and Growth: End-quench hardenability tests were performed on these steels, using an austenitizing temperature of 1600°F. The hardenability curves, shown in Fig. 1, indicate that boron treatment resulted in considerable increase in hardenability of the steels. Any such change in hardenability must result from a change in the transformation rate of the austenite, and these rate changes can be established readily by isothermal transformation studies. Isothermal transformation studies were conducted on these steels as follows: specimens were austeni-tized at 1600°F for 15 min, transferred to a lead bath operating at a constant subcritical or intercritical temperature, held for various lengths of time, and water quenched. The specimens were sectioned for metallographic examination to determine the amount and the type of transformation products present. In order to determine the effect of boron on the formation rate of ferrite, isothermal transformation tests were made on the 0.20 pct C steel in both the boron-treated and boron-free condition at an intercritical temperature of 1375°F where ferrite is the only decomposition product of this low carbon austenite. The results of these tests are shown in Fig. 2, where the percentage of ferrite formed is plotted as a function of time at temperature. It is apparent that boron markedly decreased the transformation rate of austenite to ferrite at this temperature.

Jan 1, 1956

By E. D. Gardner

FIFTY years ago the Utah Copper enterprise at Bingham was just getting under way. An epic in metal mining was in the making. Throughout the West the bonanza deposits were approaching exhaustion and most ore still went direct to smelter. But concentrators were shortly to be constructed for treating milling grade ores, and most important, the pilot plant for the Utah Copper enterprise was being built that year at the mouth of Bingham Canyon. The same decade was to see development at the Inspiration mine in Arizona of the most important new mining method for 50 years to come—undercut block caving. Although the average grade of ore being mined has been declining for 50 years, and wage rates and prices of supplies have been greatly increased, the mining industry has continued to grow and to prosper. Technology has advanced to a point where minerals can be mined under the most severe conditions. The hardest rock can be drilled and broken and the heaviest ground handled. Large or small, an ore-body can be mined successfully, at any desired rate of production. It is possible to pump great volumes of water and to ventilate the most extensive workings; air conditioning has made practicable the mining of ore where the rock temperatures are beyond those that can be borne by man. Mining today in the U. S. is a huge earth-moving operation. In 1953 nearly 2 billion tons of material were mined for direct use or for processing. Stripping at open-cut mines totaled about 1.7 billion cu yd. Table I gives relative tonnages of the branches of the mineral industry in 1953. In addition to the solid materials moved, 350 million tons of petroleum and 340,000 tons of gas were produced in 1953. Fifteen million tons of salt and 5 million tons of liquid sulphur were pumped from wells. An appreciable amount of copper was recovered by leaching old mine workings and dumps. Total value of minerals produced in 1953 was $14.4 billion: oil and gas $7.6 billion, coal $2.6 billion, nonmetallics $2.4 billion, and metals $1.8 billion. Formidable problems face some branches of the industry today, especially pertaining to increased output tons per manshift. The time has come when these problems should be reappraised. With current wage rates, the industry no longer can afford to pay men to do manual labor. It should be recognized, also, that the miner is a skilled worker; efforts to promote the dignity of his calling and his pride of accomplishment have yielded beneficial results. Mineral deposits occur under widely varying conditions. In most instances the degree of support needed by the roof and walls is the deciding factor in selection of an underground mining method. The degree of support needed, in turn, is governed by natural physical characteristics of the ore and its enclosing rocks. Mine operators, of course, learn to judge ground by observation, and an experienced mine boss generally can anticipate what will happen following any given mining operation. A more scientific approach, however, would be advantageous in most cases. More should be known about the strength of the ore and the enclosing rocks, more about stresses set up in the ground when ore is removed, and more about the mechanics of moving ground. Better understanding would work both ways: first, favorable rock conditions could be fully utilized for more efficient mining, and second, hazards of rock falls could be minimized, loss of ore in mining reduced, and expenses caused by ground pressures and subsidence lowered. In general, mining comprises breaking the ore or rock in place, supporting the mine workings, and transporting the ore to the surface. This latter is a materials handling problem. Ventilation, of course, must be provided, and the mines must be kept free of water. Development work at some places is the most important cost item in extracting ore. Drilling and blasting remain the usual practice for breaking ore or rock from place except, of course, at block-caving mines. The drilling and blasting practice at a mine must fit the mining method. In laying out mining procedures attention is being given to

Jan 1, 1956

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.&apos; This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.&apos;" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson&apos; as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, &apos;&apos;p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler&apos;s saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By J. A. Rowland

Magnesium alloys containing nickel, nickel and manganese, lithium, lithium and manganese, and lithium and aluminum were investigated. Melting, casting, and mechanical working techniques and the heat treatment of various compositions were studied. Amenability to cold and hot working was shown for many compositions. The magnesium-nickel and magnesium-nickel-manganese alloys failed to develop superior mechanical properties and were very low in resistance to corrosion. The magnesium-lithium series, although entirely plastic, had low strength properties. The addition of small amounts of aluminum to the Mg-Li base did not affect greatly either the ductility or the strength; further additions developed increased strength, but only at room temperature, and the alloys became brittle with age. Continued study, concentrating on the ductile lithium-rich beta phase as a base composition for ternary and quaternary systems, is recommended.

Jan 1, 1956

By G. A. Vissac

The only fine coal washer with proved automatic controls, the feldspar jig is capable of good efficiencies even at low separating gravities, handles a variety of products, and treats 150 tph and over. IN continental Europe the feldspar jig is used almost exclusively for cleaning the fine sizes of coal; it operates with an artificial bed, made up generally of pieces of feldspar or of any other hard and heavy rock with good cleavages. A primitive form of this machine requiring close supervision was used in this country years ago, but output was small. The modern machines are generally air-pulsated Baum-type jigs, with capacities up to 150 tph, and treat sizes from % in. to 0, usually previously dedusted or deslimed. These jigs are equipped with very accurate and sensitive automatic controls insuring satisfactory operation even at low separating gravity and with feeds irregular in quality and quantity. This paper will deal more particularly with coal cleaning separation, but the technical studies apply equally to all minerals. Theory of the Feldspar Jig To understand fully the operation of the feldspar jig and to appreciate its potential value, it is necessary to measure and analyze the motion of small particles of various specific gravities, falling in various media, under various conditions. As no practical formulas were available for that purpose, the writer has developed new theories and established new sets of formulas, which cannot be demonstrated here. They are applicable to all minerals and to many problems of coal or mineral concentration. These formulas do not pretend to absolute accuracy, but results, tested by comparison with experimentally recorded data, are sufficient for practical purposes, as they give definite indications of trends, relative values, and order of magnitude of the many factors involved. For pulsating motions no earlier formulas are available. In the case of continuous currents or motions, such formulas as Rittinger&apos;s, Allen&apos;s, or Stokes&apos;, over a hundred years old, apply only to special shapes and sizes of particles, involve factors and coefficients difficult to measure or appreciate, and deal only with free motions. They are of little use in solving practical problems. Units used with the formulas presented here are in the CGS system. Lateral friction and suction have been taken into account according- to methods currently used in aerodynamics, and only hindered motion is dealt with. As the feldspar jig is primarily intended to create a fluid bed condition, the mixture of fluids and solids obtained is homogeneous, and the apparent specific gravity of the separating medium is calculated accordingly. For instance, if 20 pct of the volume is coal and shale, with an average of 1.60 sp gr, in a liquid of 1.10 sp gr, the actual specific gravity of the separating fluid is 0.80 x 1.1 + 0.20 X 1.6 = 1.20. The fundamental equations are as follows: The general motion of a particle falling in a medium of specific gravity equal to u, hindered motion. is dv/dt = g/Ls [ L (s-u) - u/g v2 [1] g = 981 cm per sec, acceleration of gravity, and L = thickness of the particle of specific gravity (s) and velocity (v). The initial acceleration dv/dt = g (1-u/s ) [2] is a function of the specific gravity of the particle, only for a given medium, and independent of its dimensions—an ideal separating condition. The terminal velocity Vt = gxL- (s-u)/u, [3] for a given value of u, is a function of s and L. Two particles, L, s, and L2 s2, are said to be equivalent if they have the same terminal velocity, and accordingly L1/L2=s2-u/s1-u. [4] Two such particles cannot be separated by continuous currents, in any concentrating device. Because the initial accelerated motion, which provides for efficient separation, is followed by a constant velocity, which has a limiting effect, it is essen-

Jan 1, 1956

By R. Webeler

In order to study the role of work hardening in the fatigue process, use was made of the great sensitivty of the resistivity of AuCu to cold work. A change of the resistivity of AuCu of the order of 1 to 2 pct at the temperature of liquid nitrogen was found to occur as a consequence of severe fatigue. ACCORDING to Orowan&apos;s theory,&apos; the process of fatigue In metals 1s associated with the production of a number of small regions which have undergone strain hardening. This phenomenon is supposed to occilr even if the stress applied during fatiguing is always smaller than the yield stress. In an attempt to verity the existence of such regions, Welber and Webeler&apos; undertook to detect the stored energy associated with severe fatigue in copper. Previous experiments" had shown that the energy stored in a sample of copper which has been cold worked by torsion is released in the temperature range between 150" and 250°C when the sample is heated from room temperature and that no more energy is released (or absorbed) between 250" and 450°C. In particular the stored energy amounted to 0.41 cal per g for a case in which the mechanical energy expended in twisting the sample was 11.9 cal per g. In the case of fatigued copper, however, no release of stored energy could be detected between 150" and 250°C, so that the experimental error of &0.02 cal per g represents an upper limit for the amount of energy stored in strain hardening., It seemed desirable to attack the problem in a new fashion. For this purpose, it was decided to make use of the fact that, if an alloy capable of undergoing the order-disorder transition is ordered and then cold worked, the resistivity, p, increases very greatly above the value for the ordered state even if the deformation is very small. Some insight into the nature of the fatigue process may be obtained then by measuring the resistivity of an ordered sample before and after subjecting it to fatigue. For reasons which will become apparent from the following remarks, considerably more can be learned by carrying out the resistivity measurements at two different temperatures. In the case of a material containing impurities, vacancies, dislocations, or other imperfections of essentially atomic dimensions, the resistivity, p, according to Matthiessen&apos;s rule, can be represented as a sum of two terms p = p, + p, where p, is the (temperature dependent) resistivity of the pure metal, and p, is the temperature independent contribution of the imperfections. Briefly, the physical basis for this rule is the following: The main contribution of the impurities in question to the resistivity results from the fact that they interrupt the periodicity of the lattice and thus scatter the conduction electrons with a probability which is almost independent of temperature. In order that this be the case, it is necessary that the&apos; extension of the impurities be small enough—roughly less than one electron mean free path—so that their main effect on the resistivity occurs for the foregoing reason. If an alloy like AuCu is partly or completely disordered by quenching from an appropriate temperature, Matthiessen&apos;s rule also applies to a very good approximation* with p, representing in this case the resistivity po of the ordered sample and p, the additional (temperature independent) resistivity due to the disorder. In general, the disorder can be represented in terms of atoms which are displaced from their "proper" positions in the superlattice and which thus qualitatively represent the imperfections in the superlattice responsible for the term p,. Since the misplaced atoms are distributed at random throughout the super-lattice, their contribution to the resistivity still can be considered in terms of the scattering of conduction electrons by lattice defects. The situation is somewhat more complex in the case of an alloy disordered by cold work because the process of disordering here does not involve a random redistribution of the atoms; however, Matthiessen&apos;s rule also holds in this case. Whenever Matthiessen&apos;s rule does apply, the values of the quantity /3 = (p? — /(T, — T,), where p, and p, are the values of the resistivity at two fixed temperatures, T, and T,, respectively, is constant (independent of p,) for a given alloy or metal. In particular, if a sample of AuCu is subjected to ordinary cold work, the value of /3 remains equal to Po, the value for the ordered material. According to Orowan&apos;s theory,&apos; as remarked before, a fatigued sample contains a large number of isolated severely cold-worked regions, which make up only a small proportion of the metal. Thus, if a sample of AuCu initially in the ordered state is fatigued, more or less disordered regions will be produced within the ordered material. If these regions are small enough so that Matthiessen&apos;s rule applies, then it follows from the previous discussion that /3 again will remain equal to Po. If the effect of fatigue is to produce cold-worked regions which are macroscopic—of the order of at least several electron mean free paths—the effective resistivity, p, has to be computed by use of the ordinary laws of large-scale electrodynamics. For the sake of simplicity, it will be assumed here that the cold-worked regions are completely disordered and have a resistivity, p,. For a given proportion A of disordered regions the effective resistivity, p, for the current in a given direction depends on the geometrical configuration of these regions. In any case, the value of p for such

Jan 1, 1956

By P. E. Cavanagh

FOR THE PAST seven years Mr. W. Simpson, Chief Mechanical Inspector for the Nova Scotia Department of Mines, has carried out exhaustive field trials of non-destructive inspection equipment in the coal mines of that Province. This work has demonstrated the usefulness of a number of types of non-destructive inspection when used for periodic inspection of hoisting and haulage equipment in the coal mines of Nova Scotia. As a result, the Dominion Coal Company has instituted a programme of regular preventive maintenance inspection ?by a special staff of qualified and trained men. The purpose of this present paper is to describe how non-destructive testing techniques are used on ropes, axles, couplings, and other hoisting and haulage equipment, how these methods are being used in other industries, and the expected benefits from intelligent and properly organized use of these techniques in the coal mining industry.

Jan 1, 1956

By A. Spilners, M. Simnad

The rates of formation of the different oxides on molybdenum in pure oxygen at 1 atm pressure have been determined in the temperature range 500° to 770°C. The rate of vaporization of MOO, is linear with time, and the energy of activation for its vaporization is 53,000 cal per mol below 650°C and 89,600 cal per mol at temperatures above 650°C. The ratio Mo03(vapor.lzing)/MoOS3(suriace) increases in a complicated manner with time and temperature. There is a maximum in the total rate of oxidation at 6W°C. At temperatures below 600°C, an activation energy of 48,900 cal per mol for the formation of total MOO, on molybdenum has been evaluated. The suboxide Moo2 does not increase beyond a very small critical thickness. At temperatures above 725°C, catastrophic oxidation of an autocatalytic nature was encountered. Pronounced pitting of the metal was found to occur in the temperature range 550° to 650°C. Marker movement experiments indicate that the oxides on molybdenum grow almost entirely by diffusion of oxygen anions. USEFUL life of molybdenum in air at elevated temperatures is limited by the unprotective nature of its oxide which begins to volatilize at moderate temperatures. Although the oxide/metal volume ratio is greater than one, the protective nature of the oxide film is very limited. Gulbransen and Hickman&apos; have shown, by means of electron diffraction studies, that the oxides formed during the oxidation of molybdenum are MOO, and MOO,. The dioxide is the one present next to the metal surface and the trioxide is formed by the oxidation of the dioxide. Molybdenum dioxide is a brownish-black oxide which can be reduced by hydrogen at about 500°C. Molybdenum trioxide has a colorless transparent rhombic crystal structure when sublimed, but on the metal surface it has a yellowish-white fibrous structure. It is reported to be volatile at temperatures above 500" and melts at 795°C. It is soluble in ammonia, which does not affect the dioxide or the metal. In his extensive and classic investigations of the oxidation of metals, Gulbransen2 has studied the formation of thin oxide films on molybdenum in the temperature range 250" to 523°C. These experiments were carried out in a vacuum microbalance, and the effect of pressure (in the range 10-6 yo 76 mm Hg), surface preparation, concentration of inert gas in the lattice, cycling procedures in temperature, and vacuum effect were studied. The oxidation was found to follow the parabolic law from 250" to 450°C and deviations started to occur at 450 °C. The rates of evaporation of a thick oxide film were also studied at temperatures of 474" to 523°C. In vacua of the order of 10- km Hg and at elevated temperatures, an oxidation process was observed, since the oxide that formed at these low pressures consisted of MOO, which has a protective action to further reaction in vacua at temperatures up to 1000°C. Electron diffraction studies showed that, as the film thickened in the low temperature range, MOO8 became predominant on the surface. Above 400°C MOO, was no longer observed, MOO, being the only oxide detected. The failure to detect MOO, on the surface of the film formed at the higher temperatures does not militate against the formation of this oxide, since according to free energy data MOO3, is stable up to much higher temperatures. At the low pressures employed, this oxide would volatilize off as soon as it was formed. Its vapor pressure is relatively high and is given by the equations" log p(mm iig) = -16,140 T-1 -5.53 log T + 30.69 (25°C—melting point) log p(mm He) = -14,560 T-1 -7.04 log T+1 + 34.07 (melting-boiling point). Lustman4 has reported some results on the scaling of molybdenum in air which indicate a discontinuity at the melting point of MOO, (795°C). Above the melting point of MOO,, oxidation is accompanied by loss of weight, since the oxide formed flows off the surface as soon as it is formed.5,6 Qathenau and Meijering7 point out that the eutectic MOO2-MOO3 melts at 778C, and they ascribe the catastrophic oxidation of alloys of high molybdenum content to the formation of low melting point eutectics of MOO3 with the oxides of the melts present. Fontana and Leslie -explain the same phenomenon in terms of the volatility of MOO,, which leads to the formation of a porous scale. Recent unpublished work by Speiser9 n the oxidation of molybdenum in air at temperatures between 480" and 960°C shows that the rate of weight change of molybdenum is controlled by the relationship between the rates of formation and evaporation of MOO,. They have measured the rates of evaporation of Moo3 in air at different temperatures and estimated an activation energy of 46,900 cal. This compares with the value of 50,800 cal per mol obtained by Gulbransen for the rate of sublimation of MOO, into a vacuum.

Jan 1, 1956

P. L. Pratt (University of Birmingham, Birmingham, England)—The author has measured the hardening effect of isolated edge and screw dislocation boundaries in a remarkably elegant manner, and he proposes that the detailed structure of the boundary determines its effectiveness as a barrier to slip although "there are still unknown details of the distribution which may be extremely important." On p. 678 the author states "that for a good crystal (one having a yield of about 30 psi) a change in annealing temperature from 300" to 400 °C resulted in a negligible shift in the level of the stress-strain curve." Is this in agreement with the results of the earlier paper by Li, Washburn, and Parker8 in which such a change of temperature produced notable hardening in crystals with a yield of about 30 psi? Or were these earlier crystals, of the same nominal purity, less perfect than those used in this work? The experiment illustrated in Fig. 15, p. 681, shows that the boundary has sharpened after annealing at 400 °C, the temperature at which the hardening effect first becomes apparent. Did the author verify that no sharpening of the boundary occurred at, say, 300 °C where no hardening was found? This would seem to be an important check on the proposed mechanism, especially since zinc of this purity should polygonize at temperatures well below 400 °C within the annealing times used here. There seem to be at least two alternative explanations which could fit these facts: 1—The boundary may sharpen at 300 °C or even lower temperatures but be unable to contribute greatly to the hardening until jogged by thermal vacancies and other impurity atoms after 400 °C anneal. This mechan- ism, discussed in the earlier paper,&apos; is believed to account for the thermal hardening observed by Blank&apos;" in NaCl, as stated elsewhere: and by results from recent experiments which tend to confirm this view. 2—The dislocations in the diffuse boundary may be locked by impurity atoms at 300 °C and thus only sharpen the boundary at 400 °C with the aid of thermal vacancies. In this case it would be difficult to distinguish between the two sources of hardening (sharpening or jogging), using metal of this purity. Jack Washburn (author&apos;s reply)—The author wishes to thank Dr. Pratt for his discussion. In connection with his first comment, it should be pointed out that the temperature of testing in the present series of experiments was —196°C, whereas, in the earlier experiments he referred to,&apos; it was 20°C. Therefore, the yield values should not be directly compared. It is likely that the crystals used in the present work were initially more perfect macroscopically than the large shear specimens used previously. The small size of the test section in the kink specimens made it possible to select regions of the large crystals, from which they were acid-cut, that were free of observable small angle boundaries. The sharpening of a microscopically diffuse boundary such as that in Fig. 15 begins in zinc of this purity well below 300°C. However, it is probably not justified to conclude that because a boundary looks sharp under the microscope it has attained the ideal structure. The author agrees with Dr. Pratt that jogging of dislocation lines is one of the structural features of a small angle boundary that should be important in determining its strengthening effect. More detailed information concerning the changes in boundary structure as a

Jan 1, 1956

By C. E. Armantrout, J. A. Rowland, D. F. Walsh

THE close-packed-hexagonal structure of mag-J- nesium is converted to a ductile and malleable body-centered-cubic lattice by the addition of lithium in excess of 10 pct. Further, the density of magnesium or magnesium-base alloys is decreased by additions of lithium. The practical possibilities of such alloys as a basis for uniquely light, malleable, and ductile structural materials were pointed out by Dean in 1944&apos; and by Hume-Rothery in 1945.2 It was apparent to these investigators, however, that more complex compositions would be required if strengths sufficient for structural applications were to be developed in these alloys. In a search for strengthening additions, various investigators w have examined a number of the ternary and more complex alloys containing magnesium and lithium. An investigation of the fundamental characteristics of these alloys was undertaken by the Bureau of Mines. The investigation was initiated with a study of the magnesium-rich corner of the equilibrium diagram for the ternary system, Mg-Li-Al. The following data from published investigations of Mg-Li-A1 alloys were available: 1—a description of isothermal sections at 20" and 400°C through the Mg-Li-A1 constitution diagram by F. I. Shamrai;&apos; 2—a diagram by P. D. Frost et al." showing approximate phase relationships at 700°F for a number of the Mg-Li-A1 alloys; and 3—diagrams showing the constitution at 500" and 700°F for the Mg-Li-A1 alloy system published by A. Jones et al.&apos; Where compositions and temperatures permit comparison, these diagrams show disagreement. The 700°F isotherms of Frost and Jones differ only in the placement of the phase boundaries. But Sham-rai&apos;s 400°C (752°F) isotherm shows a variation in phases as well as in phase boundaries. Although rigid comparison of these different isothermal sections might not be justifiable, it seems impossible to reconcile Shamrai&apos;s construction with the isotherms of Frost or Jones. The isothermal sections presented in this paper were prepared to determine compositions which might be suitable for age hardening and to develop the general slope and placement of the various phase boundaries in the magnesium-rich corner of the diagram. Sections at 375", 200°, and 100°C were selected for investigation. In constructing these sections, the solubility of aluminum in magnesium, as reported by W. L. Fink and L. A. Willey Vn 1948, was used at the binary Mg-A1 boundary and the solubility of lithium in magnesium was obtained from the equilibrium diagram for that system as reported by G. F. Sager and B. J. Nelson" in the same year. The solubility of magnesium in lithium was determined experimentally and conforms in general to data reported by P. Saldau and F. Shamrai." Parameters for AlLi and MgI7A1, were taken from American Society for Testing Materials X-ray diffraction data cards. Experimental Procedures Although the isothermal sections presented in this paper are not unusually complex, the experimental techniques involved in their construction are made extremely difficult by the relatively high vapor pressure of lithium and the great chemical activity of both magnesium and lithium. Because of these characteristics, which make precise control of the composition of equilibrium-treated filings practically impossible, the disappearing phase method was used in preference to the parametric method in conjunction with metallographic studies. The alloys used in this investigation were melted and cast in an atmosphere of helium using a tilting-type furnace which enclosed a steel crucible and mold in a single unit. Each portion of the charge (500 to 600 g) was cleaned carefully just before placing it in the crucible; and the charge, crucible, and entire melting apparatus were evacuated and then washed with grade A helium while preheating to approximately 100°C. The alloys were melted and chill cast in an atmosphere of helium. Alloys prepared in this way were relatively free from inclusions and a fluxing treatment was considered unnecessary. The cylindrical ingots obtained were scalped and then reduced 96 pct in area by direct extrusion, yielding % in. diam rod. Sections of the rod, approximately 3 in. long, were given equilibrium heat treatments and then sampled for metallographic examination, X-ray diffraction study, and chemical analysis. The surface of each equilibrium-treated rod was machined to a depth sufficient to insure removal of contaminated material before samples for chemical analysis or X-ray diffraction study were obtained, and all decisions on microstructure were based on the examination of the central portion of the metallographic specimen. All specimens homogenized at 375°C were analyzed after this equilibrium heat treatment. When the composition of an alloy placed it in a critical area of the 200" or 100°C isothermal section, a check chemical analysis was made on a sample taken from the alloy specimen as-heat-treated at the particular temperature. Standard chemical procedures of gravimetric analysis were used in the determination of magnesium and aluminum; lithium, potassium, and sodium were determined by flame photometer methods

Jan 1, 1956

By K. B. Higbie

The quantitative separation of tantalum from columbium has been obtained through several liquid-liquid extraction processes. The valuable metals are separated by selective extraction from organic feed solution using a mineral acid or by selective extraction from aqueous feed solutions employing an organic solvent. The greatest degree of separation was obtained when organic ketones, particularly methyl isobutyl ketone, were used. Approximately 200 combinations of various organic solvents and mineral acids were tested as possible separation systems in which the tantalum or columbium content was extracted from organic solutions of the anhydrous pentachlorides.

Jan 1, 1956

By F. W. Wessel

This report summarizes Bureau of Mines laboratory tests of four tungsten¬-bearing materials of various grades, The test work has demonstrated that the dry reaction between sodium carbonate and scheelite is best conducted at 900° C. or a few degrees less. The sodium carbonate requirement, in addition to the stoichiometric equivalent of the scheelite, is in some inverse relationship to the grade of tungsten in the ore. Residence time and particle size exert a definite but minor control on the reaction. Pressure-digestion tests on an impure concentrate indicate the technical feasibility of extraction by this process. INTRDUCTION Over 100 years ago Oxland discovered that tungstic oxide could be removed from wolframite and converted to a soluble form by reacting the mineral with a soluble alkaline salt at elevated temperatures. He patented this discovery, and this patent 4/ since has been the basis for most tungsten extraction. Much literature exists on this process and its modifications, and the characteristics and possibilities of the reaction are quite well defined.

Jan 1, 1956

It has been established that molybdenum sesquisulphide, not molybdenite, is in equilibrium with molybdenum metal and sulphur vapor in the vicinity of 1100°C. The S2 pressure for this system has been obtained using the Knudsen orifice method and the standard free energy for the dissociation of S2. THIS work was undertaken to help in determining the thermodynamic properties of the molybdenum sulphide which is in equilibrium with metallic molybdenum and sulphur vapor in the temperature range 1025" to 1150°C. From the results of MontoroL and of Parravano and Malquori&apos; molybdenite would be expected to be in equilibrium with molybdenum metal, while the results of Guichard indicate that a lower sulphide must be in equilibrium with the metal. Thus it was concluded that the problem warranted reconsideration, especially in view of the suspiciously low temperature independent term for the standard free-energy function for the reaction MoS² Mo + S,. The reaction was calculated and duly noted as being low by Richardson and Jeffes,&apos; using the data of Parravano and Malquori.&apos; Experimental Method The general method used in this investigation is that of the Knudsen orifice method for the determination of equilibrium pressure. The apparatus and technique are similar to those described for the determination of the vapor pressure of silver.% owever, a closed-end McDanel tube instead of fused silica was used to maintain the vacuum, a molybdenum effusion cell with a replaceable lid was employed instead of a silica cell, and a titanium getter maintained at run temperature was used to assure that no oxidation of the molybdenum or molybdenum sulphide was taking place. All runs were made at a residual pressure less than 10-5 mm Hg. The data are given in Table I. Runs 1 through 13 were obtained using molybdenite, analyzed 98.5 pct, from the Molybdenum Corp. of America. The remaining runs were done with a sample from the Climax Molybdenum Corp. which was their grade No. 3 and analyzed 59.87 pct Mo. The weight loss of the cell during heating up and cooling down was subtracted from the total weight loss of the cell during the run. Also, when the tem- perature was changed, the Knudsen cell was placed in the vacuum chamber and heated at temperature for several hours in order to allow the sulphide and the metal to adjust their compositions to the equilibrium values, to desorb or adsorb gases into or from the molybdenum cell itself, and to desorb any water from the molybdenum sulphide or molybdenum powder inside the cell. Water may have been adsorbed inside the cell because, after each run, the top of the cell was removed and the material in the cell was stirred to insure that a layer of molybdenum metal would not build up and obstruct the passage of sulphur vapor into the gas phase. It was established that the molybdenum cell alone decreased in weight an inappreciable amount when heated at the highest run temperature for long periods of time. There are two questions to be answered before the data in Table I can be used to calculate thermodynamic functions: 1—Which molybdenum sulphide is in equilibrium with molybdenum metal and sulphur vapor? 2—What sulphur species are present in the vapor phase? It can be assumed safely that no molybdenum is vaporized, since its vapor pressure is almost negligible at these temperatures. It will be shown subsequently that no sulphide of molybdenum is volatile. Question 1 was answered in the following way: The especially purified molybdenite, obtained from the suppliers mentioned previously, was charged

Jan 1, 1956

By H. Kenworthy

[Experimental studies were made to develop a laboratory technique for direct removal of cadmium and germanium from sphalerite concentrates. Cadmium- and germanium-bearing concentrates from the Illinois-Kentucky fluorspar field were sound to be, amenable to an inert atmosphere fuming process for removing these two moats in the form of gaseous sulfides. Treating the condensed fume by pyrometallurgical methods upgraded the material end provided a means of partly separating the constituents. Cadmium was concentrated about 35:1 arid germanium about 300:1. The extractive investigations were supplemented by vapor-pressure studies on the sulfides of germanium to obtain fundamental data for larger scale laboratory conditioning and control when treating the zinc concentrates. Vapor-pressure curves were developed for synthesized monosulfide and disulfide The results of these- investigations indicate the possibility of significantly increasing the recovery of cadmium from zinc concentrates. Comparison with present recovery of germanium cannot be made, since commercial recovery data arc not available.]

Jan 1, 1956

By A. L. Engel

Production of chromite in California has been from many small, high-grade mines. The opening of the Purchase Depot at Grants Pass, Oreg., in 1951 has stimulated chromite mining in California, and a large number of properties are being reexamined as there is a possibility that some low-grade ores from many of these properties can be beneficiated to meet the purchasing schedule. The Bureau of Mines in its program of conservation is continuing ore-dressing tests on chromite ores to better evaluate their potential. This report is a compilation of preliminary concentration tests on samples from five different properties in California. The concentration tests were made on ores from the David mine, Butte County, the Seiad Creek mine, Siskiyou County, the High Plateau mine, Del Norte County, Bud&apos;s mine, Tuolumne County, and tailings from the Miller concentration plant in San Luis Obispo County, Calif., to determine the possibility of beneficiating these ores so that they will meet the specifications for the Government stockpile.

Jan 1, 1956

By W. L. Dare

This information circular is one of a series the Bureau of Mines plans to publish describing the methods and costs of mining uranium on the Colorado Plateau. The Big Buck mine is one of the larger underground uranium-vanadium ore mines on the plateau. The mine is about 39 miles southeast of Moab in the Big Indian mining district, San Juan County, Utah. The Big Buck claims were located late in 1947, when uranium mineralization was discovered in the Cutler formation at its outcrop along the escarpment that forms the west side of Big Indian Wash. Charles A. Steen made the first major discovery of uranium ore in the Chinle formation in the Big Indian mining district on July 6, 1952, when 14 feet of high-grade uranium ore was encountered in a diamond-drill hole drilled on his Mi Vida claim. The Big Buck ore body now being mined by Standard Uranium Corp. is a southeast extension of Steen&apos;s original discovery.

Jan 1, 1956

By T. E. Evans, C. T. Baroch

ZrB2 was produced in batches of 4 to 6 Ib by interaction of ZrO2, B4C, B203, and carbon at around 2000°C in a simple graphite resistance furnace. Techniques of production are discussed and the final design of a suitable furnace is described in detail. Several other borides were made by the same technique and the process appears to have possibilities for commercial production. N seeking out new hard and refractory com- pounds, many researchers have turned to the investigation of the borides and excellent papers have been published on the properties of these compounds. Few papers, however, have appeared on the techniques and problems concerned with the production of these high temperature substances. This report describes progress made in developing a method for preparing zirconium diboride, ZrB2, on a pilot plant scale. The literature of the borides and other refractory hard metals recently has been reviewed, annotated, and classified so completely&apos; that it is needless to attempt such an outline here. It is enough to say that three borides of zirconium have been reported: ZrB, ZrB2, and ZrB12.2 ZrB2 is the most stable of these and is especially stable in the presence of carbon up to and including its melting point of around 3000°C. Like most borides, it can be prepared in several ways. It can be prepared by synthesis of the elements, but these are expensive and difficult to produce in a high state of purity. Obviously, production directly from the oxides would have decided economic advantages. In electrolytic production such as that of calcium boride,:&apos; the product is recovered as a sludge mixed with electrolyte; and separation of product from adhering electrolyte and regeneration of the electrolyte is an involved and difficult process. The work on borides was started on a small scale in 1948. Late in 1949, Naval Ordnance expressed a specific interest in ZrB2 and the project then centered on this compound. After the usual experimental work necessary in a new field, ZrB2 of good quality was produced by heating mixtures of B4C, ZrO2, B2O3, and carbon to a temperature of about 2000 °C in a resistance-type electric furnace. Over 100 lb was made for experimental use tests, and the method of production probably could be expanded into a commercial operation. A similar process has been described by Kieffer and coworkers.&apos; The main chemical problems were the development of proper charges to insure complete reduction of the elements, determination of the proper temperature range at which these reductions took place, and adoption of techniques necessary to pre- vent inclusion of such impurities as carbon and nitrides. The mechanical problems consisted of developing a simple practical furnace that would attain the high temperatures required and permit use of a controlled atmosphere when necessary and determining of suitable refractories. Both problems were solved by designing a crucible resistance furnace. Crucible Resistance Electric Furnace Attempts were first made to produce ZrB2 in an electric arc furnace, but such a furnace would not provide the degree of carbon control required for producing clean graphite-free borides, so it was decided to try working in a crucible. Obviously, the furnace would have to be constructed of graphite, as the temperatures required are too high for other refractories or heating elements. Crucibles were made by hollowing out segments of graphite electrodes, which were fitted with a cover and clamped between two electrodes so that the current passing through the thin wall of the crucible would generate heat, using the principle of the Helberger crucible furnace."? Preliminary tests with this type of furnace were encouraging and led to the furnace design shown in Fig. 1. The essential components were a thin-walled graphite crucible resting on a graphite block, which formed the lower electrode assembly, and a top electrode assembly swung from a pipe column making contact with the top of the crucible. The space around the crucible was filled with graphite prepared from waste electrodes crushed to about ¼ in. This packing had excellent insulating properties, both electrically and thermally, and could be removed easily and quickly from around the crucible by means of an industrial vacuum cleaner. The largest resistor crucibles were machined from 8 in. electrode stock and were 26 in. long, with a side wall Yi in. thick and a 1 in. bottom. Temperatures were determined optically by sighting down a 1 in. hole drilled longitudinally through the top electrode and the crucible cover. Sealing this hole at the top was a water-cooled brass sight-glass assembly, shown in Fig. 2. An opening was provided for a light flow of helium to keep the sight opening clear of smoke, and a glass prism above the sight glass changed the line of sight to the horizontal for easier reading. More recently, the prism and optical pyrometer were replaced by a photoelectric recording pyrometer. At first the charges were placed directly in the resistor crucible but this meant that everything had to be withdrawn from the furnace every time the charge was emptied. Later, smaller crucibles were made up that could be placed inside the resistor

Jan 1, 1956

By R. H. Nielsen

A new, cheaper precipitation scheme has been developed to produce purified zirconium oxide, Technical-grade sulfuric acid is used to precipitate a basic zirconium sulfate from a hot dilute hydrochloric acid solution. With close control of temperature, pH, and zirconium - sulfate ratio, excellent purification and complete zirconium recovery can be attained. The process has been successfully applied for 3 months and has proved to be a more satisfactory procedure than the ammonium phthalate process used previously. INTRODUCTION The Northwest Electrodevelopment Laboratory of the Federal Bureau of Mines has developed and improved the Kroll process for the production of pure ductile zirconium and hafnium. metal. Since 1946 over 1 million pounds of zirconium sponge metal has been produced, mostly high-purity material for the Atomic Energy Commission

Jan 1, 1956

By Howard L. Hartman, Eugene P. Pfleider

The paper relates to the laboratory and pilot plant studies that have been carried out by Sherritt Gordon Mines Ltd., Metallurgical Research Div., in developing the ammonia pressure leach process for extracting Cu, Ni, Co, and S from high grade Ni concentrate produced from Lynn Lake ores and describes in some detail the chemistry of the process. In the leaching stage air, ammonia, and sulphide minerals react in a sequence of inter-related steps to produce soluble amines of Ni, Cu, and Co in a solution containing sulphate, thiosulphate, polythionate, and sulphamate ions and a controlled amount of free ammonia, the iron and other components of the concentrate remaining as an insoluble residue which is separated from the leach solution by filtration. The pregnant solution produced in leaching is further treated by boiling to precipitate and remove Cu as cuprous sulphide, leaving a copper-free solution with a composition suitable fir subsequent precipitation of Ni and Cu by H,. The progress of individual reactions in leaching and copper removal is discussed. The effect of variables such as temperature, pressure, ammonia concentration, particle size, and agitation is outlined and the technique of thionate control in leach solutions is described. Data is given for the physical and chemical reactions involved in precipitating copper from leach solutions as Cu sulphide by boiling.

Jan 1, 1956