Search Documents

By Frank G. Schwartz

VARIABLES OF composition and environment affecting storage stability of gasoline-type fuels were studied, utilizing radioactive tracers and other analytical techniques. Changes in gasoline composition brought about by aging were determined and correlated with gum formation. The amounts of reaction of selected gasoline components, measured by radioactive tracers, were determined in a gasoline-type blend and in a mixture of 17 selected pure gasoline components. The data show that sulfur compounds, nitrogen compounds, polycyclics, and olefins enter into gum-forming reactions. Certain sulfur and nitrogen compounds were found to be most reactive in the gum-forming process. Results of this study indicate that the aromatic constituents of gasolines may contribute substantially and directly to gum formation. A mixture of tetralin and indan-type compounds is reactive, and this mixture appears to be the main aromatic portion entering into gum formation. A secondary but significant amount of naphthalenes also appears to have reacted in the gum-forming process. Analyses of the sulfm compounds in a fresh and an aged fuel indicated that elemental sulfur, hydrogen sulfide, thiols, sulfides, and disulfides were depleted during aging, but thiophenes and residual sulfur compounds were not depleted by fuel deterioration.

Jan 1, 1964

By Forrest T. Moyer

The National Safety Competition was inaugurated in 1925 by the Bureau o1 Mines, U.S. Department of the Interior, in cooperation With the Explosives Engineer. In the first nationwide contest, 210 mines and quarries were enrolled. In 1962, the thirty-eighth anniversary of the competition, 910 mines and quarries were enrolled. These participating plants were worked a total of 133,292,989 man-hours. Of the enrolled plants, 415 achieved injury-free operations tar the year, the largest number of perfect safety records in the history of the contest. In 1961 and 1962, the National Safety Competition was conducted and sponsored by the Bureau of Mines. In January 1963, the American Mining Congress became a cosponsor and participated with the Bureau in the award activities related to the 1962 contest. The basic purpose of the competition is to stimulate employees to work safely and too give impetus to the building of better accident-prevention programs. A well-designed and efficient safety program helps a company economically by cutting costs, preventing damage to equipment and materials, and reducing nonproductive delays. An effective safety program benefits the employee more directly because his injuries cause personal suffering, lost time, and lower living standards for his family. Since both have much to gain, management and workers should cooperate closely to eliminate disabling work injuries. The greater contest participation and the larger number of perfect safety records indicate increasing safety consciousness on the part of management and employees.

Jan 1, 1964

1. Scientific prospecting has had a profound and some-what unexpected effect on the world's supply of raw materials over the past twenty years. Where shortages were recently anticipated, abundance now prevails. It seems probable that, for the foreseeable future, adequate metallic resources will be found at costs well within the world's economic means. 2. The amount of research devoted to scientific prospecting has been extremely small in relation to the possible importance of the problem and to what could be done. It has been dominated by the thought of a dozen brilliant men, and true research expenditures have not amounted to more than a few million dollars. 3. An undue proportion of the expenditures have been for so-called geological research -mostly of a petrologial character. The results have essentially been of historic interest only. However, there has been some in-crease in genetic understanding, and this is of great importance for future resources. 4. Basic advances in mineral exploration have been made in detection techniques, generally called geophysics and geochemistry.

Jan 1, 1964

A semi-automatic device has been constructed that can be used to check the solution strength of cyanide solutions. It consists of a wheel on which a gold-foil-bearing glass slide is mounted. The wheel moves the gold foil through the solution under test and intercepts a light beam. As the gold foil is attacked by the cyanide solution its light absorption diminishes. The successive in-crease in transmitted light intensity is recorded and gives a measure of the gold dissolution rate. Curves have been obtained to show the effect of cyanide concentration and oxygen content on dissolution rates. Details are presented of the construction of the unit, and some practical operating procedures are outlined. 0 NE of the important, although often neglected, factors in the extraction of gold by cyanidation is the actual dissolving strength of the cyanide solution. This depends in a

Jan 1, 1964

The methods employed for the addition of uranium to steels and cast iron in the Physical Metallurgy Division are outlined. It has been found that the segregation of? uranium is a major problem in aluminum and/or silicon killed steels and that the cooling rate is important in al-lowing the segregate to settle to one area, which can subsequently be discarded. The unsegregated areas were found to be extremely low in total oxygen, acid insoluble aluminum (AizOg) and, in some cases, slightly lower in nitrogen. Uranium recoveries, based on analyses of the unsegregated areas, were quite constant, at about 45 per cent, regardless of the type of uranium master alloy used for the addition. No segregation of carbon, manganese, silicon, sulphur, phosphorous, chromium or copper was observed in these steels. In commercial heats, the recoveries ranged from 7 to? 29 per cent for ladle additions to oxygen converted steel. When the steel was fully deoxidized prior to the uranium addition, recoveries ranged from 49 to 66 per cent, regardless of the steelmaking process.

Jan 1, 1964

By L. D. Clark, S. S. Saluja

A physical law, governing the rupture of rock by confined explosive charge correspondent to current expressions for determining weight of charge to rupture rock burden, W, was developed in the form Q = cVw3 by two early investigators performing unique experiments with ice. The coefficient C, is found by trial blast. Recent physical tests conducted with rock, synthetic materials and ice to establish the validity of the theory on which it and other related formulae are based indicated: (a) that failure under hydrodynamic impact pressure is by tension rather than shear as was assumed; (b) that the fundamental law of mechanics, enabling the determination of Q = cvw3, modified to the form P = R x Sa x Wb is valid when low velocity explosives are used; (c) that rock breakage under the action of low velocity explosives is entirely due to explosion gas pressure, as was believed; (d) that under the action of high velocity explosive it is due to the joint effects of scabbing and gas pressure; and that further possible modification could make the above equation also applicable to these joint mechanisms. shape could be easily frozen and because large loads would not be required. They found: (a) that the not unfamiliar shearing equation for metals was applicable to ice where P = load in lb; S = periphery of pressure surface, in.; W = burden, in.; K = modulus of rupture by shear in lb per in.2; and (b) that "the form of cavity produced by the application of gradual pressure is similar to that obtained by blasting in rock under similar conditions of free face and pressure surface!" This similarity in crater shapes leads to the conclusion that rock would rupture by shear, as did ice, and its behavior under the force of a blast could be governed by such a relationship as P = S x W x K. Three important interrelated empirical expressions were derived and rock, charging and spacing coefficients C,, C, and e were established and substantiated by trial blasts. In checking the accuracy of the main assumptions, duplication of the ice tests, substituting rock, suggested that K is not constant and that P = K x W x S, though valid for ice, does not necessarily hold for homogeneous limestone.' Conclusions from this later work raised questions making continued investigation desirable because such conclusions do not destroy the practical value of the empirical equations or theory. Further study for the establishment of the relationship between load, burden and periphery of the pressure surface and possible application of these to the mechanism of rock blasting was undertaken by the authors of this paper. MECHANICAL TESTING - EXPERIMENTAL PROCEDURE Certain inconsistencies in the results of the aforementioned tests repeated on three types of limestone suggested these inconsistencies be attributed to rock inhomogeneity. It was also suspected that the loading speed, which could not be held uniform, may have contributed. The earlier work with both rock and ice

Jan 1, 1964

By A. R. Conroy

Microscopic observation of physical and chemical changes which take place in various materials under conditions of elevated temperature and controlled atmosphere can often yield valuable insight into the fundamental physical-chemical reactions which control processes in which these materials play an active role. The technique of high-temperature microscopy thus becomes an important tool for basic and applied research in pyrometallurgical and allied fields. Investigators have long been aware of this and through the years have applied the technique to a wide variety of problems. However, up to this time, application has been on a rather limited scale due to the high initial cost of equipment and the relatively low rate of production of data resulting from the complexity of the apparatus and attendant problems in manipulation.

Jan 1, 1964

By Forrest T. Moyer

The National Safety Competition was inaugurated in 1925 by the Bureau of Mines, U.S. Department of the Interior, in cooperation with the Explosives Engineer. In the first nationwide contest, 210 mines and quarries were enrolled. In 1962, the thirty-eighth anniversary of the competition, 910 mines and quarries were enrolled. These participating plants were worked a total of 133,292,989 man-hours. Of the enrolled plants, 415 achieved injury-free operations for the year, the largest number of perfect safety records in the history of the contest.

Jan 1, 1964

By Sidney Fischler

Large striation-free single crystals of bismuth have been grown from the melt by rapid freezing. Zone-refined bismuth, together with doping impurities if desired, is placed in a shallow flat-bottomed graphite boat and melted in air with a propane hand torch. The torch is then withdrawn in a manner which causes the melt to freeze direction-ally. Crystallization, which resuires only a few minutes, usually results in the formation of a single crystal even when a seed crystal is not used. Crys -tals of any desired orientation may be grown by using oriented seeds. Undoped crystals grown by this method have residual resistivity ratios greater than 200. THE growth of large single crystals of bismuth by either the Czochralski or horizontal zoning technique is not entirely satisfactory. Specifically, difficulties are encountered in producing single crystals of the required dimensions in all desired orientations, and striations caused by low-angle polysynthetic twins are frequently present in the crystals. In addition, both methods are time-consuming and require special apparatus of some complexity. A simpler method has now been developed for growing large striation-free bismuth single crystals of desired orientation in a short time. Fig. 1 shows a typical setup consisting of a rectangular graphite boat which contains zone-refined bismuth, a 1/8-in.-thick flat quartz plate which covers the entire inner bottom of the boat, and three additional quartz plates about 1/4 in. thick which are used to separate the bismuth from the graphite everywhere except at a small area at the left of the boat. The graphite boat is 1 in. high, and its sides and bottom are about 1/8 in. thick. The quartz plates should be smooth and clean. The graphite boat is heated from the right with a propane torch, as shown in Fig. 1, until the bismuth is completely melted. The melt has the shape of a triangle with a narrow neck at the apex farthest from the torch. The melt is frozen direc-tionally by gradually moving the torch toward the right, away from the boat. The bismuth in contact with the graphite, at the left end of the neck, freezes first. The freezing interface then moves down the neck into the main bulk of material, where it develops a convex shape ideal for the continuation of single-crystal growth. The interface continues to move through the melt until the entire bulk is solid. The entire procedure may be completed, in air, in a matter of minutes. The technique described almost always yields a single crystal whose basal plane is nearly perpendi,cular to the bottom of the graphite boat. In earlier experiments, in which the bottom of the melt was in direct contact with the graphite boat, single crystals were grown with basal planes parallel, perpendicular, or at some intermediate angle to the bottom of the boat. At times the orientation of the bulk of the material differed from the orientation of the material in the narrow neck. In these cases, a nucleation site initiated the growth of a differently oriented crystal, and the thermal conditions favored the new orientation over the initial one. The thermal conditions depend on a number of factors, including the heating technique, the placement, shape, and thickness of the quartz plates, the thickness of the walls and bottom of the graphite boat, and the quantity of bulk bismuth employed. All of these factors, plus the initial orientation and the presence and effectiveness of nucleation sites, will determine the orientation of the final large single-crystal slab. When a crystal of specific orientation is desired, an oriented section of a rapid-freeze crystal is shaped by spark cutting and grinding for use as a seed. To grow a doped crystal, the desired impurity is placed in the graphite boat together with the bismuth chunks and seed. Crystals doped with mercury, cadmium, lead, and selenium have been grown. The rate of freezing is so great that the distribution coefficient of any impurity approximates unity. On a gross scale, therefore, impurities should be more homogeneously distributed in rapid-freeze crystals than in Czochralski or zoned crystals. Because of the possibility of constitutional supercooling, however, it is quite possible that impurities are not homogeneously distributed on a microscopic scale in the rapid-freeze crystals. Generally the single crystal slabs which have been prepared are initially 5 to 7 mm thick. Thicker crystals may be obtained by using one of these slabs as a seed. The slab is placed in a graphite boat resting on a large aluminum block, either air- or

Jan 1, 1964

By M. Semchyshen, A. P. Coldren, W. G. Scholz

A survey of the Fe-Mo-B system was made to determine the extent to which boron might affect the microstructure and strength properties of iron-rich Fe-Mo alloys. Seventeen vacuum-induc tion melted ingots were prepared with approximate mo-lybednum contents 01 2, 4, 9, and 19 wt pct and approximate boron contents of 5, 14,50, and 630 ppm by weight. Phases extracted from annealed specimens and identified by X-ray diffraction analysis included E Fe3MO2, Mo2FeB2, and an oxide hazling a diffraction pattern practically identical to that of MnFez04. Three types of alloy strengthening were observed: a) Fe-2 pct Mo-B alloys were hardenable by a bainitic-type transformtion of austenite to ferrile; b) Fe-4 pct Mo-B alloys were hardened by the solid-solution mechanism; and C) Fe-9 pct Mo-B and Fe-19 pct Mo-B alloys were hardened by precipitation of the E Fe3Moz phase. Boron was observed to have a very strong hardening effect in the Fe-2 pct Mo alloys and a mild strengthening effect on the 1200°F properties of the Fe-4 pct Mo alloys. In the Fe-9 pct Mo alloys there was no consistent effect of boron on strength at either room temperature or 1200° F. The Fe-19 pct Mo alloys were so brittle that meaningful tensile or creep-rupture data could not he obtained. No dispersion hardening from borides was recognized in any of the alloys. THE high-temperature properties of iron-rich Fe-Mo alloys were studied by Reiter and Hibbard.' They found that the strength of the alloys increased markedly as the molybdenum content was raised from 0 to 15.9 pct by weight. The authors explained the various degrees of strengthening in terms of a) solid-solution strengthening, b) strengthening from a martensitic-type transformation, and C) precipitation strengthening. The objective of the present investigation was to conduct a survey of the iron-rich portion of the Fe-Mo-B system to determine whether the beneficial effects of molybdenum on the strength of iron can be enhanced by the presence of boron. It was thought that perhaps fine dispersions of molybdenum- rich borides would be found which could improve the high-temperature strength of ferritic alloys beyond the strengths attainable by molybdenum additions alone. Also, it was considered worthwhile to study the effects of boron in alloys which are essentially free of carbon. Most, if not all, of our present knowledge about boron in high-temperature alloys pertains to alloys containing carbon and carbides. EXPERIMENTAL PROCEDURES Alloy Preparation. Seventeen 8-lb ingots were prepared from electrolytic Plastiron, unalloyed molybdenum chips, and boron powder by a vacuum-induction melting procedure employing hydrogen as the main deoxidizer. The alloys were melted in alumina crucibles using 35-lb melts, with each melt being split four ways to achieve varying boron contents within four Fe-Mo base compositions. The results of chemical analyses conducted on chips machined from the chilled ends of the ingots are presented in Table I. The boron analyses were performed by a spectrographic method utilizing primary standards prepared from boric acid. They indicated that in ingots to which no boron was

Jan 1, 1964

By H. C. Fiedler

The development of cube-on-edge secondary re crystallization texture in Si-Fe strip depends upon the ability of inclusions, such as manganese sulfide, to restrain nomal grain gvowth. The ability of inclusions to perform this function is shown to depend upon their size and distribution. The desired uniform dispersion of many small inclusions is obtained by controlling the cooling rate from above the solution tempmature of the inclusions or, alternatively, by drastic 'quenching from above the solution temperature followed by heat treating at a lower temperature. The development of the cube-on-edge secondary recrystallization texture in Si-Fe strip depends upon both establishing the proper primary recrystallization texture and having inclusions to restrain normal grain growth. It has been suggested that the first requirement is met with a texture which, though weak, is near (110)[001]. A mechanism for secondary recrystallization originally proposed by ielsen' is consistent with the presence of this primary texture. It is visualized that a secondary grain appears where two adjacent grains happen to be sufficiently similar in orientation to be capable of behaving as a single large grain. This pair of grains will grow at the expense of its smaller neighbors as a consequence of its having lower grain boundary free energy. Other explanations of the origin of the secondary recrystallization texture have been offered,' and it can be concluded that the mechanism is not fully understood. Nevertheless, it is apparent that operationally the necessary primary recrystallization texture is obtained simply by interposing an anneal during the cold reduction to final gage. The role of inclusions in the development of the secondary recrystallization texture has been demonstrated by May and Turnbull4 in a comparison of a high-purity heat and a heat containing manganese sulfide. They showed that the driving force for secondary recrystallization is inversely proportional to the diameter of the matrix grains and that the function of the inclusions is to maintain a small matrix grain size. Other inclusions, such as various sul- fides,')' silicon nitride,8 and vanadium nitride,' titanium carbide,'' and vanadium carbide," have been shown to be effective in promoting secondary recrystallization to the cube-on-edge texture. There is also evidence that silica inclusions in Si-Fe strip made by powder-metallurgy techniques perform this function.' This report is concerned with the second of the two requirements for secondary recrystallization, namely the importance of the metallurgical control of the size and therefore number of inclusions. While the concepts involved are simple, they are fundamental to the making of this material. EXPERIMENTAL PROCEDURE A heat containing 3.27 pct Si, 0.026 pct S, 0.06 pct Mn, and 0.004 pct C was made in an air induction furnace from electrolytic iron, 98 pct ferro-silicon, electrolytic manganese, and iron sulfide. The heat was divided between graphite and baked-sand molds with a cavity 2-5/8 by 5 in. and with walls 2-3/4 in. thick. Slabs, 1 in. thick and 2-5/8 by 5 in., were cut from the ingots and hot-rolled either in the as-cast condition or after one of the heat treatments described later. After pickling, the 80- to 100-mil-thick hot-rolled band was, unless otherwise noted, heat-treated for 5 min at 900°C before being cold-rolled to 25 mils. After a heat treatment of 1 to 3 min at 860°C, the strip was cold-rolled to 12 mils, the final thickness. The percent cube-on-edge texture was determined by dividing the maximum torque as averaged from four samples by the maximum torque of a 3-1/4 pct Si-Fe single crystal having the (110) plane in the plane of the sample. The torque measurements were made in a field of 1000 oe on 1-in.-diam disks. RESULTS AND DISCUSSION The importance of the thermal history of the ingot is evident in Fig. 1 from the appearance of strips heat-treated in a temperature gradient. The sample

Jan 1, 1964

By Walter Kawa

Bureau of Mines research on the hydrogenation of coal has been concerned with developing processes that could be used to supplement the Nation's petroleum and natural gas resources. Motor fuel was produced in a subsidized coal hydrogenation industry in Europe prior to 1945, but the process used is still not economical and other methods of producing liquid and gaseous fuels from coal are being investigated. As an aid to the planning of coal hydrogenation research, a literature survey was made of processes or methods of hydrogenating coal that differ from the subsidized or conventional process. This report contains a bibliography of unconventional methods of hydrogenating coal and a brief discussion of the economics of the conventional method. A general discussion of unconventional methods is included, and the advantages and disadvantages are pointed out where possible. The survey supplements a previous Bureau of Mines survey3 and a comprehensive review published in 1930.4

Jan 1, 1964

By C. C. Herrick

The vapor pressure of indium has been measured by the torque-effusion technique, as a function of temperature between 1102o and 1422oK. For liquid indium, the vapor pressure (in atmospheres) can be represented by the equation -R In P = 5.782 x104/T - 25.29from 1000o to 1422oK. Extrapolation yields a calculated normal boiling point of 2329°K and a heat of vaporization at 298 oK of 58.09 kcal per mole by the third-law method and of 58.39 kcal per mole by the second-law method. Calculations indicate that the free-energy functions of Hultgren are to be preferred to those of Guruich. BECAUSE of the potential uses of liquid metals, it is important that convenient experimental methods be developed which will lead to a sufficient body of thermodynamic data so that reasonable estimates of properties of liquid metals can be made. Indium is particularly well-suited to investigation, since it remains liquid over a long temperature interval, it alloys readily, suitable containers for it are easily procured, and relatively few investigations of its thermodynamic properties in the region above 1000°K have been made. PREVIOUS RESEARCH The first determination of the vapor pressure of indium was made by Anderson,' using the Knudsen method and silica-lines stainless-steel cells. Kohlmeyer and spandau2 determined the normal boiling point, and a mass-spectroscopic investigation has been made by Lyubimov and Lyubitov.3 (Unfortunately, only an equation representing the data of the latter investigators has been available to us.) Hultgren et al.4 and Gurvich5 have published discordant tables of the free-energy functions for indium. EXPERIMENTAL METHOD The torsion-effusion principle has been described amply in the literature.8,7 With this method, one observes the angular deflection induced by effusion of vapor from a multihole effusion cell which is suspended from a filament producing a small rotational restoring force. The pressure within the effusion cell can be computed from the relation ziaifiai where k is the torsion constant of the filament, 6 is the observed angular deflection, and ai, fi, and qi are the area, force factor, and moment arm of the ith effusion orifice. The force factor f is analogous to the Clausing factor,' and corrects for the reduction in effusive force attributable to the finite geometry of the effusion orifice. Schultz and Searcy' have tabulated the force factors for various tube geometries. EXPERIMENTAL APPARATUS The physical arrangement employed in this study is shown in Fig. 1. The furnace elements are six Globar heat rods with 15-in. hot zones. Temperature is maintained to * 1°K by a Beck mechanism driving two 26-amp Powerstats in parallel. A Pt (Pt, Rh 10 pct) thermocouple serves as the sensing element. Four inner tubes act as vibration isolators; the air pressure required for maximum isolation was determined empirically, and is maintained by a solenoid valve. The tungsten fiber, 9 by 0.002 in., is joined to an 0.008-in. tungsten wire or graphite rod via a machined lightweight chuck.

Jan 1, 1964

By B. S. Tani, R. V. Schablaske, M. G. Chasanov

MEASUREMENTS of the solubility of scandium in liquid cadmium from 349" to 606°C by Chasanov, Hunt, Johnson, and eder' led to the isolation and characterization of the intermetallic compound ScCQ. The solid phase found in equilibrium with a saturated solution of scandium in liquid cadmium above 422°C is ScCQ. The equilibrium solid phase below this temperature has not as yet been characterized. Hexagonal needles of ScCG were isolated from a 5 wt pct Sc alloy which had been ice-quenched from 500°C. Free cadmium was leached away from the intermetallic with saturated ammonium nitrate solution. The concentration of cadmium in successive leaches was followed polarographically and the leaching process was terminated when the rate of cadmium dissolution decreased markedly. Chemical analysis of the intermetallic thus isolated is as follows: 11.5 wt pct Sc and 88.3 wt pct Cd. The composition of ScCQ is 11.8 wt pct Sc and 88.2 wt pct Cd. X-ray diffraction powder photographs of ScCds taken in a 114.6-mm Debye-Scherrer camera with CuKa, radiation can be indexed on the basis of a hexagonal nit cell. Lattice coonstants are a. = 6.330 ± 0.001A to 6.324 i 0.001A and co = 4.853 i 0.001A. The a0 has a slight range with the lower value seemingly associated with the cadmium-rich terminus of the phase. With eight atoms in the unit cell the calculated intermetallic density is 7.54 g per cu cm; the density as determined by a liquid-displacement method is 7.7 g per cu cm. Powder-diffraction data for ScCQ are recorded in Table I. Stoichiometry, symmetry, unit-cell dimensions, and the number of atoms per unit cell indicate the MgsCd (D019) type structure for ScCQ; space group is D,&-P6,/mmc. Atomic coordinates are:

Jan 1, 1964

By F. F. Netzeband

This report relates to the sulfur industry of seven States--Arkansas, Kansas, Louisiana, Mississippi, Missouri, Oklahoma, and Texas--and is part of a national study of the sulfur industry by the Bureau of Mines. Markets as used 1n this report are divided into two components for individual analysis--(1) supplier markets which include regional Frasch and byproduct sulfur producers and (2) consumer markets which include processors and manufacturers requiring sulfur in their operations. The term sulfur as used in this report includes brimstone, native sulfur, elemental sulfur, or sulfur equivalents.

Jan 1, 1964

Safety rules for installing and using electrical equipment in and about coal mines covered in this information circular supersede those previously included in Bureau of Mines Bulletin 514, issued in 1952. This revision brings these rules up to date and more nearly in line with present operating and safety practices in the industry. The rules are intended to supplement existing Federal and State regulations, and no provision shall be construed to oppose or supersede any provisions of the Federal Mine Safety Codes, the Federal Coal Mine Safety Act, or the mining laws of any State. The rules were designed to permit progress, such as application of new or improved materials and equipment or use of new practices where these materials, equipment, or practices retain or improve the level of safety established by these requirements. It is hoped that they will fill the need for a concise edition for mine electricians and electrical engineers, especially those who do not have ready access to more detailed rules or codes.

Jan 1, 1964

By R. F. Mitchell, G. F. Dillon, A. F. Armington

In this paper the present methods of boron preparation are discussed with emphasis on the iodide intermediate. Several methods of boron triiodide preparation were investigated, the most satisfactory method being the preparation from the elements. A yield of 60 pct based on iodine is found for this method. Zone-refining, sublinzation, distillation, and fractional-recrystallization results are given for the boron triiodide, with distillation producing the best results. Several methods of decomposition are also discussed. The purity of the resulting iodide boron approximates the puritjl of the best available bromide boron, ELEMENTAL boron has been suggested as a possible high-temperature semiconductor by several workers,' but has never been exploited as a device material. The principal difficulty with boron is the unavailability of pure crystalline material from which accurate information on electrical properties could be obtained. Most boron crystals presently produced are very imperfect in structure and of questionable purity, particularly in relation to carbon content. Several methods of boron purification have been reported in the past few years, all of which produce material with a purity better than 99.0 pct. Most of these methods have been the subject of a recent review by Starks' and will not be elaborated upon in this report. However, of all the purification methods reported, only those using halide intermediates produce a purity approaching that usually required for electronic applications. The bromide intermediate has been most used for the preparation of high-purity boron.'y3 This material is easily prepared from the elements and can be effectively purified by distillation and decomposed by hydrogen reduction. The resulting product contains a trace of silicon, and an uncertain amount of carbon, believed to be approximately 100 ppm. It has been recently reported by Russian workers that high-purity boron can be produced using an iodide intermediate.' In the work cited, boron is reported free of spectro-scopically determined impurities, but the reported detection limits are quite high (- 100 ppm). In addition, no data is given on the carbon content of the product. In the present paper, boron triiodide was chosen as the intermediate for several reasons. First, carbon tetraiodide, which could be a major impurity, is reported to be unstable above 200" and hence could be easily separated from the boron triiodide by its decomposition, since temperatures greater than this are attained during the purification process. The low melting point (45°C) and boiling point (20B°C) and the relatively high vapor pressure of boron triiodide should allow the application of any physical purification technique to the material. The possibility of a lower decomposition temperature than that used for the bromide process is another advantage which might cut down extraneous contamination. The iodide, however, does have certain disadvantages when compared with the bromide, the production cost being the most significant. This is the result of a higher halide-to-boron weight ratio, which means more intermediate must be employed. The cost of the starting material is also greater for the iodide. This cost could be considerably reduced however, by recycling the iodine byproduct. Epitaxial growth of boron, which is probably the best method of producing junctions, should be possible with either the bromide or the iodide as the intermediate. However, this has been attempted only on a limited scale up to the present time because of the unavailability of good crystals. The authors have been relatively successful in laying down a heterotaxy of boron on silicon, however. This will be reported at a later date. Several crystalline modifications have been reported for boron, four of which are now believed to be real.' These are the a! and 0 rhombohedral and the a, and 0 tetragonal. In general, the a! rhombohedral is the low-temperature form and the B rhombohedral is the high-temperature form. The tetragonal structures are detected between 1000"

Jan 1, 1964

By G. Koves

The behavior of case-hardened AISI C-1213 free -machining steel under complex impact-fatigue -wear load conditions was investigated. The inherently poor dynamic properties of the steel are mainly affected by the stress distribution in the case, component shape, and tempering. Cold-riveted components showed unexpectedly high dynamic strength compared to basic parts. A compromise beatment—which provides good dynamic properties, reasonable wear resistance, and fair riveting characteristics—zuas developed. A number of mechanical components in data-processing machines are made of free-machining carbon steel. Although, selected primarily due to manufacturing requirements, components made of these grades frequently undergo complex heat treatment and must sustain impact-fatigue loads. A typical free-machining steel is the AISI C-1213 grade, which is a resulfurized and rephosphorized open-hearth steel. While the undesirable effects of sulfur and phosphorus on the mechanical properties are well-known, data on dynamic properties are scarce.1"3 Rapid rotating or oscillating motion while carry- ing a high cyclic load requires a combination of wear resistance with high endurance limit and impact toughness. The inherently poor dynamic properties of the free-machining steel are further degraded by the machining, which introduces local stress-concentration areas. While the heat treatment (usually case hardening) improves some mechanical properties, it necessarily impairs others. Another problem arises when components, such as studs, must be fastened by riveting. The high crack-sensitivity of the free-machining steel, especially in the presence of a hardened case, makes this operation difficult. In view of the preceding considerations, it is of interest to investigate the behavior of a typical component under complex impact-fatigue-wear loading conditions in order to explore the effects of material, machining, and heat treatment, to obtain specific data on the dynamic characteristics of free-machining steel, and to arrive at a process which would adequately utilize the inherent qualities of this material. EXPERIMENTAL PROCEDURE To simulate actual service conditions, a typical component was selected, based on frequency of application, complexity of load, and processing difficulties. The dimensions and shape of the component—a stud used in many electromechanical document-handling machines—are shown in Fig. 1.

Jan 1, 1964

By R. B. Toombs

In describing the Canadian mineral industry in a world setting, this paper examines the industry from four points of view. First, mineral industry growth is related to trends in economic activity thereby providing a measure of the industry's importance in the Canadian economy. To give perspective to the Canadian scene, reference is made to economic trends in several of the world's leading mineral producing and mineral consuming countries. The Canadian mineral industry is next examined in terms of its major developments of the past 20 years and the resultant size, structure, and production diversity of 1964. The position of the Canadian mineral industry in the world industry is then analyzed by tracing changes in mineral supply and demand patterns. Growth of the Canadian industry depends greatly on expansion of export markets because three fifths of the value of production is accounted for by exports. Finally, attention is directed to the outlook for the Canadian mineral industry. Problems facing the industry are surveyed, and an appraisal is made of economic policies that have encouraged industry growth. A forecast of mineral production value in 1970 is included.

Jan 1, 1964

By E. F. Poncelet

Forty years ago A. A. Griffith developed a theory explaining why brittle materials displayed such low tensile strengths.' He based his views on two points. First, he found himself compelled to assume that all brittle materials are replete with flaws, cracks, and other defects that act, although quite invisible, as large stress raisers. Second, he applied the "theorem of minimum potential energy," which says that the total potential energy of a system must pass from the unbroken to the broken condition by a process involving a continuous decrease in potential energy. By this means he satisfactorily accounted for the noted low strength of such solids and also for the wide spread obtained in experimental measurement of these strengths. So successful has the theory been that it is favored by some to this day. Unfortunately this theory is of limited use beyond the explanation of these two noted phenomena and it is keenly felt that a better theoretical insight into the physics of the fracturing process is needed as the volume of experimental evidence accumulates. The author proposes in the following to build on the fundamentally sound concepts of Griffith and, with the help of increased theoretical knowledge over that available to Griffith, develop a mechanism for frac-ture which will provide far greater understanding of the experimental evidence accumulated to date than is possible from the original Griffith idea. THE GRlFFlTH THEORY Very little progress indeed can be made without accepting the first postulate of Griffith which supposes all brittle solids to be full of microcracks. It would be difficult indeed to find a better mechanism for the small strength of such brittle materials, in conjunction with the fact that the energy that must be expended for comminution is by no means small. The postulate of the existence of the microcracks permits the breakup of the various bonds a few at a time by concentrating the stress at the tip of the progressing crack, while the total energy expended is the same as if they all had been ruptured simultaneously. The only flaw in the argument is that no reasonable explanation has been proposed to account for the genesis of such cracks. Indeed their very presence is in violation of the Griffith second postulate, the potential energy theorem. This theorem is straightforward for isothermal processes, and, in spite of Griffith, there is some doubt that treating the problem isothermally is legitimate. The surface energy of bodies is a free energy, not a potential energy as stated by Griffith, and the production of new surface free energies is not necessarily an isothermal process. There is ample evidence to the contrary. Generally speaking, if heating a body increases its surface area, then, by virtue of Le Chatelier's principle, any increase of that area by other means will tend to lower its surface temperature. Lord Kelvin calculated the actual cooling that resulted in drawing out a film of liquid.2 R. A. Houston calculated the surface cooling that resulted in stretching a metal wire.3 These calculations were made by applying the Carnot cycle to the process and evaluating the thermodynamics thereof. IRREVERSIBILITY OF THE FRACTURING PROCESS While Griffith was very careful not to say so, the impression gained from studying his papers is that he considered the fracturing process as reversible, that is, a succession of quasi-equilibrium states. There is ample evidence that it is not. The indication that the new surfaces produced by the propagation of a crack are cooler than the original body points to an irreversible heat flow from the interior to the new surfaces to equalize the temperatures. If the process be reversible, any crack accidentally formed should immediately close up as, in the absence of any strain energy, the potential energy would thereby be lowered. The fact that they do not, constitutes a paradox. Such paradoxes are nothing new where certain phenomena that propagate from minuscule nuclei are assumed to be reversible. Such is, for instance, the condensation of a pure saturated vapor that is suddenly chilled by adiabatic expansion. At the beginning the tiny droplets that are formed should be only a few angstroms in size, but the vapor pressure at such droplets is so high that they should evaporate at once. A similar situation arises if a saturated pure solution becomes super-saturated upon cooling; the first tiny crystal nuclei should dissolve as fast as

Jan 1, 1964