By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid binary and ternary Fe-Ni-Co alloys has been measured by the Sieverts' method between 1550°and 1700°C. Solubility data and standard free energzes and enthalpies of solution for nitrogen in the alloys are presented. Interaction parameters are discussed and presented for binary and ternary alloys. MOST of the studies of nitrogen solubility in liquid metals have been directed toward the dilute alloys of iron. Several of these investigations have included measurements of the nitrogen solubility in Fe-Ni al10s'- and in Fe-Co alloys.435 There has been some work, however, that has extended across the e-i-" and F-CO" binaries. This investigation was undertaken to determine the nitrogen solubility in both binary and ternary alloys of the Fe-Ni-Co system. It was also hoped that the differences between earlier studies might be resolved. EXPERIMENTAL METHOD This investigation was made using a Sieverts' apparatus described previously." The nickel (99.85 pct) and cobalt (99.9 pct) were obtained from Sherritt-Gordon Mines, Ltd., and the iron (99.95 pct) was Fer-rovac-E obtained from Crucible Steel Co. Recrystal-lized alumina crucibles were used throughout the entire investigation with no evidence of crucible-melt reaction. Melt temperatures were measured with an optical pyrometer and the temperature scale calibrated against the melting points of the three pure metals. The emissivity of the melt was assumed to be a linear function of composition for all alloys, as has been shown for Fe-Ni alloys.lZ The emissivity of the pure metals at 1600°C were taken as 0.43 for iron, 0.44 for cobalt, and 0.45 for nickel. Using these emissivities, the trans mis sivity of the system was found to be 0.51 i 0.01. The Sieverts' method was used for this study and followed the procedures outlined previously.l' The individual metals were weighed to give about 100 g of alloy. The alloys were melted in the crucible under a partial pressure of argon. The system was evacuated, and the "hot volume" was measured with argon. To avoid the errors caused by vaporization, the melt was held under vacuum only long enough to ensure that all of the gas in the system had been removed. The influence of any small amount of vaporization on the "hot volume" was shown to be negligible by measuring the "hot volume" after a run. This measurement agreed with that made at the start of the run within the implicit error, 0.2 cc, caused by the limitations in accurately reading the buret. The solubility-pressure relationship was measured in the pure metals and in several alloy compositions throughout the ternary system. These measurements were made by admitting measured amounts of nitrogen to the system, and then determining the equilibrium nitrogen pressure above the melt. This method has the distinct advantage of higher accuracy, particularly at lower pressures, than measurements made by withdrawing gas from the system to reduce the pressure after determining the solubility at 1 atm nitrogen pressure. This latter method has a practical lower limit of about 0.4 atm where an increased error is encountered because the buret must be emptied to permit further measurements at lower pressures. By determining the relation between apparent solubility and pressure, it was possible to make a good estimate of the initial nitrogen content of the metal from the intercept of the solubility curve extrapolated to zero pressure.11 DISCUSSION The solubility data corrected to 1 atm nitrogen pressure are summarized in Table I. The reported solubility has been corrected for the initial nitrogen content of the alloys. The initial nitrogen contents fell between 0.0002 and 0.0010 wt pct, and were lower in the iron and nickel than in the cobalt. Sieverts' law was obeyed in all alloys at pressures up to 1 atm. Examples of this behavior are shown in Fig. 1. The reaction for solution of nitrogen is Taking the standard state as 1 wt pct N in the alloy and the reference state as nitrogen at infinite dilution in the alloy, and noting the adherence to Sieverts' law, K becomes the solubility of nitrogen in the alloy at 1 atm pressure. Thus the solubility data of Table I were used directly to calculate the standard free energy for the solution reaction. These results are also presented in Table I. The enthalpy of solution is also summarized in Table I as calculated from a form of the van't Hoff relation: Iron-Nickel System. The data for the solubility of nitrogen in liquid Fe-Ni binary alloys is presented in Fig. 2 along the with data of aito, Schenck et al.,' and Humbert and 1liott.l' The data for studies of nitrogen solubility in Fe-Ni alloys containing less than 20 pc t i'- are not presented in Fig. 2, although they are in good agreement with the present work. The results of this study are in good agreement with Schenck

Jan 1, 1967

By R. F. Waters

Laboratory-scale selective volatilization methods developed by the Bureau of Mines to recover germanium and gallium concentrates from coal fly ash and phosphorus furnace flue dust are summarized. In the better experiments between 85 and 98 percent of the germanium was recovered as the lower oxide and as sulfides, and between 75 and 97 percent of the gallium was recovered as the lower oxide and as the trichloride. Grades of the condensates were inconsistent and varied between a few tenths of a percent and 8 percent, depending on the method used. In the primary extractions of germanium alone the degree of enrichment surpassed 100 to 1, and for gallium the best ratio was 30 to 1. Upgrading of condensates by vaporization retreatment and by leaching and precipitation is discussed. An appreciable degree of mechanical preconcentration by attrition scrubbing and elutriation was possible on two fly ash samples.

Jan 1, 1967

By Roger V. Pierce

"WITHOUT mineral wealth, modern man would not exist. True, man could survive on a stone-age basis with an average life expectancy of, say, 25 to 30 years -once he got past infancy.However, no metal would tip his arrow in a hunt for protein; no steel plough would break the soil for the organized planting of seed; and no coal, nor oil, nor natural gas nor uranium fuels would pro-vide him with light or beat or safety from either beasts, or other men, or an unkind nature that threatened him and his family.Modern agriculture, fishing and forestry represent the other three wealth-producing industries. With-out metals, non-metallics and energy minerals, however, it would be impossible to fit any of these to man's modern needs."

Jan 1, 1967

By John E. Miller

A high accuracy Burnett apparatus for use at 12,000 psi and 0° to 65° C has been constructed at the Bureau of Mines Helium Research Center. The apparatus is patterned after Burnett's original apparatus, but the working pressure is much higher and elastic distortion can be essentially eliminated. An operating procedure to permit faster experimental measurements is suggested.

Jan 1, 1967

By Eugene S. Machlin

A classical theory of solid solutions involving neavest-nergkbor intevactions with both central and linked-central forces between atoms has been developed. It has been found that the theory, where it can be checked quantitatively, is in ageement with experiment. The theory encompasses a description of many diverse pkenomena, such as antiphase shift structures, size effect, relative stabilities of various solutions, lattice para,neters, and order-disorder transitions. In particulav. a quantitative prediction not involving adjustable pavameters is made concevning the deviation of the Au-Cu interatonlic distance in long-range ordered (Ll,) Cu-Au I fronl the average distance based on the distances in pure gold and copper. This prediction, which is in agreement with expel-intent, has not been encompassed by any preuious theory. The theory of order-disorder is fragmentary. That is, no one theory exists that can explain the variety of qualitative phenomena observed. Further, many theories are not in good quantitative agreement with experiment. This subject has been reviewed by Muto and Takagi, Tuttman, and Oriani.3 There exists no doubt that the quasi-chemical approximation is not a complete description and that the inclusion of strain energy using macroscopic elasticity theory concepts leads to results in disagreement with experimenL4 The observation of antiphase domains and ordering systems such as Cu-Pt has led to Brillouin zone treat-ment of the order-disorder transition as opposed to the classical Ising model. The objective of this paper is to demonstrate that it is possible to develop a pairwise approximation model that can explain many of the observed order-disorder phenomena that have puzzled investigators in the past. This theory is based upon an empirical model due to ergmman' for the elastic constants of metals. This model is generalized for multicomponent systems. As will be shown, the theory yields a short-range ordering energy for the disordered solution which differs from the ordering energy calculated from the differences in energy of disordered and long-range ordered solutions. It will be demonstrated that there is no necessary correlation between heats of formation and the tendency to order or between size effect and the tendency to order. Also, the existence of antiphase domains and iso-short-range-order systems that form superlattices (Cu-Pt) is predicted on the basis of the theory. Further, the relative stability of competing superlattices is calculable from the theory. If single-crystal elastic-moduli data are available for the pure components and one superlattice then there exists but one adjustable parameter in the calculation of lattice parameters for both the disordered and ordered solid solutions. In one special case, no adjustable parameters are required and a quantitative prediction is made. For the calculation of energies and partial order, there exists but one additional adjustable parameter, the pair-exchange energy V used in the quasi-chemical approximation (or the Ising model.) However, in these calculations, much more precise values are required for the single-crystal elastic moduli than available if the quantitative uncertainties in the predicted values of the energies are to be sufficiently small. THEORY ~er~man' has developed a model with which he was able to obtain fair agreement with experiment for the relations between the elastic constants for metals. This model which we shall call Bergman's model is a linear combination of his models I and 11. In effect, Bergman, in this model, considers that each interatomic distortion is composed of two components: a classical central force distortion with an associated central force constant and what we shall call a linked-central force distortion with an associated linked central-force constant. The linked-central force distortion component obeys the constraint that the sum of such distortions over all the bonds equals zero. No constraint is imposed on the classical central force distortion component. Bergman' derives the constraint on the linked-central force distortion on the basis of application of Pauling's relation between bond distortion and bond number to metals.ga This assumption is not logically necessary, however, and the Bergman model may be taken as a mathematical model for elastic constants, e.g., a purely empirical model without a physical basis. In the present work, the method of Bergman has been applied to two-component systems (solid solutions). In place of an external strain—which would allow a calculation of the elastic constants for the two-component system—it is considered that internal interatomic distortions exist as a consequence of having three potentially unequal distortion-free interatomic distances and but one "average" interatomic distance. It is assumed that the distortion-free interatomic distances between atoms of the same element are those found in the pure element having the same undistorted crystal structure as the solid solution. The distortion-free interatomic distance between unlike atoms is in general not measurable except in the probably nonexistent

Jan 1, 1967

By H. M. Woodrooffe

This paper deals with the laboratory facilities at the Mines Branch for carrying out research in the industrial minerals field, and also reviews current programs in ceramics and construction materials, in non-metallic minerals and in the milling of industrial minerals. It then discusses the application of these pro-grams to industrial problems.

Jan 1, 1967

By Charles B. Kenahan

The effects of ultrasonic radiation on the electrodeposition of copper-zinc, copper-cadmium, and copper-tin alloys from cyanide baths were investigated by the Bureau of Mines at frequencies of 18.5 and 38 kilocycles per second, and at acoustic intensities up to 0.5 watt per cm3. Significant changes occurred in the composition of the deposited alloys; some of these deposits were brighter, harder, more adherent, or of finer grain size than nonirradiated deposits. The irradiated deposits were also smoother and less porous, and they afforded better corrosion protection for the substrate metal in sodium chloride solution. The limiting current densities of the cyanide baths were increased by the application of ultrasonics. Anode and cathode current efficiencies also were increased, and cell voltages were lowered; the relationship of these effects to current density is discussed. Electrode potential measurements showed significant depolarization effects at both electrodes during ultrasonic irradiation. The resulting decrease in cell voltage was due chiefly to depolarization at the anode, and the anode became less passive.

Jan 1, 1967

By Robert C. Ellman

Stockpiles containing 2.3 million tons of lignite constructed in the period 1948-56 in conjunction with the construction of Garrison Dam on the Missouri River demonstrate successful stable long-term storage of lignite. Uniform and thorough compaction of each of the I-foot-thick layers by which the piles were constructed produced a bulk density of 70 Ib/cu ft. Air penetration into the stockpiles was restricted to a degree that prevents spontaneous heating or deterioration of the stored lignite, A continuing record of observations beginning with stockpiling operations in 1948 has been accumulated, This includes periodic fuel analysis, analysis of pile gases, and measurement of pile temperatures on the first large stock-pile, pile 5. This report describes the stockpiling method, the changes in heating value, pile gas composition, and pile temperature and summarizes observations from 1953 to 1964, Data accumulated attest to the stability of the stored lignite. The variation of the average heating value of periodic pile-depth samples is only 160 Btu/lb (11,990 to 11,830) on the moisture" and ash-free (maf) basis during almost 10 years of storage. Temperature levels of the pile interior are progressively decreasing. At pile surface, cyclic variations occur with the season. The only problem encountered with the large stockpiles is wind and water erosion of the pile surface. The partially successful control measures used are described.

Jan 1, 1967

By C. C. Shale

Current-voltage relationships for air at high temperature in negative corona are compared with relationships predicted by theory. Deviations are discussed. Eased on the latest theoretical concept of electron detachment from negative ions and recent findings in basic research on free electron gases, results of applied research show the existence of free electrons in air at high temperature and high field strength-to-pressure ratios.

Jan 1, 1967

By Claude H. P. Lupis, John F. Elliott

QUITE generally an increase in the temperature tends to bring a system closer to ideality. It is reasonable as a first approximation to consider that the excess free energy will vary linearly with the temperature, or: where t may be defined as the "characteristic temperature" of the solution, or the temperature at which the system would become ideal if the results at T were linearly extrapolated. It must be emphasized that consideration of this hypothetical property is an appeal to intuition rather than an established physical concept. The order of magnitude of 7 for dilute solutions will depend on the nature of the solvent; a value of 3000° + 1000°K may be suggested for ordinary metallic solutions. In terms of free energy, entropy, and enthalpy first-order interaction coefficients, differentiation of the above equations with respect to composition leads to The concept of t offers a simple and plausible interpretation of Chipman and corrigan's3 recent empirical correlation between and a for a number of groups of ternary systems 1-24. The authors found that in each group the ratio was approximately constant. The corresponding calculated from their data by Eq. [4] are listed in Table I. The expected order of magnitude is obtained for 7. As noted by Darken,4 if a regular solution is not assumed, thus if utj) # 0, Chipman and Crrigan's results imply that, as T is increased, ultimately changes in sign, Fig. 1. Clearly Eq. [4] is valid only in a limited range of temperatures since at the temperature 7 at which the system becomes ideal not only should become null but also and . Thus, both and are functions of

Jan 1, 1967

By Hillary W. St. Clair

The reduction zone of the iron blast furnace is represented by a mathematical model of the chemical reactions and heat transfer that occurs between gas and solids during the deoxidation of iron oxide. The model consists of a set of equations and an algorithm whereby the equations may be solved to give the temperature and composition of gas and solids at any position in the reaction zone and at any time after a specified initial state. The model is applied to the special case in which ferric oxide is reduced by graphitic carbon and carbon monoxide produced by burning carbon in dry air. The rate of reduction, carbon consumption and maximum temperature are shown as functions of the temperature and rate of flow of the incoming reducing gas and external heat loss. The model of the reduction zone is the essential part of a general mathematical model for simulation of the iron blast furnace. The simulation model will serve as a research tool to be used in conjunction with an experimental or operating furnace. After the simulation model has been correlated with the real furnace, it is proposed that further experimentation be done mostly with the model. The real furnace will then be operated primarily to test and confirm the model.

Jan 1, 1967

By W. B. Braden

This paper presents a suitable method for predicting gas-free oil viscosities at temperatures up to 500F knowing only the API gravity of the oil at 60F and the viscosity of the oil measured at any relatively low temperature. The API pravity and the one viscosity value are used as parameters to determine the slope of a straight line on the ASTM slanaord viscosity-temperature chart. Then, knowing the slope of the line and one point on the line, the vrscosities at higher temperatures can be determined. The line slope correlations were developed at I00 and 210F since viscosity data are frequently measured at these temperatures. A procedure is given for predicting line slopes from measurements at other tetnperatures. A nomogram is furnished for solving the relationship. The correlation has been evaluated at temperatures up to 5OOF for oils varyzng in gravity from 10 to 33 " API. The correiution is applicable only to Newtonian fluids. Comparison at 500F of true viscosities and those predicted from values at 100F shows an average deviation of 3.0 per cent (maximum deviation of 6.0 per cent). Predictions from the values at 21 0F for the same oils how an average deviation of 1.5 per cent (maximum deviation of 3.4 per cent). INTRODUCTION Correlations have been developed by Beal' and by Chew and Connally' for predicting viscosities of gas-saturated oils at reservoir conditions. Each of these correlations requires a knowledge of the solution gas-oil ratio and the viscosity of the gas-free oil at the reservoir temperature. For temperatures below 350F, measurements of the gas-free oil viscosities can be made easily using commercially available equipment. In thermal recovery processes, however, reservoir temperatures well in excess of 350F are encountered. Viscosity measurements at such conditions are more difficult and time consuming and require modification of existing equipment or the construction of new equipment. Measurements are further complicated by the difficulty of handling highly viscous oils associated with thermal recovery processes. Therefore, it is desirable to have a correlation which allows accurate prediction of viscosities at high temperatures. A commonly used technique for predicting viscosities at high temperatures is to measure the viscosities at two lower temperatures, plot the values on ASTM standard viscosity-temperature charts and extrapolate to the temperatures desired. If either of the values is slightly in error, the extrapolated value can be significantly in error. To justify an extrapolation, three points are actually necessary. This procedure can consume much time, particularly with heavy oils. Considering the cost of viscosity measurements, it would be desirable to eliminate the need for direct measurements by having correlations which would allow viscosity predictions from other physical or chemical properties. Beal1 investigated the possibility of correlating viscosity with oil gravity at temperatures from 100 to 220F. While showing that a general relationship exists, he also found significant deviations. It is possible that correlations will be developed based on oil composition as more information becomes available. While not eliminating the need for viscosity rneasurements, the method presented herein requires that only one viscosity measurement be made. The API gravity must also be known. The theory is based on the fact that the viscosity of paraffins (high gravity) changes less with temperature than does the viscosity of naph-thenes or aromatics (low gravity). The gravity. therefore, is used as a parameter to determine the slope of a straight line on the ASTM standard viscosity-temperature charts. The correlation is applicable only to Newtonian oils, and deviations due to thermal decomposition and nonhomo-geneity cannot be predicted. Oils containing additives have not been evaluated. PROCEDURE Fifteen oils were used in developing the correlation; eight were crudes and seven were processed oils. Oil gravities varied from 9.9" API (naphthene base) to 32.7' API (paraffin base). The temperature range studied was 81 to 516F. Each oil used had a minimum of three viscosity measurements and each plotted essentially as a straight line on the ASTM charts. In all, 91 viscosity measurements were used in the correlation. Saybolt, rolling ball and capillary tube viscometers were used for the measurements. Viscosity data for Samples 1, 2, 4, 7, 10, 11 and 14 were obtained in Texaco, Inc. laboratories. The data for Samples 3, 5, 6, 8, 9, 12 and 15 were from Fortsch and Wilson,3 and data for Sample 13 were from Dean and Lane.' All data points used in the correlation are plotted in Fig. 1. It is seen that some of the viscosity values deviated slightly from the straight-line plots at the higher temperatures. Properties of the oils after exposure to the

Jan 1, 1967

By W. S. Sanner

Seven samples were analyzed from the major reserves of the Bottom Red Ash bed, Northern anthracite field. The data show variations in thickness and geo-logic structure and in the amount of coal that can be recovered. Recovery of market-grade (less than 17 percent ash) coal is high for all samples, ranging from 76 tp 95 percent in the 3-1/4-by 9/16-inch sizes. The occurrence of coal containing less than 5 percent ash varies from 19.5 to as much as 57.5 percent. Crushing the coarse sizes to minus 9/16 inch increased recovery of market-grade coal in six of seven bed samples. Crushing released sufficient impurities to cause substantial increases in yield of coal containing less than 5 percent ash for all samples. Analyses of the float coal indicate that the quality of coal is comparable for all samples.

Jan 1, 1967

By A. O. P. Casbarian

An analytical method is developed to determine the variation of the ultimate lateral resistance of a plate in a cohesionless soil with depth. This analysis is based on a modification of Rankine's classical earth pressure theory and the theory of plasticity as applied to soils. The ultimate resistance is defined as the product of the effective stress at the midpoint of the plate, the area of the plate and a dimensionless variable termed the ultimate resistance factor. This variable has been plotted us the depth ratio: i.e., the ratio of of the depth of embedment us the height of the plate. The resistance of a plate may then be calculated using the values af the ultimate resistance factor from the chart provided or the equation may be programmed for use in an analysis of anchor systems in cohesionless soils. It is emphasized that the analysis is semitheoretical. The theory has been compared with experimental results reported in the literature and results indicate general agreement. Actual field tests are necessary to further verify this theory. INTRODUCTION With the exploration for oil offshore in waters all over the world, it is of importance to determine the behavior of the various soils in relation to their ultimate resistance to deformation. Examples of such problems are the holding capacity of anchors and the lateral resistance of piles. Very little information is available in the published literature on the design and performance of anchors, in either cohesive or cohesionless soils. The analysis developed in this report is the first step in obtaining a solution for the determination of anchor holding capacity in a cohesionless material. DISCUSSION The theory used in the analysis is based on the ultimate strength of the soil and is the maximum resistance developed by the plate against further movement. In such a state the elastic deformations are disregarded in comparison with the plastic deformations. Hence, the plate can be considered as completely rigid. The theory of plasticity determines the three unknown stresses at any point by means of two equilibrium conditions for a small earth element in combination with the failure condition. However, the exact solutions can only be carried out in a few simple cases such as, for example, when the rupture or failure lines are straight (Rankine theory) or with spiral and straight rupture lines (Prandtl theory).l Kiitter 2 derived a single equation expressing the variation of the stress in any given rupture line. To utilize this equation, it is necessary to know the stress in the rupture line at a certain point. Unfortunately, this is difficult to obtain unless the rupture line intersects the free surface at a certain angle or when the earth is cohesion-less and unloaded. A method to overcome this is to consider only the boundary conditions at both ends of a rupture line without investigating the equilibrium of the earth above the rupture line. This assumes that the rupture lines meet the surface at statically correct angles, so that boundary stresses may be determined. As Kiitter's equation furnished a relation between these stresses, the unit earth pressure may be calculated at the point where the rupture line meets the wall. Another way in which Kotter's equation may be applied is in investigating the equilibrium of a soil mass above a rupture line. This method assumes that the failure or rupture line is known and that the boundary stresses in the rupture line at the ground surface can be determined. In this case it is possible to determine the earth pressure from the equations of equilibrium.

Jan 1, 1967

By W. P. Haynes

To evaluate the potential use of battery-powered vehicles, the Bureau of Mines studied the performance of a battery-powered truck propelled by a 9.6 kw dc motor in considerable detail under various driving conditions. Some of the factors investigated were: Gear ratios, payload (1,468 lb maximum), road grade, stops made per mile, and charging time. With the exception of some difficulty with brush wear, operation and maintenance of the truck was generally trouble-free. On range tests carrying an 868-lb payload a distance of about 50 miles at an average speed of about 19 mph in normal driving, the Bureau's battery-powered truck averaged 1.6 to 1.9 miles per ac kwhr input. Stop-and-go tests indicated that prospects for the use of battery-powered trucks in house delivery service within city limits are good; performance of the Bureau truck was sufficiently high for that type of service. The estimated power cost of 2.65 cents per mile while making 10 stops per mile was attractively low from the standpoint of fuel costs.

Jan 1, 1967

By E. P. Dahlberg, R. E. Reed-Hill

On the assumption that stress or strain relaxation occurs as the result of a thermally activated process, equations are derived relating to tensile experiments that give the strain as a function of the time under the condition of constant stress, and the stress as a function of the time for constant strain. It is demonstrated that if the strain-rate equation i = previously proPosed by Kuhlmann., is used as a starting point, then the relaxation of strain at constant stress may be expressed by the equation c = (-RT/(Y) 1tz tanh (t + is the strain capable of being relaxed at any given instant. Similarly, it is shown that the relaxation of stress at constant strain may be given by a = (-RT/B) In tanh (t + t0)/27, where a is the instantaneois value of the relaxable stress. The fact that these relationships reduce to well-known empirical equations at both large and small values of the stress Or strain is also shozcn. The present theory is shown to agree well with experimental data obtained from tensile elastic aftereffect experiments on a zirconium specimen prestrained at 77 k as to make it strongly anelastic. It is also demonstrated that elastic aftereffect data obtained using torsional specimens ?,Lay agree reasonably well with the equation derived for the case of tension. RELAXATION experiments are often employed as a means of studying metallic deformation mechanisms.' The simplest and most commonly employed techniques involve stress relaxation at constant strain and strain relaxation at constant stress. In general, however, investigations of this nature have been seriously handicapped in the past by a lack of suitable equations giving the time dependence of the relaxing variable over an interval that extends from small strains up into the region where internal-friction experiments become strain-amplitude dependent. This paper presents a derivation of such a set of equations for the case where the time-dependent part of the strain is anelastic or recoverable and the specimens are loaded in simple tension. The relaxation of strain under the condition of constant stress will be considered first. Let us assume that strain relaxation occurs as the result of a reversible thermally activated process that occurs at a number of relaxation centers lying in an elastic matrix. Then, following Kuhlmann,2 we may express the rate of strain relaxation as follows: where C is the strain rate, AFx the free energy of activation of the process controlling strain relaxation, a, the effective or average resolved stress at the relaxation centers, u an activation volume, R the universal gas constant, T the absolute temperature, > a factor with dimensions of a volume that accounts for the strain contribution of a successful operation of a unit process, N the number of relaxation centers per unit volume, and v the Debye frequency. The first term on the right of Eq. [I] represents a strain rate in the direction favored by the stress, while the second term represents the rate in the opposite direction. It is implied in Eq. [I.] that both F and v are symmetrical with respect to the two basic directions of operation of a relaxation process. Eq. [I] may also be written where and S and Q are the activation entropy and activation energy, respectively, of the relaxation process. In the following, A will be considered a constant. This is compatible with a set of experimental conditions where the relaxation rate is controlled by a single basic reversible process in which it may be assumed that the temperature dependence of the product ?Nv is negligible in comparison with the temperature variation of the exponential term. It is also implied that v, 7, and N do not depend strongly on a, . In deriving a relationship for the strain as a function of the time from her equation, equivalent to Eq. [2], Kuhlmann2 chose to consider only the limiting cases where the time was either very small or very large. It will now be shown that it is possible to integrate Eq. [2] to obtain a single equation valid over a wide range of strains if the concept of relaxable strain is introduced. The use of this quantity, which is the difference between the instantaneous value of the strain and the value of the strain at complete relaxation, represents the primary point of departure of the present theory from that of earlier workers. Let us express the effective stress at the relaxation centers in terms of strain. For this purpose we may use the following equation derived by zener3 for the case of strain relaxation at slip bands: where M? and M are the relaxed and unrelaxed moduli respectively, go the applied constant tensile stress, and m an average orientation factor that takes account of the fact that a,, the effective stress at the relaxation center, may not be a tensile stress (i.e., a

Jan 1, 1967

By William R. Hardwick

Present information indicates that a copper deposit can be safely fractured with a nuclear explosive and the copper successfully recovered by the in-situ leaching method. The process is not yet at the stage where it can be presented t ) the mining industry as a technique proven in all its aspects, but it is a method with high success potential. Unknown factors must be evaluated by a full-scale test before the economics or the extent of the use of the method by the mining industry can be predicted. Preliminary calculations indicate that the cost of fracturing a copper deposit nuclear explosives may range from l.8 to 55.2 cents per ton or in some case: less than a cent per pound of recoverable copper. Copper may be recovered at less cost than by conventional methods. Deposits with 4 pounds of recoverable copper may be economic and production from a deposit may begin in less than half the time required for conventional methods.

Jan 1, 1967

By Robert E. Barieau

The following zero pressure thermodynamic properties of nitrogen gas are tabulated: [C°p, H° -o, S°], These properties are tabulated in units of joules, gram mole, degrees Kelvin and in calories, gram-mole, degrees Kelvin for every degree Kelvin from 50° to 550°. The same functions are also tabulated in units of British thermal units pound-mole, degrees Rankine for every degree Rankine from 100° to 1,000°.

Jan 1, 1967

By James W. Estep

The sulphur shortage that has occurred in the past two years has directed attention more and more toward sour natural gas reserves, Wellhead values of sour gas vary widely depending upon the acid gas composition, location, market conditions, and necessary processing charges. Preparation of a saleable residue gas is considerably more involved and expensive than that normally encountered in treating a sweet gas. Recent revisions in sales gas specifications have increased capital costs and processing charges. The presence of hydrogen sulphide and carbon dioxide in a natural gas contributes to shrinkage factors that may approach 50%. Fuel required by the gas sweetening process and sulphur slant tail gas incineration also contributes to a further reduction in the volume of residue gas available for sale. The additional processing facilities involving gas sweetening, mercaptan removal, expanded utilities, sulphur recovery and sulphur handling, all demand additional operating and maintenance staff. A favorable sulphur market under certain conditions may justify the processing of sour gas whereby sulphur is either a by-product or a co-product, Five typical cases involving different compositions of sour gas are presented for evaluation. Capital costs, operating problems, and operating costs are presented in detail for full economic evaluation

Jan 1, 1967

By D. A. Koss, R. O. Gordon

Changes in the ultrasonic attenuation in steel specimens have been observed during tensile tests. Samples of AISI 1020, 1045, and 1095 steel quenched and tempered to a spheroidized condition have been used. Both attenuation and microstrain measurements fail to reveal preyield dislocation motion in the as-tempered specimens. Upon reapplication of the load to samples in the strain-aged condition there is a large preyield attenuation increase but no observable micvostrain up to 90 pct of the flow stress. These and other observed changes can be related to changes in the free disloca-tion density and the average dislocation segment length. The results show that the increase inflow stress in the strain-aged condition is caused by increased fric-tional stresses rather than by dislocation pinning. Strain aging is found to proceed through three distinct stages. The second of these follows the t2,3 law and is characterized by an activation energy of 20 kcal per mole. RECENT years have seen substantial progress in the understanding of the sharp yield-point phenomenon in metals; the influence of solute atom pinning of dislocations, of dislocation multiplication, and of the stress dependence of dislocation velocity on the stress-strain curve has been investigated. Evaluation of the relative importance of these factors in the various metals and alloys is not complete, however, because observation of the stress-strain curve alone is not sufficient to determine the yield mechanism. In the experimental study of the sharp yield point it would be desirable to be able to directly observe the dislocations in a bulk specimen. Ideally, the observations should be made during deformation because of the rapidity of recovery processes in lightly strained metals. While direct observation of dislocations under these conditions is not possible, certain physical properties sensitive to the dislocation structure can be observed while a test specimen is undergoing deformation. Of these properties, one of the most useful is the ultrasonic attenuation. The total observed attenuation, a, is due to a number of causes: acoustic diffraction, scattering by inhomogeneities in the structure, heat flow, magnetostriction, and dislocation damping. Satisfactory measurements of the absolute a are difficult to make because all of these factors cannot be evaluated in any given specimen, but changes in a due to changes in the dislocation contribution alone can be reliably observed by appropriate technique. Because dislocation damping is sensitive to small concentrations of long, free dislocation segments, observation of acoustic attenuation due to dislocations is particularly useful in the study of the early stages of plastic deformation. In the experiments to be described, acoustic-attenuation measurements have been made on steel samples as these were pulled through their yield in tension. While many details of dislocation-damping phenomena in the bee metals remain obscure, the main characteristics of this type of internal friction are established. At low strain amplitudes and at frequencies well below that of dislocation resonance (the conditions of these experiments) the dislocation contribution to a is given by1 where A is the density of freely oscillating dislocation segments, L is the average segment length, B is the damping constant for a moving dislocation, w is the frequency, O is an orientation factor, C is the dislocation line tension, and t is a numerical factor relating average segment length to the distribution of lengths. Because of its fourth-power dependence on L, a is highly sensitive to changes in dislocation free segment length such as might arise from unpinning, recovery, jog formation, or dislocation intersection. The above equation is not valid near the resonant frequency of dislocations, but the segment length in steel is believed to be much too short to cause over-damped resonance near 10 Mc; this will be discussed later. In the present experiments plastic-strain measurements with a sensitivity of 2 x 10-5 were also made during the early stages of loading in order to detect preyield strain. The general plan of the experiments is to observe

Jan 1, 1967